Name: Gyroid镍纳米结构的嵌段共聚物超分子 (视频) | JoVE Journal
Uploaded: 2014-04-28T13:00:00.000+00:00
Duration: 8 min 40 s
Description: 学习利用嵌段共聚物超分子模板制备有序镍纳米泡沫的方法。通过无电沉积和热解技术，研究人员成功构建了具有双螺旋反转结构的纳米多孔金属材料。

ai_agent_IP

ai_agent

maintenance

instantTrialDurationMinutes

isBiopharma

enableNewMyJoveSectionDesign

educationFeatures

seoMetaApi

ai_copilot_institution_blacklist

ai_chat_institution_blacklist

freeAccessWindow

ssoRoleCapture

scheduledMaintenanceBanner

joveLabsFeatures

disable_autoplay_for_bots

extended_trial_duration

5 minutes

我们感谢格罗宁根大学Zernike先进材料研究所提供的财务支持。

1. 具有双螺旋形态的PS-b-P4VP(PDP)复合物的制备与表征
<ol>
	<li>称取聚苯乙烯-阻断聚(4-乙烯基吡啶) (PS-b-P4VP）和十五烷基苯酚（PDP，Mr = 304.51 g/mol)。为了获得陀螺形态，应谨慎选择PDP的用量（P4VP(PDP)嵌段的重量分数（fP4VP(PDP)应为 约 0.6（根据线性AB二嵌段共聚物的相图）。通常，使用0.15–0.2 g的PS-b-P4VP 导致 PS-b-P4VP(PDP) 薄膜 50-100 μm 厚（鉴于步骤1.3中使用的培养皿直径为5-6 cm）。根据以下公式计算PDP的用量： 
	<img alt="Polymer composition equation, f(P4VP(PDP)) ratio, calculation of polymer mass fractions." src="/files/ftp_upload/50673/50673eq1.jpg" data-altupdatedat="1787630408000" data-alt="Equation 1"> 
	<img alt="Mathematical equation for copolymer mass; m(P4VP)=f(P4VP)×m(copolymer); polymer chemistry." src="/files/ftp_upload/50673/50673eq2.jpg" data-altupdatedat="1787630408000" data-alt="Equation 2"> 
	<img alt="Polymer composition formula: f(P4VP)=Mn(P4VP)/Mn(copolymer), ratio calculation, diagram." src="/files/ftp_upload/50673/50673eq3.jpg" data-altupdatedat="1787630408000" data-alt="Equation 3"> 
	<img alt="Polymer mass calculation equation; chemical composition; educational diagram." src="/files/ftp_upload/50673/50673eq4.jpg" data-altupdatedat="1787630408000" data-alt="Equation 4"></li>
	<li>溶解 PS-b- 将P4VP和PDP溶于氯仿中，在室温下搅拌数小时。保持聚合物浓度低于2 wt%，以确保形成均匀的复合物。</li>
	<li>将溶液倒入玻璃培养皿中。</li>
	<li>将培养皿放入饱和氯仿环境中。</li>
	<li>约一周后，取出培养皿，此时已形成超分子复合物的薄膜。</li>
	<li>在真空条件下干燥薄膜 30 °C 过夜。</li>
	<li>将薄膜放入特制容器中，抽出容器中的空气并充入氮气。将薄膜在烘箱中于指定温度下退火4天。 120 °C 在 N 条件下2 1 bar 过压的环境</li>
	<li>裁剪一小块薄膜，包埋于环氧树脂中，并在 40 °C.</li>
	<li>使用金刚石刀在室温下将样品切成约80 nm厚的切片。切好的切片将漂浮于水面上。用铜网捞取切片并置于其上。</li>
	<li>将含有超薄切片的载网放入盛有碘液的容器中。45分钟后，样品染色完成，可进行透射电子显微镜观察。</li>
	<li>将载有染色切片的铜网放入透射电子显微镜中，在120 kV加速电压下观察并成像样品。</li>
	<li>将步骤1.7中获得的薄膜样品插入小角X射线散射（SAXS）样品架中，并用聚酰亚胺胶带固定。将制备好的样品架放入SAXS仪器中。打开X射线快门，采集二维散射图样。对获得的二维图样进行积分，分析其在一维图谱中的峰位。</li>
</ol>
2. 多孔结构的制备与表征
<ol>
	<li>将步骤 1.7 所得的薄膜样品放入乙醇中，浸泡三天。</li>
	<li>干燥样品。</li>
	<li>制备 1H NMR 测量样品。将 PDP 粉末、PS-b-P4VP 粉末、超分子复合物 PS-b-P4VP(PDP)（步骤 1.7 后）以及多孔薄膜（步骤 2.2 后）分别溶解于 CDCl3 中，在室温下记录 1H NMR 谱图。</li>
	<li>采用差示扫描量热法分析 PS-b-P4VP 粉末、超分子复合物 PS-b-P4VP(PDP)（步骤 1.7 后）以及多孔薄膜（步骤 2.2 后）。使用调制模式，升/降温速率为 1 °C/min，振荡振幅为 0.5 °C，振荡周期为 60 秒。将样品在 -30 °C 下平衡，加热至 180 °C，再冷却至 -30 °C，然后再次加热至 180 °C。分析时采用第二次加热循环的数据。</li>
	<li>将多孔样品（步骤 2.2 后）在室温下脱气 8 小时，随后在 70 °C 下脱气 18 小时，并在 77 K 下进行氮气吸附测量。</li>
	<li>使用适当的软件（例如 WinADP）和模型分析所获得的吸附等温线。</li>
	<li>将多孔样品（步骤 2.2 后）在 50 °C 下干燥 8 小时，并在室温和 0.5 Pa 压力下脱气 2 小时。</li>
	<li>进行压汞法孔隙度测量。</li>
</ol>
3. 在聚合物模板中插入镍
<ol>
	<li>称取氯化亚锡（SnCl2，Mr = 189.60 g/mol），配制水溶液（0.1 M SnCl2 / 0.1 M HCl；1.896 g SnCl2、0.8 ml HCl 和 100 ml H2O）。将溶液置于摇床中过夜，以确保 SnCl2 完全溶解。</li>
	<li>称取氯化钯（PdCl2，Mr = 177.33 g/mol），配制水溶液（0.0014 M PdCl2 / 0.25 M HCl；0.025 g PdCl2、2 ml HCl 和 100 ml H2O）。</li>
	<li>配制镀镍液的第一部分：称取 6.78 g 六水合硫酸镍（NiSO4•6H2O，Mr = 262.85 g/mol）和 2 g 柠檬酸钠（Na3C6H5O7，Mr = 258.06 g/mol），溶于 80 ml 水中。加入 828 μl 85% 乳酸（C3H6O3，Mr = 90.08 g/mol）。</li>
	<li>配制镀镍液的第二部分：称取 0.2 g 二甲胺硼烷络合物（(CH3)2NHBH3，Mr = 58.92 g/mol），溶于 20 ml 水中。二甲胺硼烷络合物应在通风良好的通风橱中操作。</li>
	<li>将多孔薄膜（步骤 2.2 之后）浸入氯化亚锡水溶液（步骤 3.1）中 1 小时。</li>
	<li>用去离子水彻底冲洗薄膜。</li>
	<li>将薄膜浸入氯化钯水溶液（步骤 3.2）中 1 小时。</li>
	<li>用去离子水彻底冲洗薄膜。</li>
	<li>将镀镍液的第一部分（3.3）与第二部分（3.4）混合。用氢氧化铵调节 pH 至 7.0。</li>
	<li>将薄膜浸入镀镍液中 1 小时。</li>
	<li>用去离子水彻底冲洗薄膜。</li>
	<li>干燥样品。</li>
	<li>按照步骤 1.8–1.9 所述方法制备用于电子显微镜观察的镀膜样品。</li>
	<li>按照步骤 1.11 所述方法对样品进行成像。</li>
	<li>将含有镀膜样品切片的铜网插入高分辨率透射电子显微镜中，获取高分辨率 TEM 显微图像。在显微镜下观察样品，并选择用于 EDX（X 射线能谱分析）元素分析的区域。对选定区域进行 EDX 分析，并解析所得谱图。</li>
</ol>
4. 暴露反螺旋镍泡沫
<ol>
	<li>将镀镍薄膜（经过步骤 3.12 处理后）放入 350 °C 的烘箱中，保持 1 小时至 4 天。</li>
	<li>使用银浆将样品固定在样品台上。</li>
	<li>将样品插入扫描电子显微镜中，获取该样品的多张图像。</li>
	<li>将样品插入扫描电子显微镜中，在显微镜下观察样品，并选择用于 EDX 元素分析的区域。对选定区域进行 EDX 分析，并解析所得谱图。</li>
</ol>

