Description: Keşfedin, 3D baskılı nanoselüloz hidrojel iskeleler ile kıkırdak rejenerasyonu için doğal dokuları taklit eden mekanik özellikler ve gradyan gözenek yapıları nasıl oluşturulur.

ai_agent_IP

ai_agent

maintenance

instantTrialDurationMinutes

isBiopharma

enableNewMyJoveSectionDesign

educationFeatures

seoMetaApi

ai_copilot_institution_blacklist

ai_chat_institution_blacklist

freeAccessWindow

ssoRoleCapture

scheduledMaintenanceBanner

joveLabsFeatures

disable_autoplay_for_bots

extended_trial_duration

5 minutes

Bu çalışmada mali Knut ve Alice Wallenberg Vakfı (Wallenberg ahşap Bilim Merkezi), İsveçli Araştırma Konseyi, VR (Bioheal, DNR 2016-05709 ve DNR 2017-04254) tarafından desteklenmektedir.

1. kara filmin tarih öncesi hazırlanması
<ol><li>Selüloz nanocrystals süspansiyon hazırlanması Not: Selüloz nanocrystals yalıtım Mathew tarafından bildirilen yordamına uygun olarak yapılır ve ark30.<ol>
<li>Seyreltik 17 wt % askıya ekleyerek 2 wt % selüloz nanocrystals iyice ultra sonication ve kullanımı daha küçük toplu (250-300 mL) etkili karıştırma için 2 L. karışımının toplam hacmi yapmak için su distile.</li>
		<li>Sonified süspansiyon homogenizer üzerinden 10 kat 500-600 bar basınçta geçmek. Bu noktada, 2 wt % selüloz nanocrystals kalın bir şeffaf jel elde edilir.</li>
		<li>11 wt % 24.500 x g 1.5 h. arasında her 30 dk. dışarı Decant su için de centrifugations aracılığıyla nanocrystals jel 2 wt % selüloz konsantre. Not: Deneme burada duraklatılmış.</li>
	</ol>
</li>
	<li>Matris aşamaları hazırlanması<ol>
<li>Sürekli karıştırma altında 60 ° C'de distile su içinde 6 wt % sodyum aljinat (SA) homojen çözüm hazırlamak.</li>
		<li>Homojen çözüm 12 wt % jelatin (jel) sürekli karıştırma altında 60 ° C'de distile su hazırlayın. Not: 20 mL hacmi matris çözümleri için hazırlamak ve buzdolabında saklayın.</li>
	</ol>
</li>
	<li>Crosslinkers hazırlanması<ol>
<li>3 wt % Kalsiyum klorür sürekli karıştırma altında oda sıcaklığında distile su içinde çözüm hazırlamak.</li>
		<li>3 wt % oxazolidin sürekli karıştırma altında oda sıcaklığında distile su içinde çözüm hazırlamak. Not: 50 mL hacmi crosslinking çözümleri için hazırlamak ve oda sıcaklığında saklayın. Satıcı bilgileri Tablo reçetesi bakın. Deneme burada duraklatılmış.</li>
	</ol>
</li>
</ol>2. hidrojel mürekkep hazırlanması
<ol><li>Polistren bir kap içinde hidrojel mürekkep 40 mL 11 wt % CNC, karıştırarak hazırlayın 6 wt % SA ve 12 wt % jel ıslak (wt %) elde etmek için CNC/SA/jel/su bileşimi: 6.87/1.50/1.50/90.12.</li>
	<li>40 ° C ve mix karışıma spatula ile ısı kadar pürüzsüz bir hamur elde edilir.</li>
	<li>Karışımı bir 60 mL şırınga aktarın. Başka bir 60 mL şırınga, mekanik kelepçe yardımıyla içine karışımı bir dizi farklı çaplarda püskürtme uçlarını geçmek. Sorunsuz haddelenmiş filamentler hidrojel mürekkep elde edilen kadar işlemi tekrarlayın. Meme en büyük çapı 800 µm, ardından 600 µm ve 400 µm ile başlayın.</li>
	<li>Şırınga dolu kaldırmak için hidrojel mürekkeple yavaşça santrifüj (4.000 x g) hava tuzağa. Not: Deneme burada duraklatılmış.</li>
</ol>3. ölçü hidrojel rheological özelliklerinin
NTE: rheological özellikleri düzgün bir plaka üzerinde koni geometri kullanarak gerçekleştirmek CP25-2-SN7617, çapı 25 mm, 2 ° nominal açı ve boşluğu yüksekliği 25 ° C'de 0.05 mm
<ol><li>Rheometer, hava kompresörü ve sıcaklık kontrol kutusunu açın. Belgili tanımlık bilgisayar yazılımı başlatmak.</li>
	<li>Rheometer ölçme aracında dağ ve sıfır-boşluğu ayarla.</li>
	<li>Rheometer platformu üzerine hidrojel mürekkep yaklaşık 1 mL A'ya.</li>
	<li>Kesme hızı bir fonksiyonu olarak viskozite ölçmek. Kesme hızı aralığı 0,001 1.000 seçin.</li>
	<li>Ölçüm yapıldıktan sonra rheometer platformu temiz ve Kesici takımlar için ölçme. 1 mL taze hidrojel mürekkep rheometer platformda yine A'ya.</li>
	<li>Ölçüm depolama dönmeler (G′) ve kaybı dönmeler (G″) gibi kesme stres bir frekansta 1 Hz. fonksiyon seçin kesme stres aralığı 10'dan3 ' e 107.</li>
	<li>Testler tamamlandığında, verileri metin dosyasına kopyalayın ve logaritmik ölçekte rheological eğriler çizmek.</li>
</ol>4. dosya hazırlama için 3D baskı
Not: Cura 2.4.0 yazılımı 3D İskele (20 mm3) üç tür gözenekleri olan tasarlamak için kullanılır. 1-üniforma gözenekleri 0.6 mm, 2-üniforma gözenekleri 1.0 mm ve 3-gradient gözenekleri aralığı 0.5-1 mm.
<ol><li>Thingsinverse.com sağlam bir küp Stereolitografi (stl) dosya indirmek ve Cura içinde dosyayı açın.</li>
