Uploaded: 2015-12-21T13:00:00.000+00:00
Duration: 8 min 58 s
Description: Learn seedless growth of bismuth nanowire arrays via vacuum thermal evaporation for scalable nanotechnology synthesis. This catalyst-free method produces high-purity single crystalline nanowires efficiently.

ai_agent_IP

ai_agent

maintenance

instantTrialDurationMinutes

isBiopharma

enableNewMyJoveSectionDesign

educationFeatures

seoMetaApi

ai_copilot_institution_blacklist

ai_chat_institution_blacklist

freeAccessWindow

ssoRoleCapture

scheduledMaintenanceBanner

joveLabsFeatures

disable_autoplay_for_bots

extended_trial_duration

5 minutes

Research is carried out at the Center for Functional Nanomaterials, Brookhaven National Laboratory, which is supported by the U.S. Department of Energy, Office of Basic Energy Sciences, under Contract No. DE-SC0012704.

Caution: Please consult all relevant material safety data sheets (MSDS) before use. Nanomaterials may have additional hazards compared to their bulk counterpart. Please use all appropriate safety practices when handling nanomaterial-covered substrates, including the use of engineering controls (fume hood) and personal protective equipment (safety glasses, gloves, lab coat, full length pants, closed-toe shoes).
1. Preparatory Work
<ol>
	<li>Preparation of vapor deposition system
	<ol>
		<li>Vent the deposition chamber to atmosphere pressure and open the chamber. The venting is done by pressing the &#34;Start PC Venting&#34; button on the control software interface, which automatically starts a sequence that vent the chamber to atmosphere pressure. On reaching the atmosphere pressure open the chamber by pulling the front accessing door.</li>
		<li>Mount a tungsten evaporation boat (alumina coated) between a pair of thermal evaporation electrodes. Place 1 g bismuth pellets into the evaporation boat.</li>
		<li>Mount a vanadium sputtering target to the magnetron sputtering source. Refer to step 1.1.4) for deposition system that is not equipped with a sputtering source.</li>
		<li>(optional, for deposition system that is not equipped with a sputtering source) Mount a tungsten evaporation boat between a pair of thermal evaporation electrodes. Place 0.5 g vanadium slugs into the evaporation boat.</li>
		<li>Connect the mini-banana connectors (two for heating/cooling power and two for temperature probe) of the closed loop temperature controller to the electrical feedthrough of the deposition system.</li>
	</ol>
	</li>
	<li>Preparation of growth substrates 
	Note: The formation of bismuth nanowires is insensitive to the growth substrate of choice. Similar results have been obtained from glass slide, silicon wafer, or sheet metal. It is recommended by the authors that the substrate shall be cleaned immediately prior to the vapor deposition process, in order to achieve a consistent adhesion of the vanadium underlayer. Various substrate cleaning techniques, including plasma cleaning and wet chemical cleaning, can be applied and lead to similar results.
	<ol>
		<li>Cleaning the growth substrates by oxygen plasma
		<ol>
			<li>Place the growth substrates into a plasma cleaner and pump the chamber, by pressing the &#34;VAC ON&#34; button, to its base pressure of 10 mTorr.</li>
			<li>Open the oxygen gas valve and introduce oxygen gas to the chamber by pressing the &#34;GAS ON&#34; button on the front panel and adjust the flow rate by pressing the &#34;INCR&#34; and &#34;DECR&#34; buttons for gas flow rate control to maintain a chamber pressure of about 100 mTorr.</li>
			<li>Set the plasma power at 20 W by pressing the &#34;INCR&#34; and &#34;DECR&#34; buttons for power control and ignite the plasma by pressing the &#34;RF ON&#34; button.</li>
			<li>Wait for 5 min before turning off the plasma by pressing the &#34;RF ON&#34; button. Vent the chamber by pressing the &#34;BLEED&#34; button and retrieve the substrates.</li>
		</ol>
		</li>
		<li>Cleaning the growth substrates by wet chemical method
		<ol>
			<li>Immerse the growth substrates in acetone contained in a beaker. Place the beaker into an ultrasonicator and sonicate for 2 min at the maximum power.</li>
			<li>Remove the substrates from the beaker and rinse them with a stream of absolute alcohol from a wash bottle for 30 sec.</li>
			<li>Dry the substrates in a stream of nitrogen gas.</li>
		</ol>
		</li>
	</ol>
	</li>
	<li>Substrate loading and deposition system pumping
	<ol>
		<li>Mount the substrate temperature control assembly to the substrate holder.</li>
		<li>Use spring clips to mount the growth substrates on top of the Peltier cooler/heater assembly.</li>
