Name: Fabrication of a Microfluidic Device for the Compartmentalization of Neuron Soma and Axons (Video) | JoVE Journal
Uploaded: 2007-08-22T00:00:00.000+00:00
Duration: 10 min 58 s
Description: Learn soft lithography using PDMS to fabricate a microfluidic device for compartmentalizing neuron soma and axons. This method enables pure axonal fraction collection and advanced neurobiology studies.

ai_agent_IP

ai_agent

maintenance

instantTrialDurationMinutes

isBiopharma

enableNewMyJoveSectionDesign

educationFeatures

seoMetaApi

ai_copilot_institution_blacklist

ai_chat_institution_blacklist

freeAccessWindow

ssoRoleCapture

scheduledMaintenanceBanner

joveLabsFeatures

disable_autoplay_for_bots

extended_trial_duration

5 minutes

Part 1: Preparing the microfluidic neuron device
<ol>
<li>A&nbsp;3" silicon wafer with a pattern made out of SU-8 by photolithography is used to cast the Polydimethylsiloxane (PDMS) microfluidic mold. We refer to the SU-8 patterned silicon wafer as master molds, or "masters".</li>
<li>PDMS is mixed with curing agent at a w/w ratio of 10:1, that is, for 10 grams of PDMS, 1 gram of curing agent is added to it.</li>
<li>The PDMS is then mixed well and poured onto the silicon wafer. The silicon wafer is contained within a 10 cm polystyrene Petri dish. It takes approximately 12 g to 15 g of PDMS to cover the master with a thickness of approximately 4 mm.</li>
<li>The master with the PDMS is then placed in a vacuum dessicator with the lid off the Petri dish, and vacuum is applied. This is done to help remove air bubbles from the PDMS that were introduced during the stirring in of the curing agent.&nbsp; It takes approximately 15 minutes for the air bubbles to be removed.</li>
<li>The master with PDMS is removed from the dessicator. An air gun with a 0.45 um filter is used to remove any remaining bubbles.</li>
<li>The master is then placed on an 80&deg;C hot plate for 1 hour to cure.</li>
</ol>
Note: If a vacuum dessicator is not available, the master can be left at room temperature for several hours. The air bubbles will eventually dissipate on their own. If a hot plate is not available, the PDMS will cure at room temperature after 24 hours.
Note: It is also important to make sure that the master is level during the curing process.
Part 2: Cutting out the neuron microfluidic device
<ol>
<li>Once the PDMS is cured on the master, it is taken to a clean hood.</li>
<li>Using a surgical blade, a circle is cut around the perimeter of the devices. When one inserts the blade into the PDMS, it is important to make contact with the silicon wafer but to NOT put too much pressure on the wafer, else the master will crack.</li>
<li>With a circle cut all the way around the devices (there are 4 devices per each 3" Silicon Master), the PDMS is carefully lifted off the master. This can be started by gently twisting the surgical blade as it is inserted into the prior cut.</li>
<li>Next, reservoirs are punched into the device using an 8 mm tissue biopsy punch.</li>
<li>The devices are then quartered and excess PDMS trimmed away so that the device will fit neatly on Corning Cover Glass (No. 1) 24 mm x 40 mm. Nitrogen air is used to blow away any excess debris. Stubborn debris can also be removed using 3M Scotch Brand 471 vinyl tape.</li>
</ol>
Part 3: Plasma bonding the devices to glass cover slips.
<ol>
<li>Plasma Cleaner is used to bond A Harrick the neuron devices to the cover slips. Briefly, the devices are placed in the plasma cleaner and a vacuum pump is used to evacuate air from the chamber.</li>
<li>After the vacuum pressure has reached 300 milliTorr, power is turned on to the electrical coil and set to high.</li>
<li>The electrical coil creates plasma, "a partially ionized gas consisting of electrons, ions and neutral atoms or molecules" - <a href="http://www.harrickplasma.com/plasma_physics.php">http://www.harrickplasma.com/plasma_physics.php</a>, out of the remaining air molecules left in the chamber. The plasma creates reactive species on the surfaces of the glass and the device, which when placed together will form a permanent bond. The plasma also turns the surfaces hydrophilic, which helps facilitate the addition of liquids. Additionally, the plasma cleaner sterilizes the devices. The surface of the PDMS device that contains the microfluidic device is placed face up into the plasma cleaner along with the glass slides. The plasma treated surfaces of the glass and microfluidic device are assembled in contact with each other&nbsp;at a clean bench, then placed in sterile 60 mm dishes. The treated surfaces form a tight irreversible bond. </li>
<li>Within 10 minutes of plasma bonding the devices to glass, Poly-L-Lysine (PLL) is added to the device. After 10 minutes, the hydrophilicity of the device will decrease making it difficult for the PLL to enter the device. Note: It is important to check for air bubbles in the device after the addition of PLL. Air bubbles in the main channel are undesirable, as they would oxidize cells. An easy method to remove any existing air bubbles is to use a P200 pipet filled with 150 ul of liquid (in this case PLL), place the tip directly at the opening of the main channel, and depress the P200 forcefully. This may need to be repeated several times but eventually the force from the pipet will drive the bubbles out. </li>
<li>The devices containing PLL are allowed to incubate overnight in a standard tissue culture incubator at 37&deg;C with 5% CO2.</li>
<li>The next day, the devices are rinsed twice quickly with autoclaved dH2O. During this process, liquid is never entirely removed from the main channels, only from the reