Name: Colloidal Synthesis of Nanopatch Antennas for Applications in Plasmonics and Nanophotonics (Video) | JoVE Journal
Uploaded: 2016-05-28T15:00:00.000+00:00
Duration: 9 min 12 s
Description: Learn colloidal synthesis of silver nanocubes for fabricating nanopatch antennas with sub-10 nm gaps. This method enables enhanced fluorescence and controlled light-matter interactions in nanophotonic applications.

ai_agent_IP

ai_agent

maintenance

instantTrialDurationMinutes

isBiopharma

enableNewMyJoveSectionDesign

educationFeatures

seoMetaApi

ai_copilot_institution_blacklist

ai_chat_institution_blacklist

freeAccessWindow

ssoRoleCapture

scheduledMaintenanceBanner

joveLabsFeatures

disable_autoplay_for_bots

extended_trial_duration

5 minutes

This work was supported by the Air Force Office of Scientific Research Young Investigator Research Program (AFOSR, Grant. No. FA9550-15-1-0301).

Caution: Several chemicals (such as concentrated nitric acid (15.698 M HNO3) and hydrochloric acid (6 M HCl)) used in these procedures are hazardous. Proper gloves, eye protection and other safety equipment must be used. Please refer to the materials safety datasheets (MSDS) of all chemicals before use.
1. Nanocube Synthesis
<ol>
	<li>Preparation of reagents 
	Note: Ethylene glycol (EG) must be anhydrous. Close the EG container's cap whenever it is not used to prevent water absorption. Silver trifluoroacetate (AgC2F3O2) is very sensitive to light therefore the AgC2F3O2 solution is prepared in the last step.
	<ol>
		<li>Prepare 1.3 mM sodium hydrosulfide hydrate (NaSH) solution by dissolving 1 mg of NaSH in 13.5 ml of EG.</li>
		<li>Prepare 20 mg/ml poly vinylpyrrolidone (PVP) solution by dissolving 0.1 g of PVP in 5 ml of EG.</li>
		<li>Prepare 3 mM hydrochloric solution by mixing 2.5 µl of 6.0 M liquid HCl solution with 4.9975 ml of EG.</li>
		<li>Prepare AgC2F3O2 solution by dissolving 0.1 g of AgC2F3O2 in 0.8 ml of EG.</li>
	</ol>
	</li>
	<li>Equipment setup
	<ol>
		<li>Clean the round-bottom flask (RBF) and its cap with concentrated (70%, 15.698 M) nitric acid HNO3. Fill the RBF with HNO3 and put the cap on for 30 min. Ensure the cap touches the acid.</li>
		<li>After HNO3 acid, clean the RBF and cap again with clean de-ionized (DI) water. Use clean nitrogen gas to dry the RBF and cap afterwards. The RBF and its cap must be clean and dry.</li>
		<li>Clean a magnetic stirring bar by immersing it in HNO3 for 30 min. After HNO3, clean it again with DI water and dry it with clean nitrogen gas.</li>
		<li>Prepare a heating bath. Place a silicone fluid bath (shown in Figure 1A) on top of a stirring hotplate with a well-controlled temperature. Use an external thermometer to monitor the fluid bath temperature. Set the temperature to 150 °C and the stirring speed to 260 rpm.</li>
		<li>Mount the RBF with a clamp as shown in Figure 1B. Place the magnetic stirring bar (prepared in step 1.2.3) into the RBF.</li>
	</ol>
	</li>
	<li>Synthesis procedure
	<ol>
		<li>Dip the RBF into the heating bath (approximately 10 mm deep into the liquid; see Figures 1A-1B).</li>
		<li>Use a micropipette to place 10 ml of EG solution into the RBF. Put the cap on the RBF and wait for 20 min. The purpose of this step is to clean the RBF again, this time with EG.</li>
		<li>After 20 min, remove the cap and then lift the RBF out of the heating bath, pour the 10 ml of EG into a disposal container. Note: The EG solution is hot (150 °C) and it is recommended to take the entire clamp out (Figure 1B). Make sure that the magnetic stirring bar (see step 1.2.5) does not fall off.</li>
		<li>Put the RBF back into the heating bath (see step 1.3.1).</li>
		<li>Use a micropipette to place 5 ml of EG into the RBF and put the cap on.</li>
		<li>Wait for 5 min.</li>
		<li>Take the RBF's cap off, use a micropipette to place 60 µl of NaSH (as prepared in step 1.1.1 above) into the RBF. Put the cap back on.</li>
		<li>Wait for 2 min.</li>
		<li>Take the RBR's cap off, use a micropipette to place 500 µl of the HCl solution (as prepared in step 1.1.3 above) into the RBF.</li>
		<li>Immediately after the previous step, use a micropipette to place 1.25 ml of the PVP solution (as prepared in step 1.1.2 above) into the RBF. Put the cap back on.</li>
		<li>Wait for 2 min.</li>
		<li>Take the RBF's cap off, use a micropipette to place 400 µl of the AgC2F3O2 solution (as prepared in step 1.1.4 above) into the RBF. Put the cap back on.</li>
		<li>Wait for 2.5 hr. Ag nanocubes are forming during this step. If possible, during this time, reduce the room light to a minimum.</li>
		<li>After 2.5 hr, turn the heater off but leave the stirring on to avoid the fluid burning on the bottom. Use the clamp (shown in Figure 1B) to raise the RBF above the heating bath. Remove the cap.</li>
		<li>Remove the RBF from the heating bath such that it will cool off faster. After ~20 min, add 5 ml of acetone into the RBF. Vortex it in order to mix the solutions well. In the end, the total volume of the solution is 12 ml. See Figure 2A.</li>
		<li>Use a micropipette and transfer the final solution to eight smaller 1.5 ml plastic tubes.</li>
		<li>Centrifuge these eight tubes at a speed of 5150 x g for 10 min. As a result, all the Ag nanocubes will be at the bottom of the tubes. Use a micropipette to remove the top supernatant, leaving ~100 µl at the bottom of each tube.</li>
		<li>Fill 1 ml of DI water into each of these tubes (obtained from step 1.3.17). Vortex and sonicate (5 min) the tubes. Nanocubes are now suspended in mainly DI water.</li>
		<li>Centrifuge again the eight tubes prepared in step 1.3.18 at 5,150 x g for 5 min. All the Ag nanocubes will be at the bottom of the tubes. Use a micropipette to remove the top supernatant, leaving around 100 µl at the bottom of each tube.</li>
		<li>Fill 1 ml of DI water into each of the tubes obtained from step 1.3.19. Vortex and sonicate the tubes. Nanocubes are now suspended in DI water. The final nanocube solution obtained from this synthesis is shown in Figure 2B as an example.</li>
	</ol>
	</li>
</ol>
2. Gold Film Evaporation
Note: An electron-beam evaporator was used to deposit gold (Au) films onto purchased cleanroom cleaned slides, with chromium (Cr) acting as an adhesion layer. The evaporation process takes place inside a vacuum chamber, enabling the molecules to evaporate freely in the chamber and then sublimate on the substrate. The operation procedure is:
<ol>
	<li>Vent the chamber, by pressing "Auto Vent".</li>
	<li>Open chamber door and load substrates in the dome.</li>
	<li>Close the door and pump down by pressing "Auto Pump", it takes approximately 1 hr for the chamber to pump down until the pressure is below 5×10-6 Torr.</li>
	<li>Edit the recipe. Layer#1: Cr, thickness: 5 nm, deposition rate: 1 Å/sec; layer#2: Au, thickness: 50 nm, deposition rate: 2 Å/sec.</li>
	<li>Upon reaching the desired vacuum level, the deposition process of the first metal will automatically start by pressing "Auto Run". 
	Note: During the deposition, the high voltage module is turned on and the voltage is 10 kV. Gun rotation module is turned on, and fixture rotation is 20 rpm. After the first layer finishes, the system will automatically move to the pocket location of the second metal and start deposition.</li>
	<li>After the entire process is complete, press "Auto Vent" to vent the chamber and take the sample out. 
	Note: The total thickness of the Au film was 50 nm and the surface roughness was measured using an atomic force microscope (AFM) yielding a typical root mean square (RMS) of 0.7 nm. No special treatment was performed of the purchased glass substrates before Au film deposition.</li>
</ol>
3. Deposition of PE Layers
<ol>
	<li>Preparation of reagents
	<ol>
		<li>For the sodium chloride (NaCl) solution, mix 29 g of NaCl powder with 500 ml of DI water.</li>
		<li>For the polystyrene sulfonate (PSS) solution, mix 29 g of NaCl powder with 500 ml of DI water then add 1.5 ml of the PSS stock solution.</li>
		<li>For the poly(allylamine) hydrochloride (PAH) solution, mix 29 g of NaCl powder with 500 ml of DI water then add 132 mg of PAH.</li>
	</ol>
	</li>
	<li>Layer-by-layer deposition 
	Note: PAH is slightly positively charged while PSS is slightly negatively charged. As the Au film fabricated in Section 2 above is slightly negatively charged, a PAH layer will be deposited first. The steps below will demonstrate in details how to deposit five PE layers: PAH/PSS/PAH/PSS/PAH.
	<ol>
		<li>First, deposit a PAH layer by immersing the gold film (fabricated in Section 2 above) into a PAH solution (prepared in step 3.1.3) for 5 min. This results in a PAH layer on top of the Au film with a thickness of ~1 nm.</li>
		<li>After 5 min, rinse the Au film + 1 PAH layer with clean DI water.</li>
		<li>Immerse the Au film + 1 PAH layer into a NaCl solution (prepared in step 3.1.1) for 1 min.</li>
		<li>Immerse the Au film + 1 PAH layer (after step 3.2.3) into a PSS solution for 5 min. This results in a PSS layer with a thickness of ~1 nm on top of the PAH layer.</li>
		<li>After 5 min, rinse the Au film + 1 PAH layer +1 PSS layer with clean DI water.</li>
		<li>Immerse the Au film + 1 PAH layer + 1 PSS layer into the NaCl solution for 1 min.</li>
		<li>Immerse the Au film + 1 PAH layer + 1 PSS layer into the PAH solution for 5 min. This results in another PAH layer with a thickness of ~1 nm on top of the PSS layer (prepared in step 3.2.4 above).</li>
		<li>After 5 min, rinse the Au film + 1 PAH +1 PSS + 1 PAH layers with clean DI water.</li>
		<li>Immerse the Au film + 1 PAH + 1 PSS + 1 PAH layers into the NaCl solution for 1 min.</li>
		<li>Immerse the Au film + 1 PAH + 1 PSS + 1 PAH layers into the PAH solution for 5 min. This results in a second PSS layer with a thickness of ~1 nm on top of the PAH layer (which was prepared in step 3.2.7 above).</li>
		<li>After 5 min, rinse the Au film + 1 PAH +1 PSS + 1 PAH + 1 PSS layers with clean DI water.</li>
		<li>Immerse the Au film + 1 PAH + 1 PSS + 1 PAH +1 PSS layers into the NaCl solution for 1 min.</li>
		<li>Immerse the Au film + 1 PAH + 1 PSS + 1 PAH +1 PSS layers into the PAH solution for 5 min. This results in another PAH layer with a thickness of ~1 nm on top of the PSS layer (which was prepared in step 3.2.10 above).</li>
		<li>Finally, rinse the Au film + 1 PAH + 1 PSS + 1 PAH +1 PSS + 1 PAH with DI water and dry the sample using clean nitrogen gas. 
		Note: The total thickness of the five PE layers was measured in air using a spectroscopic ellipsometer at incidence angles of 65°, 70°, and 75°, yielding a thickness of 5.0 ± 0.1 nm.</li>
	</ol>
	</li>
</ol>
4. Deposition of Cy5 Dye Molecules
<ol>
	<li>Prepare a 25 µM Cy5 solution with DI water as the solvent.</li>
	<li>Expose the surface of the sample (which has a series of five PE layers, as described in Section 3 above) to 100 µl of a 25 µM Cy5 solution for 10 min. First drop cast 100 µl of the Cy5 solution (prepared in step 4.1) onto the sample surface and then place a cover slip on top of the solution drop. Cy5 molecules will incorporate into the top PE layers uniformly.</li>
	<li>After 10 min, rinse the sample with DI water and dry it with clean nitrogen gas.</li>
</ol>
5. Deposition of Nanocubes to Form Nanopatch Antennas (NPAs)
<ol>
	<li>Dilute the nanocube solution obtained from Section 1 by a factor of 1/100 using DI water to enable the optical study of individual NPAs.</li>
	<li>Use a micropipette to place a drop of 20 µl of diluted nanocube solution (prepared in step 5.1) onto a clean cover slip. Place the sample (prepared in Section 4) in contact with the cover slip for 2 min. This results in the Ag nanocubes to be immobilized on the top terminal PAH layer because the nanocubes synthesized here are negatively charged and the top PAH layer is positively charged.</li>
	<li>After 2 min, rinse the sample with DI water and dry with clean nitrogen gas. 
	Note: Steps 5.1 - 5.3 describe a procedure to prepare a sample for optical studies of single NPAs using a dark field microscope (dark field scattering). To prepare a sample for reflectivity measurements, a similar procedure is applied except that in step 5.1 the original nanocube solution is diluted by a factor of 1/10 instead of 1/100.</li>
</ol>
6. Optical Measurements
Note: A custom built optical bright-/dark-field microscope is used in these measurements. The NPAs are illuminated by a white light source through a long working distance bright-/dark-field objective. The reflected/scattered light from the NPAs is collected by the same objective. A pinhole aperture (50 μm diameter) is used at an image plane to select signal from an individual nanoantenna. A digital camera is used to capture a color image. A spectrometer and a charge coupled device (CCD) camera are used to acquire spectral data. For fluorescence measurements, a 633 nm continuous wave HeNe laser is used for excitation and the signal was spectrally filtered by a long pass filter.
<ol>
	<li>Dark field scattering spectrum of single NPAs
	<ol>
		<li>Under white light illumination, identify single NPAs on the sample that was prepared in Section 5. Under white light illumination, individual NPAs appear as bright, red or pink colored dots as shown in Figure 4C.</li>
		<li>Align a single NPA with the pinhole aperture using a translation stage. Ensure that the dark field scattering image of the NPA is still observed after the pinhole aperture.</li>
		<li>Acquire a spectrum of the scattered light from the NPA using the spectrometer and CCD camera with a 1 sec integration time. Because the aperture area (50 µm) is much bigger than the physical size of the NPA (~ 75 nm) the spectrum contains scattered light from the NPA in addition to signal from the area surrounding the NPA.</li>
		<li>Move the sample to an area without any NPAs and acquire another spectrum with a 1 s integration time. This spectrum represents scattered light from the background.</li>
		<li>Remove the sample with NPAs and place a certified reflectance standard sample in the setup. Acquire a spectrum of the scattered light with a 0.1 sec integration time in order to normalize the signal from the NPA.</li>
		<li>Close the pinhole aperture and acquire a spectrum with a 0.1 sec integration time without any input signal. This spectrum represents the CCD dark counts.</li>
		<li>Calculate the final scattering spectrum of an NPA as follows: 
		<img alt="NPA scattering equation; describes light intensity ratio in scattering experiments; spectroscopic analysis." src="/files/ftp_upload/53876/53876eq1.jpg" data-altupdatedat="1788235205000" data-alt="Equation 1"> 
		where INPA+background, Ibackground, Iwhite light, ICCD dark are the scattering spectra measured by steps 6.1.3, 6.1.4, 6.1.5 and 6.1.6, respectively.</li>
		<li>Extract the plasmon resonance of the NPA by calculating the centroid of the scattering resonance peak.16</li>
	</ol>
	</li>
	<li>Fluorescence enhancement of Cy5 molecules by single NPAs
	<ol>
		<li>Under white light illumination, identify single NPAs from the sample prepared in Section 5. In dark field, individual NPAs appear as bright, red or pink colored dots as shown in Figure 4C.</li>
		<li>Align a single NPA with the pinhole aperture using a translation stage. Ensure that the dark field scattering image of the NPA is detected by the camera placed after the pinhole aperture.</li>
		<li>Turn off the white light illumination and turn on the 633 nm continuous wave HeNe laser used for excitation.</li>
		<li>Place a 633 nm long pass laser filter in the optical path right before the entrance to the spectrometer in order to block any scattered laser light.</li>
		<li>Acquire a fluorescence spectrum of the emission from the Cy5 molecules using a 1 sec integration time. Because the aperture area (50 µm) is much larger than the physical size of the NPA (~ 75 nm) this spectrum contains emission from both molecules embedded in the NPA as well as molecules surrounding the NPA.</li>
		<li>Move the sample to an area without any NPAs and acquire another spectrum with a 1 sec integration time. This spectrum represents the emission from molecules in the background, without any NPAs.</li>
		<li>Prepare a separate sample, which will be used as a control sample, following the procedure in Sections 3 and 4 where Cy5 molecules are incorporated with PE layers on top of a glass slide (without a Au film and Ag nanocubes).</li>
		<li>Acquire a fluorescence spectrum of the emission from Cy5 molecules on the control sample prepared in the previous step using a 10 sec integration time.</li>
		<li>Determine the fluorescence enhancement factor by using the fluorescence spectra measured in steps 6.2.5, 6.2.6 and 6.2.8, taking into account the CCD dark counts, normalization by unit area and acquisition times.12,14</li>
	</ol>
	</li>
</ol>

<ol><li>Fan, J. A., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Self-Assembled+Plasmonic+Nanoparticle+Clusters%5BTitle%5D)+AND+%22Science%22%5BJournal%5D)">Self-Assembled Plasmonic Nanoparticle Clusters.</a> Science. 328 (5982), 1135-1138 (2010).</li>
<li>Zhang, Q., Li, W., Wen, L. -P., Chen, J., Xia, Y. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Facile+Synthesis+of+Ag+Nanocubes+of+30+to+70+in+Edge+Length+with+CF3COOAg+as+a+Precursor%5BTitle%5D)+AND+%22Chem.+Eur.+J%22%5BJournal%5D)">Facile Synthesis of Ag Nanocubes of 30 to 70 in Edge Length with CF3COOAg as a Precursor.</a> Chem. Eur. J. 16 (33), 10234-10239 (2010).</li>
<li>Sun, Y., Xia, Y. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Shape-Controlled+Synthesis+of+Gold+and+Silver+Nanoparticles%5BTitle%5D)+AND+%22Science%22%5BJournal%5D)">Shape-Controlled Synthesis of Gold and Silver Nanoparticles.</a> Science. 298 (5601), 2176-2179 (2002).</li>
<li>Xia, Y., Halas, N. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Shape-Controlled+Synthesis+and+Surface+Plasmonic+Properties+of+Metallic+Nanostructures%5BTitle%5D)+AND+%22MRS+Bull%22%5BJournal%5D)">Shape-Controlled Synthesis and Surface Plasmonic Properties of Metallic Nanostructures.</a> MRS Bull. 30 (05), 338-348 (2005).</li>
<li>Ciraci, C., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Probing+the+Ultimate+Limits+of+Plasmonic+Enhancement%5BTitle%5D)+AND+%22Science%22%5BJournal%5D)">Probing the Ultimate Limits of Plasmonic Enhancement.</a> Science. 337 (6098), 1072-1074 (2012).</li>
<li>Chandran, S. P., Chaudhary, M., Pasricha, R., Ahmad, A., Sastry, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Synthesis+of+Gold+Nanotriangles+and+Silver+Nanoparticles+Using+Aloevera+Plant+Extract%5BTitle%5D)+AND+%22Biotechnol.+Prog%22%5BJournal%5D)">Synthesis of Gold Nanotriangles and Silver Nanoparticles Using Aloevera Plant Extract.</a> Biotechnol. Prog. 22 (2), 577-583 (2006).</li>
<li>Perez-Juste, J., Pastoriza-Santos, I., Liz-Marzán, L. M., Mulvaney, P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Gold+nanorods%3A+Synthesis%2C+characterization+and+applications%5BTitle%5D)+AND+%22Coord.+Chem.+Rev%22%5BJournal%5D)">Gold nanorods: Synthesis, characterization and applications.</a> Coord. Chem. Rev. 249 (17-18), 1870-1901 (2005).</li>
<li>Nikoobakht, B., El-Sayed, M. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Preparation+and+Growth+Mechanism+of+Gold+Nanorods+%28NRs%29+Using+Seed-Mediated+Growth+Method%5BTitle%5D)+AND+%22Chem.+Mater%22%5BJournal%5D)">Preparation and Growth Mechanism of Gold Nanorods (NRs) Using Seed-Mediated Growth Method.</a> Chem. Mater. 15 (10), 1957-1962 (2003).</li>
<li>Rycenga, M., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Controlling+the+Synthesis+and+Assembly+of+Silver+Nanostructures+for+Plasmonic+Applications%5BTitle%5D)+AND+%22Chem.+Rev%22%5BJournal%5D)">Controlling the Synthesis and Assembly of Silver Nanostructures for Plasmonic Applications.</a> Chem. Rev. 111 (6), 3669-3712 (2011).</li>
<li>Cortie, M. B., McDonagh, A. M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Synthesis+and+Optical+Properties+of+Hybrid+and+Alloy+Plasmonic+Nanoparticles%5BTitle%5D)+AND+%22Chem.+Rev%22%5BJournal%5D)">Synthesis and Optical Properties of Hybrid and Alloy Plasmonic Nanoparticles.</a> Chem. Rev. 111 (6), 3713-3735 (2011).</li>
<li>Halas, N. J., Lal, S., Chang, W. -S., Link, S., Nordlander, P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Plasmons+in+Strongly+Coupled+Metallic+Nanostructures%5BTitle%5D)+AND+%22Chem.+Rev%22%5BJournal%5D)">Plasmons in Strongly Coupled Metallic Nanostructures.</a> Chem. Rev. 111 (6), 3913-3961 (2011).</li>
<li>Rose, A., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Control+of+Radiative+Processes+Using+Tunable+Plasmonic+Nanopatch+Antennas%5BTitle%5D)+AND+%22Nano+Lett%22%5BJournal%5D)">Control of Radiative Processes Using Tunable Plasmonic Nanopatch Antennas.</a> Nano Lett. 14 (8), 4797-4802 (2014).</li>
<li>Akselrod, G. M., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Probing+the+mechanisms+of+large+Purcell+enhancement+in+plasmonic+nanoantennas%5BTitle%5D)+AND+%22Nature+Photon%22%5BJournal%5D)">Probing the mechanisms of large Purcell enhancement in plasmonic nanoantennas.</a> Nature Photon. 8 (11), 835-840 (2014).</li>
<li>Hoang, T. B., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Ultrafast+spontaneous+emission+source+using+plasmonic+nanoantennas%5BTitle%5D)+AND+%22Nat.+Commun%22%5BJournal%5D)">Ultrafast spontaneous emission source using plasmonic nanoantennas.</a> Nat. Commun. 6, (2015).</li>
<li>Akselrod, G. M., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Leveraging+Nanocavity+Harmonics+for+Control+of+Optical+Processes+in+2D+Semiconductors%5BTitle%5D)+AND+%22Nano+Lett%22%5BJournal%5D)">Leveraging Nanocavity Harmonics for Control of Optical Processes in 2D Semiconductors.</a> Nano Lett. 15 (5), 3578-3584 (2015).</li>
<li>Mock, J. J., Hill, R. T., Tsai, Y. -J., Chilkoti, A., Smith, D. R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Probing+Dynamically+Tunable+Localized+Surface+Plasmon+Resonances+of+Film-Coupled+Nanoparticles+by+Evanescent+Wave+Excitation%5BTitle%5D)+AND+%22Nano+Lett%22%5BJournal%5D)">Probing Dynamically Tunable Localized Surface Plasmon Resonances of Film-Coupled Nanoparticles by Evanescent Wave Excitation.</a> Nano Lett. 12 (4), 1757-1764 (2012).</li>
<li>Skrabalak, S. E., Au, L., Li, X., Xia, Y. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Facile+synthesis+of+Ag+nanocubes+and+Au+nanocages%5BTitle%5D)+AND+%22Nat.+Protocols%22%5BJournal%5D)">Facile synthesis of Ag nanocubes and Au nanocages.</a> Nat. Protocols. 2 (9), 2182-2190 (2007).</li>
<li>Im, S. H., Lee, Y. T., Wiley, B., Xia, Y. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Large-Scale+Synthesis+of+Silver+Nanocubes%3A+The+Role+of+HCl+in+Promoting+Cube+Perfection+and+Monodispersity%5BTitle%5D)+AND+%22Angew.+Chem.+Int.+Ed%22%5BJournal%5D)">Large-Scale Synthesis of Silver Nanocubes: The Role of HCl in Promoting Cube Perfection and Monodispersity.</a> Angew. Chem. Int. Ed. 44 (14), 2154-2157 (2005).</li>
<li>Moreau, A., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Controlled-reflectance+surfaces+with+film-coupled+colloidal+nanoantennas%5BTitle%5D)+AND+%22Nature%22%5BJournal%5D)">Controlled-reflectance surfaces with film-coupled colloidal nanoantennas.</a> Nature. 492 (7427), 86-89 (2012).</li>
<li>Lassiter, J. B., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Plasmonic+Waveguide+Modes+of+Film-Coupled+Metallic+Nanocubes%5BTitle%5D)+AND+%22Nano+Lett%22%5BJournal%5D)">Plasmonic Waveguide Modes of Film-Coupled Metallic Nanocubes.</a> Nano Lett. 13 (12), 5866-5872 (2013).</li>
</ol>

The authors declare that they have no competing financial interests.

Silver nanocubes were chemically synthesized using reaction conditions similar to previously reported syntheses.2,12,17-20 This synthesis enables the fabrication of nanocubes with side lengths ranging from 50 to 100 nm. For example, a typical heating time of 2.5 hr will result in nanocubes with side lengths of ~75 nm. A longer synthesis time (&#62; 3 hr) will lead to larger nanoparticles, however, this may also result in different shapes such as truncated nanocubes or octahedrons. The final solution was centrifuged and re-suspended in deionized water, and may be stored for at least one month in a fridge at 4 &#176;C without any noticeable changes in the scattering spectra of the plasmon resonances.12
The size and shape of the Ag nanocubes from the process presented in the above protocol are very sensitive to the cleaning of the RBF, its cap and the stirring bar as well as the quality of the EG solution. Nanoparticles with different shapes such as rounded or elongated nanoparticles is a sign that there is likely an issue with one of these steps in the synthesis. It is therefore advised that steps 1.1.1-1.1.4 and 1.2.1-1.2.2 are critically important.
In Figure 4b the scattering spectrum collected from a single nanopatch antenna is shown which exhibits a strong plasmon resonance at 650 nm. Such a resonance indicates an excellent mode confinement in the gap region between the Ag nanocube and Au film made possible by high-quality nanocubes. Additionally, to obtain such a spectrum, it is also required that the sample is clean, the spacer layers (PE layers) have a uniform thickness and that the underlying Au film is smooth. The strong plasmon resonance is further confirmed by the data presented in Figure 4c where individual nanopatch antennas can be observed in the dark field image and in Figure 4d where large fluorescence enhancement is observed of Cy5 molecules located in the gap region. It should also be noted that the Ag nanocubes oxidize over time despite the PVP coating when exposed to air and thus it is recommended that optical measurements should be performed on the day the sample is prepared or within 1 to 3 days. To minimize oxidation, it is recommended that the nanopatch antenna samples be stored in vacuum or nitrogen gas.
The method presented in this paper enables the fabrication of Ag nanocubes and plasmonic nanopatch antennas with well-controlled dimensions utilizing colloidal synthesis and a layer-by-layer dip-coating process. Compared with other techniques such as optical or electron beam lithography, the technique presented here offers the potential for low cost and large-scale production while producing a narrow size distribution of nanoparticles.
The plasmonic nanopatch antennas presented in this paper also hold great promise for new nanomaterials by design exhibiting unique properties which may not exist in their macroscopic counterparts. In particular, these nanoantennas have shown record-high fluorescence enhancement of embedded dye molecules exceeding 30,000;12 spontaneous emission rate enhancements of 1,000; ultrafast spontaneous emission and high quantum yield.13,14 Additionally, it has been shown that emitters coupled to these nanopatch antennas exhibit highly directional emission which is critical for applications where coupling to an external detector or single mode fiber is required. Future applications of the nanoscale patch antennas may range from ultrafast optoelectronic devices, such as light emitting diodes, to high efficiency photodetectors and photovoltaic devices, sensing and quantum information processing technologies.12-14

In recent years, colloidal synthesis of nanoparticles and the assembly of these into advanced structures have attracted great interests both in research and industrial developments.1-4 Colloidal synthesis of nanoparticles have several advantages over lithographically fabricated nanostructures including superior size homogeneity, low cost and the possibility of large-scale, parallel production.
Metal nanoparticles such as silver (Ag) and gold (Au) can support localized surface plasmon polaritons and have the ability to confine light in a volume much smaller than the diffraction limit.1,3-5 The resulting high field intensity creates an enhanced local density of states enabling light-matter interactions to be tailored at the nanoscale. Recent efforts have demonstrated procedures to synthesize Ag and Au nanoparticles in a wide range of sizes and shapes, including triangles,4,6 cages,3,4 and rods4,7,8 in addition to the nanocubes discussed here. Nanostructures composed of several Ag or Au nanocomponents have also been fabricated demonstrating tailored properties.1,9-11
Here, we demonstrate a procedure to synthesize Ag nanocubes and more importantly, to couple these Ag nanocubes with an underlying Au film in order to form plasmonic nanopatch antennas. The distance between Ag nanocubes and the Au film can be controlled with ~1 nm resolution by using a series of polyelectrolyte spacer layers. We also demonstrate how to incorporate an active medium, such as an organic dye, into the plasmonic nanopatch antennas. Due to the strongly confined electromagnetic fields in the gap region between the nanocubes and the Au film, the nanopatch antennas can be used for highly enhanced fluorescence and spontaneous emission of the embedded dye molecules.12,13 The methods presented in this paper can be generalized to other emitters, such as colloidal solid-state quantum dots14 or two-dimensional semiconductor materials,15 and the plasmon resonance can be tuned over a wide spectral range by varying the size of the nanocubes or the gap.

