Name: A Practical Guide on Coupling a Scanning Mobility Sizer and Inductively Coupled Plasma Mass Spectrometer (SMPS-ICPMS) (Video) | JoVE Journal
Uploaded: 2017-07-11T12:30:00.000+00:00
Duration: 11 min 18 s
Description: Learn to couple SMPS with ICPMS for real-time aerosol analysis. This method enables simultaneous measurement of particle size and chemical composition using a rotating disc diluter system.

ai_agent_IP

ai_agent

maintenance

instantTrialDurationMinutes

isBiopharma

enableNewMyJoveSectionDesign

educationFeatures

seoMetaApi

ai_copilot_institution_blacklist

ai_chat_institution_blacklist

freeAccessWindow

ssoRoleCapture

scheduledMaintenanceBanner

joveLabsFeatures

disable_autoplay_for_bots

extended_trial_duration

5 minutes

Financial support was provided by the Competence Center for Materials Science and Technology (CCMX, Project NanoAir), the Swiss National Science Foundation (Project 139136), the Swiss Nanoscience Institute (Argovia, Project NanoFil), and the Swiss Competence Center for Bioenergy Research (SCCER BIOSWEET). The authors thank Albert Schuler for his support in operating the TGA, and Adelaide Calbry-Muzyka for reviewing this manuscript.

1. RDD-SMPS-ICPMS Setup
<ol>
	<li>Coupling strategy of the RDD-SMPS-ICPMS setup 
	NOTE: In order to couple the different instruments, i.e. RDD, SMPS and ICPMS, and to control the different gas flows, some modifications in the instrumental arrangements are needed. The main steps of the coupling concept are summarized here:
	<ol>
		<li>Use conductive tubing with inner/outer diameters 6.0/12.0 mm (carbon impregnated silicone tubing) to connect the different instrumental parts.</li>
		<li>Install the Rotating Disk Diluter between the aerosol source and the Differential Mobility Analyzer, or DMA, where the particle size classification takes place. Split the classified aerosol at the DMA outlet in two fractions. One will be aspirated by the Condensation Particle Counter, or CPC. The other is guided towards the Inductively Coupled Plasma Mass Spectrometer, or ICPMS (Figure 1).</li>
		<li>Use a mass flow controller (MFC) and a filter, such as a High-Efficiency Particulate Air filter (HEPA), to provide the RDD with particle-free dilution argon.</li>
		<li>Add another filter at the RDD outlet for the excess raw gas (QRDD out). Check the performance of all the filters in use from time to time while using the CPC.</li>
		<li>Use another MFC and filter to adjust the sheath gas flow (Qsheath) introduced to the DMA.</li>
		<li>To adjust the DMA excess gas flow (QDMA exc), mount a filter, MFC, and vacuum pump in series at the DMA outlet.</li>
		<li>Connect an additional MFC and filter to add particle free air (QCPC air) to the CPC, as makeup flow to reduce the amount of classified aerosol (QCPC class), consumed by the CPC. 
		NOTE: This is because the CPC actively aspirates a flow defined by a critical orifice and an external pump, which is about 1 L/min. The classified flow rate at the ICP inlet (QICP in) is the difference between the flow rate at the DMA outlet (Qclass) and QCPC class.</li>
	</ol>
	</li>
</ol>
2. Measurement Protocol for RDD-SMPS-ICPMS
NOTE: Before tuning the SMPS-ICPMS parameters, the flows used for the aerosol generator must be set. Here, the procedure of using liquid and solid samples is described.
<ol>
	<li>Example of aerosol sources
	<ol>
		<li>Using aerosol generator for liquids and suspensions
		<ol>
			<li>For an example of using an aerosol generator for a suspension, prepare a zinc oxide (ZnO) suspension from a commercial ZnO nanopowder (e.g. with a nominal diameter of 50 nm) and poly-acrylic acid as stabilizer for the nanoparticles. Dilute the prepared suspension to obtain a ZnO concentration of approx. 30 &#181;g/mL. This concentration is chosen because it will lead to a good ICPMS signal later, with all the gas flows applied.</li>
			<li>For the second measurement prepare an aqueous sodium chloride (NaCl) solution with a concentration of 200 &#181;g/mL.
			<ol>
				<li>First, fill the suspension or solution into the bottle and mount it on the aerosol generator.</li>
			</ol>
			</li>
			<li>Use the aerosol generator to generate an aerosol from the salt solution or the particle suspension, and to remove the water from the particles in the silica gel drier.
			<ol>
				<li>Set the compressed air valve of the aerosol generator slightly above 1 bar. Adjust the This results in an aerosol flow behind the diffusion drier to aboutof approximately 1 L/min. Finally, connect the outlet of the drier to the RDD inlet.</li>
			</ol>
			</li>
		</ol>
		</li>
		<li>Using thermogravimeter or a tubular furnace 
		NOTE: As an example for applying the RDD-SMPS-ICPMS in measuring emissions from thermal processes, a copper chloride (CuCl2) sample is analyzed. Two aerosol sources are used, namely a TGA and a tubular furnace. In both cases, the reactive gas (e.g. O2), which is used for the thermal process, is mixed with argon to the appropriate ratio in order to prevent nucleation and condensation. In this work only the measurement procedure and representative data from a TGA experiment are presented.
		<ol>
			<li>First, tare the empty TGA crucible. Weigh 50 mg of CuCl2 powder and place it in a crucible.</li>
			<li>Adjust one MFC for the reactive gas (O2) to about 20 mL/min.</li>
			<li>Set the flow of the protective gas (argon) to about 80 mL/min. At the TGA outlet, add an argon flow of about 900 mL/min to get a total flow of about 1 L/min (i.e. the sum of the flows of O2, protective argon and added argon). If the RDD pump is used, adjust the MFC to reach the required flow.</li>
			<li>Set the desired temperature program (25 &#176;C for 18 min and 450 &#176;C for 15 min).</li>
		</ol>
		</li>
	</ol>
	</li>
	<li>Setting the flows 
	NOTE: To achieve a stable operation of the RDD-SMPS-ICPMS setup, all the gas and aerosol flows should be adjusted carefully as described below. In this section, an example of a set of parameter values for adjusting the RDD, SMPS and ICPMS are given. Another set of parameters is possible; the procedure will however remain the same. The flow abbreviations used are listed in Figure 1. In the following steps use a flowmeter, such as a flow calibrator, to measure the different gas and aerosol flows before starting the measurement.
	<ol>
		<li>First set the argon sheath flow at the DMA inlet to 3 L/min.</li>
		<li>Set the temperature of the RDD heating block to 80 &#176;C, and that of the evaporation tube to 350 &#176;C.</li>