<ol><li>Erlebacher, J., Aziz, M. J., Karma, A., Dimitrov, N., Sieradzki, K. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Evolution+of+nanoporosity+in+dealloying%5BTitle%5D)+AND+%22Nature%22%5BJournal%5D)">Evolution of nanoporosity in dealloying.</a> Nature. 410, 450-453 (2001).</li>
<li>Nyce, G. W., Hayes, J. R., Hamza, A. V., Satcher, J. H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Synthesis+and+Characterization+of+Hierarchical+Porous+Gold+Materials%5BTitle%5D)+AND+%22Chem.+Mater%22%5BJournal%5D)">Synthesis and Characterization of Hierarchical Porous Gold Materials.</a> Chem. Mater. 19, 344-346 (2007).</li>
<li>Detsi, E., van de Schootbrugge, M., Punzhin, S., Onck, P. R., De Hosson, J. T. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((On+tuning+the+morphology+of+nanoporous+gold%5BTitle%5D)+AND+%22Scripta+Mater%22%5BJournal%5D)">On tuning the morphology of nanoporous gold.</a> Scripta Mater. 64, 319-322 (2011).</li>
<li>Gacoin, T., Lahlil, K., Larregaray, P., Boilot, J. P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Transformation+of+CdS+Colloids%3A+Sols%2C+Gels%2C+and+Precipitates%5BTitle%5D)+AND+%22J.+Phys.+Chem.+B%22%5BJournal%5D)">Transformation of CdS Colloids: Sols, Gels, and Precipitates.</a> J. Phys. Chem. B. 105, 10228-10235 (2001).</li>
<li>Tappan, B. C., Steiner, S. A., Luther, E. P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Nanoporous+Metal+Foams%5BTitle%5D)+AND+%22Angew.+Chem.+Int.+Ed%22%5BJournal%5D)">Nanoporous Metal Foams.</a> Angew. Chem. Int. Ed. 49, 4544-4565 (2010).</li>
<li>Leventis, N., Chandrasekaran, N., Sadekar, A. G., Sotiriou-Leventis, C., Lu, H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((One-Pot+Synthesis+of+Interpenetrating+Inorganic%2FOrganic%5BTitle%5D)+AND+%22Networks+of+CuO%2FResorcinol-Formaldehyde+Aerogels%3A+Nanostructured+Energetic+Materials.+J.+Am.+Chem.+Soc%22%5BJournal%5D)">One-Pot Synthesis of Interpenetrating Inorganic/Organic.</a> Networks of CuO/Resorcinol-Formaldehyde Aerogels: Nanostructured Energetic Materials. J. Am. Chem. Soc. 131, 4576-4577 (2009).</li>
<li>Leventis, N., Chandrasekaran, N., Sotiriou-Leventis, C., Mumtaz, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Smelting+in+the+age+of+nano%3A+iron+aerogels%5BTitle%5D)+AND+%22J.+Mater.+Chem%22%5BJournal%5D)">Smelting in the age of nano: iron aerogels.</a> J. Mater. Chem. 19, 63-65 (2009).</li>
<li>Tappan, B. C., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Ultralow-Density+Nanostructured+Metal+Foams%3A+Combustion+Synthesis%2C+Morphology%2C+and+Composition%5BTitle%5D)+AND+%22J.+Am.+Chem.+Soc%22%5BJournal%5D)">Ultralow-Density Nanostructured Metal Foams: Combustion Synthesis, Morphology, and Composition.</a> J. Am. Chem. Soc. 128, 6589-6594 (2006).</li>
<li>Ashby, M. F., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Metal+Foams%3A+a+Design+Guide%5BTitle%5D)+AND+%22Butterworth-Heinemann%22%5BJournal%5D)">Metal Foams: a Design Guide.</a> Butterworth-Heinemann. , (2000).</li>
<li>Tekoglu, C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Size+Effects+in+Cellular+Solids%5BTitle%5D)+AND+%22%22%5BJournal%5D)">Size Effects in Cellular Solids.</a> , University of Groningen. (2007).</li>
<li>Amsterdam, E. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Structural+Performance+and+Failure+Analysis+of+Aluminium+Foams%5BTitle%5D)+AND+%22%22%5BJournal%5D)">Structural Performance and Failure Analysis of Aluminium Foams.</a> , University of Groningen. (2008).</li>
<li>Bates, F. S., Fredrickson, G. H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Block+Copolymer+Thermodynamics%3A+Theory+and+Experiment%5BTitle%5D)+AND+%22Annu.+Rev.+Phys.+Chem%22%5BJournal%5D)">Block Copolymer Thermodynamics: Theory and Experiment.</a> Annu. Rev. Phys. Chem. 41, 525-527 (1990).</li>
<li>Hamley, I. W. <a target="_blank" href="http://scholar.google.com/scholar?hl=en&safe=off&q=author%3aHamley%2C+IW+%22The+Physics+of+Block+Copolymers%22">The Physics of Block Copolymers</a>. , Oxford University Press. (1998).</li>
<li>Abetz, V., Simon, P. <a target="_blank" href="http://scholar.google.com/scholar?hl=en&safe=off&q=author%3aAbetz%2C+V+%22Advances+in+Polymer+Science%22">Advances in Polymer Science</a>. , Springer. Berlin / Heidelberg. (2005).</li>
<li>Hillmyer, M. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Nanoporous+Materials+from+Block+Copolymer+Precursors%5BTitle%5D)+AND+%22Adv.+Polym.+Sci%22%5BJournal%5D)">Nanoporous Materials from Block Copolymer Precursors.</a> Adv. Polym. Sci. 190, 137-181 (2005).</li>
