Name: Produção de Synthetic Nuclear Melt vidro (Vídeo) | JoVE Journal
Uploaded: 2016-01-04T13:00:01.000+00:00
Duration: 4 min 36 s
Description: Aprenda a produzir vidro nuclear sintético para análises forenses nucleares usando quartzo e técnicas de espectrometria de massa. Este método estabelece padrões para pesquisa em vidro de fusão nuclear.

ai_agent_IP

ai_agent

maintenance

instantTrialDurationMinutes

isBiopharma

enableNewMyJoveSectionDesign

educationFeatures

seoMetaApi

ai_copilot_institution_blacklist

ai_chat_institution_blacklist

freeAccessWindow

ssoRoleCapture

scheduledMaintenanceBanner

joveLabsFeatures

disable_autoplay_for_bots

extended_trial_duration

5 minutes

Partes deste estudo foram publicadas anteriormente no Journal of Radioanalytical and Nuclear Chemistry. 3,13 Uma patente está pendente para este método.

Atenção: O processo descrito aqui inclui o uso de material radioativo (por exemplo, Urânio Nitrato Hexahydrate) e várias matérias corrosivas. Vestuário de protecção adequado e equipamento deve ser utilizado (incluindo um jaleco, luvas, óculos de protecção, e um exaustor), durante a preparação da amostra. Além disso, áreas de laboratório utilizados para este trabalho deve ser monitorizado regularmente por contaminação radioativa. Nota:. Os compostos químicos necessários estão listados na Tabela 1 Esta formulação foi desenvolvida através do exame anteriormente relataram dados relativos à composição para trinitite 10 As fracções de massa aqui apresentados foram determinados calculando a média das fracções de massa para várias amostras trinitite diferentes 10 A massa &quot;em falta&quot;.. (as frações para não somar à unidade) existe para permitir uma certa flexibilidade quando adicionar combustível, adulteração e outros constituintes. A nossa análise independente de diversas amostras trinitite sugere que o quartzo é a única fase mineralsobrevivendo em trinitite. 5 Portanto, quartzo é o único mineral incluído em nossa Trinitite Formulação Padrão (STF). Apesar de grãos relíquia de outros minerais têm sido relatados em trinitite, 11 estes tendem a ser a excepção e não a regra. Em geral, o quartzo é a única mineral encontrado no vidro fundido. 10,12 Além disso, a areia de quartzo é um componente comum do concreto e asfalto, que será importante na formação de vidro em fusão nuclear urbano. <table fo:keep-together.within-page="1"><tbody><tr height="41"><td colspan="2" height="41" style="height:42px;width:317px;"> Média de Dados Trinitite </td><td colspan="2" style="width:317px;"> Padrão Trinitite Formulação (STF) </td></tr><tr height="22"><td height="22" style="height:22px;width:159px;"> Composto </td><td style="width:159px;"> Fração de massa </td><td style="width:159px;"> Composto </td><html><td style="width:159px;"> Fração de massa </td></tr><tr height="26"><td height="26" style="height:26px;width:159px;"> SiO2 </td><td style="width:159px;"> 6.42x10 -1 </td><td style="width:159px;"> SiO2 </td><td style="width:159px;"> 6.42x10 -1 </td></tr><tr height="26"><td height="26" style="height:26px;width:159px;"> Al 2 O 3 </td><td style="width:159px;"> 1.43x10 -1 </td><td style="width:159px;"> Al 2 O 3 </td><td style="width:159px;"> 1.43x10 -1 </td></tr><tr height="25"><td height="25" style="height:25px;width:159px;"> CaO </td><td style="width:159px;"> 9.64x10 -2 </td><td style="width:159px;"> CaO </td><td style="width:159px;"> 9.64x10 -2 </td></tr><tr height="25"><td height="25" style="height:25px;width:159px;"> FeO </td><td style="width:159px;"> 1.97x10 -2 </td><html> &quot;&gt; FeO </td><td style="width:159px;"> 1.97x10 -2 </td></tr><tr height="25"><td height="25" style="height:25px;width:159px;"> MgO </td><td style="width:159px;"> 1.15x10 -2 </td><td style="width:159px;"> MgO </td><td style="width:159px;"> 1.15x10 -2 </td></tr><tr height="26"><td height="26" style="height:26px;width:159px;"> Na2O </td><td style="width:159px;"> 1.25x10 -2 </td><td style="width:159px;"> Na2O </td><td style="width:159px;"> 1.25x10 -2 </td></tr><tr height="26"><td height="26" style="height:26px;width:159px;"> K2O </td><td style="width:159px;"> 5.13x10 -2 </td><td style="width:159px;"> KOH </td><td style="width:159px;"> 6.12x10 -2 </td></tr><tr height="25"><td height="25" style="height:25px;width:159px;"> MnO </td><td style="width:159px;"> 5.05x10 -4 </td><td style="width:159px;"> MnO </td>9px; &quot;&gt; 5.05x10 -4 </td></tr><tr height="26"><td height="26" style="height:26px;width:159px;"> TiO2 </td><td style="width:159px;"> 4.27x10 -3 </td><td style="width:159px;"> TiO2 </td><td style="width:159px;"> 4.27x10 -3 </td></tr><tr height="25"><td height="25" style="height:25px;width:159px;"> Total </td><td style="width:159px;"> 9.81x10 -1 </td><td style="width:159px;"> Total </td><td style="width:159px;"> 9.91x10 -1 </td></tr></tbody></table> Tabela 1. Lista dos compostos químicos. 1. Preparação do STF Nota: O equipamento necessário inclui uma microbalança, espátulas metálicas, uma argamassa de cerâmica e pilão, uma coifa química, luvas de látex, um jaleco e óculos de protecção. <ol><li> A mistura dos componentes não-radioactivos <ol><li> Adquirir, pelo menos, 65 g de areia de quartzo (SiO2), 15 g de Al 2 O 3 &lt;/ sub&gt; em pó, 10 g de CaO em pó, 2 g de FeO em pó, 2 g de MgO em pó, 2 g de Na 2 O pó, 7 g de pastilhas de KOH, 1 g de MnO em pó e 1 g de TiO 2 em pó ( compostos listados na Tabela 1). </li><li> Usar uma microbalança e pequena espátula para medir com precisão as fracções de massa de cada composto tal como listado na Tabela 1. Para melhores resultados a preparação de 100 g de matriz precursor não radioactivo de uma só vez. </li><li> Usar um almofariz e pilão para pulverizar (a ~ 10-20 granulação uM) e misturar completamente