Name: Controle dependente de fase da profundidade da armadilha e luminescência persistente em fósforos de aluminato de estrôncio (Vídeo) | JoVE Journal
Uploaded: 2025-12-05T13:50:00.000+00:00
Duration: 6 min 16 s
Description: Aprenda a caracterizar fósforos de aluminato de estrôncio com luminescência persistente azul e verde. Este método demonstra aplicações dinâmicas de anticontrafacção com resolução temporal e térmica.

ai_agent_IP

ai_agent

maintenance

instantTrialDurationMinutes

isBiopharma

enableNewMyJoveSectionDesign

educationFeatures

seoMetaApi

ai_copilot_institution_blacklist

ai_chat_institution_blacklist

freeAccessWindow

ssoRoleCapture

scheduledMaintenanceBanner

joveLabsFeatures

disable_autoplay_for_bots

extended_trial_duration

5 minutes

<ol><li>Giordano, L., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Persistent+luminescence+induced+by+upconversion%3A+an+alternative+approach+for+rechargeable+bio-emitters%5BTitle%5D)+AND+%22Adv+Opt+Mater%22%5BJournal%5D)">Persistent luminescence induced by upconversion: an alternative approach for rechargeable bio-emitters.</a> Adv Opt Mater. 11 (11), 2201468(2023).</li>
<li>Cai, G., Delgado, T., Richard, C., Viana, B. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((ZGSO+spinel+nanoparticles+with+dual+emission+of+NIR+persistent+luminescence+for+anti-counterfeiting+applications%5BTitle%5D)+AND+%22Materials%22%5BJournal%5D)">ZGSO spinel nanoparticles with dual emission of NIR persistent luminescence for anti-counterfeiting applications.</a> Materials. 16 (3), 1132(2023).</li>
<li>Giordano, L., Cai, G., Castaing, V., Viana, B., Richard, C. Persistently Luminescent Inorganic Materials for Anti-Counterfeiting. <a target="_blank" href="http://scholar.google.com/scholar?hl=en&safe=off&q=author%3aGiordano%2C+L+%22Persistently+Luminescent+Materials%22">Persistently Luminescent Materials</a>. , Wiley. Weinheim, Germany. (2025).</li>
<li>Gao, D., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Quintuple-mode+dynamic+anti-counterfeiting+using+multi-mode+persistent+phosphors%5BTitle%5D)+AND+%22J+Mater+Chem+C%22%5BJournal%5D)">Quintuple-mode dynamic anti-counterfeiting using multi-mode persistent phosphors.</a> J Mater Chem C. 9 (46), 16634-16644 (2021).</li>
<li>Cai, G., Delgado, T., Allix, M., Rytz, D., Viana, B. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Color-tunable+persistent+luminescence+in+Eu2%2B%2CDy3%2B%2CB3%2B+co-doped+Sr4Al14O25+and+SrAl2O4+strontium+aluminates+ceramics+for+anti-counterfeiting+applications%5BTitle%5D)+AND+%22Adv+Opt+Mater%22%5BJournal%5D)">Color-tunable persistent luminescence in Eu2+,Dy3+,B3+ co-doped Sr4Al14O25 and SrAl2O4 strontium aluminates ceramics for anti-counterfeiting applications.</a> Adv Opt Mater. 13, 32(2025).</li>
<li>Peng, Q., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Up-converted+long+persistent+luminescence+from+CsPbBr3+nanocrystals+in+glass%5BTitle%5D)+AND+%22Laser+Photonics+Rev%22%5BJournal%5D)">Up-converted long persistent luminescence from CsPbBr3 nanocrystals in glass.</a> Laser Photonics Rev. 16 (12), 2200449(2022).</li>
<li>Tanaka, R., Uematsu, K., Sato, M., Toda, K. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Afterglow+improvement+of+high+concentration+Dy3%2B+co-doped+SrAl2O4%3AEu2%2B+phosphor+prepared+by+H3BO3-free+synthesis+using+melt+quenching+method%5BTitle%5D)+AND+%22J+Ceram+Soc+Jpn%22%5BJournal%5D)">Afterglow improvement of high concentration Dy3+ co-doped SrAl2O4:Eu2+ phosphor prepared by H3BO3-free synthesis using melt quenching method.</a> J Ceram Soc Jpn. 129 (7), 372-376 (2021).</li>
