Name: Electrophoretic Crystallization of Ultrathin High-performance Metal-organic Framework Membranes (Video) | JoVE Journal
Uploaded: 2018-08-16T15:00:00.000+00:00
Duration: 7 min 45 s
Description: Learn electrophoretic crystallization for synthesizing ultrathin metal-organic framework membranes using controlled nucleation on copper substrates. This method enables reproducible fabrication of pinhole-free MOF films for gas separation applications.

ai_agent_IP

ai_agent

maintenance

instantTrialDurationMinutes

isBiopharma

enableNewMyJoveSectionDesign

educationFeatures

seoMetaApi

ai_copilot_institution_blacklist

ai_chat_institution_blacklist

freeAccessWindow

ssoRoleCapture

scheduledMaintenanceBanner

joveLabsFeatures

disable_autoplay_for_bots

extended_trial_duration

5 minutes

We acknowledge our home institution, the &#201;cole Polytechnique F&#233;d&#233;rale de Lausanne (EPFL), for its generous support. This project has received funding from the European Union&#39;s Horizon 2020 Research and innovation program under the Marie Sk&#322;odowska-Curie grant agreement No. 665667. The authors thank Pascal Alexander Schouwink for his help with XRD.

CAUTION: Read carefully the material safety data sheets (MSDS) of the chemicals involved. Some of the chemicals used in the experiment are toxic. The present method involves the synthesis of nanoparticles. Therefore, take appropriate precautions. The entire synthesis procedure must be performed in a well-ventilated fume hood.
NOTE: The details of the instruments, the chemicals, and the materials involved in the synthesis of the MOF films are listed in Table 1.
1. Preparation of a Metal Salt Solution and Linker Solution for the Precursor Sol
NOTE: For the synthesis of ZIF-8 film, zinc nitrate hexahydrate [Zn(NO3)2.6H2O] is used as the metal salt and 2-methylimidazole (HmIm) is used as the linker.
<ol>
	<li>For the metal salt solution, dissolve 2.75 g of Zn(NO3)2.6H2O in 500 mL of water.</li>
	<li>For the linker solution, dissolve 56.75 g of HmIm in 500 mL of water and stir it continuously until a clear solution is obtained.</li>
</ol>
2. Preparation of Cu Electrodes
<ol>
	<li>Cut a high purity copper foil (with 99.9% purity, 127 &#181;m-thick) into 4 x 4 cm pieces.</li>
	<li>For the ease of clamping the cut foil to a set of Cu crocodile clips, draw a line at a distance of 0.5 cm from one of the edges of the square foil.</li>
	<li>Flatten the foil using a cylindrical roller on a clean surface.</li>
	<li>Clean the copper foils thoroughly by bath sonication in acetone for 15 min, followed by bath sonication in isopropanol for 15 min.</li>
	<li>Dry the copper foils in a clean atmosphere.</li>
</ol>
3. Attachment of Substrates to the Electrode (Cathode)
NOTE: Chose an appropriate substrate to deposit the MOF film. The method can be applied to AAO (Anodisc, 13 mm-diameter hosting pores with a pore diameter of 0.1 &#181;m), polyacrylonitrile (PAN, molecular weight cut-off: 100 kDa), Cu foil (99.9% purity, 25 &#181;m-thick), a chemical-vapor-deposition-based graphene film resting on a Cu foil11, and a homemade nanoporous carbon film resting on Cu foil12,13,14.
<ol>
	<li>Carefully position the desired substrate on the center of the Cu electrode using a tape.</li>
	<li>Rinse the substrate/electrode assembly with water, followed by isopropanol, and again with water for about 1 min.</li>
	<li>Attach a bare Cu electrode (4 x 4 cm) to the anode. Then attach the substrate/electrode assembly to the cathode.</li>
	<li>Adjust the separation between the two electrodes to 1 cm inside a 100 mL glass beaker.</li>
</ol>
4. The ENACT Procedure for the ZIF-8 Film
<ol>
	<li>Mix 31.6 g of the metal precursor solution and 35 g of the ligand solution in a 100 mL beaker and stir it for 30 s at room temperature to form the precursor sol. 
	NOTE: The induction time of ZIF-8 in these conditions is less than 60 s and, therefore, the EPD has to be carried out without delay.</li>
	<li>Transfer the precursor sol&#160;to the vessel hosting the electrodes.</li>
	<li>Immerse both the electrodes up to the 3.5 cm mark on the electrodes. 
