Description: Scopri come preparare e testare adesivi per legno a base di semi vegetali come alternativa sostenibile ai prodotti sintetici. Questo metodo utilizza miscele di farina di semi e valuta la resistenza allo scorrimento per misurare le prestazioni dell'adesivo.

ai_agent_IP

ai_agent

maintenance

instantTrialDurationMinutes

isBiopharma

enableNewMyJoveSectionDesign

educationFeatures

seoMetaApi

ai_copilot_institution_blacklist

ai_chat_institution_blacklist

freeAccessWindow

ssoRoleCapture

scheduledMaintenanceBanner

joveLabsFeatures

disable_autoplay_for_bots

extended_trial_duration

5 minutes

playerTrialDesktop

I dati riportati in questo lavoro fanno parte della ricerca del progetto USDA-ARS 306 'Values-Added Products from Cottonseed' supportata dal finanziamento interno dell'Agenzia. La pubblicazione di questo articolo è supportata in parte dal Journal of Visualized Experiments. La menzione di nomi commerciali o prodotti commerciali in questa pubblicazione ha il solo scopo di fornire informazioni specifiche e non implica una raccomandazione o un'approvazione da parte del Dipartimento dell'Agricoltura degli Stati Uniti. L'USDA è un fornitore e datore di lavoro per le pari opportunità. Prendiamo atto dei commenti costruttivi dell'editore scientifico di JoVE e dei revisori nel processo di revisione e revisione.

1. di cotone e prodotti a base di farina di soia (Figura 1) <ol><li> Ottenere le materie prime, cotone sgrassato e pasti a base di soia, dalle fonti disponibili in commercio. </li><li> Ottenere il pasto lavorando macinando pasto solido sgrassata in un mulino campione ciclone per passare una schermata di acciaio 0,5 millimetri 16. </li><li> Preparare i pasti acqua lavato dai pasti di lavoro dopo l&#39;estrazione di acqua (25 g farina 200 ml di acqua) per separare i componenti solubili in acqua nei pasti 21. </li><li> Preparare proteine ​​isolate di pasti di lavoro di estrazione alcali e precipitazioni acide 16. </li></ol> 2. Preparazione di legno impiallacciatura strisce <ol><li> Impiallacciatura di legno (1,59 millimetri di spessore) ottenuti da una fonte disponibile in commercio in strisce larghe 25,4 millimetri per 88,9 millimetri lunghi. </li><li> Matita segnare una linea attraverso le venature del legno a 25,4 mm (1,0 &quot;) di lunghezza da una estremità di ogni striscia Etichetta queste strisce appropriato con testare trattamenti o numeri 5.. -10 paia di legno sono preparati per ogni variabile test. </li></ol> 3. Preparazione di Adhesive Fanghi <ol><li> Calcolare la quantità di acqua lavato pasto necessaria per i campioni di legno per test, dal tasso di applicazione (ad esempio, 4 mg secco contenuto cm -2) x area totale di legame (ad esempio, 581 centimetri 2 su 90 listelli di legno con 2,54 x 2,54 centimetri zona di incollaggio ciascuna) più circa il 30% in più per enoughness (cioè, 4 x 581 x 130% 3 g di acqua lavato pasto per l&#39;esempio). </li><li> Mescolare acqua pasto lavato con acqua deionizzata (3:25 w / w), e mescolare con un bastoncino magnetico per 2 ore in un bicchiere sigillato con Parafilm. </li></ol> 4. Preparazione di Bonded legno campioni <ol><li> Spazzolare liquami adesivo su una delle estremità delle strisce impiallacciatura di legno che coprono 2 25,4 mm (1,0 &quot;) di lunghezza di aria secca per 10 - 15 min. O fino cattivo gusto. </li><li> Spazzola un secondo strato di boiacca adesiva sulla parte superiore del primo strato e asciugare di nuovo. La quantità di adesivo seccoPreparazione applicato è di circa 4,5 mg secco solido per cm 2 di incollaggio sono di ogni striscia di legno. </li><li> Sovrapporre l&#39;area rivestita adesiva appiccicoso (25,4 x 25,4 millimetri o 1,0 &quot;x 1,0&quot;) di strisce di impiallacciatura di legno 2. Hot-press utilizzando un banco riscaldata Premere a 100 ° C per 20 minuti ad una pressione di 400 psi (2,8 MPa). Nota la pressione è la forza applicata dalla stampa diviso per l&#39;area di sovrapposizione dei campioni di legno. Questi parametri di legame possono essere modificati come necessario per ciascuna variabile test. </li><li> Raffreddare e condizionare i campioni di legno legati per 48 ore in una camera di condizionamento o di un incubatore con controllo dell&#39;umidità (temperatura di 22 - 23 ° C ed umidità relativa del 50 - 60%; la figura 2). </li></ol> 5. resistenza all&#39;acqua Experiments <ol><li> Immergere i campioni di legno incollati, dopo condizionamento iniziale, in acqua corrente per 48 h in un vassoio di plastica a RT (22 - 23 ° C). Gli esemplari bagnato dopo ammollo sono testati immediatamente per il taglioresistenza alla rottura e segnalato come resistenza all&#39;acqua. L&#39;acqua in eccesso sulla superficie rivestimento può essere rimosso tamponando delicatamente con carta velina prima di misurazioni. </li><li> Immergere un&#39;altra serie di campioni di legno incollati, dopo condizionamento iniziale, in un bagno di acqua a 63 ° C per 4 ore, poi si essicca a condizioni ambientali (temperatura di 22 - 23 ° C ed umidità relativa del 50 - 60%) O / N (18 - 20 ore). Ripetere il ciclo di immersione asciugatura volta con un tempo di asciugatura 48 hr. I campioni essiccati vengono poi testati per la resistenza al taglio in pausa e riportati come forza adesiva imbevuto. </li></ol> 6. Misure Lap Shear Forza <ol><li> Montare un campione di legno incollate nelle Scaglie di pesce morsetti a cuneo reticolati 32 x 40 mm su un Tester Materials con una pressione di presa di 7 MPa, e impostare la velocità della traversa a 1 mm min -1. </li><li> Misurare e registrare la resistenza al taglio a rottura per ogni campione di legno incollati. I risultati delle misurazioni multiple vengono mediate per ciascuna forma adesivalamento e variabile del test. </li></ol>

