Name: Impressão 3D multimodal de fantasmas para simular tecido biológico (Vídeo) | JoVE Journal
Uploaded: 2020-01-11T15:00:00.000+00:00
Duration: 5 min 11 s
Description: Explore a integração de spin coating, PolyJet e FDM para fabricar fantasmas multicamadas que simulam propriedades estruturais e funcionais de tecidos biológicos. Este método avança a validação de dispositivos ópticos biomédicos.

ai_agent_IP

ai_agent

maintenance

instantTrialDurationMinutes

isBiopharma

enableNewMyJoveSectionDesign

educationFeatures

seoMetaApi

ai_copilot_institution_blacklist

ai_chat_institution_blacklist

freeAccessWindow

ssoRoleCapture

scheduledMaintenanceBanner

joveLabsFeatures

disable_autoplay_for_bots

extended_trial_duration

5 minutes

O trabalho foi apoiado pela National Natural Science Foundation of China (Grant Nos. 11002139 e 81327803) e pelos Fundos fundamentais de pesquisa para as Universidades Centrais. Agradecemos Zachary J. Smith da Universidade de Ciência e Tecnologia para fornecer a narração de áudio.

1. Preparar materiais para impressão 3D
NOTA: Nossa linha de produção fantasma óptico usa uma variedade de materiais de impressão para simular as heterogeneidades estruturais e funcionais do tecido biológico. A seleção dos materiais de impressão também depende dos processos de fabricação.
<ol><li>Preparação material para impressão de revestimento de rotação<ol>
<li>Adicione 100 mg de dióxido de titânio (TiO2)em pó em um copo contendo 100 mL de resina fotopolímera de esteletografia (SLA).</li>
		<li>Mexa a mistura no copo por 30 min em um agitador magnético.</li>
		<li>Selar o copo com papel alumínio e sonicate-lo em uma máquina ultra-sônica por 15 min.</li>
		<li>Aspirar o material por 10 min e carregá-lo na seringa de armazenamento do dispositivo.</li>
	</ol>
</li>
	<li>Preparação material para a impressão de polijato<ol>
<li>Adicione 17,56 g de 2-hidroxi-2-metilpropiofenona (1-hidroxiciclohexyl cetona fenil) no copo contendo 80 g de trietileno glicol dimethacrylate para obter 18% (w/ w) material.</li>
		<li>Selar o copo com papel alumínio e sonicate-lo em uma máquina ultra-sônica por 15 min.</li>
		<li>Tire 20 mL da mistura e adicione 5 mg do tinulado rinque vermelho chinês solúvel em óleo. Repita o passo 1.2.2.</li>
		<li>Aspirar todos os materiais, carregar a solução com corantes nos cartuchos para o canal Y (Amarelo) e carregar a solução pura nos cartuchos para o canal K (Black).</li>
	</ol>
</li>
	<li>Preparação material para impressão FDM<ol>
<li>Carregue 200 g de cera de gel em cada um dos três copos e, em seguida, aqueça-os a 60 °C em um agitador magnético.</li>
		<li>Adicione 600 mg TiO2 pó no primeiro copo. Adicione 80 mg de pó de grafite no segundo.</li>
		<li>Mexa a cera de gel misturada com TiO2 e cera de gel misturada com pó de grafite em copos diferentes por 30 min no agitador magnético.</li>
		<li>Aspirar os três materiais diferentes para 2 min e carregá-los no extruso do módulo híbrido-três-bico antes da solidificação.</li>
	</ol>
</li>
</ol>2. Preparar modelos computacionais para impressão 3D multimodal
NOTA: O tecido heterogêneo da pele é simplificado em três camadas: epiderme, derme e tecido subcutâneo. A camada de epiderme é produzida pelo revestimento de rotação usando o material introduzido na etapa 1.1. A camada de derme é produzida pela impressão polijato usando o polímero fotossensível introduzido na etapa 1.2. A camada subcutânea do tecido é produzida por FDM usando o material introduzido na etapa 1.3. Um protótipo de computador auxiliado design (CAD) arquivo de diferentes parâmetros de impressão é gerado para orientar os processos de fabricação acima mencionados.
<ol><li>Design de um fantasma óptico digital para a pele<ol>
<li>Projete o fantasma da pele com as seguintes três camadas: uma camada de epiderme de 100 μm de espessura, uma camada de derme de 400 μm de espessura e um tecido subcutâneo de 1 cm de espessura.</li>
		<li>Desenhe um modelo de tumor usando um pacote de software de modelagem 3D (por exemplo, Solidworks) (Figura 5A).</li>
	</ol>
</li>
	<li>Ajuste do parâmetro para o revestimento da rotação<ol>
<li>Defina os parâmetros de velocidade e duração rotativas no software de controle do dispositivo de impressão. A velocidade de revestimento de rotação de primeiro estágio usada nesta demonstração é de 200 revoluções por min (rpm), o tempo de revestimento de rotação é de 20 s, a velocidade no revestimento de rotação de segunda fase é de 1.000 rpm, e o tempo de revestimento de rotação é de 40 s.</li>
		<li>Defina a quantidade de material de revestimento de rotação como 3 mL e o tempo de cura de luz como 180 s no software de controle.</li>
	</ol>
</li>
	<li>Preparação do arquivo de origem para impressão de polijato<ol>
<li>Importe a imagem do vaso sanguíneo para ser impressa no pacote de software AcroRIP Color e defina os parâmetros (posição de impressão e quantidade de jato de tinta) de acordo com a relação entre os parâmetros ópticos dos fantasmas impressos e as propriedades da imagem. Nesta imagem impressa do vaso sanguíneo, o canal K é carregado com um material fotocurável transparente, e o canal Y é carregado com um material fotocurável misturado com tinatriz vermelha chinesa.</li>
		<li>Gerar um arquivo ".prn" com parâmetros definidos para impressão 3D.</li>
	</ol>
</li>
	<li>Preparação do código G para impressão FDM<ol>
<li>Desenhe um modelo de frustum com um pacote de software de mapeamento 3D (por exemplo, Solidworks) para simular um tumor.</li>
		<li>Importe o arquivo ".stl" do modelo tumoral em um pacote de software Cura instalado com um script de corte de bico tudo-em-um.</li>
		<li>Corte o modelo para gerar o código G necessário para impressão.</li>
	</ol>
</li>
	<li>Carregamento dos documentos para o software de controle de impressão<ol>
<li>Clique no item do menu"Arquivo"na barra do menu, selecione o item do submenu"Import UV Print File"e carregue os arquivos de impressão UV ".prn" introduzidos na etapa 2.3.</li>
