Name: Simulation, Fabrication and Characterization of THz Metamaterial Absorbers (Video) | JoVE Journal
Uploaded: 2012-12-27T13:00:00.000+00:00
Duration: 13 min 44 s
Description: Learn to simulate, fabricate and characterize terahertz metamaterial absorbers using Fourier transform infrared spectroscopy. This method enables development of devices achieving over 80% absorption for terahertz imaging applications.

ai_agent_IP

ai_agent

maintenance

instantTrialDurationMinutes

isBiopharma

enableNewMyJoveSectionDesign

educationFeatures

seoMetaApi

ai_copilot_institution_blacklist

ai_chat_institution_blacklist

freeAccessWindow

ssoRoleCapture

scheduledMaintenanceBanner

joveLabsFeatures

disable_autoplay_for_bots

extended_trial_duration

5 minutes

This work is supported by the Engineering and Physical Sciences Research Council grant number EP/I017461/1. We also wish to acknowledge the contribution played by the technical staff of the James Watt Nanofabrication Centre.

1. Simulation of a Single Band THz Metamaterial Absorber
 A 3D view of the simulation set-up is shown in Figure 2.
 <ol>
 <li>Lumerical FDTD is used to optimize the transmission, reflection and absorption characteristics of the THz metamaterial absorber. All units are given in &mu;m.</li>
 <li>Define the THz polyimide material properties by left clicking Materials, Add (n,k) material and inputting 1.68 as the n and 0.06 as the k. Double left click on "new material 1" and rename it as "polyimide". Note that if theoretical or experimental refractive index data is available one can "add sampled data" to define the material properties.</li>
 <li>Draw the geometry of the device, starting with the 0.2 &mu;m thick metal ground plane. In the structures tab select rectangle and edit the properties by pressing the e key. Input "groundplane" in the name window, (0,0,0.1) as the structure centre co-ordinates and (31,31,0.2) as the span region. Move to the material tab and select Perfect Electrical Conductor (PEC). Repeat to define the 3 &mu;m thick polyimide dielectric layer typing "polyimide" in the name window, (0,0,1.7) as the centre co-ordinates and (31,31,3) as the span. Finally define the 0.2 &mu;m thick electric ring resonator by drawing two rectangular Perfect Electrical Conductor (PEC) regions called "ERR arm1" and "ERR arm2" with the same centre co-ordinates of (0,0,3.3) but different span regions of (10,26,0.2) and (26,10,0.2) respectively.</li>
 <li>Add the simulation region by left clicking on Simulation and press e to edit the properties. In the general tab input 20 psec as the simulation time. In the geometry tab choose (0,0,0) as the centre co-ordinates and (30,30,200) as the span regions. In the mesh settings tab select a mesh accuracy of 3 and keep the other default settings as they are. Set the simulation boundary conditions in the boundary conditions tab choosing "Anti-symmetric" for x min bc and x max bc, "symmetric" for y min bc and y max bc and "PML" for z min bc and z max bc (the "allow symmetry on all boundaries" must be ticked). Include a mesh override region by left clicking again on Simulation and edit by pressing e. In the general tab type 0.5 &mu;m for the dx and dy override and 0.05 &mu;m for the dz override. In the geometry tab enter the centre co-ordinates (0,0,1.7) and span regions (30,30,3.8). Note that a smaller mesh size of e.g. dx, dy 0.1 &mu;m, will increase simulation accuracy though this will come at the expense of significantly increased CPU memory and simulation time. It is best to simulate using a large mesh size until a structure with the desired properties is obtained and then re-simulate using the smaller mesh size.</li>
 <li>Define the source type by left clicking on the arrow next to sources and choosing plane wave. Press e to edit the source properties and in the general tab change the direction to backward. In the geometry tab enter the centre co-ordinates (0,0,90) and (35,35,0) for the span region. Note that you cannot modify the z span. Set the minimum and maximum frequency of the simulation in the frequency/wavelength tab. Choose a minimum of 1 THz and a maximum of 4 THz and ensure the pulse in the signal versus time graph in the bottom right corner of the window decays to zero well before 20 psec.</li>
 <li>Left click on the arrow next to Monitors and select frequency-domain field profile. Press e to edit the monitor properties and enter "r95" in the monitor name window. In the geometry tab enter the centre co-ordinates of (0,0,95) and span region (30,30,0). Repeat and create a second frequency-domain field profile monitor called "t95" with centre co-ordinates (0,0,-95) and spans (30,30,0). Left click on the arrow next to Monitors and select global properties. In the frequency/power profile tab enter 100 in the frequency points window. Figure 2 shows the perspective view displayed in Lumerical on completion of steps 1.1-1.6. Check the memory requirements are compatible with your computer by left clicking on the arrow next to the Check icon on the top toolbar and selecting check simulation memory requirements. Save the file giving it an appropriate name such as "Jove.sim".</li>
 <li>Run the simulation by left clicking on the Run icon.</li>
 <li>On completion of the simulation enter the following into the script prompt window. Note that one can also enter the following text in a text editor and save the file as a .lsf file. The script can then be run by left clicking on the arrow next to Run, selecting script and then locating the script file saved on your computer. Note that the # symbol indicates a comment. 
</li>
 </ol>

