Name: 3D afgedrukt poreuze Cellulose nanocomposietmaterialen Hydrogel steigers (Video) | JoVE Journal
Uploaded: 2019-04-24T13:00:00.000+00:00
Duration: 6 min 36 s
Description: Leer hoe je 3D-geprinte nanocellulose hydrogelsteigers maakt met gradiëntporiënstructuren die het natuurlijke kraakbeen nabootsen. Dit gebruiksvriendelijke protocol maakt aanpassing en reproduceerbaar onderzoek mogelijk.

ai_agent_IP

ai_agent

maintenance

instantTrialDurationMinutes

isBiopharma

enableNewMyJoveSectionDesign

educationFeatures

seoMetaApi

ai_copilot_institution_blacklist

ai_chat_institution_blacklist

freeAccessWindow

ssoRoleCapture

scheduledMaintenanceBanner

joveLabsFeatures

disable_autoplay_for_bots

extended_trial_duration

5 minutes

Deze studie wordt financieel gesteund door Knut en Alice Wallenberg Foundation (Wallenberg hout Science Center), Zweedse Raad voor onderzoek, VR (DNR 2016-05709, Bioheal en DNR 2017-04254).

1. bereiding van precursoren
<ol><li>Voorbereiding van cellulose nanokristallen schorsing Opmerking: De isolatie van cellulose nanokristallen gebeurt volgens de procedure die is gerapporteerd door Mathew, et al.30.<ol>
<li>Verdunde 17 wt % opschorting van cellulose nanokristallen 2 wt % door het toevoegen van gedestilleerd water om een totaal volume van 2 L. Mix grondig met behulp van ultra ultrasoonapparaat en gebruik kleinere batches (250-300 mL) voor het efficiënt mengen.</li>
		<li>Doorgeven van de sonified ophanging door middel van de homogenizer 10 keer bij een druk van 500-600 bar. Op dit punt wordt een dikke transparante gel van 2 wt % cellulose nanokristallen verkregen.</li>
		<li>Concentreren 2 wt % cellulose nanokristallen gel tot 11 wt % via centrifugations bij 24.500 x g gedurende 1,5 h. Decant water uit tussen elke 30 min. Opmerking: Experiment kan hier worden gepauzeerd.</li>
	</ol>
</li>
	<li>Voorbereiding van matrix fasen<ol>
<li>Bereiden homogene oplossing van 6 wt % natriumalginaat (SA) in gedistilleerd water van 60 ° C onder continu roeren.</li>
		<li>Bereiden homogene oplossing van 12 wt % gelatine (Gel) in gedistilleerd water van 60 ° C onder continu roeren. Opmerking: Een volume van 20 mL voorbereiden matrix oplossingen en bewaar in de koelkast.</li>
	</ol>
</li>
	<li>Voorbereiding van crosslinkers<ol>
<li>Bereid de oplossing van 3 wt % calcium chloride in gedistilleerd water op kamertemperatuur onder continu roeren.</li>
		<li>Bereid de oplossing van 3 wt % Glutaaraldehyde in gedistilleerd water op kamertemperatuur onder continu roeren. Opmerking: Een volume van 50 mL voorbereiden crosslinking oplossingen en bewaar op kamertemperatuur. Verwijzen naar de Tabel van materialen voor leveranciersgegevens. Experiment kan hier worden gepauzeerd.</li>
	</ol>
</li>
</ol>2. voorbereiding van hydrogel inkt
<ol><li>40 mL hydrogel inkt in een polystyreen container voor te bereiden door het mengen van 11 wt % CNC, 6 wt % SA en 12 wt % Gel te verkrijgen van een natte (wt %) samenstelling van CNC/SA/Gel/Water: 6.87/1.50/1.50/90.12.</li>
	<li>Verwarm het mengsel tot 40 ° C en mix met een spatel tot een gladde pasta wordt verkregen.</li>
	<li>Breng het mengsel in een injectiespuit 60 mL. Laat het mengsel door middel van een reeks van sproeiers met verschillende diameters in een andere 60 mL spuit, met behulp van mechanische klem. Herhaal dit proces totdat soepel geëxtrudeerde filamenten van hydrogel inkt worden verkregen. Begin met mondstuk met een grootste diameter van 800 µm, gevolgd door de 600 µm en 400 µm.</li>
	<li>Zachtjes centrifuge (4000 x g) de spuit gevuld met hydrogel inkt verwijderen gevangen lucht. Opmerking: Experiment kan hier worden gepauzeerd.</li>
</ol>3. meting van de reologische eigenschappen hydrogel
NTE: Uitvoeren de Rheologische eigenschappen met behulp van een soepele kegel-op-plaat geometrie, CP25-2-SN7617, diameter 25 mm, 2 ° nominale hoek en hoogte van de kloof 0.05 mm bij 25 ° C.
<ol><li>Inschakelen van de rheometer, luchtcompressor en temperatuur controle box. Initialiseren van de software.</li>
	<li>Monteren van het meetinstrument in het rheometer en instellen van nul-gap.</li>
	<li>Diepte ongeveer 1 mL van de hydrogel inkt op het platform rheometer.</li>
	<li>De viscositeit als een functie van shear rate te meten. Selecteer de shear rate bereik uit 0.001 tot 1.000.</li>
	<li>Na de meting wordt gedaan, reinigen van het rheometer platform en meetinstrument. Extruderen 1 mL verse hydrogel inkt weer op het rheometer platform.</li>
	<li>Meten van opslag modules (G′) en verlies modules (G″) als een functie van shear stress bij een frequentie van 1 Hz. Selecteer de schuifspanning bereik uit 103 tot en met 107.</li>
	<li>Zodra de tests zijn voltooid, kopieer de gegevens naar een tekstbestand en plot Rheologische krommen in een logaritmische schaal.</li>
</ol>4. file voorbereiding voor afdrukken in 3D
Opmerking: Cura 2.4.0 software wordt gebruikt voor het ontwerpen van 3D-steigers (20 mm3) hebben drie soorten poriën. 1-uniform poriën van 0,6 mm, 2-uniform poriën van 1,0 mm en 3-verloop poriën van bereik van 0.5-1 mm.
<ol><li>Download van stereolithografie (stl) bestand van een stevige kubus van thingsinverse.com en open het bestand in Cura.</li>
