Name: Su/Hava Arabiriminde Hidrofobik Organik Moleküllerle Doped Hibrid Lipid Membranların Kendi Kendine Montajı (Video) | JoVE Journal
Uploaded: 2020-05-01T14:00:00.000+00:00
Duration: 6 min 28 s
Description: Öğrenin, su/hava arabiriminde kendi kendine montaj yöntemiyle bakır ftalosiyanin katkılı hibrid lipid membranları nasıl üretilir. Bu basit protokol, katı hal cihazları ve sensör uygulamaları için hava stabilitesi sağlar.

ai_agent_IP

ai_agent

maintenance

instantTrialDurationMinutes

isBiopharma

enableNewMyJoveSectionDesign

educationFeatures

seoMetaApi

ai_copilot_institution_blacklist

ai_chat_institution_blacklist

freeAccessWindow

ssoRoleCapture

scheduledMaintenanceBanner

joveLabsFeatures

disable_autoplay_for_bots

extended_trial_duration

5 minutes

Bu çalışma, Japonya Bilim ve Teknoloji Ajansı(JPMJCR14F3) crest programı ve Japonya Bilimin Teşvik Derneği'nden (19H00846 ve 18K14120) Hibe in-Aids programı tarafından desteklenmiştir. Bu çalışma kısmen Tohoku Üniversitesi Elektrik İletişimi Araştırma Enstitüsü Nanoelektronik ve Spintronics Laboratuvarı'nda gerçekleştirilmiştir.

1. Hibrit bir çözeltinin hazırlanması
<ol><li>Yıkama dört 4 mL tek kullanımlık cam şişeleri ve vida kapakları (PTFE kaplı mühürler ile) distile suda 10 dakika ultrasonik banyo (bir filtrasyon sistemi ile arıtılmış), sırasıyla etanol ve kloroform izledi. Azot gazı akışında cam şişeleri ve kapakları kurulayın.</li>
	<li>Bir anaerobik eldiven kutusunda, kloroform toz CuPc eriterek yıkanmış cam şişe bir CuPc stok çözeltisi (10 mg / mL) hazırlamak.</li>
	<li>CuPc çözeltisini 0,2 μm politetrafloroetilen (PTFE) membrandan filtreleyin.</li>
	<li>Filtrelenmiş çözeltiyi azot dolu yıkanmış bir cam şişede saklayın ve şişeyi parafilmle kapatın.</li>
	<li>Satın alınan 1,2-diphytanoyl-sn-glycero-3-fosfokolin (DPhPC) kloroform çözeltisini (25 mg/mL) -80 °C buzdolabından çıkarın ve oda sıcaklığına kadar ısıtın.</li>
	<li>10 s için 2300 rpm bir girdap karıştırıcı kullanarak DPhPC çözeltisi karıştırın.</li>
	<li>5 kez kloroform ile bir cam mikro şırınga durulayın.</li>
	<li>DPhPC kloroform çözeltisinin 200 μL'sini yıkanmış şırınga kullanarak önceden yıkanmış cam şişeye aktarın. Şişedeki çözücüyü nazik bir nitrojen akışıyla buharlaştırın.</li>
	<li>Bir cam mikro şırıngayı 5 kez kloroformla durulayın.</li>
	<li>Temizlenmiş şırınga kullanarak DPhPC ile cam şişeye 202,6 μL kloroform ekleyin.</li>
	<li>DPhPC çözeltisine 47,4 μL filtrelenmiş 10 mg/mL CuPc çözeltisi ekleyin. DPhPC'nin CuPc'ye molar oranı 10:1 olmalıdır.</li>
	<li>Cam mikro şırıngayı 5 kez kloroformile durulayın.</li>
	<li>Şırıngayı kullanarak çözeltiye 250°L heksane ekleyin. Çözeltinin son konsantrasyonu 10 mg/mL olmalıdır.</li>
	<li>Hazırlanan çözeltiyi 10 s için 2300 rpm'de bir girdap mikseri kullanarak karıştırın.</li>
	<li>CuPc çözeltisini 0,2 μm politetrafloroetilen (PTFE) membrandan filtreleyin.</li>
	<li>Cam şişeyi parafilmle kapatın. Azot dolu bir kavrama mühürlü torbaya koyun ve kavrama mühürlü torbayı -20 °C'de bir dondurucuya yerleştirin. NOT: DPhPC ve CuPc 1.13.adımdan sonra kloroform ve heksandan (hacim oranı 1:1) oluşan karışık bir çözücü de çözüldü. Buna ek olarak, DPhPC'nin CuPc'ye molar oranı 10:1 ile sınırlı değildir. Sabit lipid konsantrasyonu (10 mg/mL) ile farklı molar oranlar kullanılabilir. Önceki deneysel sonuçlara göre, yüksek kaliteli hibrid lipid membran ı oluşturmak için 10:1 ile 3:1 arasında bir aralık tercih edilmektedir.</li>
</ol>2. Su/hava arabiriminde hibrit membran oluşumu
<ol><li>Si gofretinden Si yüzeyleri (3 cm x 3 cm) kesin.</li>
	<li>Temiz 3 cm x 3 cm Si arıtılmış suda 10 dakika ultrasonik banyoda yüzeyler, etanol ve ardından kloroform izledi. Yüzeyden adsorbe organik maddeleri kaldırmak ve hidrofililiği artırmak için Si substratını 5 dakika boyunca O2 plazmaile tedavi edin.</li>
	<li>Bir Teflon kabını 7,5 cm'lik iç çapı ile 3 dakika boyunca akan arıtılmış su ile yıkayın.</li>
	<li>Yıkanmış PTFE kabına temizlenmiş Si substratını koyun. Substrat 30° açıyla yataya doğru yatırılır.</li>
	<li>Tüm Si substrat batırılmış kadar Teflon kabı içine arıtılmış su yeterli miktarda dökün.</li>
	<li>Hazırlanan hibrid çözeltiyi dondurucudan alın ve oda sıcaklığına kadar ısıtın.</li>
	<li>15 s için 2300 rpm bir girdap karıştırıcı kullanarak hibrid çözeltisi karıştırın.</li>
	<li>Bir cam mikro şırıngayı (50°L) 5 kez kloroformla durulayın.</li>
	<li>Yüzen bir hibrid lipid membran oluşturmak için şırınga kullanarak su yüzeyine hibrid çözeltinin 3-5 μL bırakın. NOT: Çözelti bırakıldığında, damlacık su yüzeyine (1 cm'den az) yakın tutmak önemlidir. Ayrıca tek katmanlı hibrid membran çıplak gözle görülemez unutulmamalıdır, ama çok katmanlı hibrid membran ince olarak görünür, mavi renkli film. Çok katmanlı hibrid membranı Si substratına aktarmak için karışık çözeltiyi Si substratına mümkün olduğunca yakın bırakmak önemlidir.</li>
</ol>3. Membranın bir Si substratına aktarılması
<ol><li>Organik çözücübuharlaşma sonra (daha az alacak 2 saniye), 3 mm /dk bir hızda bir peristaltik pompa ile tahrik bir kauçuk tüp ile su pompalayarak su seviyesini düşürmek, Si substrat üzerine yüzen hibrid membran aktarmak için.</li>
	<li>Aktarım işlemi tamamlandıktan sonra (yaklaşık 5 dk), Si substratını temiz oda sileceklerine yerleştirin ve kalan suyun buharlaşmasına izin verin. NOT: Su seviyesinin bu kadar düşük bir oranda düşürülmesi, suyun türbülansını en aza indirmeye ve membranı korumaya hizmet eder.</li>
</ol>

<ol><li>Israelachvili, J. N., Mitchell, D. J., Ninham, B. W. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Theory+of+self-assembly+of+lipid+bilayers+and+vesicles%5BTitle%5D)+AND+%22Biochimica+Et+Biophysica+Acta-Biomembranes%22%5BJournal%5D)">Theory of self-assembly of lipid bilayers and vesicles.</a> Biochimica Et Biophysica Acta-Biomembranes. 470 (2), 185-201 (1977).</li>
<li>Venable, R. M., Zhang, Y., Hardy, B. J., Pastor, R. W. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Molecular+dynamics+simulations+of+a+lipid+bilayer+and+of+hexadecane%3A+an+investigation+of+membrane+fluidity%5BTitle%5D)+AND+%22Science%22%5BJournal%5D)">Molecular dynamics simulations of a lipid bilayer and of hexadecane: an investigation of membrane fluidity.</a> Science. 262 (5131), 223-226 (1993).</li>
<li>Ide, T., Ichikawa, T. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((A+novel+method+for+artificial+lipid-bilayer+formation%5BTitle%5D)+AND+%22Biosensors+and+Bioelectronics%22%5BJournal%5D)">A novel method for artificial lipid-bilayer formation.</a> Biosensors and Bioelectronics. 21 (4), 672-677 (2005).</li>
<li>Funakoshi, K., Suzuki, H., Takeuchi, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Lipid+bilayer+formation+by+contacting+monolayers+in+a+microfluidic+device+for+membrane+protein+analysis%5BTitle%5D)+AND+%22Analytical+Chemistry%22%5BJournal%5D)">Lipid bilayer formation by contacting monolayers in a microfluidic device for membrane protein analysis.</a> Analytical Chemistry. 78 (24), 8169-8174 (2006).</li>
<li>Kongsuphol, P., Fang, K. B., Ding, Z. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Lipid+bilayer+technologies+in+ion+channel+recordings+and+their+potential+in+drug+screening+assay%5BTitle%5D)+AND+%22Sensors+and+Actuators+B%3A+Chemical%22%5BJournal%5D)">Lipid bilayer technologies in ion channel recordings and their potential in drug screening assay.</a> Sensors and Actuators B: Chemical. 185, 530-542 (2013).</li>
<li>Demarche, S., Sugihara, K., Zambelli, T., Tiefenauer, L., Voros, J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Techniques+for+recording+reconstituted+ion+channels%5BTitle%5D)+AND+%22Analyst%22%5BJournal%5D)">Techniques for recording reconstituted ion channels.</a> Analyst. 136 (6), 1077-1089 (2011).</li>
<li>Sakaguchi, N., Kimura, Y., Hirano-Iwata, A., Ogino, T. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Fabrication+of+Au-nanoparticle-embedded+lipid+bilayer+membranes+supported+on+solid+substrates%5BTitle%5D)+AND+%22The+Journal+of+Physical+Chemistry+B%22%5BJournal%5D)">Fabrication of Au-nanoparticle-embedded lipid bilayer membranes supported on solid substrates.</a> The Journal of Physical Chemistry B. 121 (17), 4474-4481 (2017).</li>
<li>Schulz, M., Olubummo, A., Binder, W. H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Beyond+the+lipid+bilayer%3A+interaction+of+polymers+and+nanoparticles+with+membranes%5BTitle%5D)+AND+%22Soft+Matter%22%5BJournal%5D)">Beyond the lipid bilayer: interaction of polymers and nanoparticles with membranes.</a> Soft Matter. 8 (18), 4849-4864 (2012).</li>
<li>Wang, J., Wei, Y., Shi, X., Gao, H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Cellular+entry+of+graphene+nanosheets%3A+the+role+of+thickness%2C+oxidation+and+surface+adsorption%5BTitle%5D)+AND+%22RSC+Advances%22%5BJournal%5D)">Cellular entry of graphene nanosheets: the role of thickness, oxidation and surface adsorption.</a> RSC Advances. 3 (36), 15776-15782 (2013).</li>
<li>Vögele, M., Köfinger, J., Hummer, G. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Molecular+dynamics+simulations+of+carbon+nanotube+porins+in+lipid+bilayers%5BTitle%5D)+AND+%22Faraday+Discussions%22%5BJournal%5D)">Molecular dynamics simulations of carbon nanotube porins in lipid bilayers.</a> Faraday Discussions. 209, 341-358 (2018).</li>
<li>Kanomata, K., Deguchi, T., Ma, T., Haseyama, T., Miura, M., Yamaura, D., Tadaki, D., Niwano, M., Hirano-Iwata, A., Hirose, F. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Photomodulation+of+electrical+conductivity+of+a+PCBM-doped+free-standing+lipid+bilayer+in+buffer+solution%5BTitle%5D)+AND+%22Journal+of+Electroanalytical+Chemistry%22%5BJournal%5D)">Photomodulation of electrical conductivity of a PCBM-doped free-standing lipid bilayer in buffer solution.</a> Journal of Electroanalytical Chemistry. 832, 55-58 (2019).</li>
<li>Barnoud, J., Rossi, G., Monticelli, L. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Lipid+Membranes+as+Solvents+for+Carbon+Nanoparticles%5BTitle%5D)+AND+%22Physical+Review+Letters%22%5BJournal%5D)">Lipid Membranes as Solvents for Carbon Nanoparticles.</a> Physical Review Letters. 112, 068102(2014).</li>
<li>Dichello, G. A., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Preparation+of+liposomes+containing+small+gold+nanoparticles+using+electrostatic+interactions%5BTitle%5D)+AND+%22European+Journal+of+Pharmaceutical+Sciences%22%5BJournal%5D)">Preparation of liposomes containing small gold nanoparticles using electrostatic interactions.</a> European Journal of Pharmaceutical Sciences. 105, 55-63 (2017).</li>
<li>Sullivan, P., Heutz, S., Schultes, S. M., Jones, T. S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Influence+of+codeposition+on+the+performance+of+CuPc%E2%88%92C60+heterojunction+photovoltaic+devices%5BTitle%5D)+AND+%22Applied+Physics+Letters%22%5BJournal%5D)">Influence of codeposition on the performance of CuPc−C60 heterojunction photovoltaic devices.</a> Applied Physics Letters. 84 (7), 1210-1212 (2004).</li>
<li>Miyata, T., Kawaguchi, S., Ishii, M., Minami, T. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((High+sensitivity+chlorine+gas+sensors+using+Cu%E2%88%92phthalocyanine+thin+films%5BTitle%5D)+AND+%22Thin+Solid+Films%22%5BJournal%5D)">High sensitivity chlorine gas sensors using Cu−phthalocyanine thin films.</a> Thin Solid Films. 425 (1-2), 255-259 (2003).</li>
<li>Barrena, E., de Oteyza, D. G., Dosch, H., Wakayama, Y. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((2D+supramolecular+self-assembly+of+binary+organic+monolayers%5BTitle%5D)+AND+%22ChemPhysChem%22%5BJournal%5D)">2D supramolecular self-assembly of binary organic monolayers.</a> ChemPhysChem. 8 (13), 1915-1918 (2007).</li>
<li>Xiao, K., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Surface-induced+orientation+control+of+CuPc+molecules+for+the+epitaxial+growth+of+highly+ordered+organic+crystals+on+graphene%5BTitle%5D)+AND+%22Journal+of+the+American+Chemical+Society%22%5BJournal%5D)">Surface-induced orientation control of CuPc molecules for the epitaxial growth of highly ordered organic crystals on graphene.</a> Journal of the American Chemical Society. 135 (9), 3680-3687 (2013).</li>
<li>Feng, X., Ma, T., Yamaura, D., Tadaki, D., Hirano-Iwata, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Formation+and+characterization+of+air-stable+lipid+bilayer+membranes+incorporated+with+phthalocyanine+molecules%5BTitle%5D)+AND+%22The+Journal+of+Physical+Chemistry+B%22%5BJournal%5D)">Formation and characterization of air-stable lipid bilayer membranes incorporated with phthalocyanine molecules.</a> The Journal of Physical Chemistry B. 123 (30), 6515-6520 (2019).</li>
<li>Wu, Y., He, K., Ludtke, S. J., Huang, H. W. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((X-ray+diffraction+study+of+lipid+bilayer+membranes+interacting+with+amphiphilic+helical+peptides%3A+diphytanoyl+phosphatidylcholine+with+alamethicin+at+low+concentrations%5BTitle%5D)+AND+%22Biophysical+Journal%22%5BJournal%5D)">X-ray diffraction study of lipid bilayer membranes interacting with amphiphilic helical peptides: diphytanoyl phosphatidylcholine with alamethicin at low concentrations.</a> Biophysical Journal. 68 (6), 2361-2369 (1995).</li>
<li>Zaitseva, S. V., Bettini, S., Valli, L., Kolker, A. M., Borovkov, N. Y. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Atypical+film-forming+behavior+of+soluble+tetra-3-nitro-substituted+copper+phthalocyanine%5BTitle%5D)+AND+%22ChemPhysChem%22%5BJournal%5D)">Atypical film-forming behavior of soluble tetra-3-nitro-substituted copper phthalocyanine.</a> ChemPhysChem. 20 (3), 422-428 (2019).</li>
<li>Ghani, F., Gojzewski, H., Riegler, H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Nucleation+and+growth+of+copper+phthalocyanine+aggregates+deposited+from+solution+on+planar+surfaces%5BTitle%5D)+AND+%22Applied+Surface+Science%22%5BJournal%5D)">Nucleation and growth of copper phthalocyanine aggregates deposited from solution on planar surfaces.</a> Applied Surface Science. 351, 969-976 (2015).</li>
</ol>

Yazarların açıklayacak bir şeyi yok.

Melez membranın öncü çözeltisinde, saf kloroform yerine karışık organik çözücü (kloroform ve hekzan) lipidleri ve CuPc'yi eritmek için kullanılır. Saf kloroform kullanılırsa, öncül çözeltinin yoğunluğu sudan daha yüksek olacaktır. Bu nedenle, çözeltinin su yüzeyine yayılmak yerine suyun dibine batması çok olasıdır. Öncül çözeltiye düşük yoğunluklu bir çözücü olan heksanın eklenmesi, çözeltinin su yüzeyinde süzülmesini ve çözücünün buharlaşmasından sonra tek tip bir hibrid membran oluşturmasını sağlar. Ayrıca, çözelti su ...

Hücre zarlarının temel çerçeveleri olarak, hücrelerin iç bir lipid çift katmanlı sistemi ile dış ayrılır. Bu sistem fofilik fosfolipidler oluşur, hangi hidrofilik fosforik ester oluşur "kafaları" ve hidrofobik yağ asitleri "kuyrukları". Sulu ortamda lipid iki katlarının olağanüstü akışkanlığı ve kendi kendine montaj yeteneği nedeniyle1,2, yapay lipid bilayers basit yöntemlerkullanılarak oluşturulabilir3,4. Iyon kanalları, membran reseptörleri ve enzimler gibi çeşitli membran proteinlerinin, hücre zarlarının işlevlerini taklit etmek ve incelemek için yapay lipid bilayer içine dahil edilmiştir5,6. Daha yakın zamanlarda, lipid iki katmanlı nanomalzemeler ile doped edilmiştir (örneğin, metal nano tanecikleri, grafen, ve karbon nanotüpler) fonksiyonel hibrid membranlar oluşturmak için7,8,9,10,11,12,13. Bu tür hibrid membranlar oluşturmak için yaygın olarak kullanılan bir yöntem, modifiye Au-nanotanecikleri7 veya karbon nanotüpler11gibi hidrofobik malzemeler içeren doped lipid veziküloluşumunu içerir , ve ortaya çıkan veziküller daha sonra düzlemsel destekli lipid bilayers içine eritilir. Ancak, bu yaklaşım karmaşık ve zaman alıcı, bu tür hibrid membranların potansiyel kullanımları sınırlar.
Bu çalışmada, lipid membranlar kendi kendine montaj ile su / hava arabiriminde oluşan hibrid lipid membranlar üretmek için organik moleküller ile doped edildi. Bu protokol üç adım dan oluşur: karışık çözeltinin hazırlanması, su/hava arabiriminde hibrit membran oluşumu ve membranın Si substratına aktarılması. Daha önce bildirilen diğer yöntemlerle karşılaştırıldığında, burada açıklanan yöntem daha basittir ve gelişmiş enstrümantasyon gerektirmez. Bu yöntem kullanılarak daha geniş bir alana sahip hava stabil hibrid lipid membranlar daha kısa sürede oluşturulabilir. Bu çalışmada kullanılan nanomalzeme bir yarı iletken organik molekül, bakır (II) 2,9,16,23-tetra-tert-butyl-29H, 31H-phthalocyanine (CuPc), yaygın olarak güneş pilleri, fotodedektörler, gaz sensörleri ve kataliz14,15dahil olmak üzere bir dizi uygulamada kullanılır . Düzlemsel yapıya sahip küçük bir organik molekül olan CuPc, fosfolipid ikilisinin hidrofobik özelliklerine "kuyrukları" için yüksek bir afiniteye sahiptir. Diğer gruplar CuPc moleküllerinin tek kristal yüzeylerde yüksek sıralı yapıların oluşumu ile kendi kendine biraraya getirebildiği bildirilmiştir16,17. Bu nedenle, CuPc moleküllerinin kendi kendine montaj yoluyla lipid iki katiçine dahil edilebilir son derece mümkündür.
Membranoluşturmak için kullanılan prosedürlerin ayrıntılı bir açıklamasını sağlar ve bu prosedürün sorunsuz bir şekilde uygulanması için bazı öneriler sayılmaktayız. Buna ek olarak, hibrid lipid membranların bazı sunum sonuçları sunmak ve bu yöntemin potansiyel uygulamaları tartışmak.