		<li>Adjust the mass flow controller of the dilution argon in order to obtain 0.6 L/min as flow of the diluted sample at the outlet of the rotating disk diluter (Qsample). The ratio 0.6/3 of the sheath gas to the sample gas is chosen to cover a particle size ranging from about 14 to about 340 nm.</li>
		<li>Then, carefully adjust the excess gas mass flow controller (QDMA exc) to achieve a classified aerosol flow of 0.6 L/min (Qclass), the same flow rate as that of the diluted polydispersed aerosol at the DMA inlet (Qpoly).</li>
		<li>Next, Place the flow calibrator between DMA and CPC, and adjust the CPC makeup air flow, to reduce the flow rate of classified aerosol aspirated by the CPC to 0.18 L/min. This corresponds to 30% of Qclass.</li>
		<li>Check the remaining flow of classified aerosol to ensure that 0.42 Liter per min are directed to the ICPMS, i.e. 70% of the classified aerosol (Qclass). Slight change of this flow can be corrected by fine-tuning the MFC of the DMA excess gas again.</li>
	</ol>
	</li>
	<li>Setting the SMPS software
	<ol>
		<li>Next, calculate the dynamic viscosity and the mean free path of argon at ambient temperature and pressure23. Enter both values in the SMPS software.</li>
		<li>In the SMPS software, set the up and down scan durations of the DMA scanning cycle to 150 s and 30 s (i.e. 1 DMA cycle = 1 scan = 180 s).</li>
		<li>In the SMPS software, set the DMA maximum voltage to 4.5 kV to cover the PSD interval ranging from about 14 to about 340 nm. 
		NOTE: A voltage maximum of 10 kV is normally used in air-operated SMPS. Due to the lower dielectric strength of argon relative to that of air, the limit should be set lower in this application, since otherwise electric arcing would occur, leading to instrument damage and signal errors.</li>
	</ol>
	</li>
	<li>Setting the ICPMS
	<ol>
		<li>Remove the conventional introduction system of liquid samples to introduce dry aerosol directly into ICPMS. Add a conductive tube between the respective port of DMA outlet and the ICPMS. Use this tube for xenon (Xe), with a concentration of about 100 ppmv in argon matrix, to optimize the ICPMS plasma prior to each measurement and to control the plasma stability during the measurement.</li>
		<li>Maintain the Xe flow constant for all measurements (e.g. at 4 mL/min) and tune the other parameters in the ICPMS software, including ICP dilution gas and sampling depth, to achieve a fixed Xe intensity. 
		NOTE: The main ICPMS tuning parameters are listed in Table 1. The parameters to be tuned prior to each measurement are indicated in the last column.</li>
		<li>Set the SMPS and ICPMS acquisition time to cover the desired total duration of the aerosol measurement (e.g., for 10 SPMS scan, set the ICPMS acquisition time to at least 30 min).</li>
		<li>After setting the gas flows and the SMPS and the ICPMS parameters run the two instruments manually at the same time. In the case of the TGA, acquire SMPS and ICPMS blank signals at 25 &#176;C for 18 min (6 scans). In the case of the suspension or liquid sample, acquire blank signals during 2 scans of 6 min with the disk rotation speed set to zero. Then set the dilution factor of the RDD to the desired value by adjusting the disk rotation speed manually. With the current configuration, 100% rotating speed corresponds to a dilution factor of 14.9.</li>
	</ol>
	</li>
	<li>Data analysis 
	NOTE: ICPMS measures the ion intensity per unit time (unit: count per second, or cps) for each m/z. This intensity is proportional to the analyte mass. SMPS data represent the number-weighted PSD of classified aerosol (PSDn) entering the DMA (unit: 1/cm3), based on the number concentrations determined by the CPC behind the DMA. To compare both ICP and SMPS signals, the volume-weighted PSD (PSDv) must be calculated. The following calculations and corrections should be made:
	<ol>
		<li>Export the raw signal intensities versus time for each m/z from the ICPMS data, and the PSDn- determined by the SMPS software &#8211; as a function of the particle diameter (dp). From the SMPS raw data, export the particle diameter and the corresponding scanning time. Use the latter in order to correlate the ICPMS measurement time with the particle diameter (see below). 
		NOTE: The SMPS software must consider that the aerosol flow at the DMA outlet is split, and only 30% of the classified particles reach the CPC. This can be achieved by multiplying the counting efficiency values &#8211; stored in a separate table as type-specific CPC characteristics &#8211; by a factor of 0.3.</li>
		<li>Since the desired information is not primarily the particle concentration between RDD and DMA, but that at the RDD inlet, multiply the measured concentrations by the RDD dilution factor, i.e. 14.9 in the current configuration.</li>
		<li>To calculate volume-weighted data from the original number-weighted SMPS data, multiply the recorded concentrations of PSDn by the volume V(dP) of the measured particles6 (V(dP)= (&#960;/6)&#8729;dP3).</li>
		<li>Calculate the ICPMS net signal by subtracting the background signal from the raw ion signal for each isotope. Then, multiply the net signal by the inverse single charge probability 1/p+1(dp) to get the corrected ICP intensity, which is approximately proportional to the concentration at the DMA inlet and hence at the RDD inlet (assuming no particle losses between RDD inlet and ICPMS or CPC inlets).
		<ol>
			<li>Calculate the probability of particles to carry one elemental positive charge by using the Wiedensohler approximation24. For the SMPS data processed by the SMPS software, the correction for this charge probability is normally implemented in the software.</li>
		</ol>
		</li>
		<li>For a given SMPS scan, plot the SMPS particle concentration or the ICPMS intensity as a function of particle diameter in an x-y diagram. In the case of a steady-state aerosol, use the same type of diagram to present the concentration or intensity averaged over several scans.</li>
		<li>For a series of scans, use 2D surface or 3D diagrams to plot the SMPS concentration or ICPMS intensity as functions of diameter and time. In the case of thermal processes, if a temperature program is used, substitute the time by the corresponding temperature values. 
		NOTE: Moreover, the calculations needed for ICPMS and SMPS data to make such plots can be automated using calculation software like MATLAB or Igor Pro, which allows for obtaining robust final results in a short time.</li>
	</ol>
	</li>
</ol>

