Name: Anyonik Seryum oksit nano tanecikleri tarafından bitki reaktif oksijen türleri içinde Vivo katalitik kayıt atma (Video) | JoVE Journal
Uploaded: 2018-08-26T15:00:00.000+00:00
Duration: 9 min 46 s
Description: Öğrenin seryum oksit nano taneciklerinin bitkilerde reaktif oksijen türlerini katalitik olarak temizleme yöntemini. Arabidopsis thaliana kullanarak oksidatif stres yanıtlarını in vivo görüntüleyin.

ai_agent_IP

ai_agent

maintenance

instantTrialDurationMinutes

isBiopharma

enableNewMyJoveSectionDesign

educationFeatures

seoMetaApi

ai_copilot_institution_blacklist

ai_chat_institution_blacklist

freeAccessWindow

ssoRoleCapture

scheduledMaintenanceBanner

joveLabsFeatures

disable_autoplay_for_bots

extended_trial_duration

5 minutes

Bu eser University of California, Riverside ve USDA Ulusal Enstitüsü Gıda ve tarım, Hatch projeye J.P.G. 1009710 tarafından desteklenmiştir Bu malzeme Grant No 1817363 J.P.G. için altında Ulusal Bilim Vakfı tarafından desteklenen çalışma üzerine kuruludur

