Production of Extracellular Matrix Fibers via Sacrificial Hollow Fiber Membrane Cell Culture

Summary

The goal of this protocol is production of whole extracellular matrix fibers targeted for wound repair which are suitable for preclinical evaluation as part of a regenerative scaffold implant. These fibers are produced by the culture of fibroblasts on hollow fiber membranes and extracted by dissolution of the membranes.

Abstract

Engineered scaffolds derived from extracellular matrix (ECM) have driven significant interest in medicine for their potential in expediting wound closure and healing. Extraction of extracellular matrix from fibrogenic cell cultures in vitro has potential for generation of ECM from human- and potentially patient-specific cell lines, minimizing the presence of xenogeneic epitopes which has hindered the clinical success of some existing ECM products. A significant challenge in in vitro production of ECM suitable for implantation is that ECM production by cell culture is typically of relatively low yield. In this work, protocols are described for the production of ECM by cells cultured within sacrificial hollow fiber membrane scaffolds. Hollow fiber membranes are cultured with fibroblast cell lines in a conventional cell medium and dissolved after cell culture to yield continuous threads of ECM. The resulting ECM fibers produced by this method can be decellularized and lyophilized, rendering it suitable for storage and implantation.

Introduction

Implantable surgical scaffolds are a fixture of wound repair,with over one million synthetic polymer meshes implanted worldwide each year for abdominal wall repair alone¹. However, following implantation the synthetic materials polymers traditionally used in the fabrication of these scaffolds tend to provoke a foreign body response, resulting in inflammation deleterious to the function of the implant and scarring of tissue². Further, as the predominant synthetic mesh materials (i.e., polypropylene) are not appreciably remodeled by the body, they are generally applicable to tissues where scarring can be tolerated, limiting their clinical usefulness toward the treatment of tissues with higher-order function such as muscle. While there are many surgical mesh products which have been applied with clinical success, recent manufacturer recalls of synthetic surgical meshes and complications from interspecies tissue implants highlight the importance of maximizing implant biocompatibility, prompting the FDA to tighten regulations on surgical mesh manufacturers^3,4. Implantation of scaffolds derived from patients' own tissues reduces this immune response, but can result in significant donor-site morbidity⁵. Extracellular matrix (ECM) scaffolds produced in vitro are a possible alternative, as decellularized ECM scaffolds exhibit excellent biocompatibility, particularly in the case of autologous ECM implants⁶.

Because of the limited availability of patient tissue to harvest for autologous implantation and the risk of impeding function at the donor site, the ability to produce ECM scaffolds in vitro from the culture of human cell lines or, if possible, a patient's own cells is an attractive alternative. The primary challenges in the manufacture of substantial amounts of ECM in vitro is the sequestration of these difficult-to-capture molecules. In previous work, we have demonstrated that ECM can be produced by culturing ECM-secreting fibroblasts in sacrificial polymeric foams that are dissolved after the culture period to yield ECM which can be decellularized for implantation^7,8,9,10. As ECM produced in foams tend to adopt the internal architecture of the foams, hollow fiber membranes (HFMs) were explored as a sacrificial scaffold for production of threads of ECM. Described herein are methods tasked for lab scale manufacturing of cell culture quality hollow fiber membranes and the extraction of bulk extracellular matrix fibers from the same following a period of fibroblast culture. This static culture approach is readily adoptable by laboratories containing standard mammalian cell culture equipment. ECM produced by this approach could be applied toward a variety of clinical applications.

Protocol

1. Production of Extracellular Matrix Using Sacrificial Hollow Fiber Membranes

CAUTION: N-methyl-2-pyrrolidone is an irritating solvent and reproductive toxicant. Exposure to NMP may cause irritation to the skin, eyes, nose, and throat. Solvent-resistant personal protective equipment should be used when handling NMP. Use of NMP should be performed within a fume hood.

