Name: Gyroid Nickel Nanoestruturas de dibloco copolímero supramoléculas (Vídeo) | JoVE Journal
Uploaded: 2014-04-28T13:00:00.000+00:00
Duration: 8 min 40 s
Description: Aprenda a preparar nanofoams de níquel ordenados a partir de complexos supramoleculares de copolímeros de bloco. Este método utiliza deposição eletrolítica e pirólise para criar estruturas nanoporosas com morfologia giroide inversa.

ai_agent_IP

ai_agent

maintenance

instantTrialDurationMinutes

isBiopharma

enableNewMyJoveSectionDesign

educationFeatures

seoMetaApi

ai_copilot_institution_blacklist

ai_chat_institution_blacklist

freeAccessWindow

ssoRoleCapture

scheduledMaintenanceBanner

joveLabsFeatures

disable_autoplay_for_bots

extended_trial_duration

5 minutes

Reconhecemos o apoio financeiro do Instituto de Zernike de Materiais Avançados, da Universidade de Groningen.

1. Preparação e Caracterização de PS-b-P4VP (PDP) Complexos com duplo Gyroid Morfologia <ol><li> Pesar de poliestireno-bloco-poli (4-vinilpiridina) (PS-b-P4VP) e pentadecilfenol (PDP, Mr = 304,51 g / mol). De modo a obter a morfologia gyroid, seleccionar cuidadosamente a quantidade de PDP deve ser (a fracção de peso de P4VP (PDP) bloco (f P4VP (PDP)) deve ser ca. 0,6 de acordo com o diagrama de fases de copolímeros em dibloco lineares AB). Normalmente, 0,15-0,2 g de um PS-b-P4VP leva a PS-b-P4VP (PDP), os filmes de 50-100 mm de espessura (uma vez que o diâmetro de um prato Petri usado no passo 1.3 é 5-6 cm). Calcular a quantidade de PDP de acordo com as seguintes equações: <img alt="Equação 1" src="/files/ftp_upload/50673/50673eq1.jpg" /> <img alt="Equação 2" src="/files/ftp_upload/50673/50673eq2.jpg" /> <img alt="Equação 3" src="/files/ftp_upload/50673/50673eq3.jpg" /><br/&gt; <img alt="Equação 4" src="/files/ftp_upload/50673/50673eq4.jpg" /></li><li> Dissolver PS-b-P4VP e PDP em clorofórmio e mexa por um par de horas a temperatura ambiente. Manter a concentração de polímero inferior a 2% em peso, para assegurar a formação de um complexo homogéneo. </li><li> Despeje a solução numa placa de Petri de vidro. </li><li> Colocar a cápsula num ambiente saturado de clorofórmio. </li><li> Após cerca de uma semana, retire a placa de Petri. Um filme do complexo supramolecular é formado. </li><li> Seca-se a película no vácuo a 30 ° C durante a noite. </li><li> Coloque o filme em um recipiente especialmente projetado, retire o ar do recipiente e, em seguida, preenchê-lo com nitrogênio. Recozer o filme durante 4 dias na estufa a 120 ° C sob atmosfera de N 2, com 1 bar de pressurização. </li><li> Cortar o pequeno pedaço da película, incorporar em epóxi e curá-la durante a noite a 40 ° C. </li><li> Micrótomo a amostra com uma espessura de cerca de 80 nm, usando uma faca de diamante, à temperatura ambiente. The seção microtomed irá flutuar na água. Buscá-las e colocar grades de Cu. </li><li> Coloque as grades contendo os cortes microtomed em uma jarra com iodo. Após 45 minutos as amostras são e pronto para microscopia eletrônica de transmissão. </li><li> Insira as grades de Cu com cortes corados no microscópio eletrônico de transmissão operando com uma tensão de aceleração de 120 kV e imagem da amostra. </li><li> Insira a parte do filme (obtido após o passo 1.7) no suporte da amostra para pequenas ângulo de espalhamento de raios-X e corrigi-lo com uma fita Kapton. Coloque o suporte de amostra preparada para a máquina de SAXS. Abra o obturador de raios-X e adquirir o padrão de espalhamento 2D. Integrar o padrão de 2D obtido e analisar a posição dos picos de padrão de 1D. </li></ol> 2. Geração e caracterização da estrutura porosa <ol><li> Coloque a peça da película (obtido após o passo 1.7) em etanol e mantê-lo durante três dias. </li><li> Seca-se a amostra. </li><li> Préaparar as amostras para um medições H RMN. Dissolve-se pó de PDP, PS-b-P4VP pó, PS-b-P4VP (PDP) (depois do passo 1.7), e porosa filme complexo supramolecular (após o passo 2.2) em CDCl3. Ficha 1 H espectros RMN à temperatura ambiente. </li><li> Analise PS-b-P4VP pó, complexo supramolecular PS-b-P4VP (PDP) (depois do passo 1.7), e película porosa (após o passo 2.2) por meio de calorimetria diferencial de varrimento. Usar um modo modulado com uma velocidade de aquecimento / arrefecimento de 1 ° C / min, uma amplitude de oscilação de 0,5 ° C, e um período de oscilação de 60 seg. Equilibrar as amostras à temperatura de -30 ° C, aquecer até 180 ° C, arrefecer a -30 ° C, e em seguida aquecer de novo a 180 ° C. Usar os dados a partir do segundo ciclo de aquecimento para a análise. </li><li> Desgaseificar a amostra porosa (após o passo 2.2) durante 8 horas à temperatura ambiente e durante 18 horas a 70 ° C e realizar medições de adsorção de azoto a 77 K. </li><li> Use o software apropriado (por exemplo, WinADP) e modelos para analisar as isotermas obtidas. </li><li> Seca-se a amostra porosa (após o passo 2.2) a 50 ° C durante 8 horas e desgaseifica-la à temperatura ambiente e à pressão de 0,5 Pa, durante 2 horas. </li><li> Realizar porosimetria de mercúrio. </li></ol> 3. Inserção de níquel no modelo Polymer <ol><li> Pesar de cloreto de estanho (SnCl2, Mr = 189,60 g / mol) e preparar uma solução aquosa (0,1 M SnCl 2 / HCl 0,1 M, 1,896 g de SnCl 2, 0,8 ml de HCl, e 100 ml de H2O). Colocar a solução em um dia para o outro agitador para garantir a dissolução completa de SnCl2. </li><li> Pesar o cloreto de paládio (PdCl2, Mr = 177,33 g / mol) e preparar uma solução aquosa (0,0014 M PdCl2 / 0,25 M de HCl; 0,025 g PdCl 2, 2 mL de HCl e 100 mL de H 2 O). </li><li> Prepare a parte 1 do banho de níquel: pesar 6,78 g de sulfato de níquel hexahidratado (NISO 4 • 6H 2 O, M r = 2620,85 g / mol) e 2 g de citrato de sódio (Na 3 C 6 H 5 O 7, Mr = 258,06 g / mol) e dissolvê-los em 80 ml ​​de água. Adicionar 828 ul de 85% de ácido láctico (C 3 H 6 O 3, M r = 90,08 g / mol). </li><li> Prepare a parte 2 do banho níquel: peso fora 0,2 g complexo dimetilamina borano ((CH 3) 2 NHBH 3, M r = 58,92 g / mol) e dissolvê-la em 20 ml de água. Complexo dimetilamina Borane deve ser tratado em um exaustor bem ventilado. </li><li> Mergulha-se o filme poroso (após o passo 2.2) em solução aquosa de cloreto de estanho (passo 3.1), durante 1 hora. </li><li> Lavar a película completamente com água desionizada. </li><li> Mergulha-se o filme da solução aquosa de cloreto de paládio (passo 3.2), durante 1 hora. </li><li> Lavar a película completamente com água desionizada. </li><li> Misture parte 1 (3.3) e parte 2 (3.4) do banho de níquel. Ajustar o pH para 7,0 utilizando hidróxido de amónio. </li><li> Mergulha-se o filme no banho de niquelagem, durante 1 hora. </li><li> Lavar a película completamente com água desionizada. </li><li> Seca-se a amostra. </li><li> Preparar a amostra inoculada, em microscopia electrónica, tal como descrito nos passos 1,8-1,9. </li><li> Imagem da amostra, tal como descrito no passo 1.11. </li><li> Coloque grades Cu contendo as seções da amostra banhado na alta resolução de microscópio eletrônico de transmissão. Adquirir microscopia eletrônica de transmissão de alta resolução. Observar a amostra sob o microscópio e escolher a área para análise elementar por EDX (Energia Dispersiva Análise de Raios-X). Realize a análise EDX da área escolhida e analisar o padrão obtido. </li></ol> 4. Exposição do Inverso Gyroid Nickel Foam <ol><li> Coloque a película de níquel (após o passo 3.12) num forno a 350 ° C e mantê-lo a partir de 1 hora até 4 dias. </li><li> Prenda a amostra para o titular da amostra usando um colar de prata. </li><li> Insira a amostra no microfone eletrônica de varreduraroscope. Adquirir várias imagens da amostra. </li><li> Coloque a amostra no microscópio eletrônico de varredura. Observe o exemplo sob o microscópio e escolher a área para análise elementar por EDX. Realize a análise EDX da área escolhida e analisar o padrão obtido. </li></ol>