<ol><li>Frihart, C. R., Hunt, C. G. <a target="_blank" href="http://scholar.google.com/scholar?hl=en&safe=off&q=author%3aFrihart%2C+CR+%22Wood+Handbook%3A+wood+as+an+engineering+material%3A+General+technical+report+FPL%3B+GTR-190%22">Wood Handbook: wood as an engineering material: General technical report FPL; GTR-190</a>. , Dept. of Agriculture, Forest Service, Forest Products Laboratory. (2010).</li>
<li>Lambuth, A. L. <a target="_blank" href="http://scholar.google.com/scholar?hl=en&safe=off&q=author%3aLambuth%2C+AL+%22Handbook+of+Adhesive+Technology%22">Handbook of Adhesive Technology</a>. Pizza, A., Mittal, K. L. , Marcel Dekker, Inc. 457-478 (2003).</li>
<li>Kalapathy, U., Hettiarachchy, N. S., Myers, D., Hanna, M. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Modification+of+soy+proteins+and+their+adhesive+properties+on+woods%5BTitle%5D)+AND+%22J.+Am.+Oil+Chem.+Soc%22%5BJournal%5D)">Modification of soy proteins and their adhesive properties on woods.</a> J. Am. Oil Chem. Soc. 72 (5), 507-510 (1995).</li>
<li>Li, K., Peshkova, S., Geng, X. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Investigation+of+soy+protein-Kymene+adhesive+systems+for+wood+composites%5BTitle%5D)+AND+%22J.+Am.+Oil+Chem.+Soc%22%5BJournal%5D)">Investigation of soy protein-Kymene adhesive systems for wood composites.</a> J. Am. Oil Chem. Soc. 81 (5), 487-491 (2004).</li>
<li>Qi, G., Li, N., Wang, D., Sun, X. S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Adhesion+and+physicochemical+properties+of+soy+protein+modified+by+sodium+bisulfite%5BTitle%5D)+AND+%22J.+Am.+Oil+Chem.+Soc%22%5BJournal%5D)">Adhesion and physicochemical properties of soy protein modified by sodium bisulfite.</a> J. Am. Oil Chem. Soc. 90 (12), 1917-1926 (2013).</li>
<li>Cheng, H. N., Dowd, M. K., He, Z. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Investigation+of+modified+cottonseed+protein+adhesives+for+wood+composites%5BTitle%5D)+AND+%22Ind.+Crop.+Prod%22%5BJournal%5D)">Investigation of modified cottonseed protein adhesives for wood composites.</a> Ind. Crop. Prod. 46, 399-403 (2013).</li>
<li>Pan, Z., Cathcart, A., Wang, D. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Thermal+and+chemical+treatments+to+improve+adhesive+property+of+rice+bran%5BTitle%5D)+AND+%22Ind.+Crop.+Prod%22%5BJournal%5D)">Thermal and chemical treatments to improve adhesive property of rice bran.</a> Ind. Crop. Prod. 22 (3), 233-240 (2005).</li>
<li>Nordqvist, P., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Wheat+gluten+fractions+as+wood+adhesives-glutenins+versus+gliadins%5BTitle%5D)+AND+%22J.+Appl.+Polymer+Sci%22%5BJournal%5D)">Wheat gluten fractions as wood adhesives-glutenins versus gliadins.</a> J. Appl. Polymer Sci. 123 (3), 1530-1538 (2012).</li>
<li>Bandara, N., Chen, L., Wu, J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Adhesive+properties+of+modified+triticale+distillers+grain+proteins%5BTitle%5D)+AND+%22Int.+J.+Adhes.+Adhes%22%5BJournal%5D)">Adhesive properties of modified triticale distillers grain proteins.</a> Int. J. Adhes. Adhes. 44, 122-129 (2013).</li>
<li>Li, N., Qi, G., Sun, X. S., Stamm, M. J., Wang, D. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Physicochemical+properties+and+adhesion+performance+of+canola+protein+modified+with+sodium+bisulfite%5BTitle%5D)+AND+%22J.+Am.+Oil+Chem.+Soc%22%5BJournal%5D)">Physicochemical properties and adhesion performance of canola protein modified with sodium bisulfite.</a> J. Am. Oil Chem. Soc. 89 (5), 897-908 (2012).</li>