os compostos, a formação de uma mistura em pó homogénea contendo 64,2 g de SiO2, 14,2 g de Al 2 O 3, 9,64 g de CaO, 1,97 g de FeO, 1,15 g de MgO, 1,25 g de Na 2 O. 6,12 g de KOH, 0,0505 g de MnO, e 0,427 g de TiO 2. </li><li> Agita-se a mistura, utilizando um misturador de bola, pouco antes de o próximo passo é dado. </li></ol></li><li> Mistura de STF com Urânio Nitrato Hexahydrate (UNH) <ol><li> Acquire, pelo menos, 1 g de UNH. </li><li> Dentro de um exaustor, pulverizar alguns cristais UNH (utilizando um almofariz e pilão) para formar um pó fino de 1-2 mm grânulos. </li><li> Adicionar 33,75 g de UNH por grama da matriz precursor não radioactivo (esta relação é apropriado para simular uma arma simples, com um rendimento de 1 kilotoneladas) 13. </li><li> Misture bem a mistura em pó, incluindo o UNH, utilizando um almofariz e pilão. Conclua mistura final, pouco antes do passo de fusão. </li></ol></li></ol> 2. Produção de 1 grama Melt vidro Amostra Nota: O equipamento necessário inclui uma HTF avaliado em 1.600 ° C ou superior, cadinhos de alta pureza grafite, aço inoxidável longas pinças cadinho, luvas resistentes ao calor e proteção para os olhos. Luvas resistentes ao calor e proteção para os olhos devem ser usados ​​ao introduzir ou retirar amostras do forno. Óculos de segurança matizado (ou óculos de sol) são úteis como eles reduzem o brilho do forno. <ol><li> Produção de uma amostra não-radioactivos <ol><li> Encher um prato cerâmico de espessura (tal como um almofariz) com ~ 100 g de areia de quartzo puro e mantida a temperatura ambiente perto da localização do forno onde as amostras vai ser derretido. </li><li> Pré-aqueça o HTF a 1.500 ° C. </li><li> Medir cuidadosamente 1,00 g da mistura em pó não-radioactiva e colocar o pó num cadinho de grafite de alta pureza. </li><li> Com cuidado, coloque o cadinho no HTF aquecida (usando um longo par de pinças de aço cadinho) e derreter a mistura durante 30 min. </li><li> Retirar a amostra (de novo usando pinças) e verter a amostra fundida na argamassa preenchido com areia. </li><li> Permitir que a pérola de vidro para esfriar por 1-2 min antes de utilizar. </li><li> Polir o talão para remover a areia residual (se necessário). </li></ol></li><li> Produção de uma amostra radioactiva <ol><li> Repita os passos pontos 2.1.1 e 2.1.2 supra. </li><li> Meça cuidadosamente 1,00 grama da mistura em pó radioativo (incluindo UNH) e coloque o powd<html> er num cadinho de grafite de elevada pureza utilizando uma espátula e microbalança separado para evitar contaminação cruzada. </li><li> Repita os passos 2.1.4 - 2.1.6 supra. </li><li> Monitorar a área ao redor do forno (com um detector portátil de radiação e / ou ensaios de furto) para verificar se há contaminação radioativa. </li></ol></li></ol> 3. Amostra de Activação Nota: As equações que se seguem foram obtidos assumindo que o grau de utilização de armas (enriquecido) de metal de urânio. As quantidades de óxido de urânio UNH ou terá de ser dimensionados de acordo com a fracção de massa de urânio elementar e o nível de enriquecimento de 235 L. <ol><li> A ativação de uma amostra Melt vidro com urânio Fue <ol><li> Calcule a fração de massa de metal de urânio necessário para a amostra usando a equação abaixo de 13 (onde m U representa a fração de massa de urânio e Y representa o rendimento arma): 473 / 53473eq1.jpg &quot;/&gt; </li><li> Opcional: Calcula-se a fracção de massa de violação (por exemplo, urânio natural, de chumbo, de tungsténio) utilizando a equação abaixo: 13 <img alt="Equação 2" src="/files/ftp_upload/53473/53473eq2.jpg" /></li><li> Calcular o número alvo de fissão na amostra utilizando a seguinte equação 13 em que M representa o s massa da amostra em gramas e N f representa o número de fissões produzidas na amostra durante a irradiação: <img alt="Equação 3" src="/files/ftp_upload/53473/53473eq3.jpg" /></li><li> Calcule o tempo de irradiação necessário usando a equação abaixo de 13 m, onde 235 representa a fração de massa 235 U (nível de enriquecimento) e t TIR é o tempo de irradiação em segundos: <img alt="Equação 4" src="/files/ftp_upload/53473/53473eq4.jpg" /></li><li> Irradiar a amostra parat segundos IRR em um fluxo de nêutrons térmicos de 4,0 x 10 14 n / cm2 / seg. Por exemplo, um 60 seg irradiação em pneumático Tubo 1 (TP-1) em HFIR (com uma térmica a ressonância proporção de 35) irá produzir cerca de 1,1 x 10 11 fissões numa amostra contendo 870 ug de UNH (equivalente a 410 mg de urânio natural, ou 3,0 ug de 235 U). Isto foi realizado por um 0,433 g de esferas de vidro concebidos para simular uma amostra de vidro em fusão produzidas por uma arma com um rendimento de 0,1 kilotoneladas. Esta amostra foi minuciosamente analisado por Cook et al 14. </li><li> Siga os protocolos de segurança aplicáveis ​​para o manuseio da amostra radioativa pós-irradiação. </li></ol></li><li> A ativação de uma amostra Melt vidro com plutônio combustível (fatores de planejamento) <ol><li> Calcule a fração de massa de plutónio metálico necessário para a amostra usando a equação abaixo, onde 13 m represen Puts a fração de massa de plutônio e Y representa o rendimento arma: <img alt="Equação 5" src="/files/ftp_upload/53473/53473eq5.jpg" /></li><li> Repita os passos 3.1.2 e 3.1.3 acima. </li><li> Determine o tempo de irradiação necessário para se obter o número desejado de fissão na amostra de vidro fundido. Este tempo depende da composição e do grau do plutónio, bem como do espectro de energia de neutrões. </li></ol></li></ol> Nota: Muito cuidado deve ser tomado quando se lida com plutônio e análise adicional será necessário. Como desta escrita, única urânio foi usado nas amostras de vidro de fusão sintéticas produzidas na UT e irradiados em HFIR.