<li>Mansky, P., Harrison, C. K., Chaikin, P. M., Register, R. A., Yao, N. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Nanolithographic+templates+from+diblock+copolymer+thin+films%5BTitle%5D)+AND+%22Appl.+Phys.+Lett%22%5BJournal%5D)">Nanolithographic templates from diblock copolymer thin films.</a> Appl. Phys. Lett. 68, 2586-2588 (1996).</li>
<li>Hashimoto, T., Tsutsumi, K., Funaki, Y. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Nanoprocessing+Based+on+Bicontinuous+Microdomains+of+Block+Copolymers%3A+Nanochannels+Coated+with+Metals%5BTitle%5D)+AND+%22Langmuir%22%5BJournal%5D)">Nanoprocessing Based on Bicontinuous Microdomains of Block Copolymers: Nanochannels Coated with Metals.</a> Langmuir. 13, 6869-6872 (1997).</li>
<li>Chen, S. -Y., Huang, Y., Tsiang, R. C. -C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Ozonolysis+efficiency+of+PS-b-PI+block+copolymers+for+forming+nanoporous+polystyrene%5BTitle%5D)+AND+%22J.+Polym.+Sci.+A+Polym.+Chem%22%5BJournal%5D)">Ozonolysis efficiency of PS-b-PI block copolymers for forming nanoporous polystyrene.</a> J. Polym. Sci. A Polym. Chem. 46, 1964-1973 (2008).</li>
<li>Thurn-Albrecht, T., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Nanoscopic+Templates+from+Oriented+Block+Copolymer+Films%5BTitle%5D)+AND+%22Adv.+Mater%22%5BJournal%5D)">Nanoscopic Templates from Oriented Block Copolymer Films.</a> Adv. Mater. 12, 787-791 (2000).</li>
<li>Park, M., Harrison, C., Chaikin, P. M., Register, R. A., Adamson, D. H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Block+Copolymer+Lithography%3A+Periodic+Arrays+of+%7E1011+Holes+in+1+Square+Centimeter%5BTitle%5D)+AND+%22Science%22%5BJournal%5D)">Block Copolymer Lithography: Periodic Arrays of ~1011 Holes in 1 Square Centimeter.</a> Science. 276, 1401-1404 (1997).</li>
<li>Cheng, J. Y., Ross, C. A., Thomas, E. L., Smith, H. I., Vancso, G. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Fabrication+of+nanostructures+with+long-range+order+using+block+copolymer+lithography%5BTitle%5D)+AND+%22Appl.+Phys.+Lett%22%5BJournal%5D)">Fabrication of nanostructures with long-range order using block copolymer lithography.</a> Appl. Phys. Lett. 81, 3657-3659 (2002).</li>
<li>Voet, V. S. D., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Interface+Segregating+Fluoralkyl-Modified+Polymers+for+High-Fidelity+Block+Copolymer+Nanoimprint+Lithography%5BTitle%5D)+AND+%22J.+Am.+Chem.+Soc%22%5BJournal%5D)">Interface Segregating Fluoralkyl-Modified Polymers for High-Fidelity Block Copolymer Nanoimprint Lithography.</a> J. Am. Chem. Soc. 133, 2812-2815 (2011).</li>
<li>Zalusky, A. S., Olayo-Valles, R., Wolf, J. H., Hillmyer, M. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Ordered+Nanoporous+Polymers+from+Polystyrene-Polylactide+Block+Copolymers%5BTitle%5D)+AND+%22J.+Am.+Chem.+Soc%22%5BJournal%5D)">Ordered Nanoporous Polymers from Polystyrene-Polylactide Block Copolymers.</a> J. Am. Chem. Soc. 124, 12761-12773 (2002).</li>
<li>Crossland, E. J. W., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((A+Bicontinuous+Double+Gyroid+Hybrid+Solar+Cell%5BTitle%5D)+AND+%22Nano+Lett%22%5BJournal%5D)">A Bicontinuous Double Gyroid Hybrid Solar Cell.</a> Nano Lett. 9, 2807-2812 (2008).</li>
<li>Uehara, H., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Size-Selective+Diffusion+in+Nanoporous+but+Flexible+Membranes+for+Glucose+Sensors%5BTitle%5D)+AND+%22ACS+Nano%22%5BJournal%5D)">Size-Selective Diffusion in Nanoporous but Flexible Membranes for Glucose Sensors.</a> ACS Nano. 3, 924-932 (2009).</li>
<li>Voet, V. S. D., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Poly%28vinylidene+fluoride%29%2Fnickel+nanocomposites+from+semicrystalline+block+copolymer+precursors%5BTitle%5D)+AND+%22Nanoscale%22%5BJournal%5D)">Poly(vinylidene fluoride)/nickel nanocomposites from semicrystalline block copolymer precursors.</a> Nanoscale. 5, 184-192 (2013).</li>
<li>Brinker, C. J., Scherer, J. W. <a target="_blank" href="http://scholar.google.com/scholar?hl=en&safe=off&q=author%3aBrinker%2C+CJ+%22Sol-Gel+Science%3A+The+Physics+and+Chemistry+of+Sol-Gel+Processing%22">Sol-Gel Science: The Physics and Chemistry of Sol-Gel Processing</a>. , Academic Press. (1990).</li>
