Name: hydrogels and their water absorption
Uploaded: 2023-04-30T07:06:34.000Z
Duration: 8 min 33 s
Channel: JoVE

The pre-gel solution was created in a 1000µl test tube; materials, role in polymerization and amounts added are listed in Tables 1.
<table border="1" fo:keep-together.within-page="1" fo:keep-with-next.within-page="always">
	<tbody>
		<tr>
			<td>Material</td>
			<td>Purpose</td>
			<td>Structure</td>
			<td>Mole percent</td>
		</tr>
		<tr>
			<td>2,2-Dimethoxy-2-phenyl-acetophenone (DMPAP)</td>
			<td>Free readical initiator (photoinitiator)</td>
			<td><img alt="Chemical structure diagram, synthesis of Benzyl acetate, organic chemistry formula." src="/files/ftp_upload/10486/10486eq5.jpg" data-altupdatedat="1761830439000" data-alt="Equation 5"> </td>
			<td>0.0012</td>
		</tr>
		<tr>
			<td>2-Hydroxethyl methacrylate
			
			(HEMA)
			</td>
			<td>Polymer backbone</td>
			<td><img alt="Chemical structure diagram of ethyl lactate molecule; organic compound formula." src="/files/ftp_upload/10486/10486eq6.jpg" data-altupdatedat="1761830439000" data-alt="Equation 6"> </td>
			<td>21.2121</td>
		</tr>
		<tr>
			<td>Tetraethylene glycol dimethacrylate (TEGDMA)</td>
			<td>Crosslinker</td>
			<td><img alt="Chemical structure, diagram, adipic acid derivative, organic compound, hexanedioic acid visualization." src="/files/ftp_upload/10486/10486eq7.jpg" style="opacity: 0.9;" data-altupdatedat="1761830439000" data-alt="Equation 7"> </td>
			<td>3.0303</td>
		</tr>
		<tr>
			<td>Ethylene glycol
			
