Name: Préparation de mousses de poly (adipate-co-téréphtalate de butylène) renforcées de fibres de carbone et de fibres de bambou par moussage au dioxyde de carbone supercritique (Vidéo) | JoVE Journal
Uploaded: 2025-10-10T13:35:00.000+00:00
Duration: 7 min 56 s
Description: Découvrez la fabrication de mousses PBAT renforcées par fibres de carbone et de bambou via moussage au CO2 supercritique. Cette méthode améliore l'anti-rétrécissement, la légèreté et la résistance mécanique pour des applications durables.

ai_agent_IP

ai_agent

maintenance

instantTrialDurationMinutes

isBiopharma

enableNewMyJoveSectionDesign

educationFeatures

seoMetaApi

ai_copilot_institution_blacklist

ai_chat_institution_blacklist

freeAccessWindow

ssoRoleCapture

scheduledMaintenanceBanner

joveLabsFeatures

disable_autoplay_for_bots

extended_trial_duration

5 minutes

playerTrialDesktop

<ol><li>Xu, X., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Material+performance%2C+manufacturing+methods%2C+and+engineering+applications+in+aviation+of+carbon+fiber+reinforced+polymers%3A+A+comprehensive+review%5BTitle%5D)+AND+%22Thin+Wall+Struct%22%5BJournal%5D)">Material performance, manufacturing methods, and engineering applications in aviation of carbon fiber reinforced polymers: A comprehensive review.</a> Thin Wall Struct. 209, 112899(2025).</li>
<li>Wang, Z., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Fabrication+of+biodegradable+poly%28butylene+adipate-co-butylene+terephthalate%29+bead+foams+through+solid+utilization+of+chitin+and+controllable+incorporation+of+porous+structure%5BTitle%5D)+AND+%22Colloids+Surf+A+Physicochem+Eng+Asp%22%5BJournal%5D)">Fabrication of biodegradable poly(butylene adipate-co-butylene terephthalate) bead foams through solid utilization of chitin and controllable incorporation of porous structure.</a> Colloids Surf A Physicochem Eng Asp. 693, 134105(2024).</li>
<li>Wang, J., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Strong+and+thermally+insulating+polylactic+acid%2Fglass+fiber+composite+foam+fabricated+by+supercritical+carbon+dioxide+foaming%5BTitle%5D)+AND+%22Int+J+Biol+Macromol%22%5BJournal%5D)">Strong and thermally insulating polylactic acid/glass fiber composite foam fabricated by supercritical carbon dioxide foaming.</a> Int J Biol Macromol. 138, 144-155 (2019).</li>
<li>Li, J., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Environmentally-friendly%2C+sustainable+ScCO2-assisted+fabrication+of+poly%28lactic+acid%29%2Framie+fiber+composite+foams%5BTitle%5D)+AND+%22J+Clean+Prod%22%5BJournal%5D)">Environmentally-friendly, sustainable ScCO2-assisted fabrication of poly(lactic acid)/ramie fiber composite foams.</a> J Clean Prod. 425, 138952(2023).</li>
<li>Li, S., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Research+progress+on+the+improvement+strategy+of+foaming+behavior+for+biodegradable+polymer+foams+and+their+functional+applications%5BTitle%5D)+AND+%22Sustain+Mater+Technol%22%5BJournal%5D)">Research progress on the improvement strategy of foaming behavior for biodegradable polymer foams and their functional applications.</a> Sustain Mater Technol. 44, e01354(2025).</li>
<li>Wang, Z., Wang, G., Xu, Z., Zhang, A., Li, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((A+novel+%26%2334%3Breinforcing-foaming-recovering%26%2334%3B+strategy+for+achieving+thermally+insulating+green+foams+with+ultrafast+degradation%5BTitle%5D)+AND+%22J+Clean+Prod%22%5BJournal%5D)">A novel &#34;reinforcing-foaming-recovering&#34; strategy for achieving thermally insulating green foams with ultrafast degradation.</a> J Clean Prod. 481, 144161(2024).</li>
<li>Wang, Z., Wang, G., Xu, Z., Chai, J., Zhao, G. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Innovative+crosslinking+and+foaming+strategies+for+advancing+biodegradable+composite+foams%3A+Enhancing+foamability%2C+flexibility%2C+and+thermal+insulation%5BTitle%5D)+AND+%22Mater+Des%22%5BJournal%5D)">Innovative crosslinking and foaming strategies for advancing biodegradable composite foams: Enhancing foamability, flexibility, and thermal insulation.</a> Mater Des. 253, 113895(2025).</li>
