Name: Gerando junções de regaço através da soldadura do ponto do stir da fricção no aço DP780 (Vídeo) | JoVE Journal
Uploaded: 2019-08-13T12:30:00.000+00:00
Duration: 7 min 18 s
Description: Aprenda a soldar junções de regaço em aço DP780 usando soldagem por fricção e mistura no ponto. Este método oferece temperaturas mais baixas, sem respingos e maior estabilidade no processo de fabricação.

ai_agent_IP

ai_agent

maintenance

instantTrialDurationMinutes

isBiopharma

enableNewMyJoveSectionDesign

educationFeatures

seoMetaApi

ai_copilot_institution_blacklist

ai_chat_institution_blacklist

freeAccessWindow

ssoRoleCapture

scheduledMaintenanceBanner

joveLabsFeatures

disable_autoplay_for_bots

extended_trial_duration

5 minutes

playerTrialDesktop

Agradecemos ao Dr. K. C. Yang na empresa China-Steel pelo apoio material e desejo expressar nossa gratidão ao Sr. RG Wang, C. K. Wang e B. Y. Hong no MIRDC para assistência com o FSSW experimental. Esta pesquisa foi apoiada pelo centro de pesquisa e desenvolvimento de indústrias metálicas, Kaohsiung, Taiwan, ROC.