	NOTE: From our experiments, we have observed that applying the electric field before 3 min of sol aging leads to the penetration of the smaller ZIF-8 nuclei into the pores of porous substrates (AAO in this particular case), which needs to be avoided. Therefore, the electric field is turned on only after 3 min, when the nuclei grow somewhat larger.</li>
	<li>Carry out the EPD with a deposition voltage of 1 V for 4 min. The current should be in the range of 2.5 - 3.5 mA.</li>
	<li>At the end of the EPD, lower the beaker slowly. As the adhesion between the freshly deposited nuclei and the substrate is weak, utmost care must be taken while handling the substrate.</li>
	<li>Transfer the dried substrate to a microscopic glass slide. Use tape to hold the substrate in place.</li>
	<li>For crystal growth, mix 31.6 g of the metal salt solution and 35 g of the linker solution in a 100 mL beaker.</li>
	<li>Place the microscopic glass slide along with the substrate vertically in the precursor solution and leave it undisturbed for 10 h at 30 &#176;C.</li>
	<li>After up to 10 h of crystal growth, rinse the substrate with water for 30 min and dry it in a clean atmosphere.</li>
</ol>
5. The ENACT Procedure for the ZIF-7 Film
<ol>
	<li>Synthesize the ZIF-7 film on an AAO support by a method similar to the one used for the ZIF-8 film but with the following differences.</li>
	<li>After mixing 0.82 g of Zn(NO3)2&#183;6H2O in 30 mL of dimethylformamide (DMF) and 0.72 g of benzimidazole in 30 mL of methanol for 3 min, carry out the EPD for 1 min.</li>
	<li>Synthesize an intergrown ZIF-7 film by immersing the ZIF-7 nuclei film in a precursor sol containing 0.58 g of Zn(NO3)2&#183;6H2O, 0.3 g of benzimidazole, and 30 mL of DMF at 110 &#176;C for 4 h.</li>
	<li>After cooling down the solution, wash the ZIF-7/AAO membrane by soaking it in DMF, followed by drying it at 60 &#176;C for 12 h.</li>
</ol>
6. Membrane Preparation and Characterization
<ol>
	<li>Preparation of the membrane
	<ol>
		<li>For the preparation of a sealant, mix thoroughly an equal proportion of the resin and the hardener and leave the mixture for 1 h.</li>
		<li>Place the ZIF-8/support membranes on a 24 mm-wide steel disc with a 5 mm-diameter hole at the center.</li>
		<li>Apply the epoxy along the edges of the substrate at first and, subsequently, cover the substrate except for the 5 mm-diameter hole at the center.</li>
		<li>Allow the epoxy to dry overnight.</li>
		<li>Use a stereo microscope to scan the membrane along with a known reference scale.</li>
		<li>Use graphical software to calculate the exposed area of the membrane from the scanned image.</li>
	</ol>
	</li>
	<li>Gas permeation test 
	NOTE: In our experiments, the single-component gas permeation tests were carried out by the Wicke-Kallenbach technique in a homemade permeation cell. The mass flow controllers (MKS) and mass spectrometer used in the permeation set-up were calibrated within a range of 5% error. Mass flow controllers (MFC) regulated the feed and the sweep gas flow rate. Ar is used as the sweep gas which carried the permeate gas to a calibrated mass spectrometer (MS) for a real-time analysis of the permeate concentration.
	<ol>
		<li>Place the steel disc with the membrane in the stainless-steel permeation cell.</li>
		<li>Ensure a leak-tight fit by placing Viton O-rings above and below the steel disc and fasten the screws. To remove the adsorbed water during the synthesis, dry the membranes at 130 &#176;C under an H2/Ar atmosphere until a steady H2 permeance is reached.</li>
		<li>Place the set-up inside the oven and set the temperature to 130 &#176;C.</li>
		<li>Ensure the feed and the sweep lines are preheated.</li>
		<li>Set the gas flow rates on the feed and the sweep sides to 30 mL/min.</li>
		<li>Maintain a pressure of 0.1 MPa at the feed and the sweep side by adjusting the needle valves on the retentate and the permeate side, respectively.</li>
		<li>Calculate the permeance once a steady state is established.</li>
		<li>Slowly cool down the oven (in about 2 h) to 30 &#176;C and record the values again once a steady state is established.</li>
	</ol>
	</li>
</ol>

<ol><li>Knebel, A., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Defibrillation+of+soft+porous+metal-organic+frameworks+with+electric+fields%5BTitle%5D)+AND+%22Science%22%5BJournal%5D)">Defibrillation of soft porous metal-organic frameworks with electric fields.</a> Science. 358, 347-351 (2017).</li>
<li>Brown, A. J., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Interfacial+microfluidic+processing+of+metal-organic+framework+hollow+fiber+membranes%5BTitle%5D)+AND+%22Science%22%5BJournal%5D)">Interfacial microfluidic processing of metal-organic framework hollow fiber membranes.</a> Science. 345, 72-75 (2014).</li>
<li>Dzubak, A. L., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Ab+initio+carbon+capture+in+open-site+metal-organic+frameworks%5BTitle%5D)+AND+%22Nature+Chemistry%22%5BJournal%5D)">Ab initio carbon capture in open-site metal-organic frameworks.</a> Nature Chemistry. 4, 810-816 (2012).</li>
<li>Gascon, J., Kapteijn, F. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Metal-organic+framework+membranes-high+potential%2C+bright+future%5BTitle%5D)+AND+%22Angewandte+Chemie+International+Edition%22%5BJournal%5D)">Metal-organic framework membranes-high potential, bright future.</a> Angewandte Chemie International Edition. 49, 1530-1532 (2010).</li>
<li>Liu, X., Wang, C., Wang, B., Li, K. <a target="_blank" href="https://onlinelibrary.wiley.com/doi/full/10.1002/adfm.201604311">Novel Organic-Dehydration Membranes Prepared from Zirconium Metal-Organic Frameworks.</a> Advanced Functional Materials. 27, 1-6 (2017).</li>
<li>Zhang, F., et al. <a target="_blank" href="https://onlinelibrary.wiley.com/doi/abs/10.1002/adfm.201200084">Hydrogen selective NH2-MIL-53(Al) MOF membranes with high permeability.</a> Advanced Functional Materials. 22, 3583-3590 (2012).</li>
<li>Kwon, H. T., Jeong, H. -K. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((In+situ+synthesis+of+thin+zeolitic-imidazolate+framework+ZIF-8+membranes+exhibiting+exceptionally+high+propylene%2Fpropane+separation%5BTitle%5D)+AND+%22Journal+of+the+American+Chemical+Society%22%5BJournal%5D)">In situ synthesis of thin zeolitic-imidazolate framework ZIF-8 membranes exhibiting exceptionally high propylene/propane separation.</a> Journal of the American Chemical Society. 135, 10763-10768 (2013).</li>
