Name: hydrogel synthesis
Uploaded: 2023-04-30T07:06:34.000Z
Duration: 8 min 33 s
Channel: JoVE

The pre-gel solution was created in a 1000µl test tube; materials, role in polymerization and amounts added are listed in Tables 1.
<table border="1" fo:keep-together.within-page="1" fo:keep-with-next.within-page="always">
	<tbody>
		<tr>
			<td>Material</td>
			<td>Purpose</td>
			<td>Structure</td>
			<td>Mole percent</td>
		</tr>
		<tr>
			<td>2,2-Dimethoxy-2-phenyl-acetophenone (DMPAP)</td>
			<td>Free readical initiator (photoinitiator)</td>
			<td><img alt="Chemical structure diagram, synthesis of Benzyl acetate, organic chemistry formula." src="/files/ftp_upload/10486/10486eq5.jpg" data-altupdatedat="1761830439000" data-alt="Equation 5"> </td>
			<td>0.0012</td>
		</tr>
		<tr>
			<td>2-Hydroxethyl methacrylate
			
			(HEMA)
			</td>
			<td>Polymer backbone</td>
			<td><img alt="Chemical structure diagram of ethyl lactate molecule; organic compound formula." src="/files/ftp_upload/10486/10486eq6.jpg" data-altupdatedat="1761830439000" data-alt="Equation 6"> </td>
			<td>21.2121</td>
		</tr>
		<tr>
			<td>Tetraethylene glycol dimethacrylate (TEGDMA)</td>
			<td>Crosslinker</td>
			<td><img alt="Chemical structure, diagram, adipic acid derivative, organic compound, hexanedioic acid visualization." src="/files/ftp_upload/10486/10486eq7.jpg" style="opacity: 0.9;" data-altupdatedat="1761830439000" data-alt="Equation 7"> </td>
			<td>3.0303</td>
		</tr>
		<tr>
			<td>Ethylene glycol
			
			(EG)
			</td>
			<td>Solvent</td>
			<td><img alt="Ethylene glycol chemical structure diagram; organic compound molecule, HO-CH2-CH2-OH." src="/files/ftp_upload/10486/10486eq8.jpg" data-altupdatedat="1761830439000" data-alt="Equation 8"></td>
			<td>75.7576</td>
		</tr>
	</tbody>
</table>
Table 1. Hydrogel pre-gel constituents, their roles in hydrogel free radical polymerization, chemical 2D polymeric structure and the amounts added to the pre-gel solution.
Synthesis
<ol>
	<li>Prior to beginning hydrogel synthesis, a synthesis mold was assembled from two glass slides and three, 520-micron thick polyolefin-sheet spacers; this configuration was held together by binder clips as shown in Figure 6. The large glass slides were offset by a few millimeters to create a channel for pipetting the pre-gel solution into the mold.</li>
	<li>Before beginning hydrogel synthesis, obtain a 1000µl test tube, the chemicals described in Table 1, a micropipette with clean tips, and setting mold (Figure 6). All work should be performed in a fume hood with proper Personal Protective Equipment (PPE). PPE includes safety glasses or goggles, a lab coat and protective gloves.</li>
</ol>
<img alt="Simple physics lever demonstration using binder clips to illustrate static equilibrium principles." src="/files/ftp_upload/10486/10486fig6.jpg" data-altupdatedat="1761830439000" data-alt="Figure 6"> 
Figure 6: Hydrogel synthesis mold, created from two glass slides, three strips of 520-micron thick polyolefin-sheet as spacers, and large binder clips.
<ol start="3">
	<li>Add 0.0012 mole percent 2,2-Dimethoxy-2-phenyl-acetophenone (DMPAP), the solid photoinitator (free radical initiator that is initiated by light), to the test tube first.</li>
	<li>Add 21.2121 mole percent 2-hydroxethyl methacrylate (HEMA), the backbone molecule, and 3.0303 mole percent tetraethylene glycol dimethacrylate (TEGDMA), the crosslinking molecule to the test tube, using new pipette tips each time. TEGDMA will chemically crosslink the HEMA chains in the presence of free radicals by connecting the polymer chains into a network polymer.</li>
	<li>Mix the solution using a vortex machine until a homogenous solution is achieved.</li>
	<li>Measure 0.25 grams of Bromocresol Purple and rinse it into the solution using 75.7576 mole percent ethylene glycol (EG), the solvent. The pigment is only for viewing purposes (the hydrogel is transparent otherwise), and EG serves as a solvent to dissolve the initiating free radical initiator and keeps the hydrogel flexible.</li>
	<li>Mix the solution using the vortex machine until the pigment completely dissolves and the solution is homogenous.</li>
	<li>Using a micropipette, deposit the solution into the mold by aligning the tip of the micropipette with the offset edge of the large glass slides and uniformly injecting the pre-gel solution into the center of the mold.</li>
	<li>Place mold 5 centimeters below a UV emitting flashlight (Warson SK66) and irradiate the mold for one minute. UV light cleaves the bonds in the initiator species, turning them into free radicals which can then attack the polymer and crosslinker molecules. When fully networked, the hydrogel should be a rubber solid with a jello-like consistency.</li>
	<li>Remove mold from the light and disassemble the mold configuration. Remove hydrogel from the glass slides.</li>
	<li>Rinse both sides of the hydrogel with deionized water to remove any unreacted chemical species and oligomers from the product.</li>
	<li>To characterize how various UV-light exposure times affect degree of crosslinking and swelling ability, this procedure can be repeated while varying step nine. For characterization, the solution was exposed to UV light for 1 minute, 1.5 minutes and 5 minutes, producing a total of three hydrogels.</li>
</ol>
Characterization
The swelling degree of the hydrogel can be calculated by drying, hydrating and then re-drying the polymer.
<ol>
	<li>Place the finished hydrogels in a container with an alcohol such as Isopropyl Alcohol so that they are totally submerged. Leave in the alchohol for 4-8 hours, when the alcohol has replaced all the ethylene glycol in the hydrogel.</li>
	<li>Remove the hydrogels from the alcohol and leave to dry in the open, about 30 minutes. The alcohol evaporates more quickly than water or the solvent, allowing the hydrogel to maintain its structure.</li>
	<li>Weigh the dried hydogels.</li>
	<li>Submerge the hydrogels in DI water for at least 30 minutes, until they're completely swollen. Remove the gels from water, gently wipe dry and weigh.</li>
	<li>Calculate the swelling degree using the equation: <img alt="Swelling percentage formula, %swelling=(ws-wd)/wd x100, equation analysis, material science." src="/files/ftp_upload/10486/10486eq9v2.jpg" style="opacity: 0.9;" data-altupdatedat="1761830439000" data-alt="Equation 9"> , where <img alt="ΣFx=0 equation, static equilibrium, formula, educational diagram" src="/files/ftp_upload/10486/10486eq10.jpg" data-altupdatedat="1761830439000" data-alt="Equation 10"> is the weight of the swollen polymer and <img alt="Equation symbol for torque, represented as W_d." src="/files/ftp_upload/10486/10486eq11.jpg" data-altupdatedat="1761830439000" data-alt="Equation 11"> is the weight of the dried polymer.</li>
</ol>

Hydrogel synthesis is a technique for producing crosslinked polymeric materials which can swell in response to liquid, UV light, pH, or a range of other stimulants. Synthesis by combination of liquid solutions is advantageous for the simplicity of mixing and forming hydrogels, though the final product is generally impure and tends to contain polymers with low molecular weights. This specific procedure, while simple, involves chemicals that are both toxic and flammable, and therefore requires extreme care and preventative...

hydrogel synthesis

Source: Amber N. Barron, Ashlea Patterson, and <a href="https://www.jove.com/author/Taylor+D._Sparks">Taylor D. Sparks</a>, Department of Materials Science and Engineering, The University of Utah, Salt Lake City, UT
Hydrogels are a versatile class of cross-linked polymers produced through relatively simple procedures and with generally inexpensive materials. They can be formed from solution and involve a polymer backbone formed from monomer reagents, an initiator which makes the polymer reactive and a crosslinking species which binds the polymer chains together. An important aspect of these materials is that they swell in the presence of water, but this response can be tuned further to enhance swelling as a function of salinity, pH, or other signals. As a final product, hydrogels can be used in aqueous or dry environments, with a range of useful properties such as flexibility, high absorbance, transparency and thermal insulation. They are commonly used for liquid absorbance, sensors, consumer products, and drug delivery.

The final hydrogel monomer is shown in Figure 7, and the synthesized hydrogels are shown in Figure 8. The degree of swelling was found to be approximately 136% for the 1 min sample, 387% for the 1.5 min sample and 81% for the 5 min sample. These results demonstrate the relationship between degree of crosslinking, or the extent to which the network is connected, and swelling ability. More links between the polymer molecules mean m...

Hydrogel Synthesis

Source: Amber N. Barron, Ashlea Patterson, and Taylor D. Sparks, Department of Materials Science and Engineering, The University of Utah, Salt Lake City, ...

