Name: Impresión 3D y modificación de superficies in situ mediante polimerización de transferencia de cadena de adición reversible-fragmentación fotoiniciada tipo I (Video) | JoVE Journal
Uploaded: 2022-02-18T14:45:00.000+00:00
Duration: 7 min 28 s
Description: Aprende a ajustar independientemente las propiedades volumétricas e interfaciales de materiales impresos en 3D mediante polimerización RAFT fotoiniciada tipo I. Esta técnica simplifica la fabricación de estructuras complejas usando equipos comerciales.

ai_agent_IP

ai_agent

maintenance

instantTrialDurationMinutes

isBiopharma

enableNewMyJoveSectionDesign

educationFeatures

seoMetaApi

ai_copilot_institution_blacklist

ai_chat_institution_blacklist

freeAccessWindow

ssoRoleCapture

scheduledMaintenanceBanner

joveLabsFeatures

disable_autoplay_for_bots

extended_trial_duration

5 minutes

Los autores reconocen la financiación del Consejo Australiano de Investigación y UNSW Australia a través del programa Discovery Research (DP210100094).

1. Preparación del programa de impresión 3D y la impresora 3D
<ol><li>Diseñe el modelo digital para impresión 3D siguiendo los pasos a continuación.<ol>
<li>Abra un programa de diseño asistido por ordenador (consulte la Tabla de materiales).</li>
		<li>En el plano x-y, cree un rectángulo centrado en el origen que tenga dimensiones de 80 mm x 40 mm, luego extruya a lo largo del eje z positivo durante 1,5 mm para hacer un prisma rectangular sólido, llamado objeto base.</li>
		<li>Sobre el objeto base, es decir, a z = 1,5 mm, dibuje los patrones de superficie deseados (en este caso, dos símbolos yin-yang) en la superficie del prisma rectangular.</li>
		<li>Extruya los patrones de superficie en regiones seleccionadas de 0,05 mm a lo largo del eje z positivo para crear un patrón ligeramente elevado en relación con el objeto base.</li>
		<li>Exporte el modelo 3D para proporcionar un archivo de estereolitografía con . Extensión de archivo STL. NOTA: En este trabajo se diseñaron ejemplares en forma de hueso de perro27. Para imprimir otros modelos deseados, siga los pasos 1.1.1-1.1.5.</li>
		<li>Abra un programa de corte de impresora 3D (consulte Tabla de materiales) para habilitar la configuración de una sola capa.</li>
		<li>Abra el archivo . STL desde el disco duro de la computadora haciendo clic en Archivo > Abrir y luego navegando a la . Archivo STL.</li>
		<li>Organice los modelos 3D en la plataforma de construcción utilizando los botones "Rotación del modelo" y "Movimiento del modelo" para que quepan al menos 1 mm entre todos los objetos en la etapa de construcción.</li>
		<li>Al introducir texto en los cuadros de campo de entrada del panel de la derecha, cambie los parámetros mencionados en la Tabla 1.</li>
		<li>Haga clic en el botón azul Slice en la esquina inferior izquierda y guárdelo como un archivo slice con una extensión de. PWS u otro archivo en rodajas legible por impresora 3D.</li>
		<li>Haga clic en el botón Vista previa una vez que aparezca el menú emergente y navegue por las capas cortadas utilizando la barra de desplazamiento en el lado derecho. Tome nota cuidadosa de los números de capa para la última capa base (capa 29 en este caso) y la capa de patrón de superficie (30 en este caso). NOTA: La primera capa impresa es "capa 0" no "capa 1".</li>
		<li>En el panel de la derecha, seleccione Configuración de una sola capa y, a continuación, expanda el menú desplegable.</li>
		<li>Cambie el "Tiempo de exposición (s)" solo para la capa superficial (capa 30) a 180 s, dejando todos los demás tiempos de exposición de la capa como el valor predeterminado.</li>
		<li>Haga clic en el botón Guardar en la esquina superior izquierda para guardar el archivo cortado en un USB.</li>
	</ol>
</li>
	<li>Prepare la impresora 3D.<ol>
<li>Inserte el USB que contiene el archivo cortado en la impresora 3D (consulte la Tabla de materiales).</li>
		<li>Antes de la impresión 3D, nivele la etapa de construcción y calibre la posición del eje z a z = 0 siguiendo el método específico de la impresora 3D (calibración manual o automática siguiendo el manual de la impresora 3D).</li>
		<li>Inspeccione la película de la cuba de la impresora 3D para garantizar una superficie lisa y limpia libre de defectos.</li>
		<li>Si la película de la cuba parece dañada, reemplácela de acuerdo con el protocolo del fabricante.</li>
	</ol>
</li>
</ol>2. Preparación de resinas
NOTA: Las resinas se clasifican como "Resina a granel" para la resina utilizada para imprimir en 3D el material original (sustrato base) y "Resina de superficie" para la solución utilizada para realizar la funcionalización de la superficie (patrón de superficie).
<ol><li>Preparar la resina a granel.<ol>
<li>Para preparar la resina a granel, pese 0,36 g de ácido propanoico (BTPA) 2-(n-butiltiocarbonotioiltio) en un vial ámbar limpio de 50 ml.</li>
		<li>Añadir 13,63 ml de diacrilato de poli (etilenglicol) promedio Mn 250 (PEGDA) al vial de ámbar utilizando una micropipeta.</li>
		<li>Añadir 14,94 ml de N, N-dimetilacrilamida (DMAm) al vial de ámbar utilizando una micropipeta.</li>
		<li>En un vial separado de vidrio limpio de 20 ml cubierto con papel de aluminio, agregue 0.53 g de óxido de fosfina (TPO) de difenilo (2,4,6-trimetil benzoil).</li>
		<li>Usando una micropipeta, agregue 10 ml de DMAm al vial de vidrio de 20 ml que contiene el TPO y selle el vial con la tapa.</li>
		<li>Homogeneice completamente la solución de TPO y DMAm mezclando usando un mezclador de vórtice durante 10 s y luego usando un baño sónico de laboratorio estándar (~ 40 kHz) para sonicar la mezcla durante 1 minuto a temperatura ambiente (Figura 1C, izquierda).</li>
		<li>Usando una pipeta de vidrio y una bombilla de pipeta de goma, transfiera la solución del vial de vidrio de 20 ml al vial de ámbar de 50 ml y selle el vial con una tapa y una película de plástico moldeable.</li>
		<li>Agite suavemente el vial de ámbar de 50 ml y luego coloque el vial en un baño sónico durante 2 minutos a temperatura ambiente para asegurarse de que la mezcla sea homogénea (Figura 1C, segundo desde la izquierda).</li>
		<li>Coloque el vial ámbar sellado lleno de resina a granel en una campana extractora de humos para su uso posterior.</li>
	</ol>
</li>
	<li>Preparar la resina superficial.<ol>
<li>Para preparar la resina superficial, pese 0,50 g de TPO en un vial ámbar limpio de 50 ml.</li>
		<li>Usando una micropipeta, agregue 3.56 mL de DMAm y 11.98 mL de N, N-dimetilformamida (DMF) al vial de ámbar de 50 mL y selle el vial con una película plástica moldeable de tapa. </li>
		<li>Agite suavemente el vial de ámbar sellado y sonice durante 1 minuto a temperatura ambiente utilizando un baño sónico de laboratorio estándar (~ 40 kHz).</li>
		<li>A un vial limpio de 20 ml cubierto con papel de aluminio, agregue 0,29 g de metacrilato de 1-pirenometil (PyMMA).</li>
		<li>Agregue 10 ml de DMF al vial de 20 ml y selle el vial con una tapa con una micropipeta.</li>