	<li>Dolu modeli tıklatın ve X/Y/Z için hareket: 0/0/0 mm. tıklayın ölçek, tek tip ölçekleme için onay kutusunun işaretini kaldırın ve boyutları X/Y/Z için ayarla: 20/20/20 mm. tıkırtı Döndür ve küp tarafından XY düzlemi 45 ° döndürün.</li>
	<li>Yan panelinde Nuzul ve malzeme, 0.4 mm seçin ve profil yapıştırın. Discov3ry tam yazıcıyı seçin.</li>
	<li>Yan panel özel Yazdırma ayarlarıöğesini seçin. Kalite bölümünün altında 0.2 mm için tüm alt bölümleri girin. Kabuk bölümü altında 0 mm için tüm alt bölümleri girin. Malzeme bölümünde, 1 mm çap ve % 100 akış, 26 ° C sıcaklık için girin. Hız bölümünde, 30 mm/sn Baskı hızı ve 120 mm/s Hızolarak girin. Destek bölümünün altında uncheck belgili tanımlık kutu için Desteğini etkinleştir. Plaka yapışma inşa bölümünde, etekseçin, 3 mm 150 mm ve Etek mesafe olarak etek/ağzına kadar Minimum uzunluğugirin.</li>
	<li>İskele ile Tekdüzen gözenek boyutu için 0,6 veya 1 mm Dolgu hattı mesafe girin ve Kılavuz dolgu deseniseçin.</li>
	<li>Degrade porozite iskele için birleştirme ve aracı gruplandırma kullanılır. Sağ tıklayın yüklü modeli, Birden fazla modeli2 girin ve Tamam'ıtıklatın. Her model X/Y/Z olarak ölçekleme: 20/20/7 mm. modelleri üst üste yerleştirin. Dolgu hattı uzaklığı 0,3, 0.5 ve 0.7 mm alt, orta ve üst modeli için sırasıyla girin. Her üç model (Ctrl + A) seçin, sağ tıklatın ve Grup modelleri' ı tıklatın.</li>
	<li>Modelleri emin Digital (SD) kart kaydedin. Cura otomatik olarak yazıcı tarafından okunan gcode olarak dosyayı kaydedin.</li>
</ol>5. 3D gözenekli iskele yazdırma
<ol><li>Transferi tüp başlığı yuvasına takın ve 400 µm meme takın. Yapı plaka ve meme arasında doğru mesafe almak için yapı plaka seviye.</li>
	<li>Centrifuged şırınga Kartuşun yük ve transferi tüp diğer tarafına bağlayın.</li>
	<li>SD oyun kağıdı yazıcının yerleştirin, hızlı temizlemek ve meme bükün başlayıncaya kadar hidrojel mürekkep tasfiye başlangıç. Homojen bir akış almak 2-3 dakika için tasfiye devam edin.</li>
	<li>--Dan SD oyun kağıdı, düzgün ve degrade porozite iskele için kaydedilmiş dosyaları seçin ve yazdırmaya başla. Ekstrüzyon oranına dikkat. Gerekirse, hız ve akış hızı uygun şekilde ayarlayın. Daha küçük gözenek boyutu için daha hızlı hızı düşük akış hızı (50 mm/s ve % 70) ile birlikte kullanın. Not: 3D yazdırılan iskele dokunmayın.</li>
</ol>6. 3D polietilenin iskele baskılı
<ol><li>Yavaşça 3D baskı tamamlandıktan sonra o tamamen ıslak hale gelene kadar iskele için 3 wt % CaCl2 damla ekleyin. İçin 5 dakika bekleyin.</li>
	<li>Çok dikkatli bir şekilde iskele transfer yazıcıdan 3 wt % CaCl2ile dolu bir 50 mL kapsayıcı. Gece bırakın.</li>
	<li>Distile su ile iyice yıkayın ve İskele 3 wt % oxazolidin ile dolu bir 50 mL kabına aktarın. Gece bırakın.</li>
	<li>İyice yıkayın ve 3D yazdırılan iskele distile su içinde saklayın.</li>
</ol>7. sıkıştırma testi
Not: Su 37 ° C'de 100 N yük hücresi ile sıkıştırma testleri gerçekleştirmek
<ol><li>2 lt su ile dalgıç sıkıştırma taban plakası ile donatılmış kapsayıcıyı doldurmak ve 37 ° c ulaşmak için Isıtma sistemi başlatmak</li>
	<li>Bluehill evrensel yazılım başlatmak ve test yönteminin ayarlayın. Dikdörtgen numune geometri ve her örnek test etmeden önce boyutları girmek için seçeneğini seçin.  Gerilme oranı % 80 basınç zorlanma ile birlikte 90 N kuvvet olarak 2 mm/dak ve sonuç olarak ayarlayın.</li>
	<li>Ölçüm bölümünde, kuvvet, yer değiştirme, basınç stres ve basınç zorlanma seçin. Gelecekteki komplo için metin dosyaları olarak veri verme seçeneğini seçin.</li>
	<li>Sıfır uzantısı noktası plaka üsse olabildiğince yakın olarak crosshead plaka düşürmek için koşu denetimleri kullanarak ayarlayın.</li>
	<li>Ölçmek ve boyutları örneklerin test edilmesi için not edin.</li>
	<li>Su sıcaklığı 37 ° C'ye ulaştığında, örnek temel tabağa yerleştirin.  Örnek örnek dokunmaya başlaması crosshead plaka taşıyarak güvenli.</li>
	<li>Böylece örnek arası pilakalar onları dalmış su banyosu, yukarı çıkar su.</li>
	<li>Örnek adı ve boyutları girin. Test başlatın.</li>
	<li>Test tamamlandıktan sonra ilk su banyosu aşağı taşı ve crosshead plaka yükseltmek.</li>
	<li>Her iki tabakları temizlemek ve yeni bir örnek yük örnek ve onun parçaları kaldırın.</li>
	<li>Tüm örnekleri test sonra ham veri verin. Basınç stres vs basınç zorlanma eğriler çizmek ve basınç teğet modülü 1-%5 ve % 25-30 zorlanma değerlerinde belirlemek. Not: degrade küp daha büyük delikler Kırtasiye taban plakası yüz şekilde yerleştirin. İlk iskele kulpları arasında güvenli ve sonra Başlat/Durdur ölçüm.</li>
</ol>

<ol><li>Moon, R. J., Martini, A., Nairn, J., Simonsen, J., Youngblood, J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Cellulose+nanomaterials+review%3A+structure%2C+properties+and+nanocomposites%5BTitle%5D)+AND+%22Chemical+Society+Reviews%22%5BJournal%5D)">Cellulose nanomaterials review: structure, properties and nanocomposites.</a> Chemical Society Reviews. 40 (7), 3941-3994 (2011).</li>
<li>Dufresne, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Nanocellulose%3A+a+new+ageless+bionanomaterial%5BTitle%5D)+AND+%22Materials+Today%22%5BJournal%5D)">Nanocellulose: a new ageless bionanomaterial.</a> Materials Today. 16 (6), 220-227 (2013).</li>
<li>Chinga-Carrasco, G. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Potential+and+limitations+of+nanocelluloses+as+components+in+biocomposite+inks+for+three-dimensional+bioprinting+and+for+biomedical+devices%5BTitle%5D)+AND+%22Biomacromolecules%22%5BJournal%5D)">Potential and limitations of nanocelluloses as components in biocomposite inks for three-dimensional bioprinting and for biomedical devices.</a> Biomacromolecules. 19 (3), 701-711 (2018).</li>
<li>Naseri, N., Poirier, J., Girandon, L., Fröhlich, M., Oksman, K., Mathew, A. P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((3-Dimensional+porous+nanocomposite+scaffolds+based+on+cellulose+nanofibers+for+cartilage+tissue+engineering%3A+tailoring+of+porosity+and+mechanical+performance%5BTitle%5D)+AND+%22Royal+Society+of+Chemistry+Advances%22%5BJournal%5D)">3-Dimensional porous nanocomposite scaffolds based on cellulose nanofibers for cartilage tissue engineering: tailoring of porosity and mechanical performance.</a> Royal Society of Chemistry Advances. 6 (8), 5999-6007 (2016).</li>
<li>Naseri, N., Deepa, B., Mathew, A. P., Oksman, K., Girandon, L. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Nanocellulose-Based+Interpenetrating+Polymer+Network+%28IPN%29+Hydrogels+for+Cartilage+Applications%5BTitle%5D)+AND+%22Biomacromolecules%22%5BJournal%5D)">Nanocellulose-Based Interpenetrating Polymer Network (IPN) Hydrogels for Cartilage Applications.</a> Biomacromolecules. 17 (11), 3714-3723 (2016).</li>
<li>Naseri, N., Mathew, A. P., Girandon, L., Fröhlich, M., Oksman, K. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Porous+electrospun+nanocomposite+mats+based+on+chitosan-cellulose+nanocrystals+for+wound+dressing%3A+effect+of+surface+characteristics+of+nanocrystals%5BTitle%5D)+AND+%22Cellulose%22%5BJournal%5D)">Porous electrospun nanocomposite mats based on chitosan-cellulose nanocrystals for wound dressing: effect of surface characteristics of nanocrystals.</a> Cellulose. 22 (1), 521-534 (2015).</li>
<li>Xing, Q., Zhao, F., Chen, S., McNamara, J., DeCoster, M. A., Lvov, Y. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Porous+biocompatible+three-dimensional+scaffolds+of+cellulose+microfiber%2Fgelatin+composites+for+cell+culture%5BTitle%5D)+AND+%22Acta+Biomaterialia%22%5BJournal%5D)">Porous biocompatible three-dimensional scaffolds of cellulose microfiber/gelatin composites for cell culture.</a> Acta Biomaterialia. 6 (6), 2132-2139 (2010).</li>
<li>Nandgaonkar, A., Krause, W., Lucia, L. Fabrication of cellulosic composite scaffolds for cartilage tissue engineering. <a target="_blank" href="http://scholar.google.com/scholar?hl=en&safe=off&q=author%3aNandgaonkar%2C+A+%22Nanocomposites+for+musculoskeletal+tissue+regeneration%22">Nanocomposites for musculoskeletal tissue regeneration</a>. , Elsevier. 187-212 (2016).</li>
<li>Gross, B. C., Erkal, J. L., Lockwood, S. Y., Chen, C., Spence, D. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Evaluation+of+3D+printing+and+its+potential+impact+on+biotechnology+and+the+chemical+sciences%5BTitle%5D)+AND+%22Analytical+Chemistry%22%5BJournal%5D)">Evaluation of 3D printing and its potential impact on biotechnology and the chemical sciences.</a> Analytical Chemistry. 86 (7), 3240-3253 (2014).</li>
<li>Markstedt, K., Mantas, A., Tournier, I., Martínez Ávila, H., Hägg, D., Gatenholm, P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((3D+bioprinting+human+chondrocytes+with+nanocellulose-alginate+bioink+for+cartilage+tissue+engineering+applications%5BTitle%5D)+AND+%22Biomacromolecules%22%5BJournal%5D)">3D bioprinting human chondrocytes with nanocellulose-alginate bioink for cartilage tissue engineering applications.</a> Biomacromolecules. 16 (5), 1489-1496 (2015).</li>
<li>Sultan, S., Mathew, A. P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((3D+printed+scaffolds+with+gradient+porosity+based+on+a+cellulose+nanocrystal+hydrogel%5BTitle%5D)+AND+%22Nanoscale%22%5BJournal%5D)">3D printed scaffolds with gradient porosity based on a cellulose nanocrystal hydrogel.</a> Nanoscale. 10, 4421-4431 (2018).</li>
<li>Sultan, S., Siqueira, G., Zimmermann, T., Mathew, A. P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((3D+printing+of+nano-cellulosic+biomaterials+for+medical+applications%5BTitle%5D)+AND+%22Current+Opinion+in+Biomedical+Engineering%22%5BJournal%5D)">3D printing of nano-cellulosic biomaterials for medical applications.</a> Current Opinion in Biomedical Engineering. 2, 29-34 (2017).</li>
<li>Sultan, S., Abdelhamid, H. N., Zou, X., Mathew, A. P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((CelloMOF%3A+Nanocellulose+Enabled+3D+Printing+of+Metal-Organic+Frameworks%5BTitle%5D)+AND+%22Advanced+Functional+Materials%22%5BJournal%5D)">CelloMOF: Nanocellulose Enabled 3D Printing of Metal-Organic Frameworks.</a> Advanced Functional Materials. , 1805372-1805384 (2018).</li>
<li>Siqueira, G., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Cellulose+Nanocrystal+Inks+for+3D+Printing+of+Textured+Cellular+Architectures%5BTitle%5D)+AND+%22Advanced+Functional+Materials%22%5BJournal%5D)">Cellulose Nanocrystal Inks for 3D Printing of Textured Cellular Architectures.</a> Advanced Functional Materials. 27 (12), 1604619-1604629 (2017).</li>
<li>Wang, J., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((All-in-One+Cellulose+Nanocrystals+for+3D+Printing+of+Nanocomposite+Hydrogels%5BTitle%5D)+AND+%22Angewandte+Chemie+International+Edition%22%5BJournal%5D)">All-in-One Cellulose Nanocrystals for 3D Printing of Nanocomposite Hydrogels.</a> Angewandte Chemie International Edition. 57 (9), 2353-2356 (2018).</li>
<li>Hausmann, M. K., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Dynamics+of+Cellulose+Nanocrystal+Alignment+during+3D+Printing%5BTitle%5D)+AND+%22ACS+Nano%22%5BJournal%5D)">Dynamics of Cellulose Nanocrystal Alignment during 3D Printing.</a> ACS Nano. 12 (7), 6926-6937 (2018).</li>
<li>Liu, Y., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Nanoscale+assembly+of+cellulose+nanocrystals+during+drying+and+redispersion%5BTitle%5D)+AND+%22ACS+Macro+Letters%22%5BJournal%5D)">Nanoscale assembly of cellulose nanocrystals during drying and redispersion.</a> ACS Macro Letters. 7 (2), 172-177 (2018).</li>
<li>Murphy, S. V., Atala, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((3D+bioprinting+of+tissues+and+organs%5BTitle%5D)+AND+%22Nature+Biotechnology%22%5BJournal%5D)">3D bioprinting of tissues and organs.</a> Nature Biotechnology. 32 (8), 773-785 (2014).</li>
