Name: Impacto de la rugosidad del raspador dental piezoeléctrico en dos materiales de relleno compuestos fluidos distintos (Video) | JoVE Journal
Uploaded: 2025-01-10T13:30:00.000+00:00
Duration: 5 min 30 s
Description: Aprende a evaluar el impacto de los raspadores dentales piezoeléctricos en la rugosidad superficial de dos materiales de relleno compuestos fluidos distintos. Este método ayuda a estandarizar parámetros clínicos para restauraciones dentales.

ai_agent_IP

ai_agent

maintenance

instantTrialDurationMinutes

isBiopharma

enableNewMyJoveSectionDesign

educationFeatures

seoMetaApi

ai_copilot_institution_blacklist

ai_chat_institution_blacklist

freeAccessWindow

ssoRoleCapture

scheduledMaintenanceBanner

joveLabsFeatures

disable_autoplay_for_bots

extended_trial_duration

5 minutes

playerTrialDesktop

<ol><li>Hossam, A. E., Rafi, A. T., Ahmed, A. S., Sumanth, P. C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Surface+topography+of+composite+restorative+materials+following+ultrasonic+scaling+and+its+impact+on+bacterial+plaque+accumulation.+An+in+vitro+sem+study%5BTitle%5D)+AND+%22J+Int+Oral+Health%22%5BJournal%5D)">Surface topography of composite restorative materials following ultrasonic scaling and its impact on bacterial plaque accumulation. An in vitro sem study.</a> J Int Oral Health. 5 (3), 13-19 (2013).</li>
<li>Zissis, A. J., Polyzois, G. L., Yannikakis, S. A., Harrison, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Roughness+of+denture+materials%3A+A+comparative+study%5BTitle%5D)+AND+%22Int+J+Prosthodont%22%5BJournal%5D)">Roughness of denture materials: A comparative study.</a> Int J Prosthodont. 13 (2), 136-140 (2000).</li>
<li>Arabaci, T., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Influence+of+tip+wear+of+piezoelectric+ultrasonic+scalers+on+root+surface+roughness+at+different+working+parameters.+A+profilometric+and+atomic+force+microscopy+study%5BTitle%5D)+AND+%22Int+J+Dent+Hyg%22%5BJournal%5D)">Influence of tip wear of piezoelectric ultrasonic scalers on root surface roughness at different working parameters. A profilometric and atomic force microscopy study.</a> Int J Dent Hyg. 11 (1), 69-74 (2013).</li>
<li>Goldstein, R. E., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Microleakage+around+class+v+composite+restorations+after+ultrasonic+scaling+and+sonic+toothbrushing+around+their+margin%5BTitle%5D)+AND+%22J+Esthet+Restor+Dent%22%5BJournal%5D)">Microleakage around class v composite restorations after ultrasonic scaling and sonic toothbrushing around their margin.</a> J Esthet Restor Dent. 29 (1), 41-48 (2017).</li>
<li>Mittal, A., Nichani, A. S., Venugopal, R., Rajani, V. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((The+effect+of+various+ultrasonic+and+hand+instruments+on+the+root+surfaces+of+human+single+rooted+teeth%3A+A+planimetric+and+profilometric+study%5BTitle%5D)+AND+%22J+Indian+Soc+Periodontol%22%5BJournal%5D)">The effect of various ultrasonic and hand instruments on the root surfaces of human single rooted teeth: A planimetric and profilometric study.</a> J Indian Soc Periodontol. 18 (6), 710-717 (2014).</li>
<li>Babina, K., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((The+effect+of+ultrasonic+scaling+and+air-powder+polishing+on+the+roughness+of+the+enamel%2C+three+different+nanocomposites%2C+and+composite%2Fenamel+and+composite%2Fcementum+interfaces%5BTitle%5D)+AND+%22Nanomaterials+%28Basel%29%22%5BJournal%5D)">The effect of ultrasonic scaling and air-powder polishing on the roughness of the enamel, three different nanocomposites, and composite/enamel and composite/cementum interfaces.</a> Nanomaterials (Basel). 11 (11), (2021).</li>
<li>Demirci, F., Birgealp Erdem, M., Tekin, M., Caliskan, C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Effect+of+ultrasonic+scaling+and+air+polishing+on+the+surface+roughness+of+polyetheretherketone+%28peek%29+materials%5BTitle%5D)+AND+%22Am+J+Dent%22%5BJournal%5D)">Effect of ultrasonic scaling and air polishing on the surface roughness of polyetheretherketone (peek) materials.</a> Am J Dent. 35 (4), 200-204 (2022).</li>
<li>Erdilek, D., Sismanoglu, S., Gumustas, B., Efes, B. G. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Effects+of+ultrasonic+and+sonic+scaling+on+surfaces+of+tooth-colored+restorative+materials%3A+An+in+vitro+study%5BTitle%5D)+AND+%22Niger+J+Clin+Pract%22%5BJournal%5D)">Effects of ultrasonic and sonic scaling on surfaces of tooth-colored restorative materials: An in vitro study.</a> Niger J Clin Pract. 18 (4), 467-471 (2015).</li>
<li>Lai, Y. L., Lin, Y. C., Chang, C. S., Lee, S. Y. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Effects+of+sonic+and+ultrasonic+scaling+on+the+surface+roughness+of+tooth-colored+restorative+materials+for+cervical+lesions%5BTitle%5D)+AND+%22Oper+Dent%22%5BJournal%5D)">Effects of sonic and ultrasonic scaling on the surface roughness of tooth-colored restorative materials for cervical lesions.</a> Oper Dent. 32 (3), 273-278 (2007).</li>
<li>Mahiroglu, M. B., Kahramanoglu, E., Ay, M., Kuru, L., Agrali, O. B. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Comparison+of+root+surface+wear+and+roughness+resulted+from+different+ultrasonic+scalers+and+polishing+devices+applied+on+human+teeth%3A+An+in+vitro+study%5BTitle%5D)+AND+%22Healthcare+%28Basel%29%22%5BJournal%5D)">Comparison of root surface wear and roughness resulted from different ultrasonic scalers and polishing devices applied on human teeth: An in vitro study.</a> Healthcare (Basel). 8 (1), (2020).</li>
<li>Cadenaro, M., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Flowability+of+composites+is+no+guarantee+for+contraction+stress+reduction%5BTitle%5D)+AND+%22Dent+Mater%22%5BJournal%5D)">Flowability of composites is no guarantee for contraction stress reduction.</a> Dent Mater. 25 (5), 649-654 (2009).</li>
<li>Basheer, R. R., Hasanain, F. A., Abuelenain, D. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Evaluating+flexure+properties%2C+hardness%2C+roughness+and+microleakage+of+high-strength+injectable+dental+composite%3A+An+in+vitro+study%5BTitle%5D)+AND+%22BMC+Oral+Health%22%5BJournal%5D)">Evaluating flexure properties, hardness, roughness and microleakage of high-strength injectable dental composite: An in vitro study.</a> BMC Oral Health. 24 (1), 546(2024).</li>
<li>Brine, E. J., Marretta, S. M., Pijanowski, G. J., Siegel, A. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Comparison+of+the+effects+of+four+different+power+scalers+on+enamel+tooth+surface+in+the+dog%5BTitle%5D)+AND+%22J+Vet+Dent%22%5BJournal%5D)">Comparison of the effects of four different power scalers on enamel tooth surface in the dog.</a> J Vet Dent. 17 (1), 17-21 (2000).</li>