1. A. thaliana bitki yetiştirme
<ol><li>5 cm x 5 cm tek kullanımlık tencere standart toprak karışımı ile dolu A. thaliana tohumları ekmek. 32 bu tencere içine su dolu bir plastik tepsi koymak (~ 0.5 cm derinlik) ve bitkiler ile plastik tepsi bir bitki büyüme odasına aktar.<ol>
<li>Büyüme odası ayarlarını aşağıdaki gibi ayarlayın: 200 µmol/ms fotosentetik aktif radyasyon (PAR), 24 ± 1 ° C gün ve 21 ± 1 ° C gece, % 60 nem ve 14/10 h gündüz/gece ışık rejimi, anılan sıraya göre.</li>
	</ol>
</li>
	<li>Sadece bir bitki çimlenmesi bir hafta sonra terk etmek her pot ince. Her pot fidan benzer boyutta tutmaya dikkat edin.</li>
	<li>Tencere Dökme musluk suyu doğrudan plastik tepsi tarafından her iki günde su. Dört hafta boyunca bitkiler büyümek. A. thaliana bitkiler daha fazla kullanıma hazır.</li>
</ol>2. malzemelerin ve PNC
<ol><li>Seryum (III) nitrat 1.08 g tartmak ve moleküler biyoloji sınıf su 50 mL konik tüp içinde 2.5 mL içinde çözülür.</li>
	<li>Poli (Akrilik) asit 4,5 g ağırlığında ve 5 ml 50 mL konik tüp moleküler biyoloji sınıf suda çözülür.</li>
	<li>Bu iki çözüm sayısal vortex Mikser kullanarak 15dk için 2.000 devirde iyice karıştırın.</li>
	<li>15 mL amonyum hidroksit çözeltisi (7.2 M) 50 mL Cam kabı aktarın.</li>
	<li>Süre karıştırma 500 rpm karışımı adım 2.3 dropwise amonyum hidroksit ekleyin ve duman başlıklı 24 hr için oda sıcaklığında 500 rpm'de karıştırın.</li>
	<li>Bir gecede reaksiyonu sırasında çözüm önemli kaybı önlemek için kağıt parçası ile kabı kapağı.</li>
	<li>24 saat sonra elde edilen çözüm 50 mL konik tüp aktarmak ve herhangi bir olası enkaz ve büyük aglomeralar kaldırmak 1 h 3900 x g, santrifüj kapasitesi.</li>
	<li>Bu 22,5 mL süpernatant çözeltisi üç 15 mL 10 kDa filtre aktarmak ve filtre kalan 45 mL toplam bir seyreltme yapmak için moleküler sınıf su ile doldurun.</li>
	<li>Ücretsiz polimerler süpernatant çözümden arındırmak ve diğer ayıraçlar ekleyerek süpernatant 15 mL 10 kDa filtre ve 15 dakika süreyle 3900 x g, santrifüj benchtop santrifüj ile en az altı kez bu adımı yineleyin.</li>
	<li>220-700 nm hiçbir ücretsiz polimerler emin olmak için gelen UV-VIS Spektrofotometre ile eluent absorbans her çevrimde ölçmek ve diğer reaktifler son PNC çözümde mevcuttur.</li>
	<li>Toplanan PNC çözüm 5 mL şırınga almak ve 20 nm gözenek boyutu şırınga filtre karşı filtre. Filtre uygulanmış PNC çözüm 50 mL konik tüp içinde toplamak.</li>
	<li>Plastik bir küvet içinde seyreltilmiş son PNC çözüm almak ve 220-700 nm gelen UV-VIS Spektrofotometre ile onun absorbans ölçün. PNC absorbans tepedir 271 nm.</li>
	<li>Bira-Lambert'ın hukuk kullanarak onun konsantrasyonu hesaplama: A εCL =. A belirli bir örnek için en yüksek değer absorbans, ɛ olduğunu PNC (cm-1 M-1) molar emme katsayısı, L. optik yol uzunluğu (küvet genişliği, bu yöntemde 1 cm), ve C ölçülen nano tanecikleri molar konsantrasyonu olduğunu.</li>
	<li>Hidrodinamik çapı ve zeta potansiyel bir parçacık boyutu ve zeta potansiyel Analyzer'ı (Şekil 1) sentezlenmiş PNC ölçmek.</li>
	<li>Bir buzdolabı (4 ° C) son PNC çözümünde daha fazla kullanılmasını kadar saklayın. Not: Lütfen Wu ve diğerleribakın. 8 daha fazla iletişim kuralı ayrıntılarını PNC karakterizasyonu için.</li>
</ol>3. PNC dıı floresan boya ile etiketleme
<ol><li>5 mm (58 mg/L) PNC 0.4 mL moleküler biyoloji 3.6 mL ile 20 mL Cam şişe suda sınıf mix ve 500 rpm'de heyecan.</li>
	<li>Ekle 24 µL 1, 1'-dioctadecyl-3,3, 3', 3'-tetramethylindocarbocyanine perklorat boya çözüm (dıı, 2.5 mg/mL; DMSO seyreltik) dıı boya çözüm yapmak DMSO (dimetil sülfoksit) 176 µL içine.</li>
	<li>Dıı boya dropwise, ortam sıcaklığında 1 dk 1000 devirde karıştırarak PNC çözüm ekleyin.</li>
	<li>Elde edilen bu karışımı 15 mL 10 kDa filtre aktarmak ve üst tüp toplam seyreltme yapmak için moleküler biyoloji sınıf su ile doldurun 15 mL.</li>
	<li>PNC (dıı-PNC) çözüm DMSO ve herhangi bir olası ücretsiz dıı boya benchtop Santrifüjü tarafından 5 min için 3900 x g de 15 mL 10 kDa filtre etiketlenmiş dıı arındırmak.<ol>
<li>Adım 3.5 en az beş kez tekrarlayın.</li>
	</ol>
</li>
	<li>Son dıı-PNC çözümleri 20 nm gözenek boyutu şırınga filtre ile filtre.</li>
	<li>UV-VIS spectrophotometry tarafından son dıı-PNC absorbans ölçmek ve bira-Lambert'ın Hukuku (Şekil 2) göre onun konsantrasyonu hesaplayın. Adım 2,13 daha fazla ayrıntı için bkz.</li>
	<li>Daha fazla kullanım için 4 ° C'de bir buzdolabında saklayın.</li>
</ol>4. bitki infiltrasyonu ile PNC bırakır
<ol><li>İnfiltrasyon 0.1 mL ekleyin (100 mM TES, 100 mM MgCl2, pH 7.5, HCl tarafından ayarlanmış) 0,5 mM PNC veya dıı-PNC çözüm ve girdap 0.9 mL bu arabellek. 10 mM TES infiltrasyon arabelleği bir çözüm bir negatif kontrol kullanın.</li>
	<li>0.2 mL PNC veya dıı-PNC infiltrasyon çözeltisi bir 1 mL steril needleless şırıngaya aktarın. Herhangi bir olası hava kabarcıkları kaldırmak için dokunun.</li>
	<li>Bitki büyüme odası hemen önce infiltrasyon mümkün stoma bantlı kapama oda ışık koşulları altında önlemek için nano tanecikleri ile al.</li>
	<li>Önce infiltrasyon, A. thaliana yaprakları klorofil içeriği benzer boyutta bir klorofil ölçeri kullanmayı ölçmek. Her yaprak üç çoğaltır ile (en az üç ölçümleri oluşan her çoğaltma) ölçmek14. A. thaliana infiltrasyon deneme için benzer klorofil içeriği bırakır seçin.</li>
