Name: Nanofabricage van Gate-gedefinieerde GaAs / AlGaAs Lateral Quantum Dots (Video) | JoVE Journal
Uploaded: 2013-11-01T19:15:00.000+00:00
Duration: 15 min 47 s
Description: Leer nanofabricage van gate-gedefinieerde laterale kwantumdots op GaAs/AlGaAs-heterostructuren voor kwantuminformatieverwerking. Dit protocol omvat mesa-etsen, ohmische contacten en elektronenbundellithografie.

ai_agent_IP

ai_agent

maintenance

instantTrialDurationMinutes

isBiopharma

enableNewMyJoveSectionDesign

educationFeatures

seoMetaApi

ai_copilot_institution_blacklist

ai_chat_institution_blacklist

freeAccessWindow

ssoRoleCapture

scheduledMaintenanceBanner

joveLabsFeatures

disable_autoplay_for_bots

extended_trial_duration

5 minutes

De auteurs danken Michael Lacerte voor technische ondersteuning. MP-L. erkent het Canadese Institute for Advanced Research (CIFAR), de Natuurwetenschappen en Engineering Research Council of Canada (NSERC), de Canadese Stichting voor Innovatie (CFI) en het Fonds de Recherche Quebec - Nature et Technologies (FRQNT) voor financiële steun. Het apparaat hier gepresenteerd werd gefabriceerd op CRN2 en IMDQ faciliteiten, deels gefinancierd door NanoQuébec. Het GaAs / AlGaAs substraat werd gefabriceerd door ZR Wasilewski van het Instituut voor Microstructuurbeheersing Wetenschappen aan de National Research Council Canada. JCL en CB-O. erkennen CRSNG en FRQNT voor financiële steun.