			(EG)
			</td>
			<td>Solvent</td>
			<td><img alt="Ethylene glycol chemical structure diagram; organic compound molecule, HO-CH2-CH2-OH." src="/files/ftp_upload/10486/10486eq8.jpg" data-altupdatedat="1761830439000" data-alt="Equation 8"></td>
			<td>75.7576</td>
		</tr>
	</tbody>
</table>
Table 1. Hydrogel pre-gel constituents, their roles in hydrogel free radical polymerization, chemical 2D polymeric structure and the amounts added to the pre-gel solution.
Synthesis
<ol>
	<li>Prior to beginning hydrogel synthesis, a synthesis mold was assembled from two glass slides and three, 520-micron thick polyolefin-sheet spacers; this configuration was held together by binder clips as shown in Figure 6. The large glass slides were offset by a few millimeters to create a channel for pipetting the pre-gel solution into the mold.</li>
	<li>Before beginning hydrogel synthesis, obtain a 1000µl test tube, the chemicals described in Table 1, a micropipette with clean tips, and setting mold (Figure 6). All work should be performed in a fume hood with proper Personal Protective Equipment (PPE). PPE includes safety glasses or goggles, a lab coat and protective gloves.</li>
</ol>
<img alt="Simple physics lever demonstration using binder clips to illustrate static equilibrium principles." src="/files/ftp_upload/10486/10486fig6.jpg" data-altupdatedat="1761830439000" data-alt="Figure 6"> 
Figure 6: Hydrogel synthesis mold, created from two glass slides, three strips of 520-micron thick polyolefin-sheet as spacers, and large binder clips.
<ol start="3">
	<li>Add 0.0012 mole percent 2,2-Dimethoxy-2-phenyl-acetophenone (DMPAP), the solid photoinitator (free radical initiator that is initiated by light), to the test tube first.</li>
	<li>Add 21.2121 mole percent 2-hydroxethyl methacrylate (HEMA), the backbone molecule, and 3.0303 mole percent tetraethylene glycol dimethacrylate (TEGDMA), the crosslinking molecule to the test tube, using new pipette tips each time. TEGDMA will chemically crosslink the HEMA chains in the presence of free radicals by connecting the polymer chains into a network polymer.</li>
	<li>Mix the solution using a vortex machine until a homogenous solution is achieved.</li>
	<li>Measure 0.25 grams of Bromocresol Purple and rinse it into the solution using 75.7576 mole percent ethylene glycol (EG), the solvent. The pigment is only for viewing purposes (the hydrogel is transparent otherwise), and EG serves as a solvent to dissolve the initiating free radical initiator and keeps the hydrogel flexible.</li>
	<li>Mix the solution using the vortex machine until the pigment completely dissolves and the solution is homogenous.</li>
	<li>Using a micropipette, deposit the solution into the mold by aligning the tip of the micropipette with the offset edge of the large glass slides and uniformly injecting the pre-gel solution into the center of the mold.</li>
	<li>Place mold 5 centimeters below a UV emitting flashlight (Warson SK66) and irradiate the mold for one minute. UV light cleaves the bonds in the initiator species, turning them into free radicals which can then attack the polymer and crosslinker molecules. When fully networked, the hydrogel should be a rubber solid with a jello-like consistency.</li>
	<li>Remove mold from the light and disassemble the mold configuration. Remove hydrogel from the glass slides.</li>
	<li>Rinse both sides of the hydrogel with deionized water to remove any unreacted chemical species and oligomers from the product.</li>
	<li>To characterize how various UV-light exposure times affect degree of crosslinking and swelling ability, this procedure can be repeated while varying step nine. For characterization, the solution was exposed to UV light for 1 minute, 1.5 minutes and 5 minutes, producing a total of three hydrogels.</li>
</ol>
Characterization
The swelling degree of the hydrogel can be calculated by drying, hydrating and then re-drying the polymer.
<ol>
	<li>Place the finished hydrogels in a container with an alcohol such as Isopropyl Alcohol so that they are totally submerged. Leave in the alchohol for 4-8 hours, when the alcohol has replaced all the ethylene glycol in the hydrogel.</li>
	<li>Remove the hydrogels from the alcohol and leave to dry in the open, about 30 minutes. The alcohol evaporates more quickly than water or the solvent, allowing the hydrogel to maintain its structure.</li>
	<li>Weigh the dried hydogels.</li>
	<li>Submerge the hydrogels in DI water for at least 30 minutes, until they're completely swollen. Remove the gels from water, gently wipe dry and weigh.</li>
	<li>Calculate the swelling degree using the equation: <img alt="Swelling percentage formula, %swelling=(ws-wd)/wd x100, equation analysis, material science." src="/files/ftp_upload/10486/10486eq9v2.jpg" style="opacity: 0.9;" data-altupdatedat="1761830439000" data-alt="Equation 9"> , where <img alt="ΣFx=0 equation, static equilibrium, formula, educational diagram" src="/files/ftp_upload/10486/10486eq10.jpg" data-altupdatedat="1761830439000" data-alt="Equation 10"> is the weight of the swollen polymer and <img alt="Equation symbol for torque, represented as W_d." src="/files/ftp_upload/10486/10486eq11.jpg" data-altupdatedat="1761830439000" data-alt="Equation 11"> is the weight of the dried polymer.</li>
</ol>

Hydrogel synthesis is a technique for producing crosslinked polymeric materials which can swell in response to liquid, UV light, pH, or a range of other stimulants. Synthesis by combination of liquid solutions is advantageous for the simplicity of mixing and forming hydrogels, though the final product is generally impure and tends to contain polymers with low molecular weights. This specific procedure, while simple, involves chemicals that are both toxic and flammable, and therefore requires extreme care and preventative...

hydrogel synthesis

Source: Amber N. Barron, Ashlea Patterson, and <a href="https://www.jove.com/author/Taylor+D._Sparks">Taylor D. Sparks</a>, Department of Materials Science and Engineering, The University of Utah, Salt Lake City, UT
Hydrogels are a versatile class of cross-linked polymers produced through relatively simple procedures and with generally inexpensive materials. They can be formed from solution and involve a polymer backbone formed from monomer reagents, an initiator which makes the polymer reactive and a crosslinking species which binds the polymer chains together. An important aspect of these materials is that they swell in the presence of water, but this response can be tuned further to enhance swelling as a function of salinity, pH, or other signals. As a final product, hydrogels can be used in aqueous or dry environments, with a range of useful properties such as flexibility, high absorbance, transparency and thermal insulation. They are commonly used for liquid absorbance, sensors, consumer products, and drug delivery.

The final hydrogel monomer is shown in Figure 7, and the synthesized hydrogels are shown in Figure 8. The degree of swelling was found to be approximately 136% for the 1 min sample, 387% for the 1.5 min sample and 81% for the 5 min sample. These results demonstrate the relationship between degree of crosslinking, or the extent to which the network is connected, and swelling ability. More links between the polymer molecules mean m...