<li>Pati, F., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Printing+three-dimensional+tissue+analogues+with+decellularized+extracellular+matrix+bioink%5BTitle%5D)+AND+%22Nature+communications%22%5BJournal%5D)">Printing three-dimensional tissue analogues with decellularized extracellular matrix bioink.</a> Nature communications. 5, 3935(2014).</li>
<li>Xia, Z., Jin, S., Ye, K. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Tissue+and+organ+3D+bioprinting%5BTitle%5D)+AND+%22SLAS+TECHNOLOGY%3A+Translating+Life+Sciences+Innovation%22%5BJournal%5D)">Tissue and organ 3D bioprinting.</a> SLAS TECHNOLOGY: Translating Life Sciences Innovation. 23 (4), 301-314 (2018).</li>
<li>Zhang, Q., Lu, H., Kawazoe, N., Chen, G. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Pore+size+effect+of+collagen+scaffolds+on+cartilage+regeneration%5BTitle%5D)+AND+%22Acta+Biomaterialia%22%5BJournal%5D)">Pore size effect of collagen scaffolds on cartilage regeneration.</a> Acta Biomaterialia. 10 (5), 2005-2013 (2014).</li>
<li>Loh, Q. L., Choong, C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Three-dimensional+scaffolds+for+tissue+engineering+applications%3A+role+of+porosity+and+pore+size%5BTitle%5D)+AND+%22Tissue+Engineering%2C+Part+B%3A+Reviews%22%5BJournal%5D)">Three-dimensional scaffolds for tissue engineering applications: role of porosity and pore size.</a> Tissue Engineering, Part B: Reviews. 19 (6), 485-502 (2013).</li>
<li>Bružauskaitė, I., Bironaitė, D., Bagdonas, E., Bernotienė, E. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Scaffolds+and+cells+for+tissue+regeneration%3A+different+scaffold+pore+sizes-different+cell+effects%5BTitle%5D)+AND+%22Cytotechnology%22%5BJournal%5D)">Scaffolds and cells for tissue regeneration: different scaffold pore sizes-different cell effects.</a> Cytotechnology. 68 (3), 355-369 (2016).</li>
<li>Zhang, L., Hu, J., Athanasiou, K. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((The+role+of+tissue+engineering+in+articular+cartilage+repair+and+regeneration%5BTitle%5D)+AND+%22Critical+Reviews%E2%84%A2+in+Biomedical+Engineering%22%5BJournal%5D)">The role of tissue engineering in articular cartilage repair and regeneration.</a> Critical Reviews™ in Biomedical Engineering. 37 (1-2), (2009).</li>
<li>Athanasiou, K., Rosenwasser, M., Buckwalter, J., Malinin, T., Mow, V. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Interspecies+comparisons+of+in+situ+intrinsic+mechanical+properties+of+distal+femoral+cartilage%5BTitle%5D)+AND+%22Journal+of+Orthopaedic+Research%22%5BJournal%5D)">Interspecies comparisons of in situ intrinsic mechanical properties of distal femoral cartilage.</a> Journal of Orthopaedic Research. 9 (3), 330-340 (1991).</li>
<li>Schinagl, R. M., Gurskis, D., Chen, A. C., Sah, R. L. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Depth-dependent+confined+compression+modulus+of+full-thickness+bovine+articular+cartilage%5BTitle%5D)+AND+%22Journal+of+Orthopaedic+Research%22%5BJournal%5D)">Depth-dependent confined compression modulus of full-thickness bovine articular cartilage.</a> Journal of Orthopaedic Research. 15 (4), 499-506 (1997).</li>
<li>Athanasiou, K., Niederauer, G., Schenck, R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Biomechanical+topography+of+human+ankle+cartilage%5BTitle%5D)+AND+%22Annals+Biomedical+Engineering%22%5BJournal%5D)">Biomechanical topography of human ankle cartilage.</a> Annals Biomedical Engineering. 23 (5), 697-704 (1995).</li>
<li>Athanasiou, K. A., Liu, G. T., Lavery, L. A., Lanctot, D. R., Schenck, R. C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Biomechanical+topography+of+human+articular+cartilage+in+the+first+metatarsophalangeal+joint%5BTitle%5D)+AND+%22Clinical+Orthopaedics+and+Related+Research%22%5BJournal%5D)">Biomechanical topography of human articular cartilage in the first metatarsophalangeal joint.</a> Clinical Orthopaedics and Related Research. 348, 269-281 (1998).</li>
<li>Guilak, F., Jones, W. R., Ting-Beall, H. P., Lee, G. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((The+deformation+behavior+and+mechanical+properties+of+chondrocytes+in+articular+cartilage%5BTitle%5D)+AND+%22Osteoarthritis+and+Cartilage%22%5BJournal%5D)">The deformation behavior and mechanical properties of chondrocytes in articular cartilage.</a> Osteoarthritis and Cartilage. 7 (1), 59-70 (1999).</li>
<li>Mathew, A. P., Oksman, K., Karim, Z., Liu, P., Khan, S. A., Naseri, N. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Process+scale+up+and+characterization+of+wood+cellulose+nanocrystals+hydrolysed+using+bioethanol+pilot+plant%5BTitle%5D)+AND+%22Industrial+Crops+and+Products%22%5BJournal%5D)">Process scale up and characterization of wood cellulose nanocrystals hydrolysed using bioethanol pilot plant.</a> Industrial Crops and Products. 58, 212-219 (2014).</li>
<li>Compton, B. G., Lewis, J. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((3D-printing+of+lightweight+cellular+composites%5BTitle%5D)+AND+%22Advanced+Materials%22%5BJournal%5D)">3D-printing of lightweight cellular composites.</a> Advanced Materials. 26 (34), 5930-5935 (2014).</li>
<li>Sarem, M., Moztarzadeh, F., Mozafari, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((How+can+genipin+assist+gelatin%2Fcarbohydrate+chitosan+scaffolds+to+act+as+replacements+of+load-bearing+soft+tissues%5BTitle%5D)+AND+%22Carbohydrate+Polymers%22%5BJournal%5D)">How can genipin assist gelatin/carbohydrate chitosan scaffolds to act as replacements of load-bearing soft tissues.</a> Carbohydrate Polymers. 93 (2), 635-643 (2013).</li>
<li>Chia, H. N., Hull, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Compressive+moduli+of+the+human+medial+meniscus+in+the+axial+and+radial+directions+at+equilibrium+and+at+a+physiological+strain+rate%5BTitle%5D)+AND+%22Journal+of+orthopaedic+research%22%5BJournal%5D)">Compressive moduli of the human medial meniscus in the axial and radial directions at equilibrium and at a physiological strain rate.</a> Journal of orthopaedic research. 26 (7), 951-956 (2008).</li>
<li>Zhang, K., Fan, Y., Dunne, N., Li, X. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Effect+of+microporosity+on+scaffolds+for+bone+tissue+engineering%5BTitle%5D)+AND+%22Regenerative+biomaterials%22%5BJournal%5D)">Effect of microporosity on scaffolds for bone tissue engineering.</a> Regenerative biomaterials. 5 (2), 115-124 (2018).</li>
<li>Lin, N., Dufresne, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Nanocellulose+in+biomedicine%3A+Current+status+and+future+prospect%5BTitle%5D)+AND+%22European+Polymer+Journal%22%5BJournal%5D)">Nanocellulose in biomedicine: Current status and future prospect.</a> European Polymer Journal. 59, 302-325 (2014).</li>
<li>Domingues, R. M., Gomes, M. E., Reis, R. L. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((The+potential+of+cellulose+nanocrystals+in+tissue+engineering+strategies%5BTitle%5D)+AND+%22Biomacromolecules%22%5BJournal%5D)">The potential of cellulose nanocrystals in tissue engineering strategies.</a> Biomacromolecules. 15 (7), 2327-2346 (2014).</li>
</ol>