<ol><li>Carnesdale, A. <a target="_blank" href="http://scholar.google.com/scholar?hl=en&safe=off&q=author%3aCarnesdale%2C+A+%22Nuclear+Forensics%3A+A+Capability+at+Risk+%28Abbreviated+Version%29%22">Nuclear Forensics: A Capability at Risk (Abbreviated Version)</a>. , Committee on Nuclear Forensics, National Research Council of the National Academies. Washington, D.C. (2010).</li>
<li>Garrison, J. R., Hanson, D. E., Hall, H. L. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Monte+Carlo+analysis+of+thermochromatography+as+a+fast+separation+method+for+nuclear+forensics%5BTitle%5D)+AND+%22J+Radioanal+Nucl+Chem%22%5BJournal%5D)">Monte Carlo analysis of thermochromatography as a fast separation method for nuclear forensics.</a> J Radioanal Nucl Chem. 291 (3), 885-894 (2011).</li>
<li>Molgaard, J. J., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Development+of+synthetic+nuclear+melt+glass+for+forensic+analysis%5BTitle%5D)+AND+%22J+Radioanal+Nucl+Chem%22%5BJournal%5D)">Development of synthetic nuclear melt glass for forensic analysis.</a> J Radioanal Nucl Chem. 304 (3), 1293-1301 (2015).</li>
<li>Fluegel, A. Modeling of Glass Liquidus Temperatures using Disconnected Peak Functions. ACerS 2007 Glas Opt Mater Div Meet, , (2007).</li>
<li>Oldham, C. J., Molgaard, J. J., Auxier, J. D., Hall, H. L. Comparison of Nuclear Debris Surrogates Using Powder X-Ray Diffraction. Southeastern Undergraduate Research Conference, , (2014).</li>
<li>Liezers, M., Fahey, A. J., Carman, A. J., Eiden, G. C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((The+formation+of+trinitite-like+surrogate+nuclear+explosion+debris+%28+SNED+%29+and+extreme+thermal+fractionation+of+SRM-612+glass+induced+by+high+power+CW+CO+2+laser+irradiation%5BTitle%5D)+AND+%22J+Radional+Nucl+Chem%22%5BJournal%5D)">The formation of trinitite-like surrogate nuclear explosion debris ( SNED ) and extreme thermal fractionation of SRM-612 glass induced by high power CW CO 2 laser irradiation.</a> J Radional Nucl Chem. 304 (2), 705-715 (2015).</li>
<li>Harvey, S. D., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Porous+chromatographic+materials+as+substrates+for+preparing+synthetic+nuclear+explosion+debris+particles%5BTitle%5D)+AND+%22J+Radioanal+Nucl+Chem%22%5BJournal%5D)">Porous chromatographic materials as substrates for preparing synthetic nuclear explosion debris particles.</a> J Radioanal Nucl Chem. 298 (3), 1885-1898 (2013).</li>
<li>Hanni, J. B., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Liquidus+temperature+measurements+for+modeling+oxide+glass+systems+relevant+to+nuclear+waste+vitrification%5BTitle%5D)+AND+%22J+Mater+Res%22%5BJournal%5D)">Liquidus temperature measurements for modeling oxide glass systems relevant to nuclear waste vitrification.</a> J Mater Res. 20 (12), 3346-3357 (2005).</li>
<li>Weber, W. J., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Radiation+Effects+in+Glasses+Used+for+Immobilization+of+High-Level+Waste+and+Plutonium+Disposition%5BTitle%5D)+AND+%22J+Mater+Res%22%5BJournal%5D)">Radiation Effects in Glasses Used for Immobilization of High-Level Waste and Plutonium Disposition.</a> J Mater Res. 12 (8), 1946-1978 (1997).</li>
<li>Eby, N., Hermes, R., Charnley, N., Smoliga, J. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Trinitite-the+atomic+rock%5BTitle%5D)+AND+%22Geol+Today%22%5BJournal%5D)">Trinitite-the atomic rock.</a> Geol Today. 26 (5), 180-185 (2010).</li>
<li>Bellucci, J. J., Simonetti, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Nuclear+forensics%3A+searching+for+nuclear+device+debris+in+trinitite-hosted+inclusions%5BTitle%5D)+AND+%22J+Radioanal+Nucl+Chem%22%5BJournal%5D)">Nuclear forensics: searching for nuclear device debris in trinitite-hosted inclusions.</a> J Radioanal Nucl Chem. 293 (1), 313-319 (2012).</li>
<li>Ross, C. S. <a target="_blank" href="http://scholar.google.com/scholar?hl=en&safe=off&q=author%3aRoss%2C+CS+%22Optical+Properties+of+Glass+from+Alamogordo%2C+New+Mexico%22">Optical Properties of Glass from Alamogordo, New Mexico</a>. , (1948).</li>
