Name: Bereiding van koolstofvezel en bamboevezel versterkt poly (butyleenadipadipaat-co-tereftalaat) schuim door superkritisch kooldioxideschuim (Video) | JoVE Journal
Uploaded: 2025-10-10T13:35:00.000+00:00
Duration: 7 min 56 s
Description: Leer hoe je PBAT-schuim versterkt met koolstofvezel en bamboevezel maakt via superkritisch CO₂-schuimen. Deze methode verbetert krimpweerstand, lichtgewicht eigenschappen en mechanische veerkracht voor duurzame toepassingen.

ai_agent_IP

ai_agent

maintenance

instantTrialDurationMinutes

isBiopharma

enableNewMyJoveSectionDesign

educationFeatures

seoMetaApi

ai_copilot_institution_blacklist

ai_chat_institution_blacklist

freeAccessWindow

ssoRoleCapture

scheduledMaintenanceBanner

joveLabsFeatures

disable_autoplay_for_bots

extended_trial_duration

5 minutes

playerTrialDesktop

<ol><li>Xu, X., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Material+performance%2C+manufacturing+methods%2C+and+engineering+applications+in+aviation+of+carbon+fiber+reinforced+polymers%3A+A+comprehensive+review%5BTitle%5D)+AND+%22Thin+Wall+Struct%22%5BJournal%5D)">Material performance, manufacturing methods, and engineering applications in aviation of carbon fiber reinforced polymers: A comprehensive review.</a> Thin Wall Struct. 209, 112899(2025).</li>
<li>Wang, Z., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Fabrication+of+biodegradable+poly%28butylene+adipate-co-butylene+terephthalate%29+bead+foams+through+solid+utilization+of+chitin+and+controllable+incorporation+of+porous+structure%5BTitle%5D)+AND+%22Colloids+Surf+A+Physicochem+Eng+Asp%22%5BJournal%5D)">Fabrication of biodegradable poly(butylene adipate-co-butylene terephthalate) bead foams through solid utilization of chitin and controllable incorporation of porous structure.</a> Colloids Surf A Physicochem Eng Asp. 693, 134105(2024).</li>
<li>Wang, J., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Strong+and+thermally+insulating+polylactic+acid%2Fglass+fiber+composite+foam+fabricated+by+supercritical+carbon+dioxide+foaming%5BTitle%5D)+AND+%22Int+J+Biol+Macromol%22%5BJournal%5D)">Strong and thermally insulating polylactic acid/glass fiber composite foam fabricated by supercritical carbon dioxide foaming.</a> Int J Biol Macromol. 138, 144-155 (2019).</li>
<li>Li, J., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Environmentally-friendly%2C+sustainable+ScCO2-assisted+fabrication+of+poly%28lactic+acid%29%2Framie+fiber+composite+foams%5BTitle%5D)+AND+%22J+Clean+Prod%22%5BJournal%5D)">Environmentally-friendly, sustainable ScCO2-assisted fabrication of poly(lactic acid)/ramie fiber composite foams.</a> J Clean Prod. 425, 138952(2023).</li>
<li>Li, S., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Research+progress+on+the+improvement+strategy+of+foaming+behavior+for+biodegradable+polymer+foams+and+their+functional+applications%5BTitle%5D)+AND+%22Sustain+Mater+Technol%22%5BJournal%5D)">Research progress on the improvement strategy of foaming behavior for biodegradable polymer foams and their functional applications.</a> Sustain Mater Technol. 44, e01354(2025).</li>
<li>Wang, Z., Wang, G., Xu, Z., Zhang, A., Li, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((A+novel+%26%2334%3Breinforcing-foaming-recovering%26%2334%3B+strategy+for+achieving+thermally+insulating+green+foams+with+ultrafast+degradation%5BTitle%5D)+AND+%22J+Clean+Prod%22%5BJournal%5D)">A novel &#34;reinforcing-foaming-recovering&#34; strategy for achieving thermally insulating green foams with ultrafast degradation.</a> J Clean Prod. 481, 144161(2024).</li>
<li>Wang, Z., Wang, G., Xu, Z., Chai, J., Zhao, G. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Innovative+crosslinking+and+foaming+strategies+for+advancing+biodegradable+composite+foams%3A+Enhancing+foamability%2C+flexibility%2C+and+thermal+insulation%5BTitle%5D)+AND+%22Mater+Des%22%5BJournal%5D)">Innovative crosslinking and foaming strategies for advancing biodegradable composite foams: Enhancing foamability, flexibility, and thermal insulation.</a> Mater Des. 253, 113895(2025).</li>