	<li>Klik op het geladen model en verplaats het naar X/Y/Z: 0/0/0 mm. Klik op schaal, uncheck de doos voor uniforme schalen en stel de afmetingen op X/Y/Z: 20/20/20 mm. Klik op draaien en draai de kubus door 45 ° in XY-vlak.</li>
	<li>In het zijpaneel, in mondstuk & materiaal, Selecteer 0,4 mm en plak van het profiel. Discov3ry volledige als de printer selecteren</li>
	<li>Selecteer in het zijpaneel, aangepast voor Printerinstelling. Voer onder kwaliteit sectie 0.2 mm voor alle sub-secties. Voer onder de sectie van de Shell , 0 mm voor alle sub-secties. Voer onder materiaal sectie 26 ° C voor temperatuur, 1 mm Diameter en 100% stromen. Geef 30 mm/s als Afdruksnelheden en 120 mm/s als Reizen snelheidonder de snelheid sectie. Onder gedeelte, uncheck de doos voor Ondersteuning inschakelen. Onder Bouwen plaat hechting sectie Selecteer rok, voert 3 mm als de Afstand van de rok en 150 mm als rok/rand minimumlengte.</li>
	<li>Voor steigers met uniforme poriegrootte, 0,6 of 1 mm "Infill" lijn afstand invoeren en selecteer "Infill" rasterpatroon.</li>
	<li>Voor kleurovergang porositeit steigers, wordt samenvoegen en groeperen van hulpmiddel gebruikt. Klik met de rechtermuisknop het geladen model, selecteer Meerdere modellen, typ 2 en druk op OK. Elk model als X/Y/Z schaal: 20/20/7 mm. plaats de modellen boven op elkaar. Typ "Infill" lijn afstand als 0.3, 0,5 en 0,7 mm voor onder-, Midden- en bovenkant model, respectievelijk. Selecteer alle drie de modellen (Ctrl + A), klik met de rechtermuisknop en klik op Groep modellen.</li>
	<li>De modellen op de zeker Digitaal (SD) kaart opgeslagen. Cura automatisch opslaan als gcode die kan worden gelezen door de printer.</li>
</ol>5. 3D printen poreuze steigers
<ol><li>De verbindingsleiding invoegen de nozzle-houder en 400 µm mondstuk verbinden. Niveau de plaat te bouwen om de juiste afstand tussen de build plaat en mondstuk.</li>
	<li>Laden van de gecentrifugeerde spuit in de cartridge en sluit deze aan de andere kant van de verbindingsleiding.</li>
	<li>Plaats de SD-kaart in de printer, selecteer snel opruimen en start de hydrogel inkt wissen tot het begint te extruderen van de verstuiver. Blijven zuiveren voor 2-3 min te verkrijgen van een homogene stroom.</li>
	<li>Van de SD-kaart, selecteert u de opgeslagen bestanden voor uniforme en kleurovergang porositeit steigers en beginnen met afdrukken. Houd een oogje op het tarief van de extrusie. Indien nodig, de snelheid en stroom tarief dienovereenkomstig aanpassen. Gebruik voor kleinere poriegrootte, sneller snelheid, gecombineerd met lage stroomsnelheid (50 mm/s en 70%). Opmerking: Raak niet de 3D gedrukte steigers.</li>
</ol>6. Crosslinking van 3D afgedrukt steigers
<ol><li>Nadat het 3D printen voltooid is, voeg voorzichtig 3 wt % CaCl2 druppels naar het schavot totdat het volledig nat wordt. 5 min wachten.</li>
	<li>Zeer zorgvuldig overbrengen de steiger van de printer naar een 50 mL flacon gevuld met 3 wt % CaCl2. Laten overnachten.</li>
	<li>Grondig wassen met gedestilleerd water en breng het schavot aan een 50 mL-container gevuld met 3 wt % Glutaaraldehyde. Laten overnachten.</li>
	<li>Grondig wassen en op te slaan van de 3D gedrukte steiger in gedestilleerd water.</li>
</ol>7. compressie testen
Opmerking: Voer compressie tests met 100 N load cel in water bij 37 ° C.
<ol><li>Vul de container uitgerust met Onderdompelbare compressie basisplaat met 2 L water en opstarten van het verwarmingssysteem tot 37 ° C.</li>
	<li>Initialiseren Bluehill universele software en instellen van de testmethode. Selecteert u rechthoekige specimen geometrie en kies de optie dimensies invoeren voor het testen van elk monster.  Stelt het tarief van de stam naar 2 mm/min en einde van resultaat als de druksterkte stam 80% samen met 90 N kracht.</li>
	<li>Selecteer in de sectie meting kracht, verplaatsing, drukspanning en druksterkte stam. Kies de optie om gegevens te exporteren als tekstbestanden voor toekomstige uitzetten.</li>
	<li>Het nulpunt van extensie instellen met behulp van de besturingselementen jog tot lagere crosshead plaat zo dicht mogelijk op basis van de plaat.</li>
	<li>Meten en Let op de afmetingen van de monsters moeten worden getest.</li>
	<li>Wanneer de temperatuur van het water tot 37 ° C bereikt, leg het monster op de grondplaat.  Beveilig het monster door het bewegen van de crosshead plaat, zodat deze begint te raken van het monster.</li>
	<li>Omhoog het waterbad, zodat de platen met de monster tussen hen worden ondergedompeld in water.</li>
	<li>Voer monster naam en afmetingen. Start de test.</li>
	<li>Nadat de test voltooid is, eerst het waterbad omlaag en vervolgens verhogen de crosshead plaat.</li>
	<li>Verwijder het monster en de stukken, als een, beide de platen schoon en laden van een nieuw monster.</li>
	<li>Nadat alle monsters worden getest, de ruwe gegevens exporteren. Plot drukspanning vs. druksterkte stam curven en bepalen de druksterkte tangent modulus op stam waarden van 1-5% en 25-30%. Opmerking: Plaats de kleurovergang kubus op een zodanige wijze dat de grotere gaten worden geconfronteerd met de grondplaat van briefpapier. Eerst veilige het schavot tussen de handvatten en vervolgens start/stop de meting.</li>
</ol>