<li>Giminaro, A. V., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Compositional+planning+for+development+of+synthetic+urban+nuclear+melt+glass%5BTitle%5D)+AND+%22J+Radional+Nucl+Chem%22%5BJournal%5D)">Compositional planning for development of synthetic urban nuclear melt glass.</a> J Radional Nucl Chem. , (2015).</li>
<li>Cook, M. T., Auxier, J. D., Giminaro, A. V., Molgaard, J. J., Knowles, J. R., Hall, H. L. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((A+comparison+of+gamma+spectra+from+trinitite+versus+irradiated+synthetic+nuclear+melt+glass%5BTitle%5D)+AND+%22J+Radioanal+Nucl+Chem%22%5BJournal%5D)">A comparison of gamma spectra from trinitite versus irradiated synthetic nuclear melt glass.</a> J Radioanal Nucl Chem. , (2015).</li>
<li>Fahey, J., Zeissler, C. J., Newbury, D. E., Davis, J., Lindstrom, R. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Postdetonation+nuclear+debris+for+attribution%5BTitle%5D)+AND+%22Proc+Natl+Acad+Sci+U+S+A%22%5BJournal%5D)">Postdetonation nuclear debris for attribution.</a> Proc Natl Acad Sci U S A. 107 (47), 20207-20212 (2010).</li>
<li>Bellucci, J. J., Simonetti, A., Koeman, E. C., Wallace, C., Burns, P. C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((A+detailed+geochemical+investigation+of+post-nuclear+detonation+trinitite+glass+at+high+spatial+resolution%3A+Delineating+anthropogenic+vs.+natural+components%5BTitle%5D)+AND+%22Chem+Geol%22%5BJournal%5D)">A detailed geochemical investigation of post-nuclear detonation trinitite glass at high spatial resolution: Delineating anthropogenic vs. natural components.</a> Chem Geol. 365, 69-86 (2014).</li>
<li>Donohue, P. H., Simonetti, A., Koeman, E. C., Mana, S., Peter, C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Nuclear+Forensic+Applications+Involving+High+Spatial+Resolution+Analysis+of+Trinitite+Cross-Sections%5BTitle%5D)+AND+%22J+Radioanal+Nucl+Chem%22%5BJournal%5D)">Nuclear Forensic Applications Involving High Spatial Resolution Analysis of Trinitite Cross-Sections.</a> J Radioanal Nucl Chem. , (2015).</li>
<li>Eaton, G. F., Smith, D. K. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Aged+nuclear+explosive+melt+glass%3A+Radiography+and+scanning+electron+microscope+analyses+documenting+radionuclide+distribution+and+glass+alteration%5BTitle%5D)+AND+%22J+Radioanal+Nucl+Chem%22%5BJournal%5D)">Aged nuclear explosive melt glass: Radiography and scanning electron microscope analyses documenting radionuclide distribution and glass alteration.</a> J Radioanal Nucl Chem. 248 (3), 543-547 (2001).</li>
<li>Kersting, A. B., Smith, D. K. <a target="_blank" href="http://scholar.google.com/scholar?hl=en&safe=off&q=author%3aKersting%2C+AB+%22Observations+of+Nuclear+Explosive+Melt+Glass+Textures+and+Surface+Areas%22">Observations of Nuclear Explosive Melt Glass Textures and Surface Areas</a>. , Lawrence Livermore National Laboratory. (2006).</li>
<li><a target="_blank" href="http://scholar.google.com/scholar?hl=en&safe=off&q=%22IAEA+Safeguards+Glossary%22">IAEA Safeguards Glossary</a>. , 2001st ed, IAEA. Vienna, Austria. (2001).</li>
<li>Glasstone, S., Dolan, P. <a target="_blank" href="http://scholar.google.com/scholar?hl=en&safe=off&q=author%3aGlasstone%2C+S+%22Effects+of+Nuclear+Weapons%22">Effects of Nuclear Weapons</a>. , 3rd ed, United States DOD/DOE. (1977).</li>
<li>Carney, K. P., Finck, M. R., McGrath, C. A., Martin, L. R., Lewis, R. R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((The+development+of+radioactive+glass+surrogates+for+fallout+debris%5BTitle%5D)+AND+%22J+Radioanal+Nucl+Chem%22%5BJournal%5D)">The development of radioactive glass surrogates for fallout debris.</a> J Radioanal Nucl Chem. 299 (1), 363-372 (2013).</li>
<li>Molgaard, J. J., Auxier, J. D., Hall, H. L. A Comparison of Activation Products in Different Types of Urban Nuclear Melt Glass. American Nuclear Society Annual Meeting, , American Nuclear Society. (2015).</li>
</ol>

