Name: Preparazione di schiume in fibra di carbonio e fibra di bambù rinforzate con poli (butilene adipato-co-tereftalato) mediante schiumatura di anidride carbonica supercritica (Video) | JoVE Journal
Uploaded: 2025-10-10T13:35:00.000+00:00
Duration: 7 min 56 s
Description: Scopri la preparazione di schiume rinforzate con fibra di carbonio e fibra di bambù in matrice PBAT mediante schiumatura con anidride carbonica supercritica. Questo metodo migliora le proprietà meccaniche e riduce il restringimento per applicazioni sostenibili.

ai_agent_IP

ai_agent

maintenance

instantTrialDurationMinutes

isBiopharma

enableNewMyJoveSectionDesign

educationFeatures

seoMetaApi

ai_copilot_institution_blacklist

ai_chat_institution_blacklist

freeAccessWindow

ssoRoleCapture

scheduledMaintenanceBanner

joveLabsFeatures

disable_autoplay_for_bots

extended_trial_duration

5 minutes

playerTrialDesktop

<ol><li>Xu, X., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Material+performance%2C+manufacturing+methods%2C+and+engineering+applications+in+aviation+of+carbon+fiber+reinforced+polymers%3A+A+comprehensive+review%5BTitle%5D)+AND+%22Thin+Wall+Struct%22%5BJournal%5D)">Material performance, manufacturing methods, and engineering applications in aviation of carbon fiber reinforced polymers: A comprehensive review.</a> Thin Wall Struct. 209, 112899(2025).</li>
<li>Wang, Z., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Fabrication+of+biodegradable+poly%28butylene+adipate-co-butylene+terephthalate%29+bead+foams+through+solid+utilization+of+chitin+and+controllable+incorporation+of+porous+structure%5BTitle%5D)+AND+%22Colloids+Surf+A+Physicochem+Eng+Asp%22%5BJournal%5D)">Fabrication of biodegradable poly(butylene adipate-co-butylene terephthalate) bead foams through solid utilization of chitin and controllable incorporation of porous structure.</a> Colloids Surf A Physicochem Eng Asp. 693, 134105(2024).</li>
<li>Wang, J., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Strong+and+thermally+insulating+polylactic+acid%2Fglass+fiber+composite+foam+fabricated+by+supercritical+carbon+dioxide+foaming%5BTitle%5D)+AND+%22Int+J+Biol+Macromol%22%5BJournal%5D)">Strong and thermally insulating polylactic acid/glass fiber composite foam fabricated by supercritical carbon dioxide foaming.</a> Int J Biol Macromol. 138, 144-155 (2019).</li>
<li>Li, J., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Environmentally-friendly%2C+sustainable+ScCO2-assisted+fabrication+of+poly%28lactic+acid%29%2Framie+fiber+composite+foams%5BTitle%5D)+AND+%22J+Clean+Prod%22%5BJournal%5D)">Environmentally-friendly, sustainable ScCO2-assisted fabrication of poly(lactic acid)/ramie fiber composite foams.</a> J Clean Prod. 425, 138952(2023).</li>
<li>Li, S., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Research+progress+on+the+improvement+strategy+of+foaming+behavior+for+biodegradable+polymer+foams+and+their+functional+applications%5BTitle%5D)+AND+%22Sustain+Mater+Technol%22%5BJournal%5D)">Research progress on the improvement strategy of foaming behavior for biodegradable polymer foams and their functional applications.</a> Sustain Mater Technol. 44, e01354(2025).</li>
<li>Wang, Z., Wang, G., Xu, Z., Zhang, A., Li, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((A+novel+%26%2334%3Breinforcing-foaming-recovering%26%2334%3B+strategy+for+achieving+thermally+insulating+green+foams+with+ultrafast+degradation%5BTitle%5D)+AND+%22J+Clean+Prod%22%5BJournal%5D)">A novel &#34;reinforcing-foaming-recovering&#34; strategy for achieving thermally insulating green foams with ultrafast degradation.</a> J Clean Prod. 481, 144161(2024).</li>
<li>Wang, Z., Wang, G., Xu, Z., Chai, J., Zhao, G. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Innovative+crosslinking+and+foaming+strategies+for+advancing+biodegradable+composite+foams%3A+Enhancing+foamability%2C+flexibility%2C+and+thermal+insulation%5BTitle%5D)+AND+%22Mater+Des%22%5BJournal%5D)">Innovative crosslinking and foaming strategies for advancing biodegradable composite foams: Enhancing foamability, flexibility, and thermal insulation.</a> Mater Des. 253, 113895(2025).</li>
