Name: Cementitious kompozit ve bükülme davranışının hazırlık hizalanmış çelik fiber takviyeli (Video) | JoVE Journal
Uploaded: 2018-06-27T12:30:00.000+00:00
Duration: 11 min 7 s
Description: Öğrenin, manyetik alanla hizalanmış çelik fiber takviyeli çimento esaslı kompozit üretim yöntemini. Bu teknik, malzeme bilimi ve inşaat mühendisliğinde üstün mekanik özellikler sağlar.

ai_agent_IP

ai_agent

maintenance

instantTrialDurationMinutes

isBiopharma

enableNewMyJoveSectionDesign

educationFeatures

seoMetaApi

ai_copilot_institution_blacklist

ai_chat_institution_blacklist

freeAccessWindow

ssoRoleCapture

scheduledMaintenanceBanner

joveLabsFeatures

disable_autoplay_for_bots

extended_trial_duration

5 minutes

Yazarlar, minnetle Ulusal Doğa Bilim Vakfı, Çin'den (Grant No. 51578208), Hebei il Doğa Bilim Vakfı (Grant No finansal destekler kabul E2017202030 ve E2014202178) ve anahtar proje Üniversitesi bilim ve teknoloji araştırma ve Hebei Eyaleti (Grant No ZD2015028).