<table><tbody><tr><td>Kloroform</td><td>Wako&nbsp; Kimyasallar</td><td>033-08631</td><td></td></tr><tr><td>CuPc</td><td>Sigma-Aldrich</td><td>423165</td><td></td></tr><tr><td>DPhPc</td><td>Avanti Polar Lipidler</td><td>850356C</td><td></td></tr><tr><td>Vidalı kapaklı cam şişeler</td><td>Nichiden-Rike Glass Co., Ltd</td><td>6-29801</td><td></td></tr><tr><td>Hexane</td><td>Wako&nbsp; Kimyasallar</td><td>084-03421</td><td></td></tr><tr><td>Membran filtreler</td><td>Merck Millipore Ltd.</td><td></td><td></td>R8CA42836</tr><tr><td>Mikro şırınga</td><td>Hamilton</td><td>80530</td><td></td></tr><tr><td>Peristaltik pompa</td><td>Tokyo Rikakikai Co., Ltd.</td><td></td><td></td>11914199</tr><tr><td>Vorteks karıştırıcı</td><td>Scientific Industries, Inc.</td><td>SI-0286</td><td></td></tr></tbody></table> Serisi

su/hava arabiriminde hidrofobik organik moleküllerle doped hibrid lipid membranların kendi kendine montajı

Self-Assembly of Hybrid Lipid Membranes Doped with Hydrophobic Organic Molecules at the Water/Air Interface

Ultraince kalınlık (3-4 nm), ultra yüksek direnç, akışkanlık ve kendi kendine montaj yeteneği gibi benzersiz özellikleri nedeniyle, lipid iki katmanları kolayca işlevsel hale getirilebilir ve biyo-sensörler ve biyo-cihazlar gibi çeşitli uygulamalarda kullanılmıştır. Bu çalışmada, bir düzlemsel organik molekül tanıttı: bakır (II) 2,9,16,23-tetra-tert-butyl-29H, 31H-phthalocyanine (CuPc) dope lipid membranlar için. CuPc/lipid hibrid membran, su/hava arabiriminde kendi kendine montaj yoluyla oluşur. Bu membranda, hidrofobik CuPc molekülleri lipid moleküllerinin hidrofobik kuyrukları arasında yer alır, bir lipid / CuPc / lipid sandviç yapısı oluşturan. İlginçtir, bir hava kararlı hibrid lipid çift katmanlı kolayca bir Si substrat üzerine hibrid membran transfer imal edilebilir. Biyosensörler ve biyocihazların üretimi için yeni bir metodolojiyi temsil eden, nanomateryalleri lipid çift katmanlı bir sisteme dahil etmek için basit bir yöntem sunacağız.

Olarak oluşan membran CuPc moleküllerinin varlığı nedeniyle düzgün bir açık mavi renge sahiptir. Renkli membran alanı normalde birkaç santimetre kare. Şekil 1A ve Şekil 1B'de,bir Si substratı üzerinde hibrit lipid membranının mikroskobik görüntü ve atomik kuvvet mikroskobu (AFM) görüntüsü (yükseklik profili dahil) gösteririz. AFM görüntüde, sol üstteki membran kalın, kalınlığı 79.4 nm ve sağ alt kısım ince, kalınlığı 4.9 nm.'dir. İnce membran, temizlenen Si subs...

