Name: Construction et dessai des Piles de batteries lithium-ion (Vidéo) | JoVE Journal
Uploaded: 2012-08-02T13:00:00.000+00:00
Duration: 7 min 23 s
Description: Apprenez à construire et tester des demi-piles bouton lithium-ion en boîte à gants. Cette méthode détaille la préparation des électrodes, l'assemblage hermétique et les tests électrochimiques pour évaluer les capacités de charge.

ai_agent_IP

ai_agent

maintenance

instantTrialDurationMinutes

isBiopharma

enableNewMyJoveSectionDesign

educationFeatures

seoMetaApi

ai_copilot_institution_blacklist

ai_chat_institution_blacklist

freeAccessWindow

ssoRoleCapture

scheduledMaintenanceBanner

joveLabsFeatures

disable_autoplay_for_bots

extended_trial_duration

5 minutes

playerTrialDesktop

Nous tenons à souligner l&#39;appui du programme dans la division Céramiques de recherche sur les matériaux de l&#39;US National Science Foundation, en vertu de la concession no. DMR-1006515 (gestionnaire de programme, le Dr D. Madsen Lynnette).

1. Préparation d&#39;une électrode de travail <ol><li> Préparer un mélange de ~ 6 en poids. % De fluorure de polyvinylidène (PVDF) liant dans de la N-méthyl-2-pyrrolidone (NMP). </li><li> Peser 80 poids. % De matière active (LiCoO 2, dans ce cas) et 10 en poids. % C noir (acétylène, 99,9% +), puis les mélanger dans un tourbillon pendant 1 min. </li><li> Ajouter NMP-liant mélange de telle sorte que le liant constitue 10 en poids. % Du poids total du mélange. </li><li> Transférer le mélange ci-dessus dans un petit flacon de verre et mélanger dans le mélangeur vortex au régime maximal pendant environ 30 min. Deux billes de zircone de 5 mm de diamètre peut être utilisé comme support pour un meilleur mélange. Si nécessaire, ajouter plus de NMP afin d&#39;obtenir une boue de consistance désirée. </li><li> Propager une feuille métallique du collecteur de courant (typiquement, d&#39;aluminium pour la cathode et l&#39;anode de cuivre pour) sur une plaque de verre. Utilisez de l&#39;acétone et d&#39;assurer qu&#39;il n&#39;y a pas de bulles d&#39;air entre la feuille et la plaque de verre. Utilisez deux couches de ruban adhésif pour former une piste et define la région à revêtir. </li><li> Appliquer la suspension sur la feuille métallique en utilisant une spatule en acier inoxydable et la propagation de la suspension uniforme sur la piste en utilisant une lame de rasoir. </li><li> Sécher le revêtement dans l&#39;air ou sous vide à 90-120 ° C ~ environ 2-8 heures pour (qui doit être ajusté en fonction du matériau et de liant utilisé). </li><li> Placez la feuille de métal enduit entre deux plaques d&#39;acier (et de deux documents de pesage pour protéger le revêtement) et de la presse sous une charge de £ 3000 ~ en utilisant une presse hydraulique. </li><li> Poinçonner la feuille métallique revêtue sèche en disques de 8 mm de diamètre (de préférence à l&#39;intérieur une boîte à gants). Peser les cathodes et les envelopper avant de transférer dans la boîte à gants. </li><li> Poinçonner la feuille métallique non revêtue du même matériau en disques de 8 mm de diamètre et peser ces disques. </li></ol> 2. Préparation de l&#39;électrolyte <ol><li> Comme l&#39;électrolyte est photosensible, stocker l&#39;électrolyte (1M LiPF 6 en CE: DMC: DEC dans ce cas) dans un bottl Nalgenee enveloppé par une feuille d&#39;aluminium. </li></ol> 3. Préparation d&#39;une contre-électrode (feuille de lithium dans ce cas) <ol><li> Nettoyer la surface de la feuille de lithium à l&#39;aide d&#39;une brosse en nylon / acier inoxydable scalpel jusqu&#39;à une surface brillante argentée apparaît (l&#39;intérieur d&#39;une boîte à gants d&#39;argon). </li><li> Percez la feuille de lithium dans les disques de ½ pouce de diamètre (l&#39;intérieur d&#39;une boîte à gants d&#39;argon). </li></ol> 4. Assemblée pile bouton <ol><li> La figure 2 montre un schéma de l&#39;assemblage de pile bouton. </li><li> Poinçon Celgard C480 membranes dans des disques de 19 mm de diamètre dans les séparateurs et les utiliser comme. </li><li> Transfert cas de cellules (CR2032), les ressorts et les entretoises (achetée chez MTI Corp), les séparateurs et électrodes de travail dans la boîte à gants (après le rinçage de l&#39;échangeur de cinq fois avec de l&#39;argon). </li><li> Assemblez les pièces de monnaie dans les cellules de la boîte à gants. </li><li> Ajouter