Name: In Vitro Evaluation of The Effects Of Er,Cr:YSGG and Diode Lasers Used on Titanium Cylinder (Video) | JoVE Journal
Uploaded: 2025-06-06T13:55:00.000+00:00
Duration: 7 min 5 s
Description: Explore laser effects on titanium surfaces for periimplantitis treatment using Er,Cr:YSGG and diode lasers. This method evaluates temperature changes and surface roughness through SEM, AFM, and profilometry analysis.

ai_agent_IP

ai_agent

maintenance

instantTrialDurationMinutes

isBiopharma

enableNewMyJoveSectionDesign

educationFeatures

seoMetaApi

ai_copilot_institution_blacklist

ai_chat_institution_blacklist

freeAccessWindow

ssoRoleCapture

scheduledMaintenanceBanner

joveLabsFeatures

disable_autoplay_for_bots

extended_trial_duration

5 minutes

The titanium cylinders used in the study were produced by Naxis Implant.

NOTE: Titanium cylinders, crafted from the same material as conventional implants and designed to replicate the implant surface with SLA technology, feature a height of 10 mm and a diameter of 5 mm. A cavity measuring 7mm in depth and 3mm in width is located at the center of the cylinders (Fig. 2). The width of 3mm reduces to 1mm at the deepest point. Measuring the surface roughness of standard implants with a profilometer is not feasible. It was possible to assess the effectiveness of the laser applied to a 5 mm diameter flat surface at the top of the titanium cylinder designed by the manufacturer, utilizing the same material that simulates the implant surface. Additionally, in order to measure temperature changes from the center of the cylinder, a groove 7 mm deep and 3 mm wide has been created from the center of the bottom surface of the titanium cylinder towards the depths of the cylinder, where the thermocouple tip will be placed. This groove allows for the evaluation of the temperature change of the treated surface from within the cylinder, rather than dependent on the outer surface. Three-dimensional visuals were obtained by analyzing the flat surfaces of specially produced titanium cylinders using an Atomic Force Microscope (AFM). A 940 nm diode (0.8 W28, 1.3 W29, 1.8 W30) and 2.780 nm Er,Cr:YSGG (1.5 W31, 2.5 W31, 3.5 W32) lasers were used at three different wattages according to company recommendations, and 12 groups were formed with 20 s and 40 s application time each. After the application, a control group was added for roughness evaluation. A stand with a finger support was printed from a three-dimensional printer to keep the Ti cylinder stable during the application (Table of Materials).
1.Sample size
<ol>
	<li>Calculate sample size using the Power analysis of the G*Power program. The minimum number of samples for each group was determined as n=8 samples for temperature change with effect size d: 0.6906, standard deviation 16.8, Power: 0.80, and α: 0.05. 
	​NOTE: In this study, an Er,Cr:YSGG laser equipped with a 940 nm diode laser with a 300 µm diameter tip (e3 tip) and a 360° firing elastic RFPT5-14 tip (580 µm diameter and 14 mm long) was used as the laser system (Figure 1).</li>
</ol>
<img alt="Dental laser equipment and accessories; includes diode laser unit, fiber optic tips." class="xfigimg" src="/files/ftp_upload/67955/67955fig01.jpg" data-altupdatedat="1762425657000" data-alt="Figure 1"> 
Figure 1: Instruments and equipment used. (A) Diode laser, (B) Er,Cr:YSGG laser, (C) E3 tip, (D) RPTF5-14 tip. <a href="https://www.jove.com/files/ftp_upload/67955/67955fig01large.jpg" target="_blank">Please click here to view a larger version of this figure.</a>
2. Determination of working groups
<ol>
	<li>Take the recommended Watt of lasers for in-pocket application in peri-implant mucositis as the ideal condition of use. Additionally, include one lower value and one higher value in the study groups relative to the recommended Watt. The values used here are 1.5 W and 3.5 W for Er,Cr:YSGG, and 0.8 W and 1.8 W for the diode laser.</li>