	<li>Son zamanlarda hazırlanmış PNC veya dıı-PNC çözüm ile yavaş yavaş yaprakları yaprak lamina (abaxial tarafı) alt karşı needleless şırınga ucu hafifçe basarak sızmak ve dalgıç (Şekil 3A) düşürmek.</li>
	<li>Hafifçe narin görev silecek (Şekil 3C) kullanarak yaprak lamina (Şekil 3B) yüzeyinde kalır fazla çözüm yok etmek ve bitki etiket. Yeni hassas görev mendil yaprakları her grup için kullanın.</li>
	<li>İnfiltre A. thaliana bitkilerin yaprak adaptasyon ve 3 h için PNC veya dıı-PNC kuluçka için tezgah üzerinde tutun. Not: İnfiltre A. thaliana bitkiler sonra daha fazla kullanılmasını (Şekil 3D) için hazırsınız demektir.</li>
</ol>5. Confocal Mikroskopi için yaprak örnekleri hazırlanması
<ol><li>Gözlem bezelye boyutlu miktarı 1 cm RADIUS (Şekil 4A) hakkında jel ve 1 mm ince bir cam slayt (Şekil 4B) kadar o zaman uzat rulo.</li>
	<li>Bir cork matkap kullanmak (çapı 0,3 cm) (Şekil 4C) cam slayt üzerinde gözlem jel merkezi dairesel bir bölüm kesmek için.</li>
	<li>Kesme yaprak dokularında daha derin ve daha iyi confocal görüntüleme çözümü için de tamamen perfluorodecalin (PFD) ile doldurun.</li>
	<li>Bir cork matkap kullanmak (çapı 0.2 cm) yaprak diskler adapte dıı PNC toplamak için A. thaliana bitkiler (Şekil 4D) sızmış.</li>
	<li>İyi doldurdu PFD yaprak disk mount; yaprak infiltre (abaxial) tarafı yukarı dönük.</li>
	<li>Bir kare coverslip yaprak disk üzerine getirin ve yavaşça eşit gözlem jel kuyu ile kapatın ve kapana kısılmış (Şekil 4E) hiçbir hava kabarcıkları kalır emin olmak için slayt coverslip basın.</li>
</ol>6. görüntüleme dıı-PNC yaprak dokularında Confocal mikroskobu tarafından
<ol><li>40 X objektif lens confocal mikroskobu tarama ters bir lazer kullanın.</li>
	<li>2-GKD2O 40 X objektif lens üst kısmında üç damla damla.</li>
	<li>Hazırlanan dıı-PNC sızmış yaprak örnek slayt ters 40 X objektif lens üstüne yerleştirin.<ol>
<li>Coverslip yan ama GKD2O ile doğrudan temas objektif üzerinde slayt cam değil emin olun.</li>
	</ol>
</li>
	<li>Mikroskop altında örnek ilgi bir bölge lazer ışığı ya da parlak alan ile bulmak.</li>
	<li>Belgili tanımlık mikroskop bilgisayar yazılımı başlatmak ve Argon lazer (%20 ayarlamak) açın.</li>
	<li>2 µm ve bir satır ortalama 4 daha az optik bir dilim toplamak için iğne deliği ve sondaj ayarlayın.</li>
	<li>Confocal mikroskop ayarları ile örnek resim: 514 nm lazer uyarma (% 30); Z-yığın bölümü kalınlığı: 2 µm; PMT1: 550-615 nm (için dıı-PNC görüntüleme); PMT2: 700-800 nm (kloroplast görüntüleme için).</li>
	<li>Confocal görüntülerini temsilcisi: yaprak örnekleri farklı bireylerin, en az üç biyolojik çoğaltır al.</li>
</ol>7. PNC vivo içinde ROS atma Confocal mikroskobu tarafından görüntüleme
<ol><li>Hazırlamak 25 µM 2', 7'-dichlorodihydrofluorescein diacetate (H2DCFDA, bir genel ROS gösteren bir boya) ve 10 µM dihydroethidium (DHE, süperoksit anyon gösteren bir boya) TES infiltrasyon arabellek (pH 7.5) 1.5 mL microcentrifuge tüpler, boyalar ayrı ayrı.</li>
	<li>Bir cork matkap kullanmak (çapı 0.2 cm) yaprak toplamak için A. thaliana bitkiler adapte PNC disklerinden sızmış.<ol>
<li>Forseps keskin ucu boya yükleme işlemi hızlandırmak için yaprak diskler üzerinde üç veya dört delik olun</li>
	</ol>
</li>
	<li>Yaprak DCFDA ve DHE diskler ayrı ayrı H2microcentrifuge tüpler için ve karanlık altında 30 dk için kuluçkaya transfer.</li>
	<li>Kuluçka sonra durulama yaprak GKD2ile O üç kez diskler ve cam içine slayt gözlem ile bağlama (bkz. iletişim kuralı Bölüm 5) jel.</li>
	<li>Slayt confocal mikroskobunun koymak ve el ile bir yaprak mesophyll hücreleri bölgesine odaklan. İletişim kuralı Bölüm 6 Ayrıntılar için bkz.</li>
	<li>UV-A yaprak disklere maruz (405 nm) lazer ROS oluşturmak ve zaman serileri ("xyt") yaprak disk başına ROS sinyal şiddeti değişikliği kaydetmek için 3 dakika için.</li>
	<li>Görüntü confocal mikroskop ayarları ile yaprak disk: 40 X su amaç; 496 nm lazer uyarma; PMT1: 500-600 nm (için boya algılama) DHE ve DCFDA; PMT2: 700-800 nm (kloroplast algılama için). Sadece infiltrasyon arabellek çözüm olarak negatif kontrol ile sızmış bir bitki kullanın.</li>
</ol>8. PNC atma H2O2içinde vitro
<ol><li>Önceki yayınları3,8,15 yöntemleri izleyerek sentezlenmiş PNC vitro kedi (katalaz) mimetic etkinliklerini yürütmek
</li>
	<li>45.4 eklemek µL 1 x TES infiltrasyon tampon (10 mM TES, 10 mM MgCl2, pH 7.5, HCl tarafından ayarlanabilir), PNC (60 nM, 3 µL) ve H2O2 (2 µM, 1 µL bir kuyuya (beyaz yuvarlak alt 96 iyi plaka)) ve pipetting tarafından karışımı yavaşça.</li>
	<li>10-asetil-3,7-dihydroxyphenoxazine (çalışma konsantrasyonu 100 µM, 0.5 µL) ve horseradish peroksidaz ekleyin (HRP; çalışma konsantrasyonu 0,2 U/mL, 0.1 µL) kuyuya yavaşça karıştırarak pipetting tarafından ve 30 dk 10-asetil-3,7-dihydroxyphenoxazine için kuluçkaya H2O2 ile reaksiyona girer ve resorufin huzurunda HRP dönüştürülür.<ol>
<li>Plaka ışık kuluçka sırasında önlemek için alüminyum folyo ile sarın.</li>
		<li>Bir negatif kontrol H2O2yerine tepki arabellek veya su kullanarak hazırlayın.</li>
		<li>Hisse senedi çözüm hariç, tüm diğer çözümleri, ortam sıcaklığında hazırlayın.</li>
	</ol>
</li>
	<li>Bir plaka okuyucu ile kuluçka sonra 560 absorbans izlemek nm H2O2düzeyini gösteren için resorufin kullanın. Zaman rejim 0, 2, 5, 10, 20 ve 30 dk ayarlayın.</li>
</ol>