		<li>Carregue o código G gerado na etapa 2.4 no software de controle de impressão como na etapa 2.5.1.</li>
		<li>Clique no botão Iniciar a Impressão para iniciar o procedimento automatizado de impressão 3D.</li>
	</ol>
</li>
</ol>3. Imprimir o componente fantasma da camada da epiderme da pele pelo revestimento da rotação
NOTA: O módulo de revestimento de rotação é composto principalmente de três partes: 1) um coater de rotação; 2) um dispensador de cola; e 3) uma lâmpada UV.
<ol><li>Mova o substrato na estação de carregamento para o estágio de amostra do coador de rotação com uma mão mecânica. Inicie a bomba de vácuo para corrigir o substrato por adsorção.</li>
	<li>O distribuidor da colagem controla a seringa para gotejar o material introduzido na etapa 2.2.2 no centro da carcaça.</li>
	<li>O coater da rotação começa trabalhar seguindo os parâmetros ajustados da velocidade e do tempo.</li>
	<li>Coloque a lâmpada UV (comprimento de onda: 395 nm) e ligá-lo por 180 s.</li>
	<li>Levante a lâmpada UV, desligue o spin-coater e imprima a camada de epiderme da pele.</li>
</ol>4. Imprimir o componente fantasma da camada de derme da pele polijorrando
NOTA: O módulo de impressão polijato consiste em um bico de jato de tinta piezoelétrico, uma plataforma móvel tridimensional, um painel de controle e uma lâmpada UV (lâmpada de mercúrio). O material fotocurável à base de solvente, material de absorção e material de dispersão são usados como matriz. Diferentes parâmetros ópticos são obtidos pulverizando materiais em diferentes proporções em diferentes regiões. Finalmente, o fantasma da camada de derme é impresso e curado camada por camada.
<ol><li>Mova o substrato para a plataforma móvel 3D e abra a válvula de sucção para adsorb o substrato na plataforma.</li>
	<li>A plataforma móvel 3D mantém o substrato para a posição inicial da impressora UV.</li>
	<li>Empurre a impressora a jato de tinta para a posição de trabalho pelo cilindro, e a impressora a jato de tinta funciona o tempo especificado no arquivo ".prn" enviado pelo computador hospedeiro. Aqui, o sinal de alimentação em papel da impressora a jato de tinta é usado para impulsionar o movimento da plataforma móvel Y-axis.</li>
	<li>A impressora a jato de tinta imprime a camada projetada na etapa 2.5.1 e o cilindro empurra a impressora a jato de tinta de volta à posição original. O eixo Y da plataforma móvel 3D colocada com o substrato é inicializado movendo-se para sua posição inicial.</li>
	<li>O substrato se move 50 mm na direção positiva do eixo Y. A lâmpada UV é empurrada para baixo pelo cilindro (10 milímetros acima do substrato).</li>
	<li>Ligue a lâmpada UV para 180 s de acordo com a configuração de tempo de cura.</li>
	<li>Empurre a lâmpada UV para a posição inicial com o cilindro. O eixo Y da plataforma móvel 3D colocado com o substrato é inicializado e devolvido à sua posição inicial.</li>
	<li>Mova a plataforma móvel 3D colocada com substrato para baixo por 0,1 mm ao longo do eixo Z.</li>
	<li>Repita os passos 4.1-4.8 para imprimir a próxima camada até que a impressão multicamada seja concluída.</li>
</ol>5. Imprimir o componente fantasma subcutâneo do tecido por FDM
NOTA: O módulo FDM é composto por um módulo híbrido de três cabeças, um módulo de cabeça única e uma plataforma móvel 3D. A cera de gel, o material absorvente e o material de dispersão são usados como matérias-primas para preparar um fantasma simulando tecido/tumor subcutâneo. A cera do gel é aquecida e derretida no alimentador. Uniformemente agitado pela cabeça de extrusão, é extruso para imprimir os fantasmas finais com os parâmetros ópticos desejados.
<ol><li>Ligue o poder de aquecimento do módulo do bico e definir a temperatura para 60 °C.</li>
	<li>Mova o bico de mistura para a posição de trabalho, empurrando o cilindro.</li>
	<li>O módulo FDM recebe os comandos de código G enviados pelo computador hospedeiro, e o bico de mistura é aquecido até 68 °C.</li>
	<li>Ligue o motor de agitação e misture bem os materiais.</li>
	<li>Inicialmente, a plataforma móvel 3D e os eixos XYZ passam para a posição inicial.</li>
	<li>O processo de impressão é executado seguindo os comandos do código G. Em um procedimento de impressão camada por camada, os materiais são extrudados em proporção à razão de mistura que determinam os parâmetros ópticos do fantasma em cada camada. A impressão continua até que a porção subcutânea do tecido ou a parcela do tumor esteja imprimida inteiramente.</li>
	<li>Mova o módulo do bocal de mistura à posição inicial empurrando o cilindro. CUIDADO: Como o pó de grafite tem forte absorção de luz, ele precisa ser misturado da forma mais uniforme possível para evitar alterações nos parâmetros ópticos induzidos pela agregação. O pó TiO2 de tamanho de partículas grande facilmente precipita e afeta a precisão de colocação de material, por isso é necessário misturá-lo totalmente. TiO2 deve ser substituído se armazenado por um longo tempo.</li>
</ol>6. Movendo o substrato de volta para a estação de carregamento
<ol><li>Inicialmente inicialize a plataforma móvel 3D e mova o eixo XYZ para a posição inicial. Mova a plataforma móvel 3D para o local de entrega.</li>
	<li>Mova a mão mecânica para a posição acima do substrato, empurrando o cilindro.</li>
	<li>Pegue o substrato e mova-o sobre a estação de carregamento com a mão mecânica. Coloque o substrato na estação de carregamento e complete a impressão automatizada.</li>
</ol>7. Fundindo o componente fantasma subcutâneo da camada do tecido moldando
NOTA: Se o modelo do tumor para o fantasma é projetado, será necessário moldar o fantasma inteiro derramando o polydimethylsiloxane (PDMS) fora do tumor. Passos 7.1-7.3 não são necessários para o módulo FDM para imprimir camada de tecido subcutânea sem um tumor.
<ol><li>Pressione um substrato com um molde retangular impresso em 3D.</li>
	<li>Despeje PDMS líquido no molde.</li>
	<li>Coloque o substrato em uma incubadora e guarde a 60 °C por 2 h.</li>
	<li>Retire o fantasma do substrato.</li>
</ol>