<li>Jian, J., Xiangbin, Z., Xianbo, H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((An+overview+on+synthesis%2C+properties+and+applications+of+poly%28butylene-adipate-co-terephthalate%29-PBAT%5BTitle%5D)+AND+%22Adv+Ind+Eng+Polym+Res%22%5BJournal%5D)">An overview on synthesis, properties and applications of poly(butylene-adipate-co-terephthalate)-PBAT.</a> Adv Ind Eng Polym Res. 3 (1), 19-26 (2020).</li>
<li>Wang, Z., Wang, G., Xu, Z., Ma, C., Zhao, G. Pore-gradient, flexible, and fully-degradable foam with outstanding noise absorption and thermal insulation. <a target="_blank" href="http://scholar.google.com/scholar?hl=en&safe=off&q=author%3aWang%2C+Z+%22Adv+Funct+Mater%22">Adv Funct Mater</a>. , (2025).</li>
<li>Wang, Z., Wang, G., Xu, Z., Yang, C., Zhao, G. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Structure-tunable+poly%28butylene+adipate-CO-terephthalate%29+foams+with+enhanced+mechanical+performance+derived+by+microcellular+foaming+with+carbon+dioxide+as+blowing+agents%5BTitle%5D)+AND+%22J+CO2+Util%22%5BJournal%5D)">Structure-tunable poly(butylene adipate-CO-terephthalate) foams with enhanced mechanical performance derived by microcellular foaming with carbon dioxide as blowing agents.</a> J CO2 Util. 72, 102495(2023).</li>
<li>Wang, Z., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((low-shrinkage+and+high+elastic+poly%28butylene+adipate-co-terephthalate%29+foams+achieved+by+microcellular+foaming+using+N2+%26+CO2+as+co-blowing+agents%5BTitle%5D)+AND+%22J+CO2+Util%22%5BJournal%5D)">low-shrinkage and high elastic poly(butylene adipate-co-terephthalate) foams achieved by microcellular foaming using N2 & CO2 as co-blowing agents.</a> J CO2 Util. 64, 102149(2022).</li>
<li>Ding, Y., Yang, Q., Wang, X., Li, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((The+compressive+resilience+and+shrinkage+resistance+properties+of+poly%28butylene+adipate-co-terephthalate%29+microcellular+composite+foams+reinforced+by+functionalized+microcrystalline+cellulose%5BTitle%5D)+AND+%22Int+J+Biol+Macromol%22%5BJournal%5D)">The compressive resilience and shrinkage resistance properties of poly(butylene adipate-co-terephthalate) microcellular composite foams reinforced by functionalized microcrystalline cellulose.</a> Int J Biol Macromol. 306, 141466(2025).</li>
<li>Pereira Da Silva, J. S., Farias Da Silva, J. M., Soares, B. G., Livi, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Fully+biodegradable+composites+based+on+poly%28butylene+adipate-co-terephthalate%29%2Fpeach+palm+trees+fiber%5BTitle%5D)+AND+%22Compos+B+Eng%22%5BJournal%5D)">Fully biodegradable composites based on poly(butylene adipate-co-terephthalate)/peach palm trees fiber.</a> Compos B Eng. 129, 117-123 (2017).</li>
<li>Liu, H., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((High+strength+microcellular+thermoplastic+polyimide%2Fcarbon+fiber+composite+foams+containing+flexible+ether+amine%2C+rigid+diaminodiphenyl+ether%2C+and+triaminopyrimidine+moieties%3A+Synthesis+and+fabrication%5BTitle%5D)+AND+%22Chem+Eng+J%22%5BJournal%5D)">High strength microcellular thermoplastic polyimide/carbon fiber composite foams containing flexible ether amine, rigid diaminodiphenyl ether, and triaminopyrimidine moieties: Synthesis and fabrication.</a> Chem Eng J. 496, 154384(2024).</li>
<li>Li, W., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Real-microcellular+poly%28ether-block-amide%29%2Fcarbon+fiber+foams+with+improved+mechanical+property+and+surface+quality+for+high-performance+electromagnetic+interference+shielding+applications%5BTitle%5D)+AND+%22J+Mater+Res+Technol%22%5BJournal%5D)">Real-microcellular poly(ether-block-amide)/carbon fiber foams with improved mechanical property and surface quality for high-performance electromagnetic interference shielding applications.</a> J Mater Res Technol. 26, 6508-6519 (2023).</li>