<ol><li>Xu, C., Qu, X. <a target="_blank" href="https://www.nature.com/articles/am201388">Cerium oxide nanoparticle: A remarkably versatile rare earth nanomaterial for biological applications.</a> NPG Asia Materials. 6 (3), 90-116 (2014).</li>
<li>Nelson, B., Johnson, M., Walker, M., Riley, K., Sims, C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Antioxidant+cerium+oxide+nanoparticles+in+biology+and+medicine%5BTitle%5D)+AND+%22Antioxidants%22%5BJournal%5D)">Antioxidant cerium oxide nanoparticles in biology and medicine.</a> Antioxidants. 5 (2), 15(2016).</li>
<li>Gupta, A., Das, S., Neal, C. J., Seal, S. <a target="_blank" href="http://pubs.rsc.org/en/content/articlelanding/2016/tb/c6tb00396f#!divAbstract">Controlling the surface chemistry of cerium oxide nanoparticles for biological applications.</a> Journal of Materials Chemistry B. 4 (19), 3195-3202 (2016).</li>
<li>Walkey, C., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Catalytic+properties+and+biomedical+applications+of+cerium+oxide+nanoparticles%5BTitle%5D)+AND+%22Environ.+Sci.%3A+Nano%22%5BJournal%5D)">Catalytic properties and biomedical applications of cerium oxide nanoparticles.</a> Environ. Sci.: Nano. 2 (1), 33-53 (2015).</li>
<li>Pulido-Reyes, G., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Untangling+the+biological+effects+of+cerium+oxide+nanoparticles%3A+the+role+of+surface+valence+states%5BTitle%5D)+AND+%22Scientific+reports%22%5BJournal%5D)">Untangling the biological effects of cerium oxide nanoparticles: the role of surface valence states.</a> Scientific reports. 5, 15613(2015).</li>
<li>Dutta, P., et al. <a target="_blank" href="https://pubs.acs.org/doi/abs/10.1021/cm061580n">Concentration of Ce3+ and oxygen vacancies in cerium oxide nanoparticles.</a> Chemistry of Materials. 18 (21), 5144-5146 (2006).</li>
<li>Boghossian, A. A., et al. <a target="_blank" href="https://www.researchgate.net/publication/259679554_Application_of_Nanoparticle_Antioxidants_to_Enable_Hyperstable_Chloroplasts_for_Solar_Energy_Harvesting">Application of nanoparticle antioxidants to enable hyperstable chloroplasts for solar energy harvesting.</a> Advanced Energy Materials. 3, 881-893 (2013).</li>
<li>Wu, H., Tito, N., Giraldo, J. P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Anionic+cerium+oxide+nanoparticles+protect+plant+photosynthesis+from+abiotic+stress+by+scavenging+reactive+oxygen+species%5BTitle%5D)+AND+%22ACS+Nano%22%5BJournal%5D)">Anionic cerium oxide nanoparticles protect plant photosynthesis from abiotic stress by scavenging reactive oxygen species.</a> ACS Nano. 11 (11), 11283-11297 (2017).</li>
<li>Giraldo, J. P., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Plant+nanobionics+approach+to+augment+photosynthesis+and+biochemical+sensing%5BTitle%5D)+AND+%22Nature+Materials%22%5BJournal%5D)">Plant nanobionics approach to augment photosynthesis and biochemical sensing.</a> Nature Materials. 13 (4), 400-408 (2014).</li>
<li>Demidchik, V. <a target="_blank" href="https://www.sciencedirect.com/science/article/pii/S0098847214001750">Mechanisms of oxidative stress in plants: From classical chemistry to cell biology.</a> Environmental and Experimental Botany. 109, 212-228 (2015).</li>
<li>Rico, C. M., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Cerium+oxide+nanoparticles+impact+yield+and+modify+nutritional+parameters+in+wheat+%28Triticum+aestivum+L.%29%5BTitle%5D)+AND+%22Journal+of+Agricultural+and+Food+Chemistry%22%5BJournal%5D)">Cerium oxide nanoparticles impact yield and modify nutritional parameters in wheat (Triticum aestivum L.).</a> Journal of Agricultural and Food Chemistry. 62 (40), 9669-9675 (2014).</li>
<li>Rossi, L., Zhang, W., Lombardini, L., Ma, X. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((The+impact+of+cerium+oxide+nanoparticles+on+the+salt+stress+responses+of+Brassica+napus+L%5BTitle%5D)+AND+%22Environmental+Pollution%22%5BJournal%5D)">The impact of cerium oxide nanoparticles on the salt stress responses of Brassica napus L.</a> Environmental Pollution. 219, 28-36 (2016).</li>
<li>Xu, J., Duan, X., Yang, J., Beeching, J. R., Zhang, P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Enhanced+reactive+oxygen+species+scavenging+by+overproduction+of+superoxide+dismutase+and+catalase+delays+postharvest+physiological+deterioration+of+cassava+storage+roots%5BTitle%5D)+AND+%22Plant+Physiology%22%5BJournal%5D)">Enhanced reactive oxygen species scavenging by overproduction of superoxide dismutase and catalase delays postharvest physiological deterioration of cassava storage roots.</a> Plant Physiology. 161 (3), 1517-1528 (2013).</li>
<li>Wu, H., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Developing+and+validating+a+high-throughput+assay+for+salinity+tissue+tolerance+in+wheat+and+barley%5BTitle%5D)+AND+%22Planta%22%5BJournal%5D)">Developing and validating a high-throughput assay for salinity tissue tolerance in wheat and barley.</a> Planta. , (2015).</li>
<li>Pirmohamed, T., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Nanoceria+exhibit+redox+state-dependent+catalase+mimetic+activity%5BTitle%5D)+AND+%22Chemical+communications%22%5BJournal%5D)">Nanoceria exhibit redox state-dependent catalase mimetic activity.</a> Chemical communications. 46 (16), Cambridge, England. 2736-2738 (2010).</li>
<li>Asati, A., Santra, S., Kaittanis, C., Perez, J. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Surface-charge-dependent+cell+localization+and+cytotoxicity+of+cerium+oxide+nanoparticles%5BTitle%5D)+AND+%22ACS+nano%22%5BJournal%5D)">Surface-charge-dependent cell localization and cytotoxicity of cerium oxide nanoparticles.</a> ACS nano. 4, 5321-5331 (2010).</li>
<li>Li, J., Wu, H., Santana, I., Fahlgren, M., Giraldo, J. P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Standoff+optical+glucose+sensing+in+photosynthetic+organisms+by+a+quantum+dot+fluorescent+probe%5BTitle%5D)+AND+%22ACS+Applied+Materials+%26+Interfaces%22%5BJournal%5D)">Standoff optical glucose sensing in photosynthetic organisms by a quantum dot fluorescent probe.</a> ACS Applied Materials & Interfaces. , (2018).</li>
<li>Wu, H., Shabala, L., Shabala, S., Giraldo, J. P. <a target="_blank" href="http://pubs.rsc.org/en/content/articlelanding/2018/en/c8en00323h#!divAbstract">Hydroxyl radical scavenging by cerium oxide nanoparticles improves Arabidopsis salinity tolerance by enhancing leaf mesophyll potassium retention.</a> Environmental Science: Nano. 5 (7), 1567-1583 (2018).</li>
<li>Merad-Boudia, M., Nicole, A., Santiard-Baron, D., Saillé, C., Ceballos-Picot, I. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Mitochondrial+impairment+as+an+early+event+in+the+process+of+apoptosis+induced+by+glutathione+depletion+in+neuronal+cells%3A+Relevance+to+Parkinson%27s+disease%5BTitle%5D)+AND+%22Biochemical+Pharmacology%22%5BJournal%5D)">Mitochondrial impairment as an early event in the process of apoptosis induced by glutathione depletion in neuronal cells: Relevance to Parkinson's disease.</a> Biochemical Pharmacology. 56 (5), 645-655 (1998).</li>
<li>Zhao, H., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Detection+and+characterization+of+the+product+of+hydroethidine+and+intracellular+superoxide+by+HPLC+and+limitations+of+fluorescence%5BTitle%5D)+AND+%22Proceedings+of+the+National+Academy+of+Sciences%22%5BJournal%5D)">Detection and characterization of the product of hydroethidine and intracellular superoxide by HPLC and limitations of fluorescence.</a> Proceedings of the National Academy of Sciences. 102 (16), 5727-5732 (2005).</li>
<li>Sun, C., Li, H., Chen, L. <a target="_blank" href="http://pubs.rsc.org/en/content/articlelanding/2012/ee/c2ee22310d#!divAbstract">Nanostructured ceria-based materials: synthesis, properties, and applications.</a> Energy & Environmental Science. 5 (9), 8475(2012).</li>
<li>Hirano, M., Inagaki, M. <a target="_blank" href="http://pubs.rsc.org/en/content/articlelanding/2000/jm/a907510k/unauth#!divAbstract">Preparation of monodispersed cerium(iv) oxide particles by thermal hydrolysis: influence of the presence of urea and Gd doping on their morphology and growth.</a> Journal of Materials Chemistry. 10 (2), 473-477 (2000).</li>
<li>Xi, D. M., Liu, W. S., Yang, G. D., Wu, C. A., Zheng, C. C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Seed-specific+overexpression+of+antioxidant+genes+in+Arabidopsis+enhances+oxidative+stress+tolerance+during+germination+and+early+seedling+growth%5BTitle%5D)+AND+%22Plant+Biotechnology+Journal%22%5BJournal%5D)">Seed-specific overexpression of antioxidant genes in Arabidopsis enhances oxidative stress tolerance during germination and early seedling growth.</a> Plant Biotechnology Journal. 8 (7), 796-806 (2010).</li>
<li>Wu, H., Santana, I., Dansie, J., Vivo Giraldo, J. P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((In+Vivo+delivery+of+nanoparticles+into+plant+leaves%5BTitle%5D)+AND+%22Current+Protocols+in+Chemical+Biology%22%5BJournal%5D)">In Vivo delivery of nanoparticles into plant leaves.</a> Current Protocols in Chemical Biology. 9 (4), 269-284 (2017).</li>
<li>Fukushima, K., Hasebe, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Adaxial-abaxial+polarity%3A+The+developmental+basis+of+leaf+shape+diversity%5BTitle%5D)+AND+%22Genesis%22%5BJournal%5D)">Adaxial-abaxial polarity: The developmental basis of leaf shape diversity.</a> Genesis. 52 (1), 1-18 (2014).</li>
<li>Monda, K., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Enhanced+stomatal+conductance+by+a+spontaneous+Arabidopsis+tetraploid%2C+Me-o%2C+results+from+increased+stomatal+size+and+greater+stomatal+aperture%5BTitle%5D)+AND+%22Plant+physiology%22%5BJournal%5D)">Enhanced stomatal conductance by a spontaneous Arabidopsis tetraploid, Me-o, results from increased stomatal size and greater stomatal aperture.</a> Plant physiology. 170 (3), 1435-1444 (2016).</li>
<li>Petrov, V., Hille, J., Mueller-Roeber, B., Gechev, T. S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((ROS-mediated+abiotic+stress-induced+programmed+cell+death+in+plants%5BTitle%5D)+AND+%22Frontiers+in+Plant+Science%22%5BJournal%5D)">ROS-mediated abiotic stress-induced programmed cell death in plants.</a> Frontiers in Plant Science. 6, 1-16 (2015).</li>
<li>Chaves, M. M., Flexas, J., Pinheiro, C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Photosynthesis+under+drought+and+salt+stress%3A+regulation+mechanisms+from+whole+plant+to+cell%5BTitle%5D)+AND+%22Annals+of+Botany%22%5BJournal%5D)">Photosynthesis under drought and salt stress: regulation mechanisms from whole plant to cell.</a> Annals of Botany. 103 (4), 551-560 (2009).</li>
</ol>