		<li>Agite suavemente el vial de vidrio de 20 ml y sonice en incrementos de 1 min a temperatura ambiente utilizando un baño sónico de laboratorio estándar, inspeccionando visualmente entre ciclos hasta que el PyMMA parezca estar disuelto por completo (Figura 1C, tercero y cuarto desde la izquierda).</li>
		<li>Usando una pipeta de vidrio y una bombilla de pipeta de goma, transfiera la solución del vial de vidrio de 20 ml al vial de ámbar de 50 ml.</li>
		<li>Agite suavemente el vial de ámbar de 50 ml y luego coloque el vial en un baño sónico durante 2 minutos a temperatura ambiente para asegurarse de que la mezcla sea homogénea (Figura 1C, derecha y segunda desde la derecha).</li>
		<li>Coloque el vial ámbar sellado lleno de resina a granel en una campana extractora de humos para su uso posterior. PRECAUCIÓN: Algunos productos químicos utilizados en este protocolo pueden causar irritación severa de la piel y los ojos y otra toxicidad para los seres humanos y el medio ambiente. Asegúrese de que se sigan los protocolos de seguridad de acuerdo con la hoja de datos de seguridad y las regulaciones locales.</li>
	</ol>
</li>
</ol>3.3D impresión y funcionalización de superficies
<ol><li>Realice la impresión 3D del sustrato base siguiendo los pasos a continuación.<ol>
<li>Vierta la resina a granel previamente preparada (paso 2.1) en la cuba de la impresora 3D (consulte la Tabla de materiales), asegurándose de que la solución cubra completamente la película inferior en la cuba sin burbujas de aire u otras inhomogeneidades, y luego cierre la caja de la impresora 3D.</li>
		<li>Navegue por el USB utilizando la pantalla de la impresora 3D y seleccione el archivo de modelo cortado haciendo clic en el botón reproducir triangular para comenzar el proceso de impresión 3D.</li>
		<li>Al observar la pantalla de la impresora 3D, tome nota cuidadosamente del número de capas impresas y detenga el programa de impresión presionando el botón Pausa de dos líneas verticales durante la impresión 3D de la última capa del sustrato base (capa 29 en este caso).</li>
		<li>Retire toda la etapa de construcción y enjuague suavemente la etapa de construcción y el material impreso con etanol 100% sin desnaturalizar de una botella de lavado durante 10 s para eliminar la resina a granel residual del material impreso en 3D y la etapa de construcción.</li>
		<li>Con aire comprimido, seque suavemente el material impreso en 3D y cree la etapa para eliminar el etanol residual y luego vuelva a insertar la etapa de construcción en la impresora 3D.</li>
		<li>Retire la cuba de la impresora 3D y vierta la resina a granel restante en un vial de color ámbar. Guarde el vial en un lugar fresco y oscuro.</li>
		<li>Usando etanol 100% sin desnaturalizar de una botella de lavado, enjuague cuidadosamente la cuba para eliminar cualquier resina a granel residual.</li>
		<li>Seque la cuba con una corriente de aire comprimido para eliminar cualquier residuo de etanol y vuelva a insertar la cuba en la impresora 3D.</li>
	</ol>
</li>
	<li>Realizar la funcionalización de la superficie.<ol>
<li>Vierta la resina de superficie previamente preparada (paso 2.2) en la cuba de la impresora 3D, asegurándose de que la solución cubra completamente la película inferior sin burbujas de aire u otras inhomogeneidades, y luego cierre la caja de la impresora 3D.</li>
		<li>Reanude el programa de impresión 3D haciendo clic en el botón Reproducir del triángulo para permitir que se produzca el patrón de superficie predeterminado.</li>
		<li>Una vez que se haya completado el programa de impresión, retire la etapa de construcción de la impresora 3D y lávela durante 10 s con etanol 100% sin desnaturalizar utilizando una botella de lavado para eliminar la resina superficial residual del material impreso en 3D y la etapa de construcción.</li>
		<li>Usando aire comprimido (caudal, 30 L/min), seque suavemente el material impreso en 3D y cree la etapa para eliminar el etanol residual.</li>
		<li>Mientras aún está unido a la etapa de construcción, cure el material invirtiendo toda la etapa de construcción y colocándolo bajo una luz de 405 nm durante 15 minutos.</li>
		<li>Retire suavemente el material impreso en 3D funcionalizado de la superficie de la etapa de construcción con una placa de metal delgada o un raspador de pintura.</li>
		<li>Sin más ajustes, analice las propiedades mecánicas y superficiales del material.</li>
	</ol>
</li>
</ol>4. Análisis de muestras impresas en 3D
<ol><li>Realizar el análisis de fluorescencia.<ol>
<li>Coloque el material funcionalizado de la superficie impreso en 3D debajo de una lámpara de descarga de gas UV de 312 nm (consulte la Tabla de materiales) en un lugar oscuro, asegurándose de que la capa funcionalizada de la superficie esté hacia arriba.</li>
		<li>Encienda la lámpara para irradiar continuamente la capa superficial con luz de 312 nm y observe el patrón fluorescente. Tome fotografías si es necesario. NOTA: Este es un paso de inspección visual; no se puede especificar la hora. La irradiación es continua mientras se produce la observación.</li>
		<li>Coloque el material funcionalizado de superficie impreso en 3D en un generador de imágenes de fluorescencia. Utilizando el software proporcionado, capture imágenes digitales de fluorescencia de las superficies superior e inferior utilizando la fuente de descarga de gas Trans-UV (302 nm) (consulte la Tabla de materiales).</li>
	</ol>
</li>
	<li>Realice el análisis de la propiedad de tracción.<ol>
<li>Mida el calibre con y el grosor de los especímenes de hueso de perro (en milímetros).</li>
		<li>Coloque las muestras en forma de hueso de perro entre las empuñaduras de una máquina de prueba de tracción, asegurando que el material impreso en 3D se coloque igualmente a una distancia especificada por el documento de estándares, en este caso, 50.3 mm.</li>
		<li>Establezca el programa de prueba de tracción; en este caso, la velocidad de elevación se estableció en 1,1 mm/min, el número de muestras se estableció en 10 por segundo.</li>
		<li>Inicie el programa para adquirir datos de fuerza (N) frente a datos de viaje (mm).</li>
		<li>Una vez que la muestra se prepara, detenga la máquina y guarde los datos como datos separados por columnas con un archivo . Extensión de archivo CSV.</li>
		<li>Convierta los datos de fuerza (N) en tensión (MPa) dividiendo cada punto de la columna de fuerza por el área del medidor (mm2, obtenido multiplicando el ancho del medidor por el grosor del medidor).</li>
		<li>Convierta los datos de viaje en tensión (%) buceando los datos de viaje por la longitud del medidor (50,3 mm) en cada punto y multiplicando cada resultado por 100.</li>
		<li>Calcule la tenacidad (MJ/m3) utilizando la regla trapezoidal para calcular el área bajo la curva tensión-deformación.</li>
		<li>Calcular el módulo de Young (MPa) tomando el gradiente de la tensión (MPa) vs. curva de deformación (%) en la región elástica, en este trabajo de alargamiento del 1%-2%27.</li>
	</ol>
</li>
</ol>