Hydrogels are a versatile class of cross-linked polymers, produced through relatively simple procedures using generally inexpensive materials. They are commonly used for liquid absorbents, sensors, consumer products and drug delivery. Hydrogels can be formed from solution, with an initiator making monomerie agents reactive to form a polymer backbone. A crosslinking species then binds the polymer chains together. An important aspect of these materials is that in the presence of water they swell. But this response can be tuned further to enhance swelling as a function of salinity, PH or other signals. Hydrogels can be used in aqueous or dry environments, with a range of useful properties such as flexibility, high absorbance, transparency and thermal insulation. This video will illustrate the synthesis and characterization of hydrogels.Hydrogels are capable of absorbing hundreds of times their weight in water. When water enters the crosslinked polymer network, it solubilizes hydrophilic, ionic or both species on the polymer backbone. The water molecules are larger than the solubilized groups. Because of this, their presence inside the network causes the hydrogel to swell. While the crosslinks connecting the polymer backbone prevent it from dissolving or breaking. Hydrogel synthesis is a technique for producing these crosslinked, polymeric materials. This is a simple procedure but involves chemicals that are both toxic and flammable and therefore requires extreme care and preventative measures. Using pre-gel constituents, hydrogels can be made via Free Radical Polymerization. One method starts with DMPAP as a Free Radical Initiator.The carbon-carbon bond in DMPAP is cleaved by ultra-violet light to form an unpaired, highly reactive electron called a free radical on each carbon atom. The free radicals react with the carbon-carbon double-bond in HEMA to form a propogating chain with a free radical on the end. The hydroxal group coming off the backbone is soluble in water, causing the cross-linked network to swell when water is present. The radicals also react with the two carbon-carbon double-bonds in TEGDMA, the chemical crosslinker. This links the backbone chains together. When the free radicals have been consumed, or have completely reacted, the hydrogel synthesis is complete. Swelling can be assessed by drying, hydrating and then re-drying the polymer. In the next section, we will synthesis and characterize hydrogels using this free radical polymerization method.Prior to beginning hydrogel synthesis, gather the necessary materials and chemicals. The glass slides in the previously assembled synthesis mold are offset by a few millimeters, to create a channel for pipetting the pre-gel solution into the mold. All work should be performed with proper Personal Protective Equipment in a fumehood, as this process involves chemicals that are both toxic and flammable. First, add 0.0012 mol percent DMPAP to the 1000 microliter test tube. Next, use a new pipette each time to add 21.2121 mol percent HEMA and then 3.0303 mol percent TEGDMA to the test tube. Mix the solution using a vortex machine until a homogenous solution is achieved. Dip the spatula into the pigment BCP and rinse it into the solution using 75.7576 mol percent of the solvent ethylene glycol.Mix the solution using the vortex machine until the pigment completely dissolves and the solution is homogenous.?This pigment is used to make the transparent hydrogel visible, while the solvent dissolves the Free Radical Initiator and keeps the hydrogel flexible. Deposit the solution into the mold using a micro pipette aligned with the offset edge of the synthesis mold. Uniformly inject the pre-gel solution into the center of the mold. Place the filled mold five centimeters below a UV-emitting flashlight and irradiate the mold for one minute. Remove the mold from the light and disassemble to remove the hydrogel from the glass slides.When fully networked, the hydrogel should be a rubber solid with a jello-like consistency. Rinse both sides of the hydrogel with deionized water to remove any unreacted chemical species and polygimers from the product. Repeat this procedure with UV light exposure times of 1.5 and five minutes to produce a total of three hydrogels.Submerge the finished hydrogels in a container with isopropyl alcohol for one to two hours. The alcohol will replace the ethylene glycol in the hydrogel, allowing it to dry quickly while maintaining its structure. Remove the hydrogels from the alcohol and leave to dry in the open for about 30 minutes. Weigh and record the weight of each of the dried hydrogels. Submerge the hydrogels in deionized water until completely swollen. Remove the gels from the water and gently wipe dry. Weigh and record the weight of the swollen hydrogels. Use the weight of the swollen hydrogels, Ws, and the dried hydrogels, Wd, to calculate the swelling degree.The degree of swelling was found to be approximately 136% for the one minute sample, 387% for the 1.5 minute sample, and 81% for the five minute sample. These results show that at the longest UV exposure time, there was less swelling. Due to the formation of more links between polymer molecules with increased UV exposure, there were more elastic restraining forces on the polymer chains. This resulted in hydrogels with more crosslinking expanding less than those with less crosslinking.Now that you appreciate the methods of synthesizing and characterizing hydrogels, let's take a look at how they are used in everyday products. Consumer products such as hospital pads, feminine hygiene pads and diapers, contain one of the most common super-absorbant polymers. This hydrogel can swell to absorb fluids up to 800 times its weight, allowing manufacturers to create products that are slim and comfortable. The hydrogel synthesized in this video is used as a sensor in a lawn sprinkler. The sensor is in contact with the soil and swells while the lawn is being watered, until it triggers the sprinkler shutoff.You've just watched Jove's introduction to hydrogel synthesis. You should now understand how hydrogels are synthesized and characterized. Thanks for watching.