<li>Jian, J., Xiangbin, Z., Xianbo, H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((An+overview+on+synthesis%2C+properties+and+applications+of+poly%28butylene-adipate-co-terephthalate%29-PBAT%5BTitle%5D)+AND+%22Adv+Ind+Eng+Polym+Res%22%5BJournal%5D)">An overview on synthesis, properties and applications of poly(butylene-adipate-co-terephthalate)-PBAT.</a> Adv Ind Eng Polym Res. 3 (1), 19-26 (2020).</li>
<li>Wang, Z., Wang, G., Xu, Z., Ma, C., Zhao, G. Pore-gradient, flexible, and fully-degradable foam with outstanding noise absorption and thermal insulation. <a target="_blank" href="http://scholar.google.com/scholar?hl=en&safe=off&q=author%3aWang%2C+Z+%22Adv+Funct+Mater%22">Adv Funct Mater</a>. , (2025).</li>
<li>Wang, Z., Wang, G., Xu, Z., Yang, C., Zhao, G. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Structure-tunable+poly%28butylene+adipate-CO-terephthalate%29+foams+with+enhanced+mechanical+performance+derived+by+microcellular+foaming+with+carbon+dioxide+as+blowing+agents%5BTitle%5D)+AND+%22J+CO2+Util%22%5BJournal%5D)">Structure-tunable poly(butylene adipate-CO-terephthalate) foams with enhanced mechanical performance derived by microcellular foaming with carbon dioxide as blowing agents.</a> J CO2 Util. 72, 102495(2023).</li>
<li>Wang, Z., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((low-shrinkage+and+high+elastic+poly%28butylene+adipate-co-terephthalate%29+foams+achieved+by+microcellular+foaming+using+N2+%26+CO2+as+co-blowing+agents%5BTitle%5D)+AND+%22J+CO2+Util%22%5BJournal%5D)">low-shrinkage and high elastic poly(butylene adipate-co-terephthalate) foams achieved by microcellular foaming using N2 & CO2 as co-blowing agents.</a> J CO2 Util. 64, 102149(2022).</li>
<li>Ding, Y., Yang, Q., Wang, X., Li, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((The+compressive+resilience+and+shrinkage+resistance+properties+of+poly%28butylene+adipate-co-terephthalate%29+microcellular+composite+foams+reinforced+by+functionalized+microcrystalline+cellulose%5BTitle%5D)+AND+%22Int+J+Biol+Macromol%22%5BJournal%5D)">The compressive resilience and shrinkage resistance properties of poly(butylene adipate-co-terephthalate) microcellular composite foams reinforced by functionalized microcrystalline cellulose.</a> Int J Biol Macromol. 306, 141466(2025).</li>
<li>Pereira Da Silva, J. S., Farias Da Silva, J. M., Soares, B. G., Livi, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Fully+biodegradable+composites+based+on+poly%28butylene+adipate-co-terephthalate%29%2Fpeach+palm+trees+fiber%5BTitle%5D)+AND+%22Compos+B+Eng%22%5BJournal%5D)">Fully biodegradable composites based on poly(butylene adipate-co-terephthalate)/peach palm trees fiber.</a> Compos B Eng. 129, 117-123 (2017).</li>
<li>Liu, H., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((High+strength+microcellular+thermoplastic+polyimide%2Fcarbon+fiber+composite+foams+containing+flexible+ether+amine%2C+rigid+diaminodiphenyl+ether%2C+and+triaminopyrimidine+moieties%3A+Synthesis+and+fabrication%5BTitle%5D)+AND+%22Chem+Eng+J%22%5BJournal%5D)">High strength microcellular thermoplastic polyimide/carbon fiber composite foams containing flexible ether amine, rigid diaminodiphenyl ether, and triaminopyrimidine moieties: Synthesis and fabrication.</a> Chem Eng J. 496, 154384(2024).</li>
<li>Li, W., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Real-microcellular+poly%28ether-block-amide%29%2Fcarbon+fiber+foams+with+improved+mechanical+property+and+surface+quality+for+high-performance+electromagnetic+interference+shielding+applications%5BTitle%5D)+AND+%22J+Mater+Res+Technol%22%5BJournal%5D)">Real-microcellular poly(ether-block-amide)/carbon fiber foams with improved mechanical property and surface quality for high-performance electromagnetic interference shielding applications.</a> J Mater Res Technol. 26, 6508-6519 (2023).</li>