De vervaardigingswerkwijze volgens deze methode wordt gedaan op een GaAs / AlGaAs-substraat met afmetingen van 1,04 x 1,04 cm. Twintig identieke apparaten worden gefabriceerd op een substraat van deze omvang. Alle stappen van het proces worden gedaan in een cleanroom en geschikte beschermende kleding moeten te allen tijde worden gebruikt. Gedeïoniseerd water wordt gebruikt in de werkwijze, maar wordt eenvoudigweg aangeduid als &quot;water&quot; in het onderstaande protocol. 1. Etsen van de Mesa Het resultaat van deze fabricagestap wordt getoond in figuur 4a. <ol><li> Plaats het monster in een plasma asjer met een O 2 plasma bij 75 W gedurende 2 minuten om alle sporen van ongewenste weerstaan ​​of organische verbindingen te verwijderen. </li><li> Reinig het monster in een sonische bad met aceton (2x) en IPA voor elke 5 minuten. Föhnen met een samengeperste N2 pistool. Gedurende de fabricage-protocol, bij gebruik van een sonische bad, vermijd het gebruik van hoge vermogens beschadiging van de GaAs-wafer te voorkomeneen neiging tot splijten is. </li><li> Bak het monster in een oven bij 125 ° C gedurende ten minste 15 minuten aan het oppervlak drogen. Uitdroging kan ook worden bereikt door het monster op een hete plaat bij 180 ° C gedurende ten minste 5 minuten. </li><li> Spin jas het monster met fotolak Shipley S1818 bij 3.500 rpm gedurende 30 seconden en bakken op een hete plaat bij 115 ° C gedurende 60 sec. De resulterende laag weerstaan ​​moet ongeveer 2,5 micrometer dik. S1818 wordt gebruikt omdat het dik en zeer weinig beïnvloed door de oplossing in stap 1.11 etsen van de ondergrond. Gedurende het fabricageproces, is het belangrijk te voorkomen moffelen fotoresist en e-beam weerstaan ​​eenvoudig verwijderen door opeenvolgende fasen te verzekeren. </li><li> Gebruik een fotolithografische masker aligner en een rand kraal masker om bloot het weerstaan ​​aan de buitenrand van het monster. De verdikte masker uit een 1 x 1 cm vierkant chroom op een glazen plaat. Gebruik licht met een golflengte van 436 nm en blootstellen weerstaan ​​10 sec bij 15 m W / cm 2. Het wavelength en macht zijn vast en kunnen variëren afhankelijk van de gebruikte machine. Pas de belichting en ontwikkeling keer op goed gedefinieerde eigenschappen van de juiste grootte te verkrijgen. </li><li> Ontwikkelen blootgesteld weerstaan ​​door onderdompeling van het monster in MF-319 gedurende 2 min. 10 sec. Schud langzaam tijdens deze stap. Spoelen in water gedurende 15 seconden en droog te blazen met een samengeperste N2 pistool. De verdikte worden verwijderd aan het einde van deze stap, waardoor een 1 x 1 cm oppervlak met een uniforme dikte van weerstand in het midden van het monster. De verdikte wordt verwijderd voordat het blootstellen van de mesa masker die het contact tussen het masker en het monster, wat leidt tot betere resultaten. </li><li> Nog steeds met behulp van de fotolithografische masker aligner, bloot het weerstaan ​​met behulp van de mesa masker en 436 nm licht voor 7 sec bij 15 mW / cm 2. </li><li> Ontwikkelen van de blootgestelde weerstaan ​​door onderdompeling van het monster in MF-319 gedurende 2 min 10 sec en langzaam roeren. Spoel gedurende 15 seconden in water en droog te blazen met een samengeperste N2 pistool. De weerstaan ​​remaining op het monster heeft nu de vorm van de mesa. De weerstaan ​​deze regio van het monster te beschermen tegen weggeëtst in de stappen die volgen. </li><li> Om alle sporen van weerstand in de eerder blootgestelde gebied te verwijderen, wordt het monster geplaatst in een plasma Asher en wordt blootgesteld aan een O2 plasma gedurende 1 min bij 75 W. </li><li> Een oplossing van H 2 SO 4: H 2 O 2: H2 O (5:01:55) wordt gebruikt voor het etsen van het monster. Combineer de juiste verhoudingen van H 2 O 2 en water en voeg vervolgens de H 2 SO 4. Deze oplossing is zeer reactief wanneer het eerst bereid. Wacht 20 minuten voordat u verder gaat met de volgende stap om overetching voorkomen. </li><li> Ets het monster door onderdompeling in de zure oplossing gedurende enkele seconden en onmiddellijk spoelen met water gedurende 30 seconden om de reactie te stoppen. Het oppervlak van het monster moet worden geëtst langs de laag van Si doteermiddelen en bijna helemaal naar beneden om de 2DEG tot uitputting zorgen in deze regio&#39;s (see Figure 1). De etsdiepte is afhankelijk van de ondergrond. Algemeen voor het type substraat, een 34 sec onderdompeling tot de gewenste etsdiepte van 90-100 nm. Het is echter belangrijk om de 2DEG overetch beschadiging te voorkomen. Aangezien de etssnelheid sterk varieert met de verhouding van H 2 SO 4 en H 2 O 2 in de oplossing en de wachttijd voor het etsen, wordt het aanbevolen om het etsen uit te voeren door meerdere onderdompelingen van 5-10 sec plaats van een enkele 34 sec etsen, en meet de geëtste diepte met een profilometer na elke ets. De relatief langzame etssnelheid van deze oplossing maakt een goede beheersing van de etsdiepte. Het koelen van de etsoplossing onder kamertemperatuur kan leiden tot etsen lagere tarieven. Aangezien het een ondiep etsen en etsen profiel onbelangrijk verschillende ets oplossingen kunnen ook worden gebruikt. </li><li> Strip de resist door onderdompeling van het monster in 1165 verwijderaar bij 65 ° C gedurende 3 uur. Spoelenin aceton en IPA voor 5 min elk. Meet de etsen profiel met een profilometer. </li></ol> 2. Fabricage van de ohmse contacten Het resultaat van deze fabricagestap wordt getoond in figuur 4b. <ol><li> Maak het monster in een sonisch bad door onderdompeling in aceton (2x) en IPA voor elke 5 minuten. Föhnen met een samengeperste N2 pistool. </li><li> Bak het monster in een oven bij 125 ° C gedurende 15 minuten aan het oppervlak drogen. </li><li> Spin jas met LOR5A bij 2500 rpm gedurende 30 seconden en bakken op een hete plaat bij 150 ° C gedurende 10 minuten. Vervolgens draaien jas met S1813 bij 5000 rpm gedurende 30 seconden en bakken op een hete plaat bij 110 ° C gedurende 60 sec. De resulterende dikte van de resist is ~ 600 nm tot ~ 1,3 urn respectievelijk. Twee lagen van weerstand worden gebruikt om de lift-off van het metaal dat wordt afgezet in stap 2.10 vergemakkelijken. </li><li> Met behulp van een fotolithografische masker aligner en de rand kraal masker, bloot het weerstaan ​​aan de buitenzijde edge van het monster met 436 nm licht voor 10 sec bij 15 mW / cm 2. </li><li> Ontwikkelen van de blootgestelde weerstaan ​​door onderdompeling van het monster in MF-319 gedurende 2 min 10 sec roeren soepel. Spoelen in water gedurende 15 seconden en droog te blazen met een samengeperste N2 pistool. </li><li> Nog steeds met behulp van de fotolithografische masker aligner, maar dit keer met de ohmse contact masker, lijnt u de patronen voor de ohmse contacten op de geëtste mesa. Bloot met 436 nm licht voor 6 sec bij 15 mW / cm 2. </li><li> Ontwikkel de resist in MF-319 gedurende 2 min 10 sec roeren soepel. Spoelen in water gedurende 15 seconden en droog te blazen met een samengeperste N2 pistool. Er is niet langer weerstaan ​​in de gebieden waar de ohmse contacten worden gestort. De ontwikkelaar lost de LOR 5A sneller dan de S1813, waardoor een ondersnijding onder de toplaag weerstaan. Dit profiel in de lak voorkomt metaal (die worden gestort in stap 2.10) van vormen wanden aan de randen van de resist en zal tevens gemakkelijk removal van de resterende weerstaan ​​en ongewenste metal. </li><li> Om alle sporen van weerstand te bieden in de eerder blootgestelde gebied te verwijderen, plaatst u het monster in een plasma Asher en het blootstellen aan een O 2 plasma gedurende 1 minuut bij 75 W. Het is belangrijk niet te laten de steekproef zitten te lang in het plasma omdat ongeveer 75 nm / min of resist geëtst tijdens deze stap. </li><li> Verwijder de GaAs natuurlijke oxidelaag door onderdompeling van het monster in een oplossing van H 2 SO 4: H2 O (01:05) gedurende 30 seconden en spoelen met water gedurende 30 sec. Föhnen met een samengeperste N2 pistool. Stap 2.10 moeten zo snel mogelijk naar de natuurlijke oxidelaag van reappearing voorkomen worden uitgevoerd. </li><li> Gebruik een e-beam verdamper tot 25 nm van Ni, 55 nm van Ge en 80 nm van Au deponeren. De deposities zijn respectievelijk 0,2 nm / sec, 0,5 nm / sec en 0,5 nm / sec. De depositie zodanig gekozen dat het indampen tijd kort genoeg om te voorkomen verwarmen van de kamer zonder zo kort om de precisie van de dikte t verliezenhij afgezette laag. De dubbellaag van Ge en Au kan worden vervangen door een enkele laag eutectische Geau indien beschikbaar 9. </li><li> De vorige stap afgezet metaal op het gehele oppervlak van het monster. Verwijdering van het metaal dat wordt afgezet op de resist wordt uitgevoerd door oplossen van de laatstgenoemde. Om dit te doen, dompel de steekproef in 1165 Remover bij 65 ° C gedurende 3 uur. Om ongewenste metalen die niet op zijn eigen kan zijn opgeheven verwijderen gebruikt u een pipet om licht bevochtigen van het oppervlak van het monster met warme remover. In aceton en IPA voor elke 5 min. Spoel de steekproef. </li><li> Een snel thermisch gloeien proces vormend gas wordt gebruikt om het afgezette metaal diffunderen naar de 2DEG van het monster. De temperatuur wordt verhoogd met een snelheid van 50 ° C / seconde tot een temperatuur van 415 ° C wordt bereikt. Het monster blijft bij deze temperatuur gedurende 20 seconden en vervolgens snel afgekoeld. De duur en de temperatuur van het uitgloeien worden gekozen om de kleinste weerstand krijgen via de ohmse contacten bij lagetemperatuur. De optimale tijd gloeien kan variëren afhankelijk van de diepte van de 2DEG in het substraat. </li></ol> 3. Fabricage van de Ti / Au Schottky Leads Het resultaat van deze fabricagestap wordt getoond in figuur 4c. <ol><li> Maak het monster in een sonisch bad door onderdompeling in aceton (2x) en IPA voor elke 5 minuten. Föhnen met een samengeperste N2 pistool. </li><li> Bak het monster in een oven bij 125 ° C gedurende 15 minuten aan het oppervlak drogen. </li><li> Spin jas PMMALMW4% op 5000rpm gedurende 30 seconden en bakken op een hete plaat bij 180 ° C gedurende 90 sec. Vervolgens draaien laag PMMA HMW 2% bij 5000 rpm gedurende 30 seconden en bakken op een hete plaat bij 180 ° C gedurende 90 sec. De resulterende dikte van de resist zijn ~ ~ 75 nm en 40 nm respectievelijk. Aangezien de Ti / Au leads zeer dun, kan een enkele laag van PMMA worden gebruikt, maar parameters spinnen, belichting en ontwikkeling moeten worden aangepast op basis. Deze opmerking geldt ook voor tHij Al leads en poorten (stap 4). </li><li> E lichtstralen: Dit deel van het proces is sterk afhankelijk van de gebruikte en protocol nodig kunnen dus sterk afwijken van de hieronder beschreven apparatuur. De patronen voor de leads worden getekend in een CAD-bestand. In dit bestand moet de draden worden getrokken als gesloten polygonen die 2 micrometer breed. De draden zijn nodig om contact bonding pads (vervaardigd in stap 5) aan de Al poorten (vervaardigd in stap 4). Vier uitrichtkenmerken moet worden blootgesteld om de verticale, horizontale en uitlijning in draairichting van de Al leads en poorten op de Ti / Au Schottky leidt. <ol><li> Het monster wordt in een Scanning Electron Microscope (SEM) die is uitgerust om e-beam lithografie doen. Gebruik een diafragma van 10 um tot de bundelvlekgrootte verminderen en zet de versnelling spanning tot 10 kV tot een goed contrast tijdens de uitlijning van de eerder gefabriceerde structuren zorgen. Pas de scherpstelling, stigmatism, en het diafragma uitlijning.Meet de straalstroom met een Faraday cup. </li><li> Lijn de balk met de eerder geëtst mesa en zet de vergroting op 300X. </li><li> Expose de leads. De SEM geprogrammeerd om het gewenste gebieden blootgesteld door ze te vullen met een array van blootgestelde punten. De afstand tussen deze punten (hart-op-hart afstand) is 5,5 nm en de dosis is 43 uC / cm 2 (de belichtingstijd zal afhangen van de straalstroom gemeten in stap 3.5.1). Bloot uitlijntekens alsook om de uitlijning van de Al poorten toe met de Ti / Au leads in stap 