	<li>Determine application time as 20 s and 40 s to evaluate the effect of operating time on temperature change. Study groups are shown in Table 1.</li>
</ol>
<table border="1" fo:keep-together.within-page="1" fo:keep-with-next.within-page="always">
	<tbody>
		<tr>
			<td>Group Name</td>
			<td>Laser Type</td>
			<td>Number of Samples (n)</td>
			<td>Watt (W)</td>
			<td>Time (s)</td>
		</tr>
		<tr>
			<td>E1</td>
			<td>Er,Cr:YSGG</td>
			<td>8</td>
			<td>1.5 W</td>
			<td>20</td>
		</tr>
		<tr>
			<td>E2</td>
			<td></td>
			<td>8</td>
			<td>2.5 W</td>
			<td>20</td>
		</tr>
		<tr>
			<td>E3</td>
			<td></td>
			<td>8</td>
			<td>3.5 W</td>
			<td>20</td>
		</tr>
		<tr>
			<td>E4</td>
			<td></td>
			<td>8</td>
			<td>1.5 W</td>
			<td>40</td>
		</tr>
		<tr>
			<td>E5</td>
			<td></td>
			<td>8</td>
			<td>2.5 W</td>
			<td>40</td>
		</tr>
		<tr>
			<td>E6</td>
			<td></td>
			<td>8</td>
			<td>3.5 W</td>
			<td>40</td>
		</tr>
		<tr>
			<td>D1</td>
			<td>Diode</td>
			<td>8</td>
			<td>0.8 W</td>
			<td>20</td>
		</tr>
		<tr>
			<td>D2</td>
			<td></td>
			<td>8</td>
			<td>1.3 W</td>
			<td>20</td>
		</tr>
		<tr>
			<td>D3</td>
			<td></td>
			<td>8</td>
			<td>1.8 W</td>
			<td>20</td>
		</tr>
		<tr>
			<td>D4</td>
			<td></td>
			<td>8</td>
			<td>0.8 W</td>
			<td>40</td>
		</tr>
		<tr>
			<td>D5</td>
			<td></td>
			<td>8</td>
			<td>1.3 W</td>
			<td>40</td>
		</tr>
		<tr>
			<td>D6</td>
			<td></td>
			<td>8</td>
			<td>1.8 W</td>
			<td>40</td>
		</tr>
		<tr>
			<td>C</td>
			<td>Control</td>
			<td>8</td>
			<td></td>
			<td></td>
		</tr>
	</tbody>
</table>
Table 1: Study groups information.
3. Preparation of experimental setup
<ol>
	<li>With the Rhinoceros (3D graphics and design) program, design a cylinder stand in 3D with a cavity slightly with a diameter of 10 mm and a thickness of 5 mm.
	<ol>
		<li>Open the app. Draw a circle 10 mm in diameter. Reduce the circle by 50% from one axis to create an ellipse. Press Extuder and raise the ellipse in the third dimension.</li>
		<li>Draw a circle again for finger support. Raise the second circle in the third dimension with the extruder key. Make the height less than the first circle.</li>
		<li>Drill a 10 mm hole in the elliptical drawing with the Boolean command. For thermocouple support, make an L-shaped line with the Sweep 1 command and create the 3rd dimension.</li>
		<li>Draw a square, enlarge it in the 3rd dimension with the extruder command, and create the base. After printing the design, apply silicone around the hole where the Ti cylinder will come and dry it. This will keep the cylinder in place while the laser is being applied.</li>
	</ol>
	</li>
	<li>Bring a closed room with air conditioning to a temperature of 27 °C. Fix the stand on which the cylinders will be fixed in the middle of a plastic tub with double-sided tape. 
	NOTE: Insert Ti Cylinder, squeeze air onto the surface.</li>
	<li>Place the thermocouple of the thermometer in the hollow part of the Ti cylinder placed in its slot on the stand.</li>
	<li>Prepare a chronometer to keep track of the application time. Record the degrees by the 3rd observer and keep track of the time with stopwatch.</li>
</ol>
4. Experimental procedure
<ol>
	<li>During laser application, wear protective glasses for practitioner safety.Insert RPTF5-14 tip for Er,Cr:YSGG laser. Insert tip E3 for diode laser.</li>
	<li>Turn on the Er,Cr:YSGG laser.Select Perio Closed Mode. Apply 1.5 W, 2.5 W and 3.5 W lasers for 20 s and 40 s each. There are 96 Ti cylinders with laser applied. Irradiate a Ti cylinder with only one laser type, one watt and one time.</li>
	<li>Turn on the diode laser. Select Perio Pocket Mode. Apply 0.8 W, 1.3 W and 1.8 W laser for 20 s and 40 s each.</li>
	<li>Have the 3rd observer start the timer when the laser starts. Warn him/her when the time is up.</li>
