In long-chain polymer solids, the polymer structure affects the proportion of crystalline domains, which are sites of ordered, close-packed polymer chains, to amorphous domains, which are regions of disordered, randomly oriented polymer chains.
Due to the large size of polymer chains, ordered close-packing is not observed across entire molecules. So, it is challenging to achieve highly crystalline polymers, and amorphous domains are always present in polymers.
Often, branching or large substituents in the polymer chain increase the proportion of amorphous domains, resulting in noncrystalline, amorphous polymers.
Crystalline domains provide toughness, whereas amorphous domains lend flexibility.
However, both domains impart hardness and brittleness below the glass transition temperature. Above that, amorphous domains become increasingly flexible.
On further heating to the crystalline melting temperature, or melt transition temperature, all crystalline regions become amorphous and fluid, so crystalline polymers melt at a precise temperature.
Amorphous polymers gradually transform to a liquid state, with no sharply defined melt transition temperature.

polymer classification: crystallinity

Polymer Classification: Crystallinity

Unlike ionic or small covalent molecules, polymers do not form crystalline solids due to the diffusion limitations of their long-chain structures. However, polymers contain microscopic crystalline domains separated by amorphous domains.
Crystalline domains are the regions where polymer chains are aligned in an orderly manner and held together in proximity by intermolecular forces. For example, chains in the crystalline domains of polyethylene and nylon are bound together by van der Waals interactions and hydrogen bonding, respectively.
Amorphous domains are the regions where the chains are randomly oriented and loosely packed, resulting in weak intermolecular interactions. The presence of branching or large substituents in the polymer chain further increases the likelihood of forming amorphous domains. Highly disordered polymer chains can result in a noncrystalline polymer; for example, poly(methyl methacrylate).
<img alt="Polymer structure diagram showing amorphous and crystalline domains; emphasizes material properties." src="/files/ftp_upload/12917/12917_PT_Figure_1.svg" style="text-align: center; height: 225px;" data-altupdatedat="1761830439000" data-alt="Figure1" />
Figure 1: A crystalline domain (rectangle) and an amorphous domain (oval) of a polymer.
Crystalline domains impart toughness to a polymer, whereas amorphous domains lend flexibility. Poly(ethylene terephthalate), or PET, is manufactured in different grades varying the proportion of crystalline domains from 0% to about 55%. Less crystalline PET is used for making plastic bottles. Highly crystalline PET is used as a textile fiber.
The thermal properties of highly crystalline polymers and noncrystalline polymers are different. At the glass transition temperature, both polymers transform from a hard solid to a flexible material. Upon heating further, only crystalline polymers exhibit a sharp melt transition temperature&#8212;at which the polymer transforms to a liquid. Noncrystalline polymers possess no definite melt transition temperature (crystalline melting temperature). Cross-linked polymers do not melt but directly decompose at extreme temperatures.

Unlike ionic or small covalent molecules, polymers do not form crystalline solids due to the diffusion limitations of their long-chain structures. ...

Education

JoVE Core

Organic Chemistry

Unit 1

Synthetic Polymers

KEY TERMS AND CONCEPTS

crystallinity in polymer structure

Crystallinity in polymer structure depends on how polymer chains are packed. Unlike ionic solids or small covalent molecules, polymers usually do not form fully crystalline solids because their long chains move and diffuse less easily. Instead, many polymers contain microscopic crystalline domains separated by amorphous domains.

Crystalline domains are the ordered regions of a polymer. In these areas, the chains line up closely and stay near each other because of intermolecular forces. In polyethylene, these forces are van der Waals interactions. In nylon, hydrogen bonding helps hold the chains together.

Amorphous domains are the disordered regions. The chains in these areas are randomly oriented and loosely packed, so the intermolecular interactions are weak. Branching or large substituents on the polymer chain can make amorphous domains more likely. If the chains are highly disordered, the polymer can be noncrystalline, as in poly(methyl methacrylate).