4. </li><li> Herhaal de stappen 3.5.2 en 3.5.3 voor elk van de 20 apparaten op het monster. </li></ol></li><li> Ontwikkel de resist door onderdompeling van het monster in IPA: H2O (9:1) gedurende 30 sec. De oplossing moet bij een temperatuur van 20 ° C. Spoelen in water gedurende 30 seconden en droog te blazen met een samengeperste N2 pistool. Indien gewenst, de PMMA resist kan worden ontwikkeld met behulp van een IPA: MIBK-oplossing en spoelen in RIE om de reactie te stoppen. Een ander development tijd zal nodig zijn als deze optie wordt gekozen. </li><li> Het monster wordt in een plasma Asher en blootgesteld aan een O2 plasma gedurende 4 seconden bij 50 W. Dit verwijdert 5 nm van weerstand en zorgt ervoor dat er geen weerstand links onder van de geulen gevormd tijdens de e-lichtstralen. </li><li> Verwijder de GaAs natuurlijke oxidelaag door onderdompeling van het monster in een oplossing van H 2 SO 4: H2 O (01:05) gedurende 30 seconden en spoelen met water gedurende 30 sec. Föhnen met een samengeperste N2 pistool. Stap 3.8 moet zo snel mogelijk om de natuurlijke oxidelaag van reappearing voorkomen worden uitgevoerd. </li><li> Plaats het monster in een e-beam verdamper en aanbetaling van 10 nm van Ti en 20 nm van Au, beide met een snelheid van 0.1 nm / sec. Het is belangrijk dat de monsterhouder goed geaard en zich ten minste 60 cm van de bron tot kosten kan ophopen op het monster tijdens het depositieproces. </li><li> Lift-off overtollige metalen door onderdompeling van de steekproef in 1165 Remover bij 65 °C gedurende 15 minuten. Om ongewenste metalen die niet op zijn eigen kan zijn opgeheven verwijderen gebruikt u een pipet om licht bevochtigen van het oppervlak van het monster met warme remover. Spoelen in aceton en IPA voor elke 5 minuten. </li></ol> 4. Fabricage van de Al Schottky Leads en Gates Het resultaat van deze fabricagestap wordt getoond in figuur 4d. De fabricage van de Al Schottky leidt en poorten vormen de meest kritische stap van het fabricageproces omdat deze de poorten die de stip definiëren. Het is belangrijk dat de elektronenbundel goed gericht en de bundelstroom goed aangepast in stap 4.2. De belichting en ontwikkeling tijden moet goed worden aangepast aan kleine, continue en goed gedefinieerde poorten vinden. In veel protocollen, zijn deze poorten en leidt gefabriceerd in Ti / Au en worden gelijktijdig blootgesteld, met de vorige leads tijdens stap 3. Echter, een voordeel van het gebruik Al is dat het kan worden geoxideerd, thereferts waardoor elementen onderwerp poorten rechtstreeks op het oppervlak van het monster worden afgezet zonder dat er een grote isolerende laag 10. <ol><li> Herhaal de stappen 3.1 tot en met 3.4.2. Echter, gebruik dan niet de sonische bad tijdens het schoonmaken van het monster schade aan de Ti / Au leads te voorkomen. </li><li> E-beam-proces: De patronen voor de Al leads en poorten zijn getekend in een CAD-bestand. De Al leads worden gebruikt om contact Ti / Au tot de Al poorten en getekend als gesloten veelhoeken met een breedte van 200 nm. Al de poorten zijn echter niet getekend als veelhoeken, maar als twee enkele lijnen gescheiden door 20 nm. <ol><li> Zodra de balk is afgestemd op de mesa, stellen de vergroting tot 1.500 X en lijn de balk met de Ti / Au Schottky leidt. </li><li> Expose de leads. Met een dosis van 43 uC / cm 2 en een hart-op-hart afstand van 3,3 nm. </li><li> Expose de poorten. Gebruik een lijn dosis van 0.149 nC / cm en een hart-op-hart afstand van 1,1 nm. Dit zal leiden tot eenlaatste poort breedte van 60 nm. </li><li> Herhaal de stappen 4.2.1 - 4.2.3 voor elk van de 20 apparaten op het monster. </li></ol></li><li> Herhaal de stappen 3,5-3,7. </li><li> Plaats het monster in een e-beam verdamper en aanbetaling van 30 nm van Al bij een snelheid van 0,3 nm / sec. </li><li> Herhaal stap 3.10. Belangrijk is zeer delicaat zijn met het monster van deze stap verder beschadiging van de kleine Al poorten vermijden. </li></ol> 5. Fabricage van de Schottky Leads en verlijming Pads Het resultaat van deze fabricagestap wordt getoond in figuur 4e. <ol><li> Herhaal stappen 2,1-2,9, met een fotolithografisch masker voor de Schottky leidt in plaats van het masker voor de ohmse pads. </li><li> Plaats het monster in een e-beam verdamper en aanbetaling van 30 nm van Ti en 350 nm van Au bij snelheden van 0,3 nm / sec en 1 nm / sec resp. De dikke laag afgezette Au vergemakkelijkt binding van het monster naar de monsterhouder omdat het minder gevoelig voor scheuren dan thinner lagen. </li><li> Loskomen de overmaat metaal en resterende weerstaan ​​door onderdompeling van het monster in 1165 verwijderaar bij 65 ° C gedurende 3 uur. Om ongewenste metalen die niet op zijn eigen kan zijn opgeheven verwijderen gebruikt u een pipet om licht bevochtigen van het oppervlak van het monster met warme remover. In aceton en IPA voor elke 5 min. Spoel de steekproef. </li></ol> 6. Blokjes snijden van de monsters <ol><li> Bak het monster in een oven bij 125 ° C gedurende 15 minuten aan het oppervlak drogen. </li><li> Spin jas met S1818 bij 3.500 rpm gedurende 30 seconden en bakken op een hete plaat bij 115 ° C gedurende 1 minuut. De dikte van deze laag resist onbelangrijk zolang deze dik genoeg is om het oppervlak van het monster te beschermen tijdens blokjes. </li><li> Leg een laag dobbelstenen snijden tape op de boven-en ondervlakken van het monster. De laag tape op het bovenvlak biedt een extra bescherming moeten tijdens blokjes. </li><li> Plaats het monster face-up in een snijmachine. Snijd het monster in afzonderlijke apparaten met blokjeshelemaal door toplaag van dobbelstenen snijden tape en de GaAs / AlGaAs wafel zonder te snijden door de onderste laag van blokjes tape. </li><li> Verwijder de blokjes tape en de beschermende weerstand door het plaatsen van het monster in aceton gedurende een paar minuten. Gebruik een pincet om voorzichtig af te trekken stukjes blokjes tape die niet op te heffen op hun eigen. Spoel de apparaten in het IPA en föhnen met behulp van een N 2 pistool. </li></ol>