<li>Hsueh, H. -Y., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Inorganic+Gyroid+with+Exceptionally+Low+Refractive+Index+from+Block+Copolymer+Templating%5BTitle%5D)+AND+%22Nano+Lett%22%5BJournal%5D)">Inorganic Gyroid with Exceptionally Low Refractive Index from Block Copolymer Templating.</a> Nano Lett. 10, 4994-5000 (2010).</li>
<li>Hsueh, H. -Y., Ho, R. -M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Bicontinuous+Ceramics+with+High+Surface+Area+from+Block+Copolymer+Templates%5BTitle%5D)+AND+%22Langmuir%22%5BJournal%5D)">Bicontinuous Ceramics with High Surface Area from Block Copolymer Templates.</a> Langmuir. 28, 8518-8529 (2012).</li>
<li>Riedel, W. Electroless Nickel Plating. , (1991).</li>
<li>Mallory, G. O., Hajdu, J. B. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Electroless+Plating%3A+Fundamentals+and+Applications%5BTitle%5D)+AND+%22American+Electroplaters+and+Surface+Finishers+Society%22%5BJournal%5D)">Electroless Plating: Fundamentals and Applications.</a> American Electroplaters and Surface Finishers Society. , (1992).</li>
<li>Djokić, S. S. <a target="_blank" href="http://scholar.google.com/scholar?hl=en&safe=off&q=author%3aDjoki%C4%87%2C+SS+%22Modern+Aspects+of+Electrochemistry%22">Modern Aspects of Electrochemistry</a>. , Springer US. (2002).</li>
<li>Djokić, S. S., Cavallotti, P. L. <a target="_blank" href="http://scholar.google.com/scholar?hl=en&safe=off&q=author%3aDjoki%C4%87%2C+SS+%22Modern+Aspects+of+Electrochemistry%22">Modern Aspects of Electrochemistry</a>. , Springer. New York. (2010).</li>
<li>Crossland, E. J. W., Ludwigs, S., Hillmyer, M. A., Steiner, U. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Control+of+gyroid+forming+block+copolymer+templates%3A+effects+of+an+electric+field+and+surface+topography%5BTitle%5D)+AND+%22Soft+Matter%22%5BJournal%5D)">Control of gyroid forming block copolymer templates: effects of an electric field and surface topography.</a> Soft Matter. 6, 670-676 (2010).</li>
<li>Hsueh, H. Y., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Nanoporous+Gyroid+Nickel+from+Block+Copolymer+Templates+via+Electroless+Plating%5BTitle%5D)+AND+%22Adv.+Mater%22%5BJournal%5D)">Nanoporous Gyroid Nickel from Block Copolymer Templates via Electroless Plating.</a> Adv. Mater. 23, 3041-3046 (2011).</li>
<li>Vukovic, I., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Supramolecular+Route+to+Well-Ordered+Metal+Nanofoams%5BTitle%5D)+AND+%22ACS+Nano%22%5BJournal%5D)">Supramolecular Route to Well-Ordered Metal Nanofoams.</a> ACS Nano. 5, 6339-6348 (2011).</li>
<li>Mao, H., Hillmyer, M. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Macroscopic+samples+of+polystyrene+with+ordered+three-dimensional+nanochannels%5BTitle%5D)+AND+%22Soft+Matter%22%5BJournal%5D)">Macroscopic samples of polystyrene with ordered three-dimensional nanochannels.</a> Soft Matter. 2, 57-59 (2006).</li>
<li>Kobayashi, Y., Tadaki, Y., Nagao, D., Konno, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Deposition+of+Gold+Nanoparticles+on+Polystyrene+Spheres+by+Electroless+Metal+Plating+Technique%5BTitle%5D)+AND+%22J.+Phys.+Conf.+Ser%22%5BJournal%5D)">Deposition of Gold Nanoparticles on Polystyrene Spheres by Electroless Metal Plating Technique.</a> J. Phys. Conf. Ser. 61, 582-586 (2007).</li>
<li>Finnefrock, A. C., Ulrich, R., Toombes, G. E., Gruner, S. M., Wiesner, U. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((The+plumber%27s+nightmare%3A+a+new+morphology+in+block+copolymer-ceramic+nanocomposites+and+mesoporous+aluminosilicates%5BTitle%5D)+AND+%22J.+Am.+Chem.+Soc%22%5BJournal%5D)">The plumber's nightmare: a new morphology in block copolymer-ceramic nanocomposites and mesoporous aluminosilicates.</a> J. Am. Chem. Soc. 125, 13084-13093 (2003).</li>
<li>Tyler, C. A., Morse, D. C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Orthorhombic+Fddd+network+in+triblock+and+diblock+copolymer+melts%5BTitle%5D)+AND+%22Phys.+Rev.+Lett%22%5BJournal%5D)">Orthorhombic Fddd network in triblock and diblock copolymer melts.</a> Phys. Rev. Lett. 94, 208-302 (2005).</li>
<li>Ranjan, A., Morse, D. C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Landau+theory+of+the+orthorhombic+Fddd+phase%5BTitle%5D)+AND+%22Phys.+Rev.+E%22%5BJournal%5D)">Landau theory of the orthorhombic Fddd phase.</a> Phys. Rev. E. 74, 011803(2006).</li>
<li>Kim, M. I., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Stability+of+the+Fddd+Phase+in+Diblock+Copolymer+Melts%5BTitle%5D)+AND+%22Macromolecules%22%5BJournal%5D)">Stability of the Fddd Phase in Diblock Copolymer Melts.</a> Macromolecules. 41, 7667-7670 (2008).</li>
</ol>