<ol><li>Lu, G., Fei, B. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Medical+hyperspectral+imaging%3A+a+review%5BTitle%5D)+AND+%22Journal+of+Biomedical+Optics%22%5BJournal%5D)">Medical hyperspectral imaging: a review.</a> Journal of Biomedical Optics. 19 (1), 010901(2014).</li>
<li>Wang, K., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Development+of+a+non-uniform+discrete+Fourier+transform+based+high+speed+spectral+domain+optical+coherence+tomography+system%5BTitle%5D)+AND+%22Optics+Express%22%5BJournal%5D)">Development of a non-uniform discrete Fourier transform based high speed spectral domain optical coherence tomography system.</a> Optics Express. 17 (14), 12121-12131 (2009).</li>
<li>Zhao, H., Gao, F., Tanikawa, Y., Homma, K., Yamada, Y. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Time-resolved+diffuse+optical+tomographic+imaging+for+the+provision+of+both+anatomical+and+functional+information+about+biological+tissue%5BTitle%5D)+AND+%22Applied+Optics%22%5BJournal%5D)">Time-resolved diffuse optical tomographic imaging for the provision of both anatomical and functional information about biological tissue.</a> Applied Optics. 44 (10), 1905-1916 (2005).</li>
<li>Ding, Z., Ren, H., Zhao, Y., Nelson, J. S., Chen, Z. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((High-resolution+optical+coherence+tomography+over+a+large+depth+range+with+an+axicon+lens%5BTitle%5D)+AND+%22Optics+Letters%22%5BJournal%5D)">High-resolution optical coherence tomography over a large depth range with an axicon lens.</a> Optics Letters. 27 (4), 243-245 (2002).</li>
<li>Iida, H., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Three-dimensional+brain+phantom+containing+bone+and+grey+matter+structures+with+a+realistic+head+contour%5BTitle%5D)+AND+%22Annals+of+Nuclear+Medicine%22%5BJournal%5D)">Three-dimensional brain phantom containing bone and grey matter structures with a realistic head contour.</a> Annals of Nuclear Medicine. 27 (1), 25-36 (2013).</li>
<li>Mobashsher, A. T., Abbosh, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Three-dimensional+human+head+phantom+with+realistic+electrical+properties+and+anatomy%5BTitle%5D)+AND+%22IEEE+Antennas+and+Wireless+Propagation+Letters%22%5BJournal%5D)">Three-dimensional human head phantom with realistic electrical properties and anatomy.</a> IEEE Antennas and Wireless Propagation Letters. 13, 1401-1404 (2014).</li>
<li>Li, J. B., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((A+new+head+phantom+with+realistic+shape+and+spatially+varying+skull+resistivity+distribution%5BTitle%5D)+AND+%22IEEE+Transactions+on+Biomedical+Engineering%22%5BJournal%5D)">A new head phantom with realistic shape and spatially varying skull resistivity distribution.</a> IEEE Transactions on Biomedical Engineering. 61 (2), 254-263 (2013).</li>
<li>Bykov, A., et al. Multilayer tissue phantoms with embedded capillary system for OCT and DOCT imaging. <a target="_blank" href="http://scholar.google.com/scholar?hl=en&safe=off&q=author%3aBykov%2C+A+%22Life+Sciences.+%28International+Society+for+Optics+and+Photonics%29%22">Life Sciences. (International Society for Optics and Photonics)</a>. , 73760(2011).</li>
<li>Bykov, A. V., Popov, A. P., Priezzhev, A. V., Myllylä, R. Skin phantoms with realistic vessel structure for OCT measurements in Laser Applications. <a target="_blank" href="http://scholar.google.com/scholar?hl=en&safe=off&q=author%3aBykov%2C+AV+%22European+Conference+on+Biomedical+Optics%22">European Conference on Biomedical Optics</a>. , Optical Society of America. 80911(2010).</li>
<li>Park, J., et al. Fabrication of double layer optical tissue phantom by spin coating method: mimicking epidermal and dermal layer. <a target="_blank" href="http://scholar.google.com/scholar?hl=en&safe=off&q=author%3aPark%2C+J+%22Design+and+Performance+Validation+of+Phantoms+Used+in+Conjunction+with+Optical+Measurement+of+Tissue+V%22">Design and Performance Validation of Phantoms Used in Conjunction with Optical Measurement of Tissue V</a>. , International Society for Optics and Photonics. 85830(2013).</li>
<li>Wróbel, M. S., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Use+of+optical+skin+phantoms+for+preclinical+evaluation+of+laser+efficiency+for+skin+lesion+therapy%5BTitle%5D)+AND+%22Journal+of+Biomedical+Optics%22%5BJournal%5D)">Use of optical skin phantoms for preclinical evaluation of laser efficiency for skin lesion therapy.</a> Journal of Biomedical Optics. 20 (8), 085003(2015).</li>
<li>Sheng, S., Wu, Q., Han, Y., Dong, E., Xu, R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Fabricating+optical+phantoms+to+simulate+skin+tissue+properties+and+microvasculature%5BTitle%5D)+AND+%22Design+and+Performance+Validation+of+Phantoms+Used+in+Conjunction+with+Optical+Measurement+of+Tissue+Vii%22%5BJournal%5D)">Fabricating optical phantoms to simulate skin tissue properties and microvasculature.</a> Design and Performance Validation of Phantoms Used in Conjunction with Optical Measurement of Tissue Vii. , International Society for Optics and Photonics. 932507(2015).</li>