<ol><li>Chen, B. T., Crow, D. J. <a target="_blank" href="http://www.sciencedirect.com/science/article/pii/0021850286900224">Use of an aerodynamic particle sizer as a real-time monitor in generation of ideal solid aerosols.</a> J Aerosol Sci. 17 (6), 963-972 (1986).</li>
<li>Intra, P., Tippayawong, N. <a target="_blank" href="https://www.researchgate.net/publication/26517300_An_overview_of_differential_mobility_analyzers_for_size_classification_of_nanometer-sized_aerosol_particles">An overview of differential mobility analyzers for size classification of nanometer-sized aerosol particles.</a> Songklanakarin J. Sci. Technol. 30 (2), 243-256 (2008).</li>
<li>Itoh, M., Takahashi, K. <a target="_blank" href="http://www.sciencedirect.com/science/article/pii/002185029190076T">Measurement of aerosol particles by dynamic light scattering-I, effects of non-Gaussian concentration fluctuation in real time photon correlation spectroscopy.</a> J Aerosol Sci. 22 (7), 815-822 (1991).</li>
<li>Nickel, C., et al. <a target="_blank" href="http://link.springer.com/article/10.1007/s11051-014-2260-2">Dynamic light-scattering measurement comparability of nanomaterial suspensions.</a> J Nanopart Res. 16 (2), 2260(2014).</li>
<li>Hagendorfer, H., et al. <a target="_blank" href="http://link.springer.com/article/10.1007/s11051-009-9816-6">Size-fractionated characterization and quantification of nanoparticle release rates from a consumer spray product containing engineered nanoparticles.</a> J Nanopart Res. 12 (7), 2481-2494 (2010).</li>
<li>Flagan, R. C. <a target="_blank" href="https://www.jstage.jst.go.jp/article/kona/26/0/26_2008023/_pdf">Differential mobility analysis of aerosols: A tutorial.</a> KONA Powder Part J. 26, 254-268 (2008).</li>
<li>Salgueiro-González, N., López de Alda, M. J., Muniategui-Lorenzo, S., Prada-Rodríguez, D., Barceló, D. <a target="_blank" href="http://www.sciencedirect.com/science/article/pii/S0165993614002593">Analysis and occurrence of endocrine-disrupting chemicals in airborne particles.</a> Trends Anal Chem. 66, 45-52 (2015).</li>
<li>Pröfrock, D., Prange, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Inductively+coupled+plasma-mass+spectrometry+%28ICP-MS%29+for+quantitative+analysis+in+environmental+and+life+sciences%3A+A+review+of+challenges%2C+solutions%2C+and+trends%5BTitle%5D)+AND+%22Appl+Spectrosc%22%5BJournal%5D)">Inductively coupled plasma-mass spectrometry (ICP-MS) for quantitative analysis in environmental and life sciences: A review of challenges, solutions, and trends.</a> Appl Spectrosc. 66 (8), 843-868 (2012).</li>
<li>Gerdes, K., Carter, K. E. <a target="_blank" href="https://inis.iaea.org/search/search.aspx?orig_q=RN:43110364">Calibration strategy for semi-quantitative direct gas analysis using inductively coupled plasma mass spectrometry.</a> Spectrochim Acta B. 66 (9-10), 712-725 (2011).</li>
<li>Wellinger, M., Wochele, J., Biollaz, S. M. A., Ludwig, C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Online+elemental+analysis+of+process+gases+with+ICP-OES%3A+A+case+study+on+waste+wood+combustion%5BTitle%5D)+AND+%22Waste+Manage%22%5BJournal%5D)">Online elemental analysis of process gases with ICP-OES: A case study on waste wood combustion.</a> Waste Manage. 32 (10), 1843-1852 (2012).</li>
<li>Edinger, P., Tarik, M., Hess, A., Testino, A., Ludwig, C. <a target="_blank" href="http://pubs.acs.org/doi/abs/10.1021/acs.energyfuels.5b02608">Online Detection of Selenium and Its Retention in Reducing Gasification Atmosphere.</a> Energy Fuels. 30 (2), 1237-1247 (2016).</li>
<li>Bouyssiere, B., Szpunar, J., Lobinski, R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Gas+chromatography+with+inductively+coupled+plasma+mass+spectrometric+detection+in+speciation+analysis%5BTitle%5D)+AND+%22Spectrochimica+Acta+B%22%5BJournal%5D)">Gas chromatography with inductively coupled plasma mass spectrometric detection in speciation analysis.</a> Spectrochimica Acta B. 57 (5), 805-828 (2002).</li>
<li>Pace, H. E., Rogers, N. J., Jarolimek, C., Coleman, V. A., Higgins, C. P., Ranville, J. F. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Determining+transport+efficiency+for+the+purpose+of+counting+and+sizing+nanoparticles+via+single+particle+inductively+coupled+plasma+mass+spectrometry%5BTitle%5D)+AND+%22Anal.+Chem%22%5BJournal%5D)">Determining transport efficiency for the purpose of counting and sizing nanoparticles via single particle inductively coupled plasma mass spectrometry.</a> Anal. Chem. 83 (24), 9361-9369 (2011).</li>
<li>Laborda, F., Jiménez-Lamana, J., Bolea, E., Castillo, J. R. <a target="_blank" href="http://pubs.rsc.org/en/Content/ArticleLanding/2011/JA/c0ja00098a">Selective identification, characterization and determination of dissolved silver (i) and silver nanoparticles based on single particle detection by inductively coupled plasma mass spectrometry.</a> J. Anal. At Spectrom. 26 (7), 1362-1371 (2011).</li>
<li>Pease, R. F. W. <a target="_blank" href="http://www.sciencedirect.com/science/article/pii/S107656700700002X">Significant advances in scanning electron microscopes.</a> Adv Imag Elect Phys. 150, 53-86 (2008).</li>
<li>Dax, M. Advancements in scanning electron microscopes. Semiconductor International. 20 (2), 60-68 (1997).</li>
<li>Kawamoto, N., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Transmission+electron+microscope+as+an+ultimate+tool+for+nanomaterial+property+studies%5BTitle%5D)+AND+%22Microscopy%22%5BJournal%5D)">Transmission electron microscope as an ultimate tool for nanomaterial property studies.</a> Microscopy. 62 (1), 157-175 (2013).</li>
<li>Weber, A. P., Baltensperger, U., Gäggeler, H. W., Tobler, L., Keil, R., Schmidt-Ott, A. <a target="_blank" href="http://www.sciencedirect.com/science/article/pii/S0021850205800849">Simultaneous in-situ measurements of mass, surface and mobility diameter of silver agglomerates.</a> J Aerosol Sci. 22, Suppl 1. S257-S260 (1991).</li>
<li>Hess, A., Tarik, M., Ludwig, C. <a target="_blank" href="http://www.sciencedirect.com/science/article/pii/S0021850215000890">A hyphenated SMPS-ICPMS coupling setup: Size-resolved element specific analysis of airborne nanoparticles.</a> J Aerosol Sci. 88, 109-118 (2015).</li>
<li>Hess, A., Tarik, M., Losert, S., Ilari, G., Ludwig, C. <a target="_blank" href="http://www.sciencedirect.com/science/article/pii/S0021850215300215">Measuring air borne nanoparticles for characterizing hyphenated RDD-SMPS-ICPMS instrumentation.</a> J Aerosol Sci. 92, 130-141 (2016).</li>
<li>Hess, A., Tarik, M., Foppiano, D., Edinger, P. <a target="_blank" href="http://pubs.acs.org/doi/abs/10.1021/acs.energyfuels.6b00174">Online Size and Element Analysis of Aerosol Particles Released from Thermal Treatment of Wood Samples Impregnated with Different Salts.</a> Energy Fuels. 30, 4072-4084 (2016).</li>
<li>Hueglin, C. h, Scherrer, L., Burtscher, H. <a target="_blank" href="http://www.sciencedirect.com/science/article/pii/S0021850296004855">An accurate, continuously adjustable dilution system (1:10 to 1:104) for submicron aerosols.</a> J Aerosol Sci. 28 (6), 1049-1055 (1997).</li>
<li>Kulkarni, P., Baron, P. A., Willeke, K. <a target="_blank" href="http://scholar.google.com/scholar?hl=en&safe=off&q=author%3aKulkarni%2C+P+%22Aerosol+Measurement%3A+Principles%2C+Techniques%2C+and+Applications%22">Aerosol Measurement: Principles, Techniques, and Applications</a>. , 3rd ed, 18-19 (2011).</li>
<li>Wiedensohler, A. <a target="_blank" href="http://www.sciencedirect.com/science/article/pii/0021850288902789">An approximation of the bipolar charge distribution for particles in the submicron size range.</a> J Aerosol Sci. 19 (3), 387-389 (1988).</li>
<li>Ludwig, C., Wochele, J., Jörimann, U. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Measuring+evaporation+rates+of+metal+compounds+from+solid+samples%5BTitle%5D)+AND+%22Anal+Chem%22%5BJournal%5D)">Measuring evaporation rates of metal compounds from solid samples.</a> Anal Chem. 79 (7), 2992-2996 (2007).</li>
<li>Kovacs, R., Nishiguchi, K., Utani, K., Günther, D. <a target="_blank" href="http://pubs.rsc.org/en/Content/ArticleLanding/2010/JA/b924425e">Development of direct atmospheric sampling for laser ablation-inductively coupled plasma-mass spectrometry.</a> J. Anal. At. Spectrom. 25 (2), 142-147 (2010).</li>
</ol>