<ol><li>Ligon, S. C., Liska, R., Stampfl, J., Gurr, M., Mülhaupt, R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Polymers+for+3D+printing+and+customized+additive+manufacturing%5BTitle%5D)+AND+%22Chemical+Reviews%22%5BJournal%5D)">Polymers for 3D printing and customized additive manufacturing.</a> Chemical Reviews. 117 (15), 10212-10290 (2017).</li>
<li>Lewis, J. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Direct+ink+writing+of+3D+functional+materials%5BTitle%5D)+AND+%22Advanced+Functional+Materials%22%5BJournal%5D)">Direct ink writing of 3D functional materials.</a> Advanced Functional Materials. 16 (17), 2193-2204 (2006).</li>
<li>Kumar, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Selective+laser+sintering%3A+A+qualitative+and+objective+approach%5BTitle%5D)+AND+%22JOM%22%5BJournal%5D)">Selective laser sintering: A qualitative and objective approach.</a> JOM. 55 (10), 43-47 (2003).</li>
<li>Jung, K., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Designing+with+light%3A+Advanced+2D%2C+3D%2C+and+4D+materials%5BTitle%5D)+AND+%22Advanced+Materials%22%5BJournal%5D)">Designing with light: Advanced 2D, 3D, and 4D materials.</a> Advanced Materials. 32 (18), 1903850(2020).</li>
<li>Lim, K. S., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Fundamentals+and+applications+of+photo-cross-linking+in+bioprinting%5BTitle%5D)+AND+%22Chemical+Reviews%22%5BJournal%5D)">Fundamentals and applications of photo-cross-linking in bioprinting.</a> Chemical Reviews. 120 (19), 10662-10694 (2020).</li>
<li>Chen, H., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Photoinitiators+derived+from+natural+product+scaffolds%3A+Monochalcones+in+three-component+photoinitiating+systems+and+their+applications+in+3D+printing%5BTitle%5D)+AND+%22Polymer+Chemistry%22%5BJournal%5D)">Photoinitiators derived from natural product scaffolds: Monochalcones in three-component photoinitiating systems and their applications in 3D printing.</a> Polymer Chemistry. 11 (28), 4647-4659 (2020).</li>
<li>Chen, H., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Novel+D-%CF%80-A+and+A-%CF%80-D-%CF%80-A+three-component+photoinitiating+systems+based+on+carbazole%2Ftriphenylamino+based+chalcones+and+application+in+3D+and+4D+printing%5BTitle%5D)+AND+%22Polymer+Chemistry%22%5BJournal%5D)">Novel D-π-A and A-π-D-π-A three-component photoinitiating systems based on carbazole/triphenylamino based chalcones and application in 3D and 4D printing.</a> Polymer Chemistry. 11 (40), 6512-6528 (2020).</li>
<li>Zhang, J., Xiao, P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((3D+printing+of+photopolymers%5BTitle%5D)+AND+%22Polymer+Chemistry%22%5BJournal%5D)">3D printing of photopolymers.</a> Polymer Chemistry. 9 (13), 1530-1540 (2018).</li>
<li>Zhu, Y., Ramadani, E., Egap, E. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Thiol+ligand+capped+quantum+dot+as+an+efficient+and+oxygen+tolerance+photoinitiator+for+aqueous+phase+radical+polymerization+and+3D+printing+under+visible+light%5BTitle%5D)+AND+%22Polymer+Chemistry%22%5BJournal%5D)">Thiol ligand capped quantum dot as an efficient and oxygen tolerance photoinitiator for aqueous phase radical polymerization and 3D printing under visible light.</a> Polymer Chemistry. 12 (35), 5106-5116 (2021).</li>
<li>Jiang, P., Ji, Z., Wang, X., Zhou, F. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Surface+functionalization+-+a+new+functional+dimension+added+to+3D+printing%5BTitle%5D)+AND+%22Journal+of+Materials+Chemistry+C%22%5BJournal%5D)">Surface functionalization - a new functional dimension added to 3D printing.</a> Journal of Materials Chemistry C. 8 (36), 12380-12411 (2020).</li>
<li>Gonzalez, G., Chiappone, A., Dietliker, K., Pirri, C. F., Roppolo, I. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Fabrication+and+functionalization+of+3D+printed+polydimethylsiloxane-based+microfluidic+devices+obtained+through+digital+light+processing%5BTitle%5D)+AND+%22Advanced+Materials+Technologies%22%5BJournal%5D)">Fabrication and functionalization of 3D printed polydimethylsiloxane-based microfluidic devices obtained through digital light processing.</a> Advanced Materials Technologies. 5 (9), 2000374(2020).</li>
<li>Yao, X., Song, Y., Jiang, L. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Applications+of+bio-inspired+special+wettable+surfaces%5BTitle%5D)+AND+%22Advanced+Materials%22%5BJournal%5D)">Applications of bio-inspired special wettable surfaces.</a> Advanced Materials. 23 (6), 719-734 (2011).</li>
<li>Bose, S., Robertson, S. F., Bandyopadhyay, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Surface+modification+of+biomaterials+and+biomedical+devices+using+additive+manufacturing%5BTitle%5D)+AND+%22Acta+Biomaterialia%22%5BJournal%5D)">Surface modification of biomaterials and biomedical devices using additive manufacturing.</a> Acta Biomaterialia. 66, 6-22 (2018).</li>
<li>Wang, X., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((i3DP%2C+a+robust+3D+printing+approach+enabling+genetic+post-printing+surface+modification%5BTitle%5D)+AND+%22Chemical+Communications%22%5BJournal%5D)">i3DP, a robust 3D printing approach enabling genetic post-printing surface modification.</a> Chemical Communications. 49 (86), 10064-10066 (2013).</li>
<li>Lee, K., Corrigan, N., Boyer, C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Rapid+high-resolution+3D+printing+and+surface+functionalization+via+type+I+photoinitiated+raft+polymerization%5BTitle%5D)+AND+%22Angewandte+Chemie+International+Edition%22%5BJournal%5D)">Rapid high-resolution 3D printing and surface functionalization via type I photoinitiated raft polymerization.</a> Angewandte Chemie International Edition. 60 (16), 8839-8850 (2021).</li>