<li>Kuka, G. I., Kuru, B., Gursoy, H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((In+vitro+evaluation+of+the+different+supragingival+prophylaxis+tips+on+enamel+surfaces%5BTitle%5D)+AND+%22Photobiomodul+Photomed+Laser+Surg%22%5BJournal%5D)">In vitro evaluation of the different supragingival prophylaxis tips on enamel surfaces.</a> Photobiomodul Photomed Laser Surg. 41 (5), 212-217 (2023).</li>
<li>Parashar, A., Bhavsar, N. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Assessing+the+effect+of+piezoelectric+ultrasonic+scaler+tip+wear+on+root+surface+roughness+under+influence+of+various+working+parameters%3A+A+profilometric+and+atomic+force+microscopic+study%5BTitle%5D)+AND+%22J+Indian+Soc+Periodontol%22%5BJournal%5D)">Assessing the effect of piezoelectric ultrasonic scaler tip wear on root surface roughness under influence of various working parameters: A profilometric and atomic force microscopic study.</a> J Indian Soc Periodontol. 27 (6), 583-589 (2023).</li>
<li>Vengatachalapathi, H., Naik, R., Rao, R., Venugopal, R., Nichani, A. S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((The+effect+of+piezoelectric+ultrasonic+scaler+tip+wear+on+root+surface+roughness+at+different+working+parameters%3A+An+atomic+force+microscopic+and+profilometric+study%5BTitle%5D)+AND+%22J+Int+Acad+Periodontol%22%5BJournal%5D)">The effect of piezoelectric ultrasonic scaler tip wear on root surface roughness at different working parameters: An atomic force microscopic and profilometric study.</a> J Int Acad Periodontol. 19 (1), 15-21 (2017).</li>
<li>Casarin, R. C., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Root+surface+defect+produced+by+hand+instruments+and+ultrasonic+scaler+with+different+power+settings%3A+An+in+vitro+study%5BTitle%5D)+AND+%22Braz+Dent+J%22%5BJournal%5D)">Root surface defect produced by hand instruments and ultrasonic scaler with different power settings: An in vitro study.</a> Braz Dent J. 20 (1), 58-63 (2009).</li>
<li>International Organization for Standardization. Part 12: Sample preparation and reference materials in Biological evaluation of medical devices. <a target="_blank" href="http://scholar.google.com/scholar?hl=en&safe=off&q=%22ISO+10993-12%3A2021%22">ISO 10993-12:2021</a>. , (2021).</li>
<li>Sabatini, C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Color+stability+behavior+of+methacrylate-based+resin+composites+polymerized+with+light-emitting+diodes+and+quartz-tungsten-halogen%5BTitle%5D)+AND+%22Oper+Dent%22%5BJournal%5D)">Color stability behavior of methacrylate-based resin composites polymerized with light-emitting diodes and quartz-tungsten-halogen.</a> Oper Dent. 40 (3), 271-281 (2015).</li>
<li>Checchi, V., et al. Wear and roughness analysis of two highly filled flowable composites. <a target="_blank" href="http://scholar.google.com/scholar?hl=en&safe=off&q=author%3aChecchi%2C+V+%22Odontology%22">Odontology</a>. , (2024).</li>
<li>Poggio, C., Dagna, A., Chiesa, M., Colombo, M., Scribante, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Surface+roughness+of+flowable+resin+composites+eroded+by+acidic+and+alcoholic+drinks%5BTitle%5D)+AND+%22J+Conserv+Dent%22%5BJournal%5D)">Surface roughness of flowable resin composites eroded by acidic and alcoholic drinks.</a> J Conserv Dent. 15 (2), 137-140 (2012).</li>
<li>Tepe, H., Erdilek, A. D., Sahin, M., Efes, B. G., Yaman, B. C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Effect+of+different+polishing+systems+and+speeds+on+the+surface+roughness+of+resin+composites%5BTitle%5D)+AND+%22J+Conserv+Dent%22%5BJournal%5D)">Effect of different polishing systems and speeds on the surface roughness of resin composites.</a> J Conserv Dent. 26 (1), 36-41 (2023).</li>
<li>Busslinger, A., Lampe, K., Beuchat, M., Lehmann, B. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((A+comparative+in+vitro+study+of+a+magnetostrictive+and+a+piezoelectric+ultrasonic+scaling+instrument%5BTitle%5D)+AND+%22J+Clin+Periodontol%22%5BJournal%5D)">A comparative in vitro study of a magnetostrictive and a piezoelectric ultrasonic scaling instrument.</a> J Clin Periodontol. 28 (7), 642-649 (2001).</li>
<li>Flemmig, T. F., Petersilka, G. J., Mehl, A., Hickel, R., Klaiber, B. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Working+parameters+of+a+magnetostrictive+ultrasonic+scaler+influencing+root+substance+removal+in+vitro%5BTitle%5D)+AND+%22J+Periodontol%22%5BJournal%5D)">Working parameters of a magnetostrictive ultrasonic scaler influencing root substance removal in vitro.</a> J Periodontol. 69 (5), 547-553 (1998).</li>
<li>Singh, S., Uppoor, A., Nayak, D. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((A+comparative+evaluation+of+the+efficacy+of+manual%2C+magnetostrictive+and+piezoelectric+ultrasonic+instruments-an+in+vitro+profilometric+and+sem+study%5BTitle%5D)+AND+%22J+Appl+Oral+Sci%22%5BJournal%5D)">A comparative evaluation of the efficacy of manual, magnetostrictive and piezoelectric ultrasonic instruments-an in vitro profilometric and sem study.</a> J Appl Oral Sci. 20 (1), 21-26 (2012).</li>
<li>Yousefimanesh, H., Robati, M., Kadkhodazadeh, M., Molla, R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((A+comparison+of+magnetostrictive+and+piezoelectric+ultrasonic+scaling+devices%3A+An+in+vitro+study%5BTitle%5D)+AND+%22J+Periodontal+Implant+Sci%22%5BJournal%5D)">A comparison of magnetostrictive and piezoelectric ultrasonic scaling devices: An in vitro study.</a> J Periodontal Implant Sci. 42 (6), 243-247 (2012).</li>
<li>Flemmig, T. F., Petersilka, G. J., Mehl, A., Hickel, R., Klaiber, B. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((The+effect+of+working+parameters+on+root+substance+removal+using+a+piezoelectric+ultrasonic+scaler+in+vitro%5BTitle%5D)+AND+%22J+Clin+Periodontol%22%5BJournal%5D)">The effect of working parameters on root substance removal using a piezoelectric ultrasonic scaler in vitro.</a> J Clin Periodontol. 25 (2), 158-163 (1998).</li>
<li>Oliveira, G., Macedo, P. D., Tsurumaki, J. N., Sampaio, J. E., Marcantonio, R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((The+effect+of+the+angle+of+instrumentation+of+the+piezoelectric+ultrasonic+scaler+on+root+surfaces%5BTitle%5D)+AND+%22Int+J+Dent+Hyg%22%5BJournal%5D)">The effect of the angle of instrumentation of the piezoelectric ultrasonic scaler on root surfaces.</a> Int J Dent Hyg. 14 (3), 184-190 (2016).</li>
<li>Bergstrom, J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Photogrammetric+registration+of+dental+plaque+accumulation+in+vivo%5BTitle%5D)+AND+%22Acta+Odontol+Scand%22%5BJournal%5D)">Photogrammetric registration of dental plaque accumulation in vivo.</a> Acta Odontol Scand. 39 (5), 275-284 (1981).</li>
<li>Quirynen, M., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((The+influence+of+surface+free+energy+and+surface+roughness+on+early+plaque+formation.+An+in+vivo+study+in+man%5BTitle%5D)+AND+%22J+Clin+Periodontol%22%5BJournal%5D)">The influence of surface free energy and surface roughness on early plaque formation. An in vivo study in man.</a> J Clin Periodontol. 17 (3), 138-144 (1990).</li>
</ol>