<li>Lurie, K. L., Smith, G. T., Khan, S. A., Liao, J. C., Ellerbee, A. K. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Three-dimensional%2C+distendable+bladder+phantom+for+optical+coherence+tomography+and+white+light+cystoscopy%5BTitle%5D)+AND+%22Journal+of+Biomedical+Optics%22%5BJournal%5D)">Three-dimensional, distendable bladder phantom for optical coherence tomography and white light cystoscopy.</a> Journal of Biomedical Optics. 19 (3), 36009(2014).</li>
<li>Hahn, C., Noghanian, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Heterogeneous+breast+phantom+development+for+microwave+imaging+using+regression+models%5BTitle%5D)+AND+%22Journal+of+Biomedical+Imaging%22%5BJournal%5D)">Heterogeneous breast phantom development for microwave imaging using regression models.</a> Journal of Biomedical Imaging. 2012, 6(2012).</li>
<li>Ansari, M. A., Mohajerani, E. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Estimation+of+optical+abnormalities+in+breast+phantom+by+diffuse+equation%5BTitle%5D)+AND+%22Optik-International+Journal+for+Light+and+Electron+Optics%22%5BJournal%5D)">Estimation of optical abnormalities in breast phantom by diffuse equation.</a> Optik-International Journal for Light and Electron Optics. 125 (20), 5978-5981 (2014).</li>
<li>Roman, M., Gonzalez, J., Carrasquilla, J., Erickson, S. J., Godavarty, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((A+Gen-2+Hand-Held+Optical+Imager%3A+Phantom+and+Preliminary+in-vivo+Breast+Imaging+Studies%5BTitle%5D)+AND+%2229th+Southern+Biomedical+Engineering+Conference%22%5BJournal%5D)">A Gen-2 Hand-Held Optical Imager: Phantom and Preliminary in-vivo Breast Imaging Studies.</a> 29th Southern Biomedical Engineering Conference. , 103-104 (2013).</li>
<li>Michaelsen, K. E., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Anthropomorphic+breast+phantoms+with+physiological+water%2C+lipid%2C+and+hemoglobin+content+for+near-infrared+spectral+tomography%5BTitle%5D)+AND+%22Journal+of+Biomedical+Optics%22%5BJournal%5D)">Anthropomorphic breast phantoms with physiological water, lipid, and hemoglobin content for near-infrared spectral tomography.</a> Journal of Biomedical Optics. 19 (2), 026012(2014).</li>
<li>Park, J., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Optical+tissue+phantoms+based+on+spin+coating+method%5BTitle%5D)+AND+%22Design+and+Performance+Validation+of+Phantoms+Used+in+Conjunction+with+Optical+Measurement+of+Tissue+VII%22%5BJournal%5D)">Optical tissue phantoms based on spin coating method.</a> Design and Performance Validation of Phantoms Used in Conjunction with Optical Measurement of Tissue VII. , International Society for Optics and Photonics. 93250(2015).</li>
<li>Mustari, A., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Agarose-based+tissue+mimicking+optical+phantoms+for+diffuse+reflectance+spectroscopy%5BTitle%5D)+AND+%22Journal+of+Visualized+Experiments%22%5BJournal%5D)">Agarose-based tissue mimicking optical phantoms for diffuse reflectance spectroscopy.</a> Journal of Visualized Experiments. (138), e57578(2018).</li>
<li>Luciano, N. J., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Utilizing+3D+printing+technology+to+merge+MRI+with+histology%3A+A+protocol+for+brain+sectioning%5BTitle%5D)+AND+%22Journal+of+Visualized+Experiments%22%5BJournal%5D)">Utilizing 3D printing technology to merge MRI with histology: A protocol for brain sectioning.</a> Journal of Visualized Experiments. (118), e54780(2016).</li>
<li>Dong, E., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Three-dimensional+fuse+deposition+modeling+of+tissue-simulating+phantom+for+biomedical+optical+imaging%5BTitle%5D)+AND+%22Journal+of+Biomedical+Optics%22%5BJournal%5D)">Three-dimensional fuse deposition modeling of tissue-simulating phantom for biomedical optical imaging.</a> Journal of Biomedical Optics. 20 (12), 121311(2015).</li>
<li>Beltrame, E. D. V., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((3D+Printing+of+Biomolecular+Models+for+Research+and+Pedagogy%5BTitle%5D)+AND+%22Journal+of+Visualized+Experiments%22%5BJournal%5D)">3D Printing of Biomolecular Models for Research and Pedagogy.</a> Journal of Visualized Experiments. (121), e55427(2017).</li>
<li>Bentz, B. Z., Chavan, A. V., Lin, D., Tsai, E. H., Webb, K. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Fabrication+and+application+of+heterogeneous+printed+mouse+phantoms+for+whole+animal+optical+imaging%5BTitle%5D)+AND+%22Applied+Optics%22%5BJournal%5D)">Fabrication and application of heterogeneous printed mouse phantoms for whole animal optical imaging.</a> Applied Optics. 55 (2), 280-287 (2016).</li>
<li>Liu, G., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Fabrication+of+a+multilayer+tissue-mimicking+phantom+with+tunable+optical+properties+to+simulate+vascular+oxygenation+and+perfusion+for+optical+imaging+technology%5BTitle%5D)+AND+%22Applied+Optics%22%5BJournal%5D)">Fabrication of a multilayer tissue-mimicking phantom with tunable optical properties to simulate vascular oxygenation and perfusion for optical imaging technology.</a> Applied Optics. 57 (23), 6772-6780 (2018).</li>
</ol>

