Name: Synthesis of Multi-walled Carbon Nanotubes Modified with Silver Nanoparticles and Evaluation of Their Antibacterial Activities and Cytotoxic Properties (Video) | JoVE Journal
Uploaded: 2018-05-10T12:30:00.000+00:00
Duration: 11 min 19 s
Description: Learn to synthesize antibacterial nanocomplexes using multiwalled carbon nanotubes and silver nanoparticles. This method evaluates antimicrobial efficacy and cytotoxicity for safe medical applications.

ai_agent_IP

ai_agent

maintenance

instantTrialDurationMinutes

isBiopharma

enableNewMyJoveSectionDesign

educationFeatures

seoMetaApi

ai_copilot_institution_blacklist

ai_chat_institution_blacklist

freeAccessWindow

ssoRoleCapture

scheduledMaintenanceBanner

joveLabsFeatures

disable_autoplay_for_bots

extended_trial_duration

5 minutes

This study was supported by Chung-Ang University Research Grants (2016) and by the Nano-Material Technology Development Program through the National Research Foundation of Korea(NRF) funded by the Ministry of Science and ICT (No. 2017M3A7B8061942).

1. MWCNT Oxidation
<ol>
	<li>Measure 30 - 50 mg of MWCNT into a 50-mL vial. Slowly add 8 mL of a H2SO4:HNO3 solution (90% initial concentration, 3:1 vol/vol) by pipette with 1 mL pipette tips. 
	CAUTION: This preparation must be conducted in a chemical fume hood.
	<ol>
		<li>Allow 30 min for the exothermic reaction to complete.</li>
	</ol>
	</li>
	<li>Sonicate the solution at 60 - 80 &#176;C and 160 W for 1 h until MWCNT settles at the bottom of the vial. 
	CAUTION: The water level in the sonicator should be lower than the top of vial so that water will not be introduced into the vial.</li>
	<li>Transfer the solution to a centrifuge tube.
	<ol>
		<li>With a micropipette, add 30 mL of distilled water dropwise to the MWCNT-COOH solution. 
		CAUTION: A strong exothermic reaction occurs during addition of distilled water. Add distilled water slowly and allow time for cooling.</li>
	</ol>
	</li>
	<li>Centrifuge the MWCNT-COOH solution at 12,000 x g and room temperature for 15 min. 
	CAUTION: When operating a centrifuge, ensure the centrifuge remains balanced by placing a tube with the same weight opposite the sample tube.</li>
	<li>Remove the supernatant with a pipette and 1 mL pipette tip. Add 5 mL of ethanol with a pipette and 1 mL pipette tip. Rinse the walls of the vial with additional pipetted ethanol. Centrifuge the solution at 12,000 x g and room temperature for 15 min.
	<ol>
		<li>Determine pH of supernatant with pH paper. Repeat washing and centrifuging until the supernatant pH is neutral.</li>
	</ol>
	</li>
	<li>Remove all supernatant. Add 1 mL of distilled water to precipitate and disperse MWCNT-COOH evenly in solution. Freeze-dry solution at -60 &#176;C under vacuum until dry.</li>
</ol>
2. Silver Nanoparticle Deposition on MWCNTs
<ol>
	<li>Place 10 mg of MWCNT-COOH in a 50-mL conical tube and dilute with 30 mL of distilled water. Sonicate solution at 60 &#176;C and 160 W for 1 h.</li>
	<li>Place 6 mL of 0.1 N AgNO3 in a 50-mL conical tube and dilute with 18 mL of distilled water. Sonicate solution at 60 &#176;C and 160 W for 1 h. 
	CAUTION: Add AgNO3 in proportion to the total mass of MWCNTs such that the total mass of Ag does not exceed 20%.</li>
	<li>Add the AgNO3 solution dropwise to the MWCNTs solution with a pipette and 1 mL pipette tip while sonicating the mixture at 60 &#176;C and 160 W. Continue sonicating for 1 h after adding the AgNO3.</li>
	<li>Centrifuge the solution at 12,000 x g and room temperature for 15 min and remove the supernatant. Centrifuge the solution and remove the supernatant two additional times.</li>
	<li>Add 1 mL of distilled water to the Ag-MWCNTs mixture and disperse the precipitate evenly in the solution. Add 5 mL of ethanol and allow the reaction to proceed at room temperature for 1 h.</li>
	<li>Centrifuge the solution at 12,000 x g and room temperature for 15 min and remove the supernatant.</li>
	<li>Determine pH of supernatant with pH paper. Repeat washing and centrifuging until supernatant pH is neutral.</li>
	<li>Add 1 mL of distilled water to Ag-MWCNTs and disperse evenly in solution. Freeze-dry the solution at -70 &#176;C under vacuum for 24 h.</li>
</ol>
3. Zone of Inhibition Test
<ol>
	<li>Mix 18.12 g of R2A agar and 1 L of distilled water in a flask. Sterilize the mixture in an autoclave at 121 &#176;C for 15 min.</li>
	<li>Allow gel to cool at room temperature. Place 10 mL of gel in Petri dishes prior to hardening to prepare the solid medium.</li>
	<li>Place 100 &#181;L of bacteria on the solid medium. Spread the bacteria on the solid medium using a spreader. 
	CAUTION: This procedure must be conducted in a chemical fume hood lit with an alcohol lamp.</li>
	<li>Incubate the dishes at 30 &#176;C for 48 h.</li>