<table><tbody><tr><td>Beautifil Flow Plus</td><td>Shofu</td><td></td><td>Estados Unidos</td></tr><tr><td>Evo MA10 Microscopio Electrónico de Barrido</td><td>Zeiss</td><td></td><td>Alemania</td></tr><tr><td>EWO Typ 990 Paralelómetro</td><td>Kavo</td><td></td><td>Alemania</td></tr><tr><td>Discos de Acabado</td><td>Bisco</td><td></td><td>Estados Unidos</td></tr><tr><td>G4 Scaler Tip</td><td>Woodpecker</td><td></td><td>China</td></tr><tr><td>Premise Flowable</td><td>Kerr</td><td></td><td>Estados Unidos</td></tr><tr><td>SC 7620 modelo SPUTTER Coater</td><td>Quorum Technologies</td><td></td><td>UK</td></tr><tr><td>Surftest SJ-210</td><td>Mitutoyo</td><td></td><td>Japón</td></tr><tr><td>UDS-A-LED Raspador dental</td><td>Woodpecker</td><td></td><td>China</td></tr><tr><td>Valo LED Lámpara de curado inalámbrica</td><td>Ultradent</td><td></td><td>Estados Unidos</td></tr><tr><td>Zetaplus Material de impresión de silicona</td><td>Zhermack</td><td></td><td>Italia</td></tr></tbody></table>

