Name: In situ Fotoreologie bewaakt visco-elastische veranderingen in fotoresponsieve polymeernetwerken (Video) | JoVE Journal
Uploaded: 2025-06-20T12:50:00.000+00:00
Duration: 7 min 14 s
Description: Leer in situ fotoreologie om visco-elastische veranderingen in fotoresponsieve polymeernetwerken te monitoren. Deze methode integreert mechanische tests met optische metingen voor dieper inzicht in materiaaleigenschappen.

ai_agent_IP

ai_agent

maintenance

instantTrialDurationMinutes

isBiopharma

enableNewMyJoveSectionDesign

educationFeatures

seoMetaApi

ai_copilot_institution_blacklist

ai_chat_institution_blacklist

freeAccessWindow

ssoRoleCapture

scheduledMaintenanceBanner

joveLabsFeatures

disable_autoplay_for_bots

extended_trial_duration

5 minutes

<ol><li>Schmidt, L. E., Leterrier, Y., Vesin, J. M., Wilhelm, M., Månson, J. A. E. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Photorheology+of+Fast+UV-Curing+Multifunctional+Acrylates%5BTitle%5D)+AND+%22Macromol+Mater+Eng%22%5BJournal%5D)">Photorheology of Fast UV-Curing Multifunctional Acrylates.</a> Macromol Mater Eng. 290 (11), 1115-1124 (2005).</li>
<li>Sun, G., Wu, X., Liu, R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((A+Comprehensive+Investigation+of+Acrylates+Photopolymerization+Shrinkage+Stress+from+Micro+and+Macro+Perspectives+by+Real+Time+MIR-Photo-Rheology%5BTitle%5D)+AND+%22Prog+Org+Coat%22%5BJournal%5D)">A Comprehensive Investigation of Acrylates Photopolymerization Shrinkage Stress from Micro and Macro Perspectives by Real Time MIR-Photo-Rheology.</a> Prog Org Coat. 155, 106229(2021).</li>
<li>Corder, R. D., Dudick, S. C., Bara, J. E., Khan, S. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Photorheology+and+Gelation+during+Polymerization+of+Coordinated+Ionic+Liquids%5BTitle%5D)+AND+%22ACS+Appl+Polym+Mater%22%5BJournal%5D)">Photorheology and Gelation during Polymerization of Coordinated Ionic Liquids.</a> ACS Appl Polym Mater. 2 (6), 2397-2405 (2020).</li>
<li>Miller, T. F. I., Wang, Z. G., Coates, G. W., Balsara, N. P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Designing+Polymer+Electrolytes+for+Safe+and+High+Capacity+Rechargeable+Lithium+Batteries%5BTitle%5D)+AND+%22Acc+Chem+Res%22%5BJournal%5D)">Designing Polymer Electrolytes for Safe and High Capacity Rechargeable Lithium Batteries.</a> Acc Chem Res. 50 (3), 590-593 (2017).</li>
<li>Paren, B. A., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Superionic+Li-Ion+Transport+in+a+Single-Ion+Conducting+Polymer+Blend+Electrolyte%5BTitle%5D)+AND+%22Macromolecules%22%5BJournal%5D)">Superionic Li-Ion Transport in a Single-Ion Conducting Polymer Blend Electrolyte.</a> Macromolecules. 55 (11), 4692-4702 (2022).</li>
<li>Wicaksono, G., Djordjevic, I., Shah, A. H., Steele, T. W. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Photorheology+of+Bioadhesive+Dendrimer+Polycaprolactone+Composites%5BTitle%5D)+AND+%22Polym+Test%22%5BJournal%5D)">Photorheology of Bioadhesive Dendrimer Polycaprolactone Composites.</a> Polym Test. 80, 106099(2019).</li>
<li>Khan, S. A., Plitz, I. M., Frantz, R. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((In+Situ+Technique+for+Monitoring+the+Gelation+of+UV+Curable+Polymers%5BTitle%5D)+AND+%22Rheol+Acta%22%5BJournal%5D)">In Situ Technique for Monitoring the Gelation of UV Curable Polymers.</a> Rheol Acta. 31 (2), 151-160 (1992).</li>
<li>Gorsche, C., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Real+Time-NIR%2FMIR-Photorheology%3A+A+Versatile+Tool+for+the+in+Situ+Characterization+of+Photopolymerization+Reactions%5BTitle%5D)+AND+%22Anal+Chem%22%5BJournal%5D)">Real Time-NIR/MIR-Photorheology: A Versatile Tool for the in Situ Characterization of Photopolymerization Reactions.</a> Anal Chem. 89 (9), 4958-4968 (2017).</li>