<li>Hou, J., Sutrisna, P. D., Zhang, Y., Chen, V. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Formation+of+ultrathin%2C+continuous+metal-organic+framework+membranes+on+flexible+polymer+substrates%5BTitle%5D)+AND+%22Angewandte+Chemie+International+Edition%22%5BJournal%5D)">Formation of ultrathin, continuous metal-organic framework membranes on flexible polymer substrates.</a> Angewandte Chemie International Edition. 55, 3947-3951 (2016).</li>
<li>Barankova, E., Tan, X., Villalobos, L. F., Litwiller, E., Peinemann, K. V. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((A+metal+chelating+porous+polymeric+support%3A+the+missing+link+for+a+defect-free+metal-organic+framework+composite+membrane%5BTitle%5D)+AND+%22Angewandte+Chemie+International+Edition%22%5BJournal%5D)">A metal chelating porous polymeric support: the missing link for a defect-free metal-organic framework composite membrane.</a> Angewandte Chemie International Edition. 56, 2965-2968 (2017).</li>
<li>He, G., Dakhchoune, M., Zhao, J., Huang, S., Agrawal, K. V. <a target="_blank" href="https://onlinelibrary.wiley.com/doi/full/10.1002/adfm.201707427">Electrophoretic Nuclei Assembly for Crystallization of High-Performance Membranes on Unmodified Supports.</a> Advanced Functional Materials. , In press (2018).</li>
<li>Li, X., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Large-area+synthesis+of+high-quality+and+uniform+graphene+films+on+copper+foils%5BTitle%5D)+AND+%22Science%22%5BJournal%5D)">Large-area synthesis of high-quality and uniform graphene films on copper foils.</a> Science. 324, 1312-1314 (2009).</li>
<li>Rodriguez, A. T., Li, X., Wang, J., Steen, W. A., Fan, H. <a target="_blank" href="https://onlinelibrary.wiley.com/doi/abs/10.1002/adfm.200600952">Facile synthesis of nanostructured carbon through self-assembly between block copolymers and carbohydrates.</a> Advanced Functional Materials. 17, 2710-2716 (2007).</li>
<li>Huang, S., et al. Large-area single-layer graphene membranes by crack-free transfer for gas mixture separation. Nature Communications. , Accepted (2018).</li>
<li>Agrawal, K. V., Dakachoune, M., Huang, S., He, G., Dudani, N. Ultrahigh flux gas-selective nanoporous carbon membrane and manufacturing method thereof. , Patent. Application PCT/EP2017/057684 (2017).</li>
<li>Liu, J., Wöll, C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Surface-supported+metal-organic+framework+thin+films%3A+fabrication+methods%2C+applications%2C+and+challenges%5BTitle%5D)+AND+%22Chemical+Society+Reviews%22%5BJournal%5D)">Surface-supported metal-organic framework thin films: fabrication methods, applications, and challenges.</a> Chemical Society Reviews. 46, 5730-5770 (2017).</li>
</ol>

