Name: Antifouling Self-assembled Monolayers on Microelectrodes for Patterning Biomolecules (Video) | JoVE Journal
Uploaded: 2009-08-25T16:00:00.000+00:00
Duration: 10 min 27 s
Description: Learn to fabricate antifouling PEG-SAM coated gold microelectrodes on silicon substrates for precise biomolecule patterning. This method enables nanoscale electrophoretic positioning of microtubules while preventing biofouling.

ai_agent_IP

ai_agent

maintenance

instantTrialDurationMinutes

isBiopharma

enableNewMyJoveSectionDesign

educationFeatures

seoMetaApi

ai_copilot_institution_blacklist

ai_chat_institution_blacklist

freeAccessWindow

ssoRoleCapture

scheduledMaintenanceBanner

joveLabsFeatures

disable_autoplay_for_bots

extended_trial_duration

5 minutes

We acknowledge Melissa Grunlan for helpful discussions on SAM formation. This research was supported in part by the Robert A. Welch Foundation (A-1585).

Preparation of reagents
Prepare PIPES buffer (80 mM PIPES, 1mM MgCl2, 1mM EGTA, adjusted to pH 6.8 with KOH). Aliquot and store glucose oxidase, catalase and glucose at -70°C and taxol at -20°C according to existing protocols.1,2 Aliquot and store tubulin at -70°C according to the instructions included by the supplier.
Pattern Au microelectrodes using lithography
<ol>
<li>Cut silicon wafers into 1 cm ´ 1.5 cm substrates using a scribe or wafer cutter. Clean the substrates by placing them in a beaker with enough acetone to cover them and sonicate for 5 minutes. Without allowing the substrates to dry, rinse them in fresh acetone, then immediately rinse in isopropanol and dry using nitrogen.</li>
<li>Fabricate Au microelectrodes on the clean substrates using standard, positive-tone photolithography or electron beam lithography, depending on the size of the features desired.3 When designing the pattern geometry, keep the diameter of each electrode pattern below 100 microns to ensure coverage by the PEG SAM (described in the next section). Include contact pads (~ 300 mm
2) positioned 300 to 500 mm from the pattern with a 1 mm line connecting the pad with the electrode (Fig. 1). Place the lithographic patterns near the middle of the substrate to allow space around the pattern for assembling the flow chamber. <img border="0" src="/files/ftp_upload/1390/1390fig1thumb.jpg" alt="Silicon substrate with lithographic pattern diagram; Au scratch contact and microelectrode layout." data-altupdatedat="1787630408000" data-alt="figure 1"> Figure 1. Sample geometry. Please <a href="https://www.jove.com/files/ftp_upload/1390/1390fig1.jpg">click here</a> to see a larger version of figure 1.</li>
<li>After development of the pattern in the resist layer, scratch a line in the resist from the contact pad to the edge of the substrate using tweezers (Fig. 1). Upon metal deposition, the scratch will allow electrical contact between the electrode and the edge of the substrate. A deposition chamber, preferably with two sources, is used to deposit the metal layer. The electrodes are formed by deposition of 2 nm of Cr (for adhesion) followed by 6 nm of Au, without breaking vacuum. A quartz crystal microbalance equipped inside the chamber can be used to measure the thickness of the films during deposition.</li>
</ol>
Prepare the SAM
<ol>
<li>Preheat and oven in a well-ventilated area to 75°C. Prepare the silanization solution by adding 20 mL of toluene to a 250 mL glass beaker. Then add 1 mL PEG-silane (i.e. 5% v/v) to the toluene using a plastic pipette. Mix in the PEG-silane well by pipetting up and down 5 to 10 times and then stirring with the pipette for 30 seconds.</li>
<li>Place the patterned samples in the beaker with the patterned side facing upwards, making sure that they are completely submerged in the PEG-silane toluene solution and are evenly spaced across the bottom of the beaker. Place the beaker in the oven and bake 18 to 21 hours at 75°C. While the SAM is forming, prepare the counterelectrode (see below) and assemble any additional components required for the remaining steps.</li>
<li>After 18-21 hours in the oven, the toluene should evaporate leaving the patterned samples in a viscous PEG-silane residue. Add 20 mL of toluene to the beaker and soak the samples for 1-2 minutes. Remove the samples from the beaker and rinse with toluene, then isopropanol, and finally dry with nitrogen. At this point, the samples should look clean and the SAM layer should be invisible to the naked eye. SAMs prepared this way are usable for up to two days when stored under cool dry conditions (25 °C, moderate humidity). Unsuccessful SAM formation results in a cloudy or uneven hued residue coating on the surface.</li>
</ol>
Fabricate the counterelectrode
In the same deposition chamber setup used for microelectrode deposition, make a counterelectrode by depositing 1 nm of Cr, followed by 4 nm of Au onto a 22 x 50 mm No. 1 or No. 0 glass coverslip. The counterelectrode should be nearly transparent with a light gray or pink tint. Store the counterelectrode coated-side-up in a Petri dish to keep it clean.