1. Preparation of polysulfone polymer solution for hollow fiber membranes
   1. Weigh 70 g of polysulfone pellets (molecular weight of 35 kD) in a weigh boat using an analytical balance.
   2. Transfer 314 mL (323.3 g) of N-methyl-2-pyrrolidone (NMP) to a clean borosilicate flask.
   3. Place a stir bar in the flask with NMP and place flask onto stirrer. Set the stirrer to a moderate rate of rotation.
   4. Use a dry funnel to slowly insert the prepared 70 g of polysulfone into the flask with NMP.
   5. Allow the polymer “dope” solution to stir for three days at room temperature, or until homogenized.
2. Setting concentricity and cleaning of the hollow fiber membrane spinneret
   NOTE: Spinnerets are commercially available; correct spinneret dimensions are critical to successful membrane fabrication and are listed in the Table of Materials. Handle the spinneret very gently, as the spinneret needle is particularly fragile.
   1. Use a screwdriver or drill with an appropriate screwdriver bit to carefully disassemble the spinneret.
   2. Gently flow acetone through the inlet and outlet of the spinneret, collecting any acetone and residual polymer in a glass beaker for disposal.
   3. Secure the upper body of the spinneret with the needle facing upward in a table vise.
   4. Place the outlet (bottom) body of the spinneret onto the upper body.
   5. Move the outlet body of the spinneret laterally while holding the upper body fixed on the vise until the spinneret needle is directly in the center of the outlet body.
   6. Carefully and slowly reinsert the screws connecting the two bodies of the spinneret while ensuring that the needle visible at the spinneret outlet remains centered.
3. Fabrication of polysulfone hollow fiber membranes
   1. Prepare a “bore solution” containing 45 mL of N-methyl-2-pyrrolidone and 255 mL of deionized water, forming a 15% mixture of NMP with deionized water.
   2. Mount a concentric hollow fiber membrane spinneret 8 cm above the surface of a room-temperature tap water bath.
   3. Connect the polymer inlet of the spinneret and the bore inlet of the spinneret to two separate steel pressure vessels having an inner volume of at least 350 mL. Both vessels must have check valves at their outlets.
   4. Connect each of the pressure vessels to the regulators of separate N₂ gas cylinders
   5. Use a funnel to insert the prepared dope solution (~315 mL) into the pressure vessel connected to the polymer inlet of the spinneret. Ensure that the top of the vessel is tightly sealed.
   6. Use a funnel to insert the prepared bore solution (300 mL) into the pressure vessel connected to the bore inlet of the spinneret. Ensure that the top of the vessel is tightly sealed.
   7. Open the check valve for the bore vessel first, then the polymer vessel second. If the spinneret is sufficiently clean, the bore solution will begin to stream out of the spinneret outlet.
   8. Pressurize both vessels to 1 PSI. Visually confirm that both polymer and bore solutions are exiting the spinneret, with a continuous white filament precipitating as the combined streams contact the water bath.
   9. Use long forceps to guide the nascent fiber under the rollers in the center of the bath, and then wind the nascent fiber around a rotating wheel connected to a motor.
   10. Set the take-up wheel and motor to rotate at a rate of approximately two meters per minute.
   11. Make minor adjustments to the regulators or take-up wheel speed as needed until a steady-state flow is achieved. The nascent fiber should form a 90° angle with the surface of the water bath.
   12. Close the N₂ cylinder regulators and pressure vessel check valves and disengage the take-up wheel motor after all polymer and bore solution has been extruded from the vessels.
   13. Remove the prepared hollow fiber membranes and place them into a deionized water bath for three days, exchanging deionized water once per day to remove residual solvent.
   14. Sterilize the hollow fiber membranes by autoclaving them at 121 °C for 30 minutes or by immersing them for one day in 70% ethanol.
4. Cell seeding of hollow fiber membranes
   NOTE: All cell culture procedures should be performed within a biosafety cabinet.
   1. Treat the hollow fiber membranes with a 20 µg/mL solution of bovine plasma fibronectin in PBS (pH = 7.4) to promote cell attachment.
      1. Weigh 1 mg of powdered bovine plasma fibronectin in a weigh boat and dissolve it in 1 mL of sterile PBS (pH = 7.4) in a sterile 1.5 mL microcentrifuge tube.
      2. Incubate the 1 mg/mL bovine plasma fibronectin solution in the incubator for 30 minutes. Add the solution to 49 mL of sterile PBS in a sterile 50 mL conical centrifuge tube.
      3. Incubate the fibers in the prepared 50 mL of bovine plasma fibronectin in an incubator at 37 °C with 5% CO₂ for 1 hour. Recollect the fibronectin solution for later use and store in a sterile 50 mL conical centrifuge tube at 4 °C.
   2. Use sterile microscissors to cut the fibers to desired length (<6 cm).
   3. Seed fibroblast cells directly into the lumina of the hollow fiber membranes at a seeding density of 100,000 cells per fiber using a 21-gauge needle with 1 mL syringe.
      NOTE: A practicable target for preparing the cell-suspension for loading in the syringe is a suspension density of 100,000 cells for every 30 microliters of medium.
   4. Place six seeded fibers into a 6 cm diameter Petri dish. Allow the seeded fibers to incubate at 37 °C with 5% CO₂ for five minutes.
   5. Remove the seeded fibers from incubation and culture them for up to 3 weeks in DMEM/F-12 containing final concentrations of 50 µg/mL L-ascorbic acid and 150 µg/mL L-ascorbic acid 2-phosphate (freshly prepared and sterile filtered), 5 ng/mL TGF-β1 (from sterile filtered aliquots stored at -20 °C), and 1% penicillin-streptomycin in a 6 cm Petri dish within a 5% CO₂ incubator at 37 °C. Exchange cell medium every two days.
5. Extraction of extracellular matrix from cultured hollow fiber membranes
   1. Place cultured fibers into individual scintillation vial using forceps.
   2. Place up to 5 mL of NMP into each vial using a glass pipette.
   3. Immerse the hollow fibers in NMP, performing a total of three exchanges of NMP. Slowly aspirate the old NMP using a 1 mL pipette to prevent tearing of extracted ECM.
      NOTE: When adding fresh NMP, it is helpful to tilt the vial and allow the NMP run down the sides, otherwise the remaining ECM scaffold is subjected to shear which may cause tearing.
   4. Remove NMP and rinsed the resulting ECM thread 3 times in deionized water.
   5. Cut a 1/32-inch thick sheet of silicone rubber to a length of 3 inches, width of 1 inch and cut an 8 mm by 4 mm rectangular mold in the center of the length of rubber.
   6. Place the prepared piece of rubber onto a standard 3-inch by 1-inch microscopy slide and autoclave at 121 °C for 30 minutes.
   7. Lay each ECM fiber side by side in the 8 mm by 4 mm silicone mold until there is no visible open space.
   8. Place the mold into a 50 mL conical centrifuge tube and freeze at -80°C until completely frozen.
   9. Lyophilize frozen ECM mesh overnight or until completely dry. Store the mesh at 4°C until ready for decellularization.