1. preparação do material
Nota: a máquina de 1,6 mm de espessura DP780 folhas em 40 mm x 125 mm cupons. As junções de FSSW são projetadas como espécimes da tesoura da volta para os testes mecânicos. Juntar 2 125 mm por folhas de 40 mm com uma sobreposição de 35 mm por 40 mm, seguindo a norma RSW NF ISO 18278-2; 2005. um projeto de geometria ferramenta de diamante policristalino com um ombro Cone truncado. O desenho da geometria é mostrado na Figura 1a. O diâmetro do pino é de 5 mm; o comprimento é 2,5 milímetros, e a largura do ombro é 10 milímetros. O pino de ferramenta real é mostrado na Figura 1b.
<ol><li>Diretrizes de segurança<ol>
<li>Use dispositivos como um capuz ou defletor, óculos e luvas para proteção.</li>
		<li>Fique atrás do capô ou do defletor. Use óculos e luvas para evitar o contato com respingo ou danos causados pelo calor.</li>
	</ol>
</li>
	<li>Configuração da máquina FSSW<ol>
<li>Manufatura todas as junções usando uma máquina MIRDC-feita do soldador do stir da fricção.</li>
		<li>Registre a força axial Z e a profundidade de penetração durante cada operação de junção usando o sistema de aquisição de dados incorporado (DAQ).</li>
	</ol>
</li>
	<li>Configurações de parâmetro<ol>
<li>Neste estudo, use os seguintes parâmetros: uma velocidade de rotação do pino da ferramenta de 2.500 rpm, 4 s do tempo de permanência do pino da ferramenta, e uma taxa PF 0,5 mm/s do pino de ferramenta mergulha na folha.</li>
		<li>Otimize os parâmetros para o operador. A escala da velocidade de rotação é 1.000-2.500 rpm. A escala do tempo de permanência pode ser de 2-10 s, e a taxa de mergulho pode ser 0.1-0.5 mm/s.</li>
	</ol>
</li>
</ol>2. procedimento
Nota: o espaço de trabalho é mostrado na Figura 2. Todos os procedimentos de fabricação são concluídos no espaço de trabalho. Antes do procedimento, as sequências do processo de soldagem são compostas por uma combinação de rotações de ferramentas e profundidades de penetração, bem como uma série de sequências, incluindo pré-aquecimento, mergulhando, habitação, retracção e pós-aquecimento. Todas as etapas são mostradas na Figura 3 na forma de um fluxograma de trabalho.
<ol><li>DP780 preparação da peça<ol>
<li>Antes do processo de soldagem, assegure-se de que não haja substratos de impureza contaminando as peças. Use tecidos de microfibras de malha para limpar a superfície da peça de trabalho para eliminar quaisquer partículas pequenas.</li>
	</ol></li>
	<li>Coloque a peça DP780 e prenda 2 DP780 folhas (tamanho: 125 mm x 40 mm) com uma sobreposição de 35 mm. fixe as peças de trabalho limpas numa bigorna para evitar a deslocação.</li>
	<li>Assegure-se de que o pino esteja limpo para evitar a contaminação do substrato impuro. Use tecidos de microfibra de malha para limpar a superfície do pino de ferramenta para eliminar pequenas partículas.</li>
	<li>Fixe o pino com um grampo na máquina.<ol>
<li>Aparafuse firmemente o pino de ferramenta novamente para fixação do pino de ferramenta.</li>
		<li>Preste atenção à etapa de aperto do pino. Assegure-se de que o pino esteja apertado firmemente na máquina para evitar o perigo. A ferramenta giratória é cercada por um anel de aperto nonrotatório com que os peças são pressionados firmemente um contra o outro antes e durante a soldadura aplicando uma força de aperto. A ilustração mostrada na Figura 3a observa o anel da braçadeira usado para fixar o pino de ferramenta. Após esta etapa, a produção é mostrada no fluxograma.</li>
		<li>Assegure a segurança.</li>
		<li>Confirme que o pino de rotação de alta velocidade sem um anel de aperto afrouxa. Quando o pino de ferramenta é colocado na máquina, assegure-se de que o pino de ferramenta não separe da braçadeira durante a rotação para razões da segurança. O pino de ferramenta usa uma baixa taxa de rotação de 10 a 100 RPM em 1 minuto. A velocidade pode acelerar de 100 a 1.000 rpm dentro de 1 minuto (Figura 3B).</li>
	</ol></li>
	<li>Configurações da máquina<ol>
<li>Use os seguintes parâmetros: uma velocidade de rotação de 3.000 rpm, uma permanência de 4 s e uma taxa de imersão de 0,5 mm/s (Figura 3C).</li>