 load("Jove_sim"); # loads the simulation file 
f = getdata("r95","f"); # gets the reflection data and frequency data from the r95 monitor 
R = transmission("r95"); # defines R as a matrix containing the reflection data 
A = 1-R; # calculates the absorption 
fthz=f/1e12; # converts frequency to THz 
plot(fthz,A,R,"Frequency(THz)","Absorption","Reflection"); # plot data on a single graph 
legend("Absorption","Reflection"); 
filename = "Jove_sim.csv"; # export data for excel import 
rm(filename); # delete file if it already exists 
lambda = c/f; # converts frequency to wavelength 
for(i=1:length(lambda)) { 
 &nbsp;&nbsp;write(filename,num2str(f(i)) + "," + 
 num2str(fthz(i)) + "," + 
 num2str(R(i)) + "," +
 num2str(A(i)) + "," ); 
} # outputs a .csv file in column format of the frequency, reflection and absorption
2. Fabrication of a Single Band THz Metamaterial Absorber
 Figure 3 shows the most important fabrication steps.
 <ol>
 <li>Clean a 15 mm by 15 mm piece of silicon in sequential solutions of warm (50 &deg;C) opticlear, acetone and ispopropanol using ultrasonic agitation after initially heating the beaker containing the solvent for 10 min. Note that this protocol can also be used to fabricate several devices onto a 4 inch diameter wafer.</li>
 <li>Evaporate a metal bi-layer of 20 nm/100 nm Ti/Au onto the 15 mm by 15 mm using a Plassys 450 MEB electron beam evaporator (Figure 3, step 1). Note that the metal thickness must be greater than the skin depth at the desired operating frequency.</li>
 <li>Clean the sample as previously described in section 2.1</li>
 <li>Dispense VM651 primer onto the sample using a pipette and leave to relax for 20 sec. Spin sample at 4,000 rpm for 5 sec and then bake on a contact hotplate at 120 &deg;C for 60 sec.</li>
 <li>Remove Dupont PI2545 polyimide from the freezer. Allow 20 min for the bottle to reach room temperature. This is essential since opening the bottle directly after removal from the freezer will result in moisture condensing inside the bottle and degrading the polyimide film properties. Dispense PI2545 onto the sample using a pipette and allow 20 sec for it to relax. Spin sample using a 2 stage spin procedure with the following settings - (i) final spin speed 500 rpm, acceleration 100 rpms-1, final spin time 5 sec (ii) final spin speed 6,000 rpm, acceleration 500 rpms-1, final spin time 60 sec. Bake sample on a contact hotplate at 140 &deg;C for 5 min (Figure 3, step 2). If a thicker polyimide film is required then either spin multiple layers or reduce the final spin speed. To obtain a polyimide film thickness of 3 &mu;m with minimal edge bead three layers of PI2545 are spun using the above protocol.</li>
 <li>Cure the polyimide on a contact hotplate at 220 &deg;C for 10 min. After this cure procedure the PI2545 will be impervious to most solvents and acids and can only be removed using oxygen plasma. PI2545 can be spun onto a dummy piece of silicon, cured as above and the thickness of the film measured by scratching the polyimide and using a DEKTAK surface profilometer to measure the step height.</li>
 <li>Deposit 15% 2010 Poly(methyl methacrylate), known as PMMA, onto the sample. Spin at 5,000 rpm for 60 sec and bake in a convection oven at 180 &deg;C for 30 min. Before baking remove any excess resist that has crept on to the backside of the sample using acetone. Remove sample from the oven and leave to cool to room temperature (~5 min). Deposit 4% 2041 PMMA onto the sample, spin at 5,000 rpm for 60 sec and bake in a convection oven at 180 &deg;C for 60 min (Figure 3, step 3). Remove any excess resist that has crept on to the backside of the sample using acetone before baking.</li>
 <li>Write the desired job on a Vistec VB6 electron beam writer using a dose of 450 &mu;C/cm2. The job file is designed in Tanner L-Edit, fractured into polygons by Layout Beamer and finally submitted to the beam writer using the Java based BELLE software.</li>
 <li>Develop the sample in a solution of 1:1 MIBK:IPA at a temperature of 23 &deg;C for 60 sec (Figure 3, step 4). Rinse in a beaker of isopropanol. Inspect pattern fidelity on an optical microscope. If features are poorly resolved strip the resist in opticlear, acetone and isopropanol and start again from 2.2.</li>
 <li>Descum the sample with O2 using a Gala Plasmaprep5 barrel asher for 1 min at 0.1 mbar and 50 W RF power. Evaporate 20 nm Ti and 150 nm Au using a Plassys 450 MEB electron beam evaporator (Figure 3, step 5).</li>
 <li>Insert the sample into a beaker of warm acetone and place the beaker into a hot water bath kept at 50 &deg;C. After 4 hr remove the sample from the water bath and using a pipette suck up some of the warm acetone and spray liberally onto the sample (Figure 3, step 6). Inspect sample by eye to check that metal is lifting off from the areas where PMMA was present. If lift-off is progressing slowly place beaker in the ultrasonic water bath for 2 min. Inspect sample under the optical microscope.</li>
 <li>The protocol describes the fabrication of a single band THz absorber however multi-level dual band and broadband absorbers can be produced by repeating steps 2.3-2.11 and stacking several crosses on top of polyimide layers.</li>
 </ol>
 3. Characterization of a Single Band THz Metamaterial Absorber
 Figure 4 shows the basic FTIR instrument layout.
 <ol>
 <li>Turn on the nitrogen supply to the IFS 66V/S Fourier Transform Infra Red (FTIR) spectrometer. Press the "FIR" button on the front of the spectrometer control unit to turn on the Hg arc lamp. It takes around 15 min for the lamp power to stabilize. Insert the 6 &mu;m multilayer beam splitter into the appropriate slot in the interferometer unit.</li>
 <li>Vent the sample compartment of the spectrometer and insert the PIKE 30 &deg; reflection unit. Place the 4 mm aperture on top of the reflection unit aperture and on top of this put a gold mirror. The 4 mm aperture determines the area of the sample that will be interrogated while the gold mirror is necessary to make a background measurement.</li>
 <li>Evacuate the sample compartment and wait for the pressure to get down to 5 mbar. The spectrometer can be run in a purged nitrogen environment however the signal size typically drops to less than 20% compared to vacuum.</li>
 <li>Start the OPUS software and load the configuration file (set-up on installation of the unit) for taking measurements in the 30 cm-1 to 300 cm-1 range (1-9THz). This file sets numerous spectrometer parameters such as the scanner velocity, source aperture, source type, data collection method and Fourier transform execution mode. Ensure the LED on the front of the detector compartment is flashing green, indicating that the scanner is operating. Check that the shape of the interferogram is as expected.</li>
 <li>Run 100 background scans to obtain the background spectrum.</li>
 <li>Vent sample compartment, remove mirror and place sample face down onto the aperture. Ensure the centre of the sample is in the middle of the aperture. Evacuate the sample compartment.</li>
 <li>Run 1,000 sample scans to obtain the sample spectrum. The sample spectrum will be compared to the background reference spectrum and the final reflection spectrum of the sample obtained. Note that if the signal reaching the detector is low, a greater number of sample scans may be required to reduce the noise (e.g. 10,000 scans). Repeat sample scans should be made to ensure the measured data is reliable and consistent.</li>
 <li>Data from the completed scan can be converted into a text file and analyzed offline. The continuous ground plane of the sample means that there is no transmission ergo the absorption spectrum can be found by subtracting the reflection from 1.</li>
 </ol>