Yazarlar ifşa gerek yok.

Bu protokol için PNC sentezi, karakterizasyonu, floresan boya etiketleme ve in vivo ROS atma faaliyetlerini sergilemek için bitki mesophyll hücreleri içinde nano tanecikleri confocal görüntüleme açıklar. PNC Seryum nitrat ve PAA çözümde amonyum hidroksit karışımı üzerinden sentezledim. PNC emme spectrophotomery ve bira-Lamberts hukuk kullanarak kararlı konsantrasyon ile karakterizedir. Zeta potansiyel ölçümleri PNC olumsuz şarj edilmiş yüzey teslim kloroplast8artırılması için doğruladı. P...

Seryum oksit nano tanecikleri (nanoceria) canlı organizmalar, biyomühendislik, yetenek1,2,3atma onların ayrı katalitik reaktif oksijen türleri (ROS) nedeniyle için temel araştırma, yaygın olarak kullanılır. Çok sayıda iki oksidasyon Birleşik Devletleri (Ce3 + ve Ce4 +) 4arasında,5,6alternatif yüzey oksijen açık pozisyonlar nedeniyle yeteneklerini atma ROS Nanoceria var. Kafes suşları nano, redoks reaksiyonları7Bisiklete binme aracılığıyla bu kusur sitelerin rejenerasyon teşvik ederken Ce3 + sarkan tahvil ROS etkili bir şekilde at. Nanoceria da son zamanlarda kullanılan eğitim için ve mühendislik bitki işlevi8,9. Bitkiler abiyotik stres altında ROS, yağlar, proteinler ve DNA10oksidatif hasara sebep birikimi deneyimi. A. thaliana bitkilerde nanoceria ROS vivo içinde katalitik atma geliştirilmiş bitki fotosentez yüksek ışık, ısı ve soğutma gerilmeler8altında yol açar. Uygulanan nanoceria da artar ateş biyokütle ve tane verimi buğday (Triticum soğanı)11toprak; nanoceria ile tedavi Kolza (Brassica napus) bitkiler daha yüksek bitki biyokütle tuz stres12altında var.
Nanoceria bioengineers teklif ve biyologlar abiyotik stres yanıt-e doğru anlamak ve bitki abiyotik stres toleransı geliştirmek için Nanoteknoloji tabanlı bir araç bitki. Nanoceria'nin vivo ROS atma yetenekleri bitki türlerinin bağımsızdır ve bitki doku içine facile teslim model organizmalar dışında geniş uygulama etkinleştirmek potansiyeline sahiptir. Genetik olarak tabanlı diğer yöntemlerinden farklı olarak, nanoceria bitki satırlar ile antioksidan enzimler overexpression daha yüksek ROS yetenek13atma için değil gerektirir. Nanoceria bitkilere yaprak lamina infiltrasyonu laboratuar tabanlı araştırma için pratik bir yaklaşımdır.
Bu iletişim kuralı genel amacı 1) sentezi ve karakterizasyonu olumsuz ücret poli (Akrilik) asit nanoceria (PNC), 2) teslim ve PNC yaprak hücreleri boyunca izleme ve 3) izleme PNC etkin ROS atma tarif etmektir Vivo. Bu protokol için olumsuz ücret poli (Akrilik) asit nanoceria (PNC) sentezlenmiş ve onların soğurma spektrumu, hidrodinamik çapı ve zeta potansiyel ile karakterize. PNC bitki yaprak dokuları sunmak için basit yaprak lamina infiltrasyon yöntemi açıklanmaktadır. Vivo içinde görüntüleme için mesophyll hücrelerin içindeki nanopartikül dağılımının, floresan boya (dıı) PNC (dıı-PNC) etiket ve nano tanecikleri confocal floresans mikroskobu ile gözlemlemek için kullanıldı. Son olarak, biz in vivo PNC ROS confocal mikroskobu atma izlemek nasıl açıklar.