	</ol></li>
	<li>Calibrar o local de soldagem (Figura 3D e o produto real mostrado na figura 4a).<ol>
<li>Ajuste o pino na máquina do soldador do ponto da agitação. A folga entre o pino e a peça de trabalho é menor que 5 cm para calibrar a localização conjunta. Depois que o local é confirmado, mova-se para o processo de soldagem.</li>
	</ol></li>
	<li>Durante a soldagem, use óculos e luvas para evitar ferimentos.<ol>
<li>Inicie o processo de soldagem com a ferramenta rotação de alta velocidade para mergulhar o pino da ferramenta na peça de trabalho. O ombro da ferramenta contata os peças e para a rotação e retrona o pino.</li>
	</ol></li>
	<li>Mergulhar<ol>
<li>Gire o botão de agitação. Quando a máquina aquece, confirme que o pino de ferramenta está operando consistentemente em uma velocidade de rotação de 2.500 rpm. Assegure-se de que o pino de ferramenta esteja apertado bem a rotação de alta velocidade em 2.500 rpm. O pino mergulha nos peças uma rotação de alta velocidade e o ombro contata os peças em uma velocidade angular elevada (Figura 3E). O produto real é mostrado na Figura 4B.</li>
	</ol></li>
	<li>Mexendo<ol>
<li>Como o pino de ferramenta mergulhou continua mexendo na peça de trabalho, suavizar a interface do pino e o material do calor de fricção para criar o grão. Quando o ombro do pino de ferramenta entra em contato com a parte superior da peça de trabalho, pare o processo porque a alta rotação do pino de ferramenta pode gerar altas temperaturas. É importante usar a engrenagem protetora que assegura a segurança operacional (veja Figura 3F.) O produto real é mostrado na Figura 4C.</li>
	</ol></li>
	<li>Retracção<ol>
<li>Desenhe o pino da ferramenta na direção vertical. Após o procedimento, o pino cria o ponto de solda da chave-furo na junção de volta. Observe que a solda de ponto de agitação de atrito pára nesta etapa (Figura 3G). O produto real é mostrado na Figura 4e.</li>
	</ol></li>
	<li>Retire as peças de trabalho.<ol>
<li>Desligue a alimentação da máquina.</li>
		<li>Depois que a soldadura é terminada, remova as peças de trabalho da bigorna. Observe as amostras para rachaduras e falta de fusão.</li>
		<li>Retire o pino da ferramenta.</li>
		<li>Após o procedimento, retire o pino da ferramenta do anel de aperto. A aparência do pino da ferramenta é observada e verificada (Figura 5).</li>
	</ol></li>
</ol>3. avaliação da propriedade mecânica
<ol><li>Exame de microscopia das soldas FSSW (Figura 3h)<ol>
<li>Preparação microscópica da amostra</li>
		<li>Meça a área transversal da região ligada usando uma imagem do microscópio ótico e uma análise de imagem secundária do elétron. Prepare as amostras microscópicas usando papel de carboneto de silício aterrado com um tamanho de grão variando de 200 a 2.000 começando com um tamanho de grão de 200 e aumentando em seqüência. Polir as amostras com 0, 3% de alumina e etch com uma solução de nital de 4% para 7 – 10 s à temperatura ambiente.</li>
		<li>Observação da microscopia</li>
		<li>Observar e caracterizar as microestruturas utilizando microscopia óptica e microscopia eletrônica de varredura. Use uma tensão de 20 kV, e uma distância de trabalho de 10 μm. Da microscopia ótica, toda a linha minúscula da rachadura ou a falta de uma zona da fusão podem ser determinadas. Use microscopia eletrônica de varredura para analisar a distribuição de martensita e austenita e o tamanho do grão.</li>
	</ol>
</li>
	<li>Microdureza<ol>
<li>Verifique os experimentos de microdureza mais de 3 vezes. Os valores eram muito pequenos para denotar claramente o desvio padrão.</li>
		<li>Pressione o indenter do diamante de Vickers com uma amostra da carga de teste de 300 g e 0,5 milímetros por o teste.</li>
		<li>Realize o teste de microdureza da chapa de aço DP780 usando uma máquina de teste de microdureza com uma carga de 300 g e um tempo de retenção de 15 s. O teste da microdureza revelou a distribuição da dureza e os valores individuais da dureza na zona do stir, na zona termomecânica do efeito, na zona afetada calor, e no metal baixo das soldas.</li>
	</ol>
</li>
</ol>