<li>Jian, J., Xiangbin, Z., Xianbo, H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((An+overview+on+synthesis%2C+properties+and+applications+of+poly%28butylene-adipate-co-terephthalate%29-PBAT%5BTitle%5D)+AND+%22Adv+Ind+Eng+Polym+Res%22%5BJournal%5D)">An overview on synthesis, properties and applications of poly(butylene-adipate-co-terephthalate)-PBAT.</a> Adv Ind Eng Polym Res. 3 (1), 19-26 (2020).</li>
<li>Wang, Z., Wang, G., Xu, Z., Ma, C., Zhao, G. Pore-gradient, flexible, and fully-degradable foam with outstanding noise absorption and thermal insulation. <a target="_blank" href="http://scholar.google.com/scholar?hl=en&safe=off&q=author%3aWang%2C+Z+%22Adv+Funct+Mater%22">Adv Funct Mater</a>. , (2025).</li>
<li>Wang, Z., Wang, G., Xu, Z., Yang, C., Zhao, G. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Structure-tunable+poly%28butylene+adipate-CO-terephthalate%29+foams+with+enhanced+mechanical+performance+derived+by+microcellular+foaming+with+carbon+dioxide+as+blowing+agents%5BTitle%5D)+AND+%22J+CO2+Util%22%5BJournal%5D)">Structure-tunable poly(butylene adipate-CO-terephthalate) foams with enhanced mechanical performance derived by microcellular foaming with carbon dioxide as blowing agents.</a> J CO2 Util. 72, 102495(2023).</li>
<li>Wang, Z., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((low-shrinkage+and+high+elastic+poly%28butylene+adipate-co-terephthalate%29+foams+achieved+by+microcellular+foaming+using+N2+%26+CO2+as+co-blowing+agents%5BTitle%5D)+AND+%22J+CO2+Util%22%5BJournal%5D)">low-shrinkage and high elastic poly(butylene adipate-co-terephthalate) foams achieved by microcellular foaming using N2 & CO2 as co-blowing agents.</a> J CO2 Util. 64, 102149(2022).</li>
<li>Ding, Y., Yang, Q., Wang, X., Li, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((The+compressive+resilience+and+shrinkage+resistance+properties+of+poly%28butylene+adipate-co-terephthalate%29+microcellular+composite+foams+reinforced+by+functionalized+microcrystalline+cellulose%5BTitle%5D)+AND+%22Int+J+Biol+Macromol%22%5BJournal%5D)">The compressive resilience and shrinkage resistance properties of poly(butylene adipate-co-terephthalate) microcellular composite foams reinforced by functionalized microcrystalline cellulose.</a> Int J Biol Macromol. 306, 141466(2025).</li>
<li>Pereira Da Silva, J. S., Farias Da Silva, J. M., Soares, B. G., Livi, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Fully+biodegradable+composites+based+on+poly%28butylene+adipate-co-terephthalate%29%2Fpeach+palm+trees+fiber%5BTitle%5D)+AND+%22Compos+B+Eng%22%5BJournal%5D)">Fully biodegradable composites based on poly(butylene adipate-co-terephthalate)/peach palm trees fiber.</a> Compos B Eng. 129, 117-123 (2017).</li>
<li>Liu, H., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((High+strength+microcellular+thermoplastic+polyimide%2Fcarbon+fiber+composite+foams+containing+flexible+ether+amine%2C+rigid+diaminodiphenyl+ether%2C+and+triaminopyrimidine+moieties%3A+Synthesis+and+fabrication%5BTitle%5D)+AND+%22Chem+Eng+J%22%5BJournal%5D)">High strength microcellular thermoplastic polyimide/carbon fiber composite foams containing flexible ether amine, rigid diaminodiphenyl ether, and triaminopyrimidine moieties: Synthesis and fabrication.</a> Chem Eng J. 496, 154384(2024).</li>
<li>Li, W., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Real-microcellular+poly%28ether-block-amide%29%2Fcarbon+fiber+foams+with+improved+mechanical+property+and+surface+quality+for+high-performance+electromagnetic+interference+shielding+applications%5BTitle%5D)+AND+%22J+Mater+Res+Technol%22%5BJournal%5D)">Real-microcellular poly(ether-block-amide)/carbon fiber foams with improved mechanical property and surface quality for high-performance electromagnetic interference shielding applications.</a> J Mater Res Technol. 26, 6508-6519 (2023).</li>