<ol><li>Shor, P. W. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Polynomial-time+algorithms+for+prime+factorization+and+discrete+logarithms+on+a+quantum+computer%5BTitle%5D)+AND+%22SIAM+J.+Sci.+Comput%22%5BJournal%5D)">Polynomial-time algorithms for prime factorization and discrete logarithms on a quantum computer.</a> SIAM J. Sci. Comput. 26 (5), 1484-1509 (1997).</li>
<li>Björk, M. T., Thelander, C., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Few-Electron+Quantum+Dots+in+Nanowires%5BTitle%5D)+AND+%22Nano+Lett%22%5BJournal%5D)">Few-Electron Quantum Dots in Nanowires.</a> Nano Lett. 4 (9), 1621-1625 (2004).</li>
<li>Dekker, C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Carbon+Nanotubes+as+Molecular+Quantum+Wires%5BTitle%5D)+AND+%22Phys.+Today%22%5BJournal%5D)">Carbon Nanotubes as Molecular Quantum Wires.</a> Phys. Today. 52 (5), 22-28 (1999).</li>
<li>Klein, D. L., McEuen, P. L., Bown Katari, J. E., Roth, R., Alivisatos, A. P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((An+Approach+to+Electrical+Studies+of+Single+Nanocrystals%5BTitle%5D)+AND+%22Appl.+Phys.+Lett%22%5BJournal%5D)">An Approach to Electrical Studies of Single Nanocrystals.</a> Appl. Phys. Lett. 68 (18), 2574-2576 (1996).</li>
<li>Kouwenhoven, L. P., Oosterkamp, T. H., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Excitation+Spectra+in+Circular+Few-Electron+Quantum+Dots%5BTitle%5D)+AND+%22Science%22%5BJournal%5D)">Excitation Spectra in Circular Few-Electron Quantum Dots.</a> Science. 278 (5344), 1788-1792 (1997).</li>
<li>Ciorga, M., Sachrajda, A. S. Z., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Addition+Spectrum+of+a+Lateral+Dot+from+Coulomb+and+Spin-Blockade+Spectroscopy%5BTitle%5D)+AND+%22Phys.+Rev.+B%22%5BJournal%5D)">Addition Spectrum of a Lateral Dot from Coulomb and Spin-Blockade Spectroscopy.</a> Phys. Rev. B. 61 (24), R16315-R16318 (2000).</li>
<li>Baca, A. G., Ashby, C. I. H. <a target="_blank" href="http://scholar.google.com/scholar?hl=en&safe=off&q=author%3aBaca%2C+AG+%22Fabrication+of+GaAs+Devices%22">Fabrication of GaAs Devices</a>. , The Institute of Electrical Engineers. London, United Kingdom. 350(2005).</li>
<li>Barthel, C., Reilly, D. J., Marcus, C. M., Hanson, M. P., Gossard, A. C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Rapid+Single-Shot+Measurement+of+a+Singlet-Triplet+Qubit%5BTitle%5D)+AND+%22Phys.+Rev.+Lett%22%5BJournal%5D)">Rapid Single-Shot Measurement of a Singlet-Triplet Qubit.</a> Phys. Rev. Lett. 103 (16), 160503(2009).</li>
<li>S, <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((A+Survey+of+Ohmic+Contacts+to+III-V+Compound+Semiconductors%5BTitle%5D)+AND+%22Thin+Solid+Films%22%5BJournal%5D)">A Survey of Ohmic Contacts to III-V Compound Semiconductors.</a> Thin Solid Films. 308 (0), 599-606 (1997).</li>
<li>Lim, W. H., Huebl, H., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Electrostatically+Defined+Few-Electron+Double+Quantum+Dot+in+Silicon%5BTitle%5D)+AND+%22Appl.+Phys.+Lett%22%5BJournal%5D)">Electrostatically Defined Few-Electron Double Quantum Dot in Silicon.</a> Appl. Phys. Lett. 94 (17), 173502(2009).</li>
<li>Elzerman, J. M., Hanson, R., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Few-Electron+Quantum+Dot+Circuit+with+Integrated+Charge+Read+Out%5BTitle%5D)+AND+%22Phys.+Rev.+B%22%5BJournal%5D)">Few-Electron Quantum Dot Circuit with Integrated Charge Read Out.</a> Phys. Rev. B. 67 (16), 161308(2003).</li>
<li>Johnson, A. C., Petta, J. R., Marcus, C. M., Hanson, M. P., Gossard, A. C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Singlet-Triplet+Spin+Blockade+and+Charge+Sensing+in+a+Few-Electron+Double+Quantum+Dot%5BTitle%5D)+AND+%22Phys.+Rev.+B%22%5BJournal%5D)">Singlet-Triplet Spin Blockade and Charge Sensing in a Few-Electron Double Quantum Dot.</a> Phys. Rev. B. 72 (16), 165308(2005).</li>
<li>Hanson, R., Kouwenhoven, L. P., Petta, J. R., Tarucha, S., Vandersypen, L. M. K. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Spins+in+Few-Electron+Quantum+Dots%5BTitle%5D)+AND+%22Rev.+Mod.+Phys%22%5BJournal%5D)">Spins in Few-Electron Quantum Dots.</a> Rev. Mod. Phys. 79 (4), 1217-1265 (2007).</li>
<li>Long, A. R., Pioro-Ladrière, M., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((The+Origin+of+Switching+Noise+in+GaAs%2FAlGaAs+Lateral+Gated+Devices%5BTitle%5D)+AND+%22Physica+E+Low+Dimens.+Syst.+Nanostruct%22%5BJournal%5D)">The Origin of Switching Noise in GaAs/AlGaAs Lateral Gated Devices.</a> Physica E Low Dimens. Syst. Nanostruct. 34 (1-2), 553-556 (2006).</li>
<li>Koppens, F. H. L., Buizert, C., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Driven+Coherent+Oscillations+of+a+Single+Electron+Spin+in+a+Quantum+Dot%5BTitle%5D)+AND+%22Nature%22%5BJournal%5D)">Driven Coherent Oscillations of a Single Electron Spin in a Quantum Dot.</a> Nature. 442 (7104), 766-771 (2006).</li>
<li>Foletti, S., Bluhm, H., Mahalu, D., Umansky, V., Yakobi, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Universal+Quantum+Control+of+Two-Electron+Spin+Quantum+Bits+Using+Dynamic+Nuclear+Polarization%5BTitle%5D)+AND+%22Nat.+Phys%22%5BJournal%5D)">Universal Quantum Control of Two-Electron Spin Quantum Bits Using Dynamic Nuclear Polarization.</a> Nat. Phys. 5 (12), 903-908 (2009).</li>
<li>Petta, J. R., Lu, H., Gossard, A. C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((A+Coherent+Beam+Splitter+for+Electronic+Spin+States%5BTitle%5D)+AND+%22Science%22%5BJournal%5D)">A Coherent Beam Splitter for Electronic Spin States.</a> Science. 327 (5966), 669-672 (2010).</li>
<li>Shulman, M. D., Dial, O. E., Harvey, S. P., Bluhm, H., Umansky, V., Yacoby, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Demonstration+of+Entanglement+of+Electrostatically+Coupled+Singlet-Triplet+Qubits%5BTitle%5D)+AND+%22Science%22%5BJournal%5D)">Demonstration of Entanglement of Electrostatically Coupled Singlet-Triplet Qubits.</a> Science. 336 (6078), 202-205 (2012).</li>
<li>Khaetskii, A. V., Loss, D., Glazman, L. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Electron+Spin+Decoherence+in+Quantum+Dots+Due+to+Interaction+with+Nuclei%5BTitle%5D)+AND+%22Phys.+Rev.+Lett%22%5BJournal%5D)">Electron Spin Decoherence in Quantum Dots Due to Interaction with Nuclei.</a> Phys. Rev. Lett. 88 (18), 186802(2002).</li>
<li>Sakr, M. R., Jiang, H. W., Yablonovitch, E., Croke, E. T. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Fabrication+and+characterization+of+electrostatic+Si%2FSiGe+Quantum+Dots+with+an+Integrated+Read-Out+Channel%5BTitle%5D)+AND+%22Appl.+Phys.+Lett%22%5BJournal%5D)">Fabrication and characterization of electrostatic Si/SiGe Quantum Dots with an Integrated Read-Out Channel.</a> Appl. Phys. Lett. 87 (22), 223104(2005).</li>
<li>Liu, X. L., Hug, D., Vandersypen, L. M. K. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Gate-Defined+Graphene+Double+Quantum+Dot+and+Excited+State+Spectroscopy%5BTitle%5D)+AND+%22Nano+Lett%22%5BJournal%5D)">Gate-Defined Graphene Double Quantum Dot and Excited State Spectroscopy.</a> Nano Lett. 10 (5), 1623-1627 (2010).</li>
<li>Frey, T., Leek, P. J., Beck, M., Blais, A., Ihn, T., Ensslin, K., Wallraff, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Dipole+Coupling+of+a+Double+Quantum+Dot+to+a+Microwave+Resonator%5BTitle%5D)+AND+%22Phys.+Rev.+Lett%22%5BJournal%5D)">Dipole Coupling of a Double Quantum Dot to a Microwave Resonator.</a> Phys. Rev. Lett. 108, 046807(2012).</li>
<li>Pioro-Ladrière, M., Tokyra, Y., Obata, T., Kubo, T., Tarucha, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Micromagnets+for+coherent+control+of+spin-charge+qubit+in+lateral+quantum+dots%5BTitle%5D)+AND+%22Appl.+Phys.+Lett%22%5BJournal%5D)">Micromagnets for coherent control of spin-charge qubit in lateral quantum dots.</a> Appl. Phys. Lett. 90 (2), 024105(2007).</li>
</ol>