<ol><li>Mazda. Mazda Develops World’s First Aluminum Joining Technology Using Friction Heat. , Available from:
 <a target="_blank" href="https://www2.mazda.com/en/publicity/release/archive/2003/200302/0227e.html">https://www2.mazda.com/en/publicity/release/archive/2003/200302/0227e.html</a> (2003).</li>
<li>Piccini, J. M., Svoboda, H. G. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Effect+of+pin+length+on+Friction+Stir+Spot+Welding+%28FSSW%29+of+dissimilar+Aluminum-steel+joints%5BTitle%5D)+AND+%22Procedia+Materials+Science%22%5BJournal%5D)">Effect of pin length on Friction Stir Spot Welding (FSSW) of dissimilar Aluminum-steel joints.</a> Procedia Materials Science. 9, 504-513 (2015).</li>
<li>Iwashita, T. Method and Apparatus for joining. , USA patent US6601751B2 (2003).</li>
<li>Allen, C. D., Arbegast, W. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Evaluation+of+Friction+Spot+Welds+in+Aluminium+Alloys%5BTitle%5D)+AND+%22SAE+Technical%22%5BJournal%5D)">Evaluation of Friction Spot Welds in Aluminium Alloys.</a> SAE Technical. , No 2005-2001-1252 (2005).</li>
<li>Feng, Z., et al. <a target="_blank" href="http://scholar.google.com/scholar?hl=en&safe=off&q=author%3aFeng%2C+Z+%22Friction+Stir+Spot+Welding+of+Advanced+HighStrength+Steels+-+a+Feasibility+Study%22">Friction Stir Spot Welding of Advanced HighStrength Steels - a Feasibility Study</a>. , SAE 2005 Congress, SAE-International, Detroit, MI, Technical Paper No 2005-2001-1248 (2005).</li>
<li>Miles, M. P., Nelson, T. W., Steel, R., Olsen, E., Gallagher, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Effect+of+friction+stir+welding+conditions+on+properties+and+microstructures+of+high+strength+automotive+steel%5BTitle%5D)+AND+%22Science+and+Technology+of+Welding+and+Joining%22%5BJournal%5D)">Effect of friction stir welding conditions on properties and microstructures of high strength automotive steel.</a> Science and Technology of Welding and Joining. 14 (3), 228-232 (2009).</li>
<li>Feng, Z., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Friction+stir+spot+welding+of+advanced+high-Strength+steels-a+feasibility+study%5BTitle%5D)+AND+%22SAE+Technical+Paper+Series+2005-01-1248%22%5BJournal%5D)">Friction stir spot welding of advanced high-Strength steels-a feasibility study.</a> SAE Technical Paper Series 2005-01-1248. , (2005).</li>
<li>Santella, M., Hovanski, Y., Frederick, A., Grant, G., Dahl, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Friction+stir+spot+welding+of+DP780+carbon+steel%5BTitle%5D)+AND+%22Science+and+Technology+of+Welding+and+Joining%22%5BJournal%5D)">Friction stir spot welding of DP780 carbon steel.</a> Science and Technology of Welding and Joining. 15 (4), 271-278 (2010).</li>
<li>Saunders, N., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Joint+strength+in+high+speed+friction+stir+spot+welded+DP+980+steel%5BTitle%5D)+AND+%22International+Journal+of+Precision+Engineering+and+Manufacturing%22%5BJournal%5D)">Joint strength in high speed friction stir spot welded DP 980 steel.</a> International Journal of Precision Engineering and Manufacturing. 15 (5), 841-848 (2014).</li>
<li>Khan, M. I., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Resistance+and+friction+stir+spot+welding+of+DP600%3A+a+comparative+study%5BTitle%5D)+AND+%22Science+and+Technology+of+Welding+and+Joining%22%5BJournal%5D)">Resistance and friction stir spot welding of DP600: a comparative study.</a> Science and Technology of Welding and Joining. 12 (2), 175-182 (2007).</li>
<li>Sarkar, R., Sengupta, S., Pal, T. K., Shome, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Microstructure+and+Mechanical+Properties+of+Friction+Stir+Spot-Welded+IF%2FDP+Dissimilar+Steel+Joints%5BTitle%5D)+AND+%22Metallurgical+and+Materials+Transactions+A%22%5BJournal%5D)">Microstructure and Mechanical Properties of Friction Stir Spot-Welded IF/DP Dissimilar Steel Joints.</a> Metallurgical and Materials Transactions A. 46 (11), 5182-5200 (2015).</li>
<li>Yang, X. W., Fu, T., Li, W. Y. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Friction+Stir+Spot+Welding%3A+A+Review+on+Joint+Macro-+and+Microstructure%2C+Property%2C+and+Process+Modelling%5BTitle%5D)+AND+%22Advances+in+Materials+Science+and+Engineering%22%5BJournal%5D)">Friction Stir Spot Welding: A Review on Joint Macro- and Microstructure, Property, and Process Modelling.</a> Advances in Materials Science and Engineering. 2014, 11(2014).</li>
<li>Esther, T. A., Stephen, A. A. Trends in Welding Research 2012: Proceedings of the 9th International Conference. <a target="_blank" href="http://scholar.google.com/scholar?hl=en&safe=off&q=author%3aEsther%2C+TA+%22Materials+Characterisation+of+Friction+Stir+Processed+6082+Aluminum+Alloy%22">Materials Characterisation of Friction Stir Processed 6082 Aluminum Alloy</a>. DebRoy, T., et al. , ASM Press. Chicago, IL. 548-551 (2012).</li>
<li>Ghosh, P. K., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Influence+of+Weld+Thermal+Cycle+on+Properties+of+Flash+Butt+Welded+Mn-Cr-Mo+Dual+Phase+Steel%5BTitle%5D)+AND+%22ISIJ+International%22%5BJournal%5D)">Influence of Weld Thermal Cycle on Properties of Flash Butt Welded Mn-Cr-Mo Dual Phase Steel.</a> ISIJ International. 33 (7), 807-815 (1993).</li>
<li>Schultz, R. A. <a target="_blank" href="http://scholar.google.com/scholar?hl=en&safe=off&q=author%3aSchultz%2C+RA+%22Metallic+materials+trends+for+north+American+light+vehicles%22">Metallic materials trends for north American light vehicles</a>. , American Iron and Steel Institute. Michigan, US. Power point presentation of great designs in steel seminar (2007).</li>
<li>Horvath, C. <a target="_blank" href="http://scholar.google.com/scholar?hl=en&safe=off&q=author%3aHorvath%2C+C+%22Material+challenges+facing+the+automotive+and+steel+industries+from+globalization%22">Material challenges facing the automotive and steel industries from globalization</a>. , American Iron and Steel Institute, Michigan, USAmerican Iron and Steel Institute. Michigan, US. Power point presentation of great designs in steel seminar (2007).</li>