		<li>Mount the fully assembled substrate holder into the vapor deposition chamber, with the substrates facing the deposition sources. Connect the electrical feedthroughs to the Peltier cooler/heater assembly.</li>
		<li>Close the substrate shutter to avoid unintentional deposition to the substrate.</li>
		<li>Start pumping down the deposition chamber. The pumping is done by pressing the &#34;Start PC Pumping&#34; button on the control software interface, which automatically starts a sequence that pump the chamber to its base pressure.</li>
	</ol>
	</li>
</ol>
2. Growth of Bismuth Nanowires&#160;
Note: The experiment is not moving to the next step until the base pressure of the deposition chamber has reached 2 &#215; 10-6 Torr or below.
<ol>
	<li>The deposition of vanadium underlayer 
	Note: The best experimental reproducibility is achieved when the vanadium underlayer is deposited by the magnetron sputtering method. In the absence of a sputtering source, high reproducibility can also be still achieved by depositing the vanadium underlayer using thermal evaporation method, provided that the deposition system has a low base pressure (&#8804; 5 &#215; 10-7 Torr). Refer to step 3.1.2 for the details.
	<ol>
		<li>Vanadium deposition with a magnetron sputtering source.
		<ol>
			<li>Start argon flow in the sputtering source. Set flow rate to 40 sccm.</li>
			<li>Adjust the turbomolecular pump&#39;s revolution rate for a chamber pressure of 2.5 mTorr.</li>
			<li>While the chamber is gradually reaching its steady state pressure, set the thickness calibration factors to the QCM. For vanadium, the density is 5.96 g/cm3 and the Z-factor is 0.530.</li>
			<li>Turn on the DC sputtering source and set the power at 200-250 W. For the deposition system operated by the authors, the deposition rate is about 0.4 A/sec at this power. Without opening the substrate shutter, keep the source running for 2 min. 
			NOTE: Through this step the native oxide on the vanadium source is removed, exposing fresh vanadium surface.</li>
			<li>Open the substrate shutter to start vanadium deposition. In the meantime, reset the accumulated thickness of the QCM to zero.</li>
			<li>Continue deposition until an apparent thickness of 20 nm is accumulated, per QCM reading. Close the substrate shutter.</li>
			<li>Gradually decrease the sputter power to zero. Turn the source off.</li>
			<li>Shut off the argon flow. Return the turbomolecular pump to its full power.</li>
		</ol>
		</li>
		<li>(optional, for deposition system that is not equipped with a sputtering source) Vanadium deposition with a thermal evaporation source.
		<ol>
			<li>Due to the high melting point of vanadium (1,910 &#176;C) and its readiness to oxidation, it is recommended that its thermal evaporation to be conducted at a base pressure of 5 &#215; 10-7 Torr or lower.</li>
			<li>Set the thickness calibration factors to the QCM. For vanadium, the density is 5.96 g/cm3 and the Z-factor is 0.530.</li>
			<li>Turn on the thermal evaporation power supply to the vanadium source. Slowly increase heating power to the tungsten boat until the vanadium slugs melt.</li>
			<li>With the substrate shutter kept closed, slowly increase heating power until a deposition rate of 2 &#197;/sec is achieved, per QCM reading. Open the substrate shutter to start vanadium deposition. In the meantime, reset the accumulated thickness of the QCM to zero.</li>
			<li>Continue deposition until an apparent thickness of 50 nm is accumulated. Close the substrate shutter.</li>
			<li>Gradually decrease the thermal evaporation power to zero. Turn the source off.</li>
		</ol>
		</li>
	</ol>
	</li>
	<li>The deposition of bismuth nanowires
	<ol>
		<li>For bismuth deposition at temperature above or below RT, set the desired value to the temperature controller. Wait until the desired temperature is reached.</li>
		<li>Set the thickness calibration factors to the QCM. For bismuth, the density is 9.78 g/cm3 and the Z-factor is 0.790.</li>
		<li>Turn on the thermal evaporation power supply to the bismuth source. Slowly increase heating power to the tungsten boat until the deposition rate of 2 &#197;/sec is achieved, per QCM reading.</li>
		<li>Open the substrate shutter to start bismuth deposition. In the meantime, reset the accumulated thickness of the QCM to zero.</li>
		<li>Continue deposition until an apparent thickness of 50 nm is accumulated. Close the substrate shutter.</li>
		<li>Gradually decrease the thermal evaporation power to zero. Turn the source off.</li>
		<li>Turn off power supply to the thermal electric cooler/heater.</li>
		<li>Vent the deposition chamber to atmosphere pressure and open the chamber. Retrieve the substrate holder and collect the bismuth nanowires covered substrates.</li>
	</ol>
	</li>
</ol>