Crystalline and amorphous domains give polymers different properties. Crystalline domains make a polymer tougher, while amorphous domains make it more flexible. Poly(ethylene terephthalate), or PET, can be made in grades with about 0% to 55% crystalline domains. Less crystalline PET is used for plastic bottles, while highly crystalline PET is used as a textile fiber.

Polymers with different crystallinity also behave differently when heated. At the glass transition temperature, both crystalline and noncrystalline polymers change from a hard solid to a flexible material. With further heating, only crystalline polymers show a sharp melting transition and become liquid. Noncrystalline polymers do not have a definite melt transition temperature. Cross-linked polymers do not melt at all. They decompose at extreme temperatures.

Crystallinity in Polymer Structure

characteristics and nomenclature of homopolymers

characteristics-and-nomenclature-of-homopolymers

Naming Homopolymers from Their Monomers

Homopolymers are polymers made from identical monomer units. They contain only one repeating unit in the polymer chain. A clear example is polypropylene, which is built from propylene monomers. The name of a homopolymer is usually formed by adding the prefix poly to the monomer name. That is why the polymer from propylene is called polypropylene. When the monomer has multiple parts or substituents, the monomer name may be placed in parentheses after poly. Examples include...

characteristics and nomenclature of copolymers

characteristics-and-nomenclature-of-copolymers

Copolymers: Types, Structures, and Naming

Copolymers are polymers made from more than one kind of monomer. When different monomer species are polymerized together, the chain can contain multiple repeating units. This process is called copolymerization. Copolymers can be named by the number of monomers involved. A polymer made from two monomers is a bipolymer. Polymers made from three monomers are called terpolymers, and those made from four monomers are quaterpolymers. A common example is poly(styrene-co-acrylonitrile), also called...

polymers: defining molecular weight

Polymer Molecular Weight Averages

Polymer molecular weight is often described with averages because a polymer sample contains chains of many different lengths. Unlike a small molecule, which has one definite molecular weight, each polymer chain can have a unique molecular weight. The result is a sample made up of chains with varying sizes. The number average molecular weight, or Mn, uses the number fraction of each unique chain. A number fraction is the number of chains with a given molecular weight divided by the total number...

polymers: molecular weight distribution

Polymer Chain Size and Dispersity

Polymer chain size and dispersity describe how uniform the chains are in a polymer sample. The weight average molecular weight, Mw, is usually higher than or equal to the number average molecular weight, Mn. These two values are equal only when every chain has the same molecular weight. That exact match is rare in synthetic polymers. It is difficult to control polymerization at the molecular level with complete accuracy. Because of this, the ratio Mw to Mn is used to describe the molecular...

polymer classification: architecture

Polymer Chains: Branching and Cross-Linking

Polymer chains can be classified by their shape and by how their chains connect. Linear polymers have long chain-like structures with little or no branching. Even when a monomer has large substituent groups that look like branches, the polymer is not considered branched if those groups are part of the main chain structure. Branched polymers contain secondary chains that grow out from the main polymer chain. This branching happens when polymer growth shifts away from the edge of the growing...

Crystallinity in polymer structure depends on how polymer chains are packed. Unlike ionic solids or small covalent molecules, polymers usually do not form fully crystalline solids because their long chains move and diffuse less easily. Instead, many polymers contain microscopic crystalline domains separated by amorphous domains. Crystalline domains are the ordered regions of a polymer. In these areas, the chains line up closely and stay near each other because of intermolecular forces. In...

polymer classification: stereospecificity

Polymer Tacticity and Chain Properties

Polymer tacticity describes how side groups are arranged along a polymer chain. In polymers made from monosubstituted alkene monomers, polymerization creates chiral centers at every other carbon in the backbone. That stereochemistry can strongly affect the final properties of the polymer. There are three main configurations: isotactic, syndiotactic, and atactic. In isotactic polymers, the substituents are mostly on the same side of the backbone. In syndiotactic polymers, the substituents...