The authors declare no competing financial interests.

Compared with the state-of-the-art existing analytical methods for aerosols, such as particle sizers, the RDD-SMPS-ICPMS combination is not only able to simultaneously acquire chemical and size information, but the time-resolved ICPMS signal also allows the determination of each element&#39;s contribution in the overall PSD. However, only particles with a diameter below 500 nm can be measured by the current argon-operated SMPS-ICPMS. Furthermore, for a complete characterization of aerosol particles, other offline techniques are needed to determine other properties, including the morphology and the molecular structure.
The NaCl measurement is a simple example showing that a steady-state process can be controlled/monitored well with the coupled SMPS-ICPMS system. This setup can also be used in such experiments as an online analytical tool to reveal the effects of different experimental parameters on the properties of the generated particles. Any change in the particle size, and in the particle or elemental concentration, such as in the case of the thermal treatment of CuCl2 sample, can be tracked online by SMPS-ICPMS.
On the other hand, the SMPS-ICPMS combination allows not only to measure, but also to distinguish between gas and particle species. Indeed, the part of the signal related to the particulate matter can be easily distinguished from that of gaseous compounds, because the ICPMS signal of the latter covers the entire size range and does not follow a distribution shape such as that of the signal related to particles. This is due to the fact that the SMPS scanning has no effect on gaseous species, and the ICPMS measures the total intensity of a given isotope. This behavior is demonstrated by measuring Cl, which evaporates not only as particles, but also as gaseous species (Figure 4D-4E). Indeed, thermodynamic calculations show that under oxidizing conditions CuCl2 is evaporated at about 450 &#176;C as Cl2 gas and as condensable species CuCl2, Cu3Cl3 and Cu4Cl4 (data not shown).
Furthermore, using the ICPMS without SMPS offers the possibility to measure the overall ICPMS signal originating either from gaseous or particulate species. Using this arrangement for the measurement of CuCl2 evaporation (Figure 4F), for example, shows that the stoichiometry between the evaporated Cu and Cl does not change during the heating period, because of the similar signal shape. In addition, the gaseous species can be exclusively measured by the same setup by mounting a particle filter at the RDD outlet.
In the measurement protocol there are two critical points. On the one hand, the lower ICPMS intensity curve, compared to PSDv at large particle diameter range (e.g. in Figure 2B), can be explained by the fact that the consideration of multiple particle charges is not yet implemented in the data evaluation procedure (ongoing work). While the single-charge correction gives a good correlation between SMPS and ICPMS data when measuring small particles (up to 200 nm), correction for multiple charges on large particles should be established and implemented to improve the quality of the resulting information for particles above 200 nm. Another explanation of this effect could be that the larger particles are not completely decomposed and ionized in the plasma.
The second critical point is the choice of the appropriate RDD dilution factor. Indeed, like the analysis of liquid samples, the ICPMS intensity level of the different isotopes depends on the corresponding sensitivity. The Cu signal for example is about three orders of magnitude higher than that of Cl. Therefore, an appropriate value of the aerosol dilution must be set considering the ICPMS sensitivity of the measured elements. This presents a limitation of multi-element analysis for aerosols. However, the aerosol dilution value can be changed during the same experiment if the process of aerosol generation is known. For example, the dilution factor can be lowered during the period when a low particle amount is generated. Nevertheless, feeding highly particle-loaded aerosols into the DMA should be avoided to protect the CPC and the ICPMS instrumentation. In summary, depending on the sampled aerosol, a compromise between RDD dilution, matrix loading, and ICPMS sensitivity to the isotopes of interest should be found. Moreover, the time resolution of the SMPS-ICPMS setup is limited by the SMPS scan duration, which is in the range of a few minutes. However, for a fixed or narrow range of particles size, the time resolution can be enhanced.
Developing quantification methods for the overall setup is still needed (ongoing work). For thermal processes, a TGA can be used as a tool for quantification25. The quantification of liquids or suspensions can be made using appropriate standard solutions. Furthermore, designing a recirculation concept for argon, operating the DMA with air and exchanging this to argon &#8211; e.g. by means of a gas exchange device26 &#8211; would allow the use of higher DMA voltage and hence an increase in the measured particle range. Finally automating the setting of the different parameters and merging the needs of SMPS and ICPMS into a single concept regarding the operating condition will reduce substantially the steps of the measurement protocol. These steps help to make the SMPS-ICPMS a powerful online setup for quantitative or qualitative analyses of different kinds of aerosols generated from liquid, suspension, or emission sources.