<ol><li>Pendry, J. B., Holden, A. J., Robbins, D. J., Stewart, W. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Magnetism+from+conductors+and+enhanced+nonlinear+phenomena%5BTitle%5D)+AND+%22IEEE+Trans.+Microw.+Theory%22%5BJournal%5D)">Magnetism from conductors and enhanced nonlinear phenomena.</a> IEEE Trans. Microw. Theory. 47, 2075-2084 (1999).</li>
<li>Pendry, J. B., Holden, A. J., Robbins, D. J., Stewart, W. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Magnetism+from+conductors+and+enhanced+nonlinear+phenomena%5BTitle%5D)+AND+%22IEEE+Microw+Theory%22%5BJournal%5D)">Magnetism from conductors and enhanced nonlinear phenomena.</a> IEEE Microw Theory. 47, 2075-2084 (1999).</li>
<li>Smith, D. R., Padilla, W. J., Vier, D. C., Nemat-Nasser, S. C., Schultz, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Composite+medium+with+simultaneously+negative+permeability+and+permittivity%5BTitle%5D)+AND+%22Phys.+Rev.+Lett%22%5BJournal%5D)">Composite medium with simultaneously negative permeability and permittivity.</a> Phys. Rev. Lett. 84, 4184-4187 (2000).</li>
<li>Dolling, G., Wegener, M., Linden, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Realization+of+a+three-functional-layer+negative-index+photonic+metamaterial%5BTitle%5D)+AND+%22Opt.+Lett%22%5BJournal%5D)">Realization of a three-functional-layer negative-index photonic metamaterial.</a> Opt. Lett. 32, 551-553 (2007).</li>
<li>Zhang, S., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Experimental+demonstration+of+near-infrared+negative-index+metamaterials%5BTitle%5D)+AND+%22Phys.+Rev.+Lett%22%5BJournal%5D)">Experimental demonstration of near-infrared negative-index metamaterials.</a> Phys. Rev. Lett. 95, 137404(2005).</li>
<li>Linden, S., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Magnetic+response+of+metamaterials+at+100+terahertz%5BTitle%5D)+AND+%22Science%22%5BJournal%5D)">Magnetic response of metamaterials at 100 terahertz.</a> Science. 306, 1351-1353 (2004).</li>
<li>Landy, N. I., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Design%2C+theory%2C+and+measurement+of+a+polarization-insensitive+absorber+for+terahertz+imaging%5BTitle%5D)+AND+%22Phys.+Rev.+B%22%5BJournal%5D)">Design, theory, and measurement of a polarization-insensitive absorber for terahertz imaging.</a> Phys. Rev. B. 79, 125104-12 (2009).</li>
<li>Gokkavas, M., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Experimental+demonstration+of+a+left-handed+metamaterial+operating+at+100+GHz%5BTitle%5D)+AND+%22Phys.+Rev.+B%22%5BJournal%5D)">Experimental demonstration of a left-handed metamaterial operating at 100 GHz.</a> Phys. Rev. B. 73, 193103(2006).</li>
<li>Smith, D. R., Kroll, N. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Negative+refractive+index+in+left-handed+materials%5BTitle%5D)+AND+%22Phys.+Rev.+Lett%22%5BJournal%5D)">Negative refractive index in left-handed materials.</a> Phys. Rev. Lett. 85, 2933-2936 (2000).</li>
<li>Wiltshire, M. C. K., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Microstructured+magnetic+materials+for+RF+flux+guides+in+magnetic+resonance+imaging%5BTitle%5D)+AND+%22Science%22%5BJournal%5D)">Microstructured magnetic materials for RF flux guides in magnetic resonance imaging.</a> Science. 291, 849-851 (2001).</li>
<li>Pendry, J. B. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Negative+refraction+makes+a+perfect+lens%5BTitle%5D)+AND+%22Phys.+Rev.+Lett%22%5BJournal%5D)">Negative refraction makes a perfect lens.</a> Phys. Rev. Lett. 85, 3966-3969 (2000).</li>
<li>Kabashin, A. V., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Plasmonic+nanorod+metamaterials+for+biosensing%5BTitle%5D)+AND+%22Nat.+Mater%22%5BJournal%5D)">Plasmonic nanorod metamaterials for biosensing.</a> Nat. Mater. 8, 867-871 (2009).</li>
<li>Dolling, G., Enkrich, C., Wegener, M., Soukoulis, C. M., Linden, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Low-loss+negative-index+metamaterial+at+telecommunication+wavelengths%5BTitle%5D)+AND+%22Opt.+Lett%22%5BJournal%5D)">Low-loss negative-index metamaterial at telecommunication wavelengths.</a> Opt. Lett. 31, 1800-1802 (2006).</li>
<li>Schurig, D., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Metamaterial+electromagnetic+cloak+at+microwave+frequencies%5BTitle%5D)+AND+%22Science%22%5BJournal%5D)">Metamaterial electromagnetic cloak at microwave frequencies.</a> Science. 314, 977-980 (2006).</li>