Os autores não têm nada a divulgar.

Na fabricação do fantasma multicamadas, o material usado para revestimento de rotação é uma espécie de material curável em luz em vez de PDMS. A camada intermediária é impressa com o método de impressão polijato, que usa a resina curável como matéria-prima. Embora os fantasmas pdms finos possam ser feitos por revestimento de rotação depois de adicionar álcool tert-butyl, uma camada PDMS não pode efetivamente se ligar ao material curável à luz durante a impressão polijato. Portanto, escolhemos a resina curável para revest...

A imagem óptica biomédica representa uma família de ferramentas médicas da imagem latente que detectam doenças e anomalias do tecido baseadas em interações claras com tecido biológico. Em comparação com outras modalidades de imagem, como ressonância magnética (RM) e tomografia computadorizada (TC), imagens ópticas biomédicas aproveitam a medição não invasiva de características estruturais, funcionais e moleculares de tecidos usando dispositivos de baixo custo e portáteis1,2,3,4. No entanto, apesar de sua superioridade em custo e portabilidade, a imagem óptica não tem sido amplamente aceita para diagnóstico clínico e orientação terapêutica, em parte devido à sua baixa reprodutibilidade e falta de mapeamento quantitativo entre parâmetros ópticos e biológicos. A principal razão para essa limitação é a falta de padrões rastreáveis para calibração quantitativa e validação de dispositivos de imagem óptica biomédica.
No passado, uma variedade de fantasmas simuladores de tecidos foram desenvolvidas para pesquisa de imagem óptica biomédica em vários tipos de tecidos, como cérebro5,6,7,pele8,9,10,11,12,bexiga13,e tecidos mamários14,15,16,17. Estes fantasmas são produzidos principalmente por um dos seguintes processos de fabricação: 1) revestimento de rotação10,18 (para simular tecido homogêneo e de camadas finas); 2) moldando19 (para simular o tecido volumoso com características geométricas); e 3) impressão tridimensional (3D)20,21,22 (para simular tecido heterogêneo multicamadas). Os fantasmas da pele produzidos por moldagem são capazes de imitar as propriedades ópticas a granel do tecido da pele, mas não podem simular as heterogeneidades ópticas laterais19. Bentz et al. usaram um método de impressão 3D FDM de dois canais para imitar diferentes propriedades ópticas do tecido biológico23. No entanto, o uso de dois materiais não pode simular suficientemente a heterogeneidade óptica do tecido e anisotropia. Lurie et al. criaram um fantasma da bexiga para tomografia óptica de coerência (OCT) e cistoscopia, combinando impressão 3D e revestimento de rotação13. No entanto, características heterogêneas do fantasma, como os vasos sanguíneos, tiveram que ser pintadas à mão.
Entre os processos de fabricação fantasma acima, a impressão 3D oferece a maior flexibilidade para simular as heterogeneidades estruturais e funcionais do tecido biológico. No entanto, muitos tipos de tecidobiológico, como o tecido da pele, consistem em componentes multicamadas e multiescalados que não podem ser efetivamente duplicados por um único processo de impressão 3D. Portanto, a integração de múltiplos processos de fabricação é necessária. Propomos uma linha de produção de impressão 3D que integra vários processos de fabricação para a produção automática de tecido multicamadas e multiescalas simulando fantasmas como um padrão rastreável para imagens ópticas biomédicas (Figura 1). Embora o revestimento de rotação, a impressão polijato e o FDM sejam automatizados em nossa linha de produção de impressão 3D, cada modalidade mantém as mesmas características funcionais dos processos estabelecidos. Portanto, este artigo fornece uma diretriz geral para a produção de fantasmas de simulação de tecido multiescalados, multicamadas e heterogêneos sem a necessidade de integração física de múltiplos processos em um único aparelho.