In numerous fields, the characterization of particles in aerosols and suspensions &#8211; including the determination of chemical composition and size distribution &#8211; is an important issue. A variety of analytical techniques to determine particle properties is used in different environmental, industrial and research applications, such as measuring/monitoring air-borne or combustion-emitted particles, characterizing synthesized engineered nano-objects, and studying their health and environmental effects.
Size information of gas-borne particles and particles in suspensions is conventionally analyzed by different particle sizers, such as an Aerodynamic Particle Sizer (APS), Dynamic Light Scattering devices (DLS), or a Scanning Mobility Particle Sizer (SMPS)1,2,3,4,5. The latter &#8211; well-established aerosol measurement tool &#8211; consists of two parts, a Differential Mobility Analyzer (DMA) and a Condensation Particle Counter (CPC). Both instruments are mounted in series. The first one allows the classification of the aerosol particles according to their mobility diameters in an air stream by varying the voltage between two electrodes6. In the CPC, entering nanoparticles act as condensation nuclei, &#34;large&#34; droplets are formed, and then they are optically counted6. The SMPS output data represent size-resolved number information about the measured particles and are given as Particle Size Distributions (PSD).
On the other hand, the chemical characterization of gas-borne particles and particles in suspensions is usually performed offline7. An appropriate collection and sample preparation procedure is required prior to the analysis. Such offline investigations usually include the application of a spectroscopic technique, such as Inductively Coupled Plasma Mass Spectrometry (ICPMS). This is an established method in element and trace-element analysis of liquid samples with very high sensitivity and low detection limits8. In ICPMS, an argon plasma serves to dry and decompose introduced samples into atomic ions. These are then classified according their mass to charge ratio (m/z) and finally counted in analog or pulsed mode. Besides liquid samples, this technique is also used for gas and particle analysis. For example, gas can be directly introduced into the ICPMS and analyzed9,10,11. In speciation analysis, a Gas Chromatograph (GC) coupled to ICPMS is used to separate and detect volatile compounds12. ICPMS was further developed to so-called single particle ICPMS (sp-ICPMS) in order to characterize monodisperse particles in suspensions13,14. Other surface and/or bulk analytical techniques are used either to achieve a complete characterization, and/or to gain more information about the particle characteristics. Imaging techniques, such as Scanning Electron Microscopy (SEM) and Transmission Electron Microscopy (TEM), are widely used for this purpose15,16,17.
To simultaneously gain time-resolved chemical and size information, two different analytical techniques, such as SMPS and a plasma spectrometric technique, can be combined in one setup18. This online measurement concept can avoid problems related to sample collection, preparation and offline analysis procedure. A short overview of previous attempts to develop such a combined setup was reported by Hess et al.19.
In this work, a detailed description of a combined SMPS-ICPMS measuring arrangement and procedure is given. A Rotating Disk Diluter (RDD) is used as the introduction interface. The development of this hyphenated technique and three application studies can be found in the literature19,20,21. Figures of merit given by Hess et al.20 show that the performance of the developed SMPS-ICPMS instrumentation is comparable to that of the separate state-of-the-art systems. This study is complementary to the previous publications19,20,21 and gives a laboratory practice describing how this setup can be used. Example applications on aerosols from two different sources are shortly described, to show the versatility of the coupled system.
Before describing the measurement protocol, it is worth summarizing the individual components and the coupling strategy of the hyphenated setup. A more detailed description can be found elsewhere19. The main components of the coupled setup are: an aerosol source, RDD, DMA, CPC, and ICPMS.
To generate dried aerosol particles from a suspension or liquid solution, an aerosol generator equipped with a nozzle and a silica gel drier is used. A detailed description can be found elsewhere19. To investigate thermal processes, a Thermogravimetric Analyzer TGA (or a tubular furnace) is utilized.
The RDD is used for the aerosol sample introduction22. It consists of a heatable steel block equipped with two channels, and a rotating disk featuring several cavities. The channels are flushed with dilution gas and raw aerosol from the aerosol source. Depending on the gas flows and the disk rotation speed, a certain amount of raw aerosol is added to the dilution gas, resulting in a defined dilution ratio. Argon is used as dilution gas, because of the low air tolerance of the ICPMS. However, the DMA voltage limit should be set lower than that of air-operated DMA, in order to avoid electric arcing. Since the flow of diluted sample aerosol at the RDD outlet can be precisely controlled independently of the raw aerosol flow, the RDD sampling concept can be used for different aerosol sources. A heated tube (up to 400 &#176;C) is installed between RDD and SMPS, to evaporate volatile particles, and/or to further dilute the aerosol. This step is needed to achieve good reproducibility when processing samples containing organic matter. However, this may also trigger chemical reactions. Pyrolysis, for instance, starts at much lower temperatures and may decompose not only particles but also induce some chemical reactions. The SMPS used in this work consists of a DMA tube (similar to long DMA; see Materials table), and a commercial CPC. Before entering the DMA, the diluted aerosol must pass a radioactive source, called an aerosol neutralizer, in order to establish a known charge equilibrium (assuming a Boltzmann charge distribution)6. The particles are then classified according to their mobility diameter by varying the voltage at given DMA sheath and aerosol gas flows. The flow split at the DMA outlet is done such that 30% of the aerosol are directed to the CPC, the other 70% to the ICPMS. The number concentration of the classified particles is determined by the CPC. The other aerosol portion is analyzed by a commercial ICPMS instrument, allowing the elemental analysis of the aerosol-loaded particles. Since no liquids are investigated, the conventional sample introduction system is removed and the DMA outlet is directly connected to the ICPMS. A second RDD and another air-operated commercial SMPS are used as reference instruments to validate the PSD measured by the SMPS-ICPMS coupled setup. The RDD-SMPS reference system is connected to the raw aerosol outlet of the RDD of the coupled system.

<table><tbody><tr><td>ICPMS</td><td>Agilent Technologies, USA</td><td>7700x</td><td>Inductively Coupled&lt;br/&gt; Plasma Mass Spectrometer</td></tr><tr><td>DMA tube</td><td></td><td></td><td>similar to 3081 long DMA&lt;br/&gt; from TSI</td></tr><tr><td>Aerosol Neutralizer</td><td>TSI Inc., USA</td><td></td><td>85Kr radiation source</td></tr><tr><td>CPC</td><td>TSI Inc., USA</td><td>3010</td><td>Condensation Particle&lt;br/&gt; Counter</td></tr><tr><td>RDD</td><td>Matter Aerosol AG, Switzerland</td><td>MD193E</td><td>Rotating Disk Diluter;</td></tr><tr><td>Evaporation Tube</td><td>Matter Aerosol AG, Switzerland</td><td>ASET 15-1</td><td>Heated Tube</td></tr><tr><td>Aerosol Generator</td><td>Topas GmbH, Germany</td><td>ATM 220</td><td>aerosol generator</td></tr><tr><td>Silica Gel Drier</td><td>Topas GmbH, Germany</td><td>DDU570/H</td><td>silica gel diffusion drier</td></tr><tr><td>TGA</td><td>Mettler-Toledo Internat. Inc., CH</td><td>TGA/DCS1</td><td>Thermogravimetric analyzer</td></tr><tr><td>Gilibrator 2</td><td>Sensidyne, USA</td><td></td><td>primary flow calibrator</td></tr><tr><td>MFC</td><td>Sierra Instruments Inc., USA</td><td>Smart-Trak 50</td><td>mass flow controller</td></tr><tr><td>MFC</td><td>Brooks Instrument, Netherlands</td><td>4850</td><td>mass flow controller</td></tr><tr><td>MFC</td><td>Bronkhorst AG, Netherlands</td><td>F-201C-FAC-33-V</td><td>mass flow controller</td></tr><tr><td>In-Line Filter</td><td>Headline Filters, UK</td><td>DIF-LN30</td><td>disposable in-line filter</td></tr><tr><td>HEPA Filter</td><td>MSA (Mine Safety Appliances), USA</td><td>H cartridge #95302</td><td>High-Efficiency Particulate&lt;br/&gt; Air&lt;br/&gt; &amp;nbsp;</td></tr><tr><td>Conductive tubing</td><td>Advanced Polymers Ltd&lt;br/&gt; Worthing, UK.</td><td></td><td>carbon impregnated silicone&lt;br/&gt; tubing, inner/outer&lt;br/&gt; diameters 6.0/12.0 mm</td></tr><tr><td>&lt;strong&gt;Name&lt;/strong&gt;</td><td>&lt;strong&gt;Company&lt;/strong&gt;</td><td>&lt;strong&gt;Catalog number&lt;/strong&gt;</td><td>&lt;strong&gt;Comments&lt;/strong&gt;</td></tr><tr><td>ZnO</td><td>Auer-Remy</td><td>5810MR, 1314-13-2</td><td>Nanopowder, 50 nm</td></tr><tr><td>NaCl</td><td>Merck</td><td>106406</td><td>Powder (&gt;99.99%)</td></tr><tr><td>CuCl&lt;sub&gt;2&lt;/sub&gt;</td><td>Merck</td><td>102733</td><td>Powder (&gt;99.0%)</td></tr><tr><td>Poly-Acrylic Acid</td><td>SigmaAldrich</td><td>535931</td><td>solution (50 wt. % in H&lt;sub&gt;2&lt;/sub&gt;O)</td></tr></tbody></table>

a practical guide on coupling a scanning mobility sizer and inductively coupled plasma mass spectrometer (smps-icpms)

A Practical Guide on Coupling a Scanning Mobility Sizer and Inductively Coupled Plasma Mass Spectrometer (SMPS-ICPMS)

A large variety of analytical methods are available to characterize particles in aerosols and suspensions. The choice of the appropriate technique depends on the properties to be determined. In many fields information about particle size and chemical composition are of great importance. While in aerosol techniques particle size distributions of gas-borne particles are determined online, their elemental composition is commonly analyzed offline after an appropriate sampling and preparation procedure. To obtain both types of information online and simultaneously, a hyphenated setup was recently developed, including a Scanning Mobility Particle Sizer (SMPS) and an Inductively Coupled Plasma Mass Spectrometer (ICPMS). This allows first to classify the particles with respect to their mobility diameter, and then to determine their number concentration and elemental composition in parallel. A Rotating Disk Diluter (RDD) is used as the introduction system, giving more flexibility regarding the use of different aerosol sources. In this work, a practical guide is provided describing the different steps for establishing this instrumentation, and how to use this analysis tool. The versatility of this hyphenated technique is demonstrated in example measurements on three different aerosols generated out of a) a salt solution, b) a suspension, and c) emitted by a thermal process.

In the first example, the setup is used as tool to measure online particles generated from a ZnO suspension (Figure 2). As can be seen in Figure 2A-2B, the PSDv appears shifted towards larger particles when compared to PSDn. Moreover, at large particle diameters, the ICPMS intensity curve lies slightly below the curve detected by SMPS. In the second example, the particles were generated from an aqueous NaCl solution (200 µg/mL) using the same aerosol generator (Figures 3A-3C). The ICPMS and SMPS signals do not show a substantial change with time, and the time-resolved signal of sodium correlates well to the PSDv during the entire measuring period. Unlike Zn in the previous example, Na has a relatively high ICPMS background signal, resulting in a noisier signal than that of the concentrations recorded by the SMPS. As in the ZnO suspension sample, the mode of the PSDn lies at a lower particle diameter than that of the PSDv. Since the generated particles are NaCl particles, the behavior of the Cl signal is like that of Na and correlates well with the volume-related SMPS data (data not shown).
In the last example, the results of the thermal treatment of a CuCl2 sample by using the TGA are presented. Figure 4A shows the PSDn recorded for particles down to 20 nm at the beginning of the TGA heating (at about 21 min on time axis, i.e. at the beginning of the 7th SMPS scan). Afterwards the particle concentration in PSDn reaches a steady state when the temperature is maintained constant and the particles cover a size range between 60 and 250 nm. A slight increase is observed in the particle size after the 11th SMPS scan (at about 30 min on time axis). Considering PSDv (Figure 4B), the contribution of the different particle sizes is quite different to that of PSDn, and with the PSDv becoming high mainly between 150 and 330 nm. The ICPMS signal of Cu shown in Figure 3C correlates well with PSDv. Figure 4D-4E shows the corrected and raw 35Cl intensity during the up and down scans, respectively. After the starting point of the heating period, beside the intensity corresponding to particles of chlorine species, constant Cl intensity covers the particle size range was measured (in the time interval 18 to 33 min, i.e. from the 7th to the 11th SMPS scan). This is due to the evaporation of Cl gaseous species. The chlorine particulates are recorded in the same size range as copper, namely in particles with diameters above 150 nm. Another experiment using the same sample (CuCl2) is performed without SMPS and by using only the TG-RDD-ICPMS setup. Here the ICPMS signal of the non-classified aerosol particles is measured (Figure 4F). Similar to the case of SMPS-ICPMS, an increase of both signals (Cl and Cu) in the last scans can be observed.
The results reported in this work demonstrate the versatile use of the coupled SMPS-ICPMS system with different aerosol sources. In the examples presented the correlation between the time-resolved ICPMS signal of Cu and PSDv is obvious. For an aerosol loaded with different particles, the contribution of each element in the overall PSDv is determined by the ICPMS signals. Moreover, the example of NaCl shows that keeping the experimental conditions constant results in a steady state time-resolved signal. The SMPS-ICPMS setup allows to monitor any change in elemental and/or size concentration of the generated aerosol. For instance, the higher signal of PSDn in the CuCl2 experiment (Figure 4C) may be caused by the abrupt start of the heating process. Meanwhile, the increase in SMPS and ICPMS signals during the final scans can be explained by the change of the temperature gradient of the CuCl2 sample with time, which changes the total amount of the material reaching the evaporation temperature. Finally, considering the SMPS output data, the concentration in PSDv is shifted towards larger particle size than in PSDn. This is because the signal is multiplied with the 3rd power of the particle diameter to convert PSDn to PSDv, resulting in stronger weighting of large particles in the volume than in the number regime.
<img alt="CPC and ICP-MS setup diagram for aerosol analysis showing flow paths and data measurement." src="/files/ftp_upload/55487/55487fig1.jpg" data-altupdatedat="1788250015000" data-alt="Figure 1"> 
Figure 1: Coupling Strategy for the Different Instrumental Parts in RDD-SMPS-ICPMS Setup. Nomenclature: Qsample: flow from the aerosol generator; Qdilut: RDD dilution argon flow, QRDD out: raw aerosol flow out of the RDD; Qpoly: flow of diluted polydisperse aerosol at the DMA inlet; Qsheath: DMA sheath gas flow; Qclass: flow of classified aerosol at the DMA outlet; QDMA exc: DMA gas excess flow; QCPC class: fraction of Qclass guided into the CPC; QCPC air: additional air flow for the CPC; QCPC in: total flow entering the CPC; QICP in: fraction of Qclass guided into the ICPMS; QXe: xenon flow; MFC: mass flow controller. <a href="http://cloudflare.jove.com/files/ftp_upload/55487/55487fig1large.jpg" target="_blank">Please click here to view a larger version of this figure.</a>
<img alt="Particle size distribution; graphs showing PSDn vs. dp for SMPS and ICPMS methods." src="/files/ftp_upload/55487/55487fig2.jpg" data-altupdatedat="1788250015000" data-alt="Figure 2"> 
Figure 2: SMPS-ICPMS Data of the ZnO Suspension. (A) Number-based PSD (PSDn), recorded by SMPS. (B) The corresponding volume-based PSD (PSDv) and corrected 66Zn signal, detected by ICPMS. The three signals are an average over 4 SMPS scans. <a href="http://cloudflare.jove.com/files/ftp_upload/55487/55487fig2large.jpg" target="_blank">Please click here to view a larger version of this figure.</a>
<img alt="Particle size distribution analysis; ICPMS, PSDv, PSDn; time-varying diameter charts; research data." src="/files/ftp_upload/55487/55487fig3.jpg" data-altupdatedat="1788250015000" data-alt="Figure 3"> 
Figure 3: SMPS-ICPMS Data of the Measurement of the NaCl Solution. (A) ICP corrected signal of 23Na. (B) PSDv. (C) Corresponding PSDn. The SMPS concentrations and ICPMS intensities are plotted as functions of diameter and time. <a href="http://cloudflare.jove.com/files/ftp_upload/55487/55487fig3large.jpg" target="_blank">Please click here to view a larger version of this figure.</a>
<img alt="Size-distribution diagrams and ICP graphs of particle diameter over time; PSDN, PSVD, ICP levels." src="/files/ftp_upload/55487/55487fig4.jpg" data-altupdatedat="1788250015000" data-alt="Figure 4"> 
Figure 4: SMPS-ICPMS Data from Measuring CuCl2 Evaporation by Using the TGA. (A) 2D plot of PSDn (B) 2D plot of PSDv. (C) 2D plot of 63Cu ICPMS signal. (D) 2D plot of 35Cl ICPMS signal. (E) Non-corrected raw 35Cl ICPMS signal vs. time. (F) ICPMS signal of 65Cu and 35Cl recorded during thermal treatment of CuCl2 by using TG-RDD-ICPMS setup (without SMPS). In both experiments (with and without SMPS) blank signals at 25 °C are measured for about 18 min (6 SMPS scans), before starting and maintaining the heating period (for 15 min) at 450 °C. The recording of SMPS-ICPMS signals was started at the same time as that of the TGA signals and was stopped 1 scan after switching it off (resulting in a total of 12 SMPS scans). <a href="http://cloudflare.jove.com/files/ftp_upload/55487/55487fig4large.jpg" target="_blank">Please click here to view a larger version of this figure.</a>
<table border="1" fo:keep-together.within-page="1" fo:keep-with-next.within-page="always">
	<tbody>
		<tr>
			<td>Parameter</td>
			<td>Value</td>
			<td>To be tuned</td>
		</tr>
		<tr>
			<td>Power</td>
			<td>1350 W</td>
			<td>yes</td>
		</tr>
		<tr>
			<td>ICP dilution gas (argon)</td>
			<td>0.58 L/min</td>
			<td>Yes</td>
		</tr>
		<tr>
			<td>Sampling depth</td>
			<td>8 mm</td>
			<td>Yes</td>
		</tr>
		<tr>
			<td>Collision gas</td>
			<td>2 mL/min</td>
			<td>Yes (for the same set of measurements don’t change this value after tuning it)  </td>
		</tr>
		<tr>
			<td>Integration time </td>
			<td>0.2 s per isotope</td>
			<td>Yes, if the ICP time resolution should be changed </td>
		</tr>
		<tr>
			<td>Xe flow</td>
			<td>4 mL/min</td>
			<td>No (to keep the same ICP sensitivity)</td>
		</tr>
	</tbody>
</table>
Table 1: Typical Setting of the Main ICPMS Parameters used for the RDD-SMPS-ICPMS Measurement of Aerosol Particles.