<table><tbody><tr><td>Seryum (III) nitrat hekzahidrat</td><td>Sigma-Aldrich</td><td>238538-100G</td><td></td></tr><tr><td>Moleküler Biyoloji Sınıfı Su, Corning</td><td>VWR</td><td>45001-044&nbsp;</td><td></td></tr><tr><td>Falcon 50 mL Konik Santrifüj Tüpleri</td><td>VWR</td><td>14-959-49A</td><td></td></tr><tr><td>Poli (akrilik asit) 1.800 Mw</td><td>Sigma-Aldrich</td><td>323667-100G</td><td></td></tr><tr><td>Fisherbrand Dijital Vorteks Karıştırıcı Fisher</td><td>Scientific</td><td>02-215-370</td><td></td></tr><tr><td>Fisherbrand Dijital Vorteks Karıştırıcı Aksesuarı, Tutucu</td><td>Ekleme Fisher Scientific</td><td>02-215-391</td><td></td></tr><tr><td>Fisherbrand Dijital Vorteks Karıştırıcı Aksesuarları: Köpük Ekleme Seti</td><td>Fisher Scientific</td><td>02-215-395</td><td></td></tr><tr><td>Amonyum hidroksit çözeltisi</td><td>Sigma-Aldrich</td><td>05002-1L</td><td></td></tr><tr><td>PYREX Griffin Beherler, Mezun, Corning</td><td>VWR</td><td>13912-149&nbsp;</td><td></td></tr><tr><td>RCT basic</td><td>IKA</td><td>3810001</td><td></td></tr><tr><td>Eppendorf Mikrosantrifüj 5424</td><td>VWR</td><td>80094-126</td><td></td></tr><tr><td>Amicon Ultra-15 Santrifüj Filtre Üniteleri</td><td>Millipore-Sigma</td><td>UFC901024</td><td></td></tr><tr><td>Allegra X-30 Serisi Masaüstü Santrifüj</td><td>Beckman Coulter</td><td>B06314</td><td></td></tr><tr><td>UV-2600 Sptecrophotometer</td><td>Shimadzu</td><td>UV-2600 120V</td><td></td></tr><tr><td>Whatman Anotop 10 şırınga filtresi</td><td>Sigma-Aldrich</td><td>WHA68091102</td><td></td></tr><tr><td>BD Luer-Lok Uçlu Tek Kullanımlık Şırıngalar</td><td>Fisher Scientific</td><td>14-829-45</td><td></td></tr><tr><td>Zetasizer Nano S</td><td>Malvern Panalytical</td><td>Zen 1600</td><td></td></tr><tr><td>1,1 & prime; -Dioctadesyl-3,3,3 & prime;, 3 & prime; -tetrametilindokarbosiyanin perklorat</td><td>Sigma-Aldrich</td><td>42364-100MG</td><td></td></tr><tr><td>Dimetil Sülfoksit, ACS</td><td>VWR</td><td>BDH1115-1LP</td><td></td></tr><tr><td>Güneş Işığı Karışımı #1 LC1</td><td>Green Island Distributors, Inc</td><td>5212601.CFL080P</td><td></td></tr><tr><td>Adaptis 1000</td><td>Conviron</td><td>A1000</td><td></td></tr><tr><td>TES, %>99 (titrasyon</td><td>Sigma-Aldrich</td><td>T1375-100G</td><td></td></tr><tr><td>Magnezyum klorür</td><td>Sigma-Aldrich</td><td>M8266-1KG</td><td></td></tr><tr><td>Air-Tite Tamamen Plastik Norm-Ject Şırınga</td><td>Fisher Scientific</td><td>14-817-25</td><td></td></tr><tr><td>Kimberly-Clark Professional Kimtech Science Kimwipes Hassas Görev Silecekleri</td><td>Fisher Scientific</td><td>06-666A</td><td></td></tr><tr><td>Carolina Gözlem Jeli Carolina</td><td></td><td>132700</td><td></td></tr><tr><td>Corning mikroskop slaytları, bir tarafı buzlu, bir ucu</td><td>Sigma-Aldrich</td><td>CLS294875X25-72EA</td><td></td></tr><tr><td>Mantar Delici Kulplu Setler</td><td>Fisher Scientific</td><td>S50166A</td><td></td></tr><tr><td>Perflorodekalin</td><td>Sigma-Aldrich</td><td>P9900-25G</td><td></td></tr><tr><td>Mikro Kapaklı Gözlükler, Kare, No. 1</td><td>VWR</td><td>48366-045</td><td></td></tr><tr><td>Leica Lazer Taramalı Konfokal Mikroskop TCS SP5</td><td>Leica Microsystems</td><td>TCS SP5</td><td></td></tr><tr><td>2 & prime ;,7 & prime ;-Diklorofloresan diasetat</td><td>Sigma-Aldrich</td><td>D6883-250MG</td><td></td></tr><tr><td>Dihidroetidyum</td><td>Sigma-Aldrich</td><td>D7008-10MG</td><td></td></tr><tr><td>Fisherbrand Premium Mikrosantrifüj Tüpleri: 1.5 mL</td><td>Fisher Scientific</td><td>05-408-129</td><td></td></tr><tr><td>Eppendorf Uvette küvetleri</td><td>Sigma-Aldrich</td><td>Z605050-80EA</td><td></td></tr><tr><td>Klorofil ölçer ve nbsp;</td><td>Konica Minolta</td><td>SPAD-502</td><td></td></tr></tbody></table>

anyonik seryum oksit nano tanecikleri tarafından bitki reaktif oksijen türleri içinde vivo katalitik kayıt atma

Catalytic Scavenging of Plant Reactive Oxygen Species In Vivo by Anionic Cerium Oxide Nanoparticles

Reaktif oksijen türleri (ROS) birikimi bitki abiyotik stres tepkisi bir özelliğidir. ROS bitkilerde sinyal molekülleri düşük seviyelerde ve yüksek düzeyde moleküller zarar olarak hareket ederek ikili bir rol oynar. ROS birikimi stresli bitki metabolitleri, enzim, lipidler ve bitki büyüme ve verim azalması neden DNA, zarar verebilir. Seryum oksit nano tanecikleri (nanoceria) catalytically ROS vivo içinde çöpçülük yeteneğini anlamak için benzersiz aracı ve genetiğinin bitki abiyotik stres toleransı sağlar. Burada, sentez ve poli (Akrilik) asit kaplı nanoceria (PNC) karakterize, nano tanecikleri ile bitkilerin yaprak lamina sızma yolu ile arayüzü ve kendi dağıtım ve ROS atılmasını vivo içinde confocal kullanarak izlemek için bir iletişim kuralı mevcut mikroskobu. ROS birikimi tesislerinde değiştirmek için geçerli moleküler araç modeli türleri için sınırlıdır ve zahmetli dönüştürme yöntemleri gerektirir. Vivo ROS atma bu protokol vahşi türü bitkiler ile geniş yaprakları ve yaprak yapı Arabidopsis thalianagibi uygulanmak üzere potansiyeline sahiptir.

PNC sentezi ve karakterizasyonu . PNC sentez, saflaştırılmış ve Yöntem iletişim kuralı Bölüm 2'de açıklanan aşağıdaki karakterize. Resim 1 A Seryum nitrat, patır, Seryum nitrat ve PAA ve PNC karışımı çözümleri coloration gösterir. PNC sentezlenir sonra beyaz açık sarı bir renk değişikliği görülür. 10 kDa filtreli arıtma sonra PNC UV-VIS Spektrofotometre ile karakterize. Zirve absorbans PNC için 27...

Burada, malzemelerin ve Seryum oksit nano tanecikleri (nanoceria) (reaktif oksijen türlerine) için için bir protokol atılmasını vivo içindebitki dokularda düşsel confocal mikroskobu ve in vivo tarafından nanoceria mevcut nanoceria ROS tarafından confocal mikroskobu atma izleme.

Anyonik Seryum oksit nano tanecikleri tarafından bitki reaktif oksijen türleri içinde Vivo katalitik kayıt atma

Reactive oxygen species (ROS) accumulation is a hallmark of plant abiotic stress response. ROS play&#160;a dual role in plants by acting as signaling ...