2. Decellularization of Extracellular Matrix

1. Prepare a solution of 1% (w/w%) sodium dodecyl sulfate (SDS) in deionized water.
2. Incubate extracted extracellular matrix in the mold in 1% SDS for 24 hours at room temperature on a rocker with gentle agitation.
3. Rinse extracted extracellular matrix three times in sterile phosphate-buffered saline (PBS) with gentle agitation, using 3 mL of PBS per rinse.
   NOTE: Rinses should be performed gently to minimize tearing of prepared scaffolds.
4. Prepare 1 L of DNAse/RNAse digestion buffer.
   NOTE: DNAse/RNAse digestion buffer may be stored for several months at 4°C.
   1. Weigh 1.54 g of Tris HCl, 308 mg of MgCl₂, and 56 mg of CaCl₂ in separate weigh boats.
   2. Combine Tris HCl, MgCl₂, and CaCl₂ with 1 L of deionized water in a large flask with a stir bar and stir until all components are dissolved.
   3. Sterile filter the digestion buffer with a 0.22 µm filter into a sterile 1 L borosilicate bottle and store at 4°C.
5. Prepare 5 mL of DNAse/RNAse digestion solution.
   NOTE: Digestion solution should be used within 24 hours of preparation.
   1. Weigh 0.125 mg (50 kU) of DNAse I in a weigh boat and add to 5 mL of digestion buffer.
   2. Add 75 µL of RNAse A stock solution to the digestion buffer.
6. Fill each mold with digestion solution and incubate at 4 °C for 6 hours.
7. Aspirate the digestion solution and rinse three times in sterile PBS.
8. Aspirate the PBS and incubate scaffolds overnight in 10% penicillin-streptomycin in PBS at 4°C.
9. Aspirate the penicillin-streptomycin and rinse scaffolds three times in sterile PBS.
10. Place the mold into a 50 mL conical centrifuge tube and freeze at -80°C.
11. Lyophilize the decellularized ECM mesh overnight or until completely dry.
12. Transfer the lyophilized scaffolds within a biosafety hood to a sterile container at 4°C pending use.

Results

Successful production of extracellular matrix from sacrificial scaffolds is contingent on appropriate scaffold fabrication, cell culture, and solvent rinse procedures. Fabrication of the hollow fiber membranes is performed using a dry-jet wet-spinning system assembled from commercially available components (Figure 1) which uses extrusion of polymer solution through the annulus of a commercially available steel spinneret (inner diameter = 0.8 mm, outer diamete...