In this work a practical guide is provided, describing the different steps to establish the coupling of SMPS and ICPMS systems, and how to use them. Three descriptive examples are presented.

A large variety of analytical methods are available to characterize particles in aerosols and suspensions. The choice of the appropriate technique depends ...

The overall goal of this practical guide is to describe the different steps for coupling a scanning mobility particle sizer to an inductively coupled plasma mass spectrometer, and to explain how to use this analysis tool. The SMPS ICPMS instrumentation can help to answer questions in different environmental and technological applications, such as monitoring airborne or combustion emitted particles. We can now characterize synthesized engineered nano objects and study their fate.The main advantage of this coupling strategy is to gain information on the size and the chemical composition of particles, simultaneously and online, with a time resolution of a few minutes. Based on previous attempts to set up the SMPS ICPMS combination, we started to develop this technique for various aerosol sources using a rotating disc diluter as the introduction system. This visual demonstration described the main step of the coupling strategy of the two instruments, as well as the different settings.To couple the different instruments and to control the different gas flows, some modifications in the instrumental arrangements are needed. The main steps of the coupling concept are summarized here. Use conductive tubing with an inner diameter of 6.0 millimeters and an outer diameter of 12.0 millimeters to connect the different instrumental parts.Install the rotating disc diluter between the aerosol source and the differential mobility analyzer, or DMA, where the particle size classification takes place. Split the classified aerosol at the DMA outlet in two fractions, one will be aspirated by the condensation particle counter, or CPC, the other is guided towards the inductively coupled plasma mass spectrometer, or ICPMS. Use a mass flow controller and a HEPA filter to provide particle free dilution argon to the rotating disc diluter.Add another filter to the excess raw gas outlet of the diluter. Use an additional mass flow controller and filter to adjust the sheath gas flow introduced to the DMA. To adjust the DMA excess gas flow, mount a filter, mass flow controller, and vacuum pump, in series, at the DMA outlet.Finally, connect an additional mass flow controller and filter to add particle free air to the CPC as makeup flow to reduce the amount of classified aerosol consumed by the CPC. For an example of using an aerosol generator for a suspension, prepare zinc oxide suspension from a commercial zinc oxide nano powder and polyacrylic acid as a stabalizer for the nano-particles. Dilute the prepared suspension to obtain a zinc oxide concentration of approximately 30 micrograms per milliliter.Use the aerosol generator equipped with a nozzle and a silica gelled dryer to generate an aerosol from the particle suspension and to remove the water from the particles in the silica gel dryer. To do so, first fill the suspension or solution into the bottle and mount it on the aerosol generator. Then set the compressed air valve of the aerosol generator slightly above one bar.This results in an aerosol flow behind the diffusion dryer of approximately one liter per minute. Finally, connect the dryer outlet to the inlet of the rotating disc diluter. Mass flow controllers are calibrated to gas mass flows under standard conditions.Since volumetric flows are relevant for this type of measurements, all flows have to be manually verified, for example, by using a primary flow calibrator. First set the argon flow at the DMA sheath gas inlet to 3 liters per minute. Then set the rotating disc diluter temperature to 80 degrees celsius and set the evaporation tube temperature to 350 degrees celsius.The flow rate of the classified aerosol leaving the DMA results from all the other flows into and out the DMA. The desired classified aerosol flow can be defined by carefully adjusting the excess gas. Adjust the dilution argon flow manually to obtain 0.6 liters per minute as flow of the diluted sample at the outlet of the rotating disc diluter.Then, carefully adjust the excess gas mass flow controller to achieve a classified aerosol flow of 0.6 liters per minute, the same flow rate as that of the diluted poly dispersed aerosol at the DMA inlet. Next, place the flow calibrator between the DMA and the CPC. Adjust the CPC makeup airflow to reduce the flow rate of classified aerosol aspirated by the CPC to 0.18 liters per minute.Check the remaining flow of classified aerosol to ensure that 0.42 liters per minute are directed to the ICPMS. Next, calculate the dynamic viscosity and the mean free path of argon at ambient temperature and pressure. Enter both the values in the SMPS software.In the SMPS software, set the up and down scan durations of the DMA scanning cycle to 150 seconds and 30 seconds. Set the DMA maximum voltage to 4.5 kilovolts to prevent electric arching in the DMA, resulting in a covered particle size range of about 14 to 340 nanometers. Remove the conventional introduction system for liquid samples to directly introduce the dry aerosol into the ICPMS.Add a conductive tube between the respective port of the DMA outlet and the ICPMS. Maintain the xenon flow constant for all measurements. Tune the other parameters in the ICPMS software, including ICP dilution gas and sampling depth to achieve a fixed xenon intensity.Set the SMPS and ICPMS acquisition time to cover the desired total duration of the aerosol measurement. After setting the gas flows in the SMPS and the ICPMS parameters, run the measurement in the two instruments manually at the same time. Acquire blank signals during two scans of six minutes with the disc rotation speed set to zero.Then set the speed to the desired value. Here we show the ICPMS signal of zinc isotope 66. Additionally, here we see the volume based particle size distribution.This shows the strong correlation between the ICPMS and SMPS signals. Finally, see the text protocol for how to proceed with data analysis. Representative results of a zinc oxide suspension demonstrate that the volume based particle size distribution correlates well with the ICPMS signal.SMPS data are originally measured in the number concentration regime. The particle size distribution appears shifted towards larger particles when compared to the number based particle size distribution. This is because the conversion from number based to volume based results, and stronger weighting of large particles in the volume regime.The measurement of particles generated from an aqueous sodium chloride solution shows that keeping the experimental conditions constant results in steady state, time resolved, SMPS and ICPMS signals. The contribution of each element in the overall volume based particle size distribution is determined by the ICPMS signals. For the measurement of particles generated from the thermal treated copper chloride sample, by using a thermogravimetric analyzer, the correlation between the time resolved ICPMS signal of copper, and the volume based particle size distribution is obvious.Chlorine signals from both particulate species, which are recorded as peaks, and gaseous species, which are recorded as a constant signal covering the entire measured particle size range can be discriminated by SMPS ICPMS. While attempting this measurement procedure, it's important to remember that depending on the sample aerosol particle and the gas metrics are compromised between the RDD dilution and the ICPMS sensitivity to the isotope of interest has to be found. There's a trade off between a high number of monitored elements and their isotopes low detection limits, a high size resolution, and the wide covered particle size range on one side, and the short scan duration, or high temporal measuring resolution.After its development, this technique paved the way for researchers to explore nano objects regarding their fate, chemical composition, and size distribution. This is relevant to study gas quality as well as particle emissions, or exposure. We use this information for the further development of environmentally sound bioenergy and waste treatment technologies.After watching this video, you should have a good understanding of how to establish a robust coupling of SMPS and ICPMS instruments, and how to carry out an accurate measurement.