	<li>Mix 3.12 g of R2A broth with 1 L of distilled water in a flask. Sterilize the mixture in an autoclave at 121 &#176;C for 15 min.</li>
	<li>Transfer the grown colonies to a liquid medium using a loop and needle and incubate in an incubator at 180 rpm and 30 &#176;C.</li>
	<li>Record the OD (Optical Density) value by UV spectrophotometry at 600 nm on an hourly basis to measure bacterial growth. 
	NOTE: R2A agar was used in this test, rather than the standard Mueller-Hinton agar, because R2A is the preferred agar for growth of Methylobacterium spp.</li>
	<li>Place 10 mL of prepared R2A agar in a Petri dish to prepare a bottom agar.
	<ol>
		<li>Mix 3.12 g of R2A broth and 8 g of agar with 1 L of distilled water. Sterilize the mixture in an autoclave at 121 &#176;C for 15 min. Place 10 mL of this gel on the bottom agar.</li>
	</ol>
	</li>
	<li>Load 50 &#181;L of Ag-MWCNTs solution on sterile paper disc with a micropipette.
	<ol>
		<li>Dry and sterilize Ag-MWCNTs sample in a vacuum chamber under UV light for 30 min.</li>
	</ol>
	</li>
	<li>Place Ag-MWCNTs sample on agar.</li>
	<li>Incubate the agar plate at 30 &#176;C for 48 h.</li>
	<li>Measure zone of inhibition12. 
	NOTE: Instructions for software used are included in the references.</li>
</ol>
4. Antibacterial Test
<ol>
	<li>Repeat steps 3.1 to 3.7 to prepare bacterial culture.</li>
	<li>At maximum OD, inoculate 100 &#181;L of bacteria into 3 mL of fresh liquid medium with a pipette and 100-&#181;L micro pipette tip.</li>
	<li>Prepare five 50 &#181;L samples of the control solution in 15-mL conical tubes. Add the following to each tube: 1) methanol; 2) 1000 &#181;g/mL MWCNT-COOH; 3) 50 &#181;g/mL Ag-MWCNTs; 4) 40 &#181;g/mL Ag-MWMWCNTs; 5) 30 &#181;g/mL Ag-MWCNTs.</li>
	<li>Incubate at 180 rpm and 30 &#176;C until the control is maximally active as determined by UV spectrophotometry as described above.</li>
	<li>Measure the OD value of each sample and calculate the MIC concentration. The OD value is directly related to the number of bacterial cells in the sample broth.</li>
	<li>Spread the cultured bacteria on a solid medium with a spreader.</li>
	<li>Incubate the dish at 30 &#176;C for 48 h.</li>
	<li>Count bacterial colonies and the measure CFU values to determine antibacterial activity12. 
	NOTE: Instructions for software used are included in the references.</li>
</ol>
5. Viability Assay
<ol>
	<li>After removing the culture cells from incubator, suction the medium and wash three times with a dropwise wash of 5 mL of PBS.</li>
	<li>Add 1 mL of trypsin-EDTA in PBS to the washed cell and suction after 1 min.
	<ol>
		<li>Tap the plate to remove stuck cells.</li>
	</ol>
	</li>
	<li>Add 5 mL of DMEM (Dulbecco&#39;s Modified Eagle&#39;s Medium) and then remove the cells. Centrifuge the samples at 200 x g for 3 min and remove the supernatant.
	<ol>
		<li>Add 1 mL of DPBS and mix.</li>
		<li>Count cells in 10 &#181;L of the solution with an automated cell-counting machine. 
		NOTE: Instructions for cell-counting machine used are included in the references13.</li>
	</ol>
	</li>
	<li>Place 1 &#215; 105 of AML12 cells per well in a six-well plate containing DMEM solution. The medium contains 10% (v/v) fetal bovine serum and 1% sterile antibiotic.</li>
	<li>Incubate plate for 8&#160;- 12 h at 37 &#176;C in a 5% CO2/95% air environment.</li>
	<li>Suction the supernatant from wells with an aspirator.
	<ol>
		<li>Add each sample comprised of control, NMS-DMSO (dimethyl sulfoxide) and 30-40 &#181;g/mL Ag-MWCNT to 1 mL of DMEM.</li>
		<li>Incubate at 37 &#176;C in a 5% CO2/95% air environment for 8 h.</li>
	</ol>
	</li>
	<li>Remove supernatant and wash samples with 5 mL of PBS.</li>
	<li>Add 1 mL of prepared live/dead kit (20 &#181;L of 2 mM EthD-1 with 5 &#181;L of 4 mM calcein AM in DMSO in 10 mL of PBS) dropwise to the cell.</li>
	<li>Incubate at room temperature for 30 - 45 min or 37 &#176;C for 10 min. Measure fluorescence with standard fluorescence microscopy at 100X or 300X.</li>
</ol>
6. Trypan Blue Assay
<ol>
	<li>Prepare samples according to steps 5.1 through 5.6.2 above.</li>
	<li>Remove supernatant.</li>
	<li>Wash plate with 1 mL of 1x DPBS and decant.</li>
	<li>Add 1 mL of trypsin to plate and incubate for 3 min to detach the cells from culture. Use cell culture medium to wash plate and collect cells. Place collected cells in a 15-mL tube.</li>
	<li>Centrifuge tube at 200 x g and 4 &#176;C for 3 min.</li>
	<li>Discard supernatant. Add 1 mL of fresh medium to cell pellet and re-disperse the cells.</li>
	<li>Add 10 &#181;L of trypan blue with 10 &#181;L of dispersed cells and count the cells with an automated cell-counting machine. 
	NOTE: Instructions for cell-counting machine used are included in the references.</li>
</ol>