<table><tbody><tr><td colspan="4">&lt;strong&gt;Reagents&lt;/strong&gt;</td></tr><tr><td>Ethylene glycol&amp;nbsp;</td><td>J.T. Baker</td><td>9300</td><td>Must be anhydrous</td></tr><tr><td>Sodium hydrosulfide hydrate&amp;nbsp;&amp;nbsp;</td><td>Sigma Aldrich</td><td>161527</td><td></td></tr><tr><td>Poly vinylpyrrolidone&amp;nbsp;</td><td>Sigma Aldrich</td><td>856568</td><td></td></tr><tr><td>Hydrochroric acid BDH ARISTAR PLUS</td><td>VWR International</td><td>7647-01-0</td><td></td></tr><tr><td>Silver trifluoroacetate&amp;nbsp;</td><td>Sigma Aldrich</td><td>482307</td><td>Store in dark place</td></tr><tr><td>Acetone</td><td>Sigma Aldrich</td><td>48358</td><td></td></tr><tr><td>Nitric acid</td><td>Sigma Aldrich</td><td>7697-37-2</td><td>concentrated (70%), for cleaning</td></tr><tr><td>Poly(allylamine) hydrochloride (PAH)</td><td>Sigma-Aldrich</td><td>283215</td><td></td></tr><tr><td>Polystyrene sulfonate&amp;nbsp; (PSS)</td><td>Sigma-Aldrich</td><td>561223</td><td></td></tr><tr><td>Sodium Chloride&amp;nbsp;</td><td>Macron Inc.</td><td>7647</td><td></td></tr><tr><td>Sulfo-Cyanine5 carboxylic acid (Cy5)</td><td>Lumiprobe</td><td>13390</td><td>Fluorescent dye (molecular weight: 664.76 g/mol)</td></tr><tr><td colspan="4">&lt;strong&gt;Equipments&lt;/strong&gt;</td></tr><tr><td>Stirring hotplate with temperature control</td><td>VWR International</td><td>89000-338</td><td></td></tr><tr><td>Vortex mixers</td><td>VWR International</td><td>10153-834</td><td></td></tr><tr><td>Microcentrifuge</td><td>Thermoscientific</td><td>Model 59A</td><td></td></tr><tr><td>Silicone fluid&amp;nbsp;</td><td>Sigma-Aldrich</td><td>63148-62-9</td><td></td></tr><tr><td>Micro-scale</td><td>Mettler Toledo</td><td>Model ML 104/03</td><td></td></tr><tr><td>Electron-beam metal evaporator&amp;nbsp;</td><td>CHA Industries</td><td>E-beam evaporator</td><td>Located inside a clean room</td></tr><tr><td>Pre-cleaned glass slides</td><td>Schott North America, Inc.</td><td>Nexterion Glass B&amp;nbsp;</td><td>Clean room pre-cleaned</td></tr><tr><td>25-ml 24/40 round-bottom flask</td><td>VWR International</td><td>60002-290</td><td></td></tr><tr><td>Magnetic stirring bar</td><td>VWR International</td><td>58948-116</td><td></td></tr><tr><td>Micropipettes (1&amp;ndash;10&amp;nbsp;ml, 10&amp;ndash;100&amp;nbsp;ml and 100&amp;ndash;1,000&amp;nbsp;ml)</td><td>VWR International</td><td></td><td></td></tr><tr><td>Ultrasonic cleaning bath</td><td>Branson Ultrasonic</td><td>Model 1510R-DTH</td><td></td></tr><tr><td>Stopwatch</td><td>VWR International</td><td></td><td></td></tr><tr><td>Eppendorf centrifugation tubes (1.5&amp;nbsp;ml)</td><td>VWR International</td><td>22364111</td><td></td></tr><tr><td>Poly(propylene) coning tubes (50&amp;nbsp;ml)</td><td>VWR International</td><td></td><td></td></tr><tr><td>Home built bright/darkfield microscope</td><td></td><td></td><td>75 W Xenon white light source, Nikon BF/DF 50X ELWD&lt;br/&gt; 0.55 NA, 8.2 mm WD objective, Nikon D90 digital camera, Acton 2300i spectrometer, Photometrics CoolSnap HQ charge coupled device (CCD) camera</td></tr><tr><td>He Ne laser (633&amp;nbsp;nm), 5&amp;nbsp;mW</td><td>Newport Corp.</td><td>R-30990</td><td></td></tr><tr><td>Reflectance standard</td><td>Lab Sphere</td><td>Model SRS-99-010</td><td></td></tr><tr><td>Laser long pass filter 633&amp;nbsp;nm</td><td>Semrock</td><td>LP02-633RU-25</td><td></td></tr></tbody></table>

colloidal synthesis of nanopatch antennas for applications in plasmonics and nanophotonics

Colloidal Synthesis of Nanopatch Antennas for Applications in Plasmonics and Nanophotonics

We present a method for colloidal synthesis of silver nanocubes and the use of these in combination with a smooth gold film, to fabricate plasmonic nanoscale patch antennas. This includes a detailed procedure for the fabrication of thin films with a well-controlled thickness over macroscopic areas using layer-by-layer deposition of polyelectrolyte polymers, namely poly(allylamine) hydrochloride (PAH) and polystyrene sulfonate (PSS). These polyelectrolyte spacer layers serve as a dielectric gap in between silver nanocubes and a gold film. By controlling the size of the nanocubes or the gap thickness, the plasmon resonance can be tuned from about 500 nm to 700 nm. Next, we demonstrate how to incorporate organic sulfo-cyanine5 carboxylic acid (Cy5) dye molecules into the dielectric polymer gap region of the nanopatch antennas. Finally, we show greatly enhanced fluorescence of the Cy5 dyes by spectrally matching the plasmon resonance with the excitation energy and the Cy5 absorption peak. The method presented here enables the fabrication of plasmonic nanopatch antennas with well-controlled dimensions utilizing colloidal synthesis and a layer-by-layer dip-coating process with the potential for low cost and large-scale production. These nanopatch antennas hold great promise for practical applications, for example in sensing, ultrafast optoelectronic devices and for high-efficiency photodetectors.