<li>Pouranvari, M., Marashi, S. P. H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Critical+review+of+automotive+steels+spot+welding%3A+process%2C+structure+and+properties%5BTitle%5D)+AND+%22Science+and+Technology+of+Welding+and+Joining%22%5BJournal%5D)">Critical review of automotive steels spot welding: process, structure and properties.</a> Science and Technology of Welding and Joining. 18 (5), 361-403 (2013).</li>
<li>Khan, M. S., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Welding+behaviour%2C+microstructure+and+mechanical+properties+of+dissimilar+resistance+spot+welds+between+galvannealed+HSLA350+and+DP600+steels%5BTitle%5D)+AND+%22Science+and+Technology+of+Welding+and+Joining%22%5BJournal%5D)">Welding behaviour, microstructure and mechanical properties of dissimilar resistance spot welds between galvannealed HSLA350 and DP600 steels.</a> Science and Technology of Welding and Joining. 14 (7), 616-625 (2009).</li>
<li>Ma, C., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Microstructure+and+fracture+characteristics+of+spot-welded+DP600+steel%5BTitle%5D)+AND+%22Materials+Science+and+Engineering%3A+A%22%5BJournal%5D)">Microstructure and fracture characteristics of spot-welded DP600 steel.</a> Materials Science and Engineering: A. 485 (1), 334-346 (2008).</li>
<li>Hilditch, T. B., Speer, J. G., Matlock, D. K. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Effect+of+susceptibility+to+interfacial+fracture+on+fatigue+properties+of+spot-welded+high+strength+sheet+steel%5BTitle%5D)+AND+%22Materials+%26+Design%22%5BJournal%5D)">Effect of susceptibility to interfacial fracture on fatigue properties of spot-welded high strength sheet steel.</a> Materials & Design. 28 (10), 2566-2576 (2007).</li>
<li>Yan, B., Zhu, H., Lalam, S. H., Baczkowski, S., Coon, T. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Spot+Weld+Fatigue+of+Dual+Phase+Steels%5BTitle%5D)+AND+%22SAE+Technical+Paper+Series+2004-01-0511%22%5BJournal%5D)">Spot Weld Fatigue of Dual Phase Steels.</a> SAE Technical Paper Series 2004-01-0511. , (2004).</li>
<li>Wilson, R. B., Fine, T. E. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Fatigue+behavior+of+spot+welded+high+strength+joints%5BTitle%5D)+AND+%22SAE+Technical+Paper+Series+1981-02-01%22%5BJournal%5D)">Fatigue behavior of spot welded high strength joints.</a> SAE Technical Paper Series 1981-02-01. , (1981).</li>
<li>Sun, X., Stephens, E. V., Khaleel, M. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Effects+of+fusion+zone+size+and+failure+mode+on+peak+load+and+energy+absorption+of+advanced+high+strength+steel+spot+welds+under+lap+shear+loading+conditions%5BTitle%5D)+AND+%22Engineering+Failure+Analysis%22%5BJournal%5D)">Effects of fusion zone size and failure mode on peak load and energy absorption of advanced high strength steel spot welds under lap shear loading conditions.</a> Engineering Failure Analysis. 15 (4), 356-367 (2008).</li>
<li>Pouranvari, M., Mousavizadeh, S. M., Marashi, S. P. H., Goodarzi, M., Ghorbani, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Influence+of+fusion+zone+size+and+failure+mode+on+mechanical+performance+of+dissimilar+resistance+spot+welds+of+AISI+1008+low+carbon+steel+and+DP600+advanced+high+strength+steel%5BTitle%5D)+AND+%22Materials+%26+Design%22%5BJournal%5D)">Influence of fusion zone size and failure mode on mechanical performance of dissimilar resistance spot welds of AISI 1008 low carbon steel and DP600 advanced high strength steel.</a> Materials & Design. 32 (3), 1390-1398 (2011).</li>
<li>Hsu, T. -I., Wu, L. -T., Tsai, M. -H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Resistance+and+friction+stir+spot+welding+of+dual-phase+%28DP+780%29%E2%80%94a+comparative+study%5BTitle%5D)+AND+%22The+International+Journal+of+Advanced+Manufacturing+Technology%22%5BJournal%5D)">Resistance and friction stir spot welding of dual-phase (DP 780)—a comparative study.</a> The International Journal of Advanced Manufacturing Technology. , (2018).</li>
<li>Piccini, J. M., Svoboda, H. G. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Effect+of+the+tool+penetration+depth+in+Friction+Stir+Spot+Welding+%28FSSW%29+of+dissimilar+aluminum+alloys%5BTitle%5D)+AND+%22Procedia+Materials+Science%22%5BJournal%5D)">Effect of the tool penetration depth in Friction Stir Spot Welding (FSSW) of dissimilar aluminum alloys.</a> Procedia Materials Science. 8, 868-877 (2015).</li>
<li>Aissani, M., Gachi, S., Boubenider, F., Benkedda, Y. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Design+and+Optimization+of+Friction+Stir+Welding+Tool%5BTitle%5D)+AND+%22Materials+and+Manufacturing+Processes%22%5BJournal%5D)">Design and Optimization of Friction Stir Welding Tool.</a> Materials and Manufacturing Processes. 25 (11), 1199-1205 (2010).</li>
<li>Zhang, Y. N., Cao, X., Larose, S., Wanjara, P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Review+of+tools+for+friction+stir+welding+and+processing%5BTitle%5D)+AND+%22Canadian+Metallurgical+Quarterly%22%5BJournal%5D)">Review of tools for friction stir welding and processing.</a> Canadian Metallurgical Quarterly. 51 (3), 250-261 (2013).</li>
<li>Nandan, R., DebRoy, T., Bhadeshia, H. K. D. H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Recent+advances+in+friction-stir+welding+%E2%80%93+Process%2C+weldment+structure+and+properties%5BTitle%5D)+AND+%22Progress+in+Materials+Science%22%5BJournal%5D)">Recent advances in friction-stir welding – Process, weldment structure and properties.</a> Progress in Materials Science. 53 (6), 980-1023 (2008).</li>
<li>Tang, W., Guo, X., McClure, J., Murr, L., Nunes, A. C. <a target="_blank" href="http://scholar.google.com/scholar?hl=en&safe=off&q=author%3aTang%2C+W+%22Heat+Input+and+Temperature+Distribution+in+Friction+Stir+Welding%22">Heat Input and Temperature Distribution in Friction Stir Welding</a>. 7, (1998).</li>
</ol>