<ol><li>Erlebacher, J., Aziz, M. J., Karma, A., Dimitrov, N., Sieradzki, K. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Evolution+of+nanoporosity+in+dealloying%5BTitle%5D)+AND+%22Nature%22%5BJournal%5D)">Evolution of nanoporosity in dealloying.</a> Nature. 410, 450-453 (2001).</li>
<li>Nyce, G. W., Hayes, J. R., Hamza, A. V., Satcher, J. H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Synthesis+and+Characterization+of+Hierarchical+Porous+Gold+Materials%5BTitle%5D)+AND+%22Chem.+Mater%22%5BJournal%5D)">Synthesis and Characterization of Hierarchical Porous Gold Materials.</a> Chem. Mater. 19, 344-346 (2007).</li>
<li>Detsi, E., van de Schootbrugge, M., Punzhin, S., Onck, P. R., De Hosson, J. T. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((On+tuning+the+morphology+of+nanoporous+gold%5BTitle%5D)+AND+%22Scripta+Mater%22%5BJournal%5D)">On tuning the morphology of nanoporous gold.</a> Scripta Mater. 64, 319-322 (2011).</li>
<li>Gacoin, T., Lahlil, K., Larregaray, P., Boilot, J. P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Transformation+of+CdS+Colloids%3A+Sols%2C+Gels%2C+and+Precipitates%5BTitle%5D)+AND+%22J.+Phys.+Chem.+B%22%5BJournal%5D)">Transformation of CdS Colloids: Sols, Gels, and Precipitates.</a> J. Phys. Chem. B. 105, 10228-10235 (2001).</li>
<li>Tappan, B. C., Steiner, S. A., Luther, E. P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Nanoporous+Metal+Foams%5BTitle%5D)+AND+%22Angew.+Chem.+Int.+Ed%22%5BJournal%5D)">Nanoporous Metal Foams.</a> Angew. Chem. Int. Ed. 49, 4544-4565 (2010).</li>
<li>Leventis, N., Chandrasekaran, N., Sadekar, A. G., Sotiriou-Leventis, C., Lu, H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((One-Pot+Synthesis+of+Interpenetrating+Inorganic%2FOrganic%5BTitle%5D)+AND+%22Networks+of+CuO%2FResorcinol-Formaldehyde+Aerogels%3A+Nanostructured+Energetic+Materials.+J.+Am.+Chem.+Soc%22%5BJournal%5D)">One-Pot Synthesis of Interpenetrating Inorganic/Organic.</a> Networks of CuO/Resorcinol-Formaldehyde Aerogels: Nanostructured Energetic Materials. J. Am. Chem. Soc. 131, 4576-4577 (2009).</li>
<li>Leventis, N., Chandrasekaran, N., Sotiriou-Leventis, C., Mumtaz, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Smelting+in+the+age+of+nano%3A+iron+aerogels%5BTitle%5D)+AND+%22J.+Mater.+Chem%22%5BJournal%5D)">Smelting in the age of nano: iron aerogels.</a> J. Mater. Chem. 19, 63-65 (2009).</li>
<li>Tappan, B. C., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Ultralow-Density+Nanostructured+Metal+Foams%3A+Combustion+Synthesis%2C+Morphology%2C+and+Composition%5BTitle%5D)+AND+%22J.+Am.+Chem.+Soc%22%5BJournal%5D)">Ultralow-Density Nanostructured Metal Foams: Combustion Synthesis, Morphology, and Composition.</a> J. Am. Chem. Soc. 128, 6589-6594 (2006).</li>
<li>Ashby, M. F., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Metal+Foams%3A+a+Design+Guide%5BTitle%5D)+AND+%22Butterworth-Heinemann%22%5BJournal%5D)">Metal Foams: a Design Guide.</a> Butterworth-Heinemann. , (2000).</li>
<li>Tekoglu, C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Size+Effects+in+Cellular+Solids%5BTitle%5D)+AND+%22%22%5BJournal%5D)">Size Effects in Cellular Solids.</a> , University of Groningen. (2007).</li>
<li>Amsterdam, E. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Structural+Performance+and+Failure+Analysis+of+Aluminium+Foams%5BTitle%5D)+AND+%22%22%5BJournal%5D)">Structural Performance and Failure Analysis of Aluminium Foams.</a> , University of Groningen. (2008).</li>
<li>Bates, F. S., Fredrickson, G. H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Block+Copolymer+Thermodynamics%3A+Theory+and+Experiment%5BTitle%5D)+AND+%22Annu.+Rev.+Phys.+Chem%22%5BJournal%5D)">Block Copolymer Thermodynamics: Theory and Experiment.</a> Annu. Rev. Phys. Chem. 41, 525-527 (1990).</li>
<li>Hamley, I. W. <a target="_blank" href="http://scholar.google.com/scholar?hl=en&safe=off&q=author%3aHamley%2C+IW+%22The+Physics+of+Block+Copolymers%22">The Physics of Block Copolymers</a>. , Oxford University Press. (1998).</li>
<li>Abetz, V., Simon, P. <a target="_blank" href="http://scholar.google.com/scholar?hl=en&safe=off&q=author%3aAbetz%2C+V+%22Advances+in+Polymer+Science%22">Advances in Polymer Science</a>. , Springer. Berlin / Heidelberg. (2005).</li>
<li>Hillmyer, M. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Nanoporous+Materials+from+Block+Copolymer+Precursors%5BTitle%5D)+AND+%22Adv.+Polym.+Sci%22%5BJournal%5D)">Nanoporous Materials from Block Copolymer Precursors.</a> Adv. Polym. Sci. 190, 137-181 (2005).</li>