The authors have nothing to disclose.

The standout feature of the ENACT method with respect to the existing methods15 is that the ENACT method enables the synthesis of highly intergrown, ultrathin MOF films on a wide range of porous and nonporous substrates. Any substrate pretreatment is avoided, making this method quite straightforward for the synthesis of MOF films. Although EPD equipment has to be used for the deposition of a nuclei film, the equipment is composed of a power source, a metal electrode, and a beaker, which is quite s...

Thin molecular sieving membranes offer a high-energy efficiency in the separation of molecules and can reduce the overall cost of fuels, CO2 capture, water purification, solvent recovery, etc.1,2. MOFs are a promising class of material for the synthesis of molecular sieving membranes because of the involved isoreticular synthetic chemistry and relatively straightforward crystallization3. To date, MOF membranes comprising of diverse crystalline structures, including that of ZIF-4, -7, -8, -9, -11, -67, -90, and -93, and UiO-66, HKUST-1, and MIL-53 have been reported4,5. These membranes are synthesized by crystallizing high-quality polycrystalline MOF films on a porous support. Generally, to obtain a high separation selectivity, it is necessary to reduce the defects in the polycrystalline MOF film (such as pinholes and grain-boundary defects). A convenient approach to reduce the defects is to crystallize a thick film. Not surprisingly, several of the earlier reported on MOF membranes are extremely thick (over 5 µm). Unfortunately, thick films lead to a long diffusion path, which limits the membrane permeance. Therefore, while selectivity is improved, permeance is sacrificed. To circumvent this trade-off, it is imperative to develop methods to crystallize ultrathin (&lt; 0.5 µm-thick), defect-free MOF films.
ZIF-8 is the most intensively studied MOF for membrane synthesis, due to its exceptional chemical and thermal stability and a simple crystallization chemistry6,7. So far, the reported ultrathin ZIF-8 membranes have been realized by changing the surface chemistry or topology of the underlying porous substrate, favoring the heterogeneous nucleation of ZIF-8, which is essential for an intergrown polycrystalline film. For instance, Chen et al. reported the synthesis of 1 µm-thick ZIF-8 film on (3-aminopropyl)triethoxysilane-modified TiO2-coated poly(vinylidene fluoride) (PVDF) hollow fibres8. They observed a high heterogeneous nucleation density and attributed it to the simultaneous modification of the surface chemistry and nanostructure. The Peinemann group reported an ultrathin ZIF-8 membrane on a metal-chelating, polythiosemicarbazide (PTSC) support9. This unique metal-chelating capability of PTSC led to the binding of zinc ions, promoting the heterogeneous nucleation of ZIF-8 which, subsequently, led to high-performance ZIF-8 membranes. In general, tuning the substrate chemistry and nanostructure facilitates the synthesis of high-performance MOF membranes; however, these methods are quite complex, and usually cannot be reapplied to synthesize MOF membranes from other attractive MOF structures.
Herein, we report the synthesis of ultrathin, highly intergrown ZIF-8 films using a simple and versatile crystallization approach that can be reapplied to form a thin intergrown film of several crystalline materials10. We show examples of ZIF-8 and ZIF-7 films prepared without any substrate pretreatment, which greatly simplifies the preparation process. The ZIF-8 films are prepared on a wide range of substrates (ceramic, polymer, metal, carbon, and graphene). The 500 nm-thick ZIF-8 film on an anodic aluminum oxide (AAO) support displays an attractive separation performance. A high H2 permeance of 8.3 x 10-6 mol m-2 s-1 Pa-1 and attractive ideal selectivities of 7.3 (H2/CO2), 15.5 (H2/N2), 16.2 (H2/CH4), and 2655 (H2/C3H8) are achieved.
The crystallization approach that enables the above-mentioned feat is ENACT. ENACT deposits ZIF-8 nuclei onto a substrate directly from the crystal's precursor sol. The approach utilizes EPD for a very short period of time (1 - 4 min) right after the induction time (the time when the nuclei appear in the precursor sol). The application of an electric field to the charged MOF nuclei drives them toward an electrode with a flux that is proportional to the strength of the applied electric field (E), the electrophoretic mobility of the colloid (μ), and the concentration of nuclei (Cn) as shown in the Equations 1 and 2.
<img alt="Nuclei flux formula, symbol: Φ ∝ EμC_n, theoretical model in a scientific diagram." src="/files/ftp_upload/58301/58301eq1.jpg" data-altupdatedat="1788250015000" data-alt="Equation 1"> 
(Equation 1)
<img alt="Electrophoresis mobility equation; μ=v/E=ε₀εᵣζ/η; equation; electrokinetic analysis." src="/files/ftp_upload/58301/58301eq2.jpg" data-altupdatedat="1788250015000" data-alt="Equation 2"> 
(Equation 2)
Here, 
v = the drift velocity, 
ζ = the zeta potential of the nuclei, 
εo = the permittivity of vacuum, 
εr = the dielectric constant, and 
η = the viscosity of the precursor sol.
Therefore, by controlling E and the solution pH (which determines ζ ), the packing density of nuclei can be controlled. The subsequent growth of the densely-packed nuclei in the precursor sol allows researchers to obtain a highly intergrown polycrystalline film.