<li>Liu, Y., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Supercritical+N2+induced+sandwich+type+lightweight+and+strong+PP%2FCF+foams+with+excellent+electromagnetic+shielding+properties%5BTitle%5D)+AND+%22Chem+Eng+J%22%5BJournal%5D)">Supercritical N2 induced sandwich type lightweight and strong PP/CF foams with excellent electromagnetic shielding properties.</a> Chem Eng J. 501, 157532(2024).</li>
<li>Qiao, Y., Hou, J., Tian, D., He, Y., Chen, J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Poly%28butylene+adipate-co-terephthalate%29%2Fcarbon+fiber+foam+bonded+with+continuous+carbon+fiber+reinforced+polypropylene+prepregs+for+electromagnetic+interference+shielding%5BTitle%5D)+AND+%22Compos+Commun%22%5BJournal%5D)">Poly(butylene adipate-co-terephthalate)/carbon fiber foam bonded with continuous carbon fiber reinforced polypropylene prepregs for electromagnetic interference shielding.</a> Compos Commun. 53, 102217(2025).</li>
<li>Tang, Q., Fang, L., Guo, W. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Effects+of+bamboo+fiber+length+and+loading+on+mechanical%2C+thermal+and+pulverization+properties+of+phenolic+foam+composites%5BTitle%5D)+AND+%22J+Bioresour+Bioprod%22%5BJournal%5D)">Effects of bamboo fiber length and loading on mechanical, thermal and pulverization properties of phenolic foam composites.</a> J Bioresour Bioprod. 4 (1), 51-59 (2019).</li>
<li>Li, X., Zhong, T., Xiao, Y., Cheng, H., Chen, H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Mechanically+robust%2C+thermal+insulating+sustainable+foams+fully+derived+from+bamboo+fibers+through+high+temperature+drying%5BTitle%5D)+AND+%22Carbohydr+Polym%22%5BJournal%5D)">Mechanically robust, thermal insulating sustainable foams fully derived from bamboo fibers through high temperature drying.</a> Carbohydr Polym. 333, 121966(2024).</li>
<li>Guo, W., Zhao, J., Zhao, F., Feng, T., Liu, L. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Assessment+of+properties+of+bamboo+fiber+and+EPDM+reinforced+polypropylene+microcellular+foam+composites%5BTitle%5D)+AND+%22Polymer+%28Guildf%29%22%5BJournal%5D)">Assessment of properties of bamboo fiber and EPDM reinforced polypropylene microcellular foam composites.</a> Polymer (Guildf). 304, 127142(2024).</li>
<li>Liu, H., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Green+strategy+based+on+supercritical-fluid+foaming+for+fabricating+rigid+microcellular+thermoplastic+polyimide+foams+with+ultrahigh+compressive+strength%5BTitle%5D)+AND+%22Compos+B+Eng%22%5BJournal%5D)">Green strategy based on supercritical-fluid foaming for fabricating rigid microcellular thermoplastic polyimide foams with ultrahigh compressive strength.</a> Compos B Eng. 273, 111204(2024).</li>
<li>Sarver, J. A., Kiran, E. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Foaming+of+polymers+with+carbon+dioxide+-+The+year-in-review+2019%5BTitle%5D)+AND+%22J+Supercrit+Fluids%22%5BJournal%5D)">Foaming of polymers with carbon dioxide - The year-in-review 2019.</a> J Supercrit Fluids. 173, 105166(2021).</li>
<li>Dong, M., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((An+overview+of+polymer+foaming+assisted+by+supercritical+fluid%5BTitle%5D)+AND+%22Adv+Compos+Hybrid+Mater%22%5BJournal%5D)">An overview of polymer foaming assisted by supercritical fluid.</a> Adv Compos Hybrid Mater. 6 (6), 207(2023).</li>
<li>Zhang, X., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Green+preparation+of+lightweight+and+elastic+poly%28butylene+adipate-co-terephthalate%29%2Fthermoplastic+polyamide+elastomer+composite+foams%5BTitle%5D)+AND+%22J+Supercrit+Fluids%22%5BJournal%5D)">Green preparation of lightweight and elastic poly(butylene adipate-co-terephthalate)/thermoplastic polyamide elastomer composite foams.</a> J Supercrit Fluids. 223, 106635(2025).</li>
<li>Pang, Y., Cao, Y., Zheng, W., Park, C. B. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((A+comprehensive+review+of+cell+structure+variation+and+general+rules+for+polymer+microcellular+foams%5BTitle%5D)+AND+%22Chem+Eng+J%22%5BJournal%5D)">A comprehensive review of cell structure variation and general rules for polymer microcellular foams.</a> Chem Eng J. 430, 132662(2022).</li>
</ol>