<li>Chen, H. T., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Experimental+demonstration+of+frequency-agile+terahertz+metamaterials%5BTitle%5D)+AND+%22Nat.+Photonics%22%5BJournal%5D)">Experimental demonstration of frequency-agile terahertz metamaterials.</a> Nat. Photonics. 2, 295-298 (2008).</li>
<li>Ma, Y., Khalid, A., Saha, S. C., Grant, J. P., Cumming, D. R. S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((THz+band+pass+filter+on+plastic+substrates+and+its+application+on+biological+sensing%5BTitle%5D)+AND+%22IEEE+Photonics+Society+Winter+Topicals+Meeting+Series%22%5BJournal%5D)">THz band pass filter on plastic substrates and its application on biological sensing.</a> IEEE Photonics Society Winter Topicals Meeting Series. , 50-51 (2010).</li>
<li>Grant, J., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Polarization+insensitive+terahertz+metamaterial+absorber%5BTitle%5D)+AND+%22Opt.+Lett%22%5BJournal%5D)">Polarization insensitive terahertz metamaterial absorber.</a> Opt. Lett. 36, 1524-1526 (2011).</li>
<li>Ma, Y., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((A+terahertz+polarization+insensitive+dual+band+metamaterial+absorber%5BTitle%5D)+AND+%22Opt.+Lett%22%5BJournal%5D)">A terahertz polarization insensitive dual band metamaterial absorber.</a> Opt. Lett. 36, 945-947 (2011).</li>
<li>Grant, J., Ma, Y., Saha, S., Khalid, A., Cumming, D. R. S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Polarization+insensitive%2C+broadband+terahertz+metamaterial+absorber%5BTitle%5D)+AND+%22Opt.+Lett%22%5BJournal%5D)">Polarization insensitive, broadband terahertz metamaterial absorber.</a> Opt. Lett. 36, 3476-3478 (2011).</li>
<li>Tonouchi, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Cutting-edge+terahertz+technology%5BTitle%5D)+AND+%22Nat.+Photon%22%5BJournal%5D)">Cutting-edge terahertz technology.</a> Nat. Photon. 1, 97-105 (2007).</li>
<li>D. Schurig, J. J. M., Justice, B. J., Cummer, S. A., Pendry, J. B., Starr, A. F., Smith, D. R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Microwave+Cloaking+Realized%5BTitle%5D)+AND+%22Science%22%5BJournal%5D)">Microwave Cloaking Realized.</a> Science. 314, 889(2006).</li>
<li>Padilla, W. J., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Electrically+resonant+terahertz+metamaterials%3A+Theoretical+and+experimental+investigations%5BTitle%5D)+AND+%22Phys.+Rev.+B%22%5BJournal%5D)">Electrically resonant terahertz metamaterials: Theoretical and experimental investigations.</a> Phys. Rev. B. 75, 041102(2007).</li>
<li>Smith, D. R., Vier, D. C., Koschny, T., Soukoulis, C. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Electromagnetic+parameter+retrieval+from+inhomogeneous+metamaterials%5BTitle%5D)+AND+%22Phys.+Rev.+E%22%5BJournal%5D)">Electromagnetic parameter retrieval from inhomogeneous metamaterials.</a> Phys. Rev. E. 71, (2005).</li>
<li>Landy, N. I., Sajuyigbe, S., Mock, J. J., Smith, D. R., Padilla, W. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Perfect+metamaterial+absorber%5BTitle%5D)+AND+%22Phys.+Rev.+Lett%22%5BJournal%5D)">Perfect metamaterial absorber.</a> Phys. Rev. Lett. 100, 207402(2008).</li>
<li>Hao, J. M., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((High+performance+optical+absorber+based+on+a+plasmonic+metamaterial%5BTitle%5D)+AND+%22Appl.+Phys.+Lett%22%5BJournal%5D)">High performance optical absorber based on a plasmonic metamaterial.</a> Appl. Phys. Lett. 96, 251104(2010).</li>
<li>Chen, H. T. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Interference+theory+of+metamaterial+perfect+absorbers%5BTitle%5D)+AND+%22Opt.+Express%22%5BJournal%5D)">Interference theory of metamaterial perfect absorbers.</a> Opt. Express. 20, 7165-7172 (2012).</li>
<li>Lee, A. W. M., Hu, Q. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Real-time%2C+continuous-wave+terahertz+imaging+by+use+of+a+microbolometer+focal-plane+array%5BTitle%5D)+AND+%22Optics+Letters%22%5BJournal%5D)">Real-time, continuous-wave terahertz imaging by use of a microbolometer focal-plane array.</a> Optics Letters. 30, 2563-2565 (2005).</li>
<li>Thermo Nicolet Corporation. <a target="_blank" href="http://scholar.google.com/scholar?hl=en&safe=off&q=%22An+Introduction+to+Fourier+Transform+Infared+Spectroscopy%22">An Introduction to Fourier Transform Infared Spectroscopy</a>. , (2001).</li>
</ol>