Os autores não têm nada a revelar.

O estágio de mergulhando é o mais importante durante o processo de FSSW. Sem calor suficiente atrito proveniente do ombro do pino para suavizar a peça de trabalho, o pino vai fractura. Geometria da ferramenta, velocidade de rotação, tempo de permanência e profundidade de penetração da ferramenta26 os parâmetros do processo fssw desempenham um papel crítico na determinação da integridade articular. TPD e geometria da ferramenta27 particularmente têm um efeito importante sobr...

A soldadura do stir da fricção (FSW) foi relatada primeiramente em 1991 em TWI, Abington, Reino Unido1. Em 2003, Piccini e Svoboda determinaram um método superior de realçar as vantagens de FSW chamada soldadura do ponto da agitação da fricção (FSSW) para o uso em processos de fabricação comerciais do automóvel2. O método FSSW envolve a criação de uma junção de volta Spot sem derretimento da área em massa. O desenvolvimento mais importante para o uso da FSSW tem sido em ligas de alumínio, pois as ligas de Al se deformam no processo de soldagem condições de alta temperatura. O primeiro exemplo bem-sucedido foi na indústria automotiva, onde a fssw foi usada na fabricação de toda a porta traseira do RX-81,3,4 daMazda.
Enquanto isso, aço de alta resistência é o material dominante do corpo do carro, especificamente de aço de dupla fase. A literatura indica que DP600 produzidos com FSSW podem ter as mesmas propriedades que o metal de base, onde todas as regiões de soldagem possuem microestruturas e graus de dureza semelhantes5. Os métodos de FSSW para o uso do aço do DP em sua microestrutura da zona do stir (SZ), da zona thermos-mecanicamente afetada (TMAZ), e do modelo da falha de aço DP590 e DP600 foram estudados por alguns investigadores. Observaram diferenças na consistência da microestrutura (ferrite, bainite e martensita) de aço DP590 e DP600 em várias velocidades de rotação6,7,8,9,10. Alguns pesquisadores realizaram estudos comparativos de fssw e RSW para DP780 aços8,9. Eles relataram que tempos de junção mais longos e velocidades de rotação de ferramenta mais elevadas resultaram em uma área de colagem aumentada para todos os mergulhos, o que levou a uma maior força de cisalhamento e deslocou o modo de interfacial para puxar para fora. Concluíram também que a FSSW tinha uma força maior que a RSW. O processo FSSW inclui 3 etapas: mergulhando, mexendo e retração. A primeira etapa é mergulhar com um pino da ferramenta da rotação perto da folha da junção de regaço e obstruída na folha. O ombro giratório da ferramenta no processo de fssw pode gerar o calor de fricção. Na segunda etapa, o calor pode amaciar a folha e facilitar a obstrução do pino da ferramenta na folha, assim como habitar nos materiais para agitar dois peças junto e misturar em torno da área do pino. Finalmente, a pressão da imprensa do ombro da ferramenta nos peças pode realçar a ligação. Após o processo de soldagem, o pino pode ser retirado do buraco da fechadura. Os benefícios de FSSW comparado com o RSW são uma temperatura de soldadura mais baixa, nenhum espirro, e mais estabilidade no processo de manufactura.
Mesmo que estudos sobre o FSSW de aços avançados de alta resistência (AHSS) tenham sido relatados por vários pesquisadores, estudos sobre o FSSW de DP590, DP600 e DP780 têm se concentrado na microestrutura e nos modelos mecânicos e de falha usando vários processos Parâmetros. No presente estudo, considerou-se o FSSW de aço DP780. O protocolo do processo de FSSW foi relatado em detalhe, e a dureza individual na zona do stir, a zona thermos-mecanicamente afetada, e a zona calor-afetada, assim como o metal baixo foram avaliados baseou na microdureza medida.
Com o crescimento contínuo e a demanda pesada para a redução de peso nas indústrias automotrizes e aeroespaciais, a indústria automotriz mostrou um interesse crescente em AHSS e em junções de regaço. Por exemplo, o corpo de aço convencional de um carro, em média, tem mais de 2.000 junções de volta da solda do ponto11. Há 3 processos de soldadura comuns para as junções de regaço usadas na indústria, incluindo a soldadura do ponto da resistência, a soldadura do ponto do laser, e a soldadura do ponto da fricção12. Uma maneira de diminuir o peso é usando aços avançados de alta resistência (AHSS). Os materiais mais populares são os aços de dupla fase e de plasticidade induzida por transformação (Trip), que estão sendo cada vez mais utilizados na indústria automotiva13,14,15,16. Porque a indústria automotiva aumentou os padrões de força devido ao consumo de combustível melhorado e absorção de energia de colisão um peso reduzido do veículo, o uso de diferentes materiais e processos de soldagem está se tornando uma questão importante.