Here, we show representative results of the characteristics of the plasmonic nanopatch antennas, including SEM images of the sample structure, a reflectivity spectrum of a collection of nanopatch antennas and a scattering spectrum from a single nanopatch antenna. The energy of the plasmon resonance of the nanopatch antennas depends on the size of the nanocubes, the thickness of the dielectric gap region, i.e., the number of PE layers, as well as the dielectric material. In the procedure presented above we obtained Ag nanocubes with an average side length of 75 nm and slightly rounded corners (radius of curvature ~10 nm) coated in a PVP layer with an estimated thickness of 1-3 nm. In combination with the 5 PE layers and gold film, this result in a plasmon resonance centered at ~650 nm with a full-width-at-half-maximum (FWHM) of ~50 nm. This in turn has good spectral overlap with the absorption and emission wavelength of the Cy5 molecules which is centered at 646 and 662 nm, respectively.
Figure 3A shows a SEM image of a sample with a high concentration of nanocubes. These nanocubes were deposited on top of a Au film with 5 PE layers. Such SEM images are used to verify the overall quality of the nanocube synthesis; however, these samples are not utilized for further optical measurements as the density of the nanocubes is too high. Additionally, due to the high density, some nanocubes do not lie on the surface which is essential to form the plasmonic nanopatch antenna structure.
Figure 3B shows a SEM image of a sample of nanocubes fabricated using a nanocube solution which has been diluted by a factor of 1/10. This sample is used for measurements where the reflectivity of white light from an ensemble of nanopatch antennas was measured to determine the overall plasmon resonance. Figure 3C shows a SEM image of a sample of nanocubes fabricated using a nanocube solution which has been diluted by a factor of 1/100. This sample is used for scattering measurements of an individual nanopatch antenna. Using the diluted nanocube solution enables individual nanopatch antennas to be spatially isolated at an image plane by using a small pinhole.
Figure 4A shows a reflectivity spectrum, after normalization with the white light background, measured from a similar sample to the one shown in the SEM image in Figure 3B. Figure 4B shows a scattering spectrum from a single nanopatch antenna similar to the sample shown in the SEM image in Figure 3C.
Figure 4C shows a dark field image of a nanopatch antenna sample (prepared by a 1/100 diluted nanocube solution dispersed on a gold film with 5 PE layers) taken by a Nikon D90 digital camera. The observed bright red dots are due to scattering of white light from individual nanopatch antennas. A few spots are observed to have colors other than red, which is a result of nanocubes with different sizes or larger nanoparticles with non-cubic shapes.
Figure 4D shows two fluorescence spectra, one measured from a single nanopatch antenna (from a sample similar to the one shown in Figure 3C) and the other from a control sample consisting of a glass slide with the same number of PE layers and density of Cy5 dye molecules. The fluorescence intensity from Cy5 molecules coupled to the nanopatch antenna is much stronger than on the glass slide. This results from an enhanced excitation rate as well as a modified radiation pattern and increased quantum efficiency of the dye molecules.12 After correcting for background fluorescence and normalizing per unit area by dividing the area under the nanocube with the excitation spot size,12 we obtain an enhancement factor of ~ 12,000 from the data shown in Figure 4D. This enhancement factor is smaller compared with the previously reported value of 30,00012 likely due to the use of a Au instead of Ag film, increasing non-radiative losses.
<img alt="Chemical synthesis setup; hot plate, condenser, round-bottom flask; organic compound reaction." src="/files/ftp_upload/53876/53876fig1.jpg" data-altupdatedat="1788235205000" data-alt="Figure 1"> 
Figure 1. Equipment setup for Ag nanocube synthesis. (A) A photograph of the equipment setup showing the heating bath on top of the stirring hotplate with temperature control. (B) A close up of the round-bottom flask (RBF) containing the nanocube solution during the synthesis. The setup is located inside a fume hood with proper air ventilation. <a href="https://www.jove.com/files/ftp_upload/53876/53876fig1large.jpg" target="_blank">Please click here to view a larger version of this figure.</a>
<img alt="Biochemistry experiment setup with enzyme reaction vessel and sample tubes for protein assay." src="/files/ftp_upload/53876/53876fig2.jpg" data-altupdatedat="1788235205000" data-alt="Figure 2"> 
Figure 2. Pictures of the nanocube solution. (A) Nanocube solution after the 2.5-hr synthesis and (B) after transfer to smaller tubes and re-suspended in de-ionized water. <a href="https://www.jove.com/files/ftp_upload/53876/53876fig2large.jpg" target="_blank">Please click here to view a larger version of this figure.</a>
<img alt="Nanoparticle SEM images; scale bars 1μm, 500nm, 200nm; morphology and distribution analysis." src="/files/ftp_upload/53876/53876fig3highres.jpg" width="700" data-altupdatedat="1788235205000" data-alt="Figure 3"> 
Figure 3. SEM characterizations of Ag nanocubes. (A) SEM image of a concentrated nanocube sample, (B) a diluted (1/10) nanocube sample, and (C) a diluted (1/100) nanocube sample. <a href="https://www.jove.com/files/ftp_upload/53876/53876fig3highres.jpg" target="_blank">Please click here to view a larger version of this figure.</a>
<img alt="Spectroscopy data and microscopy for Cy5 dye; reflection, scattering, fluorescence intensity graphs." src="/files/ftp_upload/53876/53876fig4highres.jpg" width="700" data-altupdatedat="1788235205000" data-alt="Figure 4"> 
Figure 4. Optical characterizations of nanopatch antennas. (A) Normalized reflection spectrum measured from an ensemble of nanopatch antennas (non-diluted nanocube solution). (B) Scattering spectrum from a single nanopatch antenna (1/100 diluted nanocube solution). (C) A dark-field image of a nanopatch antenna sample (1/100 diluted nanocube solution) taken under white light illumination. Each bright red dot corresponds to an individual plasmonic nanopatch antenna. (D) Fluorescence from Cy5 dye molecules embedded in a nanopatch antenna (red solid line) compared to that from a glass slide with an identical concentration of Cy5 dyes (dashed black line). <a href="https://www.jove.com/files/ftp_upload/53876/53876fig4highres.jpg" target="_blank">Please click here to view a larger version of this figure.</a>