<ol><li>Löndahl, J. Physical and Biological Properties of Bioaerosols. <a target="_blank" href="http://scholar.google.com/scholar?hl=en&safe=off&q=author%3aL%C3%B6ndahl%2C+J+%22Bioaerosol+Detection+Technologies%22">Bioaerosol Detection Technologies</a>. , Springer. 33-48 (2014).</li>
<li>Jennings, S., Moran, A., Carroll, C. <a target="_blank" href="https://www.researchgate.net/publication/251238513_Bioaerosols_and_Biofilms">Bioaerosols and biofilms.</a> Biofilms in medicine, industry and environmental biotechnology. , IWA, London. 160-178 (2003).</li>
<li>Flemming, H. -C., Wingender, J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((The+biofilm+matrix%5BTitle%5D)+AND+%22Nature+Reviews+Microbiology%22%5BJournal%5D)">The biofilm matrix.</a> Nature Reviews Microbiology. 8 (9), 623-633 (2010).</li>
<li>Lewis, K. <a target="_blank" href="https://www.ncbi.nlm.nih.gov/pmc/articles/PMC90417/">Riddle of biofilm resistance.</a> Antimicrobial agents and chemotherapy. 45 (4), 999-1007 (2001).</li>
<li>Doronina, N. V., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Methylobacterium+suomiense+sp.+nov.+and+Methylobacterium+lusitanum+sp.+nov.%2C+aerobic%2C+pink-pigmented%2C+facultatively+methylotrophic+bacteria%5BTitle%5D)+AND+%22International+Journal+of+Systematic+and+Evolutionary+Microbiology%22%5BJournal%5D)">Methylobacterium suomiense sp. nov. and Methylobacterium lusitanum sp. nov., aerobic, pink-pigmented, facultatively methylotrophic bacteria.</a> International Journal of Systematic and Evolutionary Microbiology. 52 (3), 773-776 (2002).</li>
<li>Seo, Y., et al. <a target="_blank" href="https://www.ncbi.nlm.nih.gov/pmc/articles/PMC4200021/">Antibacterial activity and cytotoxicity of multiwalled carbon nanotubes decorated with silver nanoparticles.</a> International Journal of Nanomedicine. 9, 4621-4629 (2014).</li>
<li>Chen, X., Schluesener, H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Nanosilver%3A+a+nanoproduct+in+medical+application%5BTitle%5D)+AND+%22Toxicologyletters%22%5BJournal%5D)">Nanosilver: a nanoproduct in medical application.</a> Toxicologyletters. 176 (1), 1-12 (2008).</li>
<li>Singh, M., et al. <a target="_blank" href="https://www.researchgate.net/publication/256463087_Nanotechnology_in_medicine_and_antibacterial_effect_of_silver_nanoparticles">Nanotechnology in medicine and antibacterial effect of silver nanoparticles.</a> Digest Journal of Nanomaterials and Biostructures. 3 (3), 115-122 (2008).</li>
<li>Morones, J. R., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((The+bactericidal+effect+of+silver+nanoparticles%5BTitle%5D)+AND+%22Nanotechnology%22%5BJournal%5D)">The bactericidal effect of silver nanoparticles.</a> Nanotechnology. 16 (10), 2346(2005).</li>
<li>Martinez-Castanon, G., et al. <a target="_blank" href="https://www.researchgate.net/publication/225152132_Synthesis_and_antibacterial_activity_of_silver_nanoparticles_with_different_sizes">Synthesis and antibacterial activity of silver nanoparticles with different sizes.</a> Journal of Nanoparticle Research. 10 (8), 1343-1348 (2008).</li>
<li>Lok, C. -N., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Silver+nanoparticles%3A+partial+oxidation+and+antibacterial+activities%5BTitle%5D)+AND+%22JBIC+Journal+of+Biological+Inorganic+Chemistry%22%5BJournal%5D)">Silver nanoparticles: partial oxidation and antibacterial activities.</a> JBIC Journal of Biological Inorganic Chemistry. 12 (4), 527-534 (2007).</li>
<li>Ferreira, T., Rasband, W. ImageJ User Guide Home Page. , Available from:
 <a target="_blank" href="http://imageJ.nih.gov/ij/docs/guide">http://imageJ.nih.gov/ij/docs/guide</a> (2010).</li>
<li>NanoEnTek Inc. Juli Br User Guide. , Hwaseong, Korea. Available from:
 <a target="_blank" href="http://www.nanoentek.com/upload/product/11/JuLI%20Br_User%20manual%20(V.1.6).pdf">http://www.nanoentek.com/upload/product/11/JuLI%20Br_User%20manual%20(V.1.6).pdf</a> (2012).</li>
</ol>