No conflicts of interest declared.

This protocol describes the simulation, fabrication and characterization of THz metamaterial absorbers. It is essential such sub-wavelength structures are accurately simulated before any effort is committed to costly fabrication procedures. Lumerical FDTD simulations provide information on not only the MM absorption spectrum but also the location of the absorption, essential knowledge to aid placement of a transducer and obtain the maximum response. In addition the optimization algorithm in Lumerical can be implem...

This protocol describes the simulation, fabrication and characterization of single band and broadband THz MM absorbers. The device, shown in Figure 1, consists of a metal cross and a dielectric layer on top of a metal ground plane. The cross-shaped structure is an example of an electric ring resonator (ERR)20,21 and couples strongly to uniform electric fields, but negligibly to a magnetic field. By pairing the ERR with a ground plane, the magnetic component of the incident THz wave induces a current in the sections of the ERR that are parallel to the direction of the E-field. The electric and magnetic response can then be tuned independently and the impedance of the structure matched to free space by varying the geometry of the ERR and the distance between the two metallic elements. As shown in Figure 1(d), the symmetry of the structure results in a polarization insensitive absorption response.

<table><tbody><tr><td>Lumerical FDTD</td><td>Lumerical</td><td></td><td></td></tr><tr><td>Silicon wafer</td><td>IDB technologies</td><td></td><td>Single sided polished</td></tr><tr><td>Plassys 450 MEB evaporator</td><td>Plassys Bestek</td><td></td><td></td></tr><tr><td>VM651 Primer</td><td>Dupont</td><td></td><td></td></tr><tr><td>PI2545</td><td>Dupont</td><td></td><td></td></tr><tr><td>Methyl Isobutyl Ketone</td><td>Sigma-Aldrich</td><td></td><td></td></tr><tr><td>Isopropanol</td><td>Sigma-Aldrich</td><td></td><td></td></tr><tr><td>Plasmaprep5 barrel Asher</td><td>Gala Instrumente</td><td></td><td></td></tr><tr><td>VB6 UHR EWF electron beam writer</td><td>Vistec</td><td></td><td></td></tr><tr><td>Tanner L-Edit</td><td>Tanner Inc.</td><td></td><td></td></tr><tr><td>Layout Beamer</td><td>GenISys Inc.</td><td></td><td></td></tr><tr><td>Polymethyl methacrylate (PMMA)</td><td>Sigma-Aldrich</td><td>293261 Sigma-Aldrich</td><td></td></tr><tr><td>IFV 66v/s FTIR</td><td>Bruker</td><td></td><td></td></tr><tr><td>Pike 30spec reflection unit</td><td>Pike Technologies</td><td></td><td></td></tr><tr><td>Hg arc lamp</td><td>Bruker</td><td></td><td></td></tr><tr><td>Au mirror</td><td>Thor Labs</td><td>PF05-03-M01</td><td></td></tr><tr><td>Leica INM20 Optical Microscope</td><td>Leica microsystems</td><td></td><td></td></tr><tr><td>6 mm Mylar Beamsplitter</td><td>Bruker</td><td></td><td></td></tr></tbody></table>

simulation, fabrication and characterization of thz metamaterial absorbers

Simulation, Fabrication and Characterization of THz Metamaterial Absorbers

Metamaterials (MM), artificial materials engineered to have properties that may not be found in nature, have been widely explored since the first theoretical1 and experimental demonstration2 of their unique properties. MMs can provide a highly controllable electromagnetic response, and to date have been demonstrated in every technologically relevant spectral range including the optical3, near IR4, mid IR5 , THz6 , mm-wave7 , microwave8 and radio9 bands. Applications include perfect lenses10, sensors11, telecommunications12, invisibility cloaks13 and filters14,15. We have recently developed single band16, dual band17 and broadband18 THz metamaterial absorber devices capable of greater than 80% absorption at the resonance peak. The concept of a MM absorber is especially important at THz frequencies where it is difficult to find strong frequency selective THz absorbers19. In our MM absorber the THz radiation is absorbed in a thickness of ~ &lambda;/20, overcoming the thickness limitation of traditional quarter wavelength absorbers. MM absorbers naturally lend themselves to THz detection applications, such as thermal sensors, and if integrated with suitable THz sources (e.g. QCLs), could lead to compact, highly sensitive, low cost, real time THz imaging systems.

Figure 5(a) shows the experimentally obtained and simulated absorption spectra for a MM absorber with a 3.1 μm thick polyimide dielectric spacer. This MM structure has a repeat-period of 27 μm and dimensions K = 26 μm, L = 20 μm, M = 10 μm and N = 5 μm. Experimental measurements were also performed on samples with no ERR layer to confirm that absorption was a consequence of the MM structure and not of the dielectric. The 7.5 μm thick polyimide sample with no ERR structure has a maximum abso...

This protocol outlines the simulation, fabrication and characterization of THz metamaterial absorbers. Such absorbers, when coupled with an appropriate sensor, have applications in THz imaging and spectroscopy.

Metamaterials (MM),  artificial materials engineered to have properties that may not be found in  nature, have been widely explored since the first ...