Discussion

The processes described enable the production of bulk ECM biomaterials in vitro using hollow fiber membranes cast by a dry-jet wet spinning system allowing for inexpensive bulk production of membranes as well as standard cell culture equipment. While the membranes fabricated in this protocol are intended for use in cell culture, the system described can also be adapted for the production of membranes for separation purposes, with pore size distribution and hollow fiber dimensions tunable by varying spinneret dim...

Materials

List of materials used in this article

Name	Company	Catalog Number	Comments
1/32 inch thick silicone rubber	Grainger	B01LXJULOM
20 mL Scintillation Vials, Borosilicate glass, Disposable - VWR	VWR	66022-004	With attached white urea cap and cork foil liner
3 inch by 1 inch microscopy slides	VWR	75799-268
4C refrigerator	Thermo Fisher Scientific	FRGG2304D	Any commercial 4C refrigerator will suffice.
50 mL tubes	VWR	21008-178
6-well cell culture plates	VWR	10062-892	Alternative brands may be used
Acetone	VWR	E646	Alternative brands may be used
Bore vessel	McMaster-Carr	89785K867	6 ft 316 steel tubing
Bovine Plasma Fibronectin	Thermo Fisher Scientific	33010018	Comes as 1 mg of lyophilized protein
CaCl2	VWR/Amresco	97062-590
Cell Culture Incubator w/ CO2			Any appropriate CO2-supplied mammalian cell incubator will suffice.
Disposable Serological Pipets, Glass - Kimble Chase	VWR	14673-208	Alternative brands may be used
DMEM/F-12, HEPES	Thermo Fisher Scientific	11330032	Warm in water bath at 37°C for 30 minutes prior to use
DNase I	Sigma-Aldrich	DN25-10MG
Dope vessel	McMaster-Carr	89785K867	6 ft 316 steel tubing
Ethanol	VWR	BDH1160	Dilute to 70% for sterilization
Fetal Bovine Serum, qualified, US origin - Gibco	Thermo Fisher Scientific	26140079	Mix with growth media at 10% concentration (50mL in 500mL media)
Four 1/4-inch to 1" reducing unions	Swagelok	SS-1610-6-4	One reducing union for each inlet and outlet of each vessel
Freeze-dryer/lyophilizer	Labconco	117 (A65312906)	Any lyophilizer will suffice.
Hexagonal Antistatic Polystyrene Weighing Dishes - VWR	VWR	89106-752	Any weigh boat will suffice
Hollow fiber membrane immersion bath			34L polypropylene tubs may be used or large bath containers can be fabricated from welded steel sheets
Hollow Fiber Membrane Spinneret	AEI	http://www.aei-spinnerets.com/specifications.html	Made to order. Inner diameter = 0.8 mm, outer diameter = 1.6 mm
Hot plate/stirrer	VWR	97042-634
Human TGF-β1	PeproTech	100-21
L-Ascorbic acid	Sigma-Aldrich	A4544-25G
L-Ascorbic acid 2-phosphate	Sigma-Aldrich	A8960-5G
L-glutamine (200 mM) - Gibco	Thermo Fisher Scientific	25030081	Mix with growth media at 1% concentration (5mL in 500mL media)
MgCl2	VWR/Alfa Aesar	AA12315-A1
Minus 80 Freezer	Thermo Fisher Scientific	UXF40086A	Any commercial -80C freezer will suffice.
N2 gas cylinders (two)
NIH/3T3 cells	ATCC	CRL-1658	Alternative fibrogenic cell lines may be used.
N-methyl-2-pyrrolidone	VWR	BDH1141	Alternative brands may be used
Penicillin/Streptomycin Solution - Gibco	Thermo Fisher Scientific	15140122	Mix with growth media at 0.1% concentration (0.5 mL in 500mL media)
Polysulfone	Sigma-Aldrich	428302	Any polysulfone with an average Mw of 35,000 daltons may be used
Portable Pipet-Aid Pipetting Device - Drummond	VWR	53498-103	Alternative brands may be used
PTFE tubing (1/4-inch inner diameter)	McMaster-Carr	52315K24	Alternative brands may be used.
Rat skeletal muscle fibroblasts			Independently isolated from rat skeletal muscle. Alternative fibrogenic cell lines may be used.
RNase A	Sigma-Aldrich	R4642
Silicone sheet	McMaster-Carr	1460N28
Take-up motor	Greartisan	B071GTTSV3	200 RPM DC Motor
Tris HCl	VWR/Amresco	97063-756
Two needle valves	Swagelok	SS-1RS4