<li>Piguet-Ruinet, F., Love, B. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Dynamic+Photorheological+Analysis+of+Photopolymerizable+Urethane+Dimethacrylate+Resins+with+Varying+Diluent+Content+and+Light+Fluence%5BTitle%5D)+AND+%22J+Appl+Polym+Sci%22%5BJournal%5D)">Dynamic Photorheological Analysis of Photopolymerizable Urethane Dimethacrylate Resins with Varying Diluent Content and Light Fluence.</a> J Appl Polym Sci. 107 (3), 1523-1529 (2008).</li>
<li>Švajdlenková, H., Šauša, O., Peer, G., Gorsche, C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((In+Situ+Investigation+of+the+Kinetics+and+Microstructure+during+Photopolymerization+by+Positron+Annihilation+Technique+and+NIR-Photorheology%5BTitle%5D)+AND+%22RSC+Adv%22%5BJournal%5D)">In Situ Investigation of the Kinetics and Microstructure during Photopolymerization by Positron Annihilation Technique and NIR-Photorheology.</a> RSC Adv. 8 (65), 37085-37091 (2018).</li>
<li>Thijssen, Q., Ortega, A. J., Vieira, R. P., Van Vlierberghe, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Radical+Inhibition+in+Tomographic+Volumetric+3D+Printing+for+Thiol-Ene+Photoresists%3A+From+Photorheology+to+Printability%5BTitle%5D)+AND+%22React.+Funct+Polym%22%5BJournal%5D)">Radical Inhibition in Tomographic Volumetric 3D Printing for Thiol-Ene Photoresists: From Photorheology to Printability.</a> React. Funct Polym. 205, 106096(2024).</li>
<li>Fiedler-Higgins, C. I., Cox, L. M., DelRio, F. W., Killgore, J. P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Monitoring+Fast%2C+Voxel-Scale+Cure+Kinetics+via+Sample-Coupled-Resonance+Photorheology%5BTitle%5D)+AND+%22Small+Methods%22%5BJournal%5D)">Monitoring Fast, Voxel-Scale Cure Kinetics via Sample-Coupled-Resonance Photorheology.</a> Small Methods. 3 (2), 1800275(2019).</li>
<li>Coblentz, W. W. <a target="_blank" href="http://scholar.google.com/scholar?hl=en&safe=off&q=author%3aCoblentz%2C+WW+%22Absorption%2C+Reflection%2C+and+Dispersion+Constants+of+Quartz%22">Absorption, Reflection, and Dispersion Constants of Quartz</a>. , U.S. Department of Commerce, Bureau of Standards. (1915).</li>
<li>Ikushima, A. J., Fujiwara, T., Saito, K. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Silica+Glass%3A+A+Material+for+Photonics%5BTitle%5D)+AND+%22J+Appl+Phys%22%5BJournal%5D)">Silica Glass: A Material for Photonics.</a> J Appl Phys. 88 (3), 1201-1213 (2000).</li>
<li>Banerjee, A., Ogale, A. A., Das, C., Mitra, K., Subramanian, C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Temperature+Distribution+in+Different+Materials+Due+to+Short+Pulse+Laser+Irradiation%5BTitle%5D)+AND+%22Heat+Transf+Eng%22%5BJournal%5D)">Temperature Distribution in Different Materials Due to Short Pulse Laser Irradiation.</a> Heat Transf Eng. 26 (8), 41-49 (2005).</li>
<li>Mouzaoui, M., Baudez, J. C., Sauceau, M., Arlabosse, P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((How+to+Avoid+Evaporation+during+Rheological+Measurements+of+Dewatered+Pasty+Sludge+at+High+Temperature%5BTitle%5D)+AND+%22Water+Sci+Technol%22%5BJournal%5D)">How to Avoid Evaporation during Rheological Measurements of Dewatered Pasty Sludge at High Temperature.</a> Water Sci Technol. 79 (8), 1503-1510 (2019).</li>
<li>Chen, T. <a target="_blank" href="http://scholar.google.com/scholar?hl=en&safe=off&q=author%3aChen%2C+T+%22Rheological+Analysis+under+Pressure%22">Rheological Analysis under Pressure</a>. , https://www.tainstruments.com/pdf/literature/RH092.pdf (2025).</li>
<li>Leading in Thermal Analysis, Rheology and Fire Testing. Overcoming Solvent Evaporation/Drying During Rheological Testing on a Rotational Rheometer. , NETZSCH - Analyzing and Testing. 