<ol><li>Hu, J. T., Odom, T. W., Lieber, C. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Chemistry+and+physics+in+one+dimension%3A+Synthesis+and+properties+of+nanowires+and+nanotubes%5BTitle%5D)+AND+%22Acc.+Chem.+Res%22%5BJournal%5D)">Chemistry and physics in one dimension: Synthesis and properties of nanowires and nanotubes.</a> Acc. Chem. Res. 32, 435-445 (1999).</li>
<li>Akimov, A. V., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Generation+of+single+optical+plasmons+in+metallic+nanowires+coupled+to+quantum+dots%5BTitle%5D)+AND+%22Nature%22%5BJournal%5D)">Generation of single optical plasmons in metallic nanowires coupled to quantum dots.</a> Nature. 450, 402-406 (2007).</li>
<li>Thurn-Albrecht, T., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Ultrahigh-density+nanowire+arrays+grown+in+self-assembled+diblock+copolymer+templates%5BTitle%5D)+AND+%22Science%22%5BJournal%5D)">Ultrahigh-density nanowire arrays grown in self-assembled diblock copolymer templates.</a> Science. 290, 2126-2129 (2000).</li>
<li>Xia, Y. N., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((One-dimensional+nanostructures%3A+Synthesis%2C+characterization%2C+and+applications%5BTitle%5D)+AND+%22Adv.+Mater%22%5BJournal%5D)">One-dimensional nanostructures: Synthesis, characterization, and applications.</a> Adv. Mater. 15, 353-389 (2003).</li>
<li>Gudiksen, M. S., Lauhon, L. J., Wang, J., Smith, D. C., Lieber, C. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Growth+of+nanowire+superlattice+structures+for+nanoscale+photonics+and+electronics%5BTitle%5D)+AND+%22Nature%22%5BJournal%5D)">Growth of nanowire superlattice structures for nanoscale photonics and electronics.</a> Nature. 415, 617-620 (2002).</li>
<li>Yang, P. D., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Controlled+growth+of+ZnO+nanowires+and+their+optical+properties%5BTitle%5D)+AND+%22Adv.+Funct.+Mater%22%5BJournal%5D)">Controlled growth of ZnO nanowires and their optical properties.</a> Adv. Funct. Mater. 12, 323-331 (2002).</li>
<li>Allen, J. E., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((High-resolution+detection+of+Au+catalyst+atoms+in+Si+nanowires%5BTitle%5D)+AND+%22Nature+Nanotech%22%5BJournal%5D)">High-resolution detection of Au catalyst atoms in Si nanowires.</a> Nature Nanotech. 3, 168-173 (2008).</li>
<li>Lin, Y. M., Sun, X. Z., Dresselhaus, M. S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Theoretical+investigation+of+thermoelectric+transport+properties+of+cylindrical+Bi+nanowires%5BTitle%5D)+AND+%22Phys.+Rev.+B%22%5BJournal%5D)">Theoretical investigation of thermoelectric transport properties of cylindrical Bi nanowires.</a> Phys. Rev. B. 62, 4610-4623 (2000).</li>
<li>Isaacson, R. T., Williams, G. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Alfv%C3%A9n-Wave+propagation+in+solid-state+plasmas.+III.+Quantum+oscillations+of+the+Fermi+surface+of+bismuth%5BTitle%5D)+AND+%22Phys+Rev%22%5BJournal%5D)">Alfvén-Wave propagation in solid-state plasmas. III. Quantum oscillations of the Fermi surface of bismuth.</a> Phys Rev. 185, 682-688 (1969).</li>
<li>Sandomirskii, V. B. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Quantum+size+effect+in+a+semimetal+film%5BTitle%5D)+AND+%22Sov.+Phys.+JETP%22%5BJournal%5D)">Quantum size effect in a semimetal film.</a> Sov. Phys. JETP. 25, 101-106 (1967).</li>