The authors have nothing to disclose.

Here, we report a simple method for the preparation of MWCNTs with deposited Ag nanoparticles. This silver-containing nanomaterial demonstrates substantial antibacterial activity and minimal potential for uncontrolled absorption of silver nanoparticles in the body. We demonstrate that 30 &#181;g/mL of synthesized Ag-MWCNTs is an effective level of antibacterial activity against Methylobacterium spp. with negligible cytotoxicity to mammalian liver cells. Though additional improvements and biosafety assessments fo...

The ultimate goal of this study is to make environmentally friendly antibacterial nanomaterials that can inhibit the growth of bacteria that form biofilms. These antibacterial nanomaterials have the potential to overcome the toxicity and antibiotic resistance problems of commonly used chemicals or antibiotic chemical compounds. A biofilm is a hydrated extracellular polymeric substance (EPS) that is composed of polysaccharides, proteins, nucleic acids, and lipids1,2. Biofilms prevent the intrusion of foreign substances and help bacteria grow vigorously3,4. Biofilms cause odor and chronic infectious diseases5,6. Methylobacterium spp., for example, grows by adhering to places where water is always present or where it is difficult to ensure bacterial eradication on a continual basis, such as air conditioner heat exchangers, shower rooms, and medical devices. These types of biofilms cause odor and chronic infectious diseases5,6.
Typically, chemicals or antibiotic chemical compounds are used to inhibit the growth of bacteria that form biofilms. The emergence of antibiotic resistant bacteria and concerns about in vivo safety of chemicals are driving the need to develop new materials to prevent the formation of biofilms and to inhibit the growth of bacteria.
In this study, antimicrobial nanomaterials are synthesized that are free from antibiotic resistance and toxicity. Silver is a well-known antimicrobial substance, and recent developments in nanoscience and nanotechnology have led to active research into the antimicrobial effects of metal nanoparticles7,8. Recent studies have reported that the small size and high surface-to-volume ratio of the nanoparticles result in increased antibacterial activity9,10,11.
The nanomaterials presented herein combine silver nanoparticles with increased antimicrobial properties and carbon nanotubes with a high aspect ratio, thereby increasing the surface area per unit volume. The fabricated silver nanoparticle-carbon nanotube composite exhibits substantial antimicrobial properties and minimal toxicity to human and animal cells. The synthetic processes in previous studies use hazardous reducing agents such as NaBH4, formamide, dimethylformamide, and hydrazine. The process is complicated, dangerous, and time-consuming. The synthetic process reported here uses ethanol as a significantly less hazardous reducing agent.
The inhibition zone and minimum bactericidal concentration (MBC) for the Ag-MWCNTs were measured; Live/Dead and Trypan Blue assays were used to measure toxicity and antibacterial properties. Minimum inhibitory concentration (MIC) and mitochondrial toxicity (MTT) assays were not performed due to the unusual color of the carbon nanotubes which would have interfered with the assays. Finally, the minimum concentration to prevent the growth of Methylobacterium spp. without affecting mammalian cells was determined.