Education

JoVE Science Education

Engineering

Materials Engineering

optical materialography part 1: sample preparation

optical-materialography-part-1-sample-preparation

Optical Materialography Part 1: Sample Preparation

Source: Faisal Alamgir, School of Materials Science and Engineering, Georgia Institute of Technology, Atlanta, GA
The imaging of microscopic structures of ...

optical materialography part 2: image analysis

optical-materialography-part-2-image-analysis

Optical Materialography Part 2: Image Analysis

x-ray photoelectron spectroscopy

X-ray Photoelectron Spectroscopy

Source: Faisal Alamgir, School of Materials Science and Engineering, Georgia Institute of Technology, Atlanta, GA
X-ray photoelectron spectroscopy (XPS) ...

x-ray diffraction

X-ray Diffraction

Source: Faisal Alamgir, School of Materials Science and Engineering, Georgia Institute of Technology, Atlanta, GA
X-ray diffraction (XRD) is a technique ...

focused ion beams

Focused Ion Beams

Source: Sina Shahbazmohamadi and Peiman Shahbeigi-Roodposhti-Roodposhti, School of Engineering, University of Connecticut, Storrs, CT
As electron ...

directional solidification and phase stabilization

directional-solidification-and-phase-stabilization

Directional Solidification and Phase Stabilization

Source: Sina Shahbazmohamadi and Peiman Shahbeigi-Roodposhti-Roodposhti, School of Engineering, University of Connecticut, Storrs, CT
Directional ...

differential scanning calorimetry

Differential Scanning Calorimetry

Source: Danielle N. Beatty and Taylor D. Sparks, Department of Materials Science and Engineering, The University of Utah, Salt Lake City, UT
Differential ...

thermal diffusivity and the laser flash method

thermal-diffusivity-and-the-laser-flash-method

Thermal Diffusivity and the Laser Flash Method

Source: Elise S.D. Buki, Danielle N. Beatty, and Taylor D. Sparks, Department of Materials Science and Engineering, The University of Utah, Salt Lake ...

electroplating of thin films

Electroplating of Thin Films

Source: Logan G. Kiefer, Andrew R. Falkowski, and Taylor D. Sparks, Department of Materials Science and Engineering, The University of Utah, Salt Lake ...

analysis of thermal expansion via dilatometry

analysis-of-thermal-expansion-via-dilatometry

Analysis of Thermal Expansion via Dilatometry

Source: J. Jacob Chavez, Ryan T. Davis, and Taylor D. Sparks, Department of Materials Science and Engineering, The University of Utah, Salt Lake City, UT
...

electrochemical impedance spectroscopy

Electrochemical Impedance Spectroscopy

Source: Kara Ingraham, Jared McCutchen, and Taylor D. Sparks, Department of Materials Science and Engineering, The University of Utah, Salt Lake City, UT
...

ceramic-matrix composite materials and their bending properties

ceramic-matrix-composite-materials-and-their-bending-properties

Ceramic-matrix Composite Materials and Their Bending Properties

Source: Sina Shahbazmohamadi and Peiman Shahbeigi-Roodposhti-Roodposhti, School of Engineering, University of Connecticut, Storrs, CT
Bones are ...

nanocrystalline alloys and nano-grain size stability

nanocrystalline-alloys-and-nano-grain-size-stability

Nanocrystalline Alloys and Nano-grain Size Stability

Source: Sina Shahbazmohamadi and Peiman Shahbeigi-Roodposhti-Roodposhti, School of Engineering, University of Connecticut, Storrs, CT
Alloys with grain ...

materials engineering

This collection features cutting-edge methods for analysis and characterization of materials, and introduces a range of advanced materials and processes for new technologies and applications.

Explore how hydrogels are made from cross-linked polymers and why they swell in water. Learn their properties and common uses in sensors, absorbent products, and drug delivery.

Hydrogel Synthesis

Description

Transcript

Tags