<li>Wang, C., Wu, J., Bernard, G. M., Wasylishen, R. E. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Preparation+and+characterization+of+canola+protein+isolate+-poly%28glycidyl+methacrylate%29+conjugates%3A+a+bio-based+adhesive%5BTitle%5D)+AND+%22Ind.+Crop.+Prod%22%5BJournal%5D)">Preparation and characterization of canola protein isolate -poly(glycidyl methacrylate) conjugates: a bio-based adhesive.</a> Ind. Crop. Prod. 57, 124-131 (2014).</li>
<li>Kong, X., Liu, G., Curtis, J. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Characterization+of+canola+oil+based+polyurethane+wood+adhesives%5BTitle%5D)+AND+%22Int.+J.+Adhes.+Adhes%22%5BJournal%5D)">Characterization of canola oil based polyurethane wood adhesives.</a> Int. J. Adhes. Adhes. 31 (6), 559-564 (2011).</li>
<li>Xiao, Z., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Utilization+of+sorghum+lignin+to+improve+adhesion+strength+of+soy+protein+adhesives+on+wood+veneer%5BTitle%5D)+AND+%22Ind.+Crop.+Prod%22%5BJournal%5D)">Utilization of sorghum lignin to improve adhesion strength of soy protein adhesives on wood veneer.</a> Ind. Crop. Prod. 50, 501-509 (2013).</li>
<li>Moubarik, A., Grimi, N., Boussetta, N., Pizzi, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Isolation+and+characterization+of+lignin+from+Moroccan+sugar+cane+bagasse%3A+Production+of+lignin-phenol-formaldehyde+wood+adhesive%5BTitle%5D)+AND+%22Ind.+Crop.+Prod%22%5BJournal%5D)">Isolation and characterization of lignin from Moroccan sugar cane bagasse: Production of lignin-phenol-formaldehyde wood adhesive.</a> Ind. Crop. Prod. 45, 296-302 (2013).</li>
<li>Patel, A. K., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Development+of+a+chitosan-based+adhesive.+Application+to+wood+bonding%5BTitle%5D)+AND+%22J.+Appl.+Polymer+Sci%22%5BJournal%5D)">Development of a chitosan-based adhesive. Application to wood bonding.</a> J. Appl. Polymer Sci. 127 (6), 5014-5021 (2013).</li>
<li>He, Z., Cao, H., Cheng, H. N., Zou, H., Hunt, J. F. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Effects+of+vigorous+blending+on+yield+and+quality+of+protein+isolates+extracted+from+cottonseed+and+soy+flours%5BTitle%5D)+AND+%22Modern+Appl.+Sci%22%5BJournal%5D)">Effects of vigorous blending on yield and quality of protein isolates extracted from cottonseed and soy flours.</a> Modern Appl. Sci. 7 (10), 79-88 (2013).</li>
<li>Amico, S., Hrabalova, M., Muller, U., Berghofer, E. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Bonding+of+spruce+wood+with+wheat+flour+glue-Effect+of+press+temperature+on+the+adhesive+bond+strength%5BTitle%5D)+AND+%22Ind.+Crop.+Prod%22%5BJournal%5D)">Bonding of spruce wood with wheat flour glue-Effect of press temperature on the adhesive bond strength.</a> Ind. Crop. Prod. 31, 255-260 (2010).</li>
<li>Gao, Q., Shi, S. Q., Li, J., Liang, K., Zhang, X. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Soybean+meal-based+wood+adhesives+enhanced+by+modified+polyacrylic+acid+solution%5BTitle%5D)+AND+%22BioResources%22%5BJournal%5D)">Soybean meal-based wood adhesives enhanced by modified polyacrylic acid solution.</a> BioResources. 7 (1), 946-956 (2011).</li>
<li>Chen, N., Lin, Q., Rao, J., Zeng, Q. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Water+resistances+and+bonding+strengths+of+soy-based+adhesives+containing+different+carbohydrates%5BTitle%5D)+AND+%22Ind.+Crop.+Prod%22%5BJournal%5D)">Water resistances and bonding strengths of soy-based adhesives containing different carbohydrates.</a> Ind. Crop. Prod. 50, 44-49 (2013).</li>
<li>He, Z., Chapital, D. C., Cheng, H. N., Dowd, M. K. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Comparison+of+adhesive+properties+of+water-+and+phosphate+buffer-washed+cottonseed+meals+with+cottonseed+protein+isolate+on+maple+and+poplar+veneers%5BTitle%5D)+AND+%22Int.+J.+Adhes.+Adhes%22%5BJournal%5D)">Comparison of adhesive properties of water- and phosphate buffer-washed cottonseed meals with cottonseed protein isolate on maple and poplar veneers.</a> Int. J. Adhes. Adhes. 50, 102-106 (2014).</li>