<li>Zhang, Z., Corrigan, N., Bagheri, A., Jin, J., Boyer, C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((A+versatile+3D+and+4D+printing+system+through+photocontrolled+raft+polymerization%5BTitle%5D)+AND+%22Angewandte+Chemie+International+Edition%22%5BJournal%5D)">A versatile 3D and 4D printing system through photocontrolled raft polymerization.</a> Angewandte Chemie International Edition. 58 (50), 17954-17963 (2019).</li>
<li>Corrigan, N., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Reversible-deactivation+radical+polymerization+%28controlled%2Fliving+radical+polymerization%29%3A+From+discovery+to+materials+design+and+applications%5BTitle%5D)+AND+%22Progress+in+Polymer+Science%22%5BJournal%5D)">Reversible-deactivation radical polymerization (controlled/living radical polymerization): From discovery to materials design and applications.</a> Progress in Polymer Science. 111, 101311(2020).</li>
<li>Moad, G., Rizzardo, E., Thang, S. H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Living+radical+polymerization+by+the+raft+process+-+A+third+update%5BTitle%5D)+AND+%22Australian+Journal+of+Chemistry%22%5BJournal%5D)">Living radical polymerization by the raft process - A third update.</a> Australian Journal of Chemistry. 65 (8), 985-1076 (2012).</li>
<li>Chiefari, J., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Living+free-radical+polymerization+by+reversible+addition%E2%88%92Fragmentation+chain+transfer%3A+The+RAFT+process%5BTitle%5D)+AND+%22Macromolecules%22%5BJournal%5D)">Living free-radical polymerization by reversible addition−Fragmentation chain transfer: The RAFT process.</a> Macromolecules. 31 (16), 5559-5562 (1998).</li>
<li>Fromel, M., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((User-friendly+chemical+patterning+with+digital+light+projection+polymer+brush+photolithography%5BTitle%5D)+AND+%22European+Polymer+Journal%22%5BJournal%5D)">User-friendly chemical patterning with digital light projection polymer brush photolithography.</a> European Polymer Journal. 158, 110652(2021).</li>
<li>Fromel, M., Li, M., Pester, C. W. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Surface+engineering+with+polymer+brush+photolithography%5BTitle%5D)+AND+%22Macromolecular+Rapid+Communications%22%5BJournal%5D)">Surface engineering with polymer brush photolithography.</a> Macromolecular Rapid Communications. 41 (18), 2000177(2020).</li>
<li>Wang, C. -G., Chen, C., Sakakibara, K., Tsujii, Y., Goto, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Facile+fabrication+of+concentrated+polymer+brushes+with+complex+patterning+by+photocontrolled+organocatalyzed+living+radical+polymerization%5BTitle%5D)+AND+%22Angewandte+Chemie+International+Edition%22%5BJournal%5D)">Facile fabrication of concentrated polymer brushes with complex patterning by photocontrolled organocatalyzed living radical polymerization.</a> Angewandte Chemie International Edition. 57 (41), 13504-13508 (2018).</li>
<li>Zoppe, J. O., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Surface-initiated+controlled+radical+polymerization%3A+state-of-the-art%2C+opportunities%2C+and+challenges+in+surface+and+interface+engineering+with+polymer+brushes%5BTitle%5D)+AND+%22Chemical+Reviews%22%5BJournal%5D)">Surface-initiated controlled radical polymerization: state-of-the-art, opportunities, and challenges in surface and interface engineering with polymer brushes.</a> Chemical Reviews. 117 (3), 1105(2017).</li>
<li>Pester, C. W., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Ambiguous+antifouling+surfaces%3A+Facile+synthesis+by+light-mediated+radical+polymerization%5BTitle%5D)+AND+%22Journal+of+Polymer+Science+Part+A%3A+Polymer+Chemistry%22%5BJournal%5D)">Ambiguous antifouling surfaces: Facile synthesis by light-mediated radical polymerization.</a> Journal of Polymer Science Part A: Polymer Chemistry. 54 (2), 253-262 (2016).</li>
<li>Poelma, J. E., Fors, B. P., Meyers, G. F., Kramer, J. W., Hawker, C. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Fabrication+of+complex+three-dimensional+polymer+brush+nanostructures+through+light-mediated+living+radical+polymerization%5BTitle%5D)+AND+%22Angewandte+Chemie+International+Edition%22%5BJournal%5D)">Fabrication of complex three-dimensional polymer brush nanostructures through light-mediated living radical polymerization.</a> Angewandte Chemie International Edition. 52 (27), 6844-6848 (2013).</li>
<li>Zhu, Y., Egap, E. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((PET-RAFT+polymerization+catalyzed+by+cadmium+selenide+quantum+dots+%28QDs%29%3A+Grafting-from+QDs+photocatalysts+to+make+polymer+nanocomposites%5BTitle%5D)+AND+%22Polymer+Chemistry%22%5BJournal%5D)">PET-RAFT polymerization catalyzed by cadmium selenide quantum dots (QDs): Grafting-from QDs photocatalysts to make polymer nanocomposites.</a> Polymer Chemistry. 11 (5), 1018-1024 (2020).</li>
<li>ASTM International. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((ASTM+Standard+D638-14%3A+Standard+Test+method+for+tensile+properties+of+plastics%5BTitle%5D)+AND+%22ASTM+International%22%5BJournal%5D)">ASTM Standard D638-14: Standard Test method for tensile properties of plastics.</a> ASTM International. , (2014).</li>
<li>Moad, G. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((RAFT+%28Reversible+addition-fragmentation+chain+transfer%29+crosslinking+%28co%29polymerization+of+multi-olefinic+monomers+to+form+polymer+networks%5BTitle%5D)+AND+%22Polymer+International%22%5BJournal%5D)">RAFT (Reversible addition-fragmentation chain transfer) crosslinking (co)polymerization of multi-olefinic monomers to form polymer networks.</a> Polymer International. 64 (1), 15-24 (2015).</li>
<li>Li, M., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((SI-PET-RAFT%3A+Surface-initiated+photoinduced+electron+transfer-reversible+addition-fragmentation+chain+transfer+polymerization%5BTitle%5D)+AND+%22ACS+Macro+Letters%22%5BJournal%5D)">SI-PET-RAFT: Surface-initiated photoinduced electron transfer-reversible addition-fragmentation chain transfer polymerization.</a> ACS Macro Letters. 8 (4), 374-380 (2019).</li>
</ol>