deux gouttes de l&#39;électrolyte à la coupe de cellules et de placer l&#39;électrode de travail à ce sujet. Ajouter trois autresgouttes de l&#39;électrolyte et le lieu deux séparateurs à deux gouttes d&#39;électrolyte entre elles. Ajouter deux gouttes de plus de l&#39;électrolyte avant de placer la contre-électrode de lithium sur elle. Placez deux entretoises en acier inoxydable et d&#39;un ressort sur le disque de lithium. </li><li> Fermer la cellule en utilisant le couvercle de la cellule et à sertir 3-4 fois en utilisant la machine compacte sertissage (achetée chez MTI Corp). </li><li> Après le montage des cellules, gérer les cellules finis en utilisant des pinces en plastique (pour éviter les courts-circuits). </li><li> Nettoyer l&#39;excès d&#39;électrolyte fuite à partir des côtés de la cellule en utilisant une serviette en papier. </li><li> La cellule est prêt à être testé et peut être retiré de la boîte à gants. </li></ol> 5. Test de pile bouton <ol><li> Gardez la pile bouton connecté à l&#39;appareil de contrôle de la batterie dans la tension en circuit ouvert (OCV) en mode pendant une heure dès qu&#39;elle est prête. </li><li> Définir fenêtre de tension pour tester la cellule sur la base de la matière active utilisée dans l&#39;électrode de travail. </li><li> Calculer le l&#39;la capacité oretical pour la cellule en utilisant les calculs présentés ci-dessous. </li></ol> Poids du disque électrode avec le collecteur de courant = W EO Poids du disque collecteur de courant non revêtue de la même diamètre = O CC Poids de matériau d&#39;électrode, W EM, est donnée par <img alt="L&#39;équation 1" src="/files/ftp_upload/4104/4104eq1.jpg" /> Poids de matière active dans l&#39;électrode, W AM, est donnée par <img alt="L&#39;équation 2" src="/files/ftp_upload/4104/4104eq2.jpg" /> Capacité théorique pour le disque d&#39;électrode, C ED, est donnée par <img alt="L&#39;équation 3" src="/files/ftp_upload/4104/4104eq3.jpg" /> où C est la s théoriquesla capacité PECIFIQUES du matériau actif. <ol start="4"><li> Testez la cellule pièce de monnaie pour cycles charge-décharge à la C-requis taux. </li></ol> 6. Les résultats représentatifs A titre d&#39;exemple, une pile bouton a été construite en utilisant LiCoO 2 comme matériau actif pour l&#39;électrode de travail. Après la construction, la cellule a été testée à C / 5 Taux. Le profil obtenu est représenté sur la figure 3. La fenêtre de tension a été fixé à entre 3 et 4,3 V pour cette cellule pièce. La capacité est de 155 mAh / g pour le premier cycle de charge et de 140 mAh / g pour le premier cycle de décharge. <img alt="Figure 1" src="/files/ftp_upload/4104/4104fig1.jpg" /> Diagramme Figure 1. De la procédure de construction de pièces de cellule. Première, une électrode de travail est préparé à partir de la poudre du matériau actif. Puis, une contre-électrode est préparé à partir d&#39;une feuille de lithium propre et les séparateurs sont découpées. Enfin, une cellule estassemblés à l&#39;intérieur une boîte à gants d&#39;argon. <img alt="Figure 2" src="/files/ftp_upload/4104/4104fig2.jpg" /> Figure 2. Schéma d&#39;un procédé d&#39;assemblage de pièces de cellules montrant tous les composants dans l&#39;ordre où ils sont placés à l&#39;intérieur du boîtier de cellule pièce. <img alt="Figure 3" src="/files/ftp_upload/4104/4104fig3.jpg" /> Figure 3. Les résultats représentatifs obtenus à partir d&#39;une pile bouton construit en utilisant une électrode de travail composé de LiCoO 2 et une électrode de feuille de lithium compteur. Le graphique montre la première charge et les courbes de première décharge de la cellule pièce qui a été chargée et déchargée au C / 5 Taux. <img alt="Figure 4" src="/files/ftp_upload/4104/4104fig4.jpg" /> Figure 4. Comparaison des revêtements bons ou mauvais après qu&#39;ils ont été séchée. Un revêtement fissuré résulte généralement du lisier qui a un excès de NMP et d&#39;un revêtement poreux entraîne généralement de l&#39;artLurry qui a insuffisante NMP. <img alt="Figure 5" src="/files/ftp_upload/4104/4104fig5.jpg" /> Figure 5. Comparaison d&#39;une cellule pièce ainsi sertie et une pile bouton mal sertie, avec une cellule non-sertie. Typiquement, une pile au mal sertie se fend après quelques heures dans ambiante en raison de l&#39;enflure de la feuille de lithium après réaction avec l&#39;humidité.