<table><tbody><tr><td>0.1 N silver nitrate</td><td>SIGMA-ALDRICH</td><td>1090811000</td><td></td></tr><tr><td>Carbon nanotube, multi-walled</td><td>Tokyo Chemical Industry Co., LTD</td><td>308068-56-6</td><td></td></tr><tr><td>R2A agar</td><td>MBcell</td><td>MB-R1129</td><td></td></tr><tr><td>R2A broth</td><td>MBcell</td><td>MB-R2230</td><td></td></tr><tr><td>&lt;em&gt;Methylobacterium spp.&lt;/em&gt;</td><td>KCTC</td><td>12618</td><td>from Korea Collection for Type Cultures Daejeon Korea 12618, Daejon, Korea</td></tr><tr><td>LIVE/DEAD Cell imaging Kit</td><td>ThermoFisher SCIENTIFIC</td><td>R37601</td><td></td></tr><tr><td>AML12</td><td></td><td></td><td>from Chungnam University, Dajeon, Korea</td></tr><tr><td>human PBMC</td><td>ATCC</td><td>PCS-800-011</td><td></td></tr><tr><td>TEM</td><td>JEOL</td><td>JEM-2100F</td><td></td></tr><tr><td>XRD</td><td>Rigaku</td><td>D/MAX 2500</td><td>Cu K photon source (40&lt;em&gt;k&lt;/em&gt;V, 100mA)</td></tr><tr><td>JuLI Br</td><td>NanoEnTek</td><td>JULI-BRSC&amp;nbsp;</td><td></td></tr></tbody></table>

synthesis of multi-walled carbon nanotubes modified with silver nanoparticles and evaluation of their antibacterial activities and cytotoxic properties

Synthesis of Multi-walled Carbon Nanotubes Modified with Silver Nanoparticles and Evaluation of Their Antibacterial Activities and Cytotoxic Properties

In this study, multi-walled carbon nanotubes (MWCNTs) were treated with an aqueous sulfuric acid solution to form an oxygen-based functional group. Silver MWCNTs were prepared by the reductive deposition of silver from an aqueous solution of AgNO3 on the oxidized MWCNTs. Given the unique color of the CNTs, it was not possible to apply them to the minimum inhibitory concentration or mitochondrial toxicity assays to evaluate the toxicity and antibacterial properties, since they would interfere with the assays. The inhibition zone and minimum bactericidal concentration for the Ag-MWCNTs were measured and Live/Dead and Trypan Blue assays were used to measure the toxicity and antibacterial properties without interfering with the color of the CNTs.

Transmission Electron Microscopy (TEM) images confirm the formation of Ag-MWCNTs (Figure 1A and 1B). Their successful synthesis was confirmed by the change in surface charge. The size of the Ag particles deposited on the MWCNTs was calculated (Figure 1C). The average particle size was approximately 3.83 nm. The XRD pattern of the as-synthesized Ag-MWCNTs is shown in Figure 1D. The pe...

In this study, antimicrobial nanomaterials were synthesized by acidic oxidation of multiwalled carbon nanotubes and subsequent reductive deposition of silver nanoparticles. Antimicrobial activity and cytotoxicity tests were performed with the as-prepared nanomaterials.

In this study, multi-walled carbon nanotubes (MWCNTs) were treated with an aqueous sulfuric acid solution to form an oxygen-based functional group. Silver ...

synthesis-multi-walled-carbon-nanotubes-modified-with-silver

Research

JoVE Journal

Bioengineering

Tangential flow ultrafiltration (TFU) is a recirculation method used for the weight-based separation of biosamples. TFU was adapted to size-select (1-20 nm diameter) and highly concentrate a large volume of polydisperse silver nanoparticles (4 L of 15.2 μg ml-1 down to 4 ml of 8,539.9 μg ml-1) with minimal aggregation.