<li>Mansky, P., Harrison, C. K., Chaikin, P. M., Register, R. A., Yao, N. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Nanolithographic+templates+from+diblock+copolymer+thin+films%5BTitle%5D)+AND+%22Appl.+Phys.+Lett%22%5BJournal%5D)">Nanolithographic templates from diblock copolymer thin films.</a> Appl. Phys. Lett. 68, 2586-2588 (1996).</li>
<li>Hashimoto, T., Tsutsumi, K., Funaki, Y. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Nanoprocessing+Based+on+Bicontinuous+Microdomains+of+Block+Copolymers%3A+Nanochannels+Coated+with+Metals%5BTitle%5D)+AND+%22Langmuir%22%5BJournal%5D)">Nanoprocessing Based on Bicontinuous Microdomains of Block Copolymers: Nanochannels Coated with Metals.</a> Langmuir. 13, 6869-6872 (1997).</li>
<li>Chen, S. -Y., Huang, Y., Tsiang, R. C. -C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Ozonolysis+efficiency+of+PS-b-PI+block+copolymers+for+forming+nanoporous+polystyrene%5BTitle%5D)+AND+%22J.+Polym.+Sci.+A+Polym.+Chem%22%5BJournal%5D)">Ozonolysis efficiency of PS-b-PI block copolymers for forming nanoporous polystyrene.</a> J. Polym. Sci. A Polym. Chem. 46, 1964-1973 (2008).</li>
<li>Thurn-Albrecht, T., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Nanoscopic+Templates+from+Oriented+Block+Copolymer+Films%5BTitle%5D)+AND+%22Adv.+Mater%22%5BJournal%5D)">Nanoscopic Templates from Oriented Block Copolymer Films.</a> Adv. Mater. 12, 787-791 (2000).</li>
<li>Park, M., Harrison, C., Chaikin, P. M., Register, R. A., Adamson, D. H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Block+Copolymer+Lithography%3A+Periodic+Arrays+of+%7E1011+Holes+in+1+Square+Centimeter%5BTitle%5D)+AND+%22Science%22%5BJournal%5D)">Block Copolymer Lithography: Periodic Arrays of ~1011 Holes in 1 Square Centimeter.</a> Science. 276, 1401-1404 (1997).</li>
<li>Cheng, J. Y., Ross, C. A., Thomas, E. L., Smith, H. I., Vancso, G. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Fabrication+of+nanostructures+with+long-range+order+using+block+copolymer+lithography%5BTitle%5D)+AND+%22Appl.+Phys.+Lett%22%5BJournal%5D)">Fabrication of nanostructures with long-range order using block copolymer lithography.</a> Appl. Phys. Lett. 81, 3657-3659 (2002).</li>
<li>Voet, V. S. D., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Interface+Segregating+Fluoralkyl-Modified+Polymers+for+High-Fidelity+Block+Copolymer+Nanoimprint+Lithography%5BTitle%5D)+AND+%22J.+Am.+Chem.+Soc%22%5BJournal%5D)">Interface Segregating Fluoralkyl-Modified Polymers for High-Fidelity Block Copolymer Nanoimprint Lithography.</a> J. Am. Chem. Soc. 133, 2812-2815 (2011).</li>
<li>Zalusky, A. S., Olayo-Valles, R., Wolf, J. H., Hillmyer, M. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Ordered+Nanoporous+Polymers+from+Polystyrene-Polylactide+Block+Copolymers%5BTitle%5D)+AND+%22J.+Am.+Chem.+Soc%22%5BJournal%5D)">Ordered Nanoporous Polymers from Polystyrene-Polylactide Block Copolymers.</a> J. Am. Chem. Soc. 124, 12761-12773 (2002).</li>
<li>Crossland, E. J. W., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((A+Bicontinuous+Double+Gyroid+Hybrid+Solar+Cell%5BTitle%5D)+AND+%22Nano+Lett%22%5BJournal%5D)">A Bicontinuous Double Gyroid Hybrid Solar Cell.</a> Nano Lett. 9, 2807-2812 (2008).</li>
<li>Uehara, H., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Size-Selective+Diffusion+in+Nanoporous+but+Flexible+Membranes+for+Glucose+Sensors%5BTitle%5D)+AND+%22ACS+Nano%22%5BJournal%5D)">Size-Selective Diffusion in Nanoporous but Flexible Membranes for Glucose Sensors.</a> ACS Nano. 3, 924-932 (2009).</li>
<li>Voet, V. S. D., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Poly%28vinylidene+fluoride%29%2Fnickel+nanocomposites+from+semicrystalline+block+copolymer+precursors%5BTitle%5D)+AND+%22Nanoscale%22%5BJournal%5D)">Poly(vinylidene fluoride)/nickel nanocomposites from semicrystalline block copolymer precursors.</a> Nanoscale. 5, 184-192 (2013).</li>
<li>Brinker, C. J., Scherer, J. W. <a target="_blank" href="http://scholar.google.com/scholar?hl=en&safe=off&q=author%3aBrinker%2C+CJ+%22Sol-Gel+Science%3A+The+Physics+and+Chemistry+of+Sol-Gel+Processing%22">Sol-Gel Science: The Physics and Chemistry of Sol-Gel Processing</a>. , Academic Press. (1990).</li>