Este trabalho foi realizado sob o número de concessão DE-NA0001983 do Programa Stewardship Science Academic Alliances (SSAA) da National Nuclear Security Administration (NNSA).

Nota sobre passos 1.2.2 e 1.2.3: A quantidade exata de UNH vai variar dependendo do cenário que está sendo simulado. As fórmulas de planeamento desenvolvidos por Giminaro et al., Pode ser utilizado para seleccionar a massa apropriada de urânio de uma determinada amostra 13, conforme discutido na secção &quot;Amostra A activação&quot; do presente documento. Além disso, óxido de urânio (UO 2 ou U 3 O 8) pode ser usado em lugar de UNH, se disponível, e a fracção de massa...

Preocupações com o potencial uso malicioso de armas nucleares por terroristas ou nações desonestas destacaram a importância da análise forense nuclear para fins de atribuição. 1 Técnicas rápidas de análise pós-detonação são desejáveis para encurtar o cronograma de atribuição o máximo possível. O desenvolvimento e validação de tais técnicas requer amostras realistas de detritos nucleares para teste. Os testes nucleares não ocorrem mais nos Estados Unidos e os detritos nucleares da superfície da era dos testes não estão prontamente disponíveis (com exceção da trinitita - o vidro derretido produzido pelo primeiro teste nuclear no local da trindade) e, portanto, são necessários detritos substitutos realistas. 
O objetivo principal do método descrito aqui é a produção de detritos nucleares substitutos realistas semelhantes à trinitita. Amostras sintéticas de vidro fundido nuclear que estão prontamente disponíveis para a comunidade acadêmica podem ser usadas para testar técnicas de análise existentes e desenvolver novos métodos, como termocromatografia para análise rápida pós-detonação. 2 Com esse objetivo em mente, o presente estudo está focado na produção de amostras que imitam a trinitita, mas não contêm nenhuma informação sensível sobre o design de armas. Os componentes de combustível e adulteração dentro dessas amostras são completamente genéricos e a comparação com a trinitita é baseada na química, morfologia e características físicas. As semelhanças entre a trinitita e o vidro nuclear sintético produzido neste estudo foram discutidas anteriormente. 3
O objetivo deste artigo é delinear os detalhes do processo de produção usado na Universidade do Tennessee (UT). Este processo de produção foi desenvolvido com dois parâmetros principais em mente: 1) a composição do material incorporado ao vidro fundido nuclear e 2) a temperatura de fusão do material. Existem métodos para estimar a temperatura de fusão de redes formadoras de vidro4 e essas técnicas foram empregadas aqui, juntamente com experimentos adicionais para determinar a temperatura de processamento ideal para a matriz de trinitita. 5
Métodos alternativos para a produção de detritos substitutos foram publicados recentemente. O uso de lasers de alta potência tem a vantagem de criar temperaturas suficientemente altas para causar fracionamento elementar dentro da matriz alvo. 6 Substratos cromatográficos porosos têm sido usados para produzir pequenas partículas semelhantes às partículas de precipitação usando métodos de fase condensada7. O último método é mais útil para a produção de detritos particulados (precipitação nuclear) e foi demonstrado com metais naturais. As vantagens do método apresentado aqui são 1) simplicidade, 2) reprodutibilidade e 3) escalabilidade (os tamanhos das amostras podem variar de pequenas esferas a grandes pedaços de vidro fundido). Além disso, este método é expansível tanto em termos de produção quanto de variedade de cenários explosivos cobertos, e já foi demonstrado usando materiais radioativos. Uma amostra foi ativada com sucesso no Reator de Isótopos de Alto Fluxo (HFIR) no Laboratório Nacional de Oak Ridge (ORNL). Compostos naturais de urânio foram adicionados à matriz antes da fusão e os produtos de fissão foram produzidos in situ por irradiação de nêutrons. 
Métodos na indústria de fabricação de vidro e aqueles empregados para fins de imobilização de resíduos radioativos8 foram consultados no desenvolvimento do método aqui apresentado. Os efeitos únicos da radiação em vidros são de interesse inerente9 e constituirão uma importante área de estudo à medida que esse método for desenvolvido. 
O método descrito abaixo é apropriado para qualquer aplicação em que uma amostra de vidro fundido a granel seja desejada. Essas amostras se assemelham mais ao material encontrado perto do epicentro de uma explosão nuclear. Amostras de vários tamanhos podem ser produzidas, no entanto, métodos que empregam tochas de plasma ou lasers serão mais úteis para simular detritos de partículas finas. Além disso, os HTFs comerciais não atingem temperaturas altas o suficiente para causar fracionamento elementar para uma ampla gama de elementos. Este método deve ser empregado quando as características físicas e morfológicas são de importância primordial.

