Synthesis of Decellularized Cartilage Extracellular Matrix Hydrogels

Summary

This paper introduces a new method for the synthesis of decellularized cartilage extracellular matrix (DC-ECM) hydrogels. DC-ECM hydrogels have excellent biocompatibility and provide a superior microenvironment for cell growth. Therefore, they can be ideal cell scaffolds and biological delivery systems.

Abstract

Decellularized cartilage extracellular matrix (DC-ECM) hydrogels are promising biomaterials for tissue engineering and regenerative medicine due to their biocompatibility and ability to mimic natural tissue properties. This protocol aims to produce DC-ECM hydrogels that closely mimic the native ECM of cartilage tissue. The protocol involves a combination of physical and chemical disruption and enzymatic digestion to remove the cellular material while preserving the structure and composition of the ECM. The DC-ECM is cross-linked using a chemical agent to form a stable and biologically active hydrogel. The DC-ECM hydrogel has excellent biological activity, spatial structure, and biological induction function, as well as low immunogenicity. These characteristics are beneficial in promoting cell adhesion, proliferation, differentiation, and migration and for creating a superior microenvironment for cell growth. This protocol provides a valuable resource for researchers and clinicians in the field of tissue engineering. Biomimetic hydrogels can potentially enhance the development of effective tissue engineering strategies for cartilage repair and regeneration.

Introduction

Cartilage tissue engineering is a rapidly developing field that seeks to regenerate damaged or diseased cartilage tissue¹. One key challenge in this field is the development of biomimetic scaffolds that can support the growth and differentiation of chondrocytes, the cells responsible for producing cartilage². The ECM of cartilage tissue plays a critical role in regulating the behavior of chondrocytes. DC-ECM is an effective scaffold for tissue engineering applications³.

A number of techniques have been developed to produce DC-ECM from cartilage tissue, including chemical, enzymatic, and physical methods. However, these methods often result in the generation of ECM hydrogels that are insufficiently biomimetic, which limits their potential for use in tissue engineering applications^4,5. Thus, there is a need for a more effective method for producing DC-ECM hydrogels.

The development of this technique is important because it can advance the field of tissue engineering by providing a new approach for creating biomimetic scaffolds that can support tissue regeneration and repair. Furthermore, this technique could be easily adapted to produce ECM hydrogels from other tissues, thereby expanding its potential applications.

In the broader body of literature, there has been growing interest in using DC-ECM as a scaffold for tissue engineering applications⁶. Numerous studies have demonstrated the effectiveness of DC-ECM hydrogels in promoting cell growth and differentiation in various tissues, including cartilage^7,8. Therefore, the development of a protocol for producing DC-ECM hydrogels that closely mimic the natural ECM of cartilage tissue is a significant contribution to the field.

The protocol presented in this paper addresses this need by providing a novel method for producing DC-ECM hydrogels that closely mimic the natural ECM of cartilage tissue. The protocol involves decellularizing cartilage tissue, isolating the resulting ECM, and creating a hydrogel by cross-linking the ECM with a biocompatible polymer. The resulting hydrogel has shown promising results in supporting the growth and differentiation of chondrocytes.

Protocol

This study was approved by the Ethics Committee of Tongde Hospital of Zhejiang Province.

1. Preparation of the DC-ECM hydrogel

NOTE: In this study, the cartilage was obtained from the knee joints of 12 month old Bama miniature pigs, avoiding the collection of bone tissue.