<ol><li>Cairns, E. J., Albertus, P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Batteries+for+Electric+and+Hybrid-Electric+Vehicles%5BTitle%5D)+AND+%22Annual+Review+of+Chemical+and+Biomolecular+Engineering%22%5BJournal%5D)">Batteries for Electric and Hybrid-Electric Vehicles.</a> Annual Review of Chemical and Biomolecular Engineering. 1, 299-320 (2010).</li>
<li>Dunn, B., Kamath, H., Tarascon, J. -M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Electrical+Energy+Storage+for+the+Grid%3A+A+Battery+of+Choices%5BTitle%5D)+AND+%22Science%22%5BJournal%5D)">Electrical Energy Storage for the Grid: A Battery of Choices.</a> Science. 334, 928-935 (2011).</li>
<li>Goodenough, J. B. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Cathode+materials%3A+A+personal+perspective%5BTitle%5D)+AND+%22J.+Power+Sources%22%5BJournal%5D)">Cathode materials: A personal perspective.</a> J. Power Sources. 174, 996-1000 (2007).</li>
<li>Yamada, A., Chung, S. C., Hinokuma, K. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Optimized+LiFePO4+for+lithium+battery+cathodes%5BTitle%5D)+AND+%22Journal+of+the+Electrochemical+Society%22%5BJournal%5D)">Optimized LiFePO4 for lithium battery cathodes.</a> Journal of the Electrochemical Society. 148, A224-A229 (2001).</li>
<li>Whittingham, M. S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Lithium+batteries+and+cathode+materials%5BTitle%5D)+AND+%22Chemical+Reviews%22%5BJournal%5D)">Lithium batteries and cathode materials.</a> Chemical Reviews. 104, 4271-4301 (2004).</li>
<li>Tarascon, J. M., Armand, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Issues+and+challenges+facing+rechargeable+lithium+batteries%5BTitle%5D)+AND+%22Nature%22%5BJournal%5D)">Issues and challenges facing rechargeable lithium batteries.</a> Nature. 414, 359-367 (2001).</li>
<li>Goodenough, J. B., Kim, Y. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Challenges+for+Rechargeable+Li+Batteries%5BTitle%5D)+AND+%22Chemical+Materials%22%5BJournal%5D)">Challenges for Rechargeable Li Batteries.</a> Chemical Materials. 22, 587-603 (2010).</li>
<li>Ceder, G. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Identification+of+cathode+materials+for+lithium+batteries+guided+by+first-principles+calculations%5BTitle%5D)+AND+%22Nature%22%5BJournal%5D)">Identification of cathode materials for lithium batteries guided by first-principles calculations.</a> Nature. 392, 694-696 (1998).</li>
<li>Chung, S. Y., Bloking, J. T., Chiang, Y. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Electronically+conductive+phospho-olivines+as+lithium+storage+electrodes%5BTitle%5D)+AND+%22Nature+Materials%22%5BJournal%5D)">Electronically conductive phospho-olivines as lithium storage electrodes.</a> Nature Materials. 1, 123-128 (2002).</li>
<li>Bruce, P. G., Scrosati, B., Tarascon, J. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Nanomaterials+for+rechargeable+lithium+batteries%5BTitle%5D)+AND+%22Angewandte+Chemie-International+Edition%22%5BJournal%5D)">Nanomaterials for rechargeable lithium batteries.</a> Angewandte Chemie-International Edition. 47, 2930-2946 (2008).</li>