<li>Van den Eeckhout, K., Smet, P. F., Poelman, D. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Persistent+luminescence+in+Eu2%2B-doped+compounds%3A+a+review%5BTitle%5D)+AND+%22Materials%22%5BJournal%5D)">Persistent luminescence in Eu2+-doped compounds: a review.</a> Materials. 3 (4), 2536-2566 (2010).</li>
<li>Huang, Z., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Smart+mechanoluminescent+phosphors%3A+a+review+of+strontium-aluminate-based+materials%2C+properties%2C+and+their+advanced+application+technologies%5BTitle%5D)+AND+%22Adv+Sci%22%5BJournal%5D)">Smart mechanoluminescent phosphors: a review of strontium-aluminate-based materials, properties, and their advanced application technologies.</a> Adv Sci. 10 (3), 2204925(2023).</li>
<li>Van der Heggen, D., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Persistent+luminescence+in+strontium+aluminate%3A+a+roadmap+to+a+brighter+future%5BTitle%5D)+AND+%22Adv+Funct+Mater%22%5BJournal%5D)">Persistent luminescence in strontium aluminate: a roadmap to a brighter future.</a> Adv Funct Mater. 32 (52), 2208809(2022).</li>
<li>Lin, Y., Tang, Z., Zhang, Z. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Preparation+of+long-afterglow+Sr4Al14O25-based+luminescent+material+and+its+optical+properties%5BTitle%5D)+AND+%22Mater+Lett%22%5BJournal%5D)">Preparation of long-afterglow Sr4Al14O25-based luminescent material and its optical properties.</a> Mater Lett. 51 (1), 14-18 (2001).</li>
<li>Castaing, V., Giordano, L., Richard, C., Gourier, D., Allix, M., Viana, B. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Photochromism+and+persistent+luminescence+in+Ni-doped+ZnGa2O4+transparent+glass-ceramics%3A+toward+optical+memory+applications%5BTitle%5D)+AND+%22J+Phys+Chem+C%22%5BJournal%5D)">Photochromism and persistent luminescence in Ni-doped ZnGa2O4 transparent glass-ceramics: toward optical memory applications.</a> J Phys Chem C. 125 (18), 10110-10120 (2021).</li>
<li>Delgado, T., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Highly+transparent+Ce3%2B%2CCr3%2B+co-doped+GYAGG+single+crystals+with+enhanced+persistent+luminescence%5BTitle%5D)+AND+%22Photoluminescence+Rare+Earth+Doped+Mater+%28PRE+%2722%29%22%5BJournal%5D)">Highly transparent Ce3+,Cr3+ co-doped GYAGG single crystals with enhanced persistent luminescence.</a> Photoluminescence Rare Earth Doped Mater (PRE '22). 49 (24, Part B), 41031-41040 (2023).</li>
<li>Cai, G., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Chromium-doped+zinc+gallate%3A+impact+of+Sn4%2B+co-doping+on+the+persistent+luminescence+properties+at+the+nanoscale+applied+to+bio-imaging%5BTitle%5D)+AND+%22Chem+Eng+J%22%5BJournal%5D)">Chromium-doped zinc gallate: impact of Sn4+ co-doping on the persistent luminescence properties at the nanoscale applied to bio-imaging.</a> Chem Eng J. 490, 151643(2024).</li>
<li>Niittykoski, J., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Effect+of+boron+substitution+on+the+preparation+and+luminescence+of+Eu2%2B-doped+strontium+aluminates%5BTitle%5D)+AND+%22J+Alloys+Compd%22%5BJournal%5D)">Effect of boron substitution on the preparation and luminescence of Eu2+-doped strontium aluminates.</a> J Alloys Compd. 374 (1-2), 108-111 (2004).</li>