作者声明不存在竞争性财务利益。

超分子复合物已成功用作有序金属纳米泡沫的前驱体。该方法的关键步骤是获得合适的模板， 即&#160;具有gyroid形貌的模板。在嵌段共聚物的相图中，gyroid区域非常小，难以精准调控。这意味着，若以传统的嵌段共聚物作为起始材料，必须反复进行相当复杂的合成过程，直至获得能够形成gyroid形貌的理想组成。在PS-b-P4VP(PDP) 复合物的不同组成以及相应的不同形貌可通过简单改变所添加 PDP 的量来实现。尽管在 PS-b-P4VP(PDP)复合物的尺寸也相对较小，因此可以获得具有不同结构域尺寸的双连续网络复合物。还必须认识到，在具有双连续网络形貌的传统二嵌段共聚物中，少数组分网络所占据的体积分数 约 35 体积% 及主要基质组分 约 65 体积%。因此，若完全去除基质，将得到高度多孔的模板，相应地形成孔隙率显著降低的金属纳米结构。在此，我们仅去除部分基质，从而使得最终金属泡沫的孔隙率高于 50 体积%，已足以满足金属纳米泡沫形成的通常要求。5此外，在传统的嵌段共聚物方法中，如果从PS-聚环氧乙烷（PEO）或聚乳酸（PLA...