Yazarlar ifşa gerek yok.

3D baskı hidrojel mürekkebin uygun rheological özellikleri gerektirir. Düşük viskozite mürekkep şekli ekstrüzyon sonra korumak değil iken yüksek viskozite mürekkep, ekstrüzyon için aşırı basınç gerektirir. Tüm hidrojel mürekkebin viskozite malzemeyi konsantrasyon denetlenebilir. Bizim önceki çalışma11ile karşılaştırıldığında, yazdırılan iskele çözümlemesini geliştirmek için yardımcı olan konsantre hidrojel mürekkeple kaynaklanan 9.9 wt % 5.4 hidrojel mürekkep katı içeriği artar. Uzun esnek CNFs fa...

Selüloz (1-4) bağlantılı D-glikoz birimleri β doğrusal zincirine oluşan bir polisakkarit olan. Bu dünyadaki en bol doğal polimer ve kaynakları, deniz hayvanları (örneğin, tunicates), bitkiler (örneğin, ahşap, pamuk, buğday samanı) ve yosun (örneğin, Valonia), mantar ve hatta amip (protozoa gibi bakteriyel kaynakları da dahil olmak üzere çeşitli elde edilir )1,2. Selüloz nanofibers (CNF) ve selüloz nanocrystals (CNC) Nano üzerinde en az bir boyut mekanik bakımları ve selüloz gelen asit hidroliz yoluyla elde edilir. Onlar sadece selüloz, kimyasal değişiklik, düşük toksisite, Biyouyumluluk, biyolojik olarak parçalanabilen ve yenilenebilir, için potansiyel gibi özelliklere sahip ama aynı zamanda yüksek belirli yüzey alanı gibi Nano özelliklere sahip yüksek mekanik özellikleri , rheological ve optik özellikleri. Bu çekici özellikleri CNFs ve CNCs Biyomedikal uygulamalar için yaptık, esas olarak 3 boyutlu (3D) şeklinde hidrojel3iskele. Bu iskele kontrollü gözenek yapısı ve birbirine bağlı porozite özelleştirilmiş boyutları gerektirir. Bizim grup ve diğer 3D gözenekli selüloz nanokompozitlerin döküm, electrospinning ve4,5,6,7,8dağılması ile hazırlanan rapor. Ancak, gözenek yapısı üzerinde kontrol ve karmaşık geometriyi imalatı bu geleneksel teknikleri sayesinde elde değil.
3D baskı 3D nesneler mürekkep9bilgisayar kontrollü birikimi ile katman katman oluşturulur bir katkı imalat tekniğidir. 3D baskı geleneksel teknikleri üzerinde avantajları içerir tasarım özgürlüğü, kontrollü makro ve mikro boyutları, karmaşık mimarileri, özelleştirme ve tekrarlanabilirlik imalatı.  Buna ek olarak, 3D baskı CNFs ve CNCs Ayrıca kesme kaynaklı hizalamaları, nano tanecikleri, yön, degrade porozite tercih ve 3D bioprinting10,11,12' ye, kolayca genişletilebilir sunar 13 , 14 , 15. son zamanlarda,16,17CNCs hizalama 3D yazdırma sırasında olmuştur dinamikleri bildirdi. Bioprinting alanında gelişmeler var etkinleştirmek 3D yazdırılan doku ve organların seçimi ve konsantrasyon canlı hücreler ve büyüme faktörleri, baskılar ve meme çapları18 baskı taşıyıcı mürekkep bileşimi gibi ilgili meydan rağmen ,19,20.
Porozite ve kıkırdak rejeneratif iskele Basınç Dayanımı, verimlilik ve performans belirleyen önemli özelliklerdir. Gözenek boyutu yapışma, farklılaşma ve besin ve metabolik atık21değişimi gelince de hücrelerin çoğalması için önemli bir rol oynar. Ancak, ideal bir değer olarak kabul edilebilir hiçbir kesin gözenek boyutu, bazı çalışmalar gösterdi daha yüksek bioactivity daha küçük gözenekli iken diğerleri daha iyi kıkırdak yeniden oluşturma büyük gözenekler ile gösterdi. Macropores (< 500 µm) hücre eki ve daha iyi mekanik özellikleri22,23micropores (150-250 µm) kolaylaştırmak iken doku Qafqaz, besin kaynağı ve atık kaldırma kolaylaştırmak. İmplante iskele işleme, zaman yeterli mekanik bütünlük olmalıdır implantasyon ve istenen amacı tamamlanması kadar. Toplam basınç modülü doğal eklem kıkırdak için 0,1-2 aralığında olduğu bildirilmiştir MPa bağlı olarak yaş, cinsiyet ve test edilmiş konum4,24,25,26,27 ,28,29.
Bizim önceki çalışma11' de 3D baskı güçlendirilmiş CNCs sodyum aljinat ve jelatin bir matris içeren bir hidrojel mürekkep gelen polimer ağ (IPN) interpenetrating bir çift çapraz gözenekli bioscaffolds imal etmek kullanıldı. 3D yazdırma yolu nerede nanocrystals tercihen (61-%76 arasında yönlendirme derecesi) yazdırma yönde yönlendirmek düzgün ve degrade gözenek yapıları (80-2.125 µm) ile 3D iskele ulaşmak için optimize edildi. Burada, biz mevcut devamı Bu işe ve hidrojel iskele simüle vücut koşullarında porozite etkisi 3D mekanik özellikleri yazdırılan gösterir. Burada kullanılan CNCs daha önce rapor tarafımızdan cytocompatible ve non-toksik (kuluçka 15 gün sonra teyit edilen30Yani, hücre büyümesi) olmak. Ayrıca, iskele dağılması aynı CNCs sodyum aljinat ve jelatin gösterdi yüksek gözeneklilik, fosfat tampon serum ve cytocompatibility Mezenkimal Kök hücre5doğru yüksek alımını kullanarak yolu ile hazırlanmıştır. Bu eser hidrojel mürekkep işleme, gözenekli iskele, 3D baskı ve sıkıştırma test göstermek için hedeftir. Şemaları işleme rotanın şekil 1' de gösterilir.