<img alt="Figure 1" class="xfigimg" src="/files/ftp_upload/60563/60563fig1.jpg"> Figura 1: O diagrama CAD da linha de produção de impressão 3D. (A)A linha de produção de impressão 3D com o escudo superior removido. (B) O esquema do módulo de revestimento de rotação e do módulo de mão mecânica. (C)O esquema do módulo de impressão polijato. (D)O esquema do módulo de impressão FDM (a lâmpada UV pertence ao módulo de impressão polijato). <a href="https://www.jove.com/files/ftp_upload/60563/60563fig1large.jpg" target="_blank">Clique aqui para ver uma versão maior deste número.</a>

<table><tbody><tr><td>2-Hidroxi-2-metilpropiofenona</td><td>aladdin</td><td>H110280-500g</td><td>Iniciador de luz <a href="http://www.aladdin-e.com/" target="_blank">http://www.aladdin-e.com/</a></td></tr><tr><td>Sistema de controle de impressão</td><td>3D USTC</td><td>USTC-3DPrinter_control1.0</td><td>feito sob medida github: <a href="https://github.com/macanzhen/3D_printing_control_system_of_ USTC" target="_blank">https://github.com/macanzhen/</a></td></tr>Sistema <tr><td>de impressão 3D</td><td>USTC</td><td>USTC-3DPrinter1.0</td><td>personalizado</td></tr><tr><td>AcroRip cor</td><td>Human Plus</td><td>AcroRip v8.2.6</td><td></td></tr><tr><td>All-in-one bico de corte script</td><td>Shenzhen CBD Technology Co., Ltd.</td><td></td><td>github: <a href = "https://github.com/macanzhen/3D_printing_Cura_all-in-one-nozzle-slicing-script" target = "_blank" >https://github.com/macanzhen/< / a ></td></tr> <tr><td>Corante vermelho chinês</td><td>Juents</td><td></td><td>solúvel em óleo</td></tr><tr><td>Cura</td><td>Ultimaker</td><td>Cura_15.04.6</td><td></td></tr><tr><td>Cera de gel</td><td>Shanghai Lida Industry Co., ltd.</td><td>Ponto</td><td>de fusão LP: 56 &deg; C</td></tr><tr><td>Grafite</td><td>aladdin</td><td>G103922-100g</td><td>Alterar objeto parâmetros de absorção óptica <a href="http://www.aladdin-e.com/" target="_blank">http://www.aladdin-e.com/</a></td></tr><tr><td>PDMS</td><td>Dow Corning</td><td>184</td><td></td></tr><tr><td>Dióxido de titânio</td><td>ALDRICH</td><td>24858-100G</td><td>347 nm</td></tr><tr><td>Trietilenoglicol dimetacrilato</td><td>aladdin</td><td>T101642-250ml</td><td>Monômero fotopolimerizado <a href="http://www.aladdin-e.com/" target="_blank">http://www.aladdin-e.com/</a></td></tr><tr><td>Tinta UV SLA Resina de Fotopolímero</td><td>time80s</td><td>RESIN-A</td><td><a href="http://www.time80s.com/zlxz" target="_blank">http://www.time80s.com/zlxz</a></td></tr></tbody></table>

impressão 3d multimodal de fantasmas para simular tecido biológico

Multimodal 3D Printing of Phantoms to Simulate Biological Tissue

A imagem óptica biomédica está desempenhando um papel importante no diagnóstico e tratamento de várias doenças. No entanto, a precisão e a reprodutibilidade de um dispositivo de imagem óptica são muito afetadas pelas características de desempenho de seus componentes, o ambiente de teste e as operações. Portanto, é necessário calibrar esses dispositivos por padrões fantasma rastreáveis. No entanto, a maioria dos fantasmas atualmente disponíveis são fantasmas homogêneos que não podem simular características multimodais e dinâmicas do tecido biológico. Aqui, mostramos a fabricação de fantasmas heterogêneos simuladores de tecidousando uma linha de produção que integra um módulo de revestimento de rotação, um módulo de polijato, um módulo de modelagem de deposição fundida (FDM) e uma estrutura de controle automático. As informações estruturais e os parâmetros ópticos de um "fantasma óptico digital" são definidos em um arquivo protótipo, importado para a linha de produção, e fabricados camada por camada com alternagem sequencial entre diferentes modalidades de impressão. A capacidade técnica de tal linha de produção é exemplificada pela impressão automática de fantasmas simuladores de pele que compõem a epiderme, derme, tecido subcutâneo e um tumor embutido.