<table><tbody><tr><td>Fibra di bambù</td><td>Sichuan Lvzhu Plant Fiber Co., Ltd., Cina</td><td>1000 mesh</td><td>Materia prima fornita per il lavoro sperimentale</td></tr><tr><td>Pompa di supporto</td><td>Dongguan Suncenter Fuild Control Equipment Co., Ltd., Cina</td><td>DGA15C</td><td>Utilizzato per controllare la pressione</td></tr><tr><td>Anidride carbonica</td><td>Harbin Qinghua Industrial Gas Co. Ltd., Cina</td><td>Purezza del 99,9%</td><td>Utilizzato come agente schiumoso</td></tr><tr><td>Fibra di carbonio & nbsp;</td><td>Toray Industries Incorporated, &nbsp; Giappone</td><td>1000 mesh</td><td>Materia prima fornita per il lavoro sperimentale</td></tr><tr><td>Ceactor</td><td>Zhengzhou Zechen Instrument Equipment Co., Ltd., Cina</td><td>0,5 L</td><td>Usato come contenitore schiumoso</td></tr><tr><td>Compattatore</td><td>Zhejiang Kaishan Compressor Co., Ltd., Cina</td><td>XK06-010-00487</td><td>pressurizzato</td></tr><tr><td>Bagno d'olio digitale</td><td>Boho Temptech Co., Ltd., Cina</td><td>HH-5-12L</td><td>Usato per riscaldare</td></tr><tr><td>Forno di essiccazione</td><td>Shanghai Yiheng Scientific Instrument Co., Ltd., Cina</td><td>DGG-9070</td><td>Usata per essiccare le materie prime</td></tr><tr><td>Bilanciamento elettronico</td><td>Mettler Toledo (Changzhou) Sistema di Pesatura Co., Ltd</td><td>SPN501F</td><td>Utilizzato per pesare materie prime</td></tr><tr><td>Strumento di solforizzazione a piastra piatta</td><td>Bolon Precision Testing Machines Co., Ltd., Cina</td><td>BL-6170-A</td><td>Per lo stampaggio a compressione a caldo di compositi</td></tr><tr><td>Densimetro solido ad alta precisione</td><td>Yuemang Intelligent Equipment Co., Ltd., Cina</td><td>JHY-120Y</td><td>Dispositivo usato per determinare&nbsp; Densità</td></tr><tr><td>Software di analisi delle immagini Istituti Nazionali di Salute</td><td>Istituti Nazionali di Salute</td><td>ImageJ</td><td>Software utilizzato per determinare le caratteristiche morfologiche della schiuma</td></tr><tr><td>Poli (butilene adipato-co-tereftalato)</td><td>Xinjiang Blue Ridge Tunhe Sci.&amp; Tech. Co., Ltd., Cina</td><td>TH801T</td><td>Materia prima fornita per il lavoro sperimentale</td></tr><tr><td>Film politetrafluoroetilene</td><td>Società di Commercio dei Materiali Plastici Luo Huixing, Cina</td><td>0,5 mm</td><td>Usata per demoldare</td></tr><tr><td>Pulveriser</td><td>Shenzhen Chengzhongsheng Electromechanical Technology Co., Ltd., Cina</td><td>380 W, 50 Hz</td><td>Usato per schiacciare e granulare</td></tr><tr><td>Scanner</td><td>FEI Inc., USA</td><td>QUANTA 220</td><td>Scanner utilizzato per scattare immagini di schiume</td></tr><tr><td>Estrusore a doppia vite</td><td>Nanchino Jiente Machine Point Co. Ltd., Cina</td><td>SHJ-20</td><td>Miscelazione per fusione</td></tr><tr><td>Macchina universale per il test meccanico</td><td>Wance Technologies Ltd., Cina</td><td>TestPilot X10A</td><td>Utilizzato per misurare le prestazioni di compressione</td></tr></tbody></table>