<ol><li>Moon, R. J., Martini, A., Nairn, J., Simonsen, J., Youngblood, J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Cellulose+nanomaterials+review%3A+structure%2C+properties+and+nanocomposites%5BTitle%5D)+AND+%22Chemical+Society+Reviews%22%5BJournal%5D)">Cellulose nanomaterials review: structure, properties and nanocomposites.</a> Chemical Society Reviews. 40 (7), 3941-3994 (2011).</li>
<li>Dufresne, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Nanocellulose%3A+a+new+ageless+bionanomaterial%5BTitle%5D)+AND+%22Materials+Today%22%5BJournal%5D)">Nanocellulose: a new ageless bionanomaterial.</a> Materials Today. 16 (6), 220-227 (2013).</li>
<li>Chinga-Carrasco, G. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Potential+and+limitations+of+nanocelluloses+as+components+in+biocomposite+inks+for+three-dimensional+bioprinting+and+for+biomedical+devices%5BTitle%5D)+AND+%22Biomacromolecules%22%5BJournal%5D)">Potential and limitations of nanocelluloses as components in biocomposite inks for three-dimensional bioprinting and for biomedical devices.</a> Biomacromolecules. 19 (3), 701-711 (2018).</li>
<li>Naseri, N., Poirier, J., Girandon, L., Fröhlich, M., Oksman, K., Mathew, A. P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((3-Dimensional+porous+nanocomposite+scaffolds+based+on+cellulose+nanofibers+for+cartilage+tissue+engineering%3A+tailoring+of+porosity+and+mechanical+performance%5BTitle%5D)+AND+%22Royal+Society+of+Chemistry+Advances%22%5BJournal%5D)">3-Dimensional porous nanocomposite scaffolds based on cellulose nanofibers for cartilage tissue engineering: tailoring of porosity and mechanical performance.</a> Royal Society of Chemistry Advances. 6 (8), 5999-6007 (2016).</li>
<li>Naseri, N., Deepa, B., Mathew, A. P., Oksman, K., Girandon, L. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Nanocellulose-Based+Interpenetrating+Polymer+Network+%28IPN%29+Hydrogels+for+Cartilage+Applications%5BTitle%5D)+AND+%22Biomacromolecules%22%5BJournal%5D)">Nanocellulose-Based Interpenetrating Polymer Network (IPN) Hydrogels for Cartilage Applications.</a> Biomacromolecules. 17 (11), 3714-3723 (2016).</li>
<li>Naseri, N., Mathew, A. P., Girandon, L., Fröhlich, M., Oksman, K. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Porous+electrospun+nanocomposite+mats+based+on+chitosan-cellulose+nanocrystals+for+wound+dressing%3A+effect+of+surface+characteristics+of+nanocrystals%5BTitle%5D)+AND+%22Cellulose%22%5BJournal%5D)">Porous electrospun nanocomposite mats based on chitosan-cellulose nanocrystals for wound dressing: effect of surface characteristics of nanocrystals.</a> Cellulose. 22 (1), 521-534 (2015).</li>
<li>Xing, Q., Zhao, F., Chen, S., McNamara, J., DeCoster, M. A., Lvov, Y. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Porous+biocompatible+three-dimensional+scaffolds+of+cellulose+microfiber%2Fgelatin+composites+for+cell+culture%5BTitle%5D)+AND+%22Acta+Biomaterialia%22%5BJournal%5D)">Porous biocompatible three-dimensional scaffolds of cellulose microfiber/gelatin composites for cell culture.</a> Acta Biomaterialia. 6 (6), 2132-2139 (2010).</li>
<li>Nandgaonkar, A., Krause, W., Lucia, L. Fabrication of cellulosic composite scaffolds for cartilage tissue engineering. <a target="_blank" href="http://scholar.google.com/scholar?hl=en&safe=off&q=author%3aNandgaonkar%2C+A+%22Nanocomposites+for+musculoskeletal+tissue+regeneration%22">Nanocomposites for musculoskeletal tissue regeneration</a>. , Elsevier. 187-212 (2016).</li>
<li>Gross, B. C., Erkal, J. L., Lockwood, S. Y., Chen, C., Spence, D. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Evaluation+of+3D+printing+and+its+potential+impact+on+biotechnology+and+the+chemical+sciences%5BTitle%5D)+AND+%22Analytical+Chemistry%22%5BJournal%5D)">Evaluation of 3D printing and its potential impact on biotechnology and the chemical sciences.</a> Analytical Chemistry. 86 (7), 3240-3253 (2014).</li>
<li>Markstedt, K., Mantas, A., Tournier, I., Martínez Ávila, H., Hägg, D., Gatenholm, P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((3D+bioprinting+human+chondrocytes+with+nanocellulose-alginate+bioink+for+cartilage+tissue+engineering+applications%5BTitle%5D)+AND+%22Biomacromolecules%22%5BJournal%5D)">3D bioprinting human chondrocytes with nanocellulose-alginate bioink for cartilage tissue engineering applications.</a> Biomacromolecules. 16 (5), 1489-1496 (2015).</li>
<li>Sultan, S., Mathew, A. P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((3D+printed+scaffolds+with+gradient+porosity+based+on+a+cellulose+nanocrystal+hydrogel%5BTitle%5D)+AND+%22Nanoscale%22%5BJournal%5D)">3D printed scaffolds with gradient porosity based on a cellulose nanocrystal hydrogel.</a> Nanoscale. 10, 4421-4431 (2018).</li>
<li>Sultan, S., Siqueira, G., Zimmermann, T., Mathew, A. P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((3D+printing+of+nano-cellulosic+biomaterials+for+medical+applications%5BTitle%5D)+AND+%22Current+Opinion+in+Biomedical+Engineering%22%5BJournal%5D)">3D printing of nano-cellulosic biomaterials for medical applications.</a> Current Opinion in Biomedical Engineering. 2, 29-34 (2017).</li>
<li>Sultan, S., Abdelhamid, H. N., Zou, X., Mathew, A. P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((CelloMOF%3A+Nanocellulose+Enabled+3D+Printing+of+Metal-Organic+Frameworks%5BTitle%5D)+AND+%22Advanced+Functional+Materials%22%5BJournal%5D)">CelloMOF: Nanocellulose Enabled 3D Printing of Metal-Organic Frameworks.</a> Advanced Functional Materials. , 1805372-1805384 (2018).</li>
<li>Siqueira, G., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Cellulose+Nanocrystal+Inks+for+3D+Printing+of+Textured+Cellular+Architectures%5BTitle%5D)+AND+%22Advanced+Functional+Materials%22%5BJournal%5D)">Cellulose Nanocrystal Inks for 3D Printing of Textured Cellular Architectures.</a> Advanced Functional Materials. 27 (12), 1604619-1604629 (2017).</li>
<li>Wang, J., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((All-in-One+Cellulose+Nanocrystals+for+3D+Printing+of+Nanocomposite+Hydrogels%5BTitle%5D)+AND+%22Angewandte+Chemie+International+Edition%22%5BJournal%5D)">All-in-One Cellulose Nanocrystals for 3D Printing of Nanocomposite Hydrogels.</a> Angewandte Chemie International Edition. 57 (9), 2353-2356 (2018).</li>
<li>Hausmann, M. K., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Dynamics+of+Cellulose+Nanocrystal+Alignment+during+3D+Printing%5BTitle%5D)+AND+%22ACS+Nano%22%5BJournal%5D)">Dynamics of Cellulose Nanocrystal Alignment during 3D Printing.</a> ACS Nano. 12 (7), 6926-6937 (2018).</li>
<li>Liu, Y., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Nanoscale+assembly+of+cellulose+nanocrystals+during+drying+and+redispersion%5BTitle%5D)+AND+%22ACS+Macro+Letters%22%5BJournal%5D)">Nanoscale assembly of cellulose nanocrystals during drying and redispersion.</a> ACS Macro Letters. 7 (2), 172-177 (2018).</li>
<li>Murphy, S. V., Atala, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((3D+bioprinting+of+tissues+and+organs%5BTitle%5D)+AND+%22Nature+Biotechnology%22%5BJournal%5D)">3D bioprinting of tissues and organs.</a> Nature Biotechnology. 32 (8), 773-785 (2014).</li>