Auteurs hebben niets te onthullen.

De hierboven gepresenteerde beschrijft de fabricage-protocol van een dubbele quantum dot in staat om de paar-elektron regime bereiken. Echter, kunnen de parameters gegeven afhankelijk van het model en de ijking van de gebruikte apparatuur. Daarom zal parameters zoals de doses van blootstelling tijdens de e-beam en fotolithografie stappen worden gekalibreerd vóór de vervaardiging van apparaten. De werkwijze kan gemakkelijk worden aangepast aan de vervaardiging van gate gedefinieerde quantum dots van andere soorten substr...

Quantum informatica heeft getrokken veel aandacht sinds het werd aangetoond dat quantum algoritmes gebruikt kunnen worden om bepaalde problemen exponentieel sneller dan met de bekendste klassieke algoritmes 1 lossen. Een voor de hand liggende kandidaat voor een quantum bit (qubit) is de spin van enkel elektron opgesloten in een quantum dot omdat het een twee-level systeem. Talrijke architecturen zijn voorgesteld voor de uitvoering van quantum dots, waaronder halfgeleidende nanodraden 2, koolstof nanobuisjes 3, zelf-georganiseerde kwantum-dots 4, en halfgeleiders verticale 5 en laterale quantum dots 6. Gate-gedefinieerde laterale quantum dots in GaAs / AlGaAs heterostructuren zijn zeer succesvol geweest vanwege hun veelzijdigheid en hun fabricageproces is de focus van deze paper. In laterale quantum dots, de opsluiting van elektronen in de richting loodrecht op het monsteroppervlak (z-richting) is bereikt door het kiezen van de juiste substraat. Het GaAs / AlGaAs modulatie gedoteerde heterostructuur presenteert een tweedimensionaal electron gas (2DEG) beperkt tot het raakvlak tussen de AlGaAs en GaAs lagen. Deze monsters worden geteeld door moleculaire bundel epitaxie een lage onzuiverheidsdichtheid die in combinatie met de modulatie-doping techniek te verkrijgen, leidt tot hoge elektronenmobiliteit in de 2DEG. Een schema van de verschillende lagen van de heterostructuur en de bandstructuur zijn getoond in figuur 1. Een hoge beweeglijkheid van de elektronen is nodig in de 2DEG om de samenhang van de elektronische toestanden over het gehele oppervlak van de quantum dot te garanderen. Het substraat voor het fabricageproces hieronder beschreven werd gekocht van de National Research Council of Canada en fungeert elektronendichtheid van 2,2 x 10 11 cm-2 en een elektronenmobiliteit van 1,69 x 10 6 cm 2 / Vsec. De opsluiting van elektronen in de richtingen parallel aan het monster oppervlak bereikt door metalen elektroden op het oppervlak van het substraat. Wanneer deze elektroden op het oppervlak van het GaAs monster worden Schottky barrières gevormd 7. Negatieve spanningen toegepast op deze elektroden leiden tot lokale barrières in de 2DEG hieronder die alleen elektronen met voldoende energie kan steken. Uitputting van de 2DEG treedt op wanneer de spanning negatief genoeg zodat elektronen voldoende energie om de barrière. Daarom door het zorgvuldig kiezen van de geometrie van de elektroden, is het mogelijk om een ​​klein aantal elektronen tussen verarmd gebieden van het monster houden. Controle van het aantal elektronen van de stip en de tunneling energie tussen de punt en de 2DEG in de rest van het monster kan worden bereikt door het afstemmen van de spanningen op de elektroden. Een schema van de poortelektroden en de verarmde gas elektronen wordt weergegeven in fig. 2. Het ontwerp voor de poort structuren vormen de stip ingeïnspireerd door het ontwerp wordt gebruikt door Barthel et al.. 8 Om controle en uitlezen van informatie over het aantal elektronen op het punt, is het nuttig voor inductie en meten stroom door de stip. Uitlezing kan ook met een Quantum worden Contact (QPC), waarvoor ook een stroom door de 2DEG. Het contact tussen de 2DEG en spanningsbronnen verzekert ohmse contacten. Dit zijn metalen elektroden die worden verspreid vanaf het oppervlak van het monster helemaal naar beneden om de 2DEG met een standaard snelle thermische gloeien proces 7 (zie figuren 3a en 4b). Om kortsluiting tussen de source en de drain te voorkomen, wordt het oppervlak van het monster zo geëtst dat de 2DEG is uitgeput in bepaalde regio&#39;s en de huidige wordt gedwongen om te reizen via bepaalde kanalen (zie de figuren 3b en 4a). Het gebied waar de 2DEG nog steeds aangeduid als de &quot;mesa&quot;. Het volgende protocol beschrijft de gehele fabricageproces van een poort-gedefinieerde laterale quantum dot op een GaAs / AlGaAs substraat. Het proces is schaalbaar omdat het blijft hetzelfde, ongeacht of het apparaat wordt gefabriceerd is een enkele, dubbele of driedubbele quantum dot of zelfs een array van quantum dots. Manipulatie, meet-, en de resultaten voor de dubbele quantum dots gefabriceerd met behulp van deze methode worden besproken in verdere hoofdstukken.