<li>Arico, A. S., Bruce, P., Scrosati, B., Tarascon, J. M., Van Schalkwijk, W. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Nanostructured+materials+for+advanced+energy+conversion+and+storage+devices%5BTitle%5D)+AND+%22Nature+Materials%22%5BJournal%5D)">Nanostructured materials for advanced energy conversion and storage devices.</a> Nature Materials. 4, 366-377 (2005).</li>
<li>Hochbaum, A. I., Yang, P. D. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Semiconductor+Nanowires+for+Energy+Conversion%5BTitle%5D)+AND+%22Chemical+Reviews%22%5BJournal%5D)">Semiconductor Nanowires for Energy Conversion.</a> Chemical Reviews. 110, 527-546 (2010).</li>
<li>Wang, Y., Cao, G. Z. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Developments+in+nanostructured+cathode+materials+for+high-performance+lithium-ion+batteries%5BTitle%5D)+AND+%22Advanced+Materials%22%5BJournal%5D)">Developments in nanostructured cathode materials for high-performance lithium-ion batteries.</a> Advanced Materials. 20, 2251-2269 (2008).</li>
<li>Kang, B., Ceder, G. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Battery+materials+for+ultrafast+charging+and+discharging%5BTitle%5D)+AND+%22Nature%22%5BJournal%5D)">Battery materials for ultrafast charging and discharging.</a> Nature. 458, 190-193 (2009).</li>
<li>Liu, J., Manthiram, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Improved+Electrochemical+Performance+of+the+5+V+Spinel+Cathode+LiMn1.5Ni0.42Zn0.08O4+by+Surface+Modification%5BTitle%5D)+AND+%22Journal+of+the+Electrochemical+Society%22%5BJournal%5D)">Improved Electrochemical Performance of the 5 V Spinel Cathode LiMn1.5Ni0.42Zn0.08O4 by Surface Modification.</a> Journal of the Electrochemical Society. 156, A66-A72 (2009).</li>
<li>Kayyar, A., Qian, H. J., Luo, J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Surface+adsorption+and+disordering+in+LiFePO4+based+battery+cathodes%5BTitle%5D)+AND+%22Applied+Physics+Letters%22%5BJournal%5D)">Surface adsorption and disordering in LiFePO4 based battery cathodes.</a> Applied Physics Letters. 95, (2009).</li>
<li>Sun, K., Dillon, S. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((A+mechanism+for+the+improved+rate+capability+of+cathodes+by+lithium+phosphate+surficial+films%5BTitle%5D)+AND+%22Electrochemistry+Communications%22%5BJournal%5D)">A mechanism for the improved rate capability of cathodes by lithium phosphate surficial films.</a> Electrochemistry Communications. 13, 200-202 (2011).</li>
<li>Kovalenko, I. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((A+Major+Constituent+of+Brown+Algae+for+Use+in+High-Capacity+Li-Ion+Batteries%5BTitle%5D)+AND+%22Science%22%5BJournal%5D)">A Major Constituent of Brown Algae for Use in High-Capacity Li-Ion Batteries.</a> Science. 333, 75-79 (2011).</li>
</ol>