<li>He, Z., Cheng, H. N., Chapital, D. C., Dowd, M. K. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Sequential+fractionation+of+cottonseed+meal+to+improve+its+wood+adhesive+properties%5BTitle%5D)+AND+%22J.+Am.+Oil+Chem.+Soc%22%5BJournal%5D)">Sequential fractionation of cottonseed meal to improve its wood adhesive properties.</a> J. Am. Oil Chem. Soc. 91 (1), 151-158 (2014).</li>
<li>Sun, X., Bian, K. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Shear+strength+and+water+resistance+of+modified+soy+protein+adhesives%5BTitle%5D)+AND+%22J.+Am.+Oil+Chem.+Soc%22%5BJournal%5D)">Shear strength and water resistance of modified soy protein adhesives.</a> J. Am. Oil Chem. Soc. 76 (8), 977-980 (1999).</li>
<li>He, Z., Chapital, D. C., Cheng, H. N., Klasson, K. T. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Application+of+tung+oil+to+improve+adhesion+strength+and+water+resistance+of+cottonseed+meal+and+protein+adhesives+on+maple+veneer%5BTitle%5D)+AND+%22Ind.+Crop.+Prod%22%5BJournal%5D)">Application of tung oil to improve adhesion strength and water resistance of cottonseed meal and protein adhesives on maple veneer.</a> Ind. Crop. Prod. 61, 398-402 (2014).</li>
<li>Hettiarachchy, N. S., Kalapathy, U., Myers, D. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Alkali-modified+soy+protein+with+improved+adhesive+and+hydrophobic+properties%5BTitle%5D)+AND+%22J.+Am.+Oil+Chem.+Soc%22%5BJournal%5D)">Alkali-modified soy protein with improved adhesive and hydrophobic properties.</a> J. Am. Oil Chem. Soc. 72 (12), 1461-1464 (1995).</li>
<li>Wang, D., Sun, X. S., Yang, G., Wang, Y. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Improved+water+resistance+of+soy+protein+adhesive+at+isoelectric+point%5BTitle%5D)+AND+%22Trans.+ASABE%22%5BJournal%5D)">Improved water resistance of soy protein adhesive at isoelectric point.</a> Trans. ASABE. 52 (1), 173-177 (2009).</li>
<li>Zhong, Z., Sun, X. S., Fang, X., Ratto, J. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Adhesive+strength+of+guanidine+hydrochloride-modified+soy+protein+for+fiberboard+application%5BTitle%5D)+AND+%22Int.+J.+Adhes.+Adhes%22%5BJournal%5D)">Adhesive strength of guanidine hydrochloride-modified soy protein for fiberboard application.</a> Int. J. Adhes. Adhes. 22 (4), 267-272 (2002).</li>
<li>Kafkalidis, M., Thouless, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((The+effects+of+geometry+and+material+properties+on+the+fracture+of+single+lap-shear+joints%5BTitle%5D)+AND+%22Int.+J.+Solids+Structures%22%5BJournal%5D)">The effects of geometry and material properties on the fracture of single lap-shear joints.</a> Int. J. Solids Structures. 39 (17), 4367-4383 (2002).</li>
<li>Tang, L., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Dynamic+adhesive+wettability+of+poplar+veneer+with+cold+oxygen+plasma+treatment%5BTitle%5D)+AND+%22Bio+Res%22%5BJournal%5D)">Dynamic adhesive wettability of poplar veneer with cold oxygen plasma treatment.</a> Bio Res. 7 (3), 3327-3339 (2012).</li>
<li>Gui, C., Liu, X., Wu, D., Zhou, T., Wang, G., Zhu, J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Preparation+of+a+new+type+of+polyamidoamine+and+its+application+for+soy+flour-based+adhesives%5BTitle%5D)+AND+%22J.+Am.+Oil+Chem.+Soc%22%5BJournal%5D)">Preparation of a new type of polyamidoamine and its application for soy flour-based adhesives.</a> J. Am. Oil Chem. Soc. 99 (90), 265-272 (2013).</li>
</ol>