Los autores declaran que no hay conflictos de intereses.

El presente protocolo demuestra un proceso para la impresión 3D de materiales poliméricos con propiedades a granel e interfaciales sintonizables de forma independiente. El procedimiento se realiza a través de un método de dos pasos mediante la impresión 3D del sustrato base y posteriormente la modificación de la capa superficial del objeto impreso en 3D utilizando una resina funcional diferente pero utilizando el mismo hardware de impresión 3D. Si bien las impresoras 3D utilizadas en este trabajo están diseñadas...

La fabricación aditiva y la impresión 3D han revolucionado la fabricación de materiales al proporcionar rutas más eficientes y fáciles para la fabricación de materiales geométricamente complejos1. Además de las libertades de diseño mejoradas en la impresión 3D, estas tecnologías producen menos residuos que los procesos de fabricación sustractivos tradicionales a través del uso juicioso de materiales precursores en un proceso de fabricación capa por capa. Desde la década de 1980, se ha desarrollado una amplia gama de diferentes técnicas de impresión 3D para fabricar componentes poliméricos, metálicos y cerámicos1. Los métodos más comúnmente empleados incluyen la impresión 3D basada en extrusión, como la fabricación de filamentos fundidos y las técnicas de escritura directa con tinta2, las técnicas de sinterización como la sinterización selectiva por láser3, así como las técnicas de impresión 3D fotoinducida a base de resina, como la estereolitografía basada en láser y proyección y las técnicas de procesamiento de luz digital enmascarada4 . Entre las muchas técnicas de impresión 3D que existen hoy en día, las técnicas de impresión 3D fotoinducidas proporcionan algunas ventajas en comparación con otros métodos, incluida una mayor resolución y velocidades de impresión más rápidas, así como la capacidad de realizar la solidificación de la resina líquida a temperatura ambiente, lo que abre la posibilidad de una impresión 3D de biomateriales avanzados4,5,6,7,8, 9.
Si bien estas ventajas han permitido la adopción generalizada de la impresión 3D en muchos campos, la capacidad limitada de adaptar de forma independiente las propiedades del material impreso en 3D restringe las aplicaciones futuras10. En particular, la incapacidad de adaptar fácilmente las propiedades mecánicas a granel independientemente de las propiedades interfaciales limita las aplicaciones como los implantes, que requieren superficies biocompatibles finamente adaptadas y, a menudo, propiedades a granel muy diferentes, así como superficies antiincrustantes y antibacterianas, materiales de sensores y otros materiales inteligentes11,12,13 . Los investigadores han propuesto la modificación de la superficie de los materiales impresos en 3D para superar estos problemas y proporcionar propiedades a granel e interfaciales más personalizables de forma independiente10,14,15.
Recientemente, nuestro grupo desarrolló un proceso de impresión 3D fotoinducido que explota la polimerización reversible de transferencia de cadena de adición-fragmentación (RAFT) para mediar la síntesis de polímeros en red15,16. La polimerización RAFT es un tipo de polimerización radical de desactivación reversible que proporciona un alto grado de control sobre el proceso de polimerización y permite la producción de materiales macromoleculares con pesos moleculares y topologías finamente afinados, y un amplio alcance químico17,18,19. En particular, los compuestos tiocarboniltio, o agentes RAFT, utilizados durante la polimerización RAFT se conservan después de la polimerización. Por lo tanto, pueden reactivarse para modificar aún más las propiedades químicas y físicas del material macromolecular. Por lo tanto, después de la impresión 3D, estos agentes RAFT inactivos en las superficies del material impreso en 3D se pueden reactivar en presencia de monómeros funcionales para proporcionar superficies de material a medida20,21,22,23,24,25,26. La polimerización de la superficie secundaria dicta las propiedades del material interfacial y se puede realizar de manera espacialmente controlada a través de la iniciación fotoquímica.
El presente protocolo describe un método para la impresión 3D de materiales poliméricos a través de un proceso de polimerización RAFT fotoinducido y la posterior modificación de la superficie in situ para modular las propiedades interfaciales independientemente de las propiedades mecánicas del material a granel. En comparación con los enfoques anteriores de impresión 3D y modificación de superficies, el protocolo actual no requiere desoxigenación u otras condiciones estrictas y, por lo tanto, es altamente accesible para los no especialistas. Además, el uso de hardware de impresión 3D para realizar tanto la fabricación inicial del material como la postfuncionalización de la superficie proporciona un control espacial sobre las propiedades del material y se puede realizar sin la tediosa alineación de varias fotomáscaras diferentes para crear patrones complejos.