<li>Liu, Y., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Supercritical+N2+induced+sandwich+type+lightweight+and+strong+PP%2FCF+foams+with+excellent+electromagnetic+shielding+properties%5BTitle%5D)+AND+%22Chem+Eng+J%22%5BJournal%5D)">Supercritical N2 induced sandwich type lightweight and strong PP/CF foams with excellent electromagnetic shielding properties.</a> Chem Eng J. 501, 157532(2024).</li>
<li>Qiao, Y., Hou, J., Tian, D., He, Y., Chen, J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Poly%28butylene+adipate-co-terephthalate%29%2Fcarbon+fiber+foam+bonded+with+continuous+carbon+fiber+reinforced+polypropylene+prepregs+for+electromagnetic+interference+shielding%5BTitle%5D)+AND+%22Compos+Commun%22%5BJournal%5D)">Poly(butylene adipate-co-terephthalate)/carbon fiber foam bonded with continuous carbon fiber reinforced polypropylene prepregs for electromagnetic interference shielding.</a> Compos Commun. 53, 102217(2025).</li>
<li>Tang, Q., Fang, L., Guo, W. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Effects+of+bamboo+fiber+length+and+loading+on+mechanical%2C+thermal+and+pulverization+properties+of+phenolic+foam+composites%5BTitle%5D)+AND+%22J+Bioresour+Bioprod%22%5BJournal%5D)">Effects of bamboo fiber length and loading on mechanical, thermal and pulverization properties of phenolic foam composites.</a> J Bioresour Bioprod. 4 (1), 51-59 (2019).</li>
<li>Li, X., Zhong, T., Xiao, Y., Cheng, H., Chen, H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Mechanically+robust%2C+thermal+insulating+sustainable+foams+fully+derived+from+bamboo+fibers+through+high+temperature+drying%5BTitle%5D)+AND+%22Carbohydr+Polym%22%5BJournal%5D)">Mechanically robust, thermal insulating sustainable foams fully derived from bamboo fibers through high temperature drying.</a> Carbohydr Polym. 333, 121966(2024).</li>
<li>Guo, W., Zhao, J., Zhao, F., Feng, T., Liu, L. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Assessment+of+properties+of+bamboo+fiber+and+EPDM+reinforced+polypropylene+microcellular+foam+composites%5BTitle%5D)+AND+%22Polymer+%28Guildf%29%22%5BJournal%5D)">Assessment of properties of bamboo fiber and EPDM reinforced polypropylene microcellular foam composites.</a> Polymer (Guildf). 304, 127142(2024).</li>
<li>Liu, H., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Green+strategy+based+on+supercritical-fluid+foaming+for+fabricating+rigid+microcellular+thermoplastic+polyimide+foams+with+ultrahigh+compressive+strength%5BTitle%5D)+AND+%22Compos+B+Eng%22%5BJournal%5D)">Green strategy based on supercritical-fluid foaming for fabricating rigid microcellular thermoplastic polyimide foams with ultrahigh compressive strength.</a> Compos B Eng. 273, 111204(2024).</li>
<li>Sarver, J. A., Kiran, E. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Foaming+of+polymers+with+carbon+dioxide+-+The+year-in-review+2019%5BTitle%5D)+AND+%22J+Supercrit+Fluids%22%5BJournal%5D)">Foaming of polymers with carbon dioxide - The year-in-review 2019.</a> J Supercrit Fluids. 173, 105166(2021).</li>
<li>Dong, M., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((An+overview+of+polymer+foaming+assisted+by+supercritical+fluid%5BTitle%5D)+AND+%22Adv+Compos+Hybrid+Mater%22%5BJournal%5D)">An overview of polymer foaming assisted by supercritical fluid.</a> Adv Compos Hybrid Mater. 6 (6), 207(2023).</li>
<li>Zhang, X., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Green+preparation+of+lightweight+and+elastic+poly%28butylene+adipate-co-terephthalate%29%2Fthermoplastic+polyamide+elastomer+composite+foams%5BTitle%5D)+AND+%22J+Supercrit+Fluids%22%5BJournal%5D)">Green preparation of lightweight and elastic poly(butylene adipate-co-terephthalate)/thermoplastic polyamide elastomer composite foams.</a> J Supercrit Fluids. 223, 106635(2025).</li>
<li>Pang, Y., Cao, Y., Zheng, W., Park, C. B. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((A+comprehensive+review+of+cell+structure+variation+and+general+rules+for+polymer+microcellular+foams%5BTitle%5D)+AND+%22Chem+Eng+J%22%5BJournal%5D)">A comprehensive review of cell structure variation and general rules for polymer microcellular foams.</a> Chem Eng J. 430, 132662(2022).</li>
</ol>

