Name: Roughness Impact of Piezoelectric Dental Scaler on Two Distinct Flowable Composite Filling Materials (동영상) | JoVE Journal
Uploaded: 2025-01-10T13:30:00.000+00:00
Duration: 5 min 30 s
Description: 학습하세요 압전식 초음파 스케일러가 두 종류의 유동성 복합 충전 재료 표면 거칠기에 미치는 영향을 평가하는 방법을. 이 연구는 임상에서 복합 수복물 주변의 세심한 스케일링 기술의 필요성을 강조합니다.

ai_agent_IP

ai_agent

maintenance

instantTrialDurationMinutes

isBiopharma

enableNewMyJoveSectionDesign

educationFeatures

seoMetaApi

ai_copilot_institution_blacklist

ai_chat_institution_blacklist

freeAccessWindow

ssoRoleCapture

scheduledMaintenanceBanner

joveLabsFeatures

disable_autoplay_for_bots

extended_trial_duration

5 minutes

<ol><li>Hossam, A. E., Rafi, A. T., Ahmed, A. S., Sumanth, P. C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Surface+topography+of+composite+restorative+materials+following+ultrasonic+scaling+and+its+impact+on+bacterial+plaque+accumulation.+An+in+vitro+sem+study%5BTitle%5D)+AND+%22J+Int+Oral+Health%22%5BJournal%5D)">Surface topography of composite restorative materials following ultrasonic scaling and its impact on bacterial plaque accumulation. An in vitro sem study.</a> J Int Oral Health. 5 (3), 13-19 (2013).</li>
<li>Zissis, A. J., Polyzois, G. L., Yannikakis, S. A., Harrison, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Roughness+of+denture+materials%3A+A+comparative+study%5BTitle%5D)+AND+%22Int+J+Prosthodont%22%5BJournal%5D)">Roughness of denture materials: A comparative study.</a> Int J Prosthodont. 13 (2), 136-140 (2000).</li>
<li>Arabaci, T., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Influence+of+tip+wear+of+piezoelectric+ultrasonic+scalers+on+root+surface+roughness+at+different+working+parameters.+A+profilometric+and+atomic+force+microscopy+study%5BTitle%5D)+AND+%22Int+J+Dent+Hyg%22%5BJournal%5D)">Influence of tip wear of piezoelectric ultrasonic scalers on root surface roughness at different working parameters. A profilometric and atomic force microscopy study.</a> Int J Dent Hyg. 11 (1), 69-74 (2013).</li>
<li>Goldstein, R. E., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Microleakage+around+class+v+composite+restorations+after+ultrasonic+scaling+and+sonic+toothbrushing+around+their+margin%5BTitle%5D)+AND+%22J+Esthet+Restor+Dent%22%5BJournal%5D)">Microleakage around class v composite restorations after ultrasonic scaling and sonic toothbrushing around their margin.</a> J Esthet Restor Dent. 29 (1), 41-48 (2017).</li>
<li>Mittal, A., Nichani, A. S., Venugopal, R., Rajani, V. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((The+effect+of+various+ultrasonic+and+hand+instruments+on+the+root+surfaces+of+human+single+rooted+teeth%3A+A+planimetric+and+profilometric+study%5BTitle%5D)+AND+%22J+Indian+Soc+Periodontol%22%5BJournal%5D)">The effect of various ultrasonic and hand instruments on the root surfaces of human single rooted teeth: A planimetric and profilometric study.</a> J Indian Soc Periodontol. 18 (6), 710-717 (2014).</li>
<li>Babina, K., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((The+effect+of+ultrasonic+scaling+and+air-powder+polishing+on+the+roughness+of+the+enamel%2C+three+different+nanocomposites%2C+and+composite%2Fenamel+and+composite%2Fcementum+interfaces%5BTitle%5D)+AND+%22Nanomaterials+%28Basel%29%22%5BJournal%5D)">The effect of ultrasonic scaling and air-powder polishing on the roughness of the enamel, three different nanocomposites, and composite/enamel and composite/cementum interfaces.</a> Nanomaterials (Basel). 11 (11), (2021).</li>