目前已有多种技术可用于制备金属纳米泡沫材料：去合金化1-3、溶胶-凝胶法4,5、纳米熔融法6,7和燃烧合成法8。在去合金化过程中，起始材料通常为二元合金，例如银-金合金。其中较不贵金属的组分（在此例中为银）可通过化学或电化学方法去除，从而形成具有纳米尺度骨架结构的无序多孔金泡沫。在燃烧合成法中，金属与一种高能前驱体混合，该前驱体在分解过程中释放能量，从而驱动金属纳米泡沫的形成8。关于金属泡沫力学行为的研究表明，在无序结构中，应力无法有效地从纳米骨架尺度传递到整体宏观尺度9-11.&#160;因此，相较于无序结构，有序结构的金属纳米泡沫预期具有更优异的力学性能。
此处所展示的思路是利用能够自组装形成有序纳米结构的嵌段共聚物，作为金属纳米泡沫的前驱体。根据嵌段共聚物的组成、单体单元总数以及化学连接的各嵌段之间排斥程度的不同，可呈现出多种形貌，例如：球状、柱状、层状、双螺旋状、六角穿孔层状及其他结构。12-14此外，聚合物嵌段可被选择性降解，从而形成纳米多孔材料15最常见的方法包括：臭氧分解16-18，紫外照射19，反应离子刻蚀20-22，以及溶解23-26生成的多孔结构可用各种无机材料进行回填。金属氧化物（例如&#160;SiO2，TiO2通常被引入 通过 溶胶-凝胶法进入模板的通道27-29电化学镀和化学镀常用于将金属沉积到模板内部或表面30-33最后，可将剩余的聚合物从聚合物/无机纳米杂化材料中去除 通过 热解2，溶解34,35，紫外降解28,29, 等等。
在本方法中，我们从聚苯乙烯的超分子复合物出发阻断-聚(4-乙烯基吡啶) (PS-b-P4VP）嵌段共聚物与两亲性十五烷基苯酚（PDP）分子。该复合物源于PDP与吡啶环之间的氢键作用图1a）。起始嵌段共聚物的组成以及添加的PDP的量被选择为使得所得体系自组装形成双连续双螺旋结构，其中包含PS网络和P4VP(PDP)基质。图1b）。PDP 分子在乙醇中选择性溶解，而 P4VP 链则坍塌并附着于 PS 网络上（图1c随后，采用化学镀方法将镍沉积到模板的孔隙中（图1d）。在去除残留聚合物后 通过 热解后，可获得一种有序的陀螺双曲面镍纳米泡沫（图1e).

<table><tbody><tr><td colspan="4">&lt;strong&gt;试剂&lt;/strong&gt;</td></tr><tr><td>PS-&lt;em&gt;b&lt;/em&gt;-P4VP，CAS：26222-40-2</td><td>Polymer Source 公司</td><td>P9009-S4VP&lt;br/&gt; P136-S4VP&lt;br/&gt; P5462-S4VP&lt;br/&gt; P3912-S4VP</td><td>附加信息见单独表格</td></tr><tr><td>PDP</td><td>Aldrich</td><td>P4402-100G-A</td><td>用石油醚重结晶两次</td></tr><tr><td>SnCl&lt;sub&gt;2&lt;/sub&gt;</td><td>Acros Organics</td><td>196981000</td><td></td></tr><tr><td>PdCl&lt;sub&gt;2&lt;/sub&gt;</td><td>Aldrich</td><td>76050</td><td></td></tr><tr><td>NiSO&lt;sub&gt;4&lt;/sub&gt;&amp;bull;H&lt;sub&gt;2&lt;/sub&gt;O</td><td>Sigma-Aldrich</td><td>227676</td><td></td></tr><tr><td>乳酸</td><td>Aldrich</td><td>W261106</td><td></td></tr><tr><td>柠檬酸三钠盐</td><td>Sigma-Aldrich</td><td>C3674</td><td></td></tr><tr><td>二甲胺硼烷络合物</td><td>Aldrich</td><td>180238</td><td></td></tr><tr><td>&lt;strong&gt;PS-&lt;em&gt;b&lt;/em&gt;-P4VP 货号&lt;/strong&gt;</td><td>&lt;strong&gt;Mn (PS)，g/mol&lt;/strong&gt;</td><td>&lt;strong&gt;Mn(P4VP)，g/mol&lt;/strong&gt;</td><td>&lt;strong&gt;PDI&lt;/strong&gt;</td></tr><tr><td>P9009-S4VP</td><td>24000</td><td>9500</td><td>1.1</td></tr><tr><td>P136-S4VP</td><td>31900</td><td>13200</td><td>1.08</td></tr><tr><td>P5462-S4VP</td><td>37500</td><td>16000</td><td>1.3</td></tr><tr><td>P3912-S4VP</td><td>41500</td><td>17500</td><td>1.07</td></tr></tbody></table>

由二嵌段共聚物超分子制备的陀螺镍纳米结构

Gyroid Nickel Nanostructures from Diblock Copolymer Supramolecules

纳米多孔金属泡沫具有一系列独特的性能——它们具有催化活性，同时具备良好的导热性和导电性，此外还具有高孔隙率、高比表面积以及高强度重量比。然而，目前常见的金属纳米结构制备方法通常得到的是结构高度无序的材料，这可能对其力学性能产生不利影响。嵌段共聚物能够自组装形成有序的纳米结构，因而可作为模板用于制备结构有序的金属纳米泡沫。本文描述了一种基于嵌段共聚物的超分子复合体系——聚苯乙烯-阻断-聚(4-乙烯基吡啶)(十五烷基苯酚) PS-b-P4VP(PDP) 作为有序镍纳米泡沫的前驱体。该超分子复合物表现出与传统嵌段共聚物相似的相行为，可自组装形成双连续陀螺状形貌，其中两个聚苯乙烯（PS）网络嵌入于 P4VP(PDP) 基质中。PDP 可溶于乙醇，从而形成可用于金属填充的多孔结构。通过化学镀技术，可将镍沉积至模板的孔道中。最后，去除残留的聚合物模板 通过 聚合物/无机纳米杂化物热解生成具有反螺旋结构的纳米多孔镍泡沫。