<li>Hsueh, H. -Y., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Inorganic+Gyroid+with+Exceptionally+Low+Refractive+Index+from+Block+Copolymer+Templating%5BTitle%5D)+AND+%22Nano+Lett%22%5BJournal%5D)">Inorganic Gyroid with Exceptionally Low Refractive Index from Block Copolymer Templating.</a> Nano Lett. 10, 4994-5000 (2010).</li>
<li>Hsueh, H. -Y., Ho, R. -M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Bicontinuous+Ceramics+with+High+Surface+Area+from+Block+Copolymer+Templates%5BTitle%5D)+AND+%22Langmuir%22%5BJournal%5D)">Bicontinuous Ceramics with High Surface Area from Block Copolymer Templates.</a> Langmuir. 28, 8518-8529 (2012).</li>
<li>Riedel, W. Electroless Nickel Plating. , (1991).</li>
<li>Mallory, G. O., Hajdu, J. B. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Electroless+Plating%3A+Fundamentals+and+Applications%5BTitle%5D)+AND+%22American+Electroplaters+and+Surface+Finishers+Society%22%5BJournal%5D)">Electroless Plating: Fundamentals and Applications.</a> American Electroplaters and Surface Finishers Society. , (1992).</li>
<li>Djokić, S. S. <a target="_blank" href="http://scholar.google.com/scholar?hl=en&safe=off&q=author%3aDjoki%C4%87%2C+SS+%22Modern+Aspects+of+Electrochemistry%22">Modern Aspects of Electrochemistry</a>. , Springer US. (2002).</li>
<li>Djokić, S. S., Cavallotti, P. L. <a target="_blank" href="http://scholar.google.com/scholar?hl=en&safe=off&q=author%3aDjoki%C4%87%2C+SS+%22Modern+Aspects+of+Electrochemistry%22">Modern Aspects of Electrochemistry</a>. , Springer. New York. (2010).</li>
<li>Crossland, E. J. W., Ludwigs, S., Hillmyer, M. A., Steiner, U. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Control+of+gyroid+forming+block+copolymer+templates%3A+effects+of+an+electric+field+and+surface+topography%5BTitle%5D)+AND+%22Soft+Matter%22%5BJournal%5D)">Control of gyroid forming block copolymer templates: effects of an electric field and surface topography.</a> Soft Matter. 6, 670-676 (2010).</li>
<li>Hsueh, H. Y., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Nanoporous+Gyroid+Nickel+from+Block+Copolymer+Templates+via+Electroless+Plating%5BTitle%5D)+AND+%22Adv.+Mater%22%5BJournal%5D)">Nanoporous Gyroid Nickel from Block Copolymer Templates via Electroless Plating.</a> Adv. Mater. 23, 3041-3046 (2011).</li>
<li>Vukovic, I., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Supramolecular+Route+to+Well-Ordered+Metal+Nanofoams%5BTitle%5D)+AND+%22ACS+Nano%22%5BJournal%5D)">Supramolecular Route to Well-Ordered Metal Nanofoams.</a> ACS Nano. 5, 6339-6348 (2011).</li>
<li>Mao, H., Hillmyer, M. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Macroscopic+samples+of+polystyrene+with+ordered+three-dimensional+nanochannels%5BTitle%5D)+AND+%22Soft+Matter%22%5BJournal%5D)">Macroscopic samples of polystyrene with ordered three-dimensional nanochannels.</a> Soft Matter. 2, 57-59 (2006).</li>
<li>Kobayashi, Y., Tadaki, Y., Nagao, D., Konno, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Deposition+of+Gold+Nanoparticles+on+Polystyrene+Spheres+by+Electroless+Metal+Plating+Technique%5BTitle%5D)+AND+%22J.+Phys.+Conf.+Ser%22%5BJournal%5D)">Deposition of Gold Nanoparticles on Polystyrene Spheres by Electroless Metal Plating Technique.</a> J. Phys. Conf. Ser. 61, 582-586 (2007).</li>
<li>Finnefrock, A. C., Ulrich, R., Toombes, G. E., Gruner, S. M., Wiesner, U. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((The+plumber%27s+nightmare%3A+a+new+morphology+in+block+copolymer-ceramic+nanocomposites+and+mesoporous+aluminosilicates%5BTitle%5D)+AND+%22J.+Am.+Chem.+Soc%22%5BJournal%5D)">The plumber's nightmare: a new morphology in block copolymer-ceramic nanocomposites and mesoporous aluminosilicates.</a> J. Am. Chem. Soc. 125, 13084-13093 (2003).</li>
<li>Tyler, C. A., Morse, D. C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Orthorhombic+Fddd+network+in+triblock+and+diblock+copolymer+melts%5BTitle%5D)+AND+%22Phys.+Rev.+Lett%22%5BJournal%5D)">Orthorhombic Fddd network in triblock and diblock copolymer melts.</a> Phys. Rev. Lett. 94, 208-302 (2005).</li>
<li>Ranjan, A., Morse, D. C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Landau+theory+of+the+orthorhombic+Fddd+phase%5BTitle%5D)+AND+%22Phys.+Rev.+E%22%5BJournal%5D)">Landau theory of the orthorhombic Fddd phase.</a> Phys. Rev. E. 74, 011803(2006).</li>
<li>Kim, M. I., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Stability+of+the+Fddd+Phase+in+Diblock+Copolymer+Melts%5BTitle%5D)+AND+%22Macromolecules%22%5BJournal%5D)">Stability of the Fddd Phase in Diblock Copolymer Melts.</a> Macromolecules. 41, 7667-7670 (2008).</li>
</ol>