<table><tbody><tr><td>Aceton - CH3COCH3</td><td>Anachemia</td><td>AC-0150</td><td>67-64-1</td></tr><tr><td>Isopropyl Alcohol (IPA) - (CH3)2CHOH</td><td>Anachemia</td><td>AC-7830</td><td>67-63-0</td></tr><tr><td>1165 Remover</td><td>MicroChem Corp</td><td>G050200</td><td>872-50-4</td></tr><tr><td>Microposit MF-319 Developer</td><td>Shipley</td><td>38460</td><td>75-59-2</td></tr><tr><td>Zwavelzuur - H2SO4</td><td>Anachemia</td><td>AC-8750</td><td>766-93-9</td></tr><tr><td>Waterstofperoxide (30%) - H2O2</td><td>Fisher Scientific</td><td></td><td>7722-84-1</td></tr><tr><td>LOR 5A Lift-off resist</td><td>MicroChem Corp</td><td>G516608</td><td>120-92-3</td></tr><tr><td>Microposit S1813 Photo Resist</td><td>Shipley</td><td>41280</td><td>108-65-6</td></tr><tr><td>Microposit S1818 Photo Resist</td><td>Shipley</td><td>41340</td><td>108-65-6</td></tr><tr><td>PMMA LMW 4% in anisol</td><td>MicroChem Corp</td><td></td><td>100-66-3, 9011-14-7</td></tr><tr><td>PMMA HMW 2% in anisol</td><td>MicroChem Corp</td><td></td><td>100-66-3, 9011-14-7</td></tr><tr><td>GaAs/AlGaAs wafer</td><td>National Research Council Canada</td><td>Zie gedetailleerde laagstructuur in Figuur 1.</td><td></td></tr><tr><td>Ni (99,0%)</td><td>Anachemia</td><td></td><td></td></tr><tr><td>Ge (99,999%)</td><td>CERAC inc.</td><td></td><td></td></tr><tr><td>Au (99,999%)</td><td>Kamis inc.</td><td></td><td></td></tr><tr><td>Ti (99,995%)</td><td>Kurt J Lesker</td><td></td><td></td></tr><tr><td>Al</td><td>Kamis inc.</td><td></td><td></td></tr><tr><td>Silver Epoxy</td><td>Epoxy Technology</td><td>H20E</td><td></td></tr></tbody></table>

nanofabricage van gate-gedefinieerde gaas / algaas lateral quantum dots

Nanofabrication of Gate-defined GaAs/AlGaAs Lateral Quantum Dots

Een quantum computer is een computer samengesteld uit quantum bits (qubits) die gebruik maakt van de quantum effecten, zoals superpositie van toestanden en verstrengeling, om bepaalde problemen exponentieel sneller dan op te lossen met de bekendste algoritmen op een klassieke computer. Gate-gedefinieerde laterale quantum dots op GaAs / AlGaAs zijn een van de vele mogelijkheden verkend voor de uitvoering van een qubit. Bij juiste gefabriceerd, een dergelijke inrichting kan een klein aantal elektronen houden in een bepaald gebied van de ruimte. De spintoestanden van deze elektronen kunnen vervolgens worden gebruikt voor het implementeren van de logische 0 en 1 van de quantum bit. Gezien de nanometerschaal van deze quantum dots, cleanroom faciliteiten aanbieden van gespecialiseerde apparatuur-zoals scanning elektronenmicroscopen en e-beam-verdampers nodig zijn voor hun fabricage. Grote zorg moet tijdens het fabricageproces worden genomen om reinheid van het monsteroppervlak handhaven en schade aan de fragiele poorten van de constructie te voorkomen. Deze paperpresenteert de gedetailleerde fabricage protocol van gate-gedefinieerde laterale quantum dots van de wafer tot een werkend apparaat. Karakteriseringsmethodes en representatieve resultaten worden ook kort besproken. Hoewel dit document richt zich op dubbele quantum dots, het fabricageproces blijft hetzelfde voor enkele of drievoudige punten of zelfs arrays van quantum dots. Bovendien kan het protocol worden aangepast laterale quantum dots fabriceren op andere substraten, zoals Si / SiGe.

Een van de kritische stappen in de hierboven beschreven werkwijze is het etsen van de mesa (stap 1). Het is belangrijk te etsen hebben de 2DEG onderstaande verwijderen terwijl vermeden overetching. Daarom is het aanbevolen om een ​​bulk GaAs dummy monster gebruiken om de ets oplossing te testen voordat u de etsen op de GaAs / AlGaAs monster. De etssnelheid van de GaAs / AlGaAs heterostructuur is groter dan die van GaAs, maar het etsen van de dummy kan een indicatie geven of de oplossing meer of minder reactief dan norma...

Dit document presenteert een gedetailleerde fabricage protocol voor gate-gedefinieerde halfgeleider laterale quantum dots op galliumarsenide heterostructuren. Deze nanoschaal apparaten worden gebruikt om enkele elektronen vangen voor gebruik als quantum bits in quantum information processing of voor andere mesoscopic experimenten zoals coherent geleidingsmetingen.