1. solenoid manyetik alan kurulumu
Not: Manyetik alan içi boş bir oda bir solenoid tarafından oluşturulur. 4-6 kat emaye bakır tel yalıtılmış ve koruma (Şekil 1) için bir plastik yalıtkan tabaka ile sarılmış kıvrılmış bir polybutylene terephthalate (PBT) Yönetim Kurulu solenoid iskelet kurulumudur. Bobin DC'ye bağlantı kurduktan sonra bobin mevcut sabit yön ve sabit manyetik indüksiyon yoğunluğu ile solenoid odası içinde tek tip bir elektromanyetik alan oluşturur. Çelik fiberler taze harç hizalayın ve ASFRC numuneler hazırlamak için manyetik alan kullanır. Bu çalışmada, bobini 250 × 250 × 750 mm ile bir oda boyutu kullanarak 150 × 150 × 550 mm prizma örnekleri hazırladık.
<ol><li>Manyetik indüksiyon yoğunluğu solenoid elektrik akımı için aralarındaki ilişkileri belirlemektir.<ol>
<li>Solenoid DC'ye bağlanmak ve 0 ile 10 A 1 A. ölçü ve kayıt manyetik indüksiyon yoğunluğu tesla metre kullanılarak solenoid odasında adım uzunluğu ile geçerli uygulanır.</li>
		<li>Sonraki adımda solenoid gerekli geçerli belirlemek için kullanılan (resim 2), manyetik indüksiyon yoğunluğu akım eğrisi çizmek. Not: Solenoid güç kaynağı ve tüm diğer operasyon yöntemleri elektrik için bağlanırken elektrik güvenliği yordamları dikkatlice takip edin.</li>
	</ol>
</li>
</ol>2. taze harç işlenebilirlik
<ol><li>Üç hazırlamak harç karışımları ile çelik fiber birim kesirler %0,8, % 1,2 ve %2.0, sırasıyla (Tablo 1). Üç karışımları bir su 0.42:1:2 oranını kum çimento ile aynı matris kompozisyon var. Karışım oranı göre 0,5 kg çimento, kum, 1,0 kg ağırlığında ve 0,21 kg su işlenebilirlik için sınar.</li>
	<li>Su için harç mikseri önce ekleyin. Sonra çimento ekleyin. Mix su ve çimento 30 s. Sonra karıştırmak için başka bir 30 s ve bu 30 sırasında s karıştırma, yavaş yavaş karıştırıcı için kum ekleyin. Başka bir 60 için mix s.</li>
	<li>Harç (JGJ/T70-2009)19bina performans test yöntemi için Çin standart takip batan bir derinlik metre kullanılarak karışımı batan derinliği sınayın.</li>
	<li>2.2 ve 2.3, batan Derinlik 50-100 mm aralığı içine düşüyor kadar Süperakışkanlaştırıcı doz ayarlama adımları yineleyin. İstenen işlenebilirlik üretir Süperakışkanlaştırıcı doz kaydetmek ve Tablo 1' deki mix oranı parçası olarak ekleyin. İşlenebilirlik elde sonra da taze harç belirli yoğunluğu sınayın. Yukarıda belirtilen testlerden polycarboxylate Süperakışkanlaştırıcı en iyi duruma getirilmiş doz %0.10 (Çimento için kütle oranı) ve taze harç belirli yoğunluğu 2186 kg/m3.</li>
	<li>Bir koaksiyel dönme harç rheometer (Şekil 3) kullanarak taze harç viskozite sınayın. Rheometer sıcaklığı 20 ° C'de örnek kapsayıcısının koruyabilirsiniz bir su banyosu vardır<ol>
<li>300 mL taze harç önceki 5 dk içinde karışık örnek konteyner içine koymak.</li>
		<li>Viskozite test başlar. Sonda kapsayıcısında taze harç içine yavaş yavaş düşer ve konteyner döndürmek başlar. Taze harç dönen kapsayıcı içinde hareket ederken, sonda üzerinde kesme kuvveti uygular. Süreç içinde rheometer kayıtları kesme stres ve kayma oranı ve kesme hızı yamultmak için stres eğrisi çizer. Eğrinin eğimini harç20,21viskozite var. Bu araştırmada, testlerden taze harç viskozite 0,82 Pas var.</li>
	</ol>
</li>
</ol>3. numune hazırlama
<ol><li>Manyetik alan manyetik indüksiyon yoğunluğunu ve solenoid geçerli belirler.<ol>