The overall goal of this procedure is to simulate, fabricate, and characterize a terahertz metamaterial absorber structure. First, perform simulations to establish the optimum metamaterial absorber design. Then fabricate this optimized design.Next, evaluate the experimental performance of the absorber using Fourier transform infrared spectroscopy. The resulting single band, dual band and broadband ertz metamaterial absorber devices are capable of greater than 80%absorption at the resonance peak. And when coupled with an appropriate sensor, have applications in ertz imaging and spectroscopy.The technology that we're working on will enable us to make small, portable terahertz imaging systems, which will be handheld by working on Metamaterial technologies, which we hope to integrate with sensors such as barometers, we hope to able to achieve high speed, high sensitivity devices. The implications of this technique extend toward the rapid design simulation, fabrication and characterization of prototype terahertz Metamaterial Devices. Not only does this method demonstrate how to fabricate a telehealth metamaterial absorber can also be applied to the design and fabrication of other metamaterial devices and components such as filters, modulators, perfect lenses and invisibility cloaks.Follow the simulation section in the journal article protocol to design a metamaterial absorber with the desired absorption spectrum characteristics. Clean the silicon in sequential solutions of optic clear acetone and isopropanol. First immerse in the solvent at 50 degrees Celsius for 10 minutes, and then subject to ultrasonic agitation.Next, evaporate a metal bilayer of titanium and gold onto the silicon using an electron beam evaporator. Note that the metal thickness must be greater than the skin depth at the desired operating frequency. After cleaning in solvents as described earlier, pipette VM 651 primer onto the sample and leave it to relax for 20 seconds.Then spin the sample at 4, 000 RPM for five seconds and bake on a contact hot plate at 120 degrees Celsius for 60 seconds. Pipette the polyamide onto the sample and leave it to relax for 20 seconds. Remember to allow the polyamide to reach room temperature after removal from the freezer.This is in order to maintain the filling properties over time. Spin the sample first at 500 RPM for five seconds with an acceleration of 100 RPMs to the negative one and ramp to 6, 000 RPM with an acceleration of 500 RPMs to the negative one for 60 seconds. Then bake the sample on a contact hot plate at 140 degrees Celsius for five minutes.For a thicker polyamide film, spin multiple layers or reduce the final spin speed. Cure the polyamide on a contact hot plate at 220 degrees Celsius for 10 minutes. Next, deposit, 15%2010 PMMA onto the sample spin at 5, 000 RPM for 60 seconds.Remove any excess resist that is crept onto the backside of the sample using acetone. Then bake in a convection oven at 180 degrees Celsius for 30 minutes. Once the sample has cooled to room temperature deposit 4%2041 PMMA onto the sample, spin and bake as shown earlier.Now, design the job file in Tanner L.Edit fracture into polygons by layout Beamer. And finally, submit to the beam writer using the Java based bell software. Write the desired job using a dose of 450 micro curies centimeter squared on the VB six electron beam rider.Next, develop the sample in a solution of one-to-one MIBK to IPA at 23 degrees Celsius for 60 seconds. Rinse in isopropanol. Then inspect for pattern fidelity on an optical microscope.If features are poorly resolved, strip the resistant optical acetone and isopropanol and start again. Des scum the sample with oxygen using a gala, plasma prep barrel lasher then evaporate 20 nanometers of titanium and 150 nanometers of gold using an electron beam evaporator. Insert the sample into a beaker of warm acetone and heat to 50 degrees Celsius in a water bath for four hours using a pipette.Wash the sample liberally with the warm acetone. Now inspect the sample by eye for metal lifting off from the areas where the PMMA was present. If the liftoff is progressing slowly, place the beaker in the ultrasonic water bath for two minutes.Finally, inspect the sample under the optical microscope. Turn on the nitrogen supply to the Fourier, transform infrared spectrometer. Press the FIR button on the front of the spectrometer control unit to turn on the mercury arc lamp.Insert the six micron multilayer beam splitter into the appropriate slot in the interferometer unit. Next, vent the sample compartment of the spectrometer and insert the pike 30 degree reflection unit. Place