<table><tbody><tr><td>Forno de Alta Temperatura (HTF)</td><td>Carbolite</td><td>HTF 18</td><td>1.800 &#176; C HTF usado para derreter amostras</td></tr><tr><td>Forno de gota de alta temperatura</td><td>CM Inc.</td><td>1706 BL</td><td>1.700 &# 176; C Forno de gota usado para derreter amostras</td></tr><tr><td>Cadinhos de grafite</td><td>SCP Science</td><td>040-060-041</td><td>Cadinhos de grafite de alta pureza de 27 ml (pacote com 10)</td></tr><tr><td>Pinças de cadinho</td><td>Grainger</td><td>5ZPV0</td><td>26 pol., pinças de aço inoxidável para manuseio de cadinhos</td></tr><tr><td>Luvas resistentes ao calor</td><td>Grainger</td><td>8814-09</td><td>Luvas usadas para proteger as mãos do calor durante a introdução/remoção da amostra</td></tr><tr><td>Argamassa & Pilão</td><td>Fisherbrand</td><td>S337631</td><td>300 ml, Almofariz e pilão de cerâmica para pó e mistura</td></tr><tr><td>Micro Balance</td><td>Grainger</td><td>8NJG2</td><td>220 g Cap, balança de alta precisão para medir a massa de pó</td></tr><tr><td>Espátulas</td><td>Fisherbrand</td><td>14374</td><td>Espátulas de metal para medir pequenas quantidades de pó</td></tr><tr><td>SiO2</td><td>Sigma-Aldrich</td><td>274739-5KG</td><td>Quartz Sand&nbsp; Número CAS: 14808-60-7</td></tr><tr><td>Al2O3</td><td>Sigma-Aldrich</td><td>11028-1KG</td><td>Óxido de Alumínio em Pó&nbsp; Número CAS: 1344-28-1</td></tr><tr><td>CaO</td><td>Sigma-Aldrich</td><td>12047-2.5KG</td><td>Pó de Óxido de Cálcio&nbsp; Número CAS: 1305-78-8</td></tr><tr><td>FeO</td><td>Sigma-Aldrich</td><td>400866-25G</td><td>Pó de Óxido de Ferro&nbsp; Número CAS: 1345-25-1</td></tr><tr><td>MgO</td><td>Sigma-Aldrich</td><td>342793-250G</td><td>Pó de Óxido de Magnésio&nbsp; Número CAS: 1309-48-4</td></tr><tr><td>Na2O</td><td>Sigma-Aldrich</td><td>36712-25G</td><td>Pó de Óxido de Sódio&nbsp; Número CAS: 1313-59-3</td></tr><tr><td>KOH</td><td>Sigma-Aldrich</td><td>278904-250G</td><td>Pellets de Hidróxido de Potássio&nbsp; Número CAS: 12030-88-5</td></tr><tr><td>MnO</td><td>Sigma-Aldrich</td><td>377201-500G</td><td>Pó de Óxido de Manganês&nbsp; Número CAS: 1344-43-0</td></tr><tr><td>TiO2</td><td>Sigma-Aldrich</td><td>791326-5G</td><td>Contas de Óxido de Titânio&nbsp; Número CAS: 12188-41-9</td></tr></tbody></table>