Gli autori non hanno nulla da rivelare.

Questo articolo presenta una procedura di base per la preparazione e prodotti come adesivi di legno vegetale seed test-based. I fanghi adesivi exampled in questo protocollo sono semplicemente il prodotto farina di semi scremato e dell&#39;acqua. Varie formulazioni adesive possono essere raggiunti mediante aggiunta di reagenti di prova (come dodecil solfato di sodio, bisolfito di sodio o olio tung) 5,6,23 e / o variazioni di condizioni (quali pH, rapporto tra solido e acqua) miscelazione 3,24 , 25. ...

Incollaggio di legno gioca un ruolo sempre più importante nel settore dei prodotti della foresta ed è un fattore chiave per l&#39;utilizzo efficiente delle risorse di legname 1. L&#39;interesse per l&#39;uso di adesivi a base naturale dei prodotti del legno è aumentato costantemente dal 1930 a raggiungere un picco intorno al 1960 2. Dopo questo periodo, il prezzo di adesivi a base di petrolio è diventato così basso che sfollate adesivi proteine ​​da diversi mercati tradizionali. Negli ultimi due decenni, questa tendenza è invertita con rinnovato interesse per l&#39;utilizzo di materiali che sono rinnovabili, biodegradabili, e più ambientalmente accettabile. Queste risorse naturali comprendono, ma non sono limitati a, proteine ​​di soia 3-5, proteine ​​di cotone 6, crusca di riso 7, glutine di frumento 8, proteine ​​del grano distillatori 9, proteine ​​colza e olio 10-12, lignina da sorgo e di canna da zucchero bagasse 13 , 14, e polisaccaridi derivati ​​da gusci di gamberetti 15. &lt;p class = &quot;jove_content&quot;&gt; considerando che gli isolati di proteine ​​di semi sono stati ampiamente valutati come potenziali adesivi per legno, la procedura di isolamento comporta alcalina corrosivo e reagenti acidi e rende adesivi isolare basata relativamente costoso e meno favorevole all&#39;ambiente 16. Così, alcuni pasti seme sgrassate (farine) con o senza trattamento sono stati anche testati per fini adesivo, anche se le proprietà adesive di questi pasti non eseguono nonché proteine ​​isolate 17-19. Abbiamo sequenza frazionata pasto di semi di cotone (CM) in diverse frazioni, e ha esaminato la loro forza adesiva in impiallacciature di legno bonding 20,21. La frazione solida insolubile in acqua (cotone lavato seguito pasto-WCM) potrebbe essere usato come adesivi per legno, paragonabili alle proteine ​​di cotone isolato (CSPI), e sarebbe meno costosa per la preparazione di CSPI. Forza adesiva e resistenza all&#39;acqua sono due parametri critici per valutare le prestazioni diun potenziale materiale adesivo. Qui, la forza adesiva è riportato come la resistenza al taglio a rottura del legame giro di ogni campione di legno. Resistenza all&#39;acqua dell&#39;adesivo viene misurato dalla variazione nella resistenza al taglio per trazione del campione di legno legati a rottura a causa di ammollo acqua. Utilizzando sgrassate di cotone e soia pasti come materie prime, questo protocollo fornisce un modo semplice e diretto per preparare e vegetali di prova prodotti a base di semi-come adesivi legno. Questo protocollo sarebbe utile nel facilitare lo sforzo nella ricerca di formulazioni più economiche e rispettose dell&#39;ambiente di adesivi naturali del legno a base di prodotti.