impacto de la rugosidad del raspador dental piezoeléctrico en dos materiales de relleno compuestos fluidos distintos

Roughness Impact of Piezoelectric Dental Scaler on Two Distinct Flowable Composite Filling Materials

Los análisis estadísticos se realizaron mediante software de análisis estadístico. Se realizó la prueba de rango con signo de Wilcoxon para evaluar los cambios dentro del grupo. Se empleó la prueba Mann Whitney-U para realizar comparaciones intergrupales. El nivel de significancia se determinó a p &lt; 0,05.
En la comparación profilométrica intragrupo de ambos grupos, se observó que la aplicación del escalador resultó en una rugosidad considerable, que puede visualizarse cualitativamente media...

Impacto de la rugosidad del raspador dental piezoeléctrico en dos materiales de relleno compuestos fluidos distintos

Dental ultrasonic scalers are commonly employed in periodontal treatment; however, their ability to roughen tooth surfaces is a worry since roughness may ...

roughness-impact-piezoelectric-dental-scaler-on-two-distinct-flowable

Research

Investigación

JoVE Journal

Behavior

Comportamiento

Con el fin de entender el desarrollo espacial de la tensión de contracción de polimerización en restauraciones de composite de resina dental, se utilizó la correlación digital de imagen para proporcionar de campo completo de medición de desplazamiento / deformación de las cavidades de vidrio modelo restaurados mediante la correlación de las imágenes de la restauración se toma antes y después de la polimerización.