Polymerize tubulin into MTs
<ol>
<li>Thaw unlabeled tubulin and rhodamine tubulin and immediately combine at a ratio of 1:2 labeled to unlabeled to obtain bright MTs. Mix by pipetting up and down several times. Polymerize the tubulin for 20-40 minutes in a heated water bath at 37°C. The length of the MTs will be greater for longer polymerization times. While the tubulin is polymerizing, prepare a PIPES-taxol buffer by adding taxol to 20 mM into a microcentrifuge tube containing PIPES buffer. Mix the taxol well by pipetting up and down several times and vortexing, and then place the tube into the heated bath at 37°C. After polymerization, dilute the MTs by 1/100 in warm PIPES-taxol buffer and shield from light. MTs prepared in this way will elongate over time and bundle, which can be reduced by further dilution.</li>
<li>Prepare a 10x oxygen scavenging mixture (OS) by combining 30 mL cold PIPES buffer (0-4°C), 5 mL of 50% 2-mercaptoethanol, 5 mL glucose oxidase, 5 mL catalase, and 5 mL glucose.2 The glucose should be added last. Mix by pipetting up and down 3-5 times after adding each component. Place the OS mixture on ice; it will remain effective for about 2 hours.</li>
<li>Verify that the MT polymerization was successful and that the MTs are stable under several minutes of fluorescence excitation by imaging the prepared MTs with 1x OS mix. For imaging the MTs prepared in this way, be sure to use an excitation/emission filter combination suitable for rhodamine fluorescence. Determine the best working dilution for imaging individual filaments by further diluting the MTs by 1/10 to 1/100 using PIPES buffer and imaging with 1x OS mix.</li>
<li>Prepare a flow chamber by sandwiching a large (22 x 50 mm) and small (22 x 22 mm) glass coverslip with two pieces of double-sided tape placed 2-3 mm apart. The tape is easily cut into strips by placing it on a glass slide and cutting with a razor blade. Introduce a few microliters of MTs into the flow cell using a micropipette. For high magnification imaging, long working distance objectives may be required for imaging the upper surface of the flow chamber. The distance from the coverslip/sample surface to the upper surface of the flow chamber is determined by the thickness of the tape and should be 60-100 mm.</li>
</ol>
Pattern MTs using electrophoresis
<ol>
<li>Prepare an electrophoresis chamber by placing two thin strips of double-sided tape across the patterned, SAM-coated sample such that the electrode is between the strips with the connecting path running perpendicular to the tape (Fig. 2). Place the counterelectrode on the double-sided tape with the metal side touching the tape such that the edge of the sample overhangs the counterelectrode by about 3 mm (Fig. 2). Cut several 15 cm lengths of the insulated copper magnet wire and strip 1 cm of the insulation off of both ends. Attach a wire to the exposed Au area of the substrate using a small drop of silver paint while taking care to avoid making electrical contact with the counterelectrode (this can be checked with a multimeter). Attach a second wire to the counterelectrode using silver paint. Wires attached with silver paint can be further secured to the samples with tape. <img src="/files/ftp_upload/1390/1390fig2thumb.jpg" border="0" alt="Microfluidic device diagram; flow control, sample positioning, evaporation prevention method." data-altupdatedat="1787630408000" data-alt="figure 2"> Figure 2. Flow cell assembly for an inverted fluorescence microscope. Please <a href="https://www.jove.com/files/ftp_upload/1390/1390fig2.jpg">click here</a> to see a larger version of figure 2.</li>
<li>Introduce MTs at the desired dilution using PIPES buffer combined with OS at 1x final concentration. Image at 20X magnification and locate the pattern on the silicon wafer before applying a voltage. Optionally, the flow chamber can be sealed using nail polish to prevent fluid flow and MT migration in the plane of the flow chamber.</li>
<li>Apply a voltage up to 1 V and observe migration of MTs. Lower voltages (down to about 0.5 V) may be used if reversible trapping of MTs is desired; however this requires sealing the flow chamber to prevent lateral drift. Nail polish works well for sealing the open ends of the flow chamber. At voltages above about 0.7 V, some MT adhesion may be seen on the pattern, though it will be weak. At voltages above about 0.9 V, the MT migration will be faster, and the adhesion will be stronger. Above about 1.2 V the likelihood for inducing electrolysis (gas bubble formation) and also for destroying the microelectrodes increases significantly. Migration can be tracked by adjusting the vertical plane of focus of the microscope. If carried out correctly, the MTs will localize at the electrode surfaces.</li>
</ol>

<ol><li>Tubulin Polymerization with GTP/GMPCPP/Taxol [Internet]. , Harvard University. Cambridge, Ma. Available from:
 
 <a target="_blank" href="http://mitchison.med.harvard.edu/protocols/poly.html">http://mitchison.med.harvard.edu/protocols/poly.html</a> (2009).</li>
<li>Flow Cell Assays with Microtubules: Motility/Dynamics [Internet]. , Harvard University. Cambridge, Ma. Available from:
 
 <a target="_blank" href="http://mitchison.med.harvard.edu/protocols/flowcell.html">http://mitchison.med.harvard.edu/protocols/flowcell.html</a> (2009).</li>
<li><a target="_blank" href="http://scholar.google.com/scholar?hl=en&safe=off&q=%22Handbook+of+Microlithography%2C+Micromachining%2C+and+Microfabrication%3A+Microlithography%22">Handbook of Microlithography, Micromachining, and Microfabrication: Microlithography</a>. Rai-Choudhury, P. , SPIE Press. Bellingham, WA. (1997).</li>
</ol>

The authors have nothing to disclose.

The migration of MTs is easily visualized using fluorescence microscopy because of their brightness and the low background fluorescence. The method is generally applicable to biomolecule patterning, as it only requires that the biomolecules be induced to carry a net charge by suitable adjustment of the buffer pH. Electroosmosis is avoided in this setup because there are no charged surfaces such as the silica walls used in capillary electrophoresis.
Several modifications of this method are pos...

<table><tbody><tr><td>2-[methoxypoly-(ethyleneoxy)propyl]-trimethoxysilane (PEG-silane)</td><td>Gelest Inc.</td><td>SIM6492.7</td><td>6-9 PEG units;molecular weight 450-600 g mol&lt;sup&gt;-1&lt;/sup&gt;</td></tr><tr><td>2-mercapt&amp;#8211;thanol</td><td>Sigma-Aldrich</td><td>M7522</td><td></td></tr><tr><td>Acetone</td><td>EMD Millipore</td><td>AX0120-8</td><td>ACS grade</td></tr><tr><td>Catalase</td><td>Calbiochem</td><td>219001-5MU</td><td></td></tr><tr><td>Chlorobenzene</td><td>EMD Millipore</td><td>MK441908</td><td>ACS grade</td></tr><tr><td>Ethylene glycol-bis(2-amin&amp;#8211;thylether)&lt;em&gt;-N,N,N&amp;rsquo;,N&amp;rsquo;-&lt;/em&gt;tetraacetic acid (EGTA)</td><td>Calbiochem</td><td>324626</td><td></td></tr><tr><td>Glucose</td><td>EMD Millipore</td><td>DX0145-1</td><td></td></tr><tr><td>Glucose oxidase</td><td>MP Biomedicals</td><td>100330</td><td></td></tr><tr><td>Guanosine-5&amp;rsquo;-[(&amp;alpha;,&amp;#914;)-methyleno]triphosphate, Sodium salt (GMPCPP)</td><td>Jena Biosciences, GmbH</td><td>NU-405s</td><td></td></tr><tr><td>Guanosine-5&amp;rsquo;-triphosphate</td><td>Sigma-Aldrich</td><td>G8752</td><td></td></tr><tr><td>Isopropanol</td><td>EMD Millipore</td><td>PX1835-5</td><td>ACS grade</td></tr><tr><td>Methyl isobutyl ketone (MIBK)</td><td>Fisher Scientific</td><td>AC12739-0010</td><td></td></tr><tr><td>Paclitaxel (taxol)</td><td>Calbiochem</td><td>580555</td><td></td></tr><tr><td>Piperazine-N,N&amp;rsquo;&amp;rsquo;-bis(2-ethanesulfonic acid) (PIPES)</td><td>Sigma-Aldrich</td><td>P1851</td><td></td></tr><tr><td>Polymethylmethacrylate (PMMA)</td><td>Brewer Science, Inc.</td><td>950K</td><td>molecular weight 950K</td></tr><tr><td>Rhodamine tubulin</td><td>Cytoskeleton, Inc.</td><td>T331M</td><td>from bovine brain 99% pure, lyophilized</td></tr><tr><td>Toluene</td><td>EMD Millipore</td><td>TX0735-5</td><td>ACS grade</td></tr><tr><td>Tubulin</td><td>Cytoskeleton, Inc.</td><td>T238</td><td>from bovine brain 99% pure, lyophilized</td></tr><tr><td colspan="4">&lt;p class=&quot;jove_content&quot;&gt;No. 1 borosilicate glass coverslips (22 X 50 mm) were purchased from VWR. Polished electronic grade p-type &amp;lt;111&amp;gt; silicon wafers were purchased from Addison Engineering, Inc. High-purity silver paint was obtained from Structure Probe, Inc. (Catalog # 5001 AB). Insulated fine gauge copper magnet wire (~ 0.08 mm (0.003&amp;#8221;) diameter) can be obtained from electronic supply companies.&lt;/p&gt;</td></tr></tbody></table>