<li>Adım 2.5.2, belirlenen çimento harç viskozite kullanarak hesaplama denklemi (1) kullanarak çimento harç çelik lifler hizalamak için gerekli manyetik alan manyetik indüksiyon yoğunluğu:13 <img alt="Equation 1" src="/files/ftp_upload/56307/56307eq1v2.jpg">(1) B manyetik indüksiyon yoğunluğu, nerede η taze harç viskozite lf çelik lif uzunluğudur, m bireysel bir çelik elyaf kütlesinin, Çelik fiberler, μ yarıçapı rf Çelik fiberler geçirgenliği, μ0 ' dır vakum geçirgenliği, Δt olduğu zaman aralığı ise α(t + Δt) Açısal ivme sonraki zaman aralığında. Viskozite ve testlerde kullanılan çelik fiber parametreleri göre gerekli manyetik indüksiyon yoğunluğu 9.83 olduğunu mT.</li>
		<li>Şekil 2 veya Denklem (2) göre yeterli bir manyetik indüksiyon yoğunluğu oluşturmak için gereken solenoid elektrik akımı belirlemek:14 <img alt="Equation 2" src="/files/ftp_upload/56307/56307eq2v2.jpg">(2) Burada gerekli geçerli olduğunu , N bobinli döner sayısıdır ve L solenoid uzunluğudur. Denklem (2) kullanarak, gerekli geçerli Şekil 2 ' den yaklaşık 8.5 A. olmakla 8.3 A, olduğunu</li>
	</ol>
</li>
	<li>ASFRC numune hazırlama<ol>
<li>Taze harç karıştırmak için bir 15 L harç mikseri kullanın. Her toplu işlem için Tablo 1' de listelenen mix oranlara göre harç 7.5 L karıştırın. Tablo 1 ASFRC karışımları burada A Çelik fiberler hizalanır ve Vf çelik fiber birim kesir gösterir gösterir A-Vf, ifade eder. Buna göre SFRC karışımları, karşılaştırma için burada R Çelik fiberler rasgele dağıtıldığını gösterir R-Vf, belirtilir. SFRC karışımları Tablo 1 ' de listelenen değil ama ASFRC olarak aynı boyutlara sahip.</li>
		<li>Hammadde tartmak ve rutin prosedürleri takip çelik elyaf takviyeli çimento harç karışımı.</li>
		<li>Pour net ölçü, 150 × 150 × 550 mm. ile plastik kalıp içine taze harç numuneler derhal işlenebilirlik kaybetmemek için karıştırma sonra döküm. İlgili kişiden, çimento ve su arasında bir ASFRC prizma döküm için yaklaşık 25 dakika sürer.</li>
		<li>Kalıp sıkıştırma bir tablo üzerine taşıyın ve sıkıştırma masaya 30 s. eklemek için kalıp tamamen olduğunu dolu emin olmak için gerektiği gibi daha fazla harç geçin.</li>
		<li>Kalıp solenoid odanın içine koymak.</li>
		<li>Solenoid ve sıkıştırma tablo 50 için geçiş s. Not: sıradan beton için makul sıkıştırma süre civarındadır 60-120 s. Bu denemede, bu Aralık içindeki toplam sıkıştırma zamanı kontrol denemesi yapılır. Artık bu sıkıştırma zaman Çelik fiberler hizalamasını artırabilir; Ancak, sıkıştırma ve (varsa Çelik fiberler ve kaba agrega batan) ayrımı üzerinde sonuç olarak neden olabilir. Daha az sıkıştırma zaman zavallı hizalama dalgalarca beton ve çelik fiber neden olabilir.</li>
		<li>Sıkıştırma masadan geçin.</li>
		<li>Sıkıştırma tablo tamamen durduktan sonra solenoid geçin.</li>
		<li>Yavaşça solenoid kalıptan çıkarmak ve bir mala ile harç üst yüzeyi pürüzsüz. Çelik fiberler üst yüzeye yakın rahatsız edici kaçının.</li>
	</ol>
</li>
	<li>Her karıştırmak için üç elektromanyetik olarak işlenmiş örnekler (aşağıdaki adımları 3.2.2-3.2.9) ve üç elektromanyetik olarak sigara işlenmiş örnekler (aşağıdaki adımları 3.2.2-3.2.4 ve 3.2.9) hazırlayın. Elektromanyetik olarak sigara tedavi numunelerin hazırlanmasında, toplam sıkıştırma kez 80 oldu s — ki elektromanyetik olarak tedavi numunelerin hazırlanmasında aynı.</li>