radical chain-growth polymerization: overview

radical-chain-growth-polymerization-overview

Radical Chain-Growth Polymerization Steps

Radical chain-growth polymerization builds a polymer by repeated addition of monomers to a growing chain. It uses a free-radical intermediate, which is the reactive species that keeps the chain moving forward. The process starts with a radical initiator. These initiators generate free radicals on their own by homolytic fission, or splitting a bond so each atom keeps one electron. Common initiators include organic peroxides such as dibenzoyl peroxide and azo compounds. A low...

radical chain-growth polymerization: mechanism

radical-chain-growth-polymerization-mechanism

Radical Polymer Chain Growth and Ending

Radical chain-growth polymerization builds polymers through initiation, propagation, and termination. A free radical from the initiator adds to the unsaturated bond in a monomer. The unpaired electron from the radical and one pi electron from the double bond form a sigma bond. The other pi electron then becomes a new free radical on the growing molecule. The initiation step can be shown with a phenyl free radical reacting with vinyl chloride. After initiation, the new radical adds to another...

radical chain-growth polymerization: chain branching

radical-chain-growth-polymerization-chain-branching

How Radical Polymer Chains Branch

Radical polymerization can create branched polymer chains. A clear example is ethylene polymerized by a radical route, which forms a low-density type of polyethylene with a heavily branched skeletal structure. During growth, the radical site can remove a hydrogen atom from the chain and move from the end of the chain, a primary carbon center, to a point within the chain, a secondary carbon center. When that happens, the part of the chain from the hydrogen-removal site to the end becomes a...

anionic chain-growth polymerization: overview

anionic-chain-growth-polymerization-overview

Anionic Polymerization and Everyday Plastics

Anionic polymerization is a chain-growth process that uses a carbanion as an intermediate. It begins when a strong nucleophile, such as an organolithium compound or a Grignard reagent, starts the reaction. Butyl lithium is the most commonly used initiator for this process. The monomers used in anionic polymerization must have a vinyl group attached to one or two electron-withdrawing groups. Acrylonitrile, vinyl chloride, and styrene each have one electron-withdrawing group and can form anionic...

anionic chain-growth polymerization: mechanism

anionic-chain-growth-polymerization-mechanism

Living Polymers in Anionic Polymerization

Anionic chain-growth polymerization builds a polymer through initiation, propagation, and termination. It begins when a nucleophilic anion, such as butyl lithium, attacks the pi bond of a vinylic monomer. This creates a carbanion, which is a carbon atom with a negative charge. The electron-withdrawing group on the monomer helps stabilize that carbanion. The carbanion then drives the propagation step. It acts as a Michael donor and attacks a second vinylic monomer, which serves as the Michael...

cationic chain-growth polymerization: mechanism

cationic-chain-growth-polymerization-mechanism

Cationic Polymerization Steps in Chain Growth

Cationic polymerization builds a polymer chain through three stages: initiation, propagation, and termination. It starts when a monomer’s pi bond is protonated by a Lewis acid catalyst formed from boron trifluoride and water. This protonation creates a carbocation, which is stabilized by an electron-donating group. During propagation, the pi bond of a second monomer acts as a nucleophile, meaning it donates electrons. It attacks the carbocation and forms a dimer, which becomes a new...

ziegler&ndash;natta chain-growth polymerization: overview

zieglernatta-chain-growth-polymerization-overview

Ziegler-Natta Catalysts and Linear Polymers

Ziegler-Natta polymerization uses a special catalyst to make linear polymers. It is a type of addition polymerization, also called chain-growth polymerization. This method favors straight polymer chains over branched ones. The catalyst is called a Ziegler-Natta catalyst. It is named after Karl Ziegler and Giulio Natta, who developed it in 1953. The catalyst is an organometallic complex made from titanium tetrachloride and triethyl aluminum. Its active form is an alkyl titanium compound. With...