1. Take the collected cartilage, and block and chop it into 1-2 mm³ pieces with a scalpel.
2. Place 20 g of the minced cartilage in a 50 mL centrifuge tube, and add 20 mL of hypotonic Tris-HCl buffer (10 mM Tris-HCl, pH 8.0) to submerge the tissue completely. Place the centrifuge tube in a −80 °C freezer for 3 h and then in a 37 °C oven for 3 h. Repeat the freezing and heating step six times. In this step, the hypotonic Tris-HCl buffer does not need replacement.
3. Shake the centrifuge tube for 30 s using a vortex mixer at a speed of 1,000 rpm. Place a stainless-steel sieve (pore size: ~250 µm) on a new 50 mL centrifuge tube.
4. Slowly decant the decellularized cartilage into the stainless-steel sieve, wash the tissue three times with sterile PBS, and collect the cartilage.
5. Add 10 mL of trypsin solution (0.25% trypsin in PBS), and place the tube on a shaker at 37 °C for 24 h. During this period, replace the trypsin every 4 h. Filter the suspension using the stainless-steel sieve, and preserve the tissue. The trypsin can be treated overnight during one of the digestion processes, and this will not affect the final digestion.
6. Wash the trypsinized tissue with hypertonic buffer (1.5 M NaCl, 50 mM Tris-HCl, pH 7.6).
7. Add 10 mL of nuclease solution (50 U/mL deoxyribonuclease and 1 U/mL ribonuclease in 10 mM Tris-HCl, pH 7.5), and place the tube on a shaker at 37 °C for 4 h.
8. Remove the nuclease solution, wash the cartilage three times with sterile PBS, and add hypotonic Tris-HCl solution. Place the centrifuge tube on a shaker, and rinse for 20 h at room temperature (RT).
9. Remove the hypotonic Tris-HCl solution, wash the cartilage three times with sterile PBS, and add 1% Triton X-100 solution to submerge the tissue for 24 h.
10. Remove the Triton X-100 solution, and thoroughly rinse the decellularized cartilage with distilled water for 3 days, changing the distilled water every 12 h.
11. Soak the cartilage in peracetic acid solution (0.1% PAA in 4% ethanol) for 4 h. Remove the peracetic acid solution, and wash the cartilage three times with sterile distilled water.
12. Place the stainless-steel sieve (pore size: ~250 µm) on a 50 mL centrifuge tube. Slowly decant the decellularized cartilage into the stainless-steel sieve, and collect the cartilage. Test the degree of decellularization and the matrix retention of the cartilage by estimating the DNA, collagen, and glycosaminoglycan (GAG) content.
13. Put the decellularized cartilage into a grinding bowl, add liquid nitrogen, and grind the decellularized cartilage to form a powder. Take 2 g of the decellularized cartilage powder, add 80 mL of 0.5 M acetic acid and 20 mg of pepsin, and digest for 24 h. Centrifuge at 400 x g for 10 min; discard the sediment, and collect the supernatant solution (DC-ECM solution).
14. Decant 1 mL of DC-ECM solution per well into 6-well plates. Place the 6-well plates in a lyophilizer. Freeze the DC-ECM solution. Once the temperature in the freeze-dryer drops to −40 °C, turn on the vacuum pump, and maintain the vacuum degree at 10 Pa for 22 h.
15. Take out the freeze-dried DC-ECM solution, place it in centrifuge tubes, and store at −20 °C. The minimum storage period of freeze-dried DC-ECM solution exceeds half a year.
16. Add 1 mL of sterile distilled water to dissolve 20 mg of freeze-dried DC-ECM solution in the centrifuge tube. Shake for 1 min using a vortex mixer at a speed of 1,000 rpm at RT. Add 1 mg of vitamin B2 (0.1% w/v) to the DC-ECM solution, incubate at 37 °C for 60 min, and irradiate with UV light (370 nm, 3.5 mW/cm²) for 3 min to form a hydrogel (DC-ECM hydrogel).