通过透射电子显微镜（TEM）和小角X射线散射（SAXS）对嵌段共聚物超分子复合物PS-b-P4VP(PDP)x的形貌进行表征。图2a和图2b展示了一个典型超分子复合物的双连续陀螺状（gyroid）结构特征图像：分别为双波（double-wave）图案和车轮状（wagon-wheel）图案，它们分别对应于陀螺状晶胞(211)面和(111)面的投影。由于碘染色的作用，PS嵌段区域呈现亮色，而P4VP(PDP)x嵌段区域呈现暗色。图2c展示另一个陀螺状样品的双波图案，其周期性尺寸减小为原来的二分之一。SAXS衍射峰出现在√6q*、√8q*、√14q*、√22q*和√50q*位置，证实了该样品具有双连续的Ia 3d空间群结构形态（图2d）。
通过1H NMR 和 DSC 证实，将 PS-b-P4VP(PDP)x 复合物用乙醇处理可完全去除 PDP。乙醇处理后，...

本文描述了有序镍纳米泡沫的制备方法 通过 基于自组装双嵌段共聚物超分子制备的纳米多孔模板上的化学镀金属沉积

纳米多孔金属泡沫具有一系列独特的性能——它们具有催化活性，且兼具热导性和电导性，此外，……

本实验的总体目标是从一种超分子复合物——聚苯乙烯-嵌段-聚乙烯基嘌呤戊二烯酸LPH酚（polystyrene block poly for vinyl purine penedes LPH phenol）出发，制备有序金属纳米泡沫。该目标的实现分为两个步骤：首先，选择合适的体系参数，以在超分子复合物中形成双螺旋陀螺（double gyro）形貌；第二步，选择性地去除复合物中的一个组分，即戊二烯酸苯酚（penad sylph phenol），该组分构成了陀螺结构基质的一部分。接下来，通过电沉积工艺用镍填充多孔模板。最后一步是通过在350摄氏度下进行热解去除剩余的聚合物。最终，利用嵌段共聚物模板导向合成法制备出具有反向螺旋形态的高度有序纳米多孔金属泡沫。因此，与现有方法相比，该技术的主要优势在于，我们能够以一种直接的方式在阻聚物中获得双 Gyroid（GY）形貌。随后，一旦获得双涡旋形貌，便可将样品浸入乙醇中，从而以非常简单的方式去除两亲性嵌段共聚物（amphiphilic pandaol）。接着，在形成多孔结构后，通过化学镀法将金属沉积到复杂的 PO 通道结构中，最终得到金属纳米泡沫。该方法提供了一种直观的方式，可从多种金属制备有序的纳米多孔网络。首先将聚苯乙烯-聚乙烯基嘌呤-苯酚嵌段共聚物溶解于氯仿中，并在室温下搅拌数小时。将溶液倒入玻璃培养皿中，然后将培养皿置于饱和氯仿气氛中。大约一周后，将培养皿从饱和氯仿气氛中取出。在30摄氏度下真空干燥超分子复合物薄膜过夜。从烘箱中取出薄膜后，将其放入特制的容器中。然后在操作结束后将容器中的空气抽净，并充入氮气。将薄膜置于烘箱中，在氮气氛围下、1 bar 正压条件下于 120 摄氏度下退火四天。退火过程完成后，切下一小块薄膜并将其包埋在环氧树脂中。然后在 40 摄氏度下过夜固化样品。在室温下使用金刚石刀片用切片机将样品切成约 80 纳米的厚度。将切好的超薄切片置于铜网上。转移后，将含有切片的载网放入盛有碘液的染色缸中。45分钟后，取出染色的样品。为透射电镜观察做准备，将带有染色切片的铜网插入透射电子显微镜中。在120千伏的加速电压下操作并成像样品。然后将一片跪式薄膜插入用于袋子的样品 holder 中，并用胶带上的盖子固定。将制备好的样品 holder 放入仪器中。打开X射线快门，采集二维散射图样。此时，将另一小块跪压薄膜浸入乙醇中，持续三天。待多孔薄膜干燥后，将其浸入氯化亚锡水溶液中一小时。从溶液中取出薄膜后，用去离子水彻底冲洗。接着，将薄膜浸入氯化钯水溶液中。一小时后，将薄膜从溶液中取出，并用去离子水冲洗。配制镀镍液时，按四比一的比例将六水合硫酸镍溶液与Bo二甲胺络合物溶液混合，并用氨水调节pH至7。将薄膜浸入镀镍液中，反应1小时。用去离子水冲洗后，置于通风橱中干燥。按照先前所述方法制备用于电子显微镜观察的镀膜样品，然后在相同条件下进行成像。随后，将镍镀膜置于350摄氏度的烘箱中加热一小时至四天。待薄膜冷却至室温后，使用银浆将其固定在样品台上。然后将样品台插入扫描电子显微镜中。采集扫描电镜图像并进行能谱分析。双波与车轮状结构。陀螺图案分别表示通过陀螺单晶胞的 2 1 1 和 1 1 1 平面的投影。聚苯乙烯嵌段区域呈亮色，而聚。四个乙烯基嘌呤戊基酚嵌段区域因碘染色而呈现深色。对另一样品的双波纹图案进行染色，显示出周期性减小的萨克斯峰，位于六分之Q星的平方根、八分之Q星的平方根、十四分之Q星的平方根、二十二分之Q星的平方根以及五十分之Q星的平方根处。经乙醇处理后，确认其为双连续IA 3D形貌。青霉酰基苯酚质子核磁共振信号缺失。DSC 数据表明，经乙醇处理的样品与 DI 嵌段共聚物的热行为相同。多孔陀螺模板具有 104 平方米每克的高 BET 比表面积，占据近 60 体积百分比。平均孔径为40纳米，孔径分布较窄。未染色的镍板gyro的透射电镜图像对比度来源于纳米通道中沉积的金属。车轮状图案证实了双gyro形态得以保留。高分辨率透射电子显微图像显示了大面积相互连接的镍晶粒，EDX分析揭示了镀层样品的化学成分。观察到碳、镍和氧的峰，表明镍纳米泡沫在空气中储存时发生了氧化。在等温加热导致聚合物分解的过程中，镍网络保持完整。暴露的镍复制品保留了反向螺旋形态，这一点已通过扫描电镜（SEM）证实。利用我们刚刚展示的方法，我们成功制备并表征了高度有序的金属纳米泡沫材料。这些高度有序的金属纳米泡沫有望被用作驱动器。该方法为研究有序与无序多孔纳米金属在行为上的差异开辟了路径。请注意，使用电极和金属电镀过程中所涉及的化学品可能具有极高危险性，在执行该操作时应始终佩戴个人防护装备。