<table><tbody><tr><td>1-pirenemetil metacrilato</td><td>Sigma-Aldrich</td><td>765120</td><td></td></tr><tr><td>2-(n-butiltiocarbonotioiltio) ácido propanoico</td><td>Boro Molecular</td><td>BM1640</td><td></td></tr><tr><td>Impresora 3D</td><td>Photon</td><td>Mono S</td><td>intensidad de la luz en la superficie de la máscara digital = 0,81 mW cm-2</td></tr><tr><td>Software de corte de impresión 3D</td><td>Photon</td><td>Photon Photon Workshop V2.1.19</td><td></td></tr><tr><td>Baño ultrasónico de 40 kHz</td><td>Thermoline</td><td>UB-410</td><td></td></tr><tr>Tanque de <td>230142</td> de<td>aire comprimido</td><td>Coregas</td><td>que funciona a 130 kPa</td></tr><tr><td>Programa de diseño asistido por computadora SpaceClaim</td><td>SpaceClaim</td><td>Gerente de diseño V19.1</td><td></td></tr><tr><td>Óxido de difenilo (2,4,6-trimetilbenzoil) fosfina</td><td>Sigma-Aldrich 415952</td><td></td><td></td></tr><tr><td>Etanol sin desnaturalizar 100% AR</td><td>ChemSupply</td><td>EL043-2.5L-P</td><td></td></tr><tr><td>Botella de lavado de etanol</td><td>Rowe Scientific</td><td></td> AZLWGF541P <td></td></tr><tr><td>Fluorescence Imager</td><td>Bio-Rad</td><td>Gel Doc XR+</td><td>Utiliza una lámpara de descarga de gas de 302 nm como fuente de emisión</td></tr><tr><td>Medidor de potencia de intensidad lumínica</td><td>Newport</td><td>843-R</td><td></td></tr><tr><td>Probador mecánico</td><td>Mark&ndash; 10</td><td>ESM303</td><td>1 kN dinamómetro M5&ndash; 200</td></tr><tr><td>Película plástica moldeable</td><td>Parafilm</td><td>PM992</td><td></td></tr><tr><td>N,N-dimethlacrylamida</td><td>Sigma-Aldrich</td><td>274135</td><td></td></tr><tr><td>N,N-Dimetilformamida HPLC</td><td></td><td>ChemSupply LC1051-G4L</td><td></td></tr><tr><td>Diacrilato de poli(etilenglicol) promedio Mn 250</td><td>Sigma-Aldrich</td><td>475629</td><td></td></tr><tr><td>Lámpara Post Cure</td><td>Leoway</td><td>&lrm; B0869BY79P</td><td>60 W 405 nm</td></tr><tr><td>Documento de normas</td><td>ASTM</td><td>Norma ASTM D638-14</td><td></td></tr><tr><td>Máquina de ensayos de tracción</td><td>Mark-10</td><td></td><td></td></tr><tr><td>UV Light</td><td>Fisher Scientific</td><td>11-982-30</td><td>6 W Spectroline E-Series, Lámpara de descarga de gas</td></tr><tr><td>Mezclador de vórtice IKA Vortex 3</td><td>LabTek</td><td>3340000I</td><td></td></tr></tbody></table>

impresión 3d y modificación de superficies in situ mediante polimerización de transferencia de cadena de adición reversible-fragmentación fotoiniciada tipo i

3D Printing and In Situ Surface Modification via Type I Photoinitiated Reversible Addition-Fragmentation Chain Transfer Polymerization

La impresión 3D proporciona un acceso fácil a materiales geométricamente complejos. Sin embargo, estos materiales tienen propiedades a granel e interfaciales intrínsecamente vinculadas que dependen de la composición química de la resina. En el trabajo actual, los materiales impresos en 3D se post-funcionalizan utilizando el hardware de la impresora 3D a través de un proceso de polimerización secundario iniciado por la superficie, proporcionando así un control independiente sobre las propiedades del material a granel e interfacial. Este proceso comienza con la preparación de resinas líquidas, que contienen un monómero monofuncional, un monómero multifuncional de reticulación, una especie fotoquímicamente lábil que permite el inicio de la polimerización y, lo que es más importante, un compuesto tiocarboniltio que facilita la polimerización reversible de transferencia de cadena de adición-fragmentación (RAFT). El compuesto tiocarboniltio, conocido comúnmente como agente RAFT, media el proceso de polimerización del crecimiento de la cadena y proporciona materiales poliméricos con estructuras de red más homogéneas. La resina líquida se cura capa por capa utilizando una impresora 3D de procesamiento de luz digital disponible comercialmente para dar materiales tridimensionales con geometrías controladas espacialmente. La resina inicial se retira y se reemplaza con una nueva mezcla que contiene monómeros funcionales y especies fotoiniciantes. El material impreso en 3D se expone a la luz de la impresora 3D en presencia de la nueva mezcla de monómeros funcionales. Esto permite que la polimerización iniciada por la superficie fotoinducida ocurra a partir de los grupos de agentes RAFT latentes en la superficie del material impreso en 3D. Dada la flexibilidad química de ambas resinas, este proceso permite producir una amplia gama de materiales impresos en 3D con propiedades a granel e interfaciales personalizables.

El procedimiento general para la impresión 3D y la funcionalización de superficies se muestra en la Figura 1. En este protocolo, un polímero de red se sintetiza inicialmente a través de un proceso de polimerización RAFT fotoinducido15, utilizando una impresora 3D para fabricar un objeto en un proceso capa por capa (Figura 1A). La resina a granel utilizada para formar la red de polímeros contiene una especie iniciadora fotolábil (...

