Novel Process for 3D Printing Decellularized Matrices

3D bioprinting aims to create custom scaffolds that are biologically active and accommodate the desired size and geometry. A thermoplastic backbone can ...

Cincinnati Children's Hospital Medical Center

In this study, articular cartilage was decellularized preserving a majority of the inherent proteins, cytokines, growth factors and sGAGs. The decellularized cartilage matrix (dCM) was then encapsulated in poly(lactic acid) microspheres (MS+dCM) via double emulsion. Blank microspheres without dCM, MS(-), were also produced. The microspheres were spherical in shape and protein encapsulation efficiency within MS+dCM was 63.4%. The sustained release of proteins from MS+dCM was observed over 4 weeks in vitro. Both MS+dCM and MS(-) were cytocompatible. The sustained delivery of retained growth factors and cytokines from MS+dCM promoted cell migration in contrast to MS(-). Subsequently, chondrogenesis of hMSCs was upregulated in presence of MS+dCM as evidenced from immunohistochemistry, biochemical quantification and qPCR studies. Specifically, collagen II, aggrecan and SOX 9 gene expression were increased in the presence of MS+dCM by an order or more in magnitude compared to MS(-) with concomitant downregulation of hypertrophic genes (COL X) despite being cultured in the absence of chondrogenic media, (p&lt;0.05). Lastly, microspheres containing alkaline phosphatase (MS+ALP), a surrogate to assess the thermal stability of dCM proteins, incorporated within poly(caprolactone) filaments showed that the enzyme remained functional after filament production by melt extrusion. The establishment of a novel, thermally stable process for producing filaments containing chondroinductive microspheres provides evidence supporting subsequent development of a clinically-relevant, 3D scaffold fabricated from them for osteochondral regeneration and repair.

Microspheres containing decellularized cartilage induce chondrogenesis <i>in vitro</i> and remain functional after incorporation within a poly(caprolactone) filament useful for fabricating a 3D scaffold.

In this study, articular cartilage was decellularized preserving a majority of the inherent proteins, cytokines, growth factors and sGAGs. The decellularized cartilage matrix (dCM) was then encapsulated in poly(lactic acid) microspheres (MS + dCM) via double emulsion. Blank microspheres without dCM, MS(-), were also produced. The microspheres were spherical in shape and protein encapsulation efficiency within MS + dCM was 63.4%. The sustained release of proteins from MS + dCM was observed over 4 weeks in vitro. Both MS + dCM and MS(-) were cytocompatible. The sustained delivery of retained growth factors and cytokines from MS + dCM promoted cell migration in contrast to MS(-). Subsequently, chondrogenesis of human mesenchymal stem cells was upregulated in presence of MS + dCM as evidenced from immunohistochemistry, biochemical quantification and qPCR studies. Specifically, collagen II, aggrecan and SOX 9 gene expression were increased in the presence of MS + dCM by an order or more in magnitude compared to MS(-) with concomitant downregulation of hypertrophic genes (COL X) despite being cultured in the absence of chondrogenic media, (p < 0.05). Lastly, microspheres containing alkaline phosphatase (MS + ALP), a surrogate to assess the thermal stability of dCM proteins, incorporated within poly(caprolactone) filaments showed that the enzyme remained functional after filament production by melt extrusion. The establishment of a novel, thermally stable process for producing filaments containing chondroinductive microspheres provides evidence supporting subsequent development of a clinically-relevant, 3D scaffold fabricated from them for osteochondral regeneration and repair.

Microspheres containing decellularized cartilage induce chondrogenesis in vitro and remain functional after incorporation within a poly(caprolactone) filament useful for fabricating a 3D scaffold.

Article	Year
Microspheres containing decellularized cartilage induce chondrogenesis <i>in vitro</i> and remain functional after incorporation within a poly(caprolactone) filament useful for fabricating a... Biofabrication\| PubMed ID: 29313825	2018
Microspheres containing decellularized cartilage induce chondrogenesis in vitro and remain functional after incorporation within a poly(caprolactone) filament useful for fabricating a 3D sca... Biofabrication\| PubMed ID: 29394158	2018

Paulomi Ghosh

Biography

JoVE Journal Publications

Other Publications