Seryum oksit nanopartiküllerinin reaktif oksijen türlerini in vivo olarak katalitik olarak temizleme yeteneği, bitki sinyalizasyon mekanizmalarını ve strese toleransı anlamak ve tasarlamak için benzersiz bir araç sağlar. Reaktif oksijen türleri, düşük seviyelerde sinyal molekülleri olarak hareket ederek ve yüksek seviyelerde moleküllere zarar vererek bitkilerde kilit bir rol oynar. Bu tekniğin temel avantajı, Arabidopsis thaliana gibi geniş yapraklı ve yaprak yapısına sahip çeşitli yabani tip bitki türlerine uygulanabilme potansiyelidir.Arabidopsis thaliana bitkilerini büyüttükten sonra, 1.08 gram Seryum nitratı tartın ve 50 mililitrelik konik bir tüpte 2.5 mililitre biyoloji sınıfı suda çözün. 4.5 gram Poli asidi tartın ve 50 mililitrelik farklı bir konik tüpte beş mililitre biyoloji sınıfı suda çözün. Bu iki çözeltiyi birleştirin ve ardından 15 dakika boyunca 2.000 rpm'de iyice karıştırmak için dijital bir vorteks karıştırıcı kullanın.Bir davlumbazda, 15 mililitre 7.2 molar amonyum hidroksit çözeltisini 50 mililitrelik bir cam behere aktarın. 500 rpm'de ve oda sıcaklığında karıştırmaya başlayın. Seryum nitrat ve Poli asit karışımını damla damla ekleyin.Çözeltinin önemli ölçüde kaybolmasını önlemek için kabı bir parça kağıtla örtün ve 24 saat boyunca karıştırmasına izin verin. Bundan sonra, elde edilen çözeltiyi 50 mililitrelik konik bir tüpe aktarın. Herhangi bir kalıntı veya büyük topakları temizlemek için bir saat boyunca 3.900 kez g'de santrifüjleyin.Ardından, süpernatanı üç adet 50 mililitre, 10 kilodalton filtreye aktarın. Her filtrenin geri kalanını moleküler dereceli suyla doldurun, bu da toplam 45 mililitre seyreltme ile sonuçlanır. 15 dakika boyunca 3.900 kez g'de santrifüjleyin.Bu işlemi en az altı kez tekrarlayın. Bir UV-vis spektrofotometresi kullanarak, nihai PNC çözeltisinde serbest polimer veya diğer reaktiflerin bulunmadığından emin olmak için her bir eluentin absorbansını 220 nanometre ila 700 nanometre arasında ölçün. Toplanan PNC çözeltisini almak için beş mililitrelik bir şırınga kullanın.Daha sonra, çözeltiyi 20 nanometre gözenek büyüklüğünde bir şırınga filtresine karşı süzün ve filtrelenmiş çözeltiyi 50 mililitrelik konik bir tüpte toplayın. Seyreltilmiş bir nihai PNC çözeltisini plastik bir küvete aktarın ve absorbansını 220 nanometreden 700 nanometreye kadar ölçün. Bir partikül boyutlandırıcı kullanarak, sentezlenen PNC'nin hidrodinamik çapını ölçün, ardından nihai PNC çözeltisini kullanıma hazır olana kadar dört santigrat derecede bir buzdolabında saklayın.PNC'yi DiI floresan boya ile etiketledikten sonra, 0.9 milimolar PNC çözeltisi veya DiI-PNC çözeltisi içeren 0.5 mililitre bir çözeltiyi bir tüpe aktarın. 0.1 mililitre sızma tamponu ekleyin ve girdap ile karıştırın. Negatif kontrol olarak 10 milimolar bir TES sızma tamponu hazırlayın.Daha sonra, 0.2 mililitre numune ve tampon karışımını bir mililitrelik steril iğnesiz şırıngaya aktarın. Olası hava kabarcıklarını gidermek için dokunun. Sızmadan hemen önce, bitkiyi büyüme odasından alın.Bir klorofil ölçer kullanarak, A.thaliana yapraklarındaki klorofil içeriğini ölçün. Her yaprağı metin protokolünde belirtildiği gibi üç kopya ile ölçün. Benzer klorofil içeriğine sahip yaprakları seçin.İğnesiz şırınganın ucunu yaprak laminasının altına hafifçe bastırın ve yapraklara sızmak için pistona bastırın. Hassas bir görev sileceği kullanarak, yaprak laminasının yüzeyinde kalan fazla solüsyonu nazikçe silin ve ardından bitkiyi etiketleyin. Sızan bitkileri üç saat kuluçkaya yatırmak için bankta tutun.İlk olarak, bezelye büyüklüğünde bir gözlem jelini bir cam slayt üzerine yerleştirin, jeli yuvarlayın ve yaklaşık iki santimetre çapında ve bir milimetre kalınlığında olana kadar yayın. 0,3 santimetre çapında bir mantar delici kullanarak, bir kuyu oluşturmak için jelin ortasında dairesel bir bölüm kesin. Kuyuyu tamamen PFD ile doldurun, bu da daha derin ve daha iyi bir konfokal görüntüleme çözünürlüğü sağlayacaktır.Ardından, daha önce sızmış A.thaliana bitkilerinden yaprak disklerini toplamak için 0,2 santimetre çapında bir mantar kurdu kullanın. Her bir yaprak diskini, sızan tarafı yukarı bakacak şekilde PFD dolu bir kuyuya monte edin. Bundan sonra, yaprak diskin üzerine kare bir kapak fişi yerleştirin.Gözlem jeli kuyusu ile kapatmak için kapak kızağına hafifçe ve eşit şekilde bastırın ve hava kabarcıklarının sıkışmadığından emin olun. Başlamak için, ayrı 1.5 mililitrelik mikrosantrifüj tüplerinde TES infiltrasyon tamponunda 25 mikromolar H2DCFDA boya ve 10 mikromolar DHE boyası hazırlayın. 0,2 santimetre çapında bir mantar delici kullanarak, uyarlanmış PNC ile sızmış A.thaliana bitkilerinden yaprak diskleri toplayın.Boya yükleme işlemini hızlandırmak için her yaprak diskte üç ila dört delik açmak için forsepsin keskin ucunu kullanın. Ardından, her boya tüpüne eşit miktarda yaprak disk yükleyin. 30 dakika karanlıkta kuluçkaya yatırın.Bundan sonra, yaprak diskleri üç kez çift damıtılmış suyla durulayın. Her bir kanadı daha önce açıklandığı gibi bir cam slayta monte etmek için gözlem jeli kullanın. Slaytı konfokal bir mikroskoba yükleyin ve metin protokolünde belirtildiği gibi yaprak mezofil hücrelerinin bir bölgesine manuel olarak odaklanın, ardından ROS oluşturmak için yaprak disklerini üç dakika boyunca 405 nanometrede bir UVA lazere maruz bırakın.ROS sinyal yoğunluğu değişimini yaprak disk başına zaman serisinde kaydedin. 40X su objektifi ve burada gösterilen konfokal mikroskop ayarlarını kullanarak yaprak diski görüntüleyin. Negatif kontrol olarak sadece sızma tampon çözeltisi ile sızmış bir bitki kullanın.Saflaştırmadan sonra, sentezlenen PNC, bir UV-vis spektrofotometresi kullanılarak karakterize edilir ve 271 nanometrede bir absorbans zirvesine sahip olduğu görülür. Saflaştırma işlemi, nihai eluentin ölçülmesiyle doğrulanır. PNC numuneleri daha sonra nanopartiküllerin in vivo dağılımını belirlemek için bir floresan DiI boyası ile etiketlenir.DiI etiketli PNC için üç tepe noktası gözlenirken, nihai eluentin ölçümü, reaksiyona girmemiş kimyasalların saflaştırma sırasında yıkandığını doğrular. DiI-PNC'nin yaprak mezofil hücrelerindeki dağılımı konfokal görüntüleme ile belirlenir. Kontrol numunelerinde herhangi bir DiI boya sinyali tespit edilmezken, DiI-PNC'nin sızan yapraklarda kloroplastlarla birlikte lokalize olduğu gözlenmiştir.PNC tarafından sağlanan in vivo ROS süpürme, DHE ve DCF boyalarındaki floresan yoğunluğu değişikliklerinin ölçülmesiyle yaprak diskinde izlenir. Üç dakikalık UV stresinden sonra, PNC ile sızan yapraklar, nanopartikül içermeyen tampon kontrolüne kıyasla her iki boya türü için önemli ölçüde daha az yoğunluk gösterir. Bir CAT mimetik aktivite testi, PNC içeren karışımdaki resorufin seviyesinde bir azalma olduğunu ortaya koymaktadır.Bu seviye, hidrojen peroksit seviyesinin bir göstergesidir, bu nedenle de azalmaktadır ve sentezlenen PNC'nin CAT mimetik aktivitesini doğrular. Nanoceria'yı sentezlemek için kullanılan bu protokol, kontrollü boyut, yük ve ROS süpürme yeteneklerine sahip seryum oksit nanopartikülleri üreten basit, aşamalı bir prosedürdür. İn vivo ROS manipülasyonu için bitki genetik modifikasyon yöntemleri şu anda bitki modeli türleriyle sınırlıdır.Buna karşılık, nanoceria ROS süpürme, hem laboratuvarda hem de tarlada çeşitli yabani tip bitki türlerine uygulanma potansiyeline sahiptir.

