Name: Archimedes-Based Glycerol Displacement for Electrode Porosity Measurement in Lead-Acid Batteries (Video) | JoVE Journal
Uploaded: 2026-04-07T13:30:00.000+00:00
Duration: 13 min 2 s
Description: Learn the glycerol displacement method for measuring electrode porosity in lead-acid batteries using Archimedes' principle. This safer technique enables reproducible analysis of entire battery plates.

ai_agent_IP

ai_agent

maintenance

instantTrialDurationMinutes

isBiopharma

enableNewMyJoveSectionDesign

educationFeatures

seoMetaApi

ai_copilot_institution_blacklist

ai_chat_institution_blacklist

freeAccessWindow

ssoRoleCapture

scheduledMaintenanceBanner

joveLabsFeatures

disable_autoplay_for_bots

extended_trial_duration

5 minutes

The authors appreciate uYilo and the Nelson Mandela University (NMU) post-doctoral program for funding the project

NOTE: The protocol is similar to the one previously described by Ferg et al.7. The equipment and reagents used in the study are listed in the Table of Materials. An image of the equipment used for the porosity measurement of the electrodes is presented in Figure 2.
<img alt="Static equilibrium diagram, pulley system for balancing forces, mechanical setup." class="xfigimg" src="/files/ftp_upload/69319/69319fig2.jpg" data-altupdatedat="1777953618000" data-alt="Figure 2"> 
Figure 2: Simple equipment used for glycerol displacement-based porosity measurement of electrodes. The setup comprises (1) a digital electronic balance, (2) a balance attachment with crocodile clips, (3) a sturdy frame structure, (4) a negative battery plate, (5) a container with glycerol, and (6) a laboratory Jack <a href="https://www.jove.com/files/ftp_upload/69319/69319fig2large.jpg" target="_blank">Please click here to view a larger version of this figure.</a>
1. Sample preparation
<ol>
	<li>Extraction of the plates for porosity measurement
	<ol>
		<li>Using a plastic-cutting saw, carefully open the lead-acid battery by slowly cutting along the seam between the casing and the lid. 
		CAUTION: Review the material safety data sheet (MSDS) for all materials used in this protocol. A lead-acid battery contains corrosive sulfuric acid and toxic lead plates. Cut open slowly in a well-ventilated chemical fume hood while wearing full personal protective equipment, including acid-resistant gloves, in order to prevent potential injuries. Also, keep neutralizing agents and emergency facilities nearby.</li>
		<li>Carefully disassemble the lead-acid battery.</li>
		<li>Remove each battery cell and separate its components, ensuring the positive and negative plates are extracted without any alteration.</li>
	</ol>
	</li>
	<li>Preparation of the plates for porosity measurement
	<ol>
		<li>Gently rinse the plates with water to remove the residual acid. 
		NOTE: Ensure that the plates are free of any residual acid, as this might react when immersed in the glycerol.</li>
		<li>Dry the negative plate in an oven under an inert atmosphere such as nitrogen to prevent the oxidation of lead. Dry at 110 °C for 6 h or until constant mass is achieved.</li>
		<li>Dry the positive plate in the oven at 110 °C for 24 h. 
		​NOTE: In the case of pasted plates, the outer paper should be removed before drying in the oven.</li>
		<li>Remove the plates from the oven and allow them to cool in a desiccator to prevent moisture absorption.</li>
		<li>Cut off the lugs of the plates and ensure the plates are dry before commencing the porosity measurement in order to record accurate masses.</li>
	</ol>
	</li>
</ol>
2. Porosity measurement
NOTE: A Digital Electronic Balance (maximum capacity: 500 g; accuracy: 0.01 g) was used in this study.
<ol>
	<li>Place an electronic balance on a sturdy frame structure above a suitable container that contains the glycerol of a known density. 
	NOTE: The glycerol density will be used later in the calculations.</li>
	<li>Remove the dry plate from the desiccator, place it onto a tared electronic balance, and record the mass as the mass of the dry plate.</li>
	<li>Attach the telescopic (extendable) crocodile clip to the top of the lead grid.</li>
	<li>Submerge the plate completely in glycerol, ensuring that the extended portion of the clip is kept above the liquid for easy removal of the plate from the glycerol. Bubbles that are trapped in the plate should start to emerge.</li>
	<li>Put the lid onto the container and insert the stopper. 
	NOTE: The container lid should be designed to enable vacuum application.</li>
	<li>Connect the setup to a low vacuum supply and apply a vacuum of approximately 100 mbar until the sides of the container show a slight indent, then turn off the vacuum. This is to ensure that glycerol penetrates all the pores.</li>
	<li>Keep the plate under vacuum for at least 15 min. 
	NOTE: If air bubbles are still visibly emerging from the lead plate after this period, extend the vacuum time for a little longer. The average porosity of the plates can be underestimated if glycerol does not fully penetrate all the pores.</li>
	<li>Place the balance attachment onto a tared scale and record the mass.</li>
	<li>Remove the plate from the glycerol and attach it to the two crocodile clips on the balance attachment. Make sure the plate is level and adjust if necessary.</li>
	<li>Place the balance attachment with the soaked plate onto the scale and let the plate hang above the glycerol for 8 min to remove the excess glycerol that is on the surface of the plate.</li>
	<li>Wipe off any drops on the bottom of the plate.</li>
	<li>Place the balance attachment on the scale and record the mass as the mass of the glycerol-saturated plate.</li>