<li>Huber, T. E., Nikolaeva, A., Gitsu, D., Konopko, L., Graf, M. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Quantum+confinement+and+surface-state+effects+in+bismuth+nanowires%5BTitle%5D)+AND+%22Physica+E%22%5BJournal%5D)">Quantum confinement and surface-state effects in bismuth nanowires.</a> Physica E. 37, 194-199 (2007).</li>
<li>Black, M. R., Lin, Y. M., Cronin, S. B., Rabin, O., Dresselhaus, M. S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Infrared+absorption+in+bismuth+nanowires+resulting+from+quantum+confinement%5BTitle%5D)+AND+%22Phys.+Rev.+B%22%5BJournal%5D)">Infrared absorption in bismuth nanowires resulting from quantum confinement.</a> Phys. Rev. B. 65, 2921-2930 (2002).</li>
<li>Hofmann, P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((The+surfaces+of+bismuth%3A+Structural+and+electronic+properties%5BTitle%5D)+AND+%22Prog.+Surf.+Sci%22%5BJournal%5D)">The surfaces of bismuth: Structural and electronic properties.</a> Prog. Surf. Sci. 81, 191-245 (2006).</li>
<li>Huber, T. E., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Confinement+effects+and+surface-induced+charge+carriers+in+Bi+quantum+wires%5BTitle%5D)+AND+%22Appl+Phys+Lett%22%5BJournal%5D)">Confinement effects and surface-induced charge carriers in Bi quantum wires.</a> Appl Phys Lett. 84, 1326-1328 (2004).</li>
<li>Huber, T. E., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Surface+state+band+mobility+and+thermopower+in+semiconducting+bismuth+nanowires%5BTitle%5D)+AND+%22Phys.+Rev.+B%22%5BJournal%5D)">Surface state band mobility and thermopower in semiconducting bismuth nanowires.</a> Phys. Rev. B. 83, 235414-23 (2011).</li>
<li>Dresselhaus, M. S., et al. 23, 129-140 (2003).</li>
<li>Cheng, Y. -T., Weiner, A. M., Wong, C. A., Balogh, M. P., Lukitsch, M. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Stress-induced+growth+of+bismuth+nanowires%5BTitle%5D)+AND+%22Appl+Phys+Lett%22%5BJournal%5D)">Stress-induced growth of bismuth nanowires.</a> Appl Phys Lett. 81, 3248-3250 (2002).</li>
<li>Volobuev, V. V., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((The+mechanism+of+Bi+nanowire+growth+from+Bi%2FCo+immiscible+composite+thin+films%5BTitle%5D)+AND+%22J.+Nanosci.+Nanotech%22%5BJournal%5D)">The mechanism of Bi nanowire growth from Bi/Co immiscible composite thin films.</a> J. Nanosci. Nanotech. 12, 8624-8629 (2012).</li>
<li>Shim, W., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((On-film+formation+of+Bi+nanowires+with+extraordinary+electron+mobility%5BTitle%5D)+AND+%22Nano+Lett%22%5BJournal%5D)">On-film formation of Bi nanowires with extraordinary electron mobility.</a> Nano Lett. 9, 18-22 (2009).</li>
<li>Berglund, S. P., Rettie, A. J. E., Hoang, S., Mullins, C. B. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Incorporation+of+Mo+and+W+into+nanostructured+BiVO4+films+for+efficient+photoelectrochemical+water+oxidation%5BTitle%5D)+AND+%22Phys.+Chem.+Chem.+Phys%22%5BJournal%5D)">Incorporation of Mo and W into nanostructured BiVO4 films for efficient photoelectrochemical water oxidation.</a> Phys. Chem. Chem. Phys. 14, 7065-7075 (2012).</li>
<li>Liu, M., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Surface-Energy+Induced+Formation+of+Single+Crystalline+Bismuth+Nanowires+over+Vanadium+Thin+Film+at+Room+Temperature%5BTitle%5D)+AND+%22Nano+Lett%22%5BJournal%5D)">Surface-Energy Induced Formation of Single Crystalline Bismuth Nanowires over Vanadium Thin Film at Room Temperature.</a> Nano Lett. 14, 5630-5635 (2014).</li>
</ol>