	<li>Numuneler kapalı ve 24 saat için onların kalıplar bırakıyorum. Daha sonra demold ve mekanik testler için kullanıldıkları kadar örnek bir sis odada tedavi.</li>
</ol>4. üç nokta bükme testi
<ol><li>28 gün sonra numune kür odadan çıkar ve pozisyonlar (A), (B) destekler, orta açıklıklı saptırma (C) ve LVDT puan (D) (Şekil 4) tespit yükleme için işaretlemek.</li>
	<li>Örnek üç nokta bükme testi teçhizat (Şekil 4) MTS test makinesi yerleştirin ve bir LVDT LVDT sahibi her numune (Şekil 4) yan yüzeyine kullanarak orta açıklıklı için düzeltmek.</li>
	<li>LVDT datalog için bağlayın. Sonra kontrol ve test makinesini PC veri toplama sıklığını belirleme.</li>
	<li>Yavaş yavaş örnek böylece yükleme test makinesini hücrenin üst çok kapatmak için alt destekler yükselterek ama değil dokunmadan, numune üst yüzeyi yükseltmek.</li>
	<li>İlk yük, orta açıklıklı saptırma (LVDT) ve deplasman (yük hücresi) değerleri sıfır.</li>
	<li>Sınamayı başlatmak ve 0.2 mm/dak kayıt örnek yükleme ve orta açıklıklı saptırma tam tarihinin hızında bir deplasman kontrolü ile örnek bir üç nokta bükme yük uygulamak.</li>
	<li>Seyretmek belgili tanımlık yük ve deformasyon örnek. Yerinden 30 mm daha büyük olduğunda, en yüksek değerden sonra sınamayı durdurmak. Genellikle, numune çatlamış ve yükü daha az 1.0 kN.</li>
	<li>Tüm örnekleri test etmek için 4.1-4.7 adımları yineleyin.</li>
</ol>5. Çelik Fiber yönelim Analizi
<ol><li>Çelik fiberler çatlak bölümünde saymak.<ol>
<li>İki porsiyon vasıl belgili tanımlık kırık parça içine numuneler ayırın.</li>
		<li>Ölçmek ve çimento harç numune çatlamış kesit üzerinde Çelik fiberler yönünü kaydetmek. Yönlendirmeyi çelik lif ve örnek eksen arasındaki açıdır. Çünkü el ile Çelik fiberler yönelimleri ölçmek zordur ve hatalı ölçümler üretebilir, yönelimleri altı açısı aralıkları biri olarak kategorize edilebilir: 0 - 15 °, 15-30 °, 30-45 °, 45-60 °, 60-75 ° ve 75-90 °. Çelik fiberler her grupta kaydedin ve sonra ortalama lif yönlendirme verimlilik çarpanını Denklem (3) kullanarak örnek hesaplamak: <img alt="Equation 3" src="/files/ftp_upload/56307/56307eq3v2.jpg">(3) nerede ηθ ortalama yönlendirme verimlilik çarpanını çelik lifler, lf , bireysel bir çelik fiber uzunluğu, n kırık bölümünde Çelik fiberler, toplam sayısıdır ise ben θ bir çelik lif ve numune için uygulanan manyetik alanın yönünü arasındaki açı (hesaplamada, açı aralığının orta değeri her gruptaki tüm Çelik fiberler için kabul edilen).</li>
	</ol>
</li>
	<li>X-ışını bilgisayarlı tomografi çözümlemesi gerçekleştirin.<ol>
<li>Bir 75 mm küp her harç örneği kesti.</li>
		<li>X-ışını bir x-ışını bilgisayarlı tomografi sistemi kullanarak küp tarama gerçekleştirin. Bir örnek test platformu üzerinde yerleştirin ve taramaya başlamak. Makine zayıflama dönen her adımda numune neden röntgen kaydeder ve numune 360 ° yavaş yavaş döner. Bilgisayarlı tomografi sistemi bir üç boyutlu dijital küp yapısını oluşturur.</li>
		<li>Çelik fiberler dijital küp yapısı içinde siyah ve beyaz ikili işlem tarafından tanımlayın. Sonra Çelik fiberler dağıtım açıklayan dijital görüntü elde edilir.</li>
		<li>Tüm Çelik fiberler koordinatlarını görüntü analizi tarafından belirler.</li>
		<li>Her çelik fiber koordinatlarına göre yönünü hesaplayabilirsiniz.</li>
		<li>Oryantasyon verimlilik çarpanını liflerinin Denklem (3) kullanarak hesaplar.</li>
	</ol>
</li>
</ol>