A protocol for the colloidal synthesis of silver nanocubes and fabrication of plasmonic nanoscale patch antennas with sub-10 nm gaps is presented.

We present a method for colloidal synthesis of silver nanocubes and the use of these in combination with a smooth gold film, to fabricate plasmonic ...

The overall goal of this experimental procedure is to demonstrate a technique to fabricate nanopatch antennas which can enable tailored light-matter interactions such as strongly enhanced fluorescence. This method can help answer key questions in the nanophotonic and plasmonic communities such as how to achieve high fluorescence enhancement and control of other related subprocesses. The main advantage of this technique is that it enables large-scale fabrication of nanoantennas, where the critical feature size can be controlled on a single nanometer scale.Demonstrating this procedure will be Thang Hoang, a postdoctoral associate, and Jiani Huang, a graduate student from my laboratory. Begin the synthesis procedure by dipping a cleaned round-bottomed flask into the heating bath, approximately 10mm deep into the liquid. Then, use a micropipette to place 10mL of ethylene glycol, or EG, into the round-bottomed flask.Put the cap on the flask and wait for 20 minutes. The purpose of this step is to clean the flask with EG.After 20 minutes, remove the cap and then lift the round-bottomed flask out of the heating bath. Take the entire clamp out, as the EG solution is hot.Pour the 10mL of EG into a disposal container, making sure that the magnetic stirring bar does not fall out. Place the flask back into the heating bath. Use a micropipette to add 5mL of EG into the flask and put the cap on.After waiting for 5 minutes, take the cap off and use a micropipette to place 60 microliters of sodium hydrosulfide hydrate into the flask. Put the cap back on and wait for two minutes. After two minutes, take the cap off and use a micropipette to place 500 microliters of the hydrochloric acid solution into the flask.Immediately, use a micropipette to add 1.25mL of the PVP solution into the flask before putting the cap back on and waiting for two minutes. After removing the cap, use a micropipette to place 400 microliters of the silver trifluoroacetate solution into the flask, and put the cap back on. Wait for 2.5 hours.The silver nanocubes are forming during this step. Throughout this time, reduce the room light to a minimum. After 2.5 hours, turn the heater off, but leave the stirring on to avoid burning the fluid on the bottom.Use the clamp to raise the flask above the heating bath, and remove the cap. Then, remove the flask from the heating bath to allow it to cool off faster. After about 20 minutes, add 5mL of acetone into the flask.Vortex it to mix the solutions well. In the end, the total volume of the solution is 12mL. Using a micropipette, transfer the final solution to eight smaller 1.5mL plastic tubes.Centrifuge these eight tubes at a speed of 5, 150 Gs for ten minutes. As a result, all the silver nanocubes are at the bottom of the tubes. Use a micropipette to remove the top supernatant, leaving approximately 100 microliters at the bottom of each tube.Then, add 1mL of deionized water into each of these tubes. Vortex and sonicate the tubes. The nanocubes are now suspended in mainly deionized water.Repeat the centrifugation-resuspension step once more. First, deposit a polyalleleamine hydrochloride, or PAH layer, by immersing the gold film into a PAH solution for five minutes. This results in a PAH layer on top of the gold film with a thickness of approximately 1 nanometer.After five minutes, rinse the gold film using clean deionized water. There is now a single PAH layer on top of the gold film. Next, immerse the gold film with the single PAH layer into a sodium chloride solution for one minute.Next, immerse the gold film with the single PAH layer into a polystyrene sulfonate, or PSS solution for five minutes. This results in a PSS layer with a thickness of approximately 1 nanometer on top of the PAH layer. Continue this process to deposit a total of five polyelectrolyte layers on the gold film.Drop cast 100 microliters of a 25 micromolar cyanine-5 solution onto the sample surface. Then place a clean cover slip on top of the solution drop. Cyanine-5 molecules will incorporate into the top polyelectrolite layers uniformly.After ten minutes, rinse the sample with deionized water, and dry it using clean nitrogen gas. To form nanopatch antennas, dilute the prepared nanocube solution by 100 times using deionized water, to enable the optical study of individual nanopatch antennas. Use a micropipette to place a drop of 20 microliters of the diluted nanocube solution onto a clean cover slip.Place the sample in contact with the cover slip for two minutes. As a result, the silver nanocubes are immobilized on the top terminal PAH layer, because the nanocubes synthesized here are negatively charged, and the top PAH layer is positively charged. After two minutes, rinse the sample with deionized water and dry it using clean nitrogen gas.Shown here are representative scanning electron microscopy images of the silver nanocubes obtained from this procedure. Here, the sample was fabricated using an undiluted solution of nanocubes. Whereas the sample was diluted ten, and one hundred times in these images.In all cases, nanocubes of a relatively uniform size, characterized by sharp corners, with a radius of curvature of about 10 nanometers are observed. Shown here are representative optical characterizations of the final nanopatch antennas with embedded cyanine-5 dye molecules. Reflection measurements of an ensemble of nanopatch antennas show a characteristic plasmon resonance at 650 nanometers.Scattering measurements of individual nanoantennas display a resonance at the same wavelength, but with a narrower width. Dark field images of the sample show diffraction-limited spots with a uniform red color, indicating that most nanopatch antennas have very similar resonances due to the good size homogeneity of the fabricated nanocubes. Finally, large fluorescence enhancement of the embedded cyanine-5 dye molecules is observed.Once mastered, this fabrication technique can be completed in five hours if it is performed properly. After its development, this technique paved the way for researchers in the fields of nanophotonics and plasmonics to explore the fundamental applied metal interaction and potential applications in une-surface optoelectronic devices, including light-emitting diodes, high efficiency photoreflectors, and quantum information science. After watching this video, you should have a good understanding of how to fabricate nanopatch antennas utilizing colloidally synthesized silver nanocubes to enable enhanced light-matter interactions.