<li>Demirci, F., Birgealp Erdem, M., Tekin, M., Caliskan, C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Effect+of+ultrasonic+scaling+and+air+polishing+on+the+surface+roughness+of+polyetheretherketone+%28peek%29+materials%5BTitle%5D)+AND+%22Am+J+Dent%22%5BJournal%5D)">Effect of ultrasonic scaling and air polishing on the surface roughness of polyetheretherketone (peek) materials.</a> Am J Dent. 35 (4), 200-204 (2022).</li>
<li>Erdilek, D., Sismanoglu, S., Gumustas, B., Efes, B. G. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Effects+of+ultrasonic+and+sonic+scaling+on+surfaces+of+tooth-colored+restorative+materials%3A+An+in+vitro+study%5BTitle%5D)+AND+%22Niger+J+Clin+Pract%22%5BJournal%5D)">Effects of ultrasonic and sonic scaling on surfaces of tooth-colored restorative materials: An in vitro study.</a> Niger J Clin Pract. 18 (4), 467-471 (2015).</li>
<li>Lai, Y. L., Lin, Y. C., Chang, C. S., Lee, S. Y. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Effects+of+sonic+and+ultrasonic+scaling+on+the+surface+roughness+of+tooth-colored+restorative+materials+for+cervical+lesions%5BTitle%5D)+AND+%22Oper+Dent%22%5BJournal%5D)">Effects of sonic and ultrasonic scaling on the surface roughness of tooth-colored restorative materials for cervical lesions.</a> Oper Dent. 32 (3), 273-278 (2007).</li>
<li>Mahiroglu, M. B., Kahramanoglu, E., Ay, M., Kuru, L., Agrali, O. B. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Comparison+of+root+surface+wear+and+roughness+resulted+from+different+ultrasonic+scalers+and+polishing+devices+applied+on+human+teeth%3A+An+in+vitro+study%5BTitle%5D)+AND+%22Healthcare+%28Basel%29%22%5BJournal%5D)">Comparison of root surface wear and roughness resulted from different ultrasonic scalers and polishing devices applied on human teeth: An in vitro study.</a> Healthcare (Basel). 8 (1), (2020).</li>
<li>Cadenaro, M., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Flowability+of+composites+is+no+guarantee+for+contraction+stress+reduction%5BTitle%5D)+AND+%22Dent+Mater%22%5BJournal%5D)">Flowability of composites is no guarantee for contraction stress reduction.</a> Dent Mater. 25 (5), 649-654 (2009).</li>
<li>Basheer, R. R., Hasanain, F. A., Abuelenain, D. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Evaluating+flexure+properties%2C+hardness%2C+roughness+and+microleakage+of+high-strength+injectable+dental+composite%3A+An+in+vitro+study%5BTitle%5D)+AND+%22BMC+Oral+Health%22%5BJournal%5D)">Evaluating flexure properties, hardness, roughness and microleakage of high-strength injectable dental composite: An in vitro study.</a> BMC Oral Health. 24 (1), 546(2024).</li>
<li>Brine, E. J., Marretta, S. M., Pijanowski, G. J., Siegel, A. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Comparison+of+the+effects+of+four+different+power+scalers+on+enamel+tooth+surface+in+the+dog%5BTitle%5D)+AND+%22J+Vet+Dent%22%5BJournal%5D)">Comparison of the effects of four different power scalers on enamel tooth surface in the dog.</a> J Vet Dent. 17 (1), 17-21 (2000).</li>
<li>Kuka, G. I., Kuru, B., Gursoy, H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((In+vitro+evaluation+of+the+different+supragingival+prophylaxis+tips+on+enamel+surfaces%5BTitle%5D)+AND+%22Photobiomodul+Photomed+Laser+Surg%22%5BJournal%5D)">In vitro evaluation of the different supragingival prophylaxis tips on enamel surfaces.</a> Photobiomodul Photomed Laser Surg. 41 (5), 212-217 (2023).</li>