Pas de conflits d&#39;intérêt déclarés.

Dans notre expérience, l&#39;étape la plus critique dans la préparation de l&#39;électrode de travail est prise boues bonnes relations avec la cohérence. Comme le montre la figure 4, l&#39;excès de NMP dans la suspension peut résulter d&#39;un revêtement fissuré, tout insuffisante NMP peut entraîner un revêtement poreux. Dans le travail présenté ici, CR2032 pile bouton cas qui sont 20 mm de diamètre sont utilisés. Il convient de noter que les cas de cellules de pièces de monnaie de tailles différentes p...

<table border="1"><tbody><tr><td> Nom du réactif </td><td> Entreprise </td><td> Numéro de catalogue </td></tr><tr><td> Poly (fluorure de vinylidène) </td><td> Sigma-Aldrich </td><td> 182702 </td></tr><tr><td> 1-méthyl-2-pyrrolidinone, 99,5% </td><td> Alfa Aesar </td><td> 31903 </td></tr><tr><td> LiCoO 2 </td><td> Alfa Aesar </td><td> 42090 </td></tr><tr><td> Le noir de carbone, l&#39;acétylène, + 99,9% </td><td> Alfa Aesar </td><td> 39724 </td></tr><tr><td> LiPF 6 en CE: DMC: DEC </td><td> MTI Corporation </td><td> EQ-Be-LiPF6 </td></tr><tr><td> Séparateur Celgard </td><td> Celgard </td><td> C480 </td></tr><tr><td> Console de mixage Vortex analogique </td><td> VWR </td><td> 58816-121 </td></tr><tr><td> Étuve à vide </td><td></td><td></td></tr><tr><td> Videpomper </td><td></td><td></td></tr><tr><td> Presse hydraulique </td><td></td><td></td></tr><tr><td> Cas Pile bouton </td><td> MTI Corporation </td><td> EQ-CR2032-CASE-304 </td></tr><tr><td> Le printemps et l&#39;entretoise </td><td> MTI Corporation </td><td> EQ-CR20SprSpa-304 </td></tr><tr><td> Boîte à gants </td><td> MBraun </td><td> UNILAB </td></tr><tr><td> Testeur de batterie </td><td> Arbin Instruments </td><td> BT2143 </td></tr></tbody></table>

construction et d&#39;essai des piles de batteries lithium-ion

Construction and Testing of Coin Cells of Lithium Ion Batteries

Les batteries rechargeables lithium-ion ont de larges applications dans l&#39;électronique, où les clients exigent toujours plus de capacité et une plus longue vie. Les batteries au lithium-ion ont aussi été considérés pour être utilisé dans les véhicules électriques et hybrides 1 ou même de systèmes électriques de stabilisation de la grille 2. Toutes ces applications de simuler une augmentation spectaculaire dans la recherche et le développement de matériaux pour batteries 3-7, y compris de nouveaux matériaux 3,8, le dopage 9, 10-13, nanostructuration des revêtements ou des modifications de surfaces 14-17 et nouveaux liants 18. Par conséquent, un nombre croissant de physiciens, chimistes et spécialistes des matériaux ont récemment aventurés dans ce domaine. Piles sont largement utilisés dans les laboratoires de recherche pour tester les matériaux de la nouvelle batterie, même pour la recherche et le développement que les applications cibles à grande échelle et de forte puissance, cellules petite pièce de monnaie sont souvent utilisés pour tester les capacités et les moyens de tauxnouveaux matériaux dans la phase initiale. En 2010, nous avons commencé la National Science Foundation (NSF) a parrainé des projets de recherche pour étudier la surface d&#39;adsorption et de désordre dans les matériaux pour batteries (subvention n. DMR-1006515). Dans la phase initiale de ce projet, nous avons eu du mal à apprendre les techniques de montage et de tester les cellules de pièces de monnaie, qui ne peuvent pas être obtenus sans l&#39;aide de nombreux chercheurs d&#39;autres universités dans d&#39;autres (par le biais des appels fréquents, les échanges par courrier électronique et deux visites de sites). Ainsi, nous pensons qu&#39;il est bénéfique pour documenter, à la fois par texte et vidéo, un protocole d&#39;assemblage et de test d&#39;une cellule pièce de monnaie, ce qui aidera d&#39;autres nouveaux chercheurs dans ce domaine. Cet effort représente le «impact plus large des« activités de notre projet NSF, et il sera également aider à éduquer et inspirer les élèves. Dans cet article, vidéo, nous documenter un protocole d&#39;assembler une cellule bouton CR2032 avec un LiCoO 2 électrode de travail, une contre-électrode Li,et (l essentiellement couramment utilisé) fluorure de polyvinylidène (PVDF) servant de liant. Afin d&#39;assurer de nouveaux apprenants à répéter facilement le protocole, nous gardons le protocole le plus précis et explicite que nous le pouvons. Cependant, il est important de noter que dans la recherche spécifique et le travail de développement, de nombreux paramètres adoptée ici peut être modifiée. Tout d&#39;abord, on peut rendre les cellules de pièces de monnaie de différentes tailles et de tester l&#39;électrode de travail contre une contre-électrode autre que Li. Deuxièmement, les montants de C en noir et liant ajouté dans les électrodes de travail sont souvent modifiées en fonction de l&#39;usage particulier de la recherche, par exemple, de grandes quantités de C noir ou même poudre inerte ont été ajoutés à l&#39;électrode de travail pour tester le «intrinsèque» des performances de 14 matériaux de cathode. Troisièmement, les liants mieux (autre que PVDF) ont également mis au point et utilisé 18. Enfin, d&#39;autres types d&#39;électrolytes (au lieu de LiPF 6) peut également être utilisé, en fait, certains matériaux d&#39;électrodes à haute tension, il faudra les utilisations de electrol spécialeytes 7.