El presente protocolo describe la impresión 3D basada en el procesamiento digital de luz de materiales poliméricos utilizando la polimerización de transferencia de cadena de adición-fragmentación reversible fotoiniciada tipo I y la posterior postfuncionalización de material in situ a través de polimerización mediada por superficie. La impresión 3D fotoinducida proporciona a los materiales propiedades a granel e interfaciales adaptadas de forma independiente y controladas espacialmente.

Impresión 3D y modificación de superficies in situ mediante polimerización de transferencia de cadena de adición reversible-fragmentación fotoiniciada tipo I

3D printing provides facile access to geometrically complex materials. However, these materials have intrinsically linked bulk and interfacial properties ...

Este protocolo permite ajustar de forma independiente las propiedades a granel e interfaciales de los materiales impresos en 3D. Esto proporciona una mayor flexibilidad para diseñar y fabricar materiales complejos impresos en 3D. Esta técnica no requiere condiciones de reacción estrictas y se puede realizar utilizando equipos disponibles comercialmente.Como resultado, esta técnica hace que sea significativamente más fácil fabricar materiales complejos impresos en 3D. Para comenzar, prepare la resina a granel pesando 0,36 gramos de BTPA en un vial ámbar limpio de 50 mililitros. Añadir 13,63 mililitros de diacrilato de polietilenglicol y 14,94 mililitros de DMAm al vial de ámbar utilizando una micropipeta.En un vial de vidrio limpio separado de 20 mililitros cubierto con papel de aluminio, agregue 0.53 gramos de TPO. Usando una micropipeta, agregue 10 mililitros de DMAm al vial de vidrio de 20 mililitros que contiene el TPO y selle el vial con la tapa. Homogeneice completamente la solución de TPO en DMAm mezclando con un mezclador de vórtice durante 10 segundos y luego utilizando un baño sónico de laboratorio estándar para sonicar la mezcla durante 2 minutos a temperatura ambiente.Usando una pipeta de vidrio y una bombilla de pipeta de goma, transfiera la solución del vial de vidrio de 20 mililitros al vial de ámbar de 50 mililitros y selle el vial con una tapa y una película de plástico moldeable. Agite suavemente el vial de ámbar de 50 mililitros y luego coloque el vial en un baño sónico durante 2 minutos a temperatura ambiente para asegurarse de que la mezcla sea homogénea. Coloque el vial ámbar sellado lleno de resina a granel en una campana extractora de humos para su uso posterior.Prepare la resina superficial como se describió anteriormente para la preparación de la resina a granel. Después de preparar la resina superficial, coloque el vil ámbar sellado lleno de resina superficial en una campana extractora de humos para su uso posterior. Para realizar la impresión 3D, vierta la resina a granel previamente preparada en la cuba de la impresora 3D, asegurándose de que la solución cubra completamente la película inferior en la cuba sin burbujas de aire u otras inhomogeneidades, y luego cierre la caja de la impresora 3D.Navegue por el USB utilizando la pantalla de la impresora 3D y seleccione el archivo de modelo cortado haciendo clic en el botón reproducir triangular para comenzar el proceso de impresión 3D. Al observar la pantalla de la impresora 3D, tome nota cuidadosamente del número de capas impresas y detenga el programa de impresión presionando el botón Pausa de dos líneas verticales durante la impresión 3D de la última capa del sustrato base. Retire toda la etapa de construcción y enjuague suavemente la etapa de construcción y el material impreso con etanol 100% sin desnaturalizar de una botella de lavado durante 10 segundos para eliminar la resina a granel residual del material impreso en 3D y la etapa de construcción.Con aire comprimido, seque suavemente el material impreso en 3D y cree la etapa para eliminar el etanol residual y luego vuelva a insertar la etapa de construcción en la impresora 3D. Retire la cuba de la impresora 3D y vierta la resina a granel restante en un vil ámbar, y almacene la vil en un lugar fresco y oscuro. Usando etanol 100% sin desnaturalizar de una botella de lavado, enjuague cuidadosamente la cuba para eliminar cualquier resina a granel residual.Seque la cuba con una corriente de aire comprimido para eliminar cualquier residuo de etanol y vuelva a insertar la cuba en la impresora 3D. Para realizar la funcionalización de la superficie, vierta la resina de superficie previamente preparada en la cuba de la impresora 3D, asegurándose de que la solución cubra completamente la película inferior sin burbujas de aire u otras inhomogeneidades, y luego cierre la caja de la impresora 3D. Reanude el programa de impresión 3D haciendo clic en el botón Reproducir del triángulo para permitir que se produzca el patrón de superficie predeterminado.Una vez que se haya completado el programa de impresión, retire la etapa de construcción de la impresora 3D y lávela durante 10 segundos con etanol 100% sin desnaturalizar utilizando una botella de lavado para eliminar la resina superficial residual del material impreso en 3D y la etapa de construcción. Con aire comprimido, seque suavemente el material impreso en 3D y cree la etapa para eliminar el etanol residual. Mientras aún está unido a la etapa de construcción, cure el material invirtiendo toda la etapa de construcción y colocándolo bajo una luz de 405 nanómetros durante 15 minutos.Retire suavemente el material impreso en 3D funcionalizado en la superficie de la etapa de construcción con una placa de metal delgada o un raspador de pintura. Para realizar el análisis de fluorescencia, coloque el material funcionalizado de la superficie impreso en 3D debajo de una lámpara de descarga de gas ultravioleta de 312 nanómetros en un lugar oscuro, asegurándose de que la capa funcionalizada de la superficie esté hacia arriba. Encienda la lámpara para irradiar continuamente la capa superficial con luz de 312 nanómetros y observe el patrón fluorescente.Para realizar el análisis de la propiedad de tracción, coloque las muestras en forma de hueso de perro entre las empuñaduras de una máquina de prueba de tracción, asegurando que el material impreso en 3D se coloque igualmente a una distancia de 50,3 milímetros. Inicie el programa para adquirir datos de fuerza versus viajes. Después de la impresión 3D y la funcionalización de la superficie, el material se post-curó bajo irradiación de 405 nanómetros.Se observó que los materiales funcionalizados eran amarillos pero altamente transparentes con formas bien definidas. Los materiales funcionalizados no muestran fluorescencia en la oscuridad. Sin embargo, tras la irradiación ultravioleta, se observó fluorescencia superficial resuelta espacialmente en las regiones irradiadas con luz durante el paso de funcionalización de la superficie, visible como un patrón yin-yang ligeramente elevado.Las imágenes de fluorescencia mostraron que la parte inferior del material no mostró fluorescencia bajo irradiación de luz ultravioleta. Sin embargo, la parte superior del material mostró una fuerte fluorescencia en el patrón yin-yang. Se analizaron las propiedades mecánicas de las muestras en forma de hueso de perro impresas en 3D y se obtuvo una curva de tensión-deformación.El material mostró una deformación elástica, proporcionando una tensión de rendimiento de aproximadamente 25 megapascales, y luego una deformación plástica antes de la falla. El alargamiento en el descanso fue de aproximadamente el 12%, mientras que el estrés en el descanso fue de aproximadamente 22 megapascales. El módulo de Young se calculó en aproximadamente 7 megapascales, mientras que la dureza fue de aproximadamente 115 megajulios por metro cúbico.Es importante asegurarse de que el residente de la superficie cubra completamente la película de la cuba y esté libre de burbujas de aire u otras imperfecciones que puedan provocar desviaciones del patrón de superficie previsto.