<table><tbody><tr><td>Zinc nitrate hexahydrate</td><td>Sigma-Aldrich</td><td>96482-500G</td><td>98% purity</td></tr><tr><td>2-Methylimidazole</td><td>Sigma-Aldrich</td><td>M50850-500G</td><td>99% purity</td></tr><tr><td>Benzimidazole</td><td>TCI</td><td>B0054-500G</td><td>98% purity</td></tr><tr><td>Tape</td><td>DuPont</td><td>KPT-1/8</td><td></td></tr><tr><td>Epoxy</td><td>GC Electronics</td><td>19-823</td><td></td></tr><tr><td>Copper foil</td><td>Alfa Aesar</td><td>13380.CV</td><td>99.9% purity</td></tr><tr><td>Power source for EPD</td><td>Gamry Instruments</td><td>Interface 1000E Potentiostat</td><td></td></tr><tr><td>Ultrasonic cleaner</td><td>MTI corporation</td><td>VGT-1860QTD</td><td></td></tr><tr><td>AAO</td><td>GE Healthcare Life Sciences&amp;lrm;</td><td>6809-7013</td><td></td></tr><tr><td>PAN</td><td>Shandong MegaVision</td><td></td><td>The molecular weight cut-off is 100 kDa</td></tr></tbody></table>

electrophoretic crystallization of ultrathin high-performance metal-organic framework membranes

Electrophoretic Crystallization of Ultrathin High-performance Metal-organic Framework Membranes

We report the synthesis of thin, highly intergrown, polycrystalline metal-organic framework (MOF) membranes on a wide range of unmodified porous and non-porous supports (polymer, ceramic, metal, carbon, and graphene). We developed a novel crystallization technique, which is termed the ENACT approach: the electrophoretic nuclei assembly for the crystallization of highly intergrown thin films (ENACT). This approach allows for a high density of heterogeneous nucleation of MOFs on a chosen substrate via the electrophoretic deposition (EPD) directly from the precursor sol. The growth of well-packed MOF nuclei leads to a highly intergrown polycrystalline MOF film. We show that this simple approach can be used for the synthesis of thin, intergrown zeolite imidazole framework (ZIF)-7 and ZIF-8 films. The resulting 500 nm-thick ZIF-8 membranes show a considerably high H2 permeance (8.3 x 10-6 mol m-2 s-1 Pa-1) and ideal gas selectivities (7.3 for H2/CO2, 15.5 for H2/N2, 16.2 for H2/CH4, and 2655 for H2/C3H8). An attractive performance for C3H6/C3H8 separation is also achieved (a C3H6 permeance of 9.9 x 10-8 mol m-2 s-1 Pa-1 and a C3H6/C3H8 ideal selectivity of 31.6 at 25 &#176;C). Overall, the ENACT process, owing to its simplicity, can be extended to synthesize intergrown thin films of a wide range of nanoporous crystalline materials.

A homemade EPD set-up was used to synthesize the MOF films (Figure 1). Scanning electron microscopy (SEM) images and X-ray diffraction (XRD) patterns were collected for the ZIF-8 nuclei film (Figure 2). SEM was used to image the surface and cross-sectional morphologies of the AAO support, ZIF-8/AAO membrane, PAN support, ZIF-8/PAN membrane, ZIF-8/graphene film, and ZIF-7/AAO membrane (Figure 3). The ...

A simple, reproducible, and versatile approach for the synthesis of intergrown, polycrystalline metal-organic framework membranes on a wide range of unmodified porous and non-porous supports is presented.

We report the synthesis of thin, highly intergrown, polycrystalline metal-organic framework (MOF) membranes on a wide range of unmodified porous and ...

electrophoretic-crystallization-ultrathin-high-performance-metal

Research

JoVE Journal

Chemistry

Herein is described the procedure implemented in the Caffrey Membrane Structural and Functional Biology Group to set up manually crystallization trials of membrane proteins in lipidic mesophases.