<li>Parashar, A., Bhavsar, N. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Assessing+the+effect+of+piezoelectric+ultrasonic+scaler+tip+wear+on+root+surface+roughness+under+influence+of+various+working+parameters%3A+A+profilometric+and+atomic+force+microscopic+study%5BTitle%5D)+AND+%22J+Indian+Soc+Periodontol%22%5BJournal%5D)">Assessing the effect of piezoelectric ultrasonic scaler tip wear on root surface roughness under influence of various working parameters: A profilometric and atomic force microscopic study.</a> J Indian Soc Periodontol. 27 (6), 583-589 (2023).</li>
<li>Vengatachalapathi, H., Naik, R., Rao, R., Venugopal, R., Nichani, A. S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((The+effect+of+piezoelectric+ultrasonic+scaler+tip+wear+on+root+surface+roughness+at+different+working+parameters%3A+An+atomic+force+microscopic+and+profilometric+study%5BTitle%5D)+AND+%22J+Int+Acad+Periodontol%22%5BJournal%5D)">The effect of piezoelectric ultrasonic scaler tip wear on root surface roughness at different working parameters: An atomic force microscopic and profilometric study.</a> J Int Acad Periodontol. 19 (1), 15-21 (2017).</li>
<li>Casarin, R. C., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Root+surface+defect+produced+by+hand+instruments+and+ultrasonic+scaler+with+different+power+settings%3A+An+in+vitro+study%5BTitle%5D)+AND+%22Braz+Dent+J%22%5BJournal%5D)">Root surface defect produced by hand instruments and ultrasonic scaler with different power settings: An in vitro study.</a> Braz Dent J. 20 (1), 58-63 (2009).</li>
<li>International Organization for Standardization. Part 12: Sample preparation and reference materials in Biological evaluation of medical devices. <a target="_blank" href="http://scholar.google.com/scholar?hl=en&safe=off&q=%22ISO+10993-12%3A2021%22">ISO 10993-12:2021</a>. , (2021).</li>
<li>Sabatini, C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Color+stability+behavior+of+methacrylate-based+resin+composites+polymerized+with+light-emitting+diodes+and+quartz-tungsten-halogen%5BTitle%5D)+AND+%22Oper+Dent%22%5BJournal%5D)">Color stability behavior of methacrylate-based resin composites polymerized with light-emitting diodes and quartz-tungsten-halogen.</a> Oper Dent. 40 (3), 271-281 (2015).</li>
<li>Checchi, V., et al. Wear and roughness analysis of two highly filled flowable composites. <a target="_blank" href="http://scholar.google.com/scholar?hl=en&safe=off&q=author%3aChecchi%2C+V+%22Odontology%22">Odontology</a>. , (2024).</li>
<li>Poggio, C., Dagna, A., Chiesa, M., Colombo, M., Scribante, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Surface+roughness+of+flowable+resin+composites+eroded+by+acidic+and+alcoholic+drinks%5BTitle%5D)+AND+%22J+Conserv+Dent%22%5BJournal%5D)">Surface roughness of flowable resin composites eroded by acidic and alcoholic drinks.</a> J Conserv Dent. 15 (2), 137-140 (2012).</li>
<li>Tepe, H., Erdilek, A. D., Sahin, M., Efes, B. G., Yaman, B. C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Effect+of+different+polishing+systems+and+speeds+on+the+surface+roughness+of+resin+composites%5BTitle%5D)+AND+%22J+Conserv+Dent%22%5BJournal%5D)">Effect of different polishing systems and speeds on the surface roughness of resin composites.</a> J Conserv Dent. 26 (1), 36-41 (2023).</li>