Fantasma fabricado pelo revestimento da rotação O revestimento da rotação distribui uniformemente as gotículas na carcaça girando a plataforma giratória, e uma única camada do corpo original é fabricada após a cura. A velocidade de rotação do substrato e o tempo de rotação não só afetam a qualidade da superfície do fantasma, mas também determinam a espessura de cada camada do fantasma. Fantasmas de diferentes espessuras podem ser fabricados por revestimento de rotação repetitivo camada por camada. Os ...

Revestimento de spin, impressão polijato e modelagem de deposição fundida são integrados para produzir fantasmas heterogêneos multicamadas que simulam propriedades estruturais e funcionais do tecido biológico.

Impressão 3D multimodal de fantasmas para simular tecido biológico

Biomedical optical imaging is playing an important role in diagnosis and treatment of various diseases. However, the accuracy and the reproducibility of ...

O spin-coating, a impressão de polijato e a modelagem de deposição fundida são integrados para produzir fantasmas heterogêneos multicamadas que simulam propriedades estruturais e funcionais do tecido biológico. A falta de padrões fantasmas rastreáveis que simulam a heterogeneidade estrutural e funcional do tecido biológico tornou-se o gargalo para o desenvolvimento e validação de dispositivos ópticos biomédicos. Este vídeo mostra a fabricação camada por camada de tecido heterogêneo simulando fantasmas integrando múltiplos processos de fabricação aditiva, como revestimento de spin, impressão PolyJet e FDM em uma linha de produção de impressão 3D.A capacidade técnica de tal linha de produção é exemplificada pela impressão automática de fantasmas simuladores de pele que compreendem epiderme, derme, tecido subcutâneo e um tumor incorporado. Preparação de material para impressão de revestimento de spin. Adicione pó de dióxido de titânio na resina fotopolímera SLA, mexa por 30 minutos em uma mexida magnética.Selar com papel alumínio e sonicato. Vácuo por 10 minutos. Carregue-o na seringa de armazenamento Preparação de material para impressão de polijato.Adicione material, sonicato, adicione corante vermelho chinês, carregue-os nos cartuchos, coloque cartuchos na impressora. Preparação de material para impressão FDM. Aqueça a cera de gel de baixa densidade em uma mexida magnética.Adicione pó de dióxido de titânio, adicione pó de grafite no segundo béquer. O vácuo os carrega na extrusora do módulo híbrido de três bocais. Design de fantasma óptico digital da pele Configurando parâmetros para spin-coating.Configure os parâmetros de velocidade e duração rotativas no software de controle. configurar a quantidade de material de revestimento de spin e o tempo de cura da luz. Elaboração de arquivo fonte para impressão de polijato, Importe a imagem do vaso sanguíneo para o software, defina a posição de impressão e ajuste os parâmetros de jato de tinta que gerem o arquivo PRN necessário para impressão após a configuração ser a preparação completa do G-code para impressão FDM, importe o modelo tumoral para o software Cura adicione o script de fatia de um nozzle no software Cura e corte o modelo para gerar o código G necessário para impressão Documentos de importação do software de controle de impressão.Clique no item Menu Arquivo na barra de menu. Carregue os arquivos PRN de impressão UV. importar o código G.Clique no botão Iniciar a impressão. A mão mecânica move o substrato na estação de carga para o centro do estágio de amostra do spin-coater. O distribuidor de cola controla um gotejamento de seringa o material para o centro do substrato.O spin-coater começa a funcionar. Solte a lâmpada UV e ligue-a e a epiderme da pele será impressa. Mova o substrato para a plataforma móvel 3D.Mova o substrato para a posição inicial da impressão UV, empurre a impressora a jato de tinta para a posição de trabalho. A impressora a jato de tinta imprime a imagem. A lâmpada UV é empurrada pelo cilindro e movida para a posição acima do substrato, ligue a lâmpada UV.Repita para a próxima camada de impressão até que a impressão multicamadas esteja completa. O bocal de mistura é movido para a posição de trabalho pelo empurrão da impressão do cilindro de acordo com as instruções do código G. A impressão é completada até que a porção de tecido subcutâneo da porção do tumor seja impressa.Mova o substrato de volta para a estação de carregamento, lance o fantasma da camada subcutânea com a ajuda de um molde Resultados representativos. Resultado da linha de produção de impressão automatizada. Ao integrar os métodos de impressão 3D, o sistema poderia criar um tumor como o fantasma seguindo as etapas do protocolo.Tomar o modelo de pele multicamadas simplificada é um exemplo. A camada de epiderme, a camada de derme e a camada de tecido subcutâneo com diferentes espessuras e diferentes propriedades ópticas são fabricadas pelo método de revestimento de spin, método de impressão de polivala e método de impressão FDM. Através do modelo foi verificada a possibilidade de combinar revestimento de spin, impressão de polijato e impressão FDM para produzir fantasmas ópticos, é comprovado que o sistema tem potencial para produzir fantasma óptico de tecido com características de simulação óptica e características de simulação estrutural.