antifouling self-assembled monolayers on microelectrodes for patterning biomolecules

Antifouling Self-assembled Monolayers on Microelectrodes for Patterning Biomolecules

We present a procedure for forming a poly(ethylene glycol) (PEG) trimethoxysilane self-assembled monolayer (SAM) on a silicon substrate with gold microelectrodes. The PEG-SAM is formed in a single assembly step and prevents biofouling on silicon and gold surfaces. The SAM is used to coat microelectrodes patterned with standard, positive-tone lithography. Using the microtubule as an example, we apply a DC voltage to induce electrophoretic migration to the SAM-coated electrode in a reversible manner. A flow chamber is used for imaging the electrophoretic migration and microtubule patterning in situ using epifluorescence microscopy. This method is generally applicable to biomolecule patterning, as it employs electrophoresis to immobilize target molecules and thus does not require specific molecular interactions. Further, it avoids problems encountered when attempting to pattern the SAM molecules directly using lithographic techniques. The compatibility with electron beam lithography allows this method to be used to pattern biomolecules at the nanoscale.

We present a procedure for forming a poly(ethylene glycol) self-assembled monolayer (PEG-SAM) on a silicon substrate with gold microelectrodes. The PEG-SAM is formed in a single step and prevents biofouling on silicon and gold surfaces. Electrophoresis is then used for patterning biomolecules down to the nanoscale.

We present a procedure for forming a poly(ethylene glycol) (PEG) trimethoxysilane self-assembled monolayer (SAM) on a silicon substrate with gold ...