<table><tbody><tr><td>Bamboo fiber</td><td>Sichuan Lvzhu Plant Fiber Co.,Ltd., China</td><td>1000 mesh</td><td>Grondstof geleverd voor het experimentele werk</td></tr><tr><td>Boosterpomp</td><td>Dongguan Suncenter Fuild Control Equipment Co.,Ltd., China</td><td>DGA15C</td><td>Gebruikt om druk te regelen</td></tr><tr><td>Koolstofdioxide</td><td>Harbin Qinghua Industrial gases Co. Ltd., China</td><td>99,9% zuiverheid</td><td>Gebruikt als schuimmiddel</td></tr><tr><td>Koolstofvezel</td><td>Toray Industries Incorporated, Japan</td><td>1000 mesh</td><td>Grondstof geleverd voor het experimentele werk</td></tr><tr><td>Ceactor</td><td>Zhengzhou Zechen Instrument Equipment Co., Ltd., China</td><td>0,5 L</td><td>Gebruikt als schuimcontainer</td></tr><tr><td>Compactor</td><td>Zhejiang Kaishan Compressor Co., Ltd., China</td><td>XK06-010-00487</td><td>onder druk</td></tr><tr><td>Digitaal oliebad</td><td>Boho Temptech Co.,Ltd., China</td><td>HH-5-12L</td><td>Gebruikt om te verwarmen</td></tr><tr><td>Droogoven</td><td>Shanghai Yiheng Scientific Instrument Co., Ltd., China</td><td>DGG-9070</td><td>Gebruikt om grondstoffen te drogen</td></tr><tr><td>Elektronische balans</td><td>Mettler Toledo (Changzhou) Weighing Equipment System Co., Ltd</td><td>SPN501F</td><td>Gebruikt om grondstoffen te wegen</td></tr><tr><td>Vlak plaat zwavelisering instrument</td><td>Bolon Precision Testing Machines Co.,Ltd., China</td><td>BL-6170-A</td><td>Voor hete compressievorming van composieten</td></tr><tr><td>Hoge-precisie vaste dichtheidsmeter</td><td>Yuemang Intelligent Equipment Co., Ltd., China</td><td>JHY-120Y</td><td>Apparaat gebruikt om de dichtheid te bepalen</td></tr><tr><td>Beeldanalyse softwareNational Institutes of Health</td><td>National Institutes of Health</td><td>ImageJ</td><td>Software gebruikt voor het bepalen van de morfologische kenmerken van schuim</td></tr><tr><td>Poly(butyleen adipat-co-tereftalaat)</td><td>Xinjiang Blue Ridge Tunhe Sci.& Tech. Co.,Ltd., China</td><td>TH801T</td><td>Grondstof geleverd voor het experimentele werk</td></tr><tr><td>Polytetrafluorethyleen film</td><td>Luo Huixing Plastic Materials Trading Company, China</td><td>0,5 mm</td><td>Gebruikt om te ontvormen</td></tr><tr><td>Pulveriseerder</td><td>Shenzhen Chengzhongsheng Electromechanical Technology Co., Ltd.,China</td><td>380 w, 50 Hz</td><td>Gebruikt om te pletten en te granuleren</td></tr><tr><td>Scanner</td><td>FEI Inc., USA</td><td>QUANTA 220</td><td>Scanner gebruikt voor het maken van een afbeelding van schuimen</td></tr><tr><td>Twee-schroeven extruder</td><td>Nanjing Jiente Machine Point Co. Ltd., China</td><td>SHJ-20</td><td>Smeltmixen</td></tr><tr><td>Universele mechanische testmachine</td><td>Wance Technologies Ltd., China</td><td>TestPilot X10A</td><td>Gebruikt om de compressieprestaties te meten</td></tr></tbody></table>