Authors have nothing to disclose.

The growth of bismuth nanowires is to be conducted in a physical vapor deposition system with at least two deposition sources, one for bismuth and another for vanadium. It is recommended that one of the sources is a magnetron sputtering source, for the deposition of vanadium. High vacuum is achieved by a turbomolecular pumps backed by a dry scroll pump. The vapor deposition system is equipped with a calibrated quartz crystal microbalance (QCM) for in situ thickness monitoring. The vapor deposition system has ele...

Nanowires confine the transport of charge carriers and other quasiparticles, such as photons and plasmons in one dimension. Accordingly, nanowires usually exhibit novel electrical, magnetic, optical and chemical properties, which grant them nearly infinite potential for applications in micro/nano electronics, photonics, biomedical, environmental and energy-related technologies.1,2 During the past two decades, numerous top-down and bottom-up approaches have been developed to synthesis a broad range of high quality metal or semiconductor nanowires at laboratory scale.3-6 Despite of these developments, each approach relies on certain unique properties of the final product for its success. For instance, the popular vapor-liquid-solid (VLS) method is better fit for the semiconductor materials that have higher melting points and form eutectic alloy with corresponding catalytic &#34;seeds&#34;.7 As a result, the synthesis of a nanowire material of particular interest may not be covered by existing techniques.
As a semimetal with small indirect band overlap (-38 meV at 0 K) and unusually light charge carriers, bismuth is one such example. The material behaves radically different at reduced dimension when compared to its bulk, as quantum confinement could turn bismuth nanowires or thin films into a narrow band gap semiconductor.8-12 In the meantime, the surface of bismuth forms a quasi-two-dimensional metal that is significantly more metallic than its bulk.13,14 It was shown that the surface of bismuth achieves an electron mobility of 2&#215;104 cm2 V-1 sec-1 and contributes strongly to its thermoelectric power in nanowire form.15 As such, there are significant interests on studying bismuth nanowires for electronic and in particular thermoelectric applications.12-16 However, due to bismuth&#39;s very low melting point (544 K) and readiness for oxidation, it remains a challenge to synthesis high quality and single crystalline bismuth nanowires using traditional vapor phase or solution phase techniques.
Previously, it has been reported by a few groups that single crystalline bismuth nanowires grow at low yield during vacuum deposition of bismuth thin film, which is attributed to the release of stress built into the film.17-20 Most recently, we discovered a novel technique that is based on the thermal evaporation of bismuth under high vacuum and leads to the scalable formation of single crystalline bismuth nanowires at high yield.21 Comparing to previously reported methods, the most unique feature of this technique is that the growth substrate is freshly coated with a thin layer of nanoporous vanadium prior to bismuth deposition. During the latter&#39;s thermal evaporation, bismuth vapor infiltrates into the nanoporous structure of the vanadium film and condenses there as nanodomains. Since vanadium is not wetted by condensed bismuth, the infiltrated domains are subsequently expulsed from the vanadium matrix to release their surface energy. It is the continuous expulsion of the bismuth nanodomains that forms the vertical bismuth nanowires. Since the bismuth domains are only 1-2 nm in diameters, they are subject to significant melting point suppression, which makes them nearly molten at RT. As a result, the nanowires growth proceeds with the substrate held at RT. On the other hand, as the migration of the bismuth domains is thermally activated, the length and width of the nanowires can be tuned over a wide range by simply controlling the temperature of the growth substrate. This detailed video protocol is intended to help new practitioners in the field avoid various common problems associated with physical vapor deposition of thin films in a high vacuum, oxygen-free environment.