Hydrogel Synthesis

Source: Amber N. Barron, Ashlea Patterson, and Taylor D. Sparks, Department of Materials Science and Engineering, The University of Utah, Salt Lake City, ...

Hydrogels are a versatile class of cross-linked polymers, produced through relatively simple procedures using generally inexpensive materials. They are commonly used for liquid absorbents, sensors, consumer products and drug delivery. Hydrogels can be formed from solution, with an initiator making monomerie agents reactive to form a polymer backbone. A crosslinking species then binds the polymer chains together. An important aspect of these materials is that in the presence of water they swell. But this response can be tuned further to enhance swelling as a function of salinity, PH or other signals. Hydrogels can be used in aqueous or dry environments, with a range of useful properties such as flexibility, high absorbance, transparency and thermal insulation. This video will illustrate the synthesis and characterization of hydrogels.Hydrogels are capable of absorbing hundreds of times their weight in water. When water enters the crosslinked polymer network, it solubilizes hydrophilic, ionic or both species on the polymer backbone. The water molecules are larger than the solubilized groups. Because of this, their presence inside the network causes the hydrogel to swell. While the crosslinks connecting the polymer backbone prevent it from dissolving or breaking. Hydrogel synthesis is a technique for producing these crosslinked, polymeric materials. This is a simple procedure but involves chemicals that are both toxic and flammable and therefore requires extreme care and preventative measures. Using pre-gel constituents, hydrogels can be made via Free Radical Polymerization. One method starts with DMPAP as a Free Radical Initiator.The carbon-carbon bond in DMPAP is cleaved by ultra-violet light to form an unpaired, highly reactive electron called a free radical on each carbon atom. The free radicals react with the carbon-carbon double-bond in HEMA to form a propogating chain with a free radical on the end. The hydroxal group coming off the backbone is soluble in water, causing the cross-linked network to swell when water is present. The radicals also react with the two carbon-carbon double-bonds in TEGDMA, the chemical crosslinker. This links the backbone chains together. When the free radicals have been consumed, or have completely reacted, the hydrogel synthesis is complete. Swelling can be assessed by drying, hydrating and then re-drying the polymer. In the next section, we will synthesis and characterize hydrogels using this free radical polymerization method.Prior to beginning hydrogel synthesis, gather the necessary materials and chemicals. The glass slides in the previously assembled synthesis mold are offset by a few millimeters, to create a channel for pipetting the pre-gel solution into the mold. All work should be performed with proper Personal Protective Equipment in a fumehood, as this process involves chemicals that are both toxic and flammable. First, add 0.0012 mol percent DMPAP to the 1000 microliter test tube. Next, use a new pipette each time to add 21.2121 mol percent HEMA and then 3.0303 mol percent TEGDMA to the test tube. Mix the solution using a vortex machine until a homogenous solution is achieved. Dip the spatula into the pigment BCP and rinse it into the solution using 75.7576 mol percent of the solvent ethylene glycol.Mix the solution using the vortex machine until the pigment completely dissolves and the solution is homogenous.?This pigment is used to make the transparent hydrogel visible, while the solvent dissolves the Free Radical Initiator and keeps the hydrogel flexible. Deposit the solution into the mold using a micro pipette aligned with the offset edge of the synthesis mold. Uniformly inject the pre-gel solution into the center of the mold. Place the filled mold five centimeters below a UV-emitting flashlight and irradiate the mold for one minute. Remove the mold from the light and disassemble to remove the hydrogel from the glass slides.When fully networked, the hydrogel should be a rubber solid with a jello-like consistency. Rinse both sides of the hydrogel with deionized water to remove any unreacted chemical species and polygimers from the product. Repeat this procedure with UV light exposure times of 1.5 and five minutes to produce a total of three hydrogels.Submerge the finished hydrogels in a container with isopropyl alcohol for one to two hours. The alcohol will replace the ethylene glycol in the hydrogel, allowing it to dry quickly while maintaining its structure. Remove the hydrogels from the alcohol and leave to dry in the open for about 30 minutes. Weigh and record the weight of each of the dried hydrogels. Submerge the hydrogels in deionized water until completely swollen. Remove the gels from the water and gently wipe dry. Weigh and record the weight of the swollen hydrogels. Use the weight of the swollen hydrogels, Ws, and the dried hydrogels, Wd, to calculate the swelling degree.The degree of swelling was found to be approximately 136% for the one minute sample, 387% for the 1.5 minute sample, and 81% for the five minute sample. These results show that at the longest UV exposure time, there was less swelling. Due to the formation of more links between polymer molecules with increased UV exposure, there were more elastic restraining forces on the polymer chains. This resulted in hydrogels with more crosslinking expanding less than those with less crosslinking.Now that you appreciate the methods of synthesizing and characterizing hydrogels, let's take a look at how they are used in everyday products. Consumer products such as hospital pads, feminine hygiene pads and diapers, contain one of the most common super-absorbant polymers. This hydrogel can swell to absorb fluids up to 800 times its weight, allowing manufacturers to create products that are slim and comfortable. The hydrogel synthesized in this video is used as a sensor in a lawn sprinkler. The sensor is in contact with the soil and swells while the lawn is being watered, until it triggers the sprinkler shutoff.You've just watched Jove's introduction to hydrogel synthesis. You should now understand how hydrogels are synthesized and characterized. Thanks for watching.