<li>Pati, F., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Printing+three-dimensional+tissue+analogues+with+decellularized+extracellular+matrix+bioink%5BTitle%5D)+AND+%22Nature+communications%22%5BJournal%5D)">Printing three-dimensional tissue analogues with decellularized extracellular matrix bioink.</a> Nature communications. 5, 3935(2014).</li>
<li>Xia, Z., Jin, S., Ye, K. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Tissue+and+organ+3D+bioprinting%5BTitle%5D)+AND+%22SLAS+TECHNOLOGY%3A+Translating+Life+Sciences+Innovation%22%5BJournal%5D)">Tissue and organ 3D bioprinting.</a> SLAS TECHNOLOGY: Translating Life Sciences Innovation. 23 (4), 301-314 (2018).</li>
<li>Zhang, Q., Lu, H., Kawazoe, N., Chen, G. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Pore+size+effect+of+collagen+scaffolds+on+cartilage+regeneration%5BTitle%5D)+AND+%22Acta+Biomaterialia%22%5BJournal%5D)">Pore size effect of collagen scaffolds on cartilage regeneration.</a> Acta Biomaterialia. 10 (5), 2005-2013 (2014).</li>
<li>Loh, Q. L., Choong, C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Three-dimensional+scaffolds+for+tissue+engineering+applications%3A+role+of+porosity+and+pore+size%5BTitle%5D)+AND+%22Tissue+Engineering%2C+Part+B%3A+Reviews%22%5BJournal%5D)">Three-dimensional scaffolds for tissue engineering applications: role of porosity and pore size.</a> Tissue Engineering, Part B: Reviews. 19 (6), 485-502 (2013).</li>
<li>Bružauskaitė, I., Bironaitė, D., Bagdonas, E., Bernotienė, E. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Scaffolds+and+cells+for+tissue+regeneration%3A+different+scaffold+pore+sizes-different+cell+effects%5BTitle%5D)+AND+%22Cytotechnology%22%5BJournal%5D)">Scaffolds and cells for tissue regeneration: different scaffold pore sizes-different cell effects.</a> Cytotechnology. 68 (3), 355-369 (2016).</li>
<li>Zhang, L., Hu, J., Athanasiou, K. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((The+role+of+tissue+engineering+in+articular+cartilage+repair+and+regeneration%5BTitle%5D)+AND+%22Critical+Reviews%E2%84%A2+in+Biomedical+Engineering%22%5BJournal%5D)">The role of tissue engineering in articular cartilage repair and regeneration.</a> Critical Reviews™ in Biomedical Engineering. 37 (1-2), (2009).</li>
<li>Athanasiou, K., Rosenwasser, M., Buckwalter, J., Malinin, T., Mow, V. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Interspecies+comparisons+of+in+situ+intrinsic+mechanical+properties+of+distal+femoral+cartilage%5BTitle%5D)+AND+%22Journal+of+Orthopaedic+Research%22%5BJournal%5D)">Interspecies comparisons of in situ intrinsic mechanical properties of distal femoral cartilage.</a> Journal of Orthopaedic Research. 9 (3), 330-340 (1991).</li>
<li>Schinagl, R. M., Gurskis, D., Chen, A. C., Sah, R. L. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Depth-dependent+confined+compression+modulus+of+full-thickness+bovine+articular+cartilage%5BTitle%5D)+AND+%22Journal+of+Orthopaedic+Research%22%5BJournal%5D)">Depth-dependent confined compression modulus of full-thickness bovine articular cartilage.</a> Journal of Orthopaedic Research. 15 (4), 499-506 (1997).</li>
<li>Athanasiou, K., Niederauer, G., Schenck, R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Biomechanical+topography+of+human+ankle+cartilage%5BTitle%5D)+AND+%22Annals+Biomedical+Engineering%22%5BJournal%5D)">Biomechanical topography of human ankle cartilage.</a> Annals Biomedical Engineering. 23 (5), 697-704 (1995).</li>
<li>Athanasiou, K. A., Liu, G. T., Lavery, L. A., Lanctot, D. R., Schenck, R. C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Biomechanical+topography+of+human+articular+cartilage+in+the+first+metatarsophalangeal+joint%5BTitle%5D)+AND+%22Clinical+Orthopaedics+and+Related+Research%22%5BJournal%5D)">Biomechanical topography of human articular cartilage in the first metatarsophalangeal joint.</a> Clinical Orthopaedics and Related Research. 348, 269-281 (1998).</li>
<li>Guilak, F., Jones, W. R., Ting-Beall, H. P., Lee, G. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((The+deformation+behavior+and+mechanical+properties+of+chondrocytes+in+articular+cartilage%5BTitle%5D)+AND+%22Osteoarthritis+and+Cartilage%22%5BJournal%5D)">The deformation behavior and mechanical properties of chondrocytes in articular cartilage.</a> Osteoarthritis and Cartilage. 7 (1), 59-70 (1999).</li>
<li>Mathew, A. P., Oksman, K., Karim, Z., Liu, P., Khan, S. A., Naseri, N. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Process+scale+up+and+characterization+of+wood+cellulose+nanocrystals+hydrolysed+using+bioethanol+pilot+plant%5BTitle%5D)+AND+%22Industrial+Crops+and+Products%22%5BJournal%5D)">Process scale up and characterization of wood cellulose nanocrystals hydrolysed using bioethanol pilot plant.</a> Industrial Crops and Products. 58, 212-219 (2014).</li>
<li>Compton, B. G., Lewis, J. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((3D-printing+of+lightweight+cellular+composites%5BTitle%5D)+AND+%22Advanced+Materials%22%5BJournal%5D)">3D-printing of lightweight cellular composites.</a> Advanced Materials. 26 (34), 5930-5935 (2014).</li>
<li>Sarem, M., Moztarzadeh, F., Mozafari, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((How+can+genipin+assist+gelatin%2Fcarbohydrate+chitosan+scaffolds+to+act+as+replacements+of+load-bearing+soft+tissues%5BTitle%5D)+AND+%22Carbohydrate+Polymers%22%5BJournal%5D)">How can genipin assist gelatin/carbohydrate chitosan scaffolds to act as replacements of load-bearing soft tissues.</a> Carbohydrate Polymers. 93 (2), 635-643 (2013).</li>
<li>Chia, H. N., Hull, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Compressive+moduli+of+the+human+medial+meniscus+in+the+axial+and+radial+directions+at+equilibrium+and+at+a+physiological+strain+rate%5BTitle%5D)+AND+%22Journal+of+orthopaedic+research%22%5BJournal%5D)">Compressive moduli of the human medial meniscus in the axial and radial directions at equilibrium and at a physiological strain rate.</a> Journal of orthopaedic research. 26 (7), 951-956 (2008).</li>
<li>Zhang, K., Fan, Y., Dunne, N., Li, X. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Effect+of+microporosity+on+scaffolds+for+bone+tissue+engineering%5BTitle%5D)+AND+%22Regenerative+biomaterials%22%5BJournal%5D)">Effect of microporosity on scaffolds for bone tissue engineering.</a> Regenerative biomaterials. 5 (2), 115-124 (2018).</li>
<li>Lin, N., Dufresne, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Nanocellulose+in+biomedicine%3A+Current+status+and+future+prospect%5BTitle%5D)+AND+%22European+Polymer+Journal%22%5BJournal%5D)">Nanocellulose in biomedicine: Current status and future prospect.</a> European Polymer Journal. 59, 302-325 (2014).</li>
<li>Domingues, R. M., Gomes, M. E., Reis, R. L. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((The+potential+of+cellulose+nanocrystals+in+tissue+engineering+strategies%5BTitle%5D)+AND+%22Biomacromolecules%22%5BJournal%5D)">The potential of cellulose nanocrystals in tissue engineering strategies.</a> Biomacromolecules. 15 (7), 2327-2346 (2014).</li>
</ol>