<ol><li>Zollo, R. F. <a target="_blank" href="http://www.sciencedirect.com/science/article/pii/S0958946596000467">Fiber-reinforced concrete: an overview after 30 years of development.</a> Cem. Concr. Compos. 19 (2), 107-122 (1997).</li>
<li>Bentur, A., Mindess, S. <a target="_blank" href="http://scholar.google.com/scholar?hl=en&safe=off&q=author%3aBentur%2C+A+%22Fiber+reinforced+cementitious+composites%22">Fiber reinforced cementitious composites</a>. , 2nd Edition, Taylor & Francis. London and New York. (2014).</li>
<li>Deeb, R., Karihaloo, B. L., Kulasegaram, S. <a target="_blank" href="http://www.sciencedirect.com/science/article/pii/S0008884613002111">Reorientation of short steel fibres during the flow of self-compacting concrete mix and determination of the fiber orientation factor.</a> Cem. Concr. Res. 56 (1), 112-120 (2013).</li>
<li>Soroushian, P., Lee, C. D. <a target="_blank" href="https://www.concrete.org/publications/internationalconcreteabstractsportal/m/details/id/1803">Distribution and orientation of fibers in steel fiber reinforced concrete.</a> ACI Mater. J. 87 (5), 433-439 (1990).</li>
<li>Sebaibi, N., Benzerzour, M., Abriak, N. E. <a target="_blank" href="https://www.researchgate.net/publication/262527132_Influence_of_the_distribution_and_orientation_of_fibres_in_a_reinforced_concrete_with_waste_fibres_and_powders">Influence of the distribution and orientation of fibres in a reinforced concrete with waste fibers and powders.</a> Constr. Build. Mater. 65 (1), 254-263 (2014).</li>
<li>Lee, C., Kim, H. <a target="_blank" href="http://www.sciencedirect.com/science/article/pii/S000888460900341X">Orientation factor and number of fibers at failure plane in ring-type steel fiber reinforced concrete.</a> Cem. Concr. Res. 40 (5), 810-819 (2010).</li>
<li>Shen, R. Effect of compaction methods on fibre orientation, flexural strength and toughness of steel fiber reinforced concrete. J. of the Chinese Ceramic Society. 12 (1), 21-31 (1984).</li>
<li>Process for producing a prepreg with aligned short fibres. US patent. , 3,641,828 (1988).</li>
<li>Building material, especially concrete or mortar, contains magnetically or electrically aligned parallel fibers. US patent. , 19,750,746 (1975).</li>
<li>Yamamoto, T., Gasawara, N., Ohashi, T. The construction method and directional dispersion of steel fiber reinforced concrete. Advances in Science and Technology of Water Resource. (4), 188-197 (1983).</li>
<li>Xu, X. A new type of steel fiber reinforced concrete. Architecture Technology. 20 (4), 240-241 (1993).</li>
<li>Rotondo, P. L., Weiner, K. H. <a target="_blank" href="https://www.concrete.org/publications/internationalconcreteabstractsportal/m/details/id/3490">Aligned steel fibers in concrete poles.</a> Con. Int. 8 (12), 22-27 (1986).</li>
<li>Michels, J., Gams, M. <a target="_blank" href="http://hrcak.srce.hr/index.php?show=clanak&id_clanak_jezik=245308">Preliminary study on the influence of fibre orientation in fibre reinforced mortars.</a> Gradevinar. 68 (8), 645-655 (2016).</li>
<li>Mu, R., Li, H., Qing, L., Lin, J., Zhao, Q. <a target="_blank" href="http://www.sciencedirect.com/science/article/pii/S0950061816318414">Aligning steel fibers in cement mortar using electro-magnetic field.</a> Constr. Build. Mater. 131 (1), 309-316 (2017).</li>
<li>Jones, D. S. <a target="_blank" href="http://scholar.google.com/scholar?hl=en&safe=off&q=author%3aJones%2C+DS+%22The+theory+of+electromagnetism%22">The theory of electromagnetism</a>. , Pergamon Press. Oxford-London-New York-Paris. (1964).</li>
<li>Liu, J., Li, C., Liu, J., Cui, G., Yang, Z. <a target="_blank" href="http://www.sciencedirect.com/science/article/pii/S0950061813006661">Study on 3D spatial distribution of steel fibers in fiber reinforced cementitious composites through micro-CT technique.</a> Constr. Build. Mater. 48 (2), 656-661 (2013).</li>
<li>Schnell, J., Schladitz, K., Schuler, F. <a target="_blank" href="http://onlinelibrary.wiley.com/doi/10.1002/best.200900055/abstract">Direction analysis of fibres in concrete on basis of computed tomography.</a> Betonund Stahlbetonbau. 105 (2), 72-77 (2010).</li>
<li>Wuest, J., Denarié, E., Brühwiler, E., Tamarit, L., Kocher, M., Gallucci, E. <a target="_blank" href="http://onlinelibrary.wiley.com/doi/10.1111/j.1747-1567.2008.00420.x/abstract">Tomography analysis of fiber distribution and orientation in ultra high-performance fiber reinforced composites with high fiber dosages.</a> Experimental Techniques. 33 (5), 50-55 (2009).</li>
<li><a target="_blank" href="http://www.chinesestandard.net/default.aspx?PDF-English-ID=JGJ/T%2070-2009">JGJ/T70-2009 Chinese standard for test method of performance on building mortar</a>. , Building Press. Beijing, China. (2009).</li>
<li>Roussel, N. <a target="_blank" href="http://scholar.google.com/scholar?hl=en&safe=off&q=author%3aRoussel%2C+N+%22Understanding+the+Rheology+of+Concrete%22">Understanding the Rheology of Concrete</a>. , Woodhead Publishing Limited. Cambridge. (2012).</li>
<li>Roussel, N. <a target="_blank" href="http://www.sciencedirect.com/science/article/pii/S0008884604003746">Steady and transient flow behaviour of fresh cement pastes.</a> Cem. Concr. Res. 35 (9), 1656-1664 (2005).</li>
</ol>