	<li>Apply the laser tip at a 15° angle to the surface, in contact, zigzagging over the entire surface for the planned time.</li>
	<li>Note the initial and final temperature values during the application. Subtract the start temperature value from the end temperature value. Calculate the temperature change. 
	NOTE: Note the temperature change values for a total of 12 groups, 6 Er,Cr:YSGG, and 6 Diode laser groups.</li>
	<li>Keep samples in transparent bags with group numbers written on them.</li>
</ol>
5.Two and Three-dimensional imaging of materials
<ol>
	<li>Perform scanning electron microscope (SEM) and atomic force microscope (AFM) analyses to evaluate and demonstrate changes in the morphology of the Ti cylinder surface. 
	NOTE: FEI Quanta FEG 250 instrument was used.</li>
	<li>Do not coat samples before being placed in the SEM. There are 13 groups, including 1 control group, 6 diode laser groups, and 6 Er,Cr: YSGG laser groups. For the control group, perform no treatment, only take surface images by AFM and SEM.</li>
	<li>Randomly select one cylinder from each of the 13 study groups. Insert them into the SEM device.Note the location on the platform and the sample code to avoid mixing samples.</li>
	<li>Place the Ti cylinder in the SEM device with the flat surface upwards. Perform analyses using Low vacuum mode. Set the chamber pressure to 60 Pa during analysis.</li>
	<li>Once the device is fully ready, record images at 250x, 1000x, and 5000x magnification from a random point on the flat surface.Repeat this procedure for all samples. 
	NOTE: When the SEM device finishes vacuuming, it is ready for image collection.</li>
	<li>For AFM measurement, randomly select one Ti cylinder from each study group. Perform measurement in tapping mode.
	<ol>
		<li>Place the Ti cylinder in the AFM instrument. Place the top cover so that the tip of the instrument is over the sample. Check that the red light from the window on the instrument is on the surface to be imaged.</li>
		<li>Set the voltage to 2. Move the tip closer to the sample with the Auto land button. Start the scan by pressing the Start Scan button.</li>
	</ol>
	</li>
	<li>Take a 5 µm x 5 µm digital image for each sample and record at a slow scan rate (1 Hz). Record images taken with the AFM instrument from the flat surfaces of Ti cylinders. AFM instrument visualizes 25 µm2 area.</li>
</ol>
6. Measurement of surface roughness
NOTE: The Surftest SJ 201, Mitutoyo, Tokyo, Japan, device was used here.
<ol>
	<li>Set the resolution of the profilometer to 0.01 mm, the transverse length to 3.0 mm and the diameter of the diamond recording pin tip to 5 µm. Set the measurement speed to 0.5 mm/s to determine the Ra value.</li>
	<li>Fix the Ti cylinder with a holder, use the presel, and fix the Ti cylinder by holding it from the side surface. Place the needle of the profilometer in contact with the Ti surface.</li>
	<li>Press the Start button. Save the Ra value found. Repeat the measurement 5x in different directions on the flat surface of each cylinder (Figure 2). To achieve the various directions, move the Ti cylinder around itself with the help of a presell. Repeat for the entire length of the Ti cylinder.</li>
</ol>
<img alt="Device setup, laser application, analysis stages; SEM, AFM, profilometer analysis; scientific diagram." class="xfigimg" src="/files/ftp_upload/67955/67955fig2v2.jpg" data-altupdatedat="1762425657000" data-alt="Figure 2"> 
Figure 2: Flowchart of study groups. (1A) Ti cylinder side view, (1B) top view, (1C) bottom view <a href="https://www.jove.com/files/ftp_upload/67955/67955fig2v2large.jpg" target="_blank">Please click here to view a larger version of this figure.</a>
7. Statistical analysis
<ol>
	<li>Perform statistical analysis using the SPSS-Windows statistical package program and apply the Kruskal-Wallis and Mann-Whitney tests. Set statistical confidence level at 95% (α = 0.05).</li>
</ol>