 <a target="_blank" href="https://analyzing-testing.netzsch.com/en-US/application-literature/overcoming-solvent-evaporation-drying-during-rheological-testing-on-a-rotational-rheometer">https://analyzing-testing.netzsch.com/en-US/application-literature/overcoming-solvent-evaporation-drying-during-rheological-testing-on-a-rotational-rheometer</a> (2025).</li>
<li>Saruwatari, A., Tamate, R., Kokubo, H., Watanabe, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Photohealable+Ion+Gels+Based+on+the+Reversible+Dimerisation+of+Anthracene%5BTitle%5D)+AND+%22Chem+Commun%22%5BJournal%5D)">Photohealable Ion Gels Based on the Reversible Dimerisation of Anthracene.</a> Chem Commun. 54 (95), 13371-13374 (2018).</li>
<li>Günay, K., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((PEG-Anthracene+HydrogelsasanOn-De+Mand+Stiffening+Matrix+To+Study+Mechanobiology%5BTitle%5D)+AND+%22Angew+Chem+Int+Ed+Engl%22%5BJournal%5D)">PEG-Anthracene HydrogelsasanOn-De Mand Stiffening Matrix To Study Mechanobiology.</a> Angew Chem Int Ed Engl. 58 (29), 9912-9916 (2019).</li>
<li>Burroughs, M. C., Schloemer, T. H., Congreve, D. N., Mai, D. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Gelation+Dynamics+during+Photo-Cross-Linking+of+Polymer+Nanocomposite+Hydrogels%5BTitle%5D)+AND+%22ACS+Polym+Au%22%5BJournal%5D)">Gelation Dynamics during Photo-Cross-Linking of Polymer Nanocomposite Hydrogels.</a> ACS Polym Au. 3 (2), 217-227 (2023).</li>
<li>Zheng, Y., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((PEG-Based+Hydrogel+Synthesis+via+the+Photodimerization+of+Anthracene+Groups%5BTitle%5D)+AND+%22Macromolecules%22%5BJournal%5D)">PEG-Based Hydrogel Synthesis via the Photodimerization of Anthracene Groups.</a> Macromolecules. 35 (13), 5228-5234 (2002).</li>
<li>Wells, L., Brook, M., Sheardown, H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Generic%2C+Anthracene-Based+Hydrogel+Crosslinkers+for+Photo-Controllable+Drug+Delivery%5BTitle%5D)+AND+%22Macromol+Biosci%22%5BJournal%5D)">Generic, Anthracene-Based Hydrogel Crosslinkers for Photo-Controllable Drug Delivery.</a> Macromol Biosci. 11 (7), 988-998 (2011).</li>
<li>Truong, V. X., Li, F., Forsythe, J. S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Versatile+Bioorthogonal+Hydrogel+Platform+by+Catalyst-Free+Visible+Light+Initiated+Photodimerization+of+Anthracene%5BTitle%5D)+AND+%22ACS+Macro+Lett%22%5BJournal%5D)">Versatile Bioorthogonal Hydrogel Platform by Catalyst-Free Visible Light Initiated Photodimerization of Anthracene.</a> ACS Macro Lett. 6 (7), 657-662 (2017).</li>
<li>Kislyak, A., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((A+Holistic+Approach+for+Anthracene+Photochemistry+Kinetics%5BTitle%5D)+AND+%22Chem+Eng+J%22%5BJournal%5D)">A Holistic Approach for Anthracene Photochemistry Kinetics.</a> Chem Eng J. 402, 126259(2020).</li>
<li>Wei, K. S., Livingston, R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Reversible+Photodimerization+of+Anthracene+and+Tetracene%5BTitle%5D)+AND+%22Photochem+Photobiol%22%5BJournal%5D)">Reversible Photodimerization of Anthracene and Tetracene.</a> Photochem Photobiol. 6 (3), 229-232 (1967).</li>
<li>Burroughs, M. C., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Light-Responsive+Star+Polymer+Networks+for+Photochemical+Recycling+and+Circular+Manufacturing%5BTitle%5D)+AND+%22Matter%22%5BJournal%5D)">Light-Responsive Star Polymer Networks for Photochemical Recycling and Circular Manufacturing.</a> Matter. , (2025).</li>
<li>Rubinstein, M., Colby, R. <a target="_blank" href="http://scholar.google.com/scholar?hl=en&safe=off&q=author%3aRubinstein%2C+M+%22Polymer+Physics%22">Polymer Physics</a>. , Oxford University Press. (2003).</li>