step-growth polymerization: overview

Step-Growth Polymerization in Common Polymers

Step-growth polymerization is a condensation process that builds long-chain polymers from bi- or multifunctional monomers. In this reaction, the monomers are reactive from the start. Early in the process, most monomers form short oligomers, which are small reactive chains. These oligomers then link together later to make long polymer chains. Because the chains grow step by step, the reaction must run for a long time to reach high molecular weight. Many natural and synthetic polymers come from...

molecular weight of step-growth polymers

Step-Growth Polymerization and Chain Length

Step-growth polymerization builds polymers by linking bi- or multifunctional monomers. Bifunctional monomers form linear step-growth polymers. Multifunctional monomers can form non-linear or branched polymers. As the reaction continues, the molecular weight keeps building up step by step. High molecular weight polymers usually appear at the late stages of the polymerization. By that point, about 99% of the monomers have been consumed. The extent of the reaction can be found with the Carothers...

types of step-growth polymers: polyesters

Polyester Uses and PET Production

Polyesters are widely used step-growth polymers, and PET is one of the most important examples. These materials helped transform the textile industry because polyester blends resist wrinkles. That reduced the need for starching and ironing clothes. Industrial PET is made from dimethyl terephthalate and ethylene glycol by transesterification at 150 °C. In this process, methanol is the by-product. It vaporizes at the reaction temperature, which helps drive the reaction to completion. PET can...

olefin metathesis polymerization: overview

olefin-metathesis-polymerization-overview

Olefin Metathesis Polymerization Pathways

Olefin metathesis polymerization creates polymers by rearranging double bonds in olefins with a catalyst. The metathesis reaction moves substituents between two alkene molecules, and that same chemistry can be used to build polymer chains. Ruthenium-based Grubbs catalyst is the most common catalyst for this process. Grubbs catalyst contains a carbon-metal double bond called a carbene. The reaction is reversible and starts when the catalyst reacts with an alkene in a [2+2] cycloaddition. This...

olefin metathesis polymerization: ring-opening metathesis polymerization (romp)

olefin-metathesis-polymerization-ring-opening-metathesis

ROMP Polymerization Driven by Ring Strain

Ring-opening metathesis polymerization, or ROMP, is a polymer method that starts with strained cycloalkenes. A cycloalkene is a ring-shaped alkene, which means it contains a carbon-carbon double bond inside a ring. In ROMP, the ring strain helps push the reaction forward. The reaction begins when a cycloalkene reacts with Grubbs catalyst. This forms a metallacyclobutane intermediate, which then opens to make a new carbene. That new carbene can react with another cycloalkene molecule, and the...

olefin metathesis polymerization: acyclic diene metathesis (admet)

olefin-metathesis-polymerization-acyclic-diene-metathesis-admet

ADMET Polymerization for Linear Polymers

ADMET polymerization is a type of olefin metathesis used to build linear unsaturated polymers from terminal dienes. In this reaction, molecules such as 1,8-nonadiene react with each other and release ethylene gas. The process is reversible, so the ethylene must be removed from the reaction mixture for polymerization to continue. ADMET works through a metallacyclobutane intermediate, which forms when one double bond in a terminal diene undergoes [2+2] cycloaddition with a Grubbs catalyst. The...

key terms and concepts

Learn how crystalline and amorphous domains shape polymer properties, from toughness and flexibility to PET uses and melting behavior.

Crystallinity in Polymer Structure | JoVE K12

organic chemistry

JoVE Core Organic Chemistry explains basic concepts of stereochemistry, reactions, and mechanisms using concise and easy-to-understand animated video lessons. Additionally, the scientist-in-action videos demonstrate the application of related concepts in classical and original research experiments performed in today's laboratories worldwide.

Crystallinity in Polymer Structure

Description

Transcript

Tags