De auteurs hebben niets te onthullen.

3D printen vereist geschikt Rheologische eigenschappen van de hydrogel inkt. De hoge viscositeit inkt vergt extreme druk voor de extrusie terwijl lage viscositeit inkt niet zijn vorm na extrusie behouden zal. De viscositeit van de hydrogel inkt kan worden gecontroleerd door middel van de concentratie van de ingrediënten. In vergelijking met onze vorige werk11, wordt het gehalte aan vaste stof van de hydrogel inkt verhoogd van 5,4 tot 9,9% van de wt resulterend in geconcentreerde hydrogel inkt die ...

Cellulose is een polysaccharide, bestaande uit lineaire ketens van β (1-4) gekoppelde D-glucose-eenheden. Het is de meest voorkomende natuurlijke polymeer op aarde en wordt gewonnen uit een verscheidenheid van bronnen, met inbegrip van zeedieren (b.v., manteldieren), planten (bijv. hout, katoen, tarwestro) en bacteriële bronnen, zoals algen (bijvoorbeeld Valonia), schimmels, en zelfs Amoebe (protozoa )1,2. Cellulose nanofibers (CNF) en cellulose nanokristallen (CNC) met ten minste één dimensie op nanoschaal zijn verkregen door middel van mechanische behandelingen en zure hydrolyse van cellulose. Zij beschikken niet alleen over de eigenschappen van cellulose, zoals potentieel voor chemische modificatie, lage toxiciteit, biocompatibiliteit, biologisch afbreekbaar en hernieuwbare, maar heeft ook kenmerken van de nanoschaal zoals hoge specifieke oppervlakte, hoge mechanische eigenschappen , rheologische en optische eigenschappen. Deze aantrekkelijke eigenschappen hebben CNFs en CNCs geschikt voor biomedische toepassingen, voornamelijk in de vorm van 3-dimensionale (3D) hydrogel steigers3. Deze steigers vereist aangepaste afmetingen met gecontroleerde poriënstructuur en onderling verbonden porositeit. Onze fractie en anderen hebben gemeld 3D poreuze cellulose nanocomposieten bereid door gieten, electrospinning en trekkers4,5,,6,,7,8. Echter controle over de structuur van de porie en fabricage van complexe geometrie wordt niet bereikt door deze traditionele technieken.
3D printen is een additief productietechniek, waarin 3D-objecten worden gemaakt laag voor laag door de computergestuurde afzetting van de inkt-9. De voordelen van 3D printen op traditionele technieken omvat ontwerpvrijheid, gecontroleerde macro en micro afmetingen, fabricage van complexe architecturen, aanpassing en reproduceerbaarheid.  Daarnaast biedt 3D printen van CNFs en CNCs ook schuintrekken-geïnduceerde uitlijning van nanodeeltjes, voorkeur directionaliteit, kleurovergang porositeit en kan gemakkelijk worden uitgebreid tot 3D bioprinting10,11,12, 13 , 14 , 15. de dynamiek van CNCs uitlijning tijdens het afdrukken in 3D geweest rapporteerde onlangs,16,17. Vooruitgang op het gebied van bioprinting hebben inschakelen 3D bedrukte weefsels en organen ondanks de betrokken uitdaging zoals keuze en concentratie van levende cellen en groeifactoren, samenstelling van de inkt van de vervoerder, afdrukken van druk en mondstuk diameters18 ,19,20.
De porositeit en druksterkte van kraakbeen regeneratieve steigers zijn belangrijke eigenschappen die dicteert de efficiëntie en prestaties. Poriegrootte speelt een belangrijke rol voor de hechting, differentiatie en proliferatie van cellen, alsook wat betreft de uitwisseling van voedingsstoffen en metabolische afvalstoffen21. Echter, er is geen duidelijke poriegrootte die kan worden beschouwd als een ideale waarde, sommige studies bleek hoger topicale met kleinere poriën, terwijl anderen betere regeneratie van het kraakbeen met grotere poriën toonde. Macroporiën (< 500 µm) weefsel mineralisatie-, nutriënten aan- en afvoer van de afvalstoffen te vergemakkelijken terwijl micropores (150-250 µm) cel gehechtheid en betere mechanische eigenschappen22,23 vergemakkelijken. De geïmplanteerde steiger moet voldoende mechanische integriteit vanaf het moment van behandeling, implantatie en tot de voltooiing van het gewenste doel. De statistische druksterkte modulus voor natuurlijke articulair kraakbeen is gemeld dat in de range van 0.1-2 MPa afhankelijk van leeftijd, geslacht en geteste locatie4,24,25,26,27 2928, ,.
In onze eerdere werk11, werd 3D printen gebruikt voor het fabriceren van poreuze bioscaffolds van een dubbele kruisverwijzende interpenetratie van polymeer network (IPN) van een hydrogel inkt met versterkte CNCs in een matrix van natriumalginaat en gelatine. Het 3D printen traject is geoptimaliseerd om 3D steigers met uniforme en kleurovergang porie structuren (80-2,125 µm) waar nanokristallen oriënteren bij voorkeur in de afdrukken richting (mate van oriëntatie tussen 61-76%). Hier presenteren wij onze de voortzetting van dit werk en toont het effect van de porositeit op de mechanische eigenschappen van 3D afgedrukt hydrogel steigers in gesimuleerde lichaam voorwaarden. CNCs hier, gebruikt werden eerder gemeld door ons cytocompatible en niet-toxisch (dat wil zeggen, celgroei na 15 dagen incubatie was bevestigd30). Bovendien, steigers bereid via freeze-drying met behulp van de dezelfde CNCs, natriumalginaat en gelatine toonde hoge poreusheid, hoge opname van fosfaat buffer zoutoplossing en cytocompatibility richting mesenchymale stamcellen5. Het doel van dit werk is om aan te tonen de hydrogel inkt verwerking, 3D printen van poreuze steigers en het testen van de compressie. Schema's van de route van de verwerking is afgebeeld in Figuur 1.