<table><tbody><tr><td>Farina di semi di cotone sgrassata</td><td>Kentwood Co-op</td><td></td><td>Kentwood, LA, USA</td></tr><tr><td>Farina di soia sgrassata</td><td>Kentwood Co-op</td><td></td><td>Kentwood, LA, USA</td></tr><tr><td>Impiallacciature di legno</td><td>Certamente Wood, Inc.</td><td></td><td>East Aurora, NY, USA</td></tr><tr><td>Mulino per campioni a ciclone (modello 3010-014)</td><td>UDY Corporation</td><td></td><td>Fort Collins, CO, USA</td></tr><tr><td>Pressa riscaldata da banco (modello 3856)</td><td>Carver, Inc.</td><td></td><td>Wabash, IN, Stati Uniti</td></tr><tr><td>Tester di materiali</td><td>Zwick GmbH & Co.</td><td></td><td>Ulm, Germania</td></tr></tbody></table>

preparazione e test di adesivi a base di legno pasto pianta seed

Preparation and Testing of Plant Seed Meal-based Wood Adhesives

Recentemente, l&#39;interesse nelle sementi di piante a base pasto-prodotti come adesivi per legno è costantemente aumentato, come queste materie prime vegetali sono considerati rinnovabile e rispettosa dell&#39;ambiente. Questi prodotti naturali possono servire come alternative ai adesivi a base di petrolio per facilitare le preoccupazioni ambientali e di sostenibilità. Questo lavoro dimostra la preparazione e collaudo degli adesivi a base di legno di semi-vegetale con cotone e farina di soia come materie prime. In aggiunta ai pasti non trattati, acqua lavato piatti e isolati proteici sono preparati e testati. Boiacche adesive vengono preparati miscelando un pasto prodotto liofilizzato con acqua deionizzata (03:25 w / w) per 2 ore. Ogni preparazione adesivo è applicato ad una estremità di strisce di impiallacciatura 2 legno utilizzando un pennello. Le aree adesivo viscoso rivestite delle strisce impiallacciatura di legno sono falde incollate da pressatura a caldo. Forza adesiva è segnalato come la resistenza al taglio del campione di legno incollate a rottura. Resistenza all&#39;acqua degli adesivi è misurato dalil cambiamento di resistenza a taglio del legno incollato provini a rottura dopo ammollo acqua. Questo protocollo permette di valutare i prodotti agricoli a base di semi di piante come candidati idonei per la sostituzione di adesivi a base di legno sintetiche. Adeguamenti formulazione adesiva con o senza additivi e condizioni di incollaggio possono ottimizzare le loro proprietà adesive per diverse applicazioni pratiche.