The authors have no conflicts of interest to disclose.

A significant discussion is underway over the optimal method for decontaminating implant surfaces in the treatment of peri-implantitis. Previous publication has proposed the utilization of local or systemic medicines, laser application, mechanical and/or chemical cleaning, and implantoplasty. Our study findings revealed that all measured temperatures rise under the critical safety threshold of 10 &#176;C13. However, keeping in mind that this is an in vitro study and cannot always replicat...

Dental implants are a commonly accepted treatment option for the replacement of lost teeth1,2. Peri-implant mucositis and peri-implantitis are classified as peri-implant diseases. Peri-implant mucositis is restricted to soft tissues, and there is no evidence of bone loss, with the exception of physiological bone remodeling. Peri-implantitis is a pathological condition that is associated with plaque and affects the tissues surrounding dental implants. It is distinguished by the inflammation of the peri-implant mucosa and the consequent increasing loss of supporting bone3. The primary etiological factor for the initiation and progression of the disorder is disruption of the peri-implant plaque biofilm4. Numerous studies on peri-implant illnesses indicate that the prevalence of peri-implant mucositis (PIM) ranges from 9.7% to 64.6%, while the prevalence of peri-implantitis (P) varies between 4.7% and 45%5.
While plaque accumulation is the main etiological factor that causes peri-implantitis, its treatment is complicated by the diverse topographical characteristics of implants. The foundation of nonsurgical peri-implantitis treatment is infection management through the debridement of the implant surface and the elimination of adhering biofilm to decrease bacterial load below the disease-causing threshold6,7. The complex micro and macro-topography of titanium interfaces and bone defect anatomy limits surface decontamination. The efficacy of different mechanical (curettes, ultrasonic devices, air-powder abrasion, titanium brushes), chemical (citric acid, chlorhexidine, antimicrobials), and physical (laser, photodynamic therapy) decontamination techniques have been assessed in combination8. Current research suggests that the combined use of non-surgical intervention techniques for peri-implantitis is more effective than debridement alone9. The incorporation of chemical antimicrobial agents or local/systemic antibiotics into mechanical therapy has demonstrated significant efficacy; nevertheless, these interventions could result in possible adverse consequences10. As laser technology has advanced, dental lasers have become increasingly popular because of their anti-infective, detoxifying, and user-friendly effects on implant surfaces10,11.
The absorption peak, operational mode of the device, and tissue properties affect the heat increase during laser irradiation. A crucial pre-clinical investigation revealed that an elevation in temperature to 50 &#176;C for 1 min caused vascular damage, whereas a rise to 60 &#176;C led to the cessation of blood flow and subsequent bone necrosis12. An in vitro investigation found that after just 10 s of diode laser irradiation, implant surfaces could reach temperatures higher than the bone safety threshold (10 &#176;C). Bone viability could be compromised by a temperature increase of just 10 &#176;C13.
Numerous recent studies have concentrated on examining the beneficial impact of lasers in this domain14,15,16,17,18. Various laser wavelengths demonstrate a significant antibacterial impact and safety on implant surfaces when appropriate parameters are applied. A number of variables, including intensity, frequency, and wavelength, influence the efficacy of laser treatments. Several studies have demonstrated the bactericidal effect of various laser wavelengths, including CO2, Er:YAG, Er,Cr:YSGG and various diode lasers, which allows us to identify the beneficial effects of different lasers in the treatment of peri-implantitis. Aoki et al19,20,21. concluded from their review that laser application facilitates surface cleaning in both non-surgical and surgical peri-implant treatments, including regenerative therapy, and promotes healing by activating surrounding tissue cells22.
Diode lasers have the ability to exert a bactericidal effect on implant surfaces without affecting the implant&#39;s surface pattern. When it comes to treating peri-implantitis, the diode laser may be the way to go because it promotes the healing of periodontal tissues23,24,25.
Erbium, chromium-doped: yttrium, scandium, gallium, garnet (Er,Cr:YSGG) lasers exhibit effective properties for the elimination of biofilm and the decontamination of implant surfaces11.&#160;Strong bactericidal effects and bone regeneration properties were demonstrated by erbium lasers without causing mechanical damage thanks to their water-powered properties11,14.
There is a shortage of data regarding the alterations caused by laser irradiation on titanium implants. Moreover, a definitive methodology for the irradiation of titanium surfaces has yet to be defined, encompassing laser parameters such as power and time of application. Previous studies showed that Er,Cr:YSGG laser16&#160;application had no effect on temperature change, however, diode laser studies exceeded13&#160;and did not exceed16,26&#160;the critical value. Different results of the effect of laser treatment on the Ra value of the titanium surface are available in the literature18,27. The null hypothesis of the study is that there will be no difference between Er,Cr:YSGG lasers, and diode lasers in terms of temperature and roughness change of titanium surfaces by using. This study aimed to determine safe operating parameters by monitoring surface roughness and temperature variations on titanium material using Er,Cr:YSGG, and diode lasers at various time and power settings. The evaluation of temperature change was conducted with a thermocouple, surface roughness was assessed using a profilometer, and surface alterations were analyzed through SEM and AFM techniques.