Un protocole de construire et de tester les cellules de pièces de monnaie de batteries lithium-ion est décrite. Les procédures spécifiques de fabrication d&#39;une électrode de travail, la préparation d&#39;un contre-électrode, l&#39;assemblage d&#39;une cellule à l&#39;intérieur une boîte à gants et la cellule test sont présentées.

Construction et d&#39;essai des Piles de batteries lithium-ion

Les batteries rechargeables au lithium-ion trouvent de larges applications dans l'électronique, où les clients exigent systématiquement une capacité accrue et une durée de vie plus longue. Le lithium-ion...

L'objectif général de cette procédure est de préparer et de tester des demi-piles bouton pour la recherche en laboratoire. Préparez tout d'abord une électrode active, une électrode auxiliaire et d'autres composants de la cellule. Assemblez ensuite soigneusement la pile bouton dans une boîte à gants et scellez-la par sertissage.Enfin, effectuez des tests électrochimiques de la pile bouton afin de déterminer ses propriétés clés telles que les capacités de charge et de décharge, les performances en fonction du taux, et d'autres informations précieuses sur la pile bouton. En général, la fabrication de la cellule est délicate, car les performances de celle-ci sont très sensibles au protocole de montage. Préparez tout d'abord un mélange liant NMP composé d'environ six parties de liant PVDF à 8 % dans le NMP.Ensuite, mélangez le matériau actif et le noir d'acétylène par vortex pendant une minute. Après avoir ajouté un peu de mélange liant NMP, transférez les ingrédients dans un petit flacon en verre. Vortexez l'échantillon à la vitesse maximale en tr/min pendant environ 30 minutes.Si nécessaire, ajoutez deux billes en zircone de cinq millimètres de diamètre pour un meilleur mélange. Conti

construction-and-testing-of-coin-cells-of-lithium-ion-batteries

Research

Recherche

JoVE Journal

Engineering

Ingénierie

Batteries au lithium-ion utilisent des électrolytes organiques inflammables et volatils qui sont adaptés aux applications de la température ambiante. Une alternative plus sûre aux électrolytes organiques sont des piles de polymère solide. Batteries polymères solides fonctionnent en toute sécurité à des températures élevées (&gt; 120 ° C), les rendant ainsi applicable aux applications à haute température tels que le forage pétrolier profond et véhicules électriques hybrides. Le présent document...