Il rendimento di ciascuna formulazione adesiva è determinata dalla resistenza al taglio del campione di legno legati a rottura e valori variano a seconda delle dimensioni della impiallacciatura di legno utilizzato. Per esempio, nella tabella 1, i valori di resistenza adesiva asciutti e bagnati dei provini incollati sono inferiori quando si utilizzano nastri di acero sottili e stretti (vedi cotone-1), in contrasto con le strisce più spesse e più ampia di cotone-2 raccomandate nel protocollo, utilizzando ...

Per facilitare lo sforzo nella ricerca di formulazioni più economiche e rispettose dell'ambiente di adesivi per legno a base di prodotti naturali, questo lavoro dimostra la preparazione e il test di adesivi per legno a base di semi vegetali. Questo protocollo consente di valutare i prodotti agricoli a base di sementi vegetali come candidati idonei per la sostituzione di adesivi per legno a base sintetica.

Preparazione e test di adesivi a base di legno pasto pianta Seed

Recently, the interest in plant seed meal-based products as wood adhesives has steadily increased, as these plant raw materials are considered renewable ...

L'obiettivo generale di questo video è mostrare una procedura di base per preparare e testare prodotti a base di semi vegetali come adesivi per legno. Questo viene realizzato innanzitutto preparando una sospensione adesiva utilizzando un seme vegetale in uso, farina e acqua. Il secondo passaggio consiste nell'applicare la sospensione adesiva su un'estremità di due strisce di legno compensato.Successivamente, unire le due strisce di legno sovrapponendo le aree rivestite con adesivo appiccicoso, quindi pressarle a caldo dopo il condizionamento. L'ultimo passaggio consiste nel misurare la resistenza a trazione al momento della rottura delle coppie di legno incollate. Infine, la resistenza al taglio alla rottura viene riportata come resistenza dell'adesivo con le condizioni di trattamento indicate.Questo metodo fornisce un modo semplice per preparare prodotti a base di amido, ad esempio adesivi per legno. Sarebbe utile negli sforzi volti a ottenere formulazioni economiche e rispettose dell'ambiente per adesivi per legno di origine biologica. Inoltre, la procedura verrà illustrata in capitoli che rivendicano risultati ottenuti nel mio laboratorio.Il primo passo consiste nel preparare la

preparation-and-testing-of-plant-seed-meal-based-wood-adhesives

Research

Ricerca

JoVE Journal

Environment

Ambiente

Vi presentiamo la procedura per assemblare un seme saggio di biancheria da letto di mano (SCBA) da Arabidopsis thaliana semi. La SCBA ha dimostrato di essere uno strumento potente per esplorare geneticamente e in vitro come il germinazione del seme controlli endosperma nei semi dormienti e in risposta a stimoli luminosi. L'autorespiratore in linea di principio applicabile in qualsiasi situazione in cui l'endosperma è sospettato di influenzare la crescita embrionale.

Un cappotto Seed Bedding Assay per esplorare geneticamente<em&gt; In Vitro</em&gt; Come la Germinazione Controlli endosperma del seme in<em&gt; Arabidopsis thaliana</em

La struttura della parete cellulare vegetale e i tratti chimici vengono valutati per identificare le materie prime ideali per i biocarburanti e i biomateriali. I metodi standard presentano limitazioni quando vengono applicati a set di dati di grandi dimensioni. Questi metodi di pretrattamento ad alto rendimento, saccarificazione enzimatica e spettrometria di massa a fascio molecolare di pirolisi confrontano un gran numero di campioni di biomassa con tempi e costi sperimentali ridotti.

High-throughput screening delle Variazioni riluttanza a lignocellulosica Biomassa: Total lignina, lignina monomeri, e enzimatica Zucchero di uscita

In questo studio, un protocollo è stato sviluppato per produrre pellet di buona qualità utilizzando un mulino pellet die piatta ridotti test consumo specifico di energia ad alta umidità paglia del mais e un legante a base di amido. I risultati hanno indicato che l'aggiunta di un legante amido di mais migliorata la durabilità pellet, ridotto ammende cento e diminuisce il consumo energetico specifico.