This procedure begins by fabricating a micro electrode on a silicone substrate. A polyethylene glycol self-assembled monolayer is formed over the micro electrode and substrate to prevent fouling of microtubules. Then rumine labeled microtubules are prepared.Finally, microtubules are patterned onto the ated electrodes using electrophoresis. Hi, I am John Noel from the Nana Lab in the Department of Physics and from the Molecular Biomechanics Laboratory in the Department of Biomedical Engineering at Texas a and m University. I'm Wil free Teza from the physics department and the director of the Center Skill Science and Technology at Texas a m University.And I'm Juan Quang, the director of the Molecular Biomechanics Laboratory at Texas a and m University Department of Biomedical Engineering. Today we'll show you a procedure for fabricating micro electrodes coated with a non fouling self-assembled monolayer. We use this procedure in our laboratory to study micro tube paling using electrophoresis.So let's get started. To begin, use a scribe or wafer cutter to cut silicon wafers into one centimeter by 1.5 centimeter pieces to use as substrates. Now clean the substrates by placing them in a beaker with enough acetone to cover them and sonicate for five minutes without allowing the substrates to dry.Rinse them in fresh acetone and then immediately rinse them again in isopropanol and use nitrogen to dry them. Using standard positive tone photolithography or electron beam lithography, fabricate the gold micro electrodes on the clean substrates. When designing the pattern geometry, keep the diameter of each electrode pattern below 100 microns To ensure coverage by the polyethylene glycol trimeth oxy seline self-assembled monolayer or peg Sam, include contact pads positioned 300 to 500 micrometers from the pattern with a one millimeter line connecting the pad with the electrode.After development of the pattern in the resist layer, use tweezers to scratch a line in the resist from the contact pad to the edge of the substrate. Upon metal deposition, the scratch will allow electrical contact between the electrode and the edge of the substrate. A deposition chamber, preferably with two sources, is used to deposit the metal layer.The electrodes are formed by deposition of two nanometers of chromium, followed by six nanometers of gold Without breaking vacuum, a quartz crystal micro balance equipped inside the chamber can be used to measure the thickness of the films during deposition. We can now begin to prepare the self-assembled monolayer in a well-ventilated area, preheat and oven to 75 degrees Celsius. Prepare the ization solution by adding one milliliter of peg seline to 20 milliliters of toluene in a 250 milliliter glass beaker.Mix well by pipetting up and down five to 10 times and then stirring with the pipette for 30 seconds. Place the pattern samples in the beaker pattern side up, making sure that they're completely submerged in the solution and are evenly spaced across the bottom of the beaker. Place the beaker in the oven and bake it for 18 to 21 hours while the Sam is forming.Prepare the counter electrode by depositing one nanometer of chromium followed by four nanometers of gold onto a 22 by 50 millimeter glass cover slip. The counter electrode should be nearly transparent with a light gray or pink tint. Store the counter electrode coated side up in a Petri dish to keep it clean.After 18 to 21 hours in the oven, remove the beaker from the oven. The toluene should have evaporated leaving the pattern samples in a viscous peg cline residue. Add 20 milliliters of toluene to the beaker and soak the samples for one to two minutes.Remove the samples from the beaker and rinse them with toluene, then isopropanol and finally dry them with nitrogen. At this point, the samples should look clean and the Sam layer should be invisible to the naked eye. Sam's prepared this way are usable for up to two days when stored in cool dry conditions.Unsuccessful Sam formation results in a cloudy or uneven hued residue coating on the surface. With the Sams prepared, we can now begin polymerization of tubulin into microtubules. Start by thawing unlabeled tubulin and r domine tubulin, and immediately combine them at a ratio of two to one unlabeled to labeled to obtain bright microtubules.Mix them well by pipetting up and down several times. Next, polymerize the tubulin for 20 to 40 minutes in a heated water bath at 37 degrees Celsius while the tubulin is polymerizing. Prepare a pipes Taxol buffer by mixing 20 micromolar Taxol with pipee buffer.Mix well by pipetting up and down several times and vortexing, and then place the tube into the heated bath at 37 degrees Celsius. After polymerization, dilute the microtubules in warm pipee Taxol buffer and shield them from light. Verify that the micro tubule polymerization was successful and that the microtubules are stable under several minutes of fluorescence excitation.By imaging the prepared microtubules with an oxygen scavenging mixture with polymerization of tubulin into microtubules complete. Let's begin patterning the MTS with electrophoresis. To begin, cut a piece of double-sided tape into thin strips by placing it on a glass slide and using a razor blade to cut place two strips of double-sided tape across the patterned Sam coated sample, such that the electrode is between the strips with the connecting path running perpendicular to the tape.Place the counter electrode on the double-sided tape with the metal side touching the tape such that the edge of the sample overhangs the counter electrode by about three millimeters. Cut several 15 centimeter lengths of insulated copper magnet wire and strip one centimeter of the insulation off of both ends. Use a small drop of silver paint to attach a wire to the exposed gold area of the substrate while taking care to avoid making electrical contact with the counter electrode.Now use silver paint to attach a second wire to the counter. Electrode wires attached with silver paint can be further secured to the samples with tape. Next, using a pipette, introduce microtubules at the desired dilution image at 20 x magnification and locate the pattern on the silicon wafer before applying a voltage.Because of the depth of the flow chamber, long working distance objectives may be needed to image the upper surface of the flow chamber. The distance from the sample surface to the upper surface of the flow chamber is determined by the thickness of the tape and should be around 60 to 100 micrometers. Apply a voltage of up to one volt and observe the migration of microtubules.If reversible trapping of microtubules is desired. Use nail polish to seal the flow chamber to prevent lateral drift and use lower voltages down to about 0.5 volts. Migration can be tracked by adjusting the vertical plane of focus of the microscope with the applied voltages around 0.9 to 1.2 volts microtubules localize at the electrode surfaces.Higher voltage will make the migration faster and adhesion stronger, but excessive voltage will induce electrolysis and depolymerize. Microtubules, We've just shown you how to prepare Sam coated micro electrodes for MT patterning because the SAM coating prevents micro tubial absorption on the micro electrodes. This procedure can also be used for reversible patterning of microtubules.Furthermore, this process is, is not just limited to microtubules, but can also be used to pattern biomolecules in general. So that's it. Thanks for watching and good luck with your experiments.