a-practical-guide-on-coupling-scanning-mobility-sizer-inductively

Research

JoVE Journal

Chemistry

We present a discrete droplet sample introduction system for inductively coupled plasma mass spectrometry (ICPMS). It is based on a cheap and disposable microfluidic chip that generates highly monodisperse droplets in a size range of 40−60 µm at frequencies from 90 to 7,000 Hz.

A Microfluidic Chip for ICPMS Sample Introduction

Integration of microalgal cultivation with industrial flue gas will ultimately introduce heavy metals and other inorganic compounds into the growth media. This study presents a procedure used to determine the end fate and impact of heavy metals and inorganic contaminants on the growth of Nannochloropsis salina grown in photobioreactors.

Quantification of Heavy Metals and Other Inorganic Contaminants on the Productivity of Microalgae

Size exclusion chromatography hyphenated with inductively coupled plasma - mass spectrometry (ICP-MS) is a powerful tool to measure changes in the abundance of metalloproteins directly from biological samples. Here we describe a set of metalloprotein standards used to estimate molecular mass and the amount of metal associated with unknown proteins.

Standards for Quantitative Metalloproteomic Analysis Using Size Exclusion ICP-MS

This iron redox speciation method is based on capillary electrophoresis-inductively coupled plasma mass spectrometry with sample stacking combined with short analysis in one run. The method quickly analyzes and provides low limits of quantification for iron redox species across a diverse range of tissues and biofluid samples.

Setup of Capillary Electrophoresis-Inductively Coupled Plasma Mass Spectrometry (CE-ICP-MS) for Quantification of Iron Redox Species (Fe(II), Fe(III))

Ion mobility spectrometry (IMS) is an interesting complement to mass spectrometry for the characterization of biomolecules, notably because it is sensitive to isomerism. This protocol describes a tandem IMS (IMS/IMS) experiment, which allows the isolation of a molecule and the generation of the mobility profiles of its fragments.

Using a Cyclic Ion Mobility Spectrometer for Tandem Ion Mobility Experiments

This protocol presents a validated liquid chromatography-ion mobility-high resolution mass spectrometry method to determine the presence of ergot alkaloids in food in compliance with the recently released Commission Regulation (EU) 2023/915.

Detection of Regulated Ergot Alkaloids in Food Matrices by Liquid Chromatography-Trapped Ion Mobility Spectrometry-Time-of-Flight Mass Spectrometry

Untargeted metabolomics provides a hypothesis generating snapshot of a metabolic profile.  This protocol will demonstrate the extraction and analysis of metabolites from cells, serum, or tissue.  A range of metabolites are surveyed using liquid-liquid phase extraction, microflow ultraperformance liquid chromatography/high-resolution mass spectrometry (UPLC-HRMS) coupled to differential analysis software.

Untargeted Metabolomics from Biological Sources Using Ultraperformance Liquid Chromatography-High Resolution Mass Spectrometry (UPLC-HRMS)

Dynamic measurement of chloride ions is presented. Transition time of an Ag/AgCl electrode, during a chronopotentiometric technique, can give the concentration of chloride ions in electrolyte. This method does not require a stable conventional reference electrode.

Dynamic Electrochemical Measurement of Chloride Ions

This paper presents a protocol for the visualization of gaseous streams of an ambient ionization source using schlieren photography and mass spectrometry.

Visualization of Ambient Mass Spectrometry with the Use of Schlieren Photography

A protocol for characterizing chemical composition of exhaled breath in real time by using secondary nanoelectrospray ionization coupled to high resolution mass spectrometry is demonstrated.

Real-time Breath Analysis by Using Secondary Nanoelectrospray Ionization Coupled to High Resolution Mass Spectrometry

Learn to couple SMPS with ICPMS for real-time aerosol analysis. This method enables simultaneous measurement of particle size and chemical composition using a rotating disc diluter system.

A Practical Guide on Coupling a Scanning Mobility Sizer and Inductively Coupled Plasma Mass Spectrometer (SMPS-ICPMS)