bereiding van koolstofvezel en bamboevezel versterkt poly (butyleenadipadipaat-co-tereftalaat) schuim door superkritisch kooldioxideschuim

Preparation of Carbon Fiber and Bamboo Fiber Reinforced Poly (butylene Adipate-co-terephthalate) Foams by Supercritical Carbon Dioxide Foaming

Bereiding van koolstofvezel en bamboevezel versterkt poly (butyleenadipadipaat-co-tereftalaat) schuim door superkritisch kooldioxideschuim

Fiber-reinforced polymer foams have found extensive applications across numerous fields. Particularly, poly (butylene adipate-co-terephthalate) (PBAT) has ...

preparation-carbon-fiber-bamboo-fiber-reinforced-poly-butylene

Research

JoVE Journal

Engineering

Techniek

We presenteren een nieuwe werkwijze voor het vervaardigen stijve en robuuste korte natuurlijke vezel preforms met behulp van een papierfabricage proces. Bacteriële cellulose fungeert tegelijkertijd als bindmiddel voor de losse vezels en geeft stijfheid aan de vezel preforms. Deze preforms kunnen worden toegediend met een hars om echt groen hiërarchische composieten te produceren.

Productie Van Robuuste Natural Fiber Preformen Gebruik makend Bacteriële Cellulose als Binder

Replicatie is een van de verwerkingstechnieken die worden gebruikt voor de productie van poreuze metalen sponzen. In dit artikel wordt één implementatie van de methode voor de productie van open cellulaire poreuze aluminium in detail getoond.

Casting Protocollen voor de productie van Open Cell Aluminium schuimen door de Replicatie Techniek en het effect op de porositeit

Deze videomethode beschrijft de synthese van 3D monolithische grafietmaterialen met een hoog oppervlak, afgeleid van polymeervoorlopers, evenals enkellaags grafietoxide.

Synthese en functionalisering van 3D Nano-grafeen Materialen: Grafeen Aerogels en Grafeen Macro Assemblies

Een nieuwe manier voor de productie van biopolymeer-gebaseerde aerogels door middel van kooldioxide (CO2) geïnduceerde gelering wordt getoond. De techniek maakt gebruik van geperst kooldioxide (5 MPa) voor de productie van biopolymeer hydrogels en superkritisch CO2 (12 MPa) om gels om te zetten in aerogels. De enige oplosmiddelen die naast CO2 nodig zijn, zijn water en ethanol.

Bereiding van Biopolymer Aerogels die Groene Oplosmiddelen

Een protocol om bloot blote vezels op het samengestelde oppervlak door het elimineren van hars rijk gebied wordt gepresenteerd. De vezels worden tijdens de fabricage van de composieten, niet door de oppervlakte na de behandeling blootgesteld. De blootgestelde koolstof composieten vertonen hoge elektrische geleidbaarheid in de richting van de via-dikte en hoge mechanische eigenschap.