<li>Liu, Y., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Supercritical+N2+induced+sandwich+type+lightweight+and+strong+PP%2FCF+foams+with+excellent+electromagnetic+shielding+properties%5BTitle%5D)+AND+%22Chem+Eng+J%22%5BJournal%5D)">Supercritical N2 induced sandwich type lightweight and strong PP/CF foams with excellent electromagnetic shielding properties.</a> Chem Eng J. 501, 157532(2024).</li>
<li>Qiao, Y., Hou, J., Tian, D., He, Y., Chen, J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Poly%28butylene+adipate-co-terephthalate%29%2Fcarbon+fiber+foam+bonded+with+continuous+carbon+fiber+reinforced+polypropylene+prepregs+for+electromagnetic+interference+shielding%5BTitle%5D)+AND+%22Compos+Commun%22%5BJournal%5D)">Poly(butylene adipate-co-terephthalate)/carbon fiber foam bonded with continuous carbon fiber reinforced polypropylene prepregs for electromagnetic interference shielding.</a> Compos Commun. 53, 102217(2025).</li>
<li>Tang, Q., Fang, L., Guo, W. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Effects+of+bamboo+fiber+length+and+loading+on+mechanical%2C+thermal+and+pulverization+properties+of+phenolic+foam+composites%5BTitle%5D)+AND+%22J+Bioresour+Bioprod%22%5BJournal%5D)">Effects of bamboo fiber length and loading on mechanical, thermal and pulverization properties of phenolic foam composites.</a> J Bioresour Bioprod. 4 (1), 51-59 (2019).</li>
<li>Li, X., Zhong, T., Xiao, Y., Cheng, H., Chen, H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Mechanically+robust%2C+thermal+insulating+sustainable+foams+fully+derived+from+bamboo+fibers+through+high+temperature+drying%5BTitle%5D)+AND+%22Carbohydr+Polym%22%5BJournal%5D)">Mechanically robust, thermal insulating sustainable foams fully derived from bamboo fibers through high temperature drying.</a> Carbohydr Polym. 333, 121966(2024).</li>
<li>Guo, W., Zhao, J., Zhao, F., Feng, T., Liu, L. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Assessment+of+properties+of+bamboo+fiber+and+EPDM+reinforced+polypropylene+microcellular+foam+composites%5BTitle%5D)+AND+%22Polymer+%28Guildf%29%22%5BJournal%5D)">Assessment of properties of bamboo fiber and EPDM reinforced polypropylene microcellular foam composites.</a> Polymer (Guildf). 304, 127142(2024).</li>
<li>Liu, H., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Green+strategy+based+on+supercritical-fluid+foaming+for+fabricating+rigid+microcellular+thermoplastic+polyimide+foams+with+ultrahigh+compressive+strength%5BTitle%5D)+AND+%22Compos+B+Eng%22%5BJournal%5D)">Green strategy based on supercritical-fluid foaming for fabricating rigid microcellular thermoplastic polyimide foams with ultrahigh compressive strength.</a> Compos B Eng. 273, 111204(2024).</li>
<li>Sarver, J. A., Kiran, E. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Foaming+of+polymers+with+carbon+dioxide+-+The+year-in-review+2019%5BTitle%5D)+AND+%22J+Supercrit+Fluids%22%5BJournal%5D)">Foaming of polymers with carbon dioxide - The year-in-review 2019.</a> J Supercrit Fluids. 173, 105166(2021).</li>
<li>Dong, M., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((An+overview+of+polymer+foaming+assisted+by+supercritical+fluid%5BTitle%5D)+AND+%22Adv+Compos+Hybrid+Mater%22%5BJournal%5D)">An overview of polymer foaming assisted by supercritical fluid.</a> Adv Compos Hybrid Mater. 6 (6), 207(2023).</li>
<li>Zhang, X., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Green+preparation+of+lightweight+and+elastic+poly%28butylene+adipate-co-terephthalate%29%2Fthermoplastic+polyamide+elastomer+composite+foams%5BTitle%5D)+AND+%22J+Supercrit+Fluids%22%5BJournal%5D)">Green preparation of lightweight and elastic poly(butylene adipate-co-terephthalate)/thermoplastic polyamide elastomer composite foams.</a> J Supercrit Fluids. 223, 106635(2025).</li>
<li>Pang, Y., Cao, Y., Zheng, W., Park, C. B. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((A+comprehensive+review+of+cell+structure+variation+and+general+rules+for+polymer+microcellular+foams%5BTitle%5D)+AND+%22Chem+Eng+J%22%5BJournal%5D)">A comprehensive review of cell structure variation and general rules for polymer microcellular foams.</a> Chem Eng J. 430, 132662(2022).</li>
</ol>