<table><tbody><tr><td>60 mL şırınga</td><td>Structur3D Baskı</td><td></td><td></td></tr><tr><td>Aljinik asit sodyum tuzu</td><td>Sigma-Aldrich</td><td>9005-38-3</td><td></td></tr><tr><td>Susuz kalsiyum klorür</td><td>Sigma-Aldrich</td><td>10043-52-4</td><td></td></tr><tr><td>Kelepçeler, üç çatallı, Talon</td><td>VWR</td><td>241-0404</td><td>102 mm, Çift ayar kelepçesi, büyük, kelepçe uzatması 127 mm</td></tr><tr><td>Cura 2.4.0</td><td>Ultimaker</td><td></td><td>Ücretsiz dilimleme yazılımı</td></tr><tr><td>Discov3ry Complete</td><td>Structur3D Baskı</td><td></td><td>Ultimaker 2+ 3D yazıcı, Discov3ry macun ekstruder ile entegre</td></tr><tr><td>Sığır derisinden elde edilen jelatin</td><td>Sigma-Aldrich</td><td>9000-70-8</td><td></td></tr><tr><td>Glutaraldehit çözeltisi ağırlıkça % 50 H2O</td><td>Sigma-Aldrich</td><td>111-30-8</td><td></td></tr><tr><td>homojenizatör</td><td>SPX</td><td>APV-2000</td><td></td></tr><tr><td>Instron 5960 Instron</td><td></td><td></td><td>Instron 5960, Biopuls Banyosu, 100 N yük hücresi, 37 & C,</td></tr> <tr><td>Physica MCR 301 reometre</td><td>Anton Paar</td><td></td><td>CP25-2-SN7617, boşluk yüksekliği 0,05 mm, 25 & C</td></tr><tr><td>Sorvall Lynx 6000 santrifüj</td><td>AB Ninolab</td><td>s/n 41881692</td><td>F12 rotorlu (6x500 ml)</td></tr> <tr><td>paslanmaz çelik nozul</td><td>Structur3D Baskı</td><td></td><td>800, 600 ve 400 &mikro; m</td></tr><tr><td>şeylerters</td><td>MakerBot's</td><td></td><td>&nbsp; stl dosyaları şeklinde 3D yazdırılabilir şeyler paylaşma ve indirme</td></tr><tr><td>ultra</td><td>sonica, LLC</td><td>Q500</td><td></td></tr><tr><td>Kabuksuz talaş</td><td>Norveç ladin (Picea abies)</td><td></td> <td>kuru madde içeriği 50 &ndash; %55</td></tr></tbody></table>

3d gözenekli selüloz nanocomposite hidrojel iskele baskılı

3D Printed Porous Cellulose Nanocomposite Hydrogel Scaffolds

Bu eser gözenekli kübik iskele selüloz nanocomposite hidrojel mürekkep, kontrollü gözenek yapısı ve mekanik özellikleri kullanarak üretmek için üç boyutlu (3D) baskı kullanımı gösterilmiştir. Selüloz nanocrystals (CNCs, 69.62 wt %) matris (sodyum aljinat ve jelatin) tabanlı hidrojel mürekkeple geliştirilmiştir ve İskele düzgün ve degrade gözenek yapısı (110-1100 µm) ile içine 3D yazdırılır. İskele gösterdi sıkıştırma modülü 0,20-0.45 aralığında test zaman MPa (37 ° C'de distile suda) içinde vivo koşulları simüle. Gözenek boyutları ve kıkırdak rejenerasyon uygulamalar için gereken gereksinimleri ile uyumlu 3D iskele sıkıştırma modülü. Bu eser mürekkep tutarlılığını öncüleri konsantrasyon tarafından kontrol edilebilir ve porozite 3D yazdırma işlemi tarafından kontrol edilebilir ve bu faktörlerin her ikisi de karşılığında mekanik tanımlar gösterir 3D özellikleri yazdırılan gözenekli hidrojel iskele. Bu işlem yöntemi bu nedenle hastalar belirli ihtiyaçlarına göre yapısal olarak ve bileşimsel özelleştirilmiş iskele imal için kullanılabilir.

Dayalı CNCs nanocomposite hidrojel mürekkep davranış (Şekil 2bir) inceltme güçlü Newton bükme gösterir. Beş büyüklük 50 s-1 (≈50 s-1 tipik makaslama oranı 3D yazdırma sırasında deneyimli olmak) kesme hızında 22.60 Pa.s değerine göre belirgin viskozite 1,55 × 105 Pa.s düşük kesme hızında (0,001 s-1) damla31 . Hidrojel mürekkep depolama modülü G viskoelastik katı davranış sergileyen ' (4,42 × 107 Pa...