<li>Intro-Guide-to-DHR. , 
 <a target="_blank" href="https://people.clarkson.edu/~skrishna/Intro-Guide-to-DHR.pdf">https://people.clarkson.edu/~skrishna/Intro-Guide-to-DHR.pdf</a> (2025).</li>
<li>Proper Sample Loading with the Brand New Discovery Hybrid Rheometer. , 
 <a target="_blank" href="https://www.youtube.com/watch?v=yHsGSGo5qos">https://www.youtube.com/watch?v=yHsGSGo5qos</a> (2020).</li>
<li>Tibbitt, M. W., Kloxin, A. M., Anseth, K. S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Modeling+Controlled+Photodegradation+in+Optically+Thick+Hydrogels%5BTitle%5D)+AND+%22J+Polym+Sci+Part+Polym+Chem%22%5BJournal%5D)">Modeling Controlled Photodegradation in Optically Thick Hydrogels.</a> J Polym Sci Part Polym Chem. 51 (9), 1899-1911 (2013).</li>
<li>Chambon, F., Winter, H. H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Linear+Viscoelasticity+at+the+Gel+Point+of+a+Crosslinking+PDMS+with+Imbalanced+Stoichiometry%5BTitle%5D)+AND+%22J+Rheol%22%5BJournal%5D)">Linear Viscoelasticity at the Gel Point of a Crosslinking PDMS with Imbalanced Stoichiometry.</a> J Rheol. 31 (8), 683-697 (1987).</li>
<li>Velankar, S. S., Giles, D. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((How+Do+I+Know+If+My+Phase+Angles+Are+Correct%5BTitle%5D)+AND+%22Rheol+Bull%22%5BJournal%5D)">How Do I Know If My Phase Angles Are Correct.</a> Rheol Bull. 76 (2), 8-20 (2007).</li>
<li>Basics of viscometry | Anton Paar Wiki. , Anton Paar. 
 <a target="_blank" href="https://wiki.anton-paar.com/en/basic-of-viscometry/">https://wiki.anton-paar.com/en/basic-of-viscometry/</a> (2025).</li>
<li>Introduction to Dynamic Mechanical Analysis and its Application to Testing of Polymer Solids - TA Instruments. , 
 <a target="_blank" href="https://www.tainstruments.com/applications-notes/introduction-to-dynamic-mechanical-analysis-and-its-application-to-testing-of-polymer-solids/">https://www.tainstruments.com/applications-notes/introduction-to-dynamic-mechanical-analysis-and-its-application-to-testing-of-polymer-solids/</a> (2025).</li>
<li>Franck, A., Grehlinger, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Benefit+of+Fast+Data+Sampling+during+Rheological+Testing%5BTitle%5D)+AND+%22Proc+XIVth+Int+Congr+on+Rheology%22%5BJournal%5D)">Benefit of Fast Data Sampling during Rheological Testing.</a> Proc XIVth Int Congr on Rheology. , RE29-1-RE29-4 (2004).</li>
<li>Grehlinger, M. <a target="_blank" href="http://scholar.google.com/scholar?hl=en&safe=off&q=author%3aGrehlinger%2C+M+%22A+Technique+for+Rapid+Acquisition+of+Rheological+Data%2C+and+Its+Application+to+Fast+Curing+Systems%22">A Technique for Rapid Acquisition of Rheological Data, and Its Application to Fast Curing Systems</a>. , https://www.tainstruments.com/pdf/literature/RH084_FDA_and_UV_curing.pdf (2025).</li>
<li>Walls, H. J., Caines, S. B., Sanchez, A. M., Khan, S. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Yield+Stress+and+Wall+Slip+Phenomena+in+Colloidal+Silica+Gels%5BTitle%5D)+AND+%22J+Rheol%22%5BJournal%5D)">Yield Stress and Wall Slip Phenomena in Colloidal Silica Gels.</a> J Rheol. 47 (4), 847-868 (2003).</li>
<li>Barnes, H. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((A+Review+of+the+Slip+%28Wall+Depletion%29+of+Polymer+Solutions%2C+Emulsions+and+Particle+Suspensions+in+Viscometers%3A+Its+Cause%2C+Character%2C+and+Cure%5BTitle%5D)+AND+%22J+Non-Newton+Fluid+Mech%22%5BJournal%5D)">A Review of the Slip (Wall Depletion) of Polymer Solutions, Emulsions and Particle Suspensions in Viscometers: Its Cause, Character, and Cure.</a> J Non-Newton Fluid Mech. 56 (3), 221-251 (1995).</li>
</ol>