colloidal-synthesis-nanopatch-antennas-for-applications-plasmonics

Research

JoVE Journal

Engineering

Plasmonic tweezers and photonic crystal nanostructures are shown to produce useful enhancements in the efficiency and orientation control of optically trapping micro- and nano-particles.

Utilization of Plasmonic and Photonic Crystal Nanostructures for Enhanced Micro- and Nanoparticle Manipulation

Solution-suspendable gold nanotubes with controlled dimensions can be synthesized by electrochemical deposition in porous anodic aluminum oxide (AAO) membranes using a hydrophobic polymer core. Gold nanotubes and nanotube arrays hold promise for applications in plasmonic biosensing, surface-enhanced Raman spectroscopy, photo-thermal heating, ionic and molecular transport, microfluidics, catalysis and electrochemical sensing.

Template Directed Synthesis of Plasmonic Gold Nanotubes with Tunable IR Absorbance

Silver nanowires can simultaneously transport electrons and optical information in the form of surface plasmons. A procedure is described here to realize such a shared circuitry and the limitations at propagating both information carriers are evaluated.

Evaluating Plasmonic Transport in Current-carrying Silver Nanowires

A simple, robust and scalable technique to functionalize and self-assemble macroscopic nanoparticle-ligand monolayer films onto template-free substrates is described in this protocol.

A Technique to Functionalize and Self-assemble Macroscopic Nanoparticle-ligand Monolayer Films onto Template-free Substrates

Here, we describe a protocol for synthesis of magneto-plasmonic nanoparticles with a strong magnetic moment and a strong near-infrared (NIR) absorbance. The protocol also includes antibody conjugation to the nanoparticles through the Fc moiety for various biomedical applications which require molecular specific targeting.

Synthesis of Immunotargeted Magneto-plasmonic Nanoclusters

We report protocols for “polymerizing” various types of polymer-encapsulated metal nanoparticles into long chains of “homo-“ and “co-polymers”.

Using Polystyrene-block-poly(acrylic acid)-coated Metal Nanoparticles as Monomers for Their Homo- and Co-polymerization

The synthesis of uniform gold nanoparticles coated with semiconductor shells of CdS or ZnS is performed. The semiconductor coating is conducted by first depositing a silver sulfide shell and exchanging the silver cations for zinc or cadmium cations.

Synthesis, Characterization, and Functionalization of Hybrid Au/CdS and Au/ZnS Core/Shell Nanoparticles

We demonstrate the fabrication of periodic gold nanocup arrays using colloidal lithographic techniques and discuss the importance of nanoplasmonic films.

Fabrication of Periodic Gold Nanocup Arrays Using Colloidal Lithography

A protocol for anisotropic photodeposition of Pd onto aqueously-suspended Au nanorods via localized surface plasmon excitation is presented.

Photodeposition of Pd onto Colloidal Au Nanorods by Surface Plasmon Excitation

Presented here is a protocol for the synthesis of silver-palladium (Ag-Pd) alloy nanoparticles (NPs) supported on ZrO2 (Ag-Pd/ZrO2). This system allows for harvesting energy from visible light irradiation to accelerate and control molecular transformations. This is illustrated by nitrobenzene reduction under light irradiation catalyzed by Ag-Pd/ZrO2 NPs.

Preparation of Silver-Palladium Alloyed Nanoparticles for Plasmonic Catalysis under Visible-Light Illumination

Here, the synthesis of gold (Au) seeds is described using the Turkevich method. These seeds are then used to synthesize gold-tin alloy (Au-Sn) nanoparticles with tunable plasmonic properties.

Aqueous Synthesis of Plasmonic Gold-Tin Alloy Nanoparticles

Learn colloidal synthesis of silver nanocubes for fabricating nanopatch antennas with sub-10 nm gaps. This method enables enhanced fluorescence and controlled light-matter interactions in nanophotonic applications.

Colloidal Synthesis of Nanopatch Antennas for Applications in Plasmonics and Nanophotonics

Explore More Videos