Metodo per la Produzione di Pellet durevoli a basso consumo energetico utilizzando ad alta umidità paglia del mais e amido di mais Binder in un appartamento Die Pellet Mill

Il flusso laterale dalla produzione di olio vegetale di Crambe abyssinica ha un valore limitato. Lo scopo di questo studio era di trovare metodi per estrusione di materiali a base di questo flusso lato, dimostrando che i prodotti con un valore superiore possono essere prodotti. Gli estrusi sono stati trovati ad avere proprietà promettenti.

Film di Estrusione Abyssinica Crambe / Glutine di frumento Miscele

Qui, presentiamo un protocollo per eseguire l'estrazione di etanolo di lignina da diverse fonti di biomassa. L'effetto delle condizioni di estrazione sul rendimento di lignina e contenuto di β-O-4 sono presentati. Depolimerizzazione selettiva viene eseguita sulle lignine ottenute per ottenere prodotti di alta monomero aromatico.

Estrazione della lignina con alto contenuto di β-O-4 da etanolo lieve estrazione ed il relativo effetto sul rendimento depolimerizzazione

Il legno densificato, delificato, rappresenta un nuovo promettente materiale leggero, ad alte prestazioni e a base biologica con un grande potenziale per sostituire parzialmente in futuro i compositi rinforzati in fibra naturale rinforzata o in fibra di vetro. Qui presentiamo due percorsi di fabbricazione versatili e dimostriamo la possibilità di creare parti composite complesse.

Fabbricazione e progettazione di compositi ad alte prestazioni basati sul legno

Presentiamo una procedura, ASTM D7998-19, per una valutazione rapida e più coerente della resistenza sia a secco che a umido dei legami adesivi sul legno. Il metodo può anche essere utilizzato per fornire informazioni sullo sviluppo della forza in funzione della temperatura e del tempo o sulla ritenzione della forza fino a 250 °C.

Metodo di prova standard ASTM D 7998-19 per lo sviluppo della resistenza coesiva degli adesivi per legno

È stato sviluppato un versatile processo di estrusione a doppia vite per fornire un efficiente pretrattamento termo-meccanico-chimico sulla biomassa lignocellulosica, che porta ad un aumento delle proporzioni medie delle fibre. Un legante naturale può anche essere aggiunto continuamente dopo la raffinazione delle fibre, portando a pannelli in fibra a base bio-con migliori proprietà meccaniche dopo la pressatura a caldo del materiale estruso ottenuto.

Processo di estrusione a doppia vite per produrre pannelli in fibra rinnovabile

Questo protocollo presenta un metodo per valutare la velocità di alimentazione del crostaceo legnoso, Limnoria, misurando la produzione di pellet fecale. Questo metodo è progettato per l'uso in laboratori non specializzati e ha il potenziale per l'incorporazione nei protocolli di test standard, per valutare una maggiore durata del legno in condizioni marine.

Test rapidi di resistenza del legno alla biodegradazione da parte di crostacei marini che annoiano il legno

Questo protocollo mirava a descrivere una guida dettagliata sulla preparazione di sezioni di campioni di semi duri a basso contenuto d'acqua per l'analisi MALDI-IMS, mantenendo la distribuzione e l'abbondanza originali degli analiti e fornendo un segnale di alta qualità e una risoluzione spaziale.

Preparazione di semi di palma dura per l'analisi di spettrometria di massa con desorbimento/ionizzazione-imaging laser assistita da matrice

Qui presentiamo una metodologia ottimizzata per la produzione di compositi a base di micelio (MBC) da prodotti petrolchimici e materiali inquinanti per applicazioni di isolamento termico. Per diventare a zero emissioni di carbonio e sostenibili, i materiali biobased e compostabili come il bio-composito di micelio potrebbero essere la soluzione. Per determinare se soddisfano gli standard di costruzione, sono stati condotti diversi esperimenti.

Produzione e test del comportamento all'umidità e delle proprietà termiche della paglia di colza e dei biocompositi di micelio Ganoderma resinaceum

Scopri come preparare e testare adesivi per legno a base di semi vegetali come alternativa sostenibile ai prodotti sintetici. Questo metodo utilizza miscele di farina di semi e valuta la resistenza allo scorrimento per misurare le prestazioni dell'adesivo.

Preparazione e test di adesivi a base di legno pasto pianta Seed

Esplora altri video