Nanofabricage van Gate-gedefinieerde GaAs / AlGaAs Lateral Quantum Dots

A quantum computer is a computer composed of quantum bits (qubits) that takes advantage of quantum effects, such as superposition of states and ...

Het algemene doel van deze procedure is het vervaardigen van laterale quantumpunten die in staat zijn het enkel-elektronenregime te bereiken. Dit wordt bereikt door eerst een geschikt substraat te kiezen en een mesa te etsen om een regio van het monster af te bakenen waarin het tweedimensionale elektronengas aanwezig zal zijn. De tweede stap is het vervaardigen van ohmse contacten met behulp van fotolithografische processen en rapid thermal annealing.Vervolgens worden de leads en gates die de dot definiëren vervaardigd via elektronenstraallithografie. De laatste stap is het vervaardigen van de bondpads en de grotere leads middels fotolithografie. Ten slotte worden stabiliteitsdiagrammen gemeten bij een lage temperatuur om aan te tonen dat het few-electron regime kan worden bereikt.Het belangrijkste voordeel van dit apparaat ten opzichte van bestaande spin-qubits, zoals verticale quantum dots, is dat de eigenschappen van de laterale quantum dots afstembaar zijn. Hoewel dit protocol wordt gebruikt voor het fabriceren van laterale quantum dots op galliumarsenide-aluminium-galliumarsenide heterostructuren, kan het ook eenvoudig worden aangepast om apparaten te fabriceren op andere subs

nanofabrication-of-gate-defined-gaasalgaas-lateral-quantum-dots

Research

JoVE Journal

Engineering

Techniek

De fabricage van elektrisch adresseerbare, high-aspect-ratio (&gt; 1000:1) metalen nanodraden gescheiden door spleten van enkele nanometers behulp van opofferende lagen aluminium en zilver of zelf-geassembleerde monolaag zoals templates wordt beschreven. Deze nanogap structuren zijn vervaardigd zonder clean room of een foto-of electron-beam lithografische processen door een vorm van edge lithografie bekend als nanoskiving.

Fabriceren Nanogaps door Nanoskiving

Dit document beschrijft het fabricageproces van een poort-afstelbaar grafeenapparaat, versierd met Coulomb-onzuiverheden voor studies met rastertunnelmicroscopie. Het in kaart brengen van de ruimtelijk afhankelijke elektronische structuur van grafeen in aanwezigheid van geladen onzuiverheden onthult het unieke gedrag van zijn relatieve ladingsdragers als reactie op een lokaal Coulomb-potentieel.

Fabricage van Gate-afstembare Grafeen Inrichtingen voor Scanning Tunneling Microscopy Studies met Coulomb Verontreinigingen

Het fabricageproces en experimentele karakteriseringstechnieken die relevant zijn voor enkele-elektronpompen op basis van silicium metaal-oxide-halfgeleider kwantumdots worden besproken.

Silicon metaal-oxide-halfgeleider Quantum Dots voor Single-electron Pumping

Quantum integrated circuits (QICs) bestaande uit array van planaire en ballistische Josephson-kruisingen (JJs) op basis van0,75ga0,25als tweedimensionaal ELEKTRONEN gas (2deg) wordt gedemonstreerd. Twee verschillende methoden voor de fabricage van de tweedimensionale (2D) JJs en QICs worden besproken, gevolgd door de demonstratie van Quantum Transport metingen in sub-Kelvin temperaturen.

Schaalbare Quantum geïntegreerde schakelingen op supergeleidend tweedimensionaal elektronen Gasplatform

Het artikel beoogt de invoering van een standaard en betrouwbare fabricage-procedure voor de ontwikkeling van toekomstige lage dimensionale nano-elektronica.

Een standaard en betrouwbare methode om te fabriceren tweedimensionale nano-elektronica

Een protocol voor grafeen-ondersteunde groei van hoogwaardige AlN-films op saffiersubstraat met nanopatroon wordt gepresenteerd.

Grafeen-Geassisteerde Quasi-van der Waals Epitaxy van AlN Film op Nano-Patroon Sapphire Substraat voor Ultraviolet Light Emitting Diodes

Dit artikel presenteert een geoptimaliseerd, op ervaring gebaseerd protocol voor het vervaardigen van hoogwaardige op grafeen gebaseerde moiré-superroosterapparaten met nauwkeurige draaihoeken, met behulp van een aangepaste droge overdrachtstechniek op basis van een zeer afstembare, op maat gemaakte overdrachtsopstelling.

Geoptimaliseerde fabricageprocedure voor hoogwaardige Moiré Superlattice-apparaten op basis van grafeen

We beschrijven de bereiding van colloïdale quantum dots met minimale hydrodynamische grootte voor single-molecule fluorescentie beeldvorming. Vergeleken met conventionele quantum dots, deze nanodeeltjes zijn vergelijkbaar in grootte met globulaire eiwitten en zijn geoptimaliseerd voor single-molecule helderheid, stabiliteit tegen afbraak en resistentie tegen specifieke binding aan eiwitten en cellen.

Compact Quantum Dots voor Single-molecule Imaging

De gradiënt echo geheugen is een protocol voor het opslaan van optische quantum toestanden van licht in atomaire ensembles. Quantum geheugen is een belangrijk element van een quantum repeater, die het bereik van de quantum key distribution kan uitbreiden. Schetsen we de werking van de regeling wanneer geïmplementeerd in een 3-niveau atomaire ensemble.

Gradient Echo Quantum Memory in Warm Atomic Vapor

Een techniek ontwikkeld die Ni / Au contact metaal films verwijdert uit hun substraat te laten voor het onderzoek en karakterisering van het contact / substraat en contact / NW interfaces van enkele GaN nanodraad apparaten.

Analyse van Contact Interfaces for Single GaN Nanodraad Devices

Leer nanofabricage van gate-gedefinieerde laterale kwantumdots op GaAs/AlGaAs-heterostructuren voor kwantuminformatieverwerking. Dit protocol omvat mesa-etsen, ohmische contacten en elektronenbundellithografie.

Nanofabricage van Gate-gedefinieerde GaAs / AlGaAs Lateral Quantum Dots

Meer video's verkennen