<table><tbody><tr><td>bigorna</td><td>MIRDC</td><td></td><td>feita por MIRDC</td></tr><tr><td>DP780</td><td>China steel Corporation</td><td>CSC DP780</td><td></td></tr><tr><td>máquina de solda de ponto de agitação</td><td>MIRDC</td><td></td><td>feita por</td></tr><tr><td>pino de ferramenta</td><td>MIRDC KINIK</td><td>COMPANY DBN2B005B</td><td></td></tr></tbody></table>

gerando junções de regaço através da soldadura do ponto do stir da fricção no aço dp780

Generating Lap Joints Via Friction Stir Spot Welding on DP780 Steel

A soldadura do ponto da agitação da fricção (FSSW), um derivado da soldadura do stir da fricção (FSW), é uma técnica do sólido-estado da soldadura que seja desenvolvida em 1991. Um aplicativo da indústria foi encontrado na indústria automotiva em 2003 para a liga de alumínio que foi usado nas portas traseiras de automóveis. A soldadura do ponto da agitação da fricção é usada na maior parte em ligas do Al para criar junções de regaço. Os benefícios da soldadura do ponto da agitação da fricção incluem uma temperatura de derretimento de quase 80% que abaixe as soldas da deformação térmica sem espirrar comparado à soldadura do ponto da resistência. A soldadura do ponto da agitação da fricção inclui 3 etapas: mergulhando, agitando, e retração. No presente estudo, outros materiais, incluindo aço de alta resistência, também são usados no método de soldagem por atrito para criar articulações. DP780, cujo o processo tradicional da soldadura envolve o uso da soldadura do ponto da resistência, é um de diversos materiais de aço de grande resistência usados na indústria automotriz. Neste trabalho, DP780 foi utilizado para a soldagem por fricção, e sua microestrutura e microdureza foram mensuradas. Os dados da microestrutura mostraram que havia uma zona da fusão com grão fino e uma zona do efeito do calor com Martensite do console. Os resultados da microdureza indicaram que a zona central exibiu maior grau de dureza em relação ao metal de base. Todos os dados indicaram que o atrito agitar ponto de solda usado em dupla fase de aço 780 pode criar uma boa junção de volta. No futuro, a soldadura do ponto do stir da fricção pode ser usada na soldadura de aço de grande resistência aplicada em processos industriais da fabricação.

Há um diagrama na Figura 3 que demonstra que o processo de soldagem por atrito de agitação é composto por 3 partes: mergulhando(figura 3E), mexendo (Figura 3F) e retraindo (Figura 3G). Em nossa pesquisa, o ponto de solda poderia ser gerado. A profundidade de penetração é um fator que foi avaliado. Na Figura 6a, o fssw cria o buraco da fechad...

Aqui, nós apresentamos um protocolo da soldadura do ponto da agitação da fricção (FSSW) no aço duplo da fase 780. Um pino da ferramenta com rotação de alta velocidade gera o calor da fricção para amaciar o material, e então, o pino mergulha em 2 junções da folha para criar a junção de regaço.

Gerando junções de regaço através da soldadura do ponto do stir da fricção no aço DP780

Friction stir spot welding (FSSW), a derivative of friction stir welding (FSW), is a solid-state welding technique that was developed in 1991. An industry ...

As demandas de redução de peso na indústria automotiva têm gerado um interesse crescente nas articulações de volta e nos aços avançados de alta resistência, ou AHSS. No entanto, as juntas de soldagem spot da AHSS têm desafios para a confiabilidade do processo. Os benefícios da soldagem de ponto de fricção, ou FSSW, em comparação com a soldagem de ponto de resistência são uma menor temperatura de soldagem, sem respingo, e mais estabilidade no processo de fabricação.Demonstrando o procedimento serão Cheng Chia-Ping e Hsu Hao, estudantes de pós-graduação do meu laboratório. Durante este procedimento use óculos e luvas para evitar contato com respingos ou danos térmicos. Também fique atrás do capô ou do defletor para proteção.Fabricar todas as juntas usando uma máquina de soldador de fricção. Registo a força z-axial e profundidade de penetração durante cada operação de junção usando o sistema de aquisição de dados incorporados. Defina uma velocidade de rotação do pino de ferramenta de 25.000 RPM, um tempo de solda de pino de ferramenta de quatro segundos e uma taxa de 0,5 milímetros por segundo de pino de ferramenta mergulhar na folha.Otimize os parâmetros para o operador. A faixa de r

generating-lap-joints-via-friction-stir-spot-welding-on-dp780-steel

Research

JoVE Journal

Engineering

Engenharia

Um procedimento simples para soldagem ultrassônica de cupons de compósitos termoplásticos para testes mecânicos básicos é descrito. As principais características deste processo de soldagem ultrassônica são o uso de diretores de energia planos para preparação simplificada do processo e o uso de dados de processo para a definição rápida das condições ideais de processamento.