<li>Busslinger, A., Lampe, K., Beuchat, M., Lehmann, B. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((A+comparative+in+vitro+study+of+a+magnetostrictive+and+a+piezoelectric+ultrasonic+scaling+instrument%5BTitle%5D)+AND+%22J+Clin+Periodontol%22%5BJournal%5D)">A comparative in vitro study of a magnetostrictive and a piezoelectric ultrasonic scaling instrument.</a> J Clin Periodontol. 28 (7), 642-649 (2001).</li>
<li>Flemmig, T. F., Petersilka, G. J., Mehl, A., Hickel, R., Klaiber, B. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Working+parameters+of+a+magnetostrictive+ultrasonic+scaler+influencing+root+substance+removal+in+vitro%5BTitle%5D)+AND+%22J+Periodontol%22%5BJournal%5D)">Working parameters of a magnetostrictive ultrasonic scaler influencing root substance removal in vitro.</a> J Periodontol. 69 (5), 547-553 (1998).</li>
<li>Singh, S., Uppoor, A., Nayak, D. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((A+comparative+evaluation+of+the+efficacy+of+manual%2C+magnetostrictive+and+piezoelectric+ultrasonic+instruments-an+in+vitro+profilometric+and+sem+study%5BTitle%5D)+AND+%22J+Appl+Oral+Sci%22%5BJournal%5D)">A comparative evaluation of the efficacy of manual, magnetostrictive and piezoelectric ultrasonic instruments-an in vitro profilometric and sem study.</a> J Appl Oral Sci. 20 (1), 21-26 (2012).</li>
<li>Yousefimanesh, H., Robati, M., Kadkhodazadeh, M., Molla, R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((A+comparison+of+magnetostrictive+and+piezoelectric+ultrasonic+scaling+devices%3A+An+in+vitro+study%5BTitle%5D)+AND+%22J+Periodontal+Implant+Sci%22%5BJournal%5D)">A comparison of magnetostrictive and piezoelectric ultrasonic scaling devices: An in vitro study.</a> J Periodontal Implant Sci. 42 (6), 243-247 (2012).</li>
<li>Flemmig, T. F., Petersilka, G. J., Mehl, A., Hickel, R., Klaiber, B. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((The+effect+of+working+parameters+on+root+substance+removal+using+a+piezoelectric+ultrasonic+scaler+in+vitro%5BTitle%5D)+AND+%22J+Clin+Periodontol%22%5BJournal%5D)">The effect of working parameters on root substance removal using a piezoelectric ultrasonic scaler in vitro.</a> J Clin Periodontol. 25 (2), 158-163 (1998).</li>
<li>Oliveira, G., Macedo, P. D., Tsurumaki, J. N., Sampaio, J. E., Marcantonio, R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((The+effect+of+the+angle+of+instrumentation+of+the+piezoelectric+ultrasonic+scaler+on+root+surfaces%5BTitle%5D)+AND+%22Int+J+Dent+Hyg%22%5BJournal%5D)">The effect of the angle of instrumentation of the piezoelectric ultrasonic scaler on root surfaces.</a> Int J Dent Hyg. 14 (3), 184-190 (2016).</li>
<li>Bergstrom, J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Photogrammetric+registration+of+dental+plaque+accumulation+in+vivo%5BTitle%5D)+AND+%22Acta+Odontol+Scand%22%5BJournal%5D)">Photogrammetric registration of dental plaque accumulation in vivo.</a> Acta Odontol Scand. 39 (5), 275-284 (1981).</li>
<li>Quirynen, M., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((The+influence+of+surface+free+energy+and+surface+roughness+on+early+plaque+formation.+An+in+vivo+study+in+man%5BTitle%5D)+AND+%22J+Clin+Periodontol%22%5BJournal%5D)">The influence of surface free energy and surface roughness on early plaque formation. An in vivo study in man.</a> J Clin Periodontol. 17 (3), 138-144 (1990).</li>
</ol>