Os autores declaram não haver interesses financeiros concorrentes.

Complexos supramoleculares são aplicadas com êxito como precursores de nanofoams de metal bem ordenadas. Neste método, o passo crucial é adquirir o modelo apropriado, ou seja, um molde com morfologia gyroid. No diagrama de fases de copolímeros em bloco da região gyroid é muito pequeno e é bastante difícil de atingir. Isto significa que, se os copolímeros em bloco convencionais são utilizados como materiais de partida, a síntese bastante elaborada tem de ser repetido até que a composição desejada, que dá origem ...

Existem várias técnicas disponíveis para a preparação de nanofoams metálicos: dealloying 1-3, sol-gel aproxima de 4,5, nanosmelting 6,7, e a síntese de combustão 8. No processo dealloying, o material de partida é geralmente uma liga binária, por exemplo, uma liga de prata e de ouro. O metal menos nobre, prata, neste caso, pode ser removido quimicamente ou electroquimicamente, resultando numa espuma de ouro poroso desordenado com ligamentos nanométricas. Na síntese de combustão, o metal é misturado com um precursor energético que liberta energia durante a sua decomposição e conduz à formação de metais nanofoam 8. Estudos sobre o comportamento mecânico de espumas de metal indicam que em arquitecturas desordenados tensões não podem ser transmitidas de forma eficaz a partir do ligamento à nanoescala macroescala geral 9-11. Assim nanofoams metálicos bem ordenadas se espera que tenham propriedades mecânicas superiores, em comparação com oos desordenados. A idéia aqui representada é empregar copolímeros em bloco que se auto-organizar em nanoestruturas ordenadas como precursores de nanofoams metal. Dependendo da composição de um copolímero em bloco, o número total de unidades de monómeros e o grau de repulsão entre os blocos quimicamente ligados, várias morfologias parecem tais como: esférica, cilíndrica, lamelar, duplo gyroid, hexagonal lamelar perfurada, e os outros 12-14 . Além disso, os blocos de polímero pode ser degradado selectivamente levando a materiais nanoporos 15. Os métodos mais comuns incluem: ozonólise 16-18, irradiação UV 19, corrosão iônica reativa 20-22, 23-26 e dissolução. As estruturas porosas gerados podem ser utilizados no enchimento com diversos materiais inorgânicos. Óxidos metálicos (por exemplo, SiO 2, TiO 2) são normalmente introduzidos através de método de sol-gel para os canais do molde 27-29. Elchapeamento electroless ectrochemical e são comumente usados ​​para depositar metal em ou em modelos de 30-33. Finalmente, o polímero restante pode ser removido a partir do polímero / nanohíbrido inorgânico através de pirólise 2, dissolução 34,35, 28,29 degradação de UV, etc Em nossa abordagem, vamos começar a partir de um complexo supramolecular de poliestireno-bloco-poli (4-vinil-piridina) (PS-b-P4VP) copolímero diblock e pentadecilfenol anfifílico (PDP) moléculas. Este complexo é um resultado da ligação de hidrogénio entre PDP e anéis de piridina (Figura 1a). A composição de copolímero em bloco de partida e a quantidade de agregado PDP são escolhidos de tal maneira que o sistema de auto-montagem obtidos na morfologia gyroid dupla bicontinua com uma rede PS e uma matriz de P4VP (PDP) (Figura 1b). Moléculas PDP ficar dissolvido seletivamente em etanol e P4VP cadeias colapso na rede PS (A Figura 1c). Subsequentemente, utilizando o método de revestimentos de níquel é depositado no interior dos poros da matriz (Figura 1d). Após a remoção do polímero remanescente através de pirólise, uma nanofoam níquel gyroid bem ordenado é obtido (Figura 1e).