<table><tbody><tr><td>Atomic Force Microscopy</td><td>ezAFM</td><td></td><td>Compact AFM Model</td></tr><tr><td>Diode</td><td>Biolase</td><td></td><td>Epic 10, 940 nm Wavelength</td></tr><tr><td>E3 Tip</td><td></td><td></td><td>Fiber Diameter: 300 &amp;micro;m, Fiber Length: 9 mm</td></tr><tr><td>Er,Cr:YSGG Laser</td><td>Iplus</td><td></td><td>2780 nm Wavelength</td></tr><tr><td>Profilometer</td><td>Mitutoyo</td><td></td><td>Surftest SJ-201 Model</td></tr><tr><td>RFPT-14 Tip</td><td></td><td></td><td>Outer Tip Diameter: 580 &amp;micro;m, Tip Length: 14 mm</td></tr><tr><td>Scanning Electron Microscope</td><td>FEI</td><td></td><td>Quanta FEG 250 Model</td></tr><tr><td>Stand</td><td>Custom Design</td><td></td><td>Rhinoceros application, Flamix PLA filament, Bambulab X1C Device</td></tr><tr><td>Thermometer</td><td>Keithley</td><td></td><td>2000 Series Model, K tip termokulp</td></tr><tr><td>Titanium Cylinder</td><td>Naxis</td><td></td><td>10 mm height, 5 mm diameter, SLA Surface, Titanium</td></tr></tbody></table>

in vitro evaluation of the effects of er,cr:ysgg and diode lasers used on titanium cylinder

In Vitro Evaluation of The Effects Of Er,Cr:YSGG and Diode Lasers Used on Titanium Cylinder

Peri-implant diseases are significant issues associated with dental implants. The aim of this study was to evaluate the surface roughness and temperature changes when diode and Erbium, Chromium-doped Yttrium-Scandium-Gallium-Garnet&#160;(Er,Cr:YSGG) lasers are applied on titanium cylinders in the treatment of non-surgical peri-implant diseases.A total of 13 groups, including the control group, were formed with 940 nm diode (0.8 W-1.3 W-1.8 W) and Er,Cr:YSGG (1.5 W-2.5 W-3.5 W) lasers in 6 different power modes, 20s/W and 40 s/W, and eight titanium cylinders were treated in each group. During the process, the initial and final temperatures were recorded with a thermocouple placed in the apical slot of the cylinder. After the application, the roughness (Ra) of all disks was measured by a profilometer. The surfaces were scanned by scanning electron microscope (SEM) and atomic force microscope (AFM) for two- and three-dimensional surface examination.When the temperature changes of the titanium cylinders during irradiation were evaluated, the cylinders irradiated with a diode laser for 40 s were significantly higher than those irradiated for 20 s. In the Er,Cr:YSGG treated cylinders, the temperature decreased in some samples and increased minimally in some samples. Profilometer values (Ra) were not statistically significant in terms of roughness for all groups. However, SEM images showed melting and an increase in the number of micropores on the treated surfaces.With the limitations of this in vitro study, the application of the Er,Cr:YSGG, and the diode can be regarded as a safe approach for the management of peri-implantitis, particularly in terms of thermal safety. While the surface roughness remains unchanged, the use of these lasers resulted in melting changes and micropores on the Ti cylinder topography. To determine how these laser settings affect bacterial decrease and osseointegration, additional research is needed.

Upon evaluation based on the application times of 20 seconds and 40 seconds, a statistically significant difference was observed. The temperature change on the 40 s laser applied Ti cylinder surfaces was observed to be greater than that on the 20 s laser applied (p=0.037; Figure 3).
<img alt="Box plot diagram; temperature change over time; comparative analysis; experimental data analysis." class="xf...