Crystallizing Membrane Proteins for Structure Determination using Lipidic Mesophases

Evaluating two-dimensional (2D) crystallization trials for the formation of ordered membrane protein arrays is a highly critical and difficult task in electron crystallography.  Here we describe our approach in screening for and identifying 2D crystals of predominantly small membrane proteins in the range of 15 – 90kDa.

Assessing Two-dimensional Crystallization Trials of Small Membrane Proteins for Structural Biology Studies by Electron Crystallography

The protocols describe the essential steps for obtaining diffraction quality crystals of a membrane protein starting from reconstitution of the protein in a lipidic cubic phase (LCP), finding initial conditions with LCP-FRAP pre-crystallization assays, setting up LCP crystallization trials and harvesting crystals.

Crystallization of Membrane Proteins in Lipidic Mesophases

Bicelles are lipid/amphiphile mixtures that maintain membrane proteins (MPs) within a lipid bilayer but have unique phase behavior that facilitates high-throughput screening by crystallization robots. This technique has successfully produced a number of high-resolution structures from both prokaryotic and eukaryotic sources. This video describes protocols for generating the lipidic bicelle mixture, incorporating MPs into the bicelle mixture, setting up crystallizations trials (manually as well...

High-throughput Crystallization of Membrane Proteins Using the Lipidic Bicelle Method

Herein the procedures for plasma enhanced chemical vapor deposition of perfluoroalkanes on microporous materials such as metal-organic frameworks to enhance their stability and hydrophobicity are described. Furthermore, breakthrough testing of milligram quantities of samples is described in detail.

Preparation of Hydrophobic Metal-Organic Frameworks via Plasma Enhanced Chemical Vapor Deposition of Perfluoroalkanes for the Removal of Ammonia

Synthesis, activation, and characterization of intentionally designed metal-organic framework materials is challenging, especially when building blocks are incompatible or unwanted polymorphs are thermodynamically favored over desired forms. We describe how applications of solvent-assisted linker exchange, powder X-ray diffraction in capillaries and activation via supercritical CO2 drying, can address some of these challenges.

Synthesis and Characterization of Functionalized Metal-organic Frameworks

A procedure for the preparation of porous hybrid separation media composed of a macroporous polymer monolith internally coated by a high surface area microporous coordination polymer is presented.

Preparation of Highly Porous Coordination Polymer Coatings on Macroporous Polymer Monoliths for Enhanced Enrichment of Phosphopeptides

In this paper we describe the interfacial synthesis of conjugated microporous polymers (CMP) on sacrificial substrates, and the dissolution of the substrate for the preparation of freestanding CMP nanomembranes. In addition, we will describe how the fragile nanomembranes can be transferred to other substrates.

Layer-by-layer Synthesis and Transfer of Freestanding Conjugated Microporous Polymer Nanomembranes

A protocol for the synthesis and characterization of self-assembled metal-organic framework monolayers is provided using polymer-grafted, metal-organic framework (MOF) crystals. The procedure shows that polymer-grafted MOF particles can be self-assembled at an air-water interface resulting in well-formed, free-standing, monolayer structures as evidenced by scanning electron microscopy imaging.

Synthesis and Characterization of Self-Assembled Metal-Organic Framework Monolayers Using Polymer-Coated Particles

This protocol describes a reproducible methodology for the fabrication of sustainable metal-organic framework/polymer mixed-matrix membranes and accurate measurement of their in-plane proton conductivity under variable temperature and humidity using electrochemical impedance spectroscopy, which can be useful for proton exchange membrane fuel cells (PEMFCs).

Measuring Proton Conductivity in MOF-Based Mixed Matrix Membranes by Electrochemical Impedance Spectroscopy

Learn electrophoretic crystallization for synthesizing ultrathin metal-organic framework membranes using controlled nucleation on copper substrates. This method enables reproducible fabrication of pinhole-free MOF films for gas separation applications.

Electrophoretic Crystallization of Ultrathin High-performance Metal-organic Framework Membranes

Explore More Videos