catalytic-scavenging-plant-reactive-oxygen-species-vivo-anionic

Research

JoVE Journal

Bioengineering

Biyomühendislik

Elektron paramanyetik rezonans (EPR) spektroskopisi demir (II)-N-metil-D-glukamin ditiokarbamat, Fe (MGD) kullanılarak, insan nötrofil gelen sığır aort endotelyal hücreler ve süperoksit anyon radikal nitrik oksit tespit etmek için...

Nitrik Oksit ve hücreler arası Elektron Paramanyetik Rezonans Spektroskopisi ile süperoksit Radikal Anyon tespiti Spin Tuzakları kullanarak

Spin-yakalama ESR spektroskopi, bitki antioksidan likopen, sigara dumanı, gaz-faz, serbest radikallerin temizlenmesi Pycnogenol ve üzüm çekirdeği ekstresi etkisini araştırmak için kullanılmıştır.

Serbest Radikaller Mainstream Sigara Duman algılama ve gaz faz Atma Protokolü

Üretim kanama suyu (PBW), bakır oksit nanopartikülleri (CuO-NP'ler) ile muamele edildi ve kültürlenmiş insan hücrelerinde hücresel toksisite değerlendirildi. Bu protokolün amacı, doğal çevresel numuneyi, CuO-NP işlemine bağlı toksisitedeki değişiklikleri değerlendiren bir hücre kültürü formatına entegre etmekti.

Uranyum dan Bakır Oksit Nanopartiküller tarafından İz Elementlerin çıkarılması<em&gt; In Situ</em&gt; Kurtarma Bleed Su ve Hücre Canlılığı Üzerine Etkisi

CdSe@CdS tohumlanmış çubuk nanopartiküllerin yüzeyinde küçük kristalli iridyum oksit nanopartiküllerinin fotokimyasal oksidatif büyümesi için bir protokol sunulmuştur.

CdSe @ CdS nanorods üzerinde İridyum Oksit Nanopartiküller Fotokimyasal Oksidatif Büyüme

Biz bir non-invaziv vivo içinde aerodinamik ve maliyet-etkin, protokolü Imaging görselleştirmek ve reaktif oksijen türlerine (ROS) bir fare excisional yara modelinde oluşturulan ölçmek için L-012, bir chemiluminescent luminol-analog, kullanan açıklar.

Vivo Reaktif oksijen türleri içinde bir fare görüntüleme modeli yara

Elektron paramagnetic rezonans (EPR) spektroskopisi serbest radikallerin ölçmek için kesin bir yöntemdir. Farklı hücresel kompartmanlarda serbest radikallerin algılanması için seçici spin sonda kullanımı sağlar. Biz tedavi, depolama ve örnekleri EPR ölçümler için aktarma kolaylaştırmak biyolojik örnekler toplamak için pratik ve verimli bir yöntem mevcut.

Elektron Paramagnetic rezonans ortam sıcaklığı ve 77 K biyolojik örneklerde kullanımı

Protocatechuate 3,4-dioxygenase (PCD) enzimatik substrat protokatechuic asit kullanarak sulu bir sistemden serbest diatomik oksijen kaldırabilirsiniz (PCA). Bu protokol, bu oksijen atma enziminin ekspresyonu, saflaştırılması ve aktivite analizini açıklar.

Nükleazsız Oksijen Çöpçü Protocatechuate 3,4-Dioksijenaz İfadesi ve Saflaştırma

Metaliçermeyen fotokatalizör olarak cercosporin kullanan azot içeren heterodöngülerin sentezi için yeni rotalar geliştirilmiştir.

Cercosporin-Photocatalyzed [4+1]- ve [4+2]-Hafif Koşullarda Azoalkenlerin Annülasyonları

Burada, patojenle ilişkili moleküler paternle tetiklenen immün yanıtta pirinç dokularında apoplastik reaktif oksijen türlerinin (ROS) üretiminin gerçek zamanlı tespiti için bir yöntem açıklanmaktadır. Bu yöntem basit, standartlaştırılmış ve kontrollü koşullar altında yüksek oranda tekrarlanabilir sonuçlar üretir.

Kemilüminesans Testi ile Pirinçte İmmün Yanıtta Reaktif Oksijen Türleri Üretiminin Gerçek Zamanlı Tespiti

Bu protokol, yüksek verimli bir tarama yaklaşımı kullanarak bir floresan boya probu olarak dihidroetidyum (DHE) kullanarak hücre içi reaktif oksijen türlerini (ROS) ölçmek için yeni bir yöntemi açıklar. Protokol, üç farklı hepatoselüler karsinom hücre hattında hücre içi reaktif oksijen türlerinin (ROS) kantitatif değerlendirme yöntemlerini açıklar.

Dihidroetidyum (DHE) Floresan Boya Kullanılarak Reaktif Oksijen Türleri (ROS) Üretiminin Yüksek Verimli Tarama Değerlendirmesi

Öğrenin seryum oksit nano taneciklerinin bitkilerde reaktif oksijen türlerini katalitik olarak temizleme yöntemini. Arabidopsis thaliana kullanarak oksidatif stres yanıtlarını in vivo görüntüleyin.

Anyonik Seryum oksit nano tanecikleri tarafından bitki reaktif oksijen türleri içinde Vivo katalitik kayıt atma

Daha fazla video keşfet