produção de synthetic nuclear melt vidro

Production of Synthetic Nuclear Melt Glass

Detritos nucleares substitutos realistas são necessários dentro da comunidade forense nuclear para testar e validar técnicas de análise pós-detonação. Aqui, descrevemos um novo processo para produzir detritos superficiais a granel usando um forno de alta temperatura. O material desenvolvido neste estudo é física e quimicamente semelhante à trinitita (o vidro fundido produzido pelo primeiro teste nuclear). Supõe-se que este vidro nuclear sintético seja semelhante ao material vitrificado produzido perto do epicentro (marco zero) de qualquer detonação nuclear de superfície em um ambiente desértico. O processo descrito aqui pode ser aplicado para produzir outros tipos de vidro fundido nuclear, incluindo aquele que provavelmente será formado em um ambiente urbano. Isso pode ser feito simplesmente modificando a matriz precursora à qual esse processo de produção é aplicado. O vidro fundido produzido neste estudo foi analisado e comparado com a trinitita, revelando uma morfologia cristalina, estrutura física, fração de vazios e composição química comparáveis.

As amostras não radioactivos produzidos neste estudo foram comparados com trinitite e as Figuras 1-3 mostram que as propriedades físicas e morfologia são de fato semelhante. A Figura 1 fornece fotografias que revelam as semelhanças na cor e textura que são observados ao nível macroscópico. A Figura 2 mostra Microscópio Eletrônico de Varredura (MEV) imagens secundárias Electron (SE) que revelam características semelhantes ao nível micron. A análise SEM f...

Um protocolo para a produção de vidro fundido nuclear sintético, semelhante à trinitita, é apresentado.

Produção de Synthetic Nuclear Melt vidro

Realistic surrogate nuclear debris is needed within the nuclear forensics community to test and validate post-detonation analysis techniques. Here we ...

O objetivo geral deste procedimento é produzir vidro fundido nuclear simulado para preparar materiais que possam ser usados como padrões pela comunidade de perícias nucleares. O método que você verá hoje pode ajudar a responder questões fundamentais na área de perícia nuclear, como os desafios na análise de vidro fundido nuclear e os efeitos que interferem nas técnicas de espectrometria de massas. A principal desvantagem desta técnica é que ela não consegue simular as pressões encontradas nas detonações de armas nucleares.No vídeo de hoje, você verá meus alunos de pós-graduação, Andrew Giminaro e Jonathan Gill, demonstrando como produzir um vidro de fusão nuclear sintético. Primeiro, obtenha as quantidades necessárias de areia de quartzo e componentes adicionais conforme indicado no protocolo descrito no texto. Utilize uma microbalança e uma espátula pequena para medir com precisão as frações mássicas de cada composto listado aqui.Em seguida, utilize o almofariz e o pilão para pulverizar e misturar completamente os compostos, formando uma mistura homogênea em pó. Agite utilizando um misturador de esferas imediatamente antes da próxima etapa. Após isso, obtenha alguns cristais de tamanho médio de UNH.Dentro de uma capela de exaustão, pulverize os cristais de UNH usando um almofariz e pistilo para formar um pó fino de grânulos de um a dois mícrons. Adicione 33,75 microgramas de UNH por grama da matriz precursora não radioativa. Misture completamente a mistura em pó, incluindo o UNH, usando um almofariz e pistilo.Neste ponto, preencha um recipiente cerâmico grosso, como um almofariz, com aproximadamente 100 gramas de areia de quartzo puro e mantenha-o à temperatura ambiente próximo ao local do forno onde as amostras serão fundidas. Pré-aqueça o forno de alta temperatura até 1.500 graus Celsius. Após medir cuidadosamente um grama da mistura em pó radioativo, coloque-o em um cadinho de grafite de alta pureza.Em seguida, coloque cuidadosamente o cadinho no forno de alta temperatura aquecido utilizando uma longa pinça de aço para cadinhos. Após fundir a mistura por 30 minutos, remova-a do forno e despeje-a em um almofariz cheio de areia. As fotografias revelam as semelhanças na cor e textura das amostras não radioativas e da trinitite produzida neste estudo, observadas ao nível macroscópico.Imagens de elétrons secundários de microscópios eletrônicos de varredura, que revelam características semelhantes em nível de micrômetro, são exibidas aqui. Numerosos vazios são observados e os defeitos e a heterogeneidade são semelhantes tanto na trinitita quanto nas amostras sintéticas. Uma comparação dos espectros de difração de raios X em pó para a trinitita e as amostras sintéticas é mostrada aqui.O quartzo é o único mineral presente em ambos os casos e as intensidades dos picos são semelhantes, sugerindo um grau comparável de amorfo. Uma vez dominada, esta técnica pode ser realizada em quatro horas, se executada corretamente. Ao realizar este método, é muito importante ter muita cautela com as altas temperaturas utilizadas neste procedimento.Após este procedimento, outros métodos, como o desenvolvimento de vidro de fusão urbano, podem ser realizados para responder perguntas adicionais, como as diferenças entre morfologias e cidades. Após seu desenvolvimento, esta técnica abriu caminho para pesquisadores na área de perícia nuclear explorarem as possíveis deficiências e técnicas analíticas necessárias para realizar análises em detritos pós-detonação. Após assistir a este vídeo, você deverá ter uma boa compreensão de como produzir e analisar detritos nucleares simulados que se assemelham estreitamente aos detritos encontrados no teste Trinity.Ao trabalhar com fornos de alta temperatura, isso pode ser extremamente perigoso e precauções, como o uso de proteção ocular apropriada e equipamento de proteção individual adequado para temperaturas elevadas, devem sempre ser tomadas ao realizar este método.