Bu protokol üç kritik adım gelişmekte olan i) doğru kompozisyon ve 3D II) İskele çeşitli yazdırma selüloz hidrojel mürekkep tutarlılığını gözenek yapıları durumu iyi sadakat ve boyutları ve III) gösterimi ile kıkırdak rejenerasyon için benzetimli vücut koşullarda mekanik özellikleri.

3D gözenekli selüloz Nanocomposite hidrojel iskele baskılı

This work demonstrates the use of three-dimensional (3D) printing to produce porous cubic scaffolds using cellulose nanocomposite hydrogel ink, with ...

Bu 3D baskılı nanoselüloz hidrojel iskeleler üzerinde ilk rapor nerede bir degrade gözenek yapısı ve kıkırdak olarak doğal yapıları taklit etmek için mekanik özelliklere sahip. 3D yazdırma tekniklerini kullanmanın iki temel avantajı özelleştirme ve tasarım özgürlüğütür. Bu yeni ve keşfedilmemiş geometrik tasarımlar imal sınırsız bir fırsat açılır.Bu protokol kullanıcı dostudur ve yeni gelenler sonuçları kolayca çoğaltabilirler. Dilimleme yazılımının seçimi ve meme hareketi nihai ürün üzerinde önemli bir etkiye sahiptir. Başlamak için, ağırlık CNC tarafından% 11, ağırlık sodyum aljinat% 6 ve bir kapta ağırlık jelatin% 12 karıştırarak hidrojel mürektürü 40 mililitre hazırlamak.Karışımı 40 dereceye ısıtın ve pürüzsüz bir hamur elde edilene kadar bir spatula ile karıştırın. Karışımı 60 mililitrelik şırıngaya aktarın. Daha sonra, mekanik bir kelepçe yardımıyla, başka bir 60 mililitreşşile farklı çaplarda nozullar bir dizi karışımı geçmek.Hidrojel mürekkirtinin düzgün ekstrüde filamentleri elde edilene kadar işlemi tekrarlayın. Yavaşça sıkışmış hava kaldırmak için 4,000 kez g hidrojel mürektürü ile dolu şırınga santrifüj. SD karttan, tek tip ve degrade gözeneklilik iskeleleri için kaydedilen dosyaları seçin ve yazdırmaya başlayın.Gerekirse, hızı ve akış hızını buna göre ayarlayın. 3D baskı tamamlandıktan sonra iskeleyi çapraz bağlamak için, tamamen ıslanıncaya kadar iskeleye ağırlık kalsiyum klorür çözeltisi ile %3'lük damlalar ekleyin. Beş dakika bekleyin.İskeleyi yazıcı yatağından ağırlık kalsiyum klorür çözeltisi ile %3'lük dolu 50 mililitrelik bir konteynere çok dikkatli bir şekilde aktarın. Bir gecede bırak. Distile su ile iyice yıkayın ve 50 mililitrelik bir konteyner ağırlık glutaraldehit çözeltisi ile% 3 ile dolu iskele aktarın.Bir gecede bırak. Iyice yıkayın ve distile suda 3D baskılı iskele saklayın. Sıkıştırma testi için, iki litre su ile bir dalgıç sıkıştırma taban plakası ile donatılmış konteyner doldurun ve 37 santigrat dereceulaşmak için ısıtma sistemi başlatın.Bluehill Universal Software'i başlangıç ve test yöntemini ayarlayın. Dikdörtgen numune geometrisini seçin ve her numuneyi test etmeden önce boyutlar girme seçeneğini seçin. 90-newton kuvveti ile birlikte% 80 sıkıştırma zorlanma olarak dakikada iki milimetre ve sonuç sonu gerilme oranı ayarlayın.Ölçüm bölümünde Kuvvet, Yer Değiştirme, Sıkıştırma Ve Sıkıştırma Gerinim'i seçin. Verileri gelecekteki çizim için metin dosyaları olarak dışa aktarma seçeneğini seçin. Crosshead plakasını taban plakasına mümkün olduğunca yakın düşürmek için koşu kontrollerini kullanarak sıfır uzatma noktasını ayarlayın.Test edilecek numunelerin boyutlarını ölçün ve kaydedin. Su sıcaklığı 37 dereceye ulaştığında, numuneyi taban plakası üzerine yerleştirin. Çapraz plakayı hareket ettirerek numuneyi sabitle ki numuneye dokunmaya başlayacak.Su banyosunu, aralarında örnek olan tabakların suya daldırılabılabilsin diye yukarı taşıyın. Örnek adı ve boyutları girin ve testi başlatın. Test tamamlandıktan sonra, önce su banyosunu aşağı doğru hareket ettirin ve sonra çapraz başlığı kaldırın.Numuneyi ve parçalarını çıkarın, varsa, her iki plakayı da temizleyin ve yeni bir numune yükleyin. Tüm numuneler test edildikten sonra ham verileri dışa aktarın. Kompresif gerilime karşı kompresif gerilimi ve %5 ila %5 ve %25 ila %30 CNC'lik gerilim değerlerinde sıkıştırıcı teğet modülünü belirleyin, belirgin viskozitenin beş sıra kadir likörü ile Newton dışı kesme inceltme davranışı gösterir.Hidrojel mürekbin viskoelastik katı bir davranış sergiler, çünkü depolama modülü düşük kesme stresindeki kayıp modülünden daha büyük bir büyüklük sırasıdır. %1-5 arasındaki düşük gerinim oranlarında kompresif modül, gözenekli olmayan referans iskeleye kıyasla her türlü gözenekli iskele için benzerdir ve hidrojel mürekkesinin elastik yapısının makrogözeneklerin varlığında bile korunduğunu gösterir. Ancak% 25-30 yüksek gerinim oranları ile en yüksek modül hiçbir gözeneklilik ile referans iskele için elde edilir.Gözenek boyutu artar artar de artar artmaz, yoğunluğun azalması nedeniyle modül azalır, iskelelerin gözenekliliği ile buna karşılık gelen mekanik özellikler arasındaki beklenen ilişkiyi gösterir. Ayrıca, 3D hidrojel iskelelerin kompresif modülü, doğal kıkırdak dokularının viskoelastiyanının sergilenme ve taklit edilebilen sıkıştırma oranı arttıkça artar. 3D baskı sırasında mürekyenin homojen ve sürekli akışı en önemli şeylerdir.Bu yöntem, 3D yazdırılabilir bir platform olarak nanoselüloz hidrojel kullanarak diğer uygulama alanlarına genişletmek için araştırmacılar tarafından kullanılacaktır. Örneğin, aynı prosedürü takiben kontrollü ilaç salınımı için nanoselüloz bazlı melezler geliştirdik.