Biz bakır ile lipid bilayer doping tarafından su / hava arayüzü bir hibrid lipid membran üretmek için bir protokol rapor (II) 2,9,16,23-tetra-tert-butyl-29H,31H-phthayanilocne (CuPc) molekülleri. Ortaya çıkan hibrid lipid membran lipid/CuPc/lipid sandviç yapısına sahiptir. Bu protokol diğer fonksiyonel nanomalzemelerin oluşumuna da uygulanabilir.

Su/Hava Arabiriminde Hidrofobik Organik Moleküllerle Doped Hibrid Lipid Membranların Kendi Kendine Montajı

Because of their unique properties, including an ultrathin thickness (3-4 nm), ultrahigh resistivity, fluidity and self-assembly ability, lipid bilayers ...

Protokolümüz, organik molekül doped hibrid lipid membranları imal etmek için basit bir yöntem göstermektedir. Membranın hava stabil özelliği katı hal cihazlarına lipid iki katmanlı yapının uygulanmasını genişletebilir. Biz birkaç nanometre kalınlığında hibrid lipid membranlar oluşturmak için kendi kendine montaj işlemi kullanın.Bu protokol basit ve takip etmek kolaydır ve karmaşık ekipman gerektirmez. Bu yöntem diğer aynı biyohibrid lipid membranlar imal etmek için kullanılabilir ve kolayca sensörler ve diğer algılama cihazları hem de kabul edilebilir. Bir anaerobik eldiven kutusunda çalışma, bir yıkanmış cam şişe içinde kloroform bakır phthalocyanine eritmek mililitre bakır phthalocyanine stok çözeltisi başına 10 miligram hazırlamak için.Çözeltiyi 0,2 mikrometrelik PTFE membranDan filtreleyin. DPHPC çözeltisini 2, 300 RPM'de 10 saniye boyunca girdap karıştırıcısıyla karıştırın. Daha sonra kloroform ile bir cam mikro şırınga beş kez durulayın ve önceden yıkanmış cam şişe içine çözelti200 mikrolitre aktarmak için kullanabilirsiniz.Şişedeki çözücüyü nazik bir nitrojen akışıyla buharlaştırın. Kloroform ile başka bir cam mikro şırınga durulayın, sonra DPHPC ile cam şişe ye kloroform 20

self-assembly-hybrid-lipid-membranes-doped-with-hydrophobic-organic

Research

JoVE Journal

Chemistry

Kimya

Desteklenen ikili lipid tabakalarıdır ve doğal zar parçacıkları hücre zarlarının özelliklerini yaklaşık ve analitik çeşitli stratejiler dahil edilmesi uygun sistemlerdir. Burada destekli lipid iki katmanlı kaplı SiO 2 boncuklar, fosfolipid vezikülleri ya da doğal zar parçacıklarının oluşan mikrodizileri hazırlanması için bir yöntemi göstermektedir.

Bir Çekçek tabanlı Meclisi Yöntemi ile Biomembrane Mikroarray&#39;ler oluşumu

Biz lipid veziküller kullanmadan katı yüzeyler üzerinde desteklenen lipid çift oluşturmak için deneysel bir protokol mevcut. Çeşitli biyolojik uygulamalarda, kolesterol açısından zengin bir etki ile, bir lipid, silikon dioksit ve altın iki tabakalı olarak desteklenen zarları meydana getirmek üzere, bir aşamalı bir yöntemi göstermektedir.

Solvent destekli çift katlı lipid (SALB) Yöntemi ile biyomembran Fabrikasyon

Çekirdeklerinde kendi kendine birleşmiş nanoyapılar içeren lipid parçacıklarının kinetik stabilizasyonu için karbon nanotüplerin akıllı bir uygulamasını rapor ediyoruz. Lipid parçacıklarının hazırlanması, ilaç dağıtımı gibi biyomedikal uygulamalarda kullanımlarına izin veren oldukça düşük konsantrasyonlarda karbon nanotüpler gerektirir.