<table><tbody><tr><td>Bismuth</td><td>Sigma-Aldrich</td><td>556130</td><td>Granular, 99.999%</td></tr><tr><td>Vanadium Slug</td><td>Alfa Aesar</td><td>42829</td><td>3.175&amp;nbsp;mm (0.125&amp;nbsp;in) dia x 6.35&amp;nbsp;mm (0.25&amp;nbsp;in) length, 99.8%</td></tr><tr><td>Vanadium Sputtering Target</td><td>Kurt J. Lesker</td><td>EJTVXXX253A2</td><td>3.00&quot; Dia. x 0.125&quot; Thick, 99.5%</td></tr><tr><td>Acetone</td><td>Sigma-Aldrich</td><td>179124</td><td>&gt;99.5%</td></tr><tr><td>Ethanol</td><td>Alfa Aesar</td><td>33361</td><td>Anhydrous</td></tr><tr><td>Silicon Wafer</td><td>University Wafers</td><td></td><td>300 microns in thickness, (100) orientation</td></tr><tr><td>Silver Filled Epoxy</td><td>Circuit Works</td><td>CW2400</td><td>Two part conductive epoxy resin</td></tr><tr><td>Tungsten Boat, Alumina Coated</td><td>R. D. Mathis</td><td>S9B-AO-W</td><td>For bismuth thermal evaporation</td></tr><tr><td>Tungsten Boat</td><td>R. D. Mathis</td><td>S4-.015W</td><td>For vanadium thermal evaporation</td></tr><tr><td>RIE Plasma</td><td>Nordson March</td><td>CS-1701</td><td></td></tr><tr><td>PVD 75 Vapor Deposition Platform</td><td>Kurt J. Lesker</td><td>PEDP75FTCLT001</td><td>Equipped with three thermal evaporation source and one DC magnetron sputtering source</td></tr><tr><td>Thermoelectric Temperature Controller</td><td>LairdTech</td><td>MTTC-1410</td><td></td></tr><tr><td>PT1000 RGD</td><td>LairdTech</td><td>340912-01</td><td>Temperature sensor for MTTC-1410</td></tr><tr><td>Thermoelectric Module</td><td>LairdTech</td><td>56910-502</td><td></td></tr><tr><td>Ultrasonicator</td><td>Crest Ultrasonics</td><td>Tru-Sweep 175</td><td></td></tr></tbody></table>

seedless growth of bismuth nanowire array via vacuum thermal evaporation

Seedless Growth of Bismuth Nanowire Array via Vacuum Thermal Evaporation

Here a seedless and template-free technique is demonstrated to scalably grow bismuth nanowires, through thermal evaporation in high vacuum at RT. Conventionally reserved for the fabrication of metal thin films, thermal evaporation deposits bismuth into an array of vertical single crystalline nanowires over a flat thin film of vanadium held at RT, which is freshly deposited by magnetron sputtering or thermal evaporation. By controlling the temperature of the growth substrate the length and width of the nanowires can be tuned over a wide range. Responsible for this novel technique is a previously unknown nanowire growth mechanism that roots in the mild porosity of the vanadium thin film. Infiltrated into the vanadium pores, the bismuth domains (~ 1 nm) carry excessive surface energy that suppresses their melting point and continuously expels them out of the vanadium matrix to form nanowires. This discovery demonstrates the feasibility of scalable vapor phase synthesis of high purity nanomaterials without using any catalysts.

The cross-sectional SEM images of vanadium underlayers formed by magnetron sputtering and thermal evaporation methods are presented in Figure 2. Scanning electron microscopy (SEM) images are presented for bismuth nanowires formed at different substrate temperatures (Figure 3). The crystal structure of the bismuth nanowires is determined through transmission electron microscopy (TEM), selective area electron diffraction (SAED), and X-ray diffraction (XRD) studies (Figure 4</strong...

A protocol for seedless and high yield growth of bismuth nanowire arrays through vacuum thermal evaporation technique is presented.

Here a seedless and template-free technique is demonstrated to scalably grow bismuth nanowires, through thermal evaporation in high vacuum at RT. ...