3d-printed-porous-cellulose-nanocomposite-hydrogel-scaffolds

Research

JoVE Journal

Bioengineering

Biyomühendislik

Bir bioprinter bir kurban kalıp dayalı desenli hidrojeller oluşturmak için kullanıldı. Poloksamer kalıp ikinci bir hidrojel ile dolduruldu ve daha sonra üçüncü bir hidrojel ile doldurulmuş boşluklar bırakarak elüt edilmiştir. Bu yöntem Biyopolimerlerin karmaşık mimarileri oluşturmak için hızlı sağım ve poloksamerin iyi baskı kullanır.

Desenli ve Yaratılış 3D Hücre Kültürü için iki bileşenli Hidrojeller için Thermoresponsive Ters Kalıpları Baskı

Bir Kartezyen biyoyazıcı, hassas, tekrarlanabilir geometrilerde çok malzemeli biriktirmeye izin verirken aynı zamanda çevresel faktörlerin kontrolüne de izin verecek şekilde tasarlanmış ve üretilmiştir. Üç boyutlu biyo-yazıcıyı kullanarak, karmaşık ve uygulanabilir yapılar basılabilir ve kolayca çoğaltılabilir.

Üç Verici Kartezyen Yazıcı Kullanımı Bioprinted Hücresel Yapıların Canlılık

Mikro desenli hidrojel levhaların üretimini, bağımsız bir biçimde monte edilebilen ve manipüle edilebilen basit bir işlem kullanarak açıklıyoruz. Bu modüler hidrojel tabakalar kullanılarak, kontrollü bir hücresel mikro çevre ile basit bir makro ölçekli 3D hücre kültürü sistemi oluşturulabilir.

Micropatterned Makro ölçekli 3D Hücresel Mimarlık Modüler Hidrojel Levhaların İnşaatı

Bu el yazması, ortaya çıkan üç boyutlu bir hepatosit kültür platformunun, ters çevrilmiş kolloidal kristal iskelenin ve hepatosit davranışını değerlendirmek için eşlik eden tekniklerin üretimi için ayrıntılı bir protokol sunmaktadır. Boyut kontrol edilebilir gözenekler, ara bağlantı ve hücre dışı matris proteinlerini poli (etilen glikol) (PEG) iskelesine konjuge etme yeteneği, Huh-7.5 hücre performansını artırır.

Ters Kolloidal Kristal Poli (etilen glikol) İskele imalatı: Karaciğer Doku Mühendisliği için Üç boyutlu Hücre Kültürü Platformu

Burada sunulan bir basit kullanımlı, çekirdek / kabuk, üç boyutlu biyobaskı kurulum içi boş iskeleler, vasküler ve diğer borulu yapıların doku mühendisliği için uygun tek adımlı imalatı için.

Boru yapıları doku mühendisliği için Çekirdek / kabuk Baskı İskeleler

Bu protokol, hücre yüzeyi reseptörlerinin, Kit'in (CD117) ve yüksek benzeşimli IgE reseptörlerinin (FcφRI) hücre canlılığı ve fenotipik ekspresyumu açısından fare kemiğinden türetilmiş mast hücreleri ile kristal nanoselüloz (CNC)/agarose kompozit hidrojel biyomalzeme mürekkebinin biyouyumluluğunu hızla değerlendirmek için bir yöntemi vurgulamaktadır.

Kemik İliği Türevi Mast Hücre Kültürü için Kristal Nanoselüloz Gömülü Agarose Biyomalzeme Mürekkep İmalatı

Tamamlayıcı reaktif gruplara sahip mikrojel çubuklar, sulu çözeltide birbirine bağlanma kabiliyetine sahip mikroakışkanlar yoluyla üretilir. Anizometrik mikrojeller, küresel tabanlı sistemlere kıyasla daha büyük gözeneklere sahip kararlı yapılara sıkışır ve birbirine bağlanır. GRGDS-PC ile modifiye edilmiş mikrojeller, hücre kültürü için kullanılabilecek makrogözenekli 3D yapılar oluşturur.

Mikrojel Çubuklardan Birbirine Bağlı Makrogözenekli 3D İskeleler

Bu makalede, mikroakışkan cihazlar kullanılarak yüksek verimli jelatin metakriloil mikrojel üretimi, mikrojellerin yeniden askıya alınabilir toza (mikro-aerojeller) dönüştürülmesi, granüler hidrojel iskeleleri oluşturmak için mikrojellerin kimyasal montajı ve 3D biyobaskı için korunmuş mikroporoziteye sahip granüler hidrojel biyomürekkeplerinin geliştirilmesi için protokoller açıklanmaktadır.

Jelatin Metakriloil Granül Hidrojel İskeleleri: Yüksek Verimli Mikrojel İmalatı, Liyofilizasyon, Kimyasal Montaj ve 3D Biyobaskı

Bu çalışma, kendi kendini iyileştiren tavlanabilir parçacık-hücre dışı matris kompozitleri içindeki nöral kök hücrelerin serbest biçimli gömülü 3D baskısı için bir protokolü açıklamaktadır. Protokol, birbirine bağlı insan sinir dokusu yapılarının yüksek doğrulukla programlanabilir modellenmesini sağlar.

İnsan Nöral Yapılarının Gömülü 3D Baskısı için Mikrojel-Hücre Dışı Matris Kompozit Desteği

Bu çalışma, dikkate değer geri dönüşümlü sıkışma-sıkışma giderme geçiş özellikleri sergileyen yeni bir κ-İrlanda yosunu alt mikrojel süspansiyon banyosunu tanıtmaktadır. Bu özellikler, gömülü 3D biyobaskıda biyomimetik doku ve organların inşasına katkıda bulunur. Kalp/özofagus benzeri dokuların yüksek çözünürlüklü ve hücre büyümesi ile başarılı bir şekilde basılması, yüksek kaliteli biyobaskı ve doku mühendisliği uygulamalarını göstermektedir.

κ-Carrageenan Sub-Microjel Ortamı Kullanılarak Doku Benzeri Yapıların Gömülü Biyobaskısı

Keşfedin, 3D baskılı nanoselüloz hidrojel iskeleler ile kıkırdak rejenerasyonu için doğal dokuları taklit eden mekanik özellikler ve gradyan gözenek yapıları nasıl oluşturulur.