the seven millimeter aperture on top of the reflection unit aperture, and on top of this, put a gold mirror.Now evacuate the sample compartment to a pressure of five millibar. Start the opus software and load the configuration file for taking measurements in the 30 to 300 inverse centimeters range. And sure the LED on the front of the detector compartment is flashing green indicating that the scanner is operating.Check that the shape of the interferogram is as expected. Run 100 background scans to obtain the background spectrum. Vent the sample compartment, remove the mirror and place the sample face down onto the aperture.Ensure the center of the sample is in the middle of the aperture, and then evacuate the sample compartment. Next, run 1000 sample scans to obtain the sample spectrum. The software automatically compares the sample spectrum with the background and the true reflection spectrum of the sample is displayed on the screen.These figures show absorption spectra for metamaterial absorbers with differing dielectric spacer thicknesses. The 7.5 micron thick polyamide sample with no electric ring resonator structure has a maximum absorption of 5%across the frequency range of interest. The experimental data shows a resonance peak at 2.12 terahertz of 77%absorption magnitude.This result is in excellent agreement with the simulated absorption maximum of 81%at 2.12 terahertz. Here, data are generated from MM absorbers with the same ERR geometry for different polyamide thicknesses ranging from one to 7.5 microns, and for an absorber where the dielectric is three microns of silicon dioxide. As the polyamide thickness increases from one micron to 3.1 microns, the peak absorption increases.But at polyamide thicknesses greater than 3.1 microns, there is a slight reduction in the peak absorption value. A distinct red shift of 0.25 terahertz is observed as the polyamide thickness increases from one micron to 7.5 microns. The effective permittivity and permeability can be extracted from the simulated data via inversion of the S parameters as shown here for the simulated MM absorber with a 3.1 micron thick polyamide spacer.The real parts of the optical Constance cross close to zero, A condition required for zero reflection at the frequency of maximum absorption. There is a peak of the imaginary component of the permeability implying high absorption.Erl. FDTD can also be used to establish the location of the absorption within the MM structure.These plots clearly demonstrate that the majority of the energy is dissipated as omic loss in the ERR layer and as dielectric loss in the first 500 nanometers of polyamide. Below this layer, several applications such as terahertz spectroscopy require sensors that exhibit broadband terahertz absorption. We have developed two strategies to realize such broadband absorption.The first strategy stacks alternating layers of metallic RR and dielectric layers on top of a continuous ground plane in different layers, crosses of differing lengths, support several resonant modes closely positioned together in the absorption spectrum. By tuning the dielectric thickness, the multi-layer structure can be impedance matched to free space at each resonant frequency and broadband absorption obtained. Then a standard electron beam registration process is used to align the RS on top of one another in a second.Strategy.Four Rs incorporated into a four color super pixel are designed onto a single dielectric layer. Such a device is much simpler to fabricate than the multi-layer absorber. This plot shows absorption spectrum and simulated data for a multi-layer mm absorber of indicated dimensions.The one layer structure has a single resonance peak at 5.42 terahertz, where 78%of the EM radiation is absorbed. In contrast, the three layer device has three closely positioned resonant peaks with a wide frequency band from 4.08 terahertz to 5.94 terahertz, where the absorption is greater than 60%To understand the origin of the spectral characteristics of the simulated absorption distributions in the XZ plane of the three resonances are plotted. These distributions clearly reveal that each ERR contributes to the broadband absorption Once mastered.This technique can be done in less than four eight hours if performed Properly. While attempting this procedure is important to remember to be methodical and consistent when performing the fabrication steps. After watching this film, you'll have a very good overview of the micro nano fabrication technologies that we use that enable us to make a range of ertz devices and components including Metamaterial absorbers.