<table><tbody><tr><td>25 mm diameter aluminum parallel plate geometry</td><td>TA Instruments</td><td>523250.937</td><td>Disposable</td></tr><tr><td>3 mm hex wrench</td><td>TA Instruments</td><td>578910.001</td><td>Gebruikt om de Upper Peltier Plate te installeren</td></tr><tr><td>365 nm LED</td><td>ThorLabs</td><td>M365LP1-C2</td><td>Met collimaterende lens</td></tr><tr><td>Acrylic sheets</td><td>McMaster-Carr</td><td>8589K923</td><td>Beschermt de gebruiker tegen UV-bestraling</td></tr><tr><td>Anthracene-terminated star poly(ethylene glycol) (40 kg/mol, 8 arms)</td><td>Made in-house</td><td>BMWR12 en BMWR14</td><td>Synthese beschreven in Burroughs et al. 2022</td></tr><tr><td>Heat spreader wrench</td><td>TA Instruments</td><td>534522.001</td><td>Gebruikt om de geometrie te installeren</td></tr><tr><td>LED Driver</td><td>ThorLabs</td><td>LEDD1B</td><td>Controleert de stroom op de LED</td></tr><tr><td>Mineral oil</td><td>Fisher chemical</td><td>O121-1</td><td>Controle van verdamping</td></tr><tr><td>Optical Post Assemblies</td><td>ThorLabs</td><td>Various</td><td>SPT2/M (voor het houden van 365 nm), TR6 (6" lange 1/2" diameter post), en RA90 (rechthoekige klem)</td></tr><tr><td>Optical Power and Energy Meter</td><td>ThorLabs</td><td>PM100D</td><td>Meet lichtintensiteit</td></tr><tr><td>Optics Plate Accessory</td><td>TA Instruments</td><td>546800.901</td><td>Maakt gelijktijdige bestraling en meting mogelijk</td></tr><tr><td>Photodiode Power Sensor, UV-Extended</td><td>ThorLabs</td><td>S120VC</td><td>Meet 200-1100 nm</td></tr><tr><td>Quartz disc (76.2 mm diameter, 1.57 mm thick)</td><td>Technical Glass Products, Inc.</td><td>3X0.062</td><td>Gebruikt in de Optics Plate Accessory; laat UV-licht door</td></tr><tr><td>Rheometer</td><td>TA Instruments</td><td>DHR 30</td><td>Voert reologische metingen uit</td></tr><tr><td>Upper Peltier Disposable Geometry Adapter</td><td>TA Instruments</td><td>534525.941</td><td>Houdt de wegwerpbare parallel plate geometrie vast</td></tr><tr><td>Upper Peltier Draft Cover</td><td>TA Instruments</td><td>534506.001</td><td>Jas voor thermische controle en lichtbescherming</td></tr><tr><td>Upper Peltier Plate</td><td>TA Instruments</td><td>534509.902</td><td>Temperatuurregeling. Wordt geleverd met zeskantsleutel en hittespreider sleutel voor installatie</td></tr></tbody></table>