preparazione di schiume in fibra di carbonio e fibra di bambù rinforzate con poli (butilene adipato-co-tereftalato) mediante schiumatura di anidride carbonica supercritica

Preparation of Carbon Fiber and Bamboo Fiber Reinforced Poly (butylene Adipate-co-terephthalate) Foams by Supercritical Carbon Dioxide Foaming

Preparazione di schiume in fibra di carbonio e fibra di bambù rinforzate con poli (butilene adipato-co-tereftalato) mediante schiumatura di anidride carbonica supercritica

Fiber-reinforced polymer foams have found extensive applications across numerous fields. Particularly, poly (butylene adipate-co-terephthalate) (PBAT) has ...

preparation-carbon-fiber-bamboo-fiber-reinforced-poly-butylene

Research

Ricerca

JoVE Journal

Engineering

Ingegneria

Vi presentiamo un nuovo metodo di produzione di brevi preformati di fibre naturali rigidi e robusti con un processo di fabbricazione della carta. Cellulosa batterica agisce contemporaneamente come legante per le fibre sciolte e fornisce rigidità alla preformati di fibre. Queste preforme possono essere infuse con una resina per la produzione di compositi gerarchici veramente verdi.

Produzione robusta fibra naturale preforme Utilizzando batterica cellulosa come Binder

La replica è una delle tecniche di lavorazione utilizzate per la produzione di spugne metalliche porose. In questo articolo viene mostrata in dettaglio un'implementazione del metodo per la produzione di alluminio poroso a celle aperte.

Casting protocolli per la produzione di cellule aperte alluminio Schiume dalla tecnica di replica e l&#39;effetto sulla porosità

Questo metodo video descrive la sintesi di materiali monolitici a base di grafene 3D ad alta superficie derivati da precursori polimerici e ossido di grafene a strato singolo.

Sintesi e funzionalizzazione di 3D Materials Nano-grafene: grafene Aerogels e grafene Assemblee Macro

Viene mostrato un nuovo modo per la produzione di aerogel a base di biopolimeri mediante gelificazione indotta da anidride carbonica (CO2). La tecnica utilizza anidride carbonica pressurizzata (5 MPa) per la produzione di idrogel biopolimerici e CO2 supercritica (12 MPa) per convertire i gel in aerogel. Gli unici solventi necessari oltre alla CO2 sono l'acqua e l'etanolo.

Preparazione del biopolimero Aerogels che utilizzano solventi verdi

Un protocollo per esporre fibre nude sulla superficie del composito eliminando la zona ricca di resina è presentato. Le fibre vengono esposti durante la fabbricazione dei compositi, non mediante il post-trattamento superficiale. I compositi di carbonio esposte presentano alta conduttività elettrica nella direzione di attraverso-spessore ed elevate proprietà meccaniche.