<table><tbody><tr><td colspan="4">Reagents</td></tr><tr><td>PS-b-P4VP, CAS: 26222-40-2</td><td>Polymer Source Inc.</td><td>P9009-S4VP P136-S4VP P5462-S4VP P3912-S4VP</td><td>informações adicionais são fornecidas em uma tabela separada</td></tr><tr><td>PDP</td><td>Aldrich</td><td>P4402-100G-A</td><td>recristalizado duas vezes a partir do éter de petróleo</td></tr><tr><td>SnCl2</td><td>Acros Organics</td><td>196981000</td><td></td></tr><tr><td>PdCl2</td><td>Aldrich</td><td>76050</td><td></td></tr><tr><td>NiSO4&bull; H2O</td><td>Sigma-Aldrich</td><td>227676</td><td></td></tr><tr><td>Ácido láctico</td><td>Aldrich</td><td>W261106</td><td></td></tr><tr><td>Sal trissódico de ácido cítrico</td><td>Sigma-Aldrich</td><td>C3674</td><td></td></tr><tr><td>Complexo de borano dimetilamina</td><td>Aldrich</td><td>180238</td><td></td></tr><tr><td>PS-b-P4VP número de catálogo</td><td>Mn (PS), g/mol</td><td>Mn (P4VP), g/mol</td><td>PDI</td></tr><tr><td>P9009-S4VP</td><td>24000</td><td>9500</td><td>1,1</td></tr><tr><td>P136-S4VP</td><td>31900</td><td>13200</td><td>1,08</td></tr><tr><td>P5462-S4VP</td><td>37500</td><td>16000 1,3</td><td></td></tr><tr><td>P3912-S4VP</td><td>41500</td><td>17500</td><td>1,07</td></tr></tbody></table>

gyroid nickel nanoestruturas de dibloco copolímero supramoléculas

Gyroid Nickel Nanostructures from Diblock Copolymer Supramolecules

Espumas metálicas Nanoporosos possuem uma combinação única de propriedades, - eles são cataliticamente activas, termicamente e electricamente condutor, e, além disso, têm uma elevada porosidade, elevada relação de superfície-para-volume e resistência-peso. Infelizmente, as abordagens comuns para a preparação de nanoestruturas metálicas tornar materiais com arquitetura altamente desordenado, o que pode ter um efeito adverso em suas propriedades mecânicas. Os copolímeros em bloco têm a capacidade de se auto-organizar em nanoestruturas ordenadas e pode ser aplicado como modelo para a preparação de nanofoams metálicos bem ordenadas. Aqui descreve-se a aplicação de um complexo supramolecular bloco baseado em copolímero - poliestireno-bloco-poli (4-vinilpiridina) (pentadecilfenol) PS-b-P4VP (PDP) - como um precursor para nanofoam níquel bem ordenada. Os complexos supramoleculares exibem um comportamento de fase semelhante a copolímeros em bloco convencionais e pode auto-montar em bicontinua o engenho morfologia gyroidh duas redes PS colocados numa matriz de P4VP (PDP). PDP pode ser dissolvido em etanol, levando à formação de uma estrutura porosa, que pode ser preenchido com metal. Usando a técnica de chapeamento electrolítico, níquel pode ser introduzido nos canais do molde. Finalmente, o polímero restante pode ser removida através de pirólise a partir de polímero / inorgânico nanohíbrido resultando em espuma de níquel nanoporoso com morfologia gyroid inversa.

A morfologia de complexos supramoleculares PS-b-P4VP (PDP) x é examinada por TEM e SAXS Figuras 2a e 2b apresentam padrões gyroid típicos de um complexo supramolecular representativo:. Da onda duplo e os padrões vagão rodas que são conhecidos para representar projecções através do (211) e o plano (111) da célula unitária gyroid, respectivamente. Os domínios bloco PS aparecer brilhante enquanto os P4VP gerados (PDP) domínios Bloco X aparecem escuras devido a manchas de iodo. <st...

Este artigo descreve a preparação de nanofoams níquel bem ordenadas por deposição química de metal para modelos nanoporous obtidos a partir supramoléculas base de copolímeros diblock auto-montados.

Gyroid Nickel Nanoestruturas de dibloco copolímero supramoléculas

Nanoporous metal foams possess a unique combination of properties - they are catalytically active, thermally and electrically conductive, and furthermore, ...