production-of-synthetic-nuclear-melt-glass

Research

JoVE Journal

Engineering

Engenharia

Apresentamos a síntese de alta temperatura dos precursores de intermetálicos...

Síntese dos Nove átomo-Deltahedral Íons Zintl de germânio e sua funcionalização com grupos orgânicos

Um método de fabrico aditivo indirecta combinando uma impressão em 3D de polímeros com uma fundição centrífuga é delineado para o fabrico de metais treliça octeto 3D (Al e Cu ligas) com um comprimento de célula unitária de 5 mm com uma espessura de parede de 0,5 mm.

Fabrication indireta de Malha Metals com cortes finos Usando Fundição

Apresentamos as experiências em que combustível nuclear real, revestimento e materiais de contenção são laser aquecido a temperaturas além de 3.000 K, enquanto que seu comportamento é estudado por espectroscopia de esplendor e análise térmica. Estas experiências simulam, em uma escala de laboratório, a formação de uma lava-fase após um colapso de núcleo do reator nuclear.

Aquecimento a laser e espectrometria de radiância para o estudo de materiais nucleares em condições que simulam um acidente em uma usina nuclear

Este manuscrito propõe um método de química suave para sintetizar microesferas de vidro oco (HGM) super-hidrofóbicas revestidas com TiO2 com altas propriedades reflexivas de infravermelho.

TiO<sub&gt; 2</subMicroesferas de vidro ocas&gt; -Revestido com propriedades super-hidrofóbicas e alta IR-reflexivo sintetizados por um método Soft-química

Este protocolo descreve a fabricação de superfícies de vidro ótico-qualidade adsorvido com compostos contendo hidrocarbonetos de cadeia longa que podem ser usados para monitorar fusão macrófago de espécimes vivos e permite a microscopia de super-resolução de espécimes fixos .

Fabricação de superfícies de vidro de qualidade óptica para estudar a fusão do macrófago

Aqui, apresentamos um protocolo para descrever as investigações ex situ e em situ das transformações estruturais em copos metálicos. Utilizamos métodos analíticos baseados em nuclear que inspecionam interações hyperfine. Vamos demonstrar a aplicabilidade da espectrometria de Mössbauer e espalhamento frontal nuclear de radiação síncrotron durante experimentos orientados a temperatura.

Métodos de Ex Situ e In Situ investigações de transformações estruturais: O caso de cristalização de vidros metálicos

Os procedimentos chaves para aperfeiçoar o processo da selagem e para conseguir a monitoração tempo real da estrutura do selo do metal-à-vidro (MTGS) são descritos em detalhe. O sensor grating incorporado da fibra Bragg (FBG) é projetado conseguir a monitoração em linha da temperatura e do esforço residual de alto nível no MTGS com monitoração simultânea da pressão ambiental.

Processo de vedação otimizado e monitoramento em tempo real de estruturas de vedação de vidro a metal

Aqui, apresentamos um protocolo para sintetizar dois tipos de cristais UTe2 : aqueles que exibem supercondutividade robusta, através da síntese de transporte de vapor químico, e aqueles que carecem de supercondutividade, via síntese de fluxo metálico derretido.

Comparação de dois métodos diferentes de síntese de cristais únicos de ditelluride de urânio supercondutor

Um protocolo é apresentado para a síntese de nanomateriais luminescentes persistentes (PLNPs) e suas potenciais aplicações em displays regraváveis e processamento artístico utilizando o efeito afterglow sob irradiação de luz ultravioleta (365 nm).

Síntese de nanopartículas luminescentes persistentes para displays regraváveis e aplicações de iluminação

A Espectroscopia Raman de Célula Fluida (FCRS) permite observações em operação de fenômenos de reação e transporte durante a corrosão aquosa de vidros de silicato em nível microscópico, em temperaturas elevadas e em tempo real. Sem interromper os processos em andamento, o FCRS fornece informações sobre mecanismos de reação, cinética e processos de transporte.

Espectroscopia Raman de célula fluida para estudos operacionais de fenômenos de reação e transporte durante a corrosão de vidro de silicato

Aprenda a produzir vidro nuclear sintético para análises forenses nucleares usando quartzo e técnicas de espectrometria de massa. Este método estabelece padrões para pesquisa em vidro de fusão nuclear.

Produção de Synthetic Nuclear Melt vidro

Explorar mais vídeos