Education

JoVE Science Education

Engineering

Materials Engineering

hydrogels and their water absorption

Hydrogels are cross-linked polymers that can absorb water and swell. They are made with relatively simple procedures and inexpensive materials, which makes them useful for many school-level chemistry and materials science topics.

A hydrogel starts with a polymer backbone built from monomer reagents. An initiator makes the polymer reactive, and a crosslinking species connects the chains together. This network gives the material its final structure.

Water absorption is one of the key features of hydrogels. Their swelling can also be tuned by salinity, pH, or other signals. That control helps explain why hydrogels can be designed for different uses.

Hydrogels may be used in either aqueous or dry environments. They can offer flexibility, high absorbance, transparency, and thermal insulation. Common applications include liquid absorbance, sensors, consumer products, and drug delivery.

Hydrogels and Their Water Absorption

optical materialography part 1: sample preparation

optical-materialography-part-1-sample-preparation

Preparing Solid Samples for Optical Microscopy

Optical microscopy of solid materials starts with careful sample preparation. Materialography is the study of microscopic structures in solids and the features seen in those images. It helps reveal details such as porosity, grain size and shape, and whether the microstructure shows anisotropy, or direction-dependent structure. This lesson focuses on the preparation steps used before optical microscopy. It covers the techniques and procedures needed to ready a solid material sample for imaging.

optical materialography part 2: image analysis

optical-materialography-part-2-image-analysis

Quantifying Microstructure in Optical Materialography

Optical materialography can be used to measure the microstructure of solid materials. It focuses on the microscopic structures seen in an exposed surface and uses them to study the material more deeply. A common goal is to estimate the three-dimensional microstructure of a sample from a two-dimensional cross section. This approach relies on the structural features visible in the image. It helps turn surface observations into quantitative data about the material. X-ray tomography can also...

x-ray photoelectron spectroscopy

XPS Surface Analysis of Materials

X-ray photoelectron spectroscopy, or XPS, is a surface analysis method for studying materials. It measures elemental composition, empirical formula, chemical state, and electronic state of the elements in a sample. Because the signal comes from the top few nanometers, XPS is especially useful for examining surfaces. To collect an XPS spectrum, a material is irradiated with an X-ray beam. At the same time, the instrument measures the kinetic energy and number of electrons that escape from the...

x-ray diffraction

Crystal Structure Using X-ray Diffraction

X-ray diffraction is a materials science method for finding crystal structure. It uses incident X-rays that strike a sample and scatter from its atoms and molecules. The scattered X-rays are measured by their intensity and scattering angle. The results are plotted as intensity versus angle. Scientists then analyze the position of the peaks and their strength to determine the structure of the material. This method can also show how a real crystal differs from an ideal one. It can reveal effects...

focused ion beams

Focused Ion Beams in Microfabrication

Focused ion beams are used in microfabrication and nano-fabrication. A focused ion beam, or FIB, is an instrument that can fabricate, trim, analyze, and characterize materials on micro- and nano-scales. These tools are used in many fields, from nano-electronics to medicine. FIB systems work with a beam of ions. That beam can mill, or sputter, material away. It can also deposit material and image surfaces at small scales. In many research labs, the ion column of a FIB is integrated with the...