Experimentele implementatie van een nieuwe methode van de samengestelde Fabrication: bloot blote vezels op het samengestelde oppervlak door de zachte laag-methode

Wij presenteren een nieuwe microfluïdische methode voor synthese van covalente organische kaders (COF's). We tonen aan hoe deze aanpak kan worden gebruikt om continue COF-vezels te produceren, en ook op 2D- of 3D-COF-structuren op oppervlakken.

Microfluïde-gebaseerde synthese van covalente organische kaders (COF&#39;s): een gereedschap voor de continue productie van COF-vezels en directe druk op een oppervlak

Hier presenteren we protocollen voor het voorbereiden en testen van katalytische aerogels door het opnemen van metaal soorten in silica en aluminiumoxide aerogel platformen. Methoden voor het voorbereiden van materialen met behulp van zouten koper en koper-bevattende nanodeeltjes worden gekenmerkt. Katalytische testprotocollen tonen de effectiviteit van deze aerogels voor drieweg katalyse toepassingen.

Fabricage en beproeving van katalytische Aerogels bereid Via snelle superkritische extractie

Een methode genaamd negatieve additieve productie wordt gebruikt om te produceren in de buurt van volledig dichte complexe gevormde borium carbide delen van verschillende lengte schalen. Deze techniek is mogelijk via de formulering van een roman schorsing waarbij resorcinol-formaldehyd als een unieke gelerend agent die een homogene koolstof sinteren steun na pyrolyse achterlaat.

Negatieve additieve vervaardiging van complexe gevormde boor carbiden

Dit artikel demonstreert de techniek van het uitbreiden van een traditionele, twee-dimensie (2D) electrospun nanofiber mat in een drie-dimensie (3D) steiger door de drukverlaging subkritische CO2 vloeistof. Deze augmented steigers zijn 3D, nauw mimic cellulaire nanotopographic signalen, en het behoud van de functies van biologische moleculen ingekapseld binnen de nanofibers.

Expansie van twee-dimensie Electrospun Nanofiber matten in de steigers van de drie-dimensie

Dit document beschrijft een protocol samen met een vergelijkende studie van twee microfluïde fabricagetechnieken, namelijk fotolithografie/wet-etching/thermisch-bonding en Selective Laser-induced Etching (SLE), die geschikt zijn voor hogedrukomstandigheden. Deze technieken vormen het mogelijk maken van platforms voor directe observatie van de vloeistofstroom in surrogaatdoorlatende media en gebroken systemen onder reservoiromstandigheden.

Microfluidic Fabrication Techniques for High-Pressure Testing of Microscale Supercritical CO 2 Foam Transport in Fractured Unconventional Reservoirs Microfluidic Fabrication Techniques for High-Pressure Testing of Microscale Supercritical CO 2 Foam Transport in Fractured Unconventional Reservoirs Microfluidic Fabrication Techniques for High-Pressure Testing of Microscale Supercritical CO2 Foam Transport in Fractured Unconventional Reservoirs Microflu

Er werd een veelzijdig extrusieproces met twee schroeven ontwikkeld om een efficiënte thermomechanochemische voorbehandeling op lignocellulosische biomassa te bieden, wat leidt tot een verhoogde gemiddelde vezelverhouding. Een natuurlijk bindmiddel kan ook continu worden toegevoegd na vezelraffinage, wat leidt tot biogebaseerde vezelplaten met verbeterde mechanische eigenschappen na het hete persing van het verkregen geëxtrudeerde materiaal.

Twin-Screw Extrusieproces om hernieuwbare vezelplaten te produceren

Leer hoe je PBAT-schuim versterkt met koolstofvezel en bamboevezel maakt via superkritisch CO₂-schuimen. Deze methode verbetert krimpweerstand, lichtgewicht eigenschappen en mechanische veerkracht voor duurzame toepassingen.

Bereiding van koolstofvezel en bamboevezel versterkt poly (butyleenadipadipaat-co-tereftalaat) schuim door superkritisch kooldioxideschuim (Video) | JoVE Journal

Bereiding van koolstofvezel en bamboevezel versterkt poly (butyleenadipadipaat-co-tereftalaat) schuim door superkritisch kooldioxideschuim

Meer video's verkennen