O objetivo geral deste procedimento é preparar nanoespumas metálicas ordenadas, partindo de um complexo supramolecular, o bloco de poliestireno poli para vinil purina penedes LPH fenol. Isso é realizado primeiramente pela seleção dos parâmetros adequados do sistema que gerariam a morfologia de duplo giro em complexos supramoleculares. O segundo passo consiste na remoção seletiva de um componente do complexo, ou seja, o penad sylph fenol, que faz parte da matriz de giro.Em seguida, o molde poroso é preenchido com níquel por meio de um procedimento de eletrodeposição. O passo final consiste na remoção do polímero remanescente por pirólise a 350 graus Celsius. Em última análise, utiliza-se a síntese direcionada por moldes de blocos copoliméricos para gerar espumas metálicas nanoporosas bem ordenadas com morfologia giroide inversa.Portanto, a principal vantagem dessa técnica em relação aos métodos existentes é que somos capazes, de maneira direta, de obter uma morfologia dupla em forma de GY em polímeros bloqueadores. Depois disso, uma vez que temos uma morfologia de duplo giro, podemos pegar nossa amostra, mergulhá-la em etanol e, então, remover o pandaol anfifílico de forma muito simples. Em seguida, quando temos uma estrutura porosa, realizamos o metalizado sem eletrodeposição para inserir metal nos complexos caminhos de PO de tal modo que, ao final, obtemos uma nanoespuma metálica.Este método fornece uma maneira intuitiva de formar redes nanoestruturadas ordenadas a partir de uma grande variedade de metais. Primeiro, dissolva o bloco de poliestireno poli para vinil purina e fenol pentes em clorofórmio e agite a solução por algumas horas à temperatura ambiente. Despeje a solução em uma placa de Petri de vidro e, em seguida, coloque a placa em uma atmosfera saturada de clorofórmio.Após aproximadamente uma semana, retire a placa de Petri da atmosfera saturada com clorofórmio. Seque o filme do complexo supramolecular em vácuo a 30 graus Celsius durante a noite. Após remover o filme da estufa, coloque-o em um recipiente especialmente projetado.Em seguida, remova o ar do recipiente e preencha-o com nitrogênio ao finalizar. Anelhe o filme por quatro dias no forno a 120 graus Celsius sob atmosfera de nitrogênio com uma pressão superior de um bar. Após a conclusão do processo de anelhamento, corte um pequeno pedaço do filme e o incorpore em resina epóxi.Em seguida, cure a amostra durante a noite a 40 graus Celsius. Corte a amostra em micrótomo com espessura de cerca de 80 nanômetros utilizando uma lâmina de diamante à temperatura ambiente. Coloque as seções microtomadas em grades de cobre.Após essa transferência, coloque as grades contendo as seções do micrótomo em um frasco com iodo. Após 45 minutos, remova as amostras coradas. Como preparação para a microscopia eletrônica de transmissão, insira as grades de cobre com as seções coradas no microscópio eletrônico de transmissão.Operando com uma tensão de aceleração de 120 quilovolts, obtenha uma imagem da amostra. Em seguida, insira um pedaço de filme dobrado no suporte da amostra para sacos e fixe-o com uma tampa aderida com fita. Coloque o suporte preparado no equipamento.Abra o obturador de raios X e adquira o padrão de dispersão 2D. Neste momento, mergulhe outro pequeno pedaço de um filme dobrado em etanol por três dias. Uma vez que o filme poroso tenha sido secado, mergulhe-o em uma solução aquosa de cloreto de estanho por uma hora.Após remover o filme da solução, enxágue-o completamente com água desionizada. Em seguida, imerja o filme em uma solução aquosa de cloreto de paládio. Após uma hora, remova o filme da solução e enxágue-o com água desionizada.Para preparar o banho de niquelagem, misture uma solução de sulfato de níquel hexaidratado com uma solução de complexo de Bo dimetilamina na proporção de quatro para um e ajuste o pH para sete. Usando hidróxido de amônio, imerja o filme no banho de niquelagem por uma hora. Após a lavagem com água desionizada, seque o filme em uma capela de exaustão.Após preparar a amostra em lâmina para microscopia eletrônica conforme descrito anteriormente, realize a imagem com as mesmas condições de antes. Em seguida, coloque o filme revestido com níquel em uma estufa a 350 graus Celsius por um período de uma hora a quatro dias.Após a película ter esfriado até a temperatura ambiente, fixe-a ao suporte da amostra utilizando uma pasta de prata. Em seguida, insira o suporte da amostra no microscópio eletrônico de varredura. Adquira micrografias de MEV e realize a análise de EDX.Onda dupla e roda de carroça. Os padrões giroscópicos representam projeções através dos planos 2 1 1 e 1 1 1 da célula unitária giro, respectivamente. Os domínios de bloco de poliestireno aparecem brilhantes, enquanto poli.Quatro domínios de bloco de fenol pentil de vinila púrica aparecem escuros com iodo. A coloração do padrão de onda dupla de outra amostra mostra uma diminuição na periodicidade com picos sax nas raízes quadradas de seis Q*, raiz quadrada de oito Q*, raiz quadrada de 14 Q*, raiz quadrada de 22 Q* e raiz quadrada de 50 Q*. Confirme a morfologia bicontínua IA 3D após o tratamento com etanol.Os sinais de RMN de próton em fenol de penad sylph estão ausentes. Os dados de DSC indicam que o comportamento térmico da amostra tratada com etanol e do copolímero em bloco DI é idêntico. O molde giro poroso possui uma alta área superficial específica BET de 104 metros quadrados por grama e ocupa quase 60 por cento em volume.O diâmetro médio dos poros é de 40 nanômetros, com distribuição estreita do tamanho dos poros. O contraste no giro de níquel não corado, na micrografia de MET, origina-se do metal depositado nos nanocanais. O padrão de roda de carroça confirma a preservação da morfologia dupla de giro. Micromicrografias de TEM de alta resolução mostram grandes cristalitos de níquel interconectados e a análise por EDX revela a amostra metalizada. Composição química. São observados picos de carbono, níquel e oxigênio, o que indica oxidação da nanoespuma de níquel quando armazenada no ar.A rede de níquel permanece intacta durante a decomposição do polímero por aquecimento isotérmico. A réplica de níquel exposta preserva a morfologia giro inversa, conforme confirmado por MEV. Usando o método que acabamos de mostrar, foi possível obter e caracterizar nanoespumas metálicas altamente ordenadas.Essas nanoespumas metálicas altamente ordenadas podem potencialmente ser usadas como atuadores. Este método abre caminho para a investigação das diferenças no comportamento de metais nanoporosos ordenados e desordenados. Não se esqueça de que o trabalho com produtos químicos utilizados para eletrodos e galvanização metálica pode ser extremamente perigoso, e deve-se sempre utilizar equipamento de proteção individual ao realizar este procedimento.