simulation-fabrication-characterization-thz-metamaterial

Research

JoVE Journal

Engineering

Metamaterials at terahertz frequencies offer unique opportunities, but are challenging to fabricate in bulk. We adapt the fabrication procedure for microstructured polymer optical fibers to inexpensively fabricate metamaterials potentially on an industrial scale. We produce polymethylmethacrylate fibers containing ~10 μm diameter indium wires separated by ~100 μm, which exhibit a terahertz plasmonic response.

Fabricating Metamaterials Using the Fiber Drawing Method

The procedure for implementing a refractive index sensor for terahertz frequencies based on a grooved parallel-plate waveguide geometry is described here.  The method yields a measurement of the refractive index of a small volume of liquid through monitoring of the shift in the resonant frequency of the waveguide...

Terahertz Microfluidic Sensing Using a Parallel-plate Waveguide Sensor

We describe methods for the design, fabrication, and experimental characterization of plasmonic photoconductive emitters, which offer two orders of magnitude higher terahertz power levels compared to conventional photoconductive emitters.

Design, Fabrication, and Experimental Characterization of Plasmonic Photoconductive Terahertz Emitters

Superconducting microwave resonators are of interest for detection of light, quantum computing applications and materials characterization. This work presents a detailed procedure for fabrication and characterization of superconducting microwave resonator scattering parameters.

Fabrication and Characterization of Superconducting Resonators

A protocol for the design and fabrication of a novel nanopillar-based split ring resonator (SRR) is presented.

Fabrication of Nanopillar-Based Split Ring Resonators for Displacement Current Mediated Resonances in Terahertz Metamaterials

A protocol for a fixed-fixed beam design using a laser Doppler vibrometer (LDV), including the measurement of frequency tuning, modification of tuning capability, and avoidance of device failure and stiction, is presented. The superiority of the LDV method over the network analyzer is demonstrated due to its higher mode capability.

Design and Characterization Methodology for Efficient Wide Range Tunable MEMS Filters

Additively manufactured polymers have been widely used for producing elastic metamaterials. The viscoelastic behavior of these polymers at ultrasonic frequencies remains, however, poorly studied. This study reports a protocol to estimate the viscoelastic properties of 3D-printed polymers and show how to use them to analyze the metamaterial dynamics.

Characterizing Dissipative Elastic Metamaterials Produced by Additive Manufacturing

Use of photonic crystal slow light waveguides and cavities has been widely adopted by the photonics community in many differing applications. Therefore fabrication and characterization of these devices are of great interest. This paper outlines our fabrication technique and two optical characterization methods, namely: interferometric (waveguides) and resonant scattering (cavities).

Fabrication And Characterization Of Photonic Crystal Slow Light Waveguides And Cavities

We develop and characterize a disordered polymer optical fiber that uses transverse Anderson localization as a novel waveguiding mechanism. This microstructured fiber can transport a small localized beam with a radius that is comparable to the beam radius of conventional optical fibers.

Fabrication and Characterization of Disordered Polymer Optical Fibers for Transverse Anderson Localization of Light

Parametric optomechanical excitations have recently been experimentally demonstrated in microfluidic optomechanical resonators by means of optical radiation pressure and stimulated Brillouin scattering. This paper describes the fabrication of these microfluidic resonators along with methodologies for generating and verifying optomechanical oscillations.

Fabrication and Testing of Microfluidic Optomechanical Oscillators

Learn to simulate, fabricate and characterize terahertz metamaterial absorbers using Fourier transform infrared spectroscopy. This method enables development of devices achieving over 80% absorption for terahertz imaging applications.

Simulation, Fabrication and Characterization of THz Metamaterial Absorbers

Explore More Videos