<table><tbody><tr><td>Fibre de bambou</td><td>Usine de Fibres de Lvzhu du Sichuan Co., Ltd., Chine</td><td>1000 mailles</td><td>Matière première fournie pour le travail expérimental</td></tr><tr><td>Pompe d’appoint</td><td>Dongguan Suncenter Fuild Control Equipment Co., Ltd., Chine</td><td>DGA15C</td><td>Utilisé pour contrôler la pression</td></tr><tr><td>Dioxyde de carbone</td><td>Harbin Qinghua Industrial Gas Co. Ltd., Chine</td><td>Pureté à 99,9 %</td><td>Utilisé comme agent moussant</td></tr><tr><td>Fibre de carbone & nbsp ;</td><td>Toray Industries Incorporated, &nbsp ; Japon</td><td>1000 mailles</td><td>Matière première fournie pour le travail expérimental</td></tr><tr><td>Ceactor</td><td>Zhengzhou Zechen Instrument Equipment Co., Ltd., Chine</td><td>0,5 L</td><td>Utilisé comme récipient à mousse</td></tr><tr><td>Compacteur</td><td>Zhejiang Kaishan Compressor Co., Ltd., Chine</td><td>XK06-010-00487</td><td>pressurisé</td></tr><tr><td>Bain d’huile numérique</td><td>Boho Temptech Co., Ltd., Chine</td><td>HH-5-12L</td><td>Utilisé pour chauffer</td></tr><tr><td>Four de séchage</td><td>Shanghai Yiheng Scientific Instrument Co., Ltd., Chine</td><td>DGG-9070</td><td>Utilisé pour sécher les matières premières</td></tr><tr><td>Balancier électronique</td><td>Mettler Toledo (Changzhou) Weighing Equipment System Co., Ltd</td><td>SPN501F</td><td>Utilisé pour peser les matières premières</td></tr><tr><td>Instrument de sulfurisation à plaque plate</td><td>Bolon Precision Testing Machines Co., Ltd., Chine</td><td>BL-6170-A</td><td>Pour le moulage à chaud de composites</td></tr><tr><td>Densimètre solide de haute précision</td><td>Yuemang Intelligent Equipment Co., Ltd., Chine</td><td>JHY-120Y</td><td>Dispositif utilisé pour déterminer &nbsp ; Densité</td></tr><tr><td>Logiciel d’analyse d’images National Institutes of Health</td><td>Instituts nationaux de la santé</td><td>ImageJ</td><td>Logiciels utilisés pour déterminer les caractéristiques morphologiques de la mousse</td></tr><tr><td>Poly (butylène adipate-co-térephtalate)</td><td>Xinjiang Blue Ridge Tunhe Sci.& Tech. Co., Ltd., Chine</td><td>TH801T</td><td>Matière première fournie pour le travail expérimental</td></tr><tr><td>Film de polytétrafluoroéthylène</td><td>Société commerciale des matériaux plastiques Luo Huixing, Chine</td><td>0,5 mm</td><td>Utilisé pour démouler</td></tr><tr><td>Pulveriser</td><td>Shenzhen Chengzhongsheng Electromechanical Technology Co., Ltd., Chine</td><td>380 W, 50 Hz</td><td>Utilisé pour broyer et granuler</td></tr><tr><td>Scanner</td><td>FEI Inc., États-Unis</td><td>QUANTA 220</td><td>Scanner utilisé pour prendre une image de mousses</td></tr><tr><td>Extrudeuse à double vis</td><td>Nankin Jiente Machine Point Co. Ltd., Chine</td><td>SHJ-20</td><td>Mélange de fusion</td></tr><tr><td>Machine universelle d’essai mécanique</td><td>Wance Technologies Ltd., Chine</td><td>TestPilot X10A</td><td>Utilisé pour mesurer la performance de compression</td></tr></tbody></table>