<table><tbody><tr><td>Beautifil Flow Plus</td><td>Shofu</td><td></td><td>미국</td></tr><tr><td>Evo MA10 주사 전자 현미경</td><td>Zeiss</td><td></td><td>독일</td></tr><tr><td>EWO Typ 990 Paralellometer</td><td>Kavo</td><td></td><td>독일</td></tr><tr><td>마감 디스크</td><td>Bisco</td><td></td><td>미국</td></tr><tr><td>G4 스케일러 팁</td><td>딱따구리</td><td></td><td>중국</td></tr><tr><td>전제 Flowable</td><td>Kerr</td><td></td><td>미국</td></tr><tr><td>SC 7620 모델 스퍼터 코터</td><td>Quorum Technologies</td><td></td><td>영국</td></tr><tr><td>Surftest SJ-210</td><td>Mitutoyo</td><td></td><td>일본</td></tr><tr><td>UDS-A-LED 치과 스케일러</td><td>딱따구리</td><td></td><td>중국</td></tr><tr><td>Valo LED 무선 경화 라이트</td><td>Ultradent</td><td></td><td>미국</td></tr><tr><td>Zetaplus 실리콘 인상 재료</td><td>Zhermack</td><td></td><td>이탈리아</td></tr></tbody></table>

roughness impact of piezoelectric dental scaler on two distinct flowable composite filling materials

Roughness Impact of Piezoelectric Dental Scaler on Two Distinct Flowable Composite Filling Materials

통계 분석은 통계 분석 소프트웨어를 사용하여 수행되었습니다. 그룹 내의 변화를 평가하기 위해 Wilcoxon Signed Rank Test를 수행했습니다. Mann Whitney-U Test는 그룹 간 비교를 수행하기 위해 사용되었습니다. 유의 수준은 p &lt; 0.05에서 결정되었습니다.
두 그룹의 그룹 내 프로필로메트릭 비교에서, 스케일러 적용으로 인해 상당한 거칠기가 발생했으며, 이는 전자 현미경 이미지로 정성적으로 시각화할 수 있음에 주목했습니다(그룹 P, p = 0.005; 그룹 B, p = 0.007; 표 1). 집단 간 프로필로메트릭 비교에서, 시작 거칠기 수준이 유사한 것으로 결정된 두 복합 유형에 대한 스케일러 적용 후의 거칠기 변화를 분석한 결과(p=0.143)에서는 유의한 차이가 나타나지 않았다(p=0.684; 표 2).
치과 기구의 사용을 표준화하...

Dental ultrasonic scalers are commonly employed in periodontal treatment; however, their ability to roughen tooth surfaces is a worry since roughness may ...

roughness-impact-piezoelectric-dental-scaler-on-two-distinct-flowable

Research

연구

JoVE Journal

Behavior

행동

치과 수지 복합 수복물의 중합 수축 응력의 공간적 발전을 이해하기 위해서는, 디지털 이미지의 상관 관계는 중합 전후에 찍은 복구 이미지의 상관 관계를 복원 모델 유리 충치의 전체 필드 변위 / 변형 측정을 제공하는 데 사용되었다.

시뮬레이션 구멍 치과 복합의 수축은 디지털 이미지의 상관 관계로 측정

치과 복합 재료의 생체 적합성 연구의 대부분의 측면은 형광 신호의 정량화와 결합 된 세포 독성 3D CLSM 시간 경과 영상은 시간이 지남에 따라 세포의 운명의 민감한 평가할 수있다. 이 방법을 활용하여 치과 복합 재료의 cytocompatibility을 평가하는 효율적인 도구가 될 수 있습니다.