gyroid-nickel-nanostructures-from-diblock-copolymer-supramolecules

Research

JoVE Journal

Chemistry

Química

Um simples e gerais método de síntese manual de peptoid envolvendo equipamentos básicos e reagentes disponíveis comercialmente é delineado, permitindo Peptóides para ser facilmente sintetizado na maioria dos laboratórios. A síntese, purificação e caracterização de um 36mer peptoid anfifílicos é descrito, bem como a sua auto-montagem em altamente ordenado nanofolhas.

Síntese em fase sólida Submonomer de Polímeros Peptoid e seus Automontagem em altamente ordenada nanofolhas

Este artigo descreve um método para sintetizar nanoprecipitation polímero baseado em nanopartículas usando dibloco co-polímeros. Vamos discutir a síntese de dibloco co-polímeros, a técnica nanoprecipitation e aplicações potenciais.

Formulação de nanopartículas poliméricas através da técnica de dibloco Nanoprecipitation

O objetivo desta experiência é determinar e controlar o tamanho, forma e estabilidade da auto-montagem anfifílicos discotic na água. Para aquosos baseados em polímeros supramoleculares tal nível de controle é muito difícil. Nós aplicamos uma estratégia usando ambas as interações repulsivas e atrativas. As técnicas experimentais aplicadas para caracterizar este sistema são amplamente aplicáveis.

Controlando o tamanho, forma e estabilidade de Polímeros Supramoleculares na Água

Laser femtosegundo escrita direta é freqüentemente usado para criar tridimensionais (3D) em polímeros padrões e óculos. No entanto, os metais de padronização em 3D continua a ser um desafio. Descreve-se um método para a fabricação de nanoestruturas de prata embutido no interior de uma matriz de polímero usando um laser de femtosegundos centrado em 800 nm.

Um método para fabricar nanoestruturas de prata desconectados em 3D

Descrevemos detalhes experimentais para a síntese de partículas e reconfiguráveis ​​estampados a partir de duas dimensões (2D) precursores. Esta metodologia pode ser utilizada para criar partículas, em uma variedade de formas, incluindo poliedros e dispositivos de preensão em escalas de comprimento variando entre o micro escala de centímetro.

Origami Inspirado Auto-montagem de Partículas estampados e Reconfigurável

Este documento descreve a formação de estruturas com base em peptídeos altamente ordenada pelo processo espontâneo de auto-montagem. O método utiliza peptídeos comercialmente disponíveis e equipamento de laboratório comum. Esta técnica pode ser aplicada a uma grande variedade de péptidos e podem conduzir à descoberta de novos conjuntos com base em peptídeos.

A formação de estruturas biomoleculares ordenada pelo auto-montagem de pequenos peptídeos

Relatamos protocolos para "polimerizar" vários tipos de nanopartículas metálicas encapsuladas em polímeros em longas cadeias de "homo-" e "copolímeros".

Usando Polystyrene-<em&gt; Bloco</em&gt; -poli (Ácido acrílico) -Revestido metal Nanopartículas como monómeros para a sua homo- e co-polimerização

Aqui, apresentamos um protocolo para preparar e visualizar estruturas secundárias (por exemplo, fibras, arquiteturas toroidal, e nano-esferas) derivados de policarbodiimidas helicoidais. A morfologia caracterizado por, tanto a microscopia de força atómica (AFM) e microscopia electrónica de varrimento (SEM) foi demonstrado que depende da estrutura molecular, concentração, e o solvente de escolha.

Morfologias de auto-montagem Obtidos a partir helicoidais policarbodiimida copolímeros e seus derivados triazólicos

Aqui, apresentamos um protocolo para a fabricação de polyhedrons 3D baseados em grafeno através do origami, como self dobrável.

Fabricação de Polyhedrons tridimensionais baseados em grafeno através do Origami, como self dobrável

A automontagem acionada por cristalização (CDSA) exibe a capacidade única de fabricar nanoestruturas cilíndricas de distribuições de comprimento estreito. A polimerização organocatalyzed da anel-abertura do ε-caprolactone e das extensões Chain subseqüentes do metacrilato de metilo e do n,acrilamida de n-dimethyl é demonstrada. Um protocolo de CDSA vivo que produza cilindros do monodispersas até 500 nanômetro do comprimento é esboçado.

Síntese de nanopartículas cilíndricas Monodispersa via auto-montagem orientada por cristalização de copolímeros de blocos biodegradáveis

Uma combinação de solução e síntese assistida por superfície abre novas direções na síntese atomicamente precisa de nanoestruturas. A microscopia de tunelamento de varredura (STM) complementada pela microscopia atômica da força do não-contato (nc-AFM) permite a caracterização detalhada de nano-objetos carbono-baseados recentemente projetados e gerados.

Visualização microscópica de nanografenos porosos sintetizados através de uma combinação de solução e química na superfície

Aprenda a preparar nanofoams de níquel ordenados a partir de complexos supramoleculares de copolímeros de bloco. Este método utiliza deposição eletrolítica e pirólise para criar estruturas nanoporosas com morfologia giroide inversa.