The overall goal of this experimental procedure is to grow single crystalline bismuth nanowires in a scalable manner through thermal evaporation in a high vacuum. This method can be used to synthesize high quality business nanos in high yields. The material has been of great interest in the field of semi electricity studies.The main advantage of this technique is that it involves no catalysts or seeds, and that the synthetic procedure is taken place in high vacuum so that the nano wire is being formed as of hyper purity. This method provides insight into how nanoscale porosity induces spontaneous business nano wire growth, but it should be also be applicable to other systems with a low melting point, such as Indio and tin. To begin vent the deposition chamber to atmospheric pressure and open the chamber.The venting is done by pressing the start PC venting button on the control software interface, which automatically starts a sequence that vents the chamber to atmospheric pressure. On reaching the atmospheric pressure. Open the chamber by pulling the front accessing door.Then mount a tungsten evaporation boat between a pair of thermal evaporation electrodes. Place one gram of bismuth pellets into the evaporation boat mount a vanadium sputtering target to the magnetron sputtering source. Next, connect the mini banana connectors of the closed loop temperature controller to the electrical feed through of the deposition system.To clean the growth substrates by oxygen plasma, place the growth substrates into a plasma cleaner and pump the chamber by pressing on the vac on button to its base pressure of 10 millitorr. Open the oxygen gas valve and introduce oxygen gas to the chamber by pressing the gas on button on the front panel. Adjust the flow rate by pressing the INCR and DECR buttons for gas flow rate control to maintain a chamber pressure of about 100 millitorr.Next, set the plasma power at 20 watts by pressing the INCR and DECR buttons for power control and ignite the plasma by pressing the RF on button. Wait for five minutes before turning off the plasma by pressing the RF on button. Then vent the chamber by pressing the bleed button before retrieving the substrates to load substrate.First, mount the substrate temperature control assembly to the substrate holder. Use spring clips to mount the growth substrates on top of the peltier cooler heater assembly. Then mount the fully assembled substrate holder into the vapor deposition chamber.With the substrates facing the deposition sources, connect the electrical feed throughs to the peltier cooler heater assembly. Close the substrate shutter to avoid unintentional deposition to the substrate. Next, start pumping down the deposition chamber.The pumping is done by pressing the start PC pumping button on the control software interface, which automatically starts a sequence that pumps the chamber to its base pressure to deposit vanadium with a magnetron sputtering source Start argon flow in the sputtering source. Set the flow rate to between 40 and 50 standard cubic centimeters per minute. Adjust the turbomolecular pumps revolution rate for a chamber pressure of 2.5 to three millitorr while the chamber is gradually reaching its steady state pressure.Set the thickness calibration factors to the quartz crystal micro balance or QCM for vanadium. The density is 5.96 grams per cubic centimeter, and the Z factor is 0.530. Turn on the DC sputtering source and set the power at 200 to 250 watts without opening the substrate shutter.Keep the source running for two minutes. Open the substrate shutter to start vanadium deposition. In the meantime, reset the accumulated thickness of the QCM to zero.Continue deposition until an apparent thickness of 20 nanometers is accumulated per QCM reading. Then close the substrate shutter, gradually decrease the sputter power to zero. Then turn the source off, shut off the argon flow.Finally return the turbomolecular pump to its full power. It's very important that the substrate temperature are maintained stably and precisely as this, and the lines of the nano virus are strongly tailored by the temperature For bismuth deposition at temperatures above or below room temperature, set the desired value to the temperature controller. Wait until the desired temperature is reached.Set the thickness calibration factors to the QCM for bismuth. The density is 9.78 grams per cubic centimeter, and the Z factor is 0.790. Turn on the thermal evaporation power supply to the bismuth source.Then slowly increase heating power to the tungsten boat until the deposition rate of two angstroms per second is achieved. Per QCM reading, reset the accumulated thickness of the QCM to zero. In the meantime, open the substrate shutter to start bismuth deposition.Continue deposition until an apparent thickness of 50 nanometers is accumulated. Then close the substrate shutter. Gradually decrease the thermal evaporation power to zero.Turn the source off. Turn off the power supply to the thermal electric cooler heater. Vent the deposition chamber to atmospheric pressure and open the chamber.Finally, retrieve the substrate holder and collect the bismuth nano wire covered substrates. The cross-sectional scanning electron microscopy or SEM images of vanadium underlay formed by magnetron, sputtering and thermal evaporation methods are presented here.Here. SEM images are presented for bismuth nanowires formed at different substrate temperatures.The crystal structure of the bismuth nanowires is determined through transmission electron microscopy, selective area electron diffraction, and x-ray diffraction studies. Elemental analysis by energy dispersive x-ray spectroscopy indicates that the bismuth nanowires are not alloyed with the vanadium underlayer. After watching this video, you should have a good understanding of how to sly grow.Single crystalline business nano wears through thermal evaporation in the high vacuum While attempting this procedure, it is important to control the substrate temperature precisely as it can significantly affect the dimension of the nano wears. Low base pressure is also critical to avoid the oxidation of devastated materials after its development. This technique paved the way for the searchers in the field of phy synthesis of nanostructures to utilize surface energy as a driven force for high quality and hyper nanostructures.

seedless-growth-bismuth-nanowire-array-via-vacuum-thermal

Research

JoVE Journal

Engineering

This article describes a simple method to fabricate vertically aligned carbon nanotube arrays by CVD and to subsequently tune their wetting properties by exposing them to vacuum annealing or dry oxidation treatment.