<li>Cai, G., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((ZGSO%3ACr3%2B%2CNi2%2B+persistent+phosphors+with+dual+emission+in+NIR-I+and+SWIR+ranges+for+bio-imaging+applications%5BTitle%5D)+AND+%22Small%22%5BJournal%5D)">ZGSO:Cr3+,Ni2+ persistent phosphors with dual emission in NIR-I and SWIR ranges for bio-imaging applications.</a> Small. 20 (51), 2406507(2024).</li>
<li>Giordano, L., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Persistent+luminescence+induced+by+upconversion%3A+an+alternative+approach+for+rechargeable+bio-emitters%5BTitle%5D)+AND+%22Adv+Opt+Mater%22%5BJournal%5D)">Persistent luminescence induced by upconversion: an alternative approach for rechargeable bio-emitters.</a> Adv Opt Mater. 11 (11), 2201468(2023).</li>
<li>Cai, G., Giordano, L., Richard, C., Viana, B. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Effect+of+the+elaboration+method+on+structural+and+optical+properties+of+Zn1.33Ga1.335Sn0.33O4%3A0.5%25Cr3%2B+persistent+luminescent+nanomaterials%5BTitle%5D)+AND+%22Nanomaterials%22%5BJournal%5D)">Effect of the elaboration method on structural and optical properties of Zn1.33Ga1.335Sn0.33O4:0.5%Cr3+ persistent luminescent nanomaterials.</a> Nanomaterials. 13 (15), 2175(2023).</li>
<li>Urbach, F. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Zur+lumineszenz+der+alkalihalogenide%5BTitle%5D)+AND+%22Sitzungsber+Akad+Wiss+Wien%22%5BJournal%5D)">Zur lumineszenz der alkalihalogenide.</a> Sitzungsber Akad Wiss Wien. 139, 363-372 (1930).</li>
<li>Richard, C., Viana, B. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Persistent+X-ray-activated+phosphors%3A+mechanisms+and+applications%5BTitle%5D)+AND+%22Light+Sci+Appl%22%5BJournal%5D)">Persistent X-ray-activated phosphors: mechanisms and applications.</a> Light Sci Appl. 11 (1), 123(2022).</li>
<li>Katayama, Y., Kayumi, T., Ueda, J., Dorenbos, P., Viana, B., Tanabe, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((The+role+of+Ln3%2B%28Ln+%3D+Eu%2C+Yb%29+in+persistent+red+luminescence+in+MgGeO3%3AMn2%2B%5BTitle%5D)+AND+%22J+Mater+Chem+C%22%5BJournal%5D)">The role of Ln3+(Ln = Eu, Yb) in persistent red luminescence in MgGeO3:Mn2+.</a> J Mater Chem C. 5 (34), 8893-8900 (2017).</li>
<li>Yang, F., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((A+biomineral-inspired+approach+of+synthesizing+colloidal+persistent+phosphors+as+a+multicolor%2C+intravital+light+source%5BTitle%5D)+AND+%22Sci+Adv%22%5BJournal%5D)">A biomineral-inspired approach of synthesizing colloidal persistent phosphors as a multicolor, intravital light source.</a> Sci Adv. 8 (30), eabo6743(2022).</li>
<li>Ding, L., Wang, X. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Luminescent+oxygen-sensitive+ink+to+produce+highly+secured+anti-counterfeiting+labels+by+inkjet+printing%5BTitle%5D)+AND+%22J+Am+Chem+Soc%22%5BJournal%5D)">Luminescent oxygen-sensitive ink to produce highly secured anti-counterfeiting labels by inkjet printing.</a> J Am Chem Soc. 142 (31), 13558-13564 (2020).</li>
<li>Sanders, S. N., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Triplet+fusion+upconversion+nanocapsules+for+volumetric+3D+printing%5BTitle%5D)+AND+%22Nature%22%5BJournal%5D)">Triplet fusion upconversion nanocapsules for volumetric 3D printing.</a> Nature. 604 (7906), 474-478 (2022).</li>
</ol>