antifouling-self-assembled-monolayers-on-microelectrodes-for

Research

JoVE Journal

Biology

Non-fouling PEG silane monolayer was desorbed from individually addressable ITO electrodes on glass by application of a reductive potential.   Electrochemical stripping of PEG-silane layer from ITO microelectrodes allowed for cell adhesion to take place in a spatially defined fashion, with cellular patterns corresponding closely to electrode patterns.

Patterning Cells on Optically Transparent Indium Tin Oxide Electrodes

Self-assembled monolayers (SAMs) formed from long chain alkane thiols on gold provide well-defined substrates for the formation of protein patterns and cell confinement.  Microcontact printing of hexadecanethiol using a polydimethylsiloxane (PDMS) stamp followed by backfilling with a glycol-terminated alkane thiol monomer produces a pattern where protein and cells adsorb only to the stamped hexadecanethiol region.

Creating Two-Dimensional Patterned Substrates for Protein and Cell Confinement

Alkanethiolate stabilized gold colloids known as monolayer protected clusters (MPCs) are synthesized, characterized, and assembled into thin films as an adsorption interface for protein monolayer electrochemistry of simple redox protein like Pseudomonas aeruginosa azurin (AZ) and cytochrome c (cyt c).

Synthesis, Assembly, and Characterization of Monolayer Protected Gold Nanoparticle Films for Protein Monolayer Electrochemistry

This protocol describes a microfabrication-compatible method for cell patterning on SiO2. A predefined parylene-C design is photolithographically printed on SiO2 wafers. Following incubation with serum (or other activation solution) cells adhere specifically to (and grow according to the conformity of) underlying parylene-C, whilst being repulsed by SiO2 regions.

Cell Patterning on Photolithographically Defined 
Parylene-C: SiO2 Substrates

Protocols for single neuron microfluidic arraying and water masking for the in-chip plasma patterning of biomaterial coatings are described. Highly interconnected co-cultures can be prepared using minimal cell inputs.

Preparation of Neuronal Co-cultures with Single Cell Precision

Supported lipid bilayers and natural membrane particles are convenient systems that can approximate the properties of cell membranes and be incorporated in a variety of analytical strategies. Here we demonstrate a method for preparing microarrays composed of supported lipid bilayer-coated SiO2 beads, phospholipid vesicles or natural membrane particles.

Formation of Biomembrane Microarrays with a Squeegee-based Assembly Method

A protocol to couple a large variety of single molecules covalently onto an AFM tip is presented. Procedures and examples to determine the adhesion force and free energy of these molecules on solid supports and bio-interfaces are provided.

Investigating Single Molecule Adhesion by Atomic Force Spectroscopy

Inter-cellular communication is critical for controlling various physiological activities within and outside the cell. This paper describes a protocol for measuring the spatio-temporal nature of single cell secretions. To achieve this, a multidisciplinary approach is used which integrates label-free nanoplasmonic sensing with live cell imaging.

A Label-free Technique for the Spatio-temporal Imaging of Single Cell Secretions

This report describes a simple, easy to perform technique, using low pressure vacuum, to fill microfluidic channels with cells and substrates for biological research.

A Versatile Method of Patterning Proteins and Cells

A bioinspired scaffold is fabricated by a soft photolithography technique using mechanically robust and electrically conductive hydrogels. The micropatterned hydrogels provide directional cardiomyocyte cell alignment, resulting in a tailored direction of actuation. Flexible microelectrodes are also integrated into the scaffold to bring electrical controllability for a self-actuating cardiac tissue.

Bioinspired Soft Robot with Incorporated Microelectrodes

We present a technology that uses capillarity-assisted assembly in a microfluidic platform to pattern micro-sized objects suspended in a liquid, such as bacteria and colloids, into prescribed arrays on a polydimethylsiloxane substrate.

Patterning of Microorganisms and Microparticles through Sequential Capillarity-assisted Assembly

Learn to fabricate antifouling PEG-SAM coated gold microelectrodes on silicon substrates for precise biomolecule patterning. This method enables nanoscale electrophoretic positioning of microtubules while preventing biofouling.

Antifouling Self-assembled Monolayers on Microelectrodes for Patterning Biomolecules