Dry Oxidation and Vacuum Annealing Treatments for Tuning the Wetting Properties of Carbon Nanotube Arrays

We describe the device fabrication and measurement protocol for carbon nanotube based high frequency biosensors. The high frequency sensing technique mitigates the fundamental ionic (Debye) screening effect and allows nanotube biosensor to be operated in high ionic strength solutions where conventional electronic biosensors fail. Our technology provides a unique platform for point-of-care (POC) electronic biosensors operating in physiologically relevant conditions.

Fabrication of Carbon Nanotube High-Frequency Nanoelectronic Biosensor for Sensing in High Ionic Strength Solutions

We report a simple method for fabricating an ultrahigh density array of vertically ordered small-molecular organic nanowires. This method allows for synthesis of complex heterostructured hybrid nanowire geometries, which can be inexpensively grown on arbitrary substrates. These structures have potential applications in organic electronics, optoelectronics, chemical sensing, photovoltaics and spintronics.

Ultrahigh Density Array of Vertically Aligned Small-molecular Organic Nanowires on Arbitrary Substrates

A technique was developed that removes Ni/Au contact metal films from their substrate to allow for the examination and characterization of the contact/substrate and contact/NW interfaces of single GaN nanowire devices.

Analysis of Contact Interfaces for Single GaN Nanowire Devices

A detailed procedure for surface doping of Silicon interfaces is provided. The ultra-shallow surface doping is demonstrated by using phosphorus containing monolayers and rapid annealing process. The method can be used for doping of macroscopic area surfaces as well as nanostructures.

Monolayer Contact Doping of Silicon Surfaces and Nanowires Using Organophosphorus Compounds

Various procedures are outlined to prepare atomically defined templates for epitaxial growth of complex oxide thin films. Chemical treatments of single crystalline SrTiO3 (001) and DyScO3 (110) substrates were performed to obtain atomically smooth, single terminated surfaces. Ca2 Nb3 O10- nanosheets were used to create atomically defined templates on arbitrary substrates.

Atomically Defined Templates for Epitaxial Growth of Complex Oxide Thin Films

Tin sulfide (SnS) is a candidate material for Earth-abundant, non-toxic solar cells. Here, we demonstrate the fabrication procedure of the SnS solar cells employing atomic layer deposition, which yields 4.36% certified power conversion efficiency, and thermal evaporation which yields 3.88%.

Making Record-efficiency SnS Solar Cells by Thermal Evaporation and Atomic Layer Deposition

A method for the growth of low temperature vertically-aligned carbon nanotubes, and the subsequent fabrication of vertical interconnect electrical test structures using semiconductor fabrication is presented.

Fabrication of Low Temperature Carbon Nanotube Vertical Interconnects Compatible with Semiconductor Technology

We report a solution-based method to synthesize substrate-bound Au nanowires. By tuning the molecular ligands used during the synthesis, the Au nanowires can be grown from various substrates with different surface properties. Au nanowire-based nanostructures can also be synthesized by adjusting the reaction parameters.

Synthesis of Substrate-Bound Au Nanowires Via an Active Surface Growth Mechanism

The article aims to introduce a standard and reliable fabrication procedure for the development of future low dimensional nanoelectronics.

A Standard and Reliable Method to Fabricate Two-Dimensional Nanoelectronics

Here we describe methods for microfabricating vertically aligned carbon nanofibers (VACNFs), transferring VACNFs to flexible substrates, and applying VACNFs on both rigid and flexible substrates to plants for biomolecule and dye delivery.

Using Vertically Aligned Carbon Nanofiber Arrays on Rigid or Flexible Substrates for Delivery of Biomolecules and Dyes to Plants

Learn seedless growth of bismuth nanowire arrays via vacuum thermal evaporation for scalable nanotechnology synthesis. This catalyst-free method produces high-purity single crystalline nanowires efficiently.

Seedless Growth of Bismuth Nanowire Array via Vacuum Thermal Evaporation

Explore More Videos