Karbon Nanotüpler tarafından Stabilize İçeriden Kendinden monte Lipid Parçacıklar uyduruk hazırlanması

Bir depolanabilir, taşınabilir lipit iki katmanlı oluşum sistemi göstermektedir. Dondurulmuş bir membran ön-madde çevre sıcaklığına getirildiğinde bir lipid iki-tabakalı zar üzerinden% 80 başarı oranı ile 1 saat içinde oluşturulabilmektedir. Bu sistem iyon kanalları ile ilişkili zahmetli süreçler ve uzmanlık azaltacaktır.

Bir polidimetilsiloksan İnce Film Kullanarak Otomatik çift katlı lipid Membran Oluşumu

Biz bir protokol vitro için zihin ve benim kendi kendine organizasyon deneyleri desteklenen lipid bilayer açık bir odasında üzerinde sağlar. Ayrıca, biz tepki doğumdan tarafından vivo koşulları taklit için PDMS microcompartments lipid kaplı tahlil içine alın anlatan.

Vitro Sulandırma Protein kalıpları üzerinde desteklenen Lipid Bilayers kendi kendini düzenleme

Bu protokol, yüksek erime sıcaklıklarına sahip lipitler için lipid monolayer montajını ve damlacık arayüzü bilayer oluşumunu teşvik etmek için geri bildirim sıcaklığı kontrollü bir ısıtma sisteminin kullanımını ve membrandaki sıcaklık odaklı değişiklikleri karakterize etmek için kapasitans ölçümlerini detaylandırıyor.

Damlacık Arayüzü Bilayer'in Sıcaklık Kontrollü Montajı ve Karakterizasyonu

Bu protokolde tek lipid ve multi-lipid vesicles, desteklenen lipid bilayerler ve askıda lipid bilayerleri taklit eden hücre oluşumu açıklanmaktadır. Bu in vitro modeller çeşitli lipit tiplerini içerecek şekilde uyarlanabilir ve çeşitli molekül ve makromolekül etkileşimlerini araştırmak için kullanılabilir.

Moleküler Etkileşimlerin Çalışması için Desteklenen ve Askıya Alınan Lipid Bilayer Modellerinin Hücre Taklit Montajı

Burada, tek moleküllü toplam iç yansıma floresan (smTIRF) mikroskobu kullanılarak yapay kalabalık lipit membranları üzerindeki tek moleküllerin bağlanma, hareketlilik ve montajını gerçekleştirmek ve analiz etmek için bir protokol sunulmaktadır.

Tek Moleküllü Difüzyon ve Polimer Kalabalık Lipid Membranlara Montaj

Mevcut protokol, biyouyumlu lipozomlar üretmek için mikroakışkan bir teknik olan oktanol yardımlı lipozom montajını (OLA) tanımlamaktadır. OLA, verimli kapsülleme ile monodispersed, mikron boyutunda lipozomlar üretir ve anında çip üzerinde deneylere izin verir. Bu protokolün sentetik biyoloji ve sentetik hücre araştırmaları için özellikle uygun olması beklenmektedir.

Biyomühendislik için On-Chip Oktanol Destekli Lipozom Montajı

Yapı ve bileşimdeki membran lipid çeşitliliği, hücresel süreçlere önemli bir katkıda bulunur ve bir hastalık belirteci olabilir. Moleküler dinamik simülasyonları, membranları ve bunların biyomoleküllerle etkileşimlerini atomistik çözünürlükte incelememizi sağlar. Burada, karmaşık membran sistemlerini oluşturmak, çalıştırmak ve analiz etmek için bir protokol sağlıyoruz.

Simülasyon Çalışmalarında Kompleks Lipid Karışımları Kullanılarak Gerçekçi Membran Modellemesi

Öğrenin, su/hava arabiriminde kendi kendine montaj yöntemiyle bakır ftalosiyanin katkılı hibrid lipid membranları nasıl üretilir. Bu basit protokol, katı hal cihazları ve sensör uygulamaları için hava stabilitesi sağlar.

Su/Hava Arabiriminde Hidrofobik Organik Moleküllerle Doped Hibrid Lipid Membranların Kendi Kendine Montajı

Daha fazla video keşfet