<table><tbody><tr><td>60 mL spuit</td><td>Structur3D Printing</td><td></td><td></td></tr><tr><td>Alginezuur natriumzout</td><td>Sigma-Aldrich</td><td>9005-38-3</td><td></td></tr><tr><td>Watervrij calciumchloride</td><td>Sigma-Aldrich</td><td>10043-52-4</td><td></td></tr><tr><td>Klemmen, driepoots, Talon</td><td>VWR</td><td>241-0404</td><td>102 mm, Dubbelverstelbare klem, groot, klemverlenging 127 mm</td></tr><tr><td>Cura 2.4.0</td><td>Ultimaker</td><td></td><td>Gratis slicersoftware</td></tr><tr><td>Discov3ry Complete</td><td>Structur3D Printing</td><td></td><td>Ultimaker 2+ 3D-printer geïntegreerd met Discov3ry pasta-extruder</td></tr><tr><td>Gelatine uit runderhuid</td><td>Sigma-Aldrich</td><td>9000-70-8</td><td></td></tr><tr><td>Glutaraldehyde oplossing 50 wt. % in H2O</td><td>Sigma-Aldrich</td><td>111-30-8</td><td></td></tr><tr><td>homogenisator</td><td>SPX</td><td>APV-2000</td><td></td></tr><tr><td>Instron 5960</td><td>Instron</td><td></td><td>Instron 5960, Biopuls Bath, 100 N belastingcel, 37 &deg;C,</td></tr><tr><td>Physica MCR 301 reometer</td><td>Anton Paar</td><td></td><td>CP25-2-SN7617, opening 0,05 mm, 25 &deg;C</td></tr><tr><td>Sorvall Lynx 6000 centrifuge</td><td>AB Ninolab</td><td>s/n 41881692</td><td>F12-rotor (6x500 ml)</td></tr><tr><td>roestvrijstalen spuitmond</td><td>Structur3D Printing</td><td></td><td>800, 600 en 400 &micro;m</td></tr><tr><td>thingsinverse</td><td>MakerBot's</td><td></td><td>&nbsp;delen en downloaden van 3D-printbare dingen in de vorm van STL-bestanden</td></tr><tr><td>ultrasonische behandeling</td><td>Qsonica, LLC</td><td>Q500</td><td></td></tr><tr><td>Stamfragmenten zonder bast</td><td>Gewone spar (Picea abies)</td><td></td><td>droogstofgehalte van 50&ndash;55%</td></tr></tbody></table>

3d afgedrukt poreuze cellulose nanocomposietmaterialen hydrogel steigers

3D Printed Porous Cellulose Nanocomposite Hydrogel Scaffolds

Dit werk toont het gebruik van driedimensionale (3D) afdrukken op het produceren van poreuze kubieke steigers met cellulose nanocomposietmaterialen hydrogel inkt, met gecontroleerde poriënstructuur en mechanische eigenschappen. Cellulose nanokristallen (CNCs, 69.62 wt %) gebaseerde hydrogel inkt met matrix (natriumalginaat en gelatine) werd ontwikkeld en 3D op steigers met uniforme en kleurovergang poriënstructuur (110-1100 µm) gedrukt. De steigers toonde compressie modulus in het bereik van 0.20-0,45 gesimuleerd MPa wanneer getest omstandigheden in vivo (in gedistilleerd water bij 37 ° C). De porie-grootte en de compressie modulus van de 3D steigers die gepaard gaan met de eisen die nodig zijn voor kraakbeen regeneratie toepassingen. Dit werk toont aan dat de consistentie van de inkt kan worden gecontroleerd door de concentratie van de precursoren en porositeit kan worden gecontroleerd door het 3D afdrukproces en beide van deze factoren bepaalt in ruil daarvoor de mechanische eigenschappen van het 3D afgedrukt poreuze hydrogel steiger. Dit proces-methode kan daarom worden gebruikt om fabriceren structureel en qua samenstelling aangepaste steigers volgens de specifieke behoeften van patiënten.