Tangential Flow Ultrafiltration: A  &ldquo;Green&rdquo; Method for the Size Selection and Concentration of Colloidal Silver Nanoparticles

Take tubes with a medium containing a nanoparticle composite, engineered from a combination of transition metals and carbon.Introduce antibiotic-resistant Gram-positive and Gram-negative pathogenic bacteria into separate tubes as test samples.Include untreated bacteria as a negative control and antibiotic-treated bacteria as a positive control.Incubate the samples with shaking.In Gram-negative bacteria, the porous outer membrane and thin peptidoglycan layer facilitate nanoparticle entry,...

Assessment of the Antimicrobial Activity of a Nanoparticle Composite Against Pathogenic Bacteria

We discussed the synthesis of individual graphitic nanocups using a series of techniques including chemical vapor deposition, acid oxidation and probe-tip sonication. By citrate reduction of HAuCl4, the graphitic nanocups were effectively corked with gold nanoparticles due to the chemically reactive edges of the cups.

Synthesis and Functionalization of Nitrogen-doped Carbon Nanotube Cups with Gold Nanoparticles as Cork Stoppers

Silver nanowires can simultaneously transport electrons and optical information in the form of surface plasmons. A procedure is described here to realize such a shared circuitry and the limitations at propagating both information carriers are evaluated.

Evaluating Plasmonic Transport in Current-carrying Silver Nanowires

We report on a smart application of carbon nanotubes for kinetic stabilization of lipid particles that contain self-assembled nanostructures in their cores. The preparation of lipid particles requires rather low concentrations of carbon nanotubes permitting their use in biomedical applications such as drug delivery.

Facile Preparation of Internally Self-assembled Lipid Particles Stabilized by Carbon Nanotubes

The antimicrobial properties of metals such as copper and silver have been recognized for centuries. This protocol describes pulsed laser-ablation in liquids, a method of synthesizing metal nanoparticles that provides the ability to fine tune the properties of these nanoparticles to optimize their antimicrobial effects.

Production of Metal Nanoparticles by Pulsed Laser-ablation in Liquids: A Tool for Studying the Antibacterial Properties of Nanoparticles

This article describes in detail a method based on silver nanoparticles for ameliorating biliary atresia syndrome in an experimental biliary atresia mouse model. A solid understanding of the reagent preparation process and the neonatal mouse injection technique will help familiarize researchers with the method used in neonatal mouse model studies.

A Silver Nanoparticle Method for Ameliorating Biliary Atresia Syndrome in Mice

We introduce four methods to evaluate the antimicrobial activities of nanoparticles and nanostructured surfaces using in vitro techniques. These methods can be adapted to study the interactions of different nanoparticles and nanostructured surfaces with a broad range of microbial species.

Evaluation of Antimicrobial Activities of Nanoparticles and Nanostructured Surfaces In Vitro

Presented here is a protocol for using silver nanoparticles to effectively ameliorate the acute symptoms of type II collagenase-induced osteoarthritis mice, including synovial inflammation, synovial hyperplasia, vascular hyperplasia, etc.

Ameliorating Osteoarthritis in Mice Using Silver Nanoparticles

In this study, zinc oxide nanoparticles were synthesized using a precipitation method. The antibacterial effect of the synthesized particles was tested against multidrug-resistant methicillin-resistant Staphylococcus aureus (MRSA) and Pseudomonas aeruginosa bacterial strains.

Preparation of Zinc Oxide Nanoparticles and the Evaluation of their Antibacterial Effects

Herein, we introduce graphene oxide/copper (GO/Cu) nanocomposites as an antibacterial nanomaterial. The antibacterial effectiveness of the GO/Cu nanocomposites was evaluated against both antibiotic-resistant gram-positive and gram-negative bacteria.

Fabrication of Antibacterial Graphene Oxide/Copper Nanocomposites

Learn to synthesize antibacterial nanocomplexes using multiwalled carbon nanotubes and silver nanoparticles. This method evaluates antimicrobial efficacy and cytotoxicity for safe medical applications.

Synthesis of Multi-walled Carbon Nanotubes Modified with Silver Nanoparticles and Evaluation of Their Antibacterial Activities and Cytotoxic Properties (Video) | JoVE Journal

Synthesis of Multi-walled Carbon Nanotubes Modified with Silver Nanoparticles and Evaluation of Their Antibacterial Activities and Cytotoxic Properties