préparation de mousses de poly (adipate-co-téréphtalate de butylène) renforcées de fibres de carbone et de fibres de bambou par moussage au dioxyde de carbone supercritique

Preparation of Carbon Fiber and Bamboo Fiber Reinforced Poly (butylene Adipate-co-terephthalate) Foams by Supercritical Carbon Dioxide Foaming

Préparation de mousses de poly (adipate-co-téréphtalate de butylène) renforcées de fibres de carbone et de fibres de bambou par moussage au dioxyde de carbone supercritique

Fiber-reinforced polymer foams have found extensive applications across numerous fields. Particularly, poly (butylene adipate-co-terephthalate) (PBAT) has ...

preparation-carbon-fiber-bamboo-fiber-reinforced-poly-butylene

Research

Recherche

JoVE Journal

Engineering

Ingénierie

Nous présentons une nouvelle méthode de fabrication de préformes rigides et robustes fibres naturelles courtes en utilisant un procédé de fabrication de papier. Cellulose bactérienne agit simultanément en tant que liant pour les fibres lâches et donne de la rigidité aux préformes de fibres. Ces préformes peuvent être infusées avec une résine pour produire des composites hiérarchiques vraiment verts.

Fabrication robuste préformes à fibres naturelles Utilisant bactérienne Cellulose Binder

La réplication est l’une des techniques de traitement utilisées pour la production d’éponges métalliques poreuses. Dans cet article, une mise en œuvre de la méthode de production d’aluminium poreux à cellules ouvertes est présentée en détail.

Coulée protocoles pour la production de cellules ouvertes aluminium Mousses par la technique de réplication et l&#39;effet sur la porosité

Cette méthode vidéo décrit la synthèse de matériaux monolithiques à base de graphène 3D à grande surface dérivés de précurseurs de polymères ainsi que d’oxyde de graphène monocouche.

Synthèse et fonctionnalisation des matériaux 3D Nano-graphène graphène: aérogels et graphène assemblées Macro

Une nouvelle méthode de production d’aérogels à base de biopolymères par gélification induite par le dioxyde de carbone (CO2) est présentée. La technique utilise du dioxyde de carbone sous pression (5 MPa) pour la production d’hydrogels biopolymères et du CO2 supercritique (12 MPa) pour convertir les gels en aérogels. Les seuls solvants nécessaires en plus du CO2 sont l’eau et l’éthanol.