Contracción de Dental Composite en Simulado Cavidad Medido con Correlación Digital de Imágenes

Se desarrolló una prueba cuasiestática de carga a fractura con una bola de acero inoxidable no fija para determinar la resistencia a la fractura de restauraciones posteriores mínimamente invasivas de diseño y fabricación asistidas por computadora cementadas con materiales análogos de dentina. Esta prueba modela el régimen de carga típico responsable de la fractura de las restauraciones dentales.

Ensayos mecánicos cuasiestáticos para el diseño y la fabricación asistidos por ordenador Carillas oclusales cementadas con material análogo de dentina fresado

Aquí, evaluamos el impacto de varios métodos de pulido en la estabilidad del color de las restauraciones de resina compuesta y compuesta utilizadas en restauraciones anteriores dentro de la odontología pediátrica. Este estudio destaca la importancia de seleccionar métodos de pulido apropiados para mejorar la estabilidad del color de las restauraciones de resina compuesta y compuesta en odontología pediátrica.

Evaluación de los efectos de diferentes métodos de pulido en la estabilidad del color de las restauraciones dentales en odontopediatría

El presente protocolo describe un modelo experimental basado en la tinción de tinta que puede ser utilizado para la descontaminación de la superficie del implante in vitro y la investigación de la rugosidad para contribuir a la toma de decisiones clínicas.

Efectos de los métodos mecánicos utilizados en el tratamiento de la periimplantitis sobre la descontaminación y rugosidad de la superficie del implante

Este artículo presenta un protocolo para evaluar los efectos de diferentes métodos de fabricación (PMMA termopolimerizado, PMMA fresado CAD-CAM y resina impresa en 3D) y técnicas de pulido (papeles abrasivos de carburo de silicio de grano 600, 800 y 1000) en la rugosidad de la superficie (Ra) de los materiales base de resina utilizados para dentaduras postizas completas.

Impacto de las técnicas de fabricación y los procedimientos de pulido en la rugosidad de la superficie de las resinas de base para dentaduras postizas

Este protocolo tiene como objetivo evaluar los efectos de los protocolos de tratamiento superficial, la selección de cemento con luto y el termociclo sobre la resistencia a la unión cortante entre PEEK y una resina compuesta indirecta.

Protocolo estandarizado para evaluar el efecto de los tratamientos superficiales, el enlucido de cementos y el termociclamiento sobre la resistencia de unión entre PEEK y compuestos

Este protocolo describe un método estandarizado in vitro para evaluar los efectos de las bebidas de proteína de suero sobre la microdureza de compuestos de resina. El enfoque permite una evaluación controlada de la exposición dietética mediante inmersión cíclica y pruebas Vickers, proporcionando un modelo reproducible para investigar la interacción entre bebidas nutricionales y biomateriales restauradores.

Un procedimiento estandarizado in vitro para evaluar los cambios de microdureza superficial en compuestos de resina nanohíbrida tras la exposición a bebidas de proteína de suero

Esto aplica paradigma experimental replica circunstancias por las que un testigo ocular de un verdadero crimen puede crear un retrato robot holística del culpable de la memoria y, a continuación, tratar de identificar al culpable de un vídeo line-up que contiene el culpable o uno en el que él o ella es no presente.

Holística Creación retrato robot y posterior Alineación vídeo Eyewitness Identificación Paradigma

Este protocolo describe un nuevo y eficiente método para iniciar rápidamente operante de responder durante etanol en ratas que, contrariamente a los métodos estándar, no requiere privación de agua o sacarina / sacarosa desvanecimiento para iniciar de responder.

Un método para evaluar las propiedades reforzantes de etanol en ratas sin privación de agua, la sacarina o el desvanecimiento de Formación Extended Access

Feeding Experimentation Device (FED) es un dispositivo de código abierto para medir la ingesta de alimentos en ratones.  FED también puede sincronizar las mediciones de ingesta de alimentos con otras técnicas a través de una salida digital en tiempo real. Aquí, proporcionamos un tutorial paso a paso para la construcción, validación y uso de FED.

La alimentación de dispositivos Experimentación (FED): construcción y validación de un dispositivo de fuente abierta para la medición de la ingesta de alimentos en roedores

Aprende a evaluar el impacto de los raspadores dentales piezoeléctricos en la rugosidad superficial de dos materiales de relleno compuestos fluidos distintos. Este método ayuda a estandarizar parámetros clínicos para restauraciones dentales.

Impacto de la rugosidad del raspador dental piezoeléctrico en dos materiales de relleno compuestos fluidos distintos