CNCs gebaseerd nanocomposietmaterialen hydrogel inkt toont een sterke niet-Newtoniaanse schuintrekken uitdunnen van gedrag (Figuur 2een). De schijnbare viscositeit van 1.55 × 105 Pa.s met een lage schuintrekken snelheid (0,001 s-1) daalt door vijf Ordes van grootte een waarde van 22.60 Pa.s met een snelheid van de afschuiving van 50 s-1 (≈50 s-1 wordt een typische schuintrekken tarief ervaren tijdens 3D printen)31...

De drie essentiële stappen van dit protocol zijn i) ontwikkeling van de juiste samenstelling en consistentie van de cellulose hydrogel inkt, ii) 3D printen van steigers in diverse poriën structuren met trouw van goede vorm en de afmetingen en de iii) demonstratie van de mechanische eigenschappen in gesimuleerde lichaam voorwaarden voor regeneratie van het kraakbeen.

3D afgedrukt poreuze Cellulose nanocomposietmaterialen Hydrogel steigers

This work demonstrates the use of three-dimensional (3D) printing to produce porous cubic scaffolds using cellulose nanocomposite hydrogel ink, with ...

Dit is het eerste rapport over 3D geprinte nanocellulose hydrogel steigers waar we een gradiënt porie structuur en mechanische eigenschappen om natuurlijke structuren na te bootsen als kraakbeen. De twee belangrijkste voordelen van het gebruik van 3D-printtechnieken zijn maatwerk en ontwerpvrijheid. Dat opent een onbeperkte mogelijkheid om nieuwe en onontgonnen geometrische ontwerpen te fabriceren.Dit protocol is gebruiksvriendelijk en nieuwkomers kunnen de resultaten eenvoudig reproduceren. De keuze van de snijsoftware en de spuitbeweging hebben een aanzienlijke impact op het eindproduct. Om te beginnen, bereid 40 milliliter hydrogel inkt door het mengen van 11% in gewicht CNC, 6% in gewicht natriumalginaat, en 12% in gewicht gelatine in een container.Verwarm het mengsel tot 40 graden Celsius en meng met een spatel tot een gladde pasta is verkregen. Breng het mengsel in een spuit van 60 milliliter. Vervolgens, met behulp van een mechanische klem, geef het mengsel door een reeks sproeiers met verschillende diameters in een andere 60-milliliter spuit.Herhaal het proces totdat soepel geëxtrudeerde filamenten van hydrogelinkt zijn verkregen. Vercentrifugeer de spuit gevuld met de hydrogelinkt op 4.000 keer g om gevangen lucht te verwijderen. Selecteer op de SD-kaart de opgeslagen bestanden voor uniforme porositeitssteigers en begin met afdrukken.Pas indien nodig de snelheid en de stroomsnelheid dienovereenkomstig aan. Om de steiger te kruisen nadat de 3D-print is voltooid, voeg voorzichtig druppels van 3% in gewicht calciumchlorideoplossing toe aan het schavot totdat het volledig nat wordt. Wacht vijf minuten.Breng het schavot zeer zorgvuldig van het printerbed naar een 50-milliliter container gevuld met 3% van het gewicht calciumchloride oplossing. Laat het 's nachts. Was grondig met gedestilleerd water en breng de steiger over op een 50-milliliter container gevuld met 3% van het gewicht glutaraldehyde oplossing.Laat het 's nachts. Was grondig en bewaar de 3D-geprinte steiger in gedestilleerd water. Voor compressietesten vult u de container met een dompelcompressiebasisplaat met twee liter water en start u met het verwarmingssysteem tot 37 graden Celsius.Initialiseer Bluehill Universal Software en stel de testmethode in. Selecteer de geometrie van rechthoekige exemplaren en kies de optie om afmetingen in te voeren voordat u elk monster test. Stel de spanningssnelheid in op twee millimeter per minuut en eindresultaat als 80% drukspanning samen met kracht van 90 newton.Selecteer in de sectie Meting de optie Kracht, verplaatsing, drukspanning en drukdruk. Kies de optie om gegevens te exporteren als tekstbestanden voor toekomstige plotten. Stel het nuluitbreidingspunt in met behulp van de jog-besturingselementen om de kruiskopplaat zo dicht mogelijk bij de basisplaat te laten zakken.Meet en noteert de afmetingen van de te testen monsters. Wanneer de watertemperatuur 37 graden Celsius bereikt, plaatst u het monster op de bodemplaat. Beveilig het monster door de kruiskopplaat te verplaatsen zodat het monster begint aan te raken.Verplaats het waterbad omhoog zodat de platen met het monster ertussen in worden ondergedompeld in water. Voer de naam en afmetingen van het monster in en start de test. Nadat de test is voltooid, eerst het waterbad naar beneden, en dan verhogen de kruiskop plaat.Verwijder het monster en de eventuele stukken, maak beide platen schoon en laad een nieuw monster. Nadat alle monsters zijn getest, exporteer je de ruwe gegevens. Plot comprimerende stress versus comprimerende stam curven, en bepalen van de comprimerende tangent modulus bij stam waarden van een tot 5%en 25 tot 30%CNCs-gebaseerde nanocomposiet hydrogel inkt toont een sterke niet-Newtoniaanse shear dunner gedrag met een vijf orde van grootte daling van de schijnbare viscositeit.De hydrogel inkt vertoont een visco-elastisch vast gedrag, als de opslag modulus is een orde van grootte groter dan het verlies modulus bij lage shear stress. Bij lage spanningspercentages van één tot 5% is de samendrukkingsmodulus vergelijkbaar voor alle soorten poreuze steigers in vergelijking met het referentiesteiger zonder poreusheid, waaruit blijkt dat de elastische aard van de hydrogelinkt zelfs in aanwezigheid van de macropores behouden blijft. Echter, bij hoge stamsnelheden van 25 tot 30%wordt de hoogste modulus verkregen voor het referentiesteiger zonder poreusheid.Zodra de poriegrootte toeneemt, neemt de modulus af als gevolg van de afname van de dichtheid, wat wijst op de verwachte relatie tussen de porositeit van de steigers en de bijbehorende mechanische eigenschappen. Bovendien neemt de comprimerende modulus van de 3D hydrogel steigers toe naarmate de compressiesnelheid toeneemt, waardoor de viscoelasticiteit van natuurlijke kraakbeenweefsels wordt tentoongesteld en nabootst. De homogene en de continue stroom van de inkt tijdens 3D-printen zijn de belangrijkste dingen.Deze methode zal worden gebruikt door onderzoekers uit te breiden naar andere toepassingsgebieden met behulp van nanocellulose hydrogel als een 3D-printbaar platform. We hebben bijvoorbeeld al op nanocellulose gebaseerde hybriden ontwikkeld voor gecontroleerde afgifte van geneesmiddelen volgens dezelfde procedure.