3d-printing-situ-surface-modification-via-type-i-photoinitiated

Research

Investigación

JoVE Journal

Chemistry

Química

Un procedimiento de polimerización inducida por plasma se describe para la polimerización iniciada por superficie en las membranas poliméricas. Además modificación posterior del polímero injertado con sustancias fotocrómicas se presenta con un protocolo de la realización de mediciones de la permeabilidad de las membranas responde a la luz.

Preparación de Membranas Light responden por un injerto superficial combinado y proceso de modificación posterior

Los sustratos de cultivo celular funcionalizados con patrones a microescala de ligandos biológicos tienen una inmensa utilidad en el campo de la ingeniería de tejidos. Aquí, demostramos la fabricación versátil y automatizada de sustratos de cultivo de tejidos con múltiples cepillos de poli(etilenglicol) micromodelados que presentan químicas ortogonales que permiten la inmovilización espacialmente precisa y específica del sitio de ligandos biológicos.

La fabricación de sustratos de cultivo complejas utilizando robótica microcontacto impresión (R-μCP) y secuencial sustitución nucleófila

Una metodología novedosa se presenta para sintetizar y elastómeros programa principal de cadena líquido-cristalinas usando monómeros de partida comercialmente disponibles. Una amplia gama de propiedades termomecánicas fue adaptado mediante el ajuste de la cantidad de agente de reticulación, mientras que el rendimiento de accionamiento era dependiente de la cantidad de tensión aplicada durante la programación.

Síntesis de programable principal cadena Elastómeros líquido-cristalinas utilizando una reacción de tiol-acrilato de dos etapas

Se presenta un protocolo para la síntesis y preparación de nanopartículas compuestas por polímeros electroactivos.

Propiedades Electroactivos Polymer Nanopartículas Exponer fototérmica

Este artículo describe un proceso para producir nanopartículas poliméricas autoensambladas utilizando polimerización por dispersión mediada por luz visible. El uso de luz visible de baja energía para controlar la polimerización permite la formación reproducible de micelas autoensambladas en forma de gusano con un alto contenido de sólidos.

Síntesis Facile de micelas similares a gusanos de luz visible mediada por dispersión Polimerización con catalizador Photoredox

El protocolo presentado aquí permite la fabricación automatizada de micropatrones que estandariza la forma celular para estudiar las estructuras citoesqueléticos dentro de las células de mamíferos. Esta técnica fácil de usar se puede configurar con sistemas de imágenes disponibles en el comercio y no requiere equipos especializados inaccesibles a los laboratorios de biología celular estándar.

Control de la geometría celular a través de micropatterning asistido por láser infrarrojo

Este protocolo detalla la síntesis de nanocápsulas de conversión ascendente para su posterior uso en resinas fotopolimerizables para la impresión 3D volumétrica facilitada por la conversión ascendente por fusión triplete.

Síntesis de nanocápsulas de conversión ascendente de fusión triplete

Con una técnica no invasiva y en tiempo real, el movimiento nanoscópico del polímero dentro de un filamento de polímero se visualiza durante la impresión 3D. Afinar este movimiento es crucial para producir construcciones con un rendimiento y apariencia óptimos. Este método llega al núcleo de la fusión de capas de plástico, ofreciendo así información sobre las condiciones óptimas de impresión y los criterios de diseño de materiales.

Imágenes en tiempo real de la unión en capas impresas en 3D

La impresión 3D a escala micrométrica permite la creación rápida de prototipos de dispositivos poliméricos para cultivos de células neuronales. Como prueba de principio, las conexiones estructurales entre las neuronas se vieron limitadas por la creación de barreras y canales que influyen en el crecimiento de las neuritas, mientras que las consecuencias funcionales de dicha manipulación fueron observadas por la electrofisiología extracelular.

Impresión 3D de polimerización de dos fotones de dispositivos de cultivo de células neuronales a microescala

Se presenta un método para imponer la topografía superficial de materiales poliméricos compuestos que absorben la luz, en particular los elastómeros magnetoactivos (MAE), mediante el uso de micromecanizado láser. Este método permite una gran flexibilidad en los diseños topográficos y la creación rápida de prototipos. Se muestra un ejemplo de estructuración de superficies MAE, caracterización y su respuesta al campo magnético externo.

Micromecanizado láser para el diseño de topografía de superficies poliméricas

Aprende a ajustar independientemente las propiedades volumétricas e interfaciales de materiales impresos en 3D mediante polimerización RAFT fotoiniciada tipo I. Esta técnica simplifica la fabricación de estructuras complejas usando equipos comerciales.

Impresión 3D y modificación de superficies in situ mediante polimerización de transferencia de cadena de adición reversible-fragmentación fotoiniciada tipo I (Video) | JoVE Journal

Impresión 3D y modificación de superficies in situ mediante polimerización de transferencia de cadena de adición reversible-fragmentación fotoiniciada tipo I

Explorar más videos