<table><tbody><tr><td>LED de 405 nm</td><td>Thorlabs</td><td>N/A</td><td>Fonte de excitação para medições de TL</td></tr><tr><td>LED de 455 nm</td><td>Thorlabs</td><td>N/A</td><td>Fonte de excitação para luminescência persistente</td></tr><tr><td>Espectrômetro Acton SpectraPro 2150i&nbsp;</td><td>Princeton Instruments</td><td>Acton Spectra Pro</td><td>Monocromador visível; 300 sulcos/mm, centralizados a 500 nm; combinado com ICCD para TL</td></tr><tr><td>Ácido bórico (H3BO3)</td><td>Sigma-Aldrich</td><td>10043-35-3</td><td>Precursor para doping B3+ em reação de estado sólido</td></tr><tr><td>Criostato de fluxo de he-pulgão em ciclo fechado</td><td>Criogenia Sumitomo</td><td>HC-4E</td><td>Usado para experimentos de TL, até 15 K</td></tr><tr><td>Placa de aquecimento</td><td>Thermo Scientifi</td><td>88880004</td><td>Usado para pré-aquecer amostras para desarmamento térmico antes das medições QY</td></tr><tr><td>Campo de luz</td><td>Princeton Inc.</td><td>N/A</td><td>Software de detecção &nbsp;</td></tr><tr><td>Brometo de Potássio (KBr)</td><td>Sigma-Aldrich</td><td>7758-02-3</td><td>Usado como matriz para pellets (amostra de 50 mg + 300 mg KBr & rarr; prensado em pellets de 1 cm de diâmetro e vezes 2 mm de espessura)</td></tr><tr><td>Câmera Scientific Pixis 100 ICCD &nbsp;</td><td>Princeton Instruments (Roper Scientific)</td><td>Pixis 100</td><td>Câmera ICCD; Usado para TL, PersL, detecção de RL (resfriado até e menos; 65 & deg; C de medições por raios X)</td></tr><tr><td>Sr4Al14O25:Eu2+,Dy3+,B3+ amostra</td><td>BREVALOR S&agrave; RL</td><td>Daniel Rytz preparou</td><td>Sintetizado em laboratório por reação em estado sólido a 1400 & graus; C usando óxidos (pureza de 4 N); Eu2+ ~1,0% mol%, Dy3+ ~1,5% mol%, B3+ ~17,5% mol%.</td></tr><tr><td>SrAl2O4:Eu2+,Dy3+,B3+ amostra</td><td>BREVALOR S&agrave; RL</td><td>Daniel Rytz preparou</td><td>Pólvora comercial; Eu2+ ~1,5% mol%, Dy3+ ~5,0% mol%, B3+ ~0,9% em peso.</td></tr><tr><td>Controlador de temperatura</td><td>Lago-margem</td><td>Modelo 340</td><td>Acoplado ao criostato para controle de TL</td></tr><tr><td>Winspec32</td><td>Winspec33</td><td>N/A</td><td>Software de detecção &nbsp;</td></tr></tbody></table>