directional solidification and phase stabilization

directional-solidification-and-phase-stabilization

Zone Melting for Alloy Refining

Zone melting directional solidification is a metallurgical process used to move a narrow molten region through a crystal, usually a bar-shaped sample. A furnace travels along the rod, so the molten zone moves from one end of the bar to the other. This controlled motion changes how material forms as it solidifies. In alloys, solute atoms tend to separate into the melt. Impurities also concentrate in the molten zone instead of staying in the solid. As the molten region moves forward, it carries...

differential scanning calorimetry

Measuring Polymer Crystallinity with DSC

Differential scanning calorimetry, or DSC, is a method used to measure the thermal properties of materials. It helps scientists see how much heat a material stores as it warms up. This heat storage is called heat capacity. DSC also measures the heat absorbed or released during chemical reactions and phase changes. From these measurements, it can help determine other properties such as glass transition temperature and polymer crystallinity. Polymers often have long, chain-like structures that...

thermal diffusivity and the laser flash method

thermal-diffusivity-and-the-laser-flash-method

How Laser Pulses Measure Heat Flow

Laser flash analysis measures thermal diffusivity, which describes how fast heat moves through a material compared with how much heat it stores. This material-specific property helps show how a sample transfers thermal energy and how it responds to temperature changes. Thermal diffusivity is related to thermal conductivity, the measure of how heat moves through a material because of a temperature difference. That relationship also depends on the material’s density, shown as ρ, and its specific...

electroplating of thin films

Fast Metal Coating Without a Vacuum

Electroplating is a way to add a thin metal coating to a surface using electric current. In this process, dissolved metal cations are reduced and form a film on an electrode. The method is also called electrodeposition. This page also compares electroplating with other thin film deposition methods. Chemical vapor deposition, or CVD, uses a gas-phase precursor. Spin coating spreads a liquid precursor by spinning it outward. Dip coating is similar, but the substrate is fully submerged instead of...

analysis of thermal expansion via dilatometry

analysis-of-thermal-expansion-via-dilatometry

Using Dilatometry to Measure Heating Effects

Dilatometry measures how a material changes in size as temperature changes. It can track changes in length, area, shape, or volume. The method is used to calculate thermal expansion, which is the expansion of a substance when it is heated. Thermal expansion matters when choosing materials for systems that face changing temperatures. Some materials need high thermal expansion, such as the liquid in a thermometer, because the change helps detect temperature shifts. Other uses need materials with...

electrochemical impedance spectroscopy

Why AC Signals Matter in Impedance

Electrical impedance describes how a circuit element resists the flow of electricity. It is a more general measure than electrical resistance, especially when a circuit is not simple enough to be described by resistance alone. Resistance is the ability of a circuit element to resist current. It is defined by Ohm's law, which relates voltage and current. That relationship works well for ideal resistors, but many real circuit elements are more complex. When an alternating current, or AC, is...

ceramic-matrix composite materials and their bending properties

ceramic-matrix-composite-materials-and-their-bending-properties

Bone-Inspired Ceramic Composites in Bending

Bone helps show how ceramic-matrix composites work. In this material system, the ceramic part gives compressive strength, while the polymer fiber reinforcement adds tensile and flexural strength. By changing the amounts of ceramic and polymer, engineers can make materials for specific uses. This idea matters in biomedical engineering, where replacing or copying bone after disease or traumatic injury is an important goal. For this study, plaster of Paris, a calcium sulfate compound, is used to...

nanocrystalline alloys and nano-grain size stability

nanocrystalline-alloys-and-nano-grain-size-stability

Keeping Nanocrystalline Alloy Grains Small

Nanocrystalline alloys are metals with grain sizes smaller than 100 nm. These tiny grains can give the material enhanced physical and mechanical properties. That is why nanocrystalline alloys are used or studied for semiconductor devices, biosensors, and aerospace parts. A major challenge is making dense bulk materials from these alloys. To reach close to 100% density, the material must be processed with elevated temperature and pressure. But as temperature and pressure rise, the small grains...

Hydrogels are cross-linked polymers that can absorb water and swell. They are made with relatively simple procedures and inexpensive materials, which makes them useful for many school-level chemistry and materials science topics. A hydrogel starts with a polymer backbone built from monomer reagents. An initiator makes the polymer reactive, and a crosslinking species connects the chains together. This network gives the material its final structure. Water absorption is one of the key features...

materials engineering

This collection features cutting-edge methods for analysis and characterization of materials, and introduces a range of advanced materials and processes for new technologies and applications.

Explore how hydrogels are made from cross-linked polymers and why they swell in water. Learn their properties and common uses in sensors, absorbent products, and drug delivery.