	<li>Slowly raise the glycerol container by using the laboratory jack until the top of the plate is just submerged. Record this mass as the mass of the glycerol submerged plate.</li>
	<li>Repeat the experiment in triplicate. 
	NOTE: Dispose of all residues as hazardous chemical waste, following the institution's waste management guidelines.</li>
</ol>
3. Analysis of the porosity data
NOTE: The data required to calculate the porosity of the plates were adapted from Ferg et. al.7, and a detailed derivation of the formulas is provided in Supplementary file 17,8,9.
<ol>
	<li>Data required to calculate the porosity of the electrode
	<ol>
		<li>Define the parameters required. The parameters required for analyzing the percentage porosity are defined as follows: 
		Mass of dry plate (g) = A 
		Mass of glycerol saturated plate (g) = B (To be measured in triplicate) 
		Mass of glycerol submerged plate (g) = C (To be measured in triplicate) 
		Mass of the grid alloy (g)= D 
		Density of the grid alloy (g/cm3) = E (NOTE: this is determined by the type of lead alloy used) 
		Density of glycerol (g/cm3) = F 
		Active material mass (g), G = (A - D) 
		Active material absolute density (g/cm3),  <img alt="Complex mathematical equation; static equilibrium principle; formula representation." src="/files/ftp_upload/69319/69319eq4.jpg" style="margin: auto;" data-altupdatedat="1777953618000" data-alt="Equation 4"> 
		Specific pore volume (cm3/g), <img alt="Intensity calculation formula, I=(B-A)/FG, equation, optics analysis." src="/files/ftp_upload/69319/69319eq2v2.jpg" style="margin: auto;" data-altupdatedat="1777953618000" data-alt="Equation 5"> 
		Bulk density (g/cm3),  <img alt="Equilibrium equation J=1/(1/H+I), static dynamics, formula illustration." src="/files/ftp_upload/69319/69319eq6.jpg" style="margin: auto;" data-altupdatedat="1777953618000" data-alt="Equation 6"> 
		% Porosity, K = IJ x 100</li>
	</ol>
	</li>
	<li>Generating the remaining data needed for the calculations
	<ol>
		<li>Determine the mass of the grid by carefully removing the active material of the electrode. 
		NOTE: Figure 6A,B show positive and negative formed lead-acid battery plates with corresponding active materials, while Figure 6C, D show the respective grids.</li>
	</ol>
	</li>
	<li>Data analysis
	<ol>
		<li>Open a spreadsheet and input each parameter listed in step 3.1 and the corresponding formulas into the appropriate columns.</li>
		<li>Input the mass of the dry plate, A into a column.</li>
		<li>Input the triplicate masses of the glycerol saturated plate, B, into a column.</li>
		<li>Input the triplicate masses of the submerged plate, C, into a column.</li>
		<li>Input the mass of the grid alloy, D, into a column.</li>
		<li>Input the density of the grid alloy, E, into a column. (Depending on the type of lead alloy used).</li>
		<li>Input the density of the glycerol, F, into a column.</li>
		<li>Input the formula for determining the active material mass of the plate, G, into a column by subtracting the mass of the dry plate, A, from the mass of the grid alloy, D, to compute the corresponding values. 
		The active material mass of the plate, G = (A -D)      (1)</li>
		<li>Input the formula for determining the absolute density of the active material, H, into a column to compute the corresponding values. 
		<img alt="Equation for variable H in scientific analysis context, featuring algebraic symbols and fractions." src="/files/ftp_upload/69319/69319eq3v2.jpg" style="margin: auto;" data-altupdatedat="1777953618000" data-alt="Equation 8"></li>
		<li>Input the formula for determining the specific pore volume, I, into a column to compute the corresponding values. 
		<img alt="Chemical equation showing pore volume to mass ratio, \( I = \frac{\text{Pore volume}}{\text{Active material mass}} \)." src="/files/ftp_upload/69319/69319eq4v2.jpg" style="margin: auto;" data-altupdatedat="1777953618000" data-alt="Equation 9"></li>
		<li>Input the formula for determining the bulk density of the active material, J, into a column to compute the corresponding values. 
		The bulk density of the active material, <img alt="Static equilibrium equation J=1/(1/H+I), mathematical formula." src="/files/ftp_upload/69319/69319eq5v3.jpg" style="margin: auto;" data-altupdatedat="1777953618000" data-alt="Equation 5"></li>
		<li>Input the formula for calculating the % Porosity of the active material mass on the plate, K, into a column to compute the corresponding values. 
		% Porosity, K = IJ x 100      (5)</li>
		<li>Determine the average percentage porosity and standard deviation of the plates using the appropriate function on the spreadsheet.</li>
	</ol>
	</li>
</ol>
4. Microstructural analysis by powder X-ray diffraction
NOTE: Powder X-ray diffraction microstructural analysis were performed on replicate plates from the same battery that have been exposed to the same condition to ensure that the data obtained is comparable and that there is no structural interference.
<ol>
	<li>Sample preparation for X-ray diffraction of the electrode surface
	<ol>
		<li>Carefully cut the dried sample of the plate to the appropriate shape to fit into the sample holder. 
		NOTE: This should be done carefully to avoid altering the surface of the electrode.</li>
		<li>Transfer the sample to a clean sample holder, ensuring that the height of the plate surface is aligned with the top edge of the sample holder.</li>
	</ol>
	</li>
	<li>Sample preparation for X-ray diffraction of active material bulk 
	NOTE: A sample preparation station obtained from Malvern Panalytical was used to enable easy back-loading of the powder sample into the sample holder.
	<ol>
		<li>Remove the dried sample of the active material of the plate from the grid.</li>
		<li>Grind the active material to powder with a mortar and pestle to uniformly reduce the particle size and ensure there is sufficient powder to fill a standard sample holder.</li>
		<li>Clean the sample holder and the sample preparation table of the sample preparation station.</li>
		<li>Place the top plate of the 2-piece powder sample holder flat-side down on the sample preparation table and secure it by pressing and releasing the clamp button of the sample preparation table.</li>
		<li>Overfill the top plate of the sample holder with the powder sample using a spatula.</li>
		<li>Gently compress the powder onto the top plate of the sample holder by pressing firmly and evenly with the powder press block of the sample preparation station. Ensure the sample height aligns with the top edge of the sample holder.</li>
		<li>Clean the edges of the sample holder with a dusting brush to remove the excess powder.</li>
		<li>Press the bottom of the 2-piece powder sample holder face-side down onto the top plate until it clicks.</li>
		<li>Flip the sample preparation table and press the clamp button to release the sample holder. Confirm that the powder surface is smooth and aligns with the top edge of the sample holder.</li>
	</ol>
	</li>
	<li>XRD data acquisition 
	NOTE: Powder X-ray diffraction patterns were recorded over a 2-theta range of 5°-80°, in a 15 min scan using a benchtop diffractometer equipped with a cobalt (Co) anode X-ray tube.
	<ol>
		<li>Load the sample holder onto the XRD diffractometer.</li>
		<li>Select the appropriate measurement program and input the sample details into the diffractometer.</li>
		<li>Start the measurement.</li>
		<li>After the data has been collected, go to the data management menu of the diffractometer and export the results to the desired folder.</li>
	</ol>
	</li>
	<li>Rietveld refinement 
	NOTE: The DIFFRAC.EVA version 4.3 and DIFFRAC.TOPAS version 6 were used for the phase identification and quantitative Rietveld refinement, respectively.
	<ol>
		<li>Identify the phases available in the sample using a dedicated phase identification software.</li>
		<li>Open the DIFFRAC.EVA software and click on the import from files tab to load the XRD scan file (.RAW file) onto the software for peak identification.</li>
		<li>Click on the Search/Match (scan) tab in the Data command panel.</li>
		<li>Click on the drop-down button beside the chemical filter tab. Right-click to select all elements on the periodic table, then right-click again to change the selected elements to 'discarded'.</li>
		<li>Uncheck the elements of interest that are contained in the sample by clicking on the element symbol.</li>
		<li>Click on the drop-down button beside the database filter tab and select the database of choice.</li>
		<li>Click on the match tab to match the diffraction pattern with the reference database to identify the phases.</li>
		<li>Quantify the identified phases in the sample using a dedicated quantitative analysis software.</li>
		<li>Open the DIFFRAC.TOPAS software and click on the load scan files to import the raw XRD data into the software for quantitative Rietveld refinement.</li>
		<li>Click on the drop-down button beside the name of the raw file.</li>
		<li>Right-click on the emission profile tab and load the emission profile.</li>
		<li>Click on the background tab and refine the background parameters.</li>
		<li>Click on the instrument tab and refine the parameters based on the instrument configuration.</li>
		<li>Click on the correction tab and refine the zero error, sample displacement, and Lorentz polarization factors.</li>
		<li>Click on the Load STR(s) tab to load the structure files of the identified phases from the CoD database of the TOPAS software.</li>
		<li>Refine the lattice parameters and atomic positions of the crystal structure(s).</li>
		<li>Click on the Run tab to initiate the refinement.</li>
		<li>Continue refining until the goodness-of-fit and weighted-profile R-factor (Rwp) is below the acceptable standard.</li>
	</ol>
	</li>
</ol>
5. Modifications and troubleshooting
NOTE: This section outlines critical protocol steps that can affect the accuracy and reproducibility of porosity measurements in lead plates and provides guidance for addressing common issues that can be encountered during the protocol.
<ol>
	<li>Fragile plates
	<ol>
		<li>Plates exposed to typical battery conditions may become fragile and could disintegrate during handling. Handle plates gently, avoiding pressure on the active material.</li>
	</ol>
	</li>
	<li>Incomplete drying of plates
	<ol>
		<li>If the plates are not dried completely, residual moisture may cause inaccuracies in the mass of the dry plate and, consequently, in all subsequent calculations. Ensure the plates are fully dry before commencing the porosity measurement, and verify that a constant mass has been achieved.</li>
	</ol>
	</li>
	<li>Residual acid plates
	<ol>
		<li>Residual acid in the plates may react when submerged in glycerol. Rinse the plates gently but thoroughly with water to remove any remaining acid, ensuring complete removal.</li>
	</ol>
	</li>
	<li>Incomplete pore penetration
	<ol>
		<li>If glycerol does not fully penetrate all pores, the calculated pore volume will be lower than the actual value, affecting the average porosity of the plates. After 15 min of vacuum-assisted infiltration, the presence of air bubbles indicates that there are pores that are yet to be filled; continue vacuuming until bubble ceases. While 15 min should be suitable for most plate sizes, optimize the infiltration time based on the plate size.</li>
	</ol>
	</li>
</ol>

<ol><li>Kurzweil, P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Gaston+Plant%C3%A9+and+his+invention+of+the+lead-acid+battery-the+genesis+of+the+first+practical+rechargeable+battery%5BTitle%5D)+AND+%22J+Power+Sources%22%5BJournal%5D)">Gaston Planté and his invention of the lead-acid battery-the genesis of the first practical rechargeable battery.</a> J Power Sources. 195 (14), 4424-4434 (2010).</li>
<li>Heth, C. L. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Energy+on+demand%3A+a+brief+history+of+the+development+of+the+battery%5BTitle%5D)+AND+%22Substantia%22%5BJournal%5D)">Energy on demand: a brief history of the development of the battery.</a> Substantia. 3 (2), 77-86 (2019).</li>
<li>Catherino, H. A., Feres, F. F., Trinidad, F. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Sulfation+in+lead-acid+batteries%5BTitle%5D)+AND+%22J+Power+Sources%22%5BJournal%5D)">Sulfation in lead-acid batteries.</a> J Power Sources. 129 (1), 113-120 (2004).</li>
<li>Pavlov, D. <a target="_blank" href="http://scholar.google.com/scholar?hl=en&safe=off&q=author%3aPavlov%2C+D+%22Lead-Acid+Batteries%3A+Science+and+Technology%22">Lead-Acid Batteries: Science and Technology</a>. , Elsevier. (2011).</li>
<li>Zau, A. T. P., Lencwe, M. J., Chowdhury, S. D., Olwal, T. O. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((A+battery+management+strategy+in+a+lead-acid+and+lithium-ion+hybrid+battery+energy+storage+system+for+conventional+transport+vehicles%5BTitle%5D)+AND+%22Energies%22%5BJournal%5D)">A battery management strategy in a lead-acid and lithium-ion hybrid battery energy storage system for conventional transport vehicles.</a> Energies. 15 (7), 2577(2022).</li>
<li>Garche, J., Karden, E., Moseley, P. T., Rand, D. A. <a target="_blank" href="http://scholar.google.com/scholar?hl=en&safe=off&q=author%3aGarche%2C+J+%22Lead-Acid+Batteries+for+Future+Automobiles%22">Lead-Acid Batteries for Future Automobiles</a>. , Elsevier. (2017).</li>
<li>Ferg, E., Loyson, P., Rust, N. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Porosity+measurements+of+electrodes+used+in+lead-acid+batteries%5BTitle%5D)+AND+%22J+Power+Sources%22%5BJournal%5D)">Porosity measurements of electrodes used in lead-acid batteries.</a> J Power Sources. 141 (2), 316-325 (2005).</li>
<li>Investigation of the effects of mass of active materials of lead-acid battery on active mass utilization coefficient. Hasan, M. K., Kibria, M. G. Proceedings of 7th International Conference on Mechanical, Industrial and Energy Engineering-Part II, 2, 57-60 (2025).</li>
<li>Zhang, Q., Cui, N., Zhou, Z., Shang, Y., Duan, B. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Critical+review+and+analysis+of+available+capacity+estimation+of+LiFePO4+battery+using+Peukert%27s+law%3A+A+case+study%5BTitle%5D)+AND+%22Int+J+Energy+Res%22%5BJournal%5D)">Critical review and analysis of available capacity estimation of LiFePO4 battery using Peukert's law: A case study.</a> Int J Energy Res. 46 (15), 23808-23823 (2022).</li>
<li>AXS, B. TOPAS v6: General Profile and Structure Analysis Software for Powder Diffraction Data. <a target="_blank" href="http://scholar.google.com/scholar?hl=en&safe=off&q=author%3aAXS%2C+B+%22User%27s+Manual%22">User's Manual</a>. , Bruker AXS. Karlsruhe, Germany. (2017).</li>
<li>Pavlov, D., Kirchev, A., Stoycheva, M., Monahov, B. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Influence+of+H2SO4+concentration+on+the+mechanism+of+the+processes+and+on+the+electrochemical+activity+of+the+Pb%2FPbO2%2FPbSO4+electrode%5BTitle%5D)+AND+%22J+Power+Sources%22%5BJournal%5D)">Influence of H2SO4 concentration on the mechanism of the processes and on the electrochemical activity of the Pb/PbO2/PbSO4 electrode.</a> J Power Sources. 137 (2), 288-308 (2004).</li>
<li>Romero, A. F., Ocón, P. Phase Transformation Processes in the Active Material of Lead-Acid Batteries. <a target="_blank" href="http://scholar.google.com/scholar?hl=en&safe=off&q=author%3aRomero%2C+AF+%22Phase+Change+Materials-Technology+and+Applications%22">Phase Change Materials-Technology and Applications</a>. , IntechOpen. (2022).</li>
<li>Liu, Z., Luo, X., Ji, D. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Effect+of+phase+composition+of+PbO2+on+cycle+stability+of+soluble+lead+flow+batteries%5BTitle%5D)+AND+%22J+Energy+Storage%22%5BJournal%5D)">Effect of phase composition of PbO2 on cycle stability of soluble lead flow batteries.</a> J Energy Storage. 38, 102524(2021).</li>
<li>Hao, H., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((A+review+of+the+positive+electrode+additives+in+lead-acid+batteries%5BTitle%5D)+AND+%22Int+J+Electrochem+Sci%22%5BJournal%5D)">A review of the positive electrode additives in lead-acid batteries.</a> Int J Electrochem Sci. 13 (3), 2329-2340 (2018).</li>
<li>Mandal, S., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Positive+electrode+active+material+development+opportunities+through+carbon+addition+in+the+lead-acid+batteries%3A+a+recent+progress%5BTitle%5D)+AND+%22J+Power+Sources%22%5BJournal%5D)">Positive electrode active material development opportunities through carbon addition in the lead-acid batteries: a recent progress.</a> J Power Sources. 485, 229336(2021).</li>
<li>Hossain, M. D., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Effects+of+additives+on+the+morphology+and+stability+of+PbO2+films+electrodeposited+on+nickel+substrate+for+light+weight+lead-acid+battery+application%5BTitle%5D)+AND+%22J+Energy+Storage%22%5BJournal%5D)">Effects of additives on the morphology and stability of PbO2 films electrodeposited on nickel substrate for light weight lead-acid battery application.</a> J Energy Storage. 27, 101108(2020).</li>
<li>Wall, M. T., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Growth+mechanisms+of+nano-to+micro-sized+lead+sulfate+particles%5BTitle%5D)+AND+%22ACS+Omega%22%5BJournal%5D)">Growth mechanisms of nano-to micro-sized lead sulfate particles.</a> ACS Omega. 6 (16), 10557-10567 (2021).</li>
<li>Kubota, Y. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Water+adsorption+on+lead+dioxide+from+ab+initio+molecular+dynamics+simulations%5BTitle%5D)+AND+%22J+Chem+Phys%22%5BJournal%5D)">Water adsorption on lead dioxide from ab initio molecular dynamics simulations.</a> J Chem Phys. 158 (13), (2023).</li>
<li>Iliev, V., Pavlov, D. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Self-discharge+and+passivation+phenomena+in+lead-acid+batteries+during+storage%5BTitle%5D)+AND+%22J+Electrochem+Soc%22%5BJournal%5D)">Self-discharge and passivation phenomena in lead-acid batteries during storage.</a> J Electrochem Soc. 129 (3), 458(1982).</li>
<li>Snyders, C., Ferg, E., Van Dyl, T. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((The+use+of+a+polymat+material+to+reduce+the+effects+of+sulphation+damage+occurring+in+negative+electrodes+due+to+the+partial+state+of+charge+capacity+cycling+of+lead+acid+batteries%5BTitle%5D)+AND+%22J+Power+Sources%22%5BJournal%5D)">The use of a polymat material to reduce the effects of sulphation damage occurring in negative electrodes due to the partial state of charge capacity cycling of lead acid batteries.</a> J Power Sources. 200, 102-107 (2012).</li>
</ol>

The authors declare that the work presented in this paper is free from conflicting interests

Capacity tests showed that Battery 1 delivered 92% of the rated capacity (6.62 Ah), Battery 2 delivered 50% (3.58 Ah) with only a partial recovery of 3.32 Ah even after a repeated recharge step, and Battery 3 delivered 91% of the rated capacity (6.57 Ah) (Table 1).
Variations in the concentration of H2SO4 within the PAM pores, resulting from chemical reactions that occur in the plates during capacity cycling, influence the structure and morphology of the ...

The lead-acid battery is one of the oldest commercial rechargeable batteries. In 1859, French physicist Gaston Plante demonstrated the battery's working principle by submerging two lead plates in sulfuric acid. The potential for commercialization was realized only 20 years later, when improvements to the technology were made in using pasted plates that allowed the battery to be discharged and charged through a reverse current1.
Even in the early stages of the invention, the significance of the exposed surface area and the porosity of the battery material became evident. It was understood that the larger the surface area of the material, the greater the battery's capacity2. At the time, the commercialization of the battery found a unique application in the emerging automotive industry1, enabling the starting of internal combustion engines of not only passenger vehicles but also larger engines that were used in the military, such as tanks and airplanes3,4,5.
As the manufacturing technologies improved over the years, so did the advancements in chemical analysis and the understanding of the processes that occur within the battery. There will always be a need to improve the manufacturing process to ensure a consistent product that is not only price competitive but also of good quality and that can provide electrical backup for longer periods of time.
The chemistry that occurs in the battery, referred to as a double sulphate theory, is unique when compared to other battery types. In this case, the electrolyte or acid forms part of the reaction mechanism during the discharge and charge process6.
<img alt="Lead-acid battery reactions; chemical equations; electrochemical process; energy storage." src="/files/ftp_upload/69319/69319eq1v2.jpg" style="margin: auto;" data-altupdatedat="1777953618000" data-alt="Equation 1">
<img alt="Static equilibrium; discharging/charging lead-acid battery; chemical reaction diagram; Pb, PbO₂, SO₄²⁻." class="xfigimg" src="/files/ftp_upload/69319/69319fig1.jpg" data-altupdatedat="1777953618000" data-alt="Figure 1"> 
Figure 1: Schematic illustration of the charging and discharging reaction mechanisms of a lead-acid battery. <a href="https://www.jove.com/files/ftp_upload/69319/69319fig1large.jpg" target="_blank">Please click here to view a larger version of this figure.</a>
Here, the electrodes or plates that can conduct electricity react with the acid to form lead sulphate, which can be seen as an insulator (Figure 1). Not all the material that is on a plate is used in the discharge process. The electrochemical reaction predominantly occurs at the surface of the material that is exposed to the acid, and when the battery is charged, the insulating lead sulphate material then converts back to the conductive lead dioxide and lead on the two plates that are referred to as the cathode and anode, respectively5. The larger the surface area, the more discharge reactions can take place and the more capacity can be obtained. Plates are designed to be relatively thin and usually specific to the application. For high power over short periods of time, as in the starting of a car, a large area is desirable where the acid can easily travel or diffuse to the middle of the plate, whereas for batteries intended to provide more capacity over longer periods of time at lower discharge rates, usually thicker plates are then used. This becomes a trade-off between the available material that the acid can easily migrate or diffuse into, and providing a thicker, more rigid support for the plate to last longer in application.
Analysis of the active material inside a battery has always been challenging due to its destructive nature. The battery has to be cut open and the plates disassembled; that can then only provide a snapshot in time of what the battery's state or condition is. This usually relates to the scientists wanting to know the battery's state of charge (SoC) and state of health (SoH). In a battery, the most important and probably the only chemical parameters one can comfortably measure as an analyst are the chemical properties that include its elemental and phase composition. These techniques usually rely on atomic absorption or X-ray fluorescence-type techniques, as well as advanced methods such as scanning electron microscopy and powder X-ray diffraction. There are also electrochemical analytical techniques that can be applied, including impedance spectroscopy and cyclic voltammetry, among others.
On the other hand, physicochemical properties include the strength of the plates, the available surface area, and the porosity of the active material. Surface area analysis is typically done by nitrogen adsorption techniques, and in this study, the porosity of the plates used in the lead-acid battery was measured. Porosity relates to the available free space that is within the active material for the acid to move freely into and to be in contact with the active sites that will then allow for an electrochemical reaction to take place. If the porosity is too high, there will be limited connective pathways between the various active material particles, increasing the likelihood of disconnection. If the porosity is too low, less of the acid will be able to reach the active sites, thereby reducing the available capacity.
Traditionally, the porosity of solid materials that have micro- to meso-sized pores is measured by mercury porosimetry. This required the active material to be physically removed from the plate in order to fit into the instrument's sample holder. This has a number of disadvantages, namely, only a representative sample from a plate area is taken; the sample as such is disconnected from the grid or current collector, thereby inducing additional cracks and cavities in the material; and many laboratories have moved away from the use of mercury due to its toxicity. The advantage of the technique is its ability to provide an estimate of the pore size distribution of the material within a certain range.
This study proposes a technique that makes use of the entire plate in measuring the total porosity of the active material by using Archimedes' principle. In its context of determining material density, Archimedes' principle states that the buoyant force on an object that is immersed in a fluid is equal to the weight of the fluid displaced by that object. This principle allows one to calculate an object's density by measuring its weight in air and its weight when submerged in a known fluid. This buoyant force is then used to calculate the volume of the displaced fluid, which is equal to the volume of the object.
The technique can be easily set up in a laboratory to measure the porosity of lead-acid battery plates that have been subjected to certain manufacturing or testing conditions. Even though the technique is still destructive in the sense of having to cut the battery open to remove the plates for analysis, the porosity of the entire plate is considered. Hence, the method measures the average porosity over the entire plate, capturing variations of certain regions of the plate that are usually not taken into account. These variations typically occur when working with relatively large plates, where possible manufacturing inconsistencies and the effects of acid stratification can affect specific plate regions over time. However, a limitation of the glycerol displacement method is that it measures porosity based on permeable pores. This means that it is possible to underestimate the plate's porosity if glycerol does not fully penetrate the pores of the active mass. When closed pores are present, the technique indirectly correlates with what happens inside the battery during application, since the acid would also not be able to completely penetrate areas of the active mass that have closed pores. Despite this limitation, the method remains safe and cost-effective and is suitable for measuring the porosity of battery plates.
In this study, the porosities of both the negative and positive plates of a relatively small 7.2 Ah valve-regulated lead-acid (VRLA) battery are measured. These batteries are typically used in household alarm and gate motor control systems. The effect on the batteries' plate porosity and chemical phase composition was studied in terms of the possible aging mechanism to which the battery was exposed. One being excessive calendar aging or shelf life, and the other being repeated capacity cycling without sufficient recharging. These are typical conditions that such batteries are exposed to. Those that remain on the electrical wholesaler's shelves for many months and sometimes years without receiving a boost charge. Moreover, those batteries that are used in standby power supply systems are subjected to repeated "load-shedding-type" capacity cycling, where the inverter system's recharge is insufficient to provide the necessary energy to fully recharge the battery during the short recharge periods available.

<table><tbody><tr><td>Aeris benchtop powder X-ray diffractometer</td><td>Malvern Panalytical B.V., Almelo, The Netherland</td><td></td><td>For the microstructural analysis&amp;nbsp;</td></tr><tr><td>Balance Attachment with crocodile clips</td><td></td><td></td><td>To allow for the weighing of the saturated and submerged plate</td></tr><tr><td>Battery cells (12 V, 7.2 Ah)&amp;nbsp;</td><td>N/A</td><td>N/A</td><td>Any&amp;nbsp;</td></tr><tr><td>DIFFRAC.EVA V 4.3</td><td>Bruker AXS&amp;nbsp;GmbH,&amp;nbsp;Karlsruhe, Germany</td><td>Version 4.3</td><td>Phase identification software</td></tr><tr><td>DIFFRAC.TOPAS V6</td><td>Bruker AXS&amp;nbsp;GmbH,&amp;nbsp;Karlsruhe, Germany</td><td>Version 6</td><td>Phase quantification software</td></tr><tr><td>Digital Electronic Balance</td><td>Dixon Science, China</td><td>EG5001-A</td><td>Digital Electronic Balance with a maximum capacity of 500 g and an accuracy of 0.01 g</td></tr><tr><td>Laboratory central vacuum line</td><td></td><td></td><td>To apply vacuum to the container to facilitate the infiltration of glycerol into the plates.</td></tr><tr><td>Laboratory Jack</td><td>Karl-Kurt Juchheim Laborger&amp;auml;te, GmbH, Germany</td><td>2290</td><td>To raise the glycerol container until the top of the plate is just submerged</td></tr><tr><td>Powder sample holders</td><td>Malvern Panalytical B.V., Almelo, The Netherland</td><td></td><td>For holding powder samples for XRD analysis</td></tr><tr><td>Sample Preparation Station</td><td>Malvern Panalytical B.V., Almelo, The Netherland</td><td>9,43,00,17,70,101</td><td>To enable easy back-loading of powders into the sample holders for XRD analysis</td></tr><tr><td>Sturdy frame structure</td><td></td><td></td><td>Any&amp;nbsp;</td></tr><tr><td>Suitable container with lid</td><td></td><td></td><td>Any&amp;nbsp;</td></tr><tr><td>Telescopic crocodile clip</td><td></td><td></td><td>For submerging the plates in the glycerol</td></tr><tr><td>Vacuum Pressure Guage</td><td>WIKA Alexander Wiegand SE &amp;amp; Co. KG, Klingenberg, Germany</td><td>Model: 611.10</td><td>To measure the pressure of the applied vacuum</td></tr></tbody></table>

archimedes-based glycerol displacement for electrode porosity measurement in lead-acid batteries

Archimedes-Based Glycerol Displacement for Electrode Porosity Measurement in Lead-Acid Batteries

The performance of lead-acid batteries is highly dependent on the structural and surface properties of the electrodes' active materials. Besides the importance of the material's phase composition at any given time in application, its surface area and porosity contribute to the overall performance of the battery. Mercury porosimetry, which uses a representative sample of the active material for its analysis, has traditionally been used to measure the porosity of battery plates. Apart from the possibility of inducing cracks and cavities in the material while taking the sample, many laboratories have moved away from the use of mercury due to its toxicity. The Archimedes-based glycerol displacement technique has the advantage of being a simple method that considers the porosity of the entire battery plate. Even though the method might not give detailed information on the material's pore volume distribution, reproducibility is achieved for individual plates as well as groups of plates taken from either a single cell or six cells from a battery. The method calculates porosity based on the material's absolute and envelope density, which makes use of absorbed glycerol volume to measure the average porosity over the entire plate. Lead-acid batteries are usually subjected to aging mechanisms that affect the active material's structural integrity and surface properties. This study describes the use of the glycerol displacement technique for the measurement of battery plate porosities, combined with powder X-ray diffraction material characterization to understand the degradation mechanisms of batteries that were subjected to capacity life cycling and calendar aging or shelf life, respectively. The results showed that the failure mechanisms of batteries are significantly different and that both the chemical and physical properties of the active material are interdependent; therefore, one cannot rely on a single analytical tool only to interpret a failure mechanism.

Capacity tests were conducted on three commercially purchased 12 V, 7.2 Ah VRLA lead-acid batteries at the C10 rate to a lower voltage limit of 10.5 V. All capacity tests were performed at 25 °C. Upon receipt, the batteries were recharged at 14.8 V for 10 h, with a maximum current of 2.9 A. This was followed by two C10 capacity tests with a standard recharge step at 14.8 V for 24 h at 2.9 A maximum. The results of the initial C10 capacities are summarized in Table 1.
...

Here, we present a simple and low-cost glycerol displacement method based on Archimedes' principle for measuring lead-acid battery electrode porosities. The method demonstrates good reproducibility and is safer than traditional techniques, requiring low-hazard chemicals and equipment. Combining the technique with microstructural analysis by X-ray diffraction provides information on battery electrode properties and degradation.

The performance of lead-acid batteries is highly dependent on the structural and surface properties of the electrodes' active materials. Besides the ...

This video demonstrates the porosity measurement of lead acid battery plates using the glycerol displacement method based on Archimedes'principle. The lead acid battery is one of the oldest commercial rechargeable batteries. When a French physicist, Gaston Plante in 1859, demonstrated the working principle of the battery by having two lead plates submerged in sulfuric acid, it was only 20 years later when improvements in the technology was made, when pasting of the plates was a possibility and one could discharge and charge these plates reversibly.Even at these early stages of the invention, the importance of the exposed surface area and the porosity of the material in the battery were realized, where the greater the surface area of the material would give a battery with more capacity. At the time, the commercialization of the battery found a unique application in emerging automotive industry, where it managed to help start the internal combustion engine of not only passenger vehicles, but also larger engines that were used in the military, such as tanks and aeroplanes. In the 1950s, we saw the introduction of the sealed lead asset battery that made use of either gel or glass mat separators.The technology helped to limit the emissions of hydrogen gas during the recharging process. These types of batteries can also be manufactured into various sizes, from small batteries for computer backup systems to large truck batteries or solar farms. As manufacturing technologies improved over the years, so that the advancements in chemical analysis and the understanding of the processes that occur in the battery.There will always be a need to improve the manufacturing process to ensure that a consistent product that is not only price competitive, but also of good quality that can provide electricity for long periods of time. In terms of the chemistry that occurs in the battery, it is referred to as a double sulfate theory and unique when compared to other battery types. In this case, the electrolyte, or the acid, forms part of the reaction mechanism during the discharge and charge process.Analysis of the active material inside a battery has always been challenging, since by its very nature, the analysis is destructive. The battery has to be cut open and the plates disassembled. This can then only provide a snapshot in time of what the battery state or condition is.This usually relates to the scientists wanting to know the battery state of charge and state of health. Besides a large range of chemical analysis that can be done on the materials, physical properties include the strength of the plates, the surface area, and the porosity of the active material. Surface area analysis is typically done by nitrogen absorption techniques, and in this study, we will look at measuring the porosity of the plates used in the lead acid battery.Porosity relates to the available free space that is in the active material for the acid to move freely in and to be in contact with the active sites that will allow for an electrochemical reaction to take place. Traditionally, porosity of solid materials that have micro mesoporous are measured by mercury porosimetry. This required the active material to be physically removed from the plates in order for it to fit into the instrument sample holder.This has a number of disadvantages, namely, only a representative sample from a plate area can be taken. The sample is such as disconnected from the grid or current collector, thereby inducing additional cracks and cavities into the material, and many laboratories have moved away from the use of mercury due to its toxicity. The advantage of the technique is that it can give you an idea of the pore size distribution of the material within a certain range.The glycerol displacement method is a technique that is based on Archimedes'principle, and it uses glycerol as displacement medium. According to Archimedes'principle, the apparent loss in mass of an immersed body is equal to the mass of liquid displaced. From this, we can determine the volume of the immersed plate, the volume of the pores, and calculate the average porosity of the active material on the plate.It is a simple and reliable method that makes use of non-toxic substances and can be used to measure the average porosity of an entire lead acid battery plate. It can measure a range of plates, types, and sizes, and it's suitable for use both in an academic lab and in an industrial lab. In addition to what is shown in this protocol, microstructural analysis using powder x-ray diffraction helps to better understand the electroactive materials inside the battery.Begin by carefully disassembling the cold lead acid battery. Remove each battery cell and separate its components, ensuring the positive and negative plates are extracted without any alteration. After rinsing the plates with water to remove the residual acid, dry the negative plate in an oven under inert atmosphere, such as nitrogen, to prevent the oxidation of lead.Dry at 110 degrees centigrade for six hours or until constant mass is achieved. Dry the positive plates in the oven at 110 degrees centigrade for 24 hours. Remove the plates from the oven and allow to cool in a desiccator to prevent moisture absorption.Cut up the log of the plates and ensure the plates are dry before commencing the porosity measurement in order to record accurate masses. Fit an electronic balance in a sturdy frame structure above a container that contains glycerol of known density. Remove the dry plate from the desiccator.Place onto the tared electronic balance and record the mass as mass of dry plate. Attach the telescopic crocodile clip to the top of the lead grid. Submerge the plate completely in glycerol, ensuring that the extended portion of the clip is kept above the liquid.Bubbles that are trapped in the plate start to emerge. Put the lead onto the container and insert the stopper. Connect the setup to a low vacuum supply and apply a vacuum of approximately 100 mbar until the sides of the container show a slight indent, then turn off the vacuum.This is to ensure that glycerol penetrates all the pores. Keep the plate on the vacuum for at least 15 minutes. If air bubbles are still visibly emerging from the lead plate after this period, extend the vacuum time for a little longer.Place the balance attachment onto the tared scale and record the mass. Remove the plate from the glycerol and attach to the two crocodile clips on the balance attachment as shown. Make sure the plate is level and adjust if necessary.Place the balance attachments with a soft plate onto the scale and let the plate hang above the glycerol for eight minutes to remove the excess glycerol that is on the surface of the plate. Wipe off any drops on the bottom of the plate Place the balance attachment on the scale and record the mass as the mass of glycerol saturated plate. Slowly raise the glycerol container by using the laboratory jack until the top of the plate is just submerged.Record this mass as the mass of glycerol submerged plate. Repeat the experiments in triplicates. The parameters required for analyzing the percentage porosity and their formulas are defined in rows two to 12, mass of the dry plate, mass of glycerol saturated plate to be measured in triplicate, mass of glycerol submerged plates to be measured in triplicate, mass of the grid alloy, density of the grid alloy, density of glycerol, active material mass, active material absolute density, specific pore volume, bulk density, and finally, the percentage porosity, all to calculated using the formulas in column D.Input the parameters listed above in the corresponding column as shown.Input the mass of the dry plate A into the column A.Click and drag to copy value to the adjacent cells for the triplicate. Input the triplicate masses obtained for the glycerol, saturated, and submerged plate into columns B and C respectively. Into columns D, E, and F, input the respective grid mass, grid density, and glycerol density masses.Click and drop to copy each value to the adjacent cells for the triplicates. Input the formula for the active material mass into column G, where subtracted the grid mass from the mass of the dry plate. Click and drag to copy the value to the adjacent cells.Input the formula for determining the absolute density of the active material into column H to compute the corresponding values. Click and drag to copy value to the adjacent cells. Input the formula for determining specific pore volume into column I to compute the corresponding values.Click and drag to copy value to the adjacent cells. Input the formula for determining bulk density of the active material into column J to compute the corresponding values. Click and drag to copy value to the adjacent cells.Finally, input the formula for calculating the percentage porosity of the active material mass on the plate into column K to compute the corresponding values. Click and drag to copy value to the adjacent cells. Then determine the average percentage porosity and the standard deviation of the plates by using the appropriate function on the spreadsheet.The porosity data obtained for the negative and positive plates of three different batteries are tabulated. The bar chart shows the porosities obtained for the batteries, while the arrow bar indicates the standard deviations across the number of plates analyzed, demonstrating that the method is highly repeatable. Exile the diffraction patterns of the active materials from the positive and negative battery plates, showing chemical face compositions and their quantifications are also presented.The glycerol displacement porosity measurement technique, notable for its ability to measure entire plates, as well as multiple plates from one or more cells, is demonstrated. The method provides a comprehensive assessment of the plates as opposed to analyzing only a portion of a single plate, making the results highly reliable.

archimedes-based-glycerol-displacement-for-electrode-porosity

Research

JoVE Journal

Chemistry

Lithium ion batteries employ flammable and volatile organic electrolytes that are suitable for ambient temperature applications. A safer alternative to organic electrolytes are solid polymer batteries. Solid polymer batteries operate safely at high temperatures (&gt;120 °C), thus making them applicable to high temperature applications such as deep oil drilling and hybrid electric vehicles. This paper will discuss (a) the polymer synthesis, (b) the polymer conduction mechanism, and (c) provide...

Solid-state Graft Copolymer Electrolytes for Lithium Battery Applications

Ultrasound velocimetry is used to study mixing by fluid flow in liquid metal electrodes. The focus of this manuscript is to illustrate the methods used for making precise, spatially-resolved ultrasound measurements while limiting oxidation and controlling and monitoring temperature, applied current, and the heater power being supplied.

Ultrasound Velocity Measurement in a Liquid Metal Electrode

Non-aqueous electrode processing is central to the construction of coin cells and the evaluation of new electrode chemistries for lithium-ion batteries. A step-by-step guide to the basic practices needed as an electrochemical engineer working with batteries in an academic experimental setting is furnished.

Non-aqueous Electrode Processing and Construction of Lithium-ion Coin Cells

A protocol for the electrochemical testing of an aprotic Li-O2 battery with the preparation of electrodes and electrolytes and an introduction of the frequently used methods of characterization is presented here.

Protocol of Electrochemical Test and Characterization of Aprotic Li-O2 Battery

Here, we describe protocols to prepare phosphonium-based ionic liquid and lithium bis(trifluoromethane)sulfonimide salt electrolytes, and assemble a non-flammable and high temperature functioning lithium-ion coin cell battery.

Synthesis of Ionic Liquid Based Electrolytes, Assembly of Li-ion Batteries, and Measurements of Performance at High Temperature

The incorporation of reference electrodes in a Li-ion battery provides valuable information to elucidate degradation mechanisms at high voltages. In this article, we present a cell design that accommodates multiple reference electrodes, along with the assembly steps to assure maximum accuracy of the data obtained in electrochemical measurements.

In Situ Lithiated Reference Electrode: Four Electrode Design for In-operando Impedance Spectroscopy

Three-electrode cells are useful in studying the electrochemistry of lithium-ion batteries. Such an electrochemical setup allows the phenomena associated with the cathode and anode to be decoupled and examined independently. Here, we present a guide for construction and use of a three-electrode coin cell with emphasis on lithium plating analytics.

Three-electrode Coin Cell Preparation and Electrodeposition Analytics for Lithium-ion Batteries

A protocol for the construction of a soluble lead flow battery with an extended lifespan, in which sodium acetate is supplied in the methanesulfonic electrolyte as an additive, is presented.

Extending the Lifespan of Soluble Lead Flow Batteries with a Sodium Acetate Additive

The goal of the reported protocols is to create rechargeable zinc-sponge electrodes that suppress dendrites and shape change in zinc batteries, such as nickel–zinc or zinc–air.

Zinc-Sponge Battery Electrodes that Suppress Dendrites

This work aims at determining the reaction kinetics of Li-ion battery cathode and anode materials undergoing thermal runaway (TR). Simultaneous Thermal Analysis (STA)/Fourier Transform Infrared (FTIR) spectrometer/Gas Chromatography Mass Spectrometry (GC-MS) were used to reveal thermal events and to detect evolved gases.

Identification and Quantification of Decomposition Mechanisms in Lithium-Ion Batteries; Input to Heat Flow Simulation for Modeling Thermal Runaway

Learn the glycerol displacement method for measuring electrode porosity in lead-acid batteries using Archimedes' principle. This safer technique enables reproducible analysis of entire battery plates.

Archimedes-Based Glycerol Displacement for Electrode Porosity Measurement in Lead-Acid Batteries