In this study, Er,Cr:YSGG and diode lasers applied separately to the flat surface of a total of 96 specially designed titanium cylinders. A thermocouple placed on the other surface and the temperature was measured. Surface roughness analyzed by profilometer, SEM and AFM.

Peri-implant diseases are significant issues associated with dental implants. The aim of this study was to evaluate the surface roughness and temperature ...

This study evaluates the use of two different types of lasers on titanium surfaces to treat periimplantitis investigating the impact on implants. One of the challenges of the experiment was to replicate the intraoral environment into a uncontrollable in-vitro models. Studies on the use of lasers in the treatment of periimplantitis should be conducted as extensive clinical trials.To begin, launch the Rhinoceros 3D graphics and design program. Draw a circle with a diameter of 10 millimeters, then reduce the circle by 50%along one axis to create an ellipse. Use the extruder function to raise the ellipse in the third dimension.Draw another circle for finger support. Use the extruder function to raise the second circle in the third dimension, ensuring it is shorter than the first shape. Now, drill a 10-millimeter hole in the elliptical drawing using the Boolean command.For thermocouple support, create an L-shaped line using the Sweep1 command and extrude it into the third dimension. Draw a square and extrude it into the third dimension to create the base. Set a closed room with air conditioning to a temperature of 27 degrees Celsius.Fix the stand in the center of a plastic tub using double-sided tape. Position the titanium cylinder on the fixing stand. Spray air into the titanium cylinder before starting the experiment.Insert the thermocouple of the thermometer into the hollow section of the titanium cylinder positioned in its slot on the stand. Prepare a chronometer to monitor application time. Assign a third observer to record temperature changes and operate the stopwatch.Wear protective glasses before beginning laser application for safety. Insert the tips for the lasers. Turn on the Er, Cr:YSGG laser and select perio closed mode.Apply 1.5, 2.5, and 3.5 watts of laser energy for 20 seconds and 40 seconds each. Then turn on the diode laser and select perio pocket mode. Apply 0.8 watts, 1.3 watts, and 1.8 watts of laser energy for 20 seconds and 40 seconds each.Have the third observer start the timer when the laser application begins. Notify the observer when the time is up. Now, apply the laser tip at a 15-degree angle to the surface, maintaining contact and moving in a zigzag pattern across the entire surface for the planned duration.Record the initial and final temperature values during laser application. Subtract the start temperature from the final value to calculate the temperature change. Store samples in transparent bags labeled with group numbers For two and three-dimensional imaging, do not coat samples before placing them in the scanning electron microscope.Randomly select one cylinder from each of the 13 study groups. Insert them into the SEM device recording their location and sample code to avoid mix-ups. Place the titanium cylinder in the SEM device with the flat surface facing upward.Perform analysis using low-vacuum mode. Set the chamber pressure to 60 pascals during analysis. For atomic force microscopy measurement, randomly select one titanium cylinder from each study group.Perform measurements in tapping mode. Transfer the cylinder into the instrument. Capture a 5 x 5 micrometer digital image for each sample and record at a slow scan rate of one hertz.For the measurement of surface roughness, first fix the titanium roller with a holder. Place the needle of the profilometer in contact with the titanium surface. Set the resolution to 0.01 millimeters, the transverse length to 3.0 millimeters, and the diamond recording pin tip diameter to five micrometers.Adjust the measurement speed to 0.5 millimeters per second to determine the mean roughness or RA value. Press start to begin the measurement. Once measurement is complete, save the recorded RA value.Repeat measurements five times in different directions on the flat surface of each cylinder. The temperature change on the 42nd laser applied cylinder surfaces was greater than that on the 22nd laser applied. The temperature change in titanium cylinders using a diode laser was significantly greater than in those using the Er, Cr:YSGG laser.Within the diode laser groups, the 42nd application resulted in significantly higher temperature changes compared to the 22nd application across all power levels. The temperature range of the diode laser groups with 1.8 watts applied to the cylinder surfaces was markedly greater than that in the diode laser groups with 0.8 watts applied. SEM images showed a porous structure in all groups characteristic of sandblasted, acid-etched implant surfaces.At 5000X magnification, laser-treated titanium surfaces showed visible enlargement of micron-sized pores compared to the control group. At 250X and 1000X magnifications, surfaces exposed to the Er, Cr:YSGG and diode lasers for 40 seconds exhibited more surface melting than those treated for 20 seconds. AFM images revealed that surface indentations were uniformly distributed in the control group compared to laser-treated samples.The roughness parameter did not show a significant difference in laser type, watt, time, or in combined evaluations.