controle dependente de fase da profundidade da armadilha e luminescência persistente em fósforos de aluminato de estrôncio

Phase-Dependent Control of Trap Depth and Persistent Luminescence in Strontium Aluminate Phosphors

Controle dependente de fase da profundidade da armadilha e luminescência persistente em fósforos de aluminato de estrôncio

Persistent luminescent (PersL) materials have garnered significant attention for applications in visualization, signaling, bioimaging, and ...

phase-dependent-control-trap-depth-persistent-luminescence-strontium

Research

JoVE Journal

Chemistry

Química

Cavitação acústica em líquidos submetidos a ultra-som poder cria condições extremas transitórios dentro das bolhas em colapso, que são a origem da reatividade química incomum e emissão de luz, conhecido como sonoluminescência. Na presença de gases nobres, de plasma de não equilíbrio é formado. As partículas "quentes" e os fotões gerados pelo colapso de bolhas são capazes de excitar as espécies em solução.

Ativando moléculas, íons e partículas sólidas com Acústico cavitação

Um dispositivo integrado, incorporando uma célula e tripleto-tripleto aniquilação solares up-conversion unidade sensibilizadas por corante foi produzida, obtendo-se a colheita de luz melhorada, a partir de uma secção mais larga do espectro solar. De acordo com os níveis de irradiação modestos foi demonstrada uma resposta melhorada significativamente para fótons de baixa energia, produzindo um número recorde de mérito para células solares sensibilizadas por corante.

Integrando um Triplet-triplete Annihilation Sistema Up-conversion para melhorar Dye-sensibilizadas Response célula solar para a Luz Sub-bandgap

Um excelente química e luminescência estabilidades de fósforos (oxi) de nitreto de apresentá-la como uma alternativa promissora para uso no momento sulfureto e óxido de fósforos. Neste artigo, apresentamos a forma de investigar suas propriedades de luminescência locais usando cathodoluminescence de baixa energia (CL).

Catodoluminescência baixa energia para (oxi) Phosphors nitreto

Este trabalho detalha os procedimentos para o crescimento e caracterização de SrTiO cristalina 3 diretamente sobre substratos de germânio por deposição de camadas atômicas. O procedimento ilustra a capacidade de um método de crescimento de todos os produtos químicos para integrar monoliticamente em óxidos semicondutores para dispositivos semicondutores de óxido de metal.

Crescimento epitaxial de Perovskita titanato de estrôncio em Germânio via deposição de camadas Atomic

Uma técnica viável para a formação de bicristais de titanato de estrôncio em alta pressão e taxa de aquecimento rápida através do aparelho de sinterização por plasma de faísca é desenvolvida.

Faísca Plasma Sintering aparelho utilizado para a Formação de titanato de estrôncio Bicrystals

Este trabalho apresenta uma metodologia de microfabrication para superfície armadilhas de íons, bem como um procedimento experimental detalhado para íons de itérbio armadilhas em um ambiente de temperatura.

Os métodos experimentais de armadilhagem sem crueldade íons usando Microfabricated íon armadilhas de superfície

Aqui, apresentamos um método de caracterização espectroscópica de moléculas orgânicas através da espectroscopia de fotoluminescência tempo-resolvido a escala temporal nanossegundo-para-milissegundo em condições de livre de oxigênio. Também são descritos métodos para eficientemente remover oxigênio das amostras e, assim, limitar a têmpera de luminescência.

Tempo-resolvido compostos orgânicos de Photophysical caracterização dos Triplet-colheita em um livre de oxigênio ambiente usando uma câmera de iCCD

Podemos fabricar metal/LaAlO3/SrTiO3 estende usando uma combinação de deposição do laser pulsado e em situ magnétron que sputtering. Através de magnetotransport e em situ x-ray Spectroscopy espectroscopia experiências, vamos investigar a interação entre fenômenos eletrostáticos e químicas do gás quase elétron bidimensional formado neste sistema.

Crescimento e eletrostático química/Propriedades de Metal/LaAlO3/SrTiO3 estende

Os materiais óxidos apresentam muitas propriedades exóticas que podem ser controladas pelo ajuste do teor de oxigênio. Aqui, demonstramos a sintonia do conteúdo de oxigênio em óxidos variando os parâmetros de deposição do laser pulsado e realizando o pós-recozimento. Como exemplo, as propriedades eletrônicas de heteroestruturas baseadas em SrTiO3 são ajustadas por modificações de crescimento e recozimento.

Ajuste das propriedades do óxido pelo controle de vacância de oxigênio durante o crescimento e recozimento

Um protocolo é apresentado para a síntese de nanomateriais luminescentes persistentes (PLNPs) e suas potenciais aplicações em displays regraváveis e processamento artístico utilizando o efeito afterglow sob irradiação de luz ultravioleta (365 nm).

Síntese de nanopartículas luminescentes persistentes para displays regraváveis e aplicações de iluminação

Aprenda a caracterizar fósforos de aluminato de estrôncio com luminescência persistente azul e verde. Este método demonstra aplicações dinâmicas de anticontrafacção com resolução temporal e térmica.

Controle dependente de fase da profundidade da armadilha e luminescência persistente em fósforos de aluminato de estrôncio

Explorar mais vídeos