Implementazione sperimentale di un nuovo metodo di fabbricazione compositi: esponendo fibre nude sulla superficie composita dal metodo strato morbido

Presentiamo un nuovo metodo basato su microfluidici per la sintesi di strutture organiche covalenti (COFs). Abbiamo dimostrato come questo approccio possa essere utilizzato per produrre fibre continue di COF, nonché strutture di COF 2D o 3D sulle superfici.

Sintesi microfluidica a base di strutture organiche COF (COF): uno strumento per la produzione continua di fibre COF e stampa diretta su una superficie

Qui presentiamo i protocolli per la preparazione e test catalitica aerogels incorporando specie metalliche nelle piattaforme di aerogel di silice e allumina. Metodi per la preparazione di materiali usando sali di rame e rame-contenente nanoparticelle sono presenti. Catalitica dei protocolli dei test dimostrano l'efficacia di questi aerogel per applicazioni di catalisi di tre vie.

Fabbricazione e collaudo di aerogel catalitico preparato tramite rapida estrazione supercritica

Un metodo chiamato produzione additiva negativo è usato per produrre vicino carburo del boro complesso completamente densi a forma parti di varie scale di lunghezza. Questa tecnica è possibile tramite la formulazione di una sospensione di romanzo che coinvolge il resorcinolo-formaldeide come agente gelificante unico che lascia dietro di sé un omogeneo carbonio sinterizzazione aiuti dopo la pirolisi.

Produzione additiva negativa del complesso a forma di carburi di boro

In questo articolo viene illustrata la tecnica di espansione una stuoia di nanofibra tradizionale, due dimensioni (2D) elettrofilate in un'impalcatura di tre dimensioni (3D) attraverso la depressurizzazione del sottocritico CO2 fluido. Queste impalcature aumentate 3D, strettamente mimica cellulare nanotopographic spunti e preservare le funzioni delle molecole biologiche incapsulati all'interno delle nanofibre.

Espansione del due-dimensione elettrofilate nanofibre in tre dimensioni ponteggi

Questo documento descrive un protocollo insieme a uno studio comparativo di due tecniche di fabbricazione microfluidica, vale a dire la fotolitografia / incisione a umido / legame termico e l'incisione selettiva indotta dal laser (LES), che sono adatte per condizioni di alta pressione. Queste tecniche costituiscono piattaforme abilitanti per l'osservazione diretta del flusso di fluido in mezzi permeabili surrogati e sistemi fratturati in condizioni di serbatoio.

Tecniche di fabbricazione microfluidiche per test ad alta pressione del trasporto supercritico in schiuma di CO2 su microscala in serbatoi non convenzionali fratturati

È stato sviluppato un versatile processo di estrusione a doppia vite per fornire un efficiente pretrattamento termo-meccanico-chimico sulla biomassa lignocellulosica, che porta ad un aumento delle proporzioni medie delle fibre. Un legante naturale può anche essere aggiunto continuamente dopo la raffinazione delle fibre, portando a pannelli in fibra a base bio-con migliori proprietà meccaniche dopo la pressatura a caldo del materiale estruso ottenuto.

Processo di estrusione a doppia vite per produrre pannelli in fibra rinnovabile

Scopri la preparazione di schiume rinforzate con fibra di carbonio e fibra di bambù in matrice PBAT mediante schiumatura con anidride carbonica supercritica. Questo metodo migliora le proprietà meccaniche e riduce il restringimento per applicazioni sostenibili.

Preparazione di schiume in fibra di carbonio e fibra di bambù rinforzate con poli (butilene adipato-co-tereftalato) mediante schiumatura di anidride carbonica supercritica (Video) | JoVE Journal

Preparazione di schiume in fibra di carbonio e fibra di bambù rinforzate con poli (butilene adipato-co-tereftalato) mediante schiumatura di anidride carbonica supercritica

Esplora altri video