multimodal-3d-printing-of-phantoms-to-simulate-biological-tissue

Research

JoVE Journal

Engineering

Engenharia

Usando extrusão de plástico moderno e tecnologias de impressão, agora é possível de forma rápida e barata de produzir modelos físicos de dados de raios-X CT tomadas em um laboratório. A impressão tridimensional de tomografia de dados é uma visualização poderosa, pesquisa e ferramenta educacional que pode agora ser acessado pela comunidade de imagem pré-clínica.

Impressão 3D de pré-clínica de raios-X tomografia computadorizada de Conjuntos de Dados

Este artigo descreve os procedimentos internos de construção de uma multimodalidade pré fantasma feito de tecido imitando (TM) materiais para garantia de qualidade (QA) de medição de tamanho de tumor em modalidades de imagem animal, tais como ultra-som (EUA), tomografia computadorizada (TC) e magnético resonance imaging (MRI).

Construção de um fantasma Multimodalidade pré-clínicos com materiais que imitam tecido para a Garantia da Qualidade no Size Measurement Tumor

Espectros de tecido óptico são ferramentas essenciais para calibração e caracterização de sistemas de imagem ópticos e validação de modelos teóricos. Este artigo detalha um método para a fabricação de fantasma que inclui replicação das propriedades ópticas do tecido e a estrutura do tecido tridimensional.

Fabricação e caracterização de espectros ópticos de tecido contendo Macrostructure

Este protocolo descreve a produção de filamento policaprolactona (PCL) com microesferas de (PLA) de ácido polilático incorporado que contêm matrizes decellularized (DM) para impressão 3D estruturais de engenharia de tecidos construções.

Novo processo de impressão 3D Decellularized matrizes

O protocolo descreve a fabricação de impressões tridimensionais totalmente coloridas de modelos de crânio anatômico específicos do paciente para serem usados para simulação cirúrgica. Os passos cruciais da combinação de diferentes modalidades de imagem, segmentação de imagem, extração de modelotridimensional e produção das impressões são explicados.

Impressão 3D multicolorida de tumores intracranianos complexos na neurocirurgia

Este protocolo descreve a fabricação de um paciente específico crânio, cérebro e tumor fantasma. Ele usa impressão 3D para criar moldes, e o álcool polivinyl (PVA-c) é usado como o tecido imitando material.

Fabricação fantasma do álcool polivinyl específico do paciente com ultrassom e contraste de raios-X para planejamento de cirurgia de tumor cerebral

Aqui apresentamos o desenvolvimento de uma configuração de circulação simulada para avaliação de terapia multimodal, planejamento pré-intervencional e treinamento médico em anatomias cardiovasculares. Com a aplicação de exames tomográficos específicos do paciente, essa configuração é ideal para abordagens terapêuticas, treinamento e educação em medicina individualizada.

Desenvolvimento e Avaliação de Fantasmas Cardiovasculares Impressos em 3D para Planejamento e Treinamento Intervencionista

Este método demonstra um fluxo de trabalho de impressão 3D baseado em voxel, que imprime diretamente de imagens médicas com fidelidade espacial exata e resolução espacial/contraste. Isso permite o controle preciso e graduado das distribuições de materiais através de materiais morfologicamente complexos e graduados correlacionados à radiodensidade sem perda ou alteração de dados.

Anatomia de Impressão Voxel: Design e Fabricação de Modelos realistas de planejamento pré-cirúrgico através da impressão bitmap

Aqui, um novo método de estabelecer um modelo personalizado impresso em 3D para avaliação pré-operatória de cirurgia de tireoide é proposto. É propício à discussão pré-operatória, reduzindo a dificuldade da cirurgia de tireoide.

Um Modelo Personalizado Impresso em 3D para Avaliação Pré-Operatória em Cirurgia de Tireoide

Este protocolo descreve a fabricação de um material simulador estável e biologicamente relevante para aplicações de imagens biomédicas ópticas e acústicas, apresentando propriedades acústicas e ópticas ajustáveis independentemente.

Um material fantasma estável para imagens ópticas e acústicas

Este artigo apresenta o protocolo de preparação de simuladores tumor-tecido que replicam propriedades ópticas para terapia fototérmica plasmônica. Ele detalha a preparação do simulador, as avaliações fototérmicas e a validação do modelo numérico desenvolvido com base em medições de temperatura fototérmica para avaliar parâmetros terapêuticos, oferecendo uma alternativa ética e econômica aos estudos in vivo para testes preliminares.

Terapia Plasmônica Fototérmica do Câncer: Fantasmas que imitam o tecido tumoral embebido em nanopartículas para visualizar a distribuição fototérmica da temperatura

Explore a integração de spin coating, PolyJet e FDM para fabricar fantasmas multicamadas que simulam propriedades estruturais e funcionais de tecidos biológicos. Este método avança a validação de dispositivos ópticos biomédicos.

Impressão 3D multimodal de fantasmas para simular tecido biológico

Explorar mais vídeos