in situ fotoreologie bewaakt visco-elastische veranderingen in fotoresponsieve polymeernetwerken

In situ Photo-rheology Monitors Viscoelastic Changes in Photo-responsive Polymer Networks

In situ Fotoreologie bewaakt visco-elastische veranderingen in fotoresponsieve polymeernetwerken

In situ photo-rheology is a powerful technique for characterizing the evolution of photo-responsive materials during irradiation. This technique enables ...

in-situ-photo-rheology-monitors-viscoelastic-changes-photo-responsive

Research

JoVE Journal

Engineering

Techniek

Milieuvriendelijke gecontroleerde Microtensile Testen van mechanisch-adaptieve nanocomposieten voor<em&gt; Ex vivo</em&gt; Karakterisering

Deeltjesvolg-microreologie onderzoekt de viscoëlasticiteit van materialen. Hier wordt de techniek gebruikt om de viscoëlasticiteit, creep-compliantie en effectieve crosslinking-rollen van verschillende matrixcomponenten van een bacteriële biofilm te bepalen. De matrix bestaat uit polymere stoffen die door de bacteriën worden uitgescheiden en de componenten bepalen de structuur en mechanische eigenschappen van de biofilm.

In Situ Mapping van de mechanische eigenschappen van Biofilms per Particle volgen Microreologie

Hier presenteren we een betrouwbare methode om de incorporatie van nanodeeltjes in een polymeer gastheermatrix te monitoren via zwellingscapsulering. We laten zien dat de oppervlakteconcentratie van cadmiumselenide kwantumdots nauwkeurig kan worden gevisualiseerd door middel van dwarsdoorsnede fluorescentiebeeldvorming.

Uitgebreide analyse van de samenstelling van nanodeeltjes-polymeer Composites Met behulp van Direct Fluorescence Imaging

Semiflexible polymeren weer unieke mechanische eigenschappen die uitgebreid door levende systemen worden toegepast. Systematische studies over biopolymeren zijn echter beperkt omdat eigenschappen zoals polymeer rigiditeit niet toegankelijk zijn. Dit manuscript wordt beschreven hoe is deze beperking omzeild door programmeerbare DNA nanobuisjes, waardoor experimentele studies over de gevolgen van de stijfheid van de gloeidraad.

DNA Nanotubes als een veelzijdig instrument om te studeren van Semiflexible polymeren

Een protocol voor de analyse van gelen gevormd uit de opto-elektronische geconjugeerd polymeer poly(3-hexylthiophene-2,5-diyl) (P3HT) met behulp van kleine en ultrakleine hoek neutronen verstrooiing in zowel de aanwezigheid en de afwezigheid van verlichting wordt gepresenteerd.

Monitoring van de gevolgen van de verlichting op de structuur van geconjugeerd polymeer Gels met behulp van Neutron Scattering

We laten zien dat de fabricage en het gebruik van een microfluidic apparaat waarmee meerdere deeltje bijhouden microrheology afmetingen om te bestuderen van de reologische effecten van herhaalde fase-overgangen op zachte materie.

Combinatie van Microfluidics en Microrheology om te bepalen de Rheologische eigenschappen van zachte materie tijdens herhaalde fase-overgangen

Hier presenteren we de protocollen van differentiaal-detectie analyses van time-resolved infrarood Vibrationele spectroscopie en elektron diffractie waarmee opmerkingen van de vervormingen van de lokale structuren rond photoexcited moleculen in een in kolomvorm vloeibare kristallen, het geven van een atomaire perspectief op de relatie tussen de structuur en de dynamiek van dit photoactive materiaal.

Nieuwe technieken voor het observeren van structurele dynamica van Photoresponsive vloeibare kristallen

We presenteren een hoge doorvoer tractiekracht assay gefabriceerd met silicone rubber (PDMS). Deze nieuwe assay is geschikt voor het bestuderen van fysieke veranderingen in cel contractiliteit tijdens verschillende biologische en biomedische processen en ziekten. We demonstreren het nut van deze methode door het meten van een TGF-β afhankelijke toename van de contractiliteit tijdens de epitheel-naar-mesenchymale overgang.

Hoge doorvoer Tractiekracht microscopie met behulp van PDM'S onthult dosisafhankelijke effecten van het transformeren van groei factor-β op de epitheliale-naar-mesenchymale overgang

Dit protocol demonstreert de voorbereiding van een foto orheologisch materiaal dat een vaste fase vertoont, verschillende vloeibare kristallijne fasen en een isotrope vloeistoffase door de temperatuur te verhogen. Gepresenteerd hier zijn methoden voor het meten van de structuur-viscoelasticiteit relatie van het materiaal.

Hoog contrast en snelle Photorheologische omschakeling van een twist-Bend Nematic Liquid Crystal

Dit protocol beschrijft de toepassing van atoomkrachtmicroscopie en infraroodspectroscopie op nanoschaal om de prestaties van fotothermische infraroodspectroscopie op nanoschaal te evalueren bij de karakterisering van driedimensionale multipolymere monsters.

Vooruitgang in infraroodspectroscopie op nanoschaal om meerfasige polymere systemen te onderzoeken

Leer in situ fotoreologie om visco-elastische veranderingen in fotoresponsieve polymeernetwerken te monitoren. Deze methode integreert mechanische tests met optische metingen voor dieper inzicht in materiaaleigenschappen.

In situ Fotoreologie bewaakt visco-elastische veranderingen in fotoresponsieve polymeernetwerken

Meer video's verkennen