in-vitro-evaluation-effects-ercrysgg-diode-lasers-used-on-titanium

Research

JoVE Journal

Bioengineering

This video demonstrates a non-invasive laser-assisted procedure to selectively damage the corneal endothelial cells in the porcine eye. The developed ex vivo model of endothelial cell damage can be used to study diseases of the corneal endothelium.

Laser-assisted Selective Ablation of Porcine Corneal Endothelial Cells: A Technique to Induce Focused Porcine Corneal Endothelial Injury for Ex Vivo Studies

An all laser procedure is proposed in the endothelial transplant. The surgical technique is based on the use of a femtosecond laser to prepare the donor tissue. Laser welding technique is then used to secure the donor endothelium in the correct position.

An &#8220;All-laser&#8221; Endothelial Transplant

An original experimental setup for heating cells in a culture dish using 1.94 µm continuous-wave laser radiation is introduced here. Using this method, the biological responses of retinal pigment epithelial (RPE) cells after different thermal exposures can be investigated.

Continuous-wave Thulium Laser for Heating Cultured Cells to Investigate Cellular Thermal Effects

Here, we present a protocol to detach corneal endothelial cells (CEC) from Descemet’s membrane (DM) using a neodymium:YAG (Nd:YAG) laser as an ex vivo disease model for bullous keratopathy (BK).

Development of a Noninvasive, Laser-Assisted Experimental Model of Corneal Endothelial Cell Loss

Here, we present a method for the isolation of Extracellular Vesicles (EVs) derived from the platelet lysates (PL) and their use for coating titanium (Ti) implant surfaces. We describe the drop casting coating method, the EVs release profile from the surfaces, and in vitro biocompatibility of EVs coated Ti surfaces.

Platelet-Derived Extracellular Vesicle Functionalization of Ti Implants

The present protocol describes an experimental model based on ink-staining which can be used for in vitro implant surface decontamination and roughness research to contribute to clinical decision-making.

Effects of Mechanical Methods Used in Peri-implantitis Treatment on Implant Surface Decontamination and Roughness

The present pilot in vitro study aimed to evaluate the cleaning efficacy of three different decontamination tools and possible surface alterations following treatment, using permanent red ink to mimic the presence of oral biofilm.

Pilot In Vitro Study to Assess Cleaning Ability and Effects of Different Decontamination Methods on Implant Surfaces

We developed a technology based on mesoporous silica thin film for the selective recovery of low molecular weight proteins and peptides from human serum. The physico-chemical properties of our mesoporous chips were finely tuned to provide substantial control in peptide enrichment and consequently profile the serum proteome for diagnostic purposes.

Low Molecular Weight Protein Enrichment on Mesoporous Silica Thin Films for Biomarker Discovery

Interstitial fluid flow is elevated in solid tumors and can modulate tumor cell invasion. Here we describe a technique to apply interstitial fluid flow to cells embedded in a matrix and then measure its effects on cell invasion. This technique can be easily adapted to study other systems.

Three-dimensional Cell Culture Model for Measuring the Effects of Interstitial Fluid Flow on Tumor Cell Invasion

We have developed an eye irritation test which utilizes a three dimensional reconstructed human cornea-like epithelial (RhCE) tissue model. The test is able to discriminate between ocular irritant and corrosive materials (GHS Categories 1 and 2 combined) and those that do not require labeling (GHS No Category).

Eye Irritation Test (EIT) for Hazard Identification of Eye Irritating Chemicals using Reconstructed Human Cornea-like Epithelial (RhCE) Tissue Model

Explore laser effects on titanium surfaces for periimplantitis treatment using Er,Cr:YSGG and diode lasers. This method evaluates temperature changes and surface roughness through SEM, AFM, and profilometry analysis.

In Vitro Evaluation of The Effects Of Er,Cr:YSGG and Diode Lasers Used on Titanium Cylinder

Explore More Videos