2. Detection of decellularized cartilage

1. DNA content detection of decellularized cartilage
   NOTE: Extract the DNA using the DNEasy Blood & Tissue Kit.
   1. First, take 20 mg of DC-ECM cartilage in a centrifuge tube. Add 180 µL of Buffer GTL and 20 µL of Proteinase K by vortex oscillation, and incubate the cartilage at 56 °C for 4 h until it is completely dissolved.
   2. Shake the centrifuge tube for 15 s using a vortex mixer at a speed of 1,000 rpm at RT. Next, add 200 µL of Buffer GL and anhydrous ethanol, and thoroughly mix by vortex vibration. Centrifuge the samples for 1 min at a speed of 6,000 x g at 4 °C.
   3. Add 500 µL of Buffer GW1 to the adsorption column, and centrifuge the samples for 1 min at a speed of 12,000 x g at 4 °C. Add 500 µL of Buffer GW2 to the adsorption column, and centrifuge at 20,000 x g at 4 °C for 1 min. Finally, add 50 µL of sterilized water to the adsorption column, and centrifuge for 1 min at a speed of 6,000 x g at 4 °C to collect the DNA solution. Determine the DNA content using a spectrophotometer.
2. Collagen content detection in the decellularized cartilage
   1. To detect the collagen content in the decellularized cartilage, use hydroxyproline as a collagen amino acid marker. Acidify 5 mg of decellularized cartilage with 5 mL of 6 M hydrochloric acid at 100 °C for 20 min, and then neutralize it with 5 mL of a 6 M sodium hydroxide solution.
   2. Calculate the content of hydroxyproline by measuring the absorbance of the sample at 570 nm with a spectrophotometer. Obtain a concentration-absorption linear regression using the standard hydroxyproline sample.
3. GAG content detection in the decellularized cartilage
   NOTE: The GAG content in the DC-ECM cartilage was detected using a tissue GAG colorimetric quantitative detection kit. All the reagents below are available in the kit.
   1. Take 200 mg of DC-ECM cartilage powder, and add 500 µL of Reagent A by vortex oscillation. Incubate the sample at 4 °C for 16 h, and then centrifuge at 14,000 x g for 10 min.
   2. Take 50 mL of sample solution, and add 50 µL of high-salt solution (Reagent B) and 50 µL of acid solution(Reagent C) by vortex oscillation. Incubate the sample for 10 min.
   3. Add 750 µL of dye solution (Reagent D) by vortex oscillation, and incubate the sample for 30 min in dark conditions. Centrifuge the sample at 14,000 x g for 10 min, and then discard the supernatant.
   4. Add 1 µL of cleaning solution (Reagent E), and mix well. Centrifuge the sample at 14,000 x g for 10 min, and discard the supernatant.
   5. Add 1 µL of dissociation solution (Reagent F) to the sample, and mix well. Incubate the sample for 30 min under dark conditions. Finally, determine the GAG content using a spectrophotometer at 600 nm.
4. Scanning electron microscope (SEM) and transmission electron microscope (TEM) analysis of the decellularized cartilage
   1. Compare the decellularized cartilage and normal cartilage tissue. Place the sample in a 2.5% glutaraldehyde solution, incubate at 4 °C overnight and then wash with PBS three times.
   2. Fix the sample in 1% OsO4 for 1 h, and then wash three times with PBS.
   3. Dehydrate the sample by sequential immersion in 50%, 70%, 90%, and 100% ethanol, as well as 100% acetone for 15 min each.Place the sample in a mixed solution of hexamethyldisilazane and ethanol (1:1) for 15 min, followed by immersion in pure hexamethyldisilazane for 15 min.
   4. Place the sample in an HCP-2 dryer, and then dry using liquid nitrogen. Then, coat the fully dried specimen with a thin layer of gold-palladium using sputter coating, and image using SEM. The sputter coating was performed at a power of 120 W for 5 min. The experiment was carried out under the following conditions: a working voltage of 15 kV, and a vacuum degree lower than 5 x 10⁻⁵ Pa.
   5. For the TEM analysis, place the sample in a mixture of anhydrous acetone and resin (1:1) for 1 h, followed by a mixture of anhydrous acetone and resin (1:3) for 3 h. Then, place the sample in resin overnight.
      1. Place the sample in embedding medium-filled capsules, and heat at 70 °C for 9 h.
      2. After embedding, cut the specimen into 70 nm thin slices using an ultrafine microtome, and place on a copper mesh.
      3. Pipet 20 µL of uranyl acetate staining solution onto the copper mesh, and stain for 15 min at RT. Remove the staining solution by gently washing the mesh twice with distilled water.
      4. Then, pipet 20 µL of lead citrate staining solution onto the copper mesh, and stain for 15 min at RT. Wash the mesh three times with distilled water.
      5. Place the copper mesh onto a clean Petri dish lined with filter paper. After air-drying, photograph the sections using TEM. The probe was applied with a downward force of 500 nN, scanned at a rate of 1 Hz, and had an elastic constant (k-value) of 40 Nm^-1. The radius of the probe tip was measured to be 8 nm.

Results

To prepare a better DC-ECM cartilage hydrogel, we studied and reviewed the previous literature and compared the various decellularization protocols in terms of the decellularization ratio, immunogenicity, and mechanical functionality⁹.

On this basis, we prepared the DC-ECM cartilage hydrogel and explored the effect of a radially oriented extractive matrix/mesenchymal stem cell exosome bio-ink in treating osteochondral defects. The results showed that the DC-ECM cartilag...

Discussion

This protocol provides a systematic approach for the preparation of decellularized cartilage extracellular matrix hydrogels that closely mimic the native ECM of cartilage tissue. The protocol involves a combination of physical, chemical, and enzymatic disruption to remove cellular material while preserving the structure and composition of the ECM. The protocol's critical steps include adjusting the decellularization time and methods and ensuring complete decellularization.

Compared to other ex...

Materials

List of materials used in this article

Name	Company	Catalog Number	Comments
1 M Tris-HCl, pH7.6	Beyotime	ST776-100 mL
1 M Tris-HCl, pH8.0	Beyotime	ST780-500 mL
-80 °C Freezer	Eppendorf	F440340034
Deoxyribonuclease	Aladdin	D128600-80KU
DNEasy Blood &Tissue Kit	Qiagen	No. 69506
GAG colorimetric quantitative detection kit	Shanghai Haling	HL19236.2
HCP-2 dryer	Hitachi	N/A
Nanodrop8000	Thermo Fisher	N/A	Spectrophotometer
PBS (10x)	Gibco	70011044
Ribonuclease	Aladdin	R341325-100 mg
Sigma500	ZIESS	N/A	Scanning electron microscope
Spectra S	Thermo Fisher	N/A	Transmission electron microscope
Stainless steel sieve	SHXB-Z-1	Shanghai Xinbu
Triton X-100	Beyotime	P0096-500 mL
Trypsin	Gibco	15050065
Ultraviolet lamp	Omnicure 2000	N/A
Vitamin B2	Gibco	R4500-5G
Vortex mixer	Shanghai Qiasen	78HW-1