Préparation de biopolymères aérogels Utilisation de Solvants verts

Un protocole d’exposer nus fibres sur la surface composite en éliminant les zones riches de résine est présenté. Les fibres sont exposés au cours de la fabrication des composites, non par le traitement de surface de post. Les composites de carbone exposés présentent une conductivité électrique élevée dans le sens de l’épaisseur et les propriétés mécaniques élevées.

Mise en œuvre expérimentale d’une nouvelle méthode de Fabrication Composite : exposer nus fibres sur la Surface Composite par la méthode de la couche molle

Nous présentons une nouvelle méthode à base de microfluidique pour la synthèse de cadres organiques covalents (COF). Nous démontrons comment cette approche peut être utilisée pour produire des fibres continues de COF, ainsi que des structures COF 2D ou 3D sur les surfaces.

Synthèse à base de microfluidique des cadres organiques covalents (COF): un outil pour la production continue de fibres COF et l&#39;impression directe sur une surface

Nous présentons ici des protocoles de préparation et d’essais des aérogels catalytiques en intégrant des espèces métalliques à plateformes d’aérogel de silice et d’alumine. Méthodes pour la préparation des matériaux à l’aide de sels de cuivre et nanoparticules contenant du cuivre sont en vedette. Les protocoles de tests catalytiques démontrent l’efficacité de ces aérogels pour des applications de catalyse de trois voies.

Fabrication et essai d’aérogels catalytiques préparés par Extraction supercritique rapide

Une méthode appelée fabrication additive négative sert à produire près de pièces de carbure de bore en forme complexe entièrement dense de diverses échelles de longueur. Cette technique est possible par l’intermédiaire de la formulation d’une nouvelle suspension impliquant la résorcine-formaldéhyde comme agent gélifiant unique qui laisse derrière lui un carbone homogène frittage aide après pyrolyse.

Fabrication Additive négative du complexe en forme de carbures de bore

Cet article illustre la technique d’élargir une natte de nanofibres électrofilées (2D) traditionnel, de deux-dimension en échafaudage tridimensionnels (3D) par le biais de la dépressurisation du sous-critique CO2 fluide. Ces échafaudages augmentés sont en 3D, indices étroitement mimiques nanotopographic cellulaires et préserver les fonctions des molécules biologiques encapsulés dans les nanofibres.

Expansion de nanofibres Électrofilées dimension deux nattes en trois dimensions les échafaudages

Cet article décrit un protocole ainsi qu’une étude comparative de deux techniques de fabrication microfluidiques, à savoir la photolithographie/gravure humide/liaison thermique et l’gravure sélective induite par laser (SLE), qui conviennent aux conditions de haute pression. Ces techniques constituent des plates-formes habilitantes pour l’observation directe du flux de fluides dans les supports perméables de substitution et les systèmes fracturés dans des conditions de réservoir.

Techniques de fabrication microfluidiques pour l’essai à haute pression du transport supercritique de mousse de CO2 à micro-échelle dans les réservoirs non conventionnels fracturés

Un procédé polyvalent d’extrusion à deux vis pour fournir un prétraitement thermo-mécano-chimique efficace sur la biomasse lignocellulosique a été développé, ce qui conduit à un rapport d’aspect moyen accru des fibres. Un liant naturel peut également être ajouté en continu après l’affinage des fibres, conduisant à des panneaux de fibres biosampés avec des propriétés mécaniques améliorées après pressage à chaud du matériau extrudé obtenu.

Procédé d’extrusion à deux vis pour produire des panneaux de fibres renouvelables

Découvrez la fabrication de mousses PBAT renforcées par fibres de carbone et de bambou via moussage au CO2 supercritique. Cette méthode améliore l'anti-rétrécissement, la légèreté et la résistance mécanique pour des applications durables.

Préparation de mousses de poly (adipate-co-téréphtalate de butylène) renforcées de fibres de carbone et de fibres de bambou par moussage au dioxyde de carbone supercritique (Vidéo) | JoVE Journal

Préparation de mousses de poly (adipate-co-téréphtalate de butylène) renforcées de fibres de carbone et de fibres de bambou par moussage au dioxyde de carbone supercritique