Yazarlar ifşa gerek yok.

Bu çalışmada geliştirilen elektromanyetik bobinli 250 × 250 × 750 mm ölçme bir odası vardır ve tam boy yapısal öğeleri taşıyamaz. Kur, kavram uygulama odası boyutunu sınırlar ve bu raporda önerilen protokol ASFRC parçalarının üretimi için tam boy Kur daha da geliştirilmesi ilham kaynağı olacak olsa da, özellikle öğeleri Prefabrik konstrüksiyon.
Çelik fiberler hizalamasını taze harç viskoz direnci aşmak gerekir bir manyetik kuvvet tarafından tahrik edilmektedir çünkü uygun bir viskozite taze ha...

Çelik fiberler beton birleşmeyle kırılganlık doğal zayıflık üstesinden gelmek ve gerilme direnci beton1artırmak için etkili bir yoldur. Son yıllarda, çelik fiber takviyeli beton yoğun olarak incelenmiş ve alanında yaygın olarak kullanılan. Çelik fiber takviyeli beton üstün çatlama direnç, çekme dayanımı, kırık tokluk, kırık enerji vb.açısından Beton çelik fiber takviyeli beton, çelik lifler2 rastgele dağınık, böylece aynı şekilde her yöne liflerinin takviye verimlilik malzemeleri. Çünkü onlar çekme dayanımı gerilmeler ilkesi ile uyumlu hale getirilmesi liflerinin takviye verimlilik gerektirir ancak, belirli yükleme koşullar altında Beton Çelik fiberler yalnızca bazılarını yapı elemanlarının performans için katkıda yapısı. Örneğin, çelik fiber takviyeli beton rastgele dağıtılmış Çelik fiberler içeren bir ışın, bazı Çelik fiberler hazırlamak için kullanırken özellikle de asıl gerilmesi, yönünü paralel yapacak büyük katkı takviye verimlilik, süre asıl gerilmesi yönüne dik takviye verimlilik için hiçbir katkı sağlayacaktır. Sonuç olarak, asıl gerilmesi beton yönünü ile Çelik fiberler hizalamak için bir yaklaşım bulma Çelik fiberler en yüksek takviye verimlilik sağlamak gereklidir.
Öngörülen uzunluğu boyunca gerilmesi lifleri, gerçek uzunluğunu için yönünü oranı olarak tanımlanan yönlendirme verimlilik çarpanını genellikle Çelik fiberler3,4 takviye verimlilik belirtmek için kullanılır . Bu tanımına göre 1.0 Yönlendirme verimlilik çarpanını liflerinin gerilmesi yönü ile uyumlu olduğunu; Bu gerilmesi için dik liflerinin 0'dır. Eğimli lifleri 0 ile 1.0 arasında bir yönlendirme verimlilik çarpanını var. Oryantasyon verimlilik çarpanını rastgele dağıtılmış çelik lifler beton 0.4054, ise sıradan çelik fiber takviyeli beton testleri bu 0.167-0.5005,6 aralıkta analitik sonuçları göster . Belli ki, tüm kısa çelik lifler beton hizalanır ve gerilmesi olarak aynı yönlendirme varsa, Çelik fiberler-ecek-si olmak yüksek takviye verimlilik ve numuneler optimum gerilme davranış olacaktır.
1980'lerden beri hizalanmış çelik fiber takviyeli beton hazırlamak için bazı başarılı girişimler yapılmıştır. 1984, Shen7 bir elektromanyetik alan çelik fiber takviyeli cementitious kompozit (SFRC) kirişler alt katmana döküm sırasında uygulanan ve x-ışını algılama analiz Çelik fiberler de uyumlu ortaya koydu. 1995 yılında, Bayer8 ve Arman9 hizalanmış çelik fiber takviyeli beton bir manyetik alanını kullanarak hazırlamak için yaklaşım patentli. Yamamoto vd. 10 esas olarak döküm yaklaşım tarafından etkilenmiş ve taze beton kalıp sürekli bir yönden içine akan tutarak hizalanmış çelik fiber takviyeli beton elde etmek için çalıştı için beton Çelik fiberler yönünü kabul. Xu11 sürekli bir yönden Çelik fiberler püskürtülerek Püskürtme Beton çelik lifler hizalamak için çalıştı. Rotondo ve Wiener12 ile hizalanmış uzun çelik lifler beton Polonyalılar tarafından savurma döküm yapmak istedi. Bu deneysel çalışmalar ortaya hizalanmış çelik fiber takviyeli beton rastgele dağıtılmış çelik fiber takviyeli beton önemli avantajlar vardır.
Son zamanlarda, Michels vd. 13 ve Mu vd. 14 başarılı bir şekilde hizalanmış çelik fiber takviyeli cementitious ve kompozitler (ASFRCs) elektromanyetik alanlar kullanarak bir grup geliştirdik. Bu çalışmalarda çeşitli Solenoid Çelik fiberler harç örnekler farklı boyutlarda hizalamak için Tekdüzen bir manyetik alan sağlamak için yapılmıştır. Solenoid önceden tanımlanmış boyutları örnekleri kalabileceği bir oyuk küboid odası vardır. Solenoid doğrudan akım (DC) bağlandığınızda, tek tip bir manyetik alan solenoid ekseni ile hizalar sabit bir yönelim ile odasında oluşturulur. Elektromanyetik15ilkesine göre manyetik alanlar döndürmek ve taze harç hizalamak için ferromanyetik lifleri sürebilirim. Harç uygun işlenebilirlik taze harç döndürmek Çelik fiberler izin verdiği için önemlidir. Düşük viskozite lifleri ayrımı için neden olabilir iken yüksek viskozite havanda Çelik fiberler hizalamasını zorluk neden olabilir.
Bu kağıt ASFRC numunelerin hazırlanması ayrıntılarını açıklar ve ASFRC ve SFRC bükülme özelliklerini sınar. Bu ASFRC bir daha yüksek bükülme gücü ve tokluk SFRC daha vardır bekleniyor. Bu nedenle, ASFRC potansiyel olarak gerilmesi dayanıklı SFRC avantajları vardır ve eğer dirençli çatlama kullanılan kapak beton, kaldırım, vb
Kırık örnekler kullanarak bükülme testlerden sonra numune Çelik fiberler yönünü çatlamış kesit gözlemci tarafından incelenmiş ve tarama kullanarak x-ışını bilgisayarlı tomografi Analizi16,17 , 18. ASFRCs bükülme güçleri ve tokluk, dahil olmak üzere, mekanik özelliklerini bildirdi ve bu elektromanyetik olarak sigara tedavi SFRCs ile karşılaştırıldığında.

<table><tbody><tr><td>Çimento</td><td>Tangshan Jidong Çimento Co., Ltd.</td><td>P & kez; Ø 42.5</td><td>Orijinal Portland Çimentosu</td></tr><tr><td>Nehir</td><td></td><td>kumu</td><td>İncelik modülü 2.4</td></tr><tr><td>Süperakışkanlaştırıcı</td><td>Subote New Materials Co., Ltd.</td>'dir.<td>PCA-III</td><td>Polikarboksilatlı tip, su azaltma oranı %35</td></tr> <tr><td>Çelik elyaf</td><td>Tianjin Hengfeng Xuxiang New Metal Materials Co., Ltd.</td><td>Yuvarlak düz</td><td>Çap 0,5 mm, uzunluk 25 mm</td></tr></tbody></table>

cementitious kompozit ve bükülme davranışının hazırlık hizalanmış çelik fiber takviyeli

Preparation of Aligned Steel Fiber Reinforced Cementitious Composite and Its Flexural Behavior