3d-printed-porous-cellulose-nanocomposite-hydrogel-scaffolds

Research

JoVE Journal

Bioengineering

Bio-engineering

Een bioprinter werd gebruikt om gevormde hydrogelen gebaseerd op een offer mal maken. De poloxamer mal werd opgevuld met een tweede hydrogel en vervolgens geëlueerd, waardoor holtes die gevuld waren met een derde hydrogel. Deze methode maakt gebruik van snelle elutie en goede bedrukbaarheid van poloxameer om complexe architecturen uit biopolymeren genereren.

Afdrukken warmteresponsieve Reverse Mallen voor de schepping van Patterned Hydrogelen Twee-component voor 3D Cell Culture

Een Cartesische bioprinter werd ontworpen en gemaakt om multi-materiaal depositie in nauwkeurige, reproduceerbare geometrieën mogelijk te maken, terwijl ook controle van omgevingsfactoren wordt toegestaan. Met behulp van de driedimensionale bioprinter kunnen complexe en levensvatbare constructies worden afgedrukt en gemakkelijk worden gereproduceerd.

Levensvatbaarheid van Bioprinted Cellular constructen met behulp van een drie Dispenser cartesiaanse Printer

We beschrijven de fabricage van microgepatternde hydrogelvellen met behulp van een eenvoudig proces, dat kan worden geassembleerd en gemanipuleerd in een zelfstandige vorm. Met behulp van deze modulaire hydrogelvellen kan een eenvoudig macro-geschaald 3D-celkweeksysteem worden gegenereerd met een gecontroleerde cellulaire micro-omgeving.

Bouw van modulaire Hydrogel Sheets voor micropatterned Macro-schaal 3D Cellular Architecture

Dit manuscript presenteert een gedetailleerd protocol voor de fabricage van een opkomend driedimensionaal hepatocytencultuurplatform, het omgekeerde colloïdale kristal-scaffold, en de bijbehorende technieken om hepatocytengedrag te beoordelen. De grootte-controleerbare poriën, interconnectiviteit en de mogelijkheid om extracellulaire matrixeiwitten te binden aan het poly(ethyleenglycol) (PEG)-scaffold verbeteren de prestaties van Huh-7.5-cellen.

Fabricage van Inverted Colloïdaal Crystal Poly (ethyleen glycol) Steiger: Een drie-dimensionale Cultuur van de Cel Platform for Liver Tissue Engineering

Gepresenteerd hier is een eenvoudig te gebruiken, Core/shell, driedimensionale bioprinten set-up voor één stap fabricage van holle steigers, geschikt voor weefsel engineering van vasculaire en andere buisvormige structuren.

Kern/shell druk steigers voor weefsel engineering van buisvormige constructies

Dit protocol benadrukt een methode om snel de biocompatibiliteit van een kristallijne nanocellulose (CNC) / agarose composiet hydrogel biomateriaal inkt met muis beenmerg-afgeleide mestcellen te beoordelen in termen van cel levensvatbaarheid en fenotypische expressie van de celoppervlak receptoren, Kit (CD117) en hoge affiniteit IgE receptor (FcεRI).

Fabricage van een kristallijne nanocellulose ingebedde agarose biomateriaal inkt voor beenmerg-afgeleide mestcelkweek

Microgelstaven met complementaire reactieve groepen worden geproduceerd via microfluïdica met het vermogen om in waterige oplossing met elkaar te verbinden. De anisometrische microgels binden en verbinden zich tot stabiele constructies met grotere poriën in vergelijking met op bolvormige systemen gebaseerde systemen. Microgels gemodificeerd met GRGDS-PC vormen macroporeuze 3D-constructies die kunnen worden gebruikt voor celkweek.

Onderling verbonden macroporeuze 3D-steigers van Microgel-staven

Dit artikel beschrijft protocollen voor high-throughput gelatine methacryloyl microgel fabricage met behulp van microfluïdische apparaten, het omzetten van microgels in resususpensable poeder (micro-aerogels), de chemische assemblage van microgels om granulaire hydrogel scaffolds te vormen, en het ontwikkelen van granulaire hydrogel bioinks met behoud van microporositeit voor 3D bioprinting.

Gelatine Methacryloyl Granular Hydrogel Scaffolds: High-throughput Microgel Fabrication, Lyophilization, Chemical Assembly, en 3D Bioprinting

Dit werk beschrijft een protocol voor de vrije vorm ingebed 3D-printen van neurale stamcellen in zelfherstellende gloeibare deeltjes-extracellulaire matrixcomposieten. Het protocol maakt het mogelijk om met hoge getrouwheid patronen te maken van onderling verbonden menselijke neurale weefselconstructies.

Microgel-extracellulaire matrixcomposietondersteuning voor het ingebed 3D-printen van menselijke neurale constructies

Deze studie introduceert een nieuw κ-carrageen sub-microgel suspensiebad, dat opmerkelijke omkeerbare jamming-unjamming overgangseigenschappen vertoont. Deze eigenschappen dragen bij aan de opbouw van biomimetische weefsels en organen in ingebedde 3D-bioprinting. Het succesvol printen van hart-/slokdarmachtige weefsels met hoge resolutie en celgroei demonstreert hoogwaardige bioprinting- en tissue engineering-toepassingen.

Ingebedde bioprinting van weefselachtige structuren met behulp van κ-carrageen sub-microgelmedium

Leer hoe je 3D-geprinte nanocellulose hydrogelsteigers maakt met gradiëntporiënstructuren die het natuurlijke kraakbeen nabootsen. Dit gebruiksvriendelijke protocol maakt aanpassing en reproduceerbaar onderzoek mogelijk.

3D afgedrukt poreuze Cellulose nanocomposietmaterialen Hydrogel steigers

Meer video's verkennen