Ultrasonic Welding de cupons termoplástica composta de Mecânica Caracterização de Juntas Soldadas através Individual Sobreposição Testing

O artigo a seguir apresenta uma nova técnica de simulação de EF (KBC-FE), que reduz o custo computacional realizando simulações em um ambiente de computação em nuvem, por meio da aplicação de módulos individuais. Além disso, estabelece uma rede colaborativa perfeita entre os principais cientistas do mundo, permitindo a integração de módulos de conhecimento de ponta em simulações de FE.

Conhecimento Baseado Simulação Nuvem FE dos Processos de formação de folha de metal

Um protocolo experimental para rotativa quente instrumentado formação de ligas de alumínio fundido com utilização de um aparelho de bespoke industrialmente escalado é apresentado. considerações experimentais, incluindo efeitos térmicos e mecânicos são discutidos, assim como a semelhança com o processamento em larga escala de rodas de automóveis.

Procedimento Experimental para a fiação quente do elenco componentes de alumínio

Este protocolo propõe um novo sistema de teste biaxial usado em um aquecimento por resistência à tracção uniaxial máquina de teste, a fim de determinar a formação de diagrama limite (FLD) de chapas de metal, sob condições de estampagem a quente.

Um novo aparelho Biaxial Teste para a Determinação do limite de conformação sob Hot Stamping Condições

Superfícies escorregadias fornecem uma nova forma de resolver o problema de aderência. Este protocolo descreve como fabricar superfícies escorregadias em altas temperaturas. Os resultados demonstram que as superfícies escorregadias mostraram antiumectantes para líquidos e um notável efeito antiaderência sobre os tecidos moles em altas temperaturas.

Comportamento de antipreparação adesão e alta temperatura de uma superfície escorregadia em aço inoxidável

A correlação de imagem digital é usada em testes de fadiga em uma máquina de teste de ressonância para detectar rachaduras macroscópicas e monitorar a propagação de crack em espécimes soldados. As rachaduras na superfície da amostra tornam-se visíveis como tensões aumentadas.

Monitoramento de crack em testes de fadiga de ressonância de espécimes soldados usando correlação de imagem digital

Este protocolo descreve um método para a fabricação rápida de atuadores pneumáticos macios e robôs com um fator de forma fina. O método de fabricação começa com laminação de folhas termoplásticas de poliuretano (TPU), seguidas de corte a laser/soldagem de um padrão bidimensional para formar atuadores e robôs.

Fabricação rápida de atuadores e robôs pneumáticos macios finos

Apresentado aqui é um procedimento para medir propriedades materiais fundamentais através de testes de tensão micromecânica. Descritos são os métodos para fabricação de amostras de micropresa (permitindo a fabricação rápida de micro-espécimes a partir de volumes de material a granel, combinando fotolitografia, gravura química e fresagem de feixe de íons focalizada), modificação da ponta do recuo e testes de tensão micromecânica (incluindo um exemplo).

Teste de tensão micromecânica de amostras de aço inoxidável fabricadas aditivamente 17-4 PH

Este protocolo descreve um fluxo de trabalho geral para a construção de uma rede neural artificial para simulação de soldagem usando conjuntos de dados gerados automaticamente por meio de scripts Python com funções macro. O fluxo de trabalho é validado em relação a um caso de referência envolvendo soldagem em linha reta de passagem única. A precisão preditiva do modelo substituto mostra uma forte concordância com simulações de elementos finitos.

Desenvolvimento de modelo substituto para experimentos digitais em soldagem

Um processo é descrito para adquirir metrologia quase em tempo real de cordões de solda e preparar a geometria resultante automaticamente para análise de elementos finitos.

Captura automática de geometria baseada em laser para análise de elementos finitos de cordões de solda

Aprenda a soldar junções de regaço em aço DP780 usando soldagem por fricção e mistura no ponto. Este método oferece temperaturas mais baixas, sem respingos e maior estabilidade no processo de fabricação.

Gerando junções de regaço através da soldadura do ponto do stir da fricção no aço DP780