Bu çalışmanın amacı, bir pusula iğnesi tutarlı bir yönlendirme Dünya'nın manyetik alanı ile hizalanmış çelik elyaf takviyeli cementitious Kompozit üretimi için eylem altında tutar bu arada ilham bir yaklaşım, sunmaktır. Hizalanmış çelik fiber takviyeli cementitious kompozit (ASFRC) taze harç sayede kısa Çelik fiberler manyetik alan ile uyum içinde döndürmek için tahrik edildi kısa Çelik fiberler içeren tek tip bir elektromanyetik alan uygulayarak hazırlanmıştır. Sertleştirilmiş ASFRC çelik lifler hizalamasını derecesini çatlamış kesit çelik lifler sayma tarafından ve x-ışını bilgisayarlı tomografi Analizi tarafından değerlendirildi. İki yöntem sonuçlarından Çelik fiberler manyetik olarak sigara ve kompozitler tedavi ederken ASFRC lifler son derece uyumlu çelik dağıtıldı rastgele olduğunu göster. Bir daha yüksek fazla takviye verimlilik hizalanmış Çelik fiberler vardı ve kompozitler, bu nedenle, önemli ölçüde geliştirilmiş bükülme gücü ve tokluk sergiledi. ASFRC böylece büyük gerilmesi dayanabilir ve daha etkili bir şekilde çatlama karşı SFRC için üstün olmamasıdır.

ASFRCs ve SFRCs üç sayılık bükme testlerden belirlenen bükülme güçlü Şekil 5' te gösterilmektedir. ASFRCs bükülme gücü tüm lif dozlarda için bu SFRCs daha yüksektir. ASFRCs bükülme gücü % 88, q ve % 57 daha yüksek bu SFRCs daha % 0.8, % 1,2 ve %2.0, fiber birim kesirler sırasıyla idi. Bu sonuçlar hizalanmış çelik fiber cementitious matris rastgele dağıtılmış Çelik fiberler daha etkili bir şekilde pekiştiriyor ima.
<p class="jove_content" fo:keep-together....

Bu protokol Tekdüzen bir elektromanyetik alan uygulama tarafından hizalanmış çelik fiber takviyeli cementitious Kompozit üretimi için bir yaklaşım açıklar. Hizalanmış çelik fiber takviyeli cementitious kompozit sıradan lif takviyeli beton için üstün mekanik özellikler sergiler.

Cementitious kompozit ve bükülme davranışının hazırlık hizalanmış çelik fiber takviyeli

The aim of this work is to present an approach, inspired by the way in which a compass needle maintains a consistent orientation under the action of the ...

Bu yöntem, önceki tekniklerle yapılanlardan daha üstün olan çelik elyaf takviyeli çimentolu bir kompozit üretir. Bu tekniğin ana avantajı, kısa çelik liflerin elektromanyetik alanla hizalanmış taze çimentolu kompozitlere ihtiyaç duymasıdır, bu da numuneleri güçlendirme yeteneğini önemli ölçüde artırır. Birkaç kişi prosedürleri göstermeye yardımcı olacaktır.Doçent Xiaowei Wang, Profesör Jian Zhou, Yüksek Lisans Öğrencisi Luansu Wei ve Doktora Öğrencisi Hui Li: Harcın işlenebilirliğini bilmek, numune hazırlamanın anahtarıdır. Harcı karakterize etmek için bir batma derinliği ölçer hazırlayın. Ek olarak, işlenebilirlik testi için hazır bir koaksiyel rotasyonel harç reometresi bulundurun.Harç karışımı için elemanlar bir harç karıştırıcısının yanında olmalıdır. Her karışıma aynı miktarda su, çimento ve kum girecektir. Test ayrıca bir süper akışkanlaştırıcı kaynağı gerektirir.Harcı yapmak için önce mikser kum tutucusuna kum ekleyin. Ardından miksere su koyun. Sonra çimentoyu ekleyin.Su ve çimentonun 30 saniye karışmasına izin verin. Yavaş, otomatik kum ilavesini başlatın ve 30 saniye daha karıştırmaya devam edin. Durmadan önce 60 saniye daha karıştırın.Bu noktada, batma derinliği ölçeri a

preparation-aligned-steel-fiber-reinforced-cementitious-composite-its

Research

JoVE Journal

Engineering

Mühendislik

Üç boyutlu (3D) mikrostrüktürlü kompozit kirişler 3D gözenekli microfluidic ağlara nanokompozitlerin yönettiği ve lokalize sızma yoluyla imal edilir. Bu imalat yönteminin esnekliği fonksiyonel 3 boyutlu takviyeli nanokompozit makroskopik çeşitli ürünler elde etmek amacıyla, farklı ısı ile sertleşen malzeme ve nanofillers kullanımını sağlar.

Mikroakışkan Sızma yoluyla üç boyutlu mikrostrüktürlü nanokompozitlerin İmalat

Reçine zengin alan ortadan kaldırarak kompozit yüzey üzerinde çıplak lifleri ortaya çıkarmak için bir protokol sunulmuştur. Lifler ve kompozitler, imalat sırasında değil sonrası yüzey işlem tarafından sunulur. Maruz kalan karbon kompozit kalınlığı ile yön ve yüksek mekanik özelliği yüksek elektriksel iletkenlik sergi.