치과 복합 재료의 Cytocompatibility 평가하기위한 효율적인 방법으로 공 촛점 시간 경과 영상

여기, 선물이 세균성 세포 생존 및 형태학 상 특성의 분석을 포함 하 여 치과 보 철물 abutments에 대 한 티타늄 및 지 르 코니 아 재료에 구두 biofilm 형성 평가 하는 프로토콜. 현장에서 모델 관련 강력한 현미경 검사 법 기술 된 구두 biofilm 분석에 사용 됩니다.

치과 임 플 란 트에 대 한 다른 자료에 구두 Biofilm 형성

고정되지 않은 스테인리스강 볼을 사용한 준정적 하중-파괴 시험은 최소 침습적 후방 컴퓨터 지원 설계 및 상아질 아날로그 재료에 접합된 제조 수복물의 파괴 강도를 결정하기 위해 개발되었습니다. 이 테스트는 치과 수복물의 골절을 담당하는 일반적인 하중 체제를 모델링합니다.

CAD(Computer-Aided Design) 및 제조 교합 베니어판을 밀링된 상아질 아날로그 재료에 접합하기 위한 준정적 기계 테스트

여기에서는 소아 치과 내에서 전방 수복물에 사용되는 콤포머 및 복합 수지 수복물의 색상 안정성에 대한 다양한 연마 방법의 영향을 평가했습니다. 이 연구는 소아 치과 진료에서 콤포머 및 복합 레진 수복물의 색상 안정성을 향상시키기 위해 적절한 연마 방법을 선택하는 것의 중요성을 강조합니다.

소아 치과에서 치과 수복물의 색상 안정성에 대한 다양한 연마 방법의 효과 평가

본 프로토콜은 임상적 의사 결정에 기여하기 위해 체외 임플란트 표면 오염 제거 및 거칠기 연구에 사용할 수 있는 잉크 염색을 기반으로 하는 실험 모델을 설명합니다.

임플란트 주위염 치료에 사용되는 기계적 방법이 임플란트 표면 오염 제거 및 거칠기에 미치는 영향

이 기사에서는 다양한 제조 방법(열처리 PMMA, CAD-CAM 밀링 PMMA 및 3D 프린팅 수지) 및 연마 기술(600, 800 및 1000 그릿 실리콘 카바이드 연마지)이 완전한 의치에 사용되는 수지 기본 재료의 표면 거칠기(Ra)에 미치는 영향을 평가하기 위한 프로토콜을 제시합니다.

Impact of Fabrication Techniques and Polishing Procedures on Surface Roughness of Denture Base Resins(의치 베이스 수지의 표면 거칠기에 대한 제작 기술 및 연마 절차의 영향)

이 프로토콜은 표면 처리 프로토콜, 루팅 시멘트 선택, 열순환이 PEEK와 간접 복합 수지 간 전단 결합 강도에 미치는 영향을 평가하는 것을 목표로 합니다.

표면 처리, 루팅 시멘트, 열순환이 PEEK–복합 결합 강도에 미치는 영향을 평가하는 표준화 프로토콜

여기에서 우리는 가상 현실 환경에서 동작하는 동안 마우스 피질의 두 광자 영상에 포함 된 실험 절차에 대해 설명합니다.

가상 현실 환경을 탐색 마우스의 두 광자 칼슘 이미징

이 실험 패러다임이 진짜 범죄에 목격자가 메모리에서 범인의 전체적인 얼굴 합성을 만든 다음 범죄자 또는 그 또는 그녀가하는 일을 포함하는 비디오 라인업에서 범인을 식별하기 위해 시도 할 수있는 상황을 복제 적용 현재가 아닌.

전체적 얼굴 복합 작성 및 후속 비디오 라인업 목격자 식별 패러다임

학습하세요 압전식 초음파 스케일러가 두 종류의 유동성 복합 충전 재료 표면 거칠기에 미치는 영향을 평가하는 방법을. 이 연구는 임상에서 복합 수복물 주변의 세심한 스케일링 기술의 필요성을 강조합니다.

Roughness Impact of Piezoelectric Dental Scaler on Two Distinct Flowable Composite Filling Materials