Solid-state greffe électrolytes de copolymère pour le lithium applications de batteries

Nous décrivons l'utilisation de rayonnement synchrotron à rayons X spectroscopie d'absorption (XAS) et diffraction des rayons X (XRD) techniques pour sonder les détails des processus d'intercalation / désintercalation dans de matériaux d'électrodes pour les batteries Li-ion et Na-ion. In situ et ex situ des expériences sont utilisés pour comprendre le comportement structurelles sur le fonctionnement des dispositifs...

Caractérisation des Matériaux pour électrodes au lithium-ion et ion sodium utilisant des techniques de rayonnement synchrotron

Nous décrivons la conception et la construction d'une cellule électrochimique pour l'examen des matériaux d'électrode en utilisant in situ diffraction de poudre de neutrons (NPD). Nous commentons brièvement sur ​​deux dans la conception des cellules NPD in situ et de discuter des méthodes pour l'analyse de la correspondante de données NPD in situ produites en utilisant cette cellule.

In Situ diffraction de poudre, l&#39;utilisation des batteries au lithium-ion sur mesure

Le traitement des électrodes non aqueuses est essentiel à la construction des piles boutons et à l’évaluation de nouvelles chimies d’électrodes pour les batteries lithium-ion. Un guide étape par étape des pratiques de base nécessaires en tant qu’ingénieur électrochimiste travaillant avec des batteries dans un cadre expérimental académique est fourni.

Traitement d&#39;électrode non-aqueux et construction de cellules lithium-ion, Monnaies

Un protocole pour l’essai électrochimique d’une batterie Li-O2 aprotique avec préparation d’électrodes et d’électrolytes et une introduction des méthodes de caractérisation fréquemment utilisées est présenté ici.

Protocole de test électrochimiques et caractérisation de aprotique Li-O<sub&gt; 2</sub&gt; Batterie

Ici, nous décrivons des protocoles pour préparer des électrolytes de sel de bis(trifluorométhane)sulfonimide à base de phosphonium, et assembler une pile bouton lithium-ion ininflammable et fonctionnant à haute température.

Synthèse du liquide ionique à base de Electrolytes, Assemblée des batteries Li-ion, et des mesures de performance à haute température

Un protocole pour la fabrication de micro-batterie électrochimiquement actives LiPON-basé à semi-conducteurs au lithium-ion à l’aide d’un faisceau ionique focalisé est présenté.

Fabrication de faisceau ionique focalisé de Lithium-ion à l’état solide axée sur les LiPON micro-batterie pour In Situ essais

Les cellules de trois électrodes sont utiles dans l’étude de l’électrochimie des batteries lithium-ion. Une telle configuration électrochimique permet les phénomènes associés à l’anode et la cathode d’être découplés et examiné indépendamment. Nous présentons ici un guide pour la construction et l’utilisation d’une cellule de trois électrodes pièce en mettant l’accent sur le lithium analytique de placage.

Pièce de trois électrodes cellule préparation et électrodéposition Analytique pour Batteries Lithium-ion

Nous présentons ici un protocole pour la fabrication et la préparation d’une cellule de liquide de graphène pour in situ l’observation microscopie électronique à transmission, ainsi qu’une synthèse de matériaux d’électrodes et essais de cellules de batterie électrochimique.

Préparation des cellules de graphène liquide pour l’Observation du matériel de batterie au Lithium-ion

Ces travaux visent à déterminer la cinétique de réaction des matériaux de cathode et d’anode de batterie Li-ion subissant un emballement thermique (TR). Le spectromètre d’analyse thermique simultanée (STA)/infrarouge à transformée de Fourier (FTIR) et la spectrométrie de masse par chromatographie en phase gazeuse (GC-MS) ont été utilisés pour révéler des événements thermiques et détecter les gaz dégagés.

l’identification et la quantification des mécanismes de décomposition dans les batteries lithium-ion; Entrée dans la simulation de flux de chaleur pour la modélisation de l’emballement thermique

Apprenez à construire et tester des demi-piles bouton lithium-ion en boîte à gants. Cette méthode détaille la préparation des électrodes, l'assemblage hermétique et les tests électrochimiques pour évaluer les capacités de charge.

Construction et d'essai des Piles de batteries lithium-ion

Explorer plus de vidéos