Deneysel yeni bir bileşik imalat yöntemi uygulanması: bileşik yüzeyi yumuşak katman yöntemi tarafından çıplak lifleri ortaya

Bu el yazması Delaminasyon dışarıdan bağlı fiber takviyeli polimerler geciktirmek için tasarlanmış spike bağlantılar için yükleme kalitesini kontrol etmek için bir yöntem sunar. Protokol matkap delik ve ekleme işlemi hazırlanması içerir. Çapa verimliliği üzerinde en etkili parametreleri ele alınmıştır.

Kalite kontrol için Fiber geliştirmek için yükleme yöntemi takviyeli polimer Spike çapa

Bileşik laminat imal etmek vakum çanta iş konsolidasyon baskı uygulamak için yeni bir yöntem açıklanır. Bu iletişim kuralının amacı laminat ıslak iş vakum çanta yöntemi tarafından fabrikasyon kalitesini artırmak için bir basit, uygun maliyetli teknik geliştirmektir.

Mıknatıs kompozit üretim destekli: Vakum çanta/Lay-yukarıya oluşum yüksek konsolidasyon basıncı elde etmek için esnek yeni bir teknik

Çalışmanın amacı, yüksek mukavemetli Aramid veya ultra yüksek-molar-kütle polietilen bazlı esnek tek yönlü kompozit laminat malzemelerin doğru mekanik testleri için tutarlı numuneler hazırlamak için protokoller geliştirmektir ve Bu malzemeler üzerinde yapay yaşlanma gerçekleştirmek için protokoller.

Esnek tek yönlü kompozit laminatlar kesme prosedürleri, çekme testi ve yaşlanma

Tam ölçekli yalıtımlı panel davranışını tahmin etmek için yalıtımlı beton duvar panellerinin tasarımında kullanılmak üzere kesme konektörlerinin mekanik özelliklerini değerlendirmek için yaygın olarak bulunan analitik yöntemlerle birleştirilebilen bir test protokolü öneriyoruz.

Yalıtımlı beton duvar panellerinde kullanılmak üzere esnek konektörlerin mekanik özelliklerinin belirlenmesi

Bu makale, ıslak el yatırma/vakum torbası yöntemi kullanılarak elde edilen elyaf takviyeli polimer matrisli kompozit laminatlar için bir üretim sürecini açıklamaktadır.

Farklı İmalat İşlemleri ile Elde Edilen Cam Elyaf Takviyeli Polimer Kompozit Laminatların Mekanik Özelliklerinin Ölçülmesi

Biz dikey olarak sipariş küçük moleküler organik nanotellerin bir ultra yüksek yoğunluklu dizi imalatı için basit bir yöntem rapor. Bu yöntem ucuz keyfi yüzeylerde yetiştirilebilir karmaşık heterostructured hibrid nanotel geometri, sentezi sağlar. Bu yapılar organik elektronik, optoelektronik, kimyasal algılama, fotovoltaik ve spintronics potansiyel uygulamalar var.

Keyfi Yüzeyler üzerinde Dikey dizilmiş Küçük-moleküler Organik Nanoteller bir ultra yüksek Yoğunluk Dizi

Bu makale, mevcut bir saha prosedürünün laboratuvar ölçeğinde araştırılmasını ve sızdıran kuyu deliklerinin sızdırmazlığına uyarlanmasını rapor etmektedir. Metal borunun mekanik olarak genleşmesinden oluşur, bu da gelişmiş bir metal/çimento bağı, hidrolik yolların nihai sızdırmazlığı ve mikrohalka şeklindeki bir kanalın varlığından kaynaklanan gaz sızıntılarının önlenmesi ile sonuçlanır.

Çatlak kuyularda Çözümüne olarak Çelik Boru Mekanik Genişleme

Polimerlerin ve elyaf takviyeli polimer kompozitlerin hizmetteki dayanıklılığı, tasarımları ve duruma dayalı bakım için kritik bir husustur. Eşzamanlı mekanik ve çevresel yüklerin etkisinin araştırılması için yeni, düşük maliyetli bir laboratuvar test platformu sunuyoruz ve daha verimli ancak daha güvenli kompozit yapıların tasarlanmasına yardımcı olabiliriz.

Polimer Dayanıklılık Çalışmaları ve Eşzamanlı Hygrothermo-mekanik Uyaranlara altında Fiber takviyeli kompozitler Polimer A Test Platformu

Öğrenin, manyetik alanla hizalanmış çelik fiber takviyeli çimento esaslı kompozit üretim yöntemini. Bu teknik, malzeme bilimi ve inşaat mühendisliğinde üstün mekanik özellikler sağlar.

Cementitious kompozit ve bükülme davranışının hazırlık hizalanmış çelik fiber takviyeli

Daha fazla video keşfet