gyroid-nickel-nanostructures-from-diblock-copolymer-supramolecules

Research

科研

JoVE Journal

Chemistry

化学

Gyroid镍纳米结构的嵌段共聚物超分子

本文概述了一种简单且通用的手动肽拟态物合成方法，该方法仅需基本设备和市售试剂，可在大多数实验室中轻松实现肽拟态物的合成。文中详细描述了由36个单体组成的两亲性肽拟态物的合成、纯化与表征过程，并阐述了其自组装形成高度有序纳米片的特性。...

固相亚单体合成肽模拟物聚合物及其自组装形成高度有序纳米片

本文介绍了一种利用嵌段共聚物合成聚合物纳米颗粒的纳米沉淀方法。我们将讨论嵌段共聚物的合成、纳米沉淀技术及其潜在应用。...

通过纳米沉淀法制备双嵌段聚合物纳米颗粒

本实验的目的是确定并控制水溶液中自组装盘状两亲分子的尺寸、形状和稳定性。对于基于水相的超分子聚合物而言，实现这种程度的控制非常困难。我们采用了一种同时利用排斥作用和吸引作用的策略。用于表征该系统的实验技术具有广泛的适用性。...

控制超分子聚合物在水中的尺寸、形状与稳定性

飞秒激光直写技术常用于在聚合物和玻璃中创建三维（3D）结构。然而，金属的三维微纳加工仍具挑战性。本文介绍一种利用中心波长为800...

一种在三维空间中制备分离银纳米结构的方法

我们描述了从二维（2D）前驱体合成具有图案化和可重构结构微粒的实验细节。该方法可用于在微米至厘米尺度范围内制备多种形状的微粒，包括多面体结构和抓取装置。...

受折纸启发的图案化与可重构颗粒自组装

本文描述了通过自组装这一自发过程形成高度有序的肽基结构的方法。该方法利用 commercially available peptides...

短肽自组装形成有序生物分子结构

我们报道了将多种类型的聚合物包覆金属纳米颗粒“聚合”成长链“均聚物”和“共聚物”的实验方案。...

使用聚苯乙烯-嵌段-聚丙烯酸包覆的金属纳米粒子作为单体进行均聚和共聚

本文介绍了一种用于制备和观察螺旋状聚碳二亚胺衍生的二级结构（例如，纤维、环状结构和纳米球）的实验方案。通过原子力显微镜（AFM）和扫描电子显微镜（SEM）表征的形貌表明，其形态依赖于分子结构、浓度以及所选溶剂。...

由螺旋聚碳二亚胺共聚物及其三唑衍生物获得的自组装形貌

在此，我们介绍一种用于制备三维石墨烯基多面体的实验方案 通过...

三维石墨烯基多面体的制备 通过 折纸式自折叠

结晶驱动的自组装（CDSA）具有独特的能力，可制备长度分布窄的圆柱形纳米结构。本文展示了有机催化下ε-己内酯的开环聚合，以及甲基丙烯酸甲酯和N,N-二甲基丙烯酰胺的后续链延伸反应。文中概述了一种活性CDSA方案，可生成长度达500...

通过可生物降解嵌段共聚物的结晶驱动自组装合成单分散柱状纳米粒子

溶液法与表面辅助合成相结合，为纳米结构的原子级精确合成开辟了新的方向。扫描隧道显微镜（STM）结合非接触原子力显微镜（nc-AFM），可对新设计和生成的碳基纳米结构进行详细表征。...

通过溶液法与表面化学相结合合成多孔纳米石墨烯的显微可视化

学习利用嵌段共聚物超分子模板制备有序镍纳米泡沫的方法。通过无电沉积和热解技术，研究人员成功构建了具有双螺旋反转结构的纳米多孔金属材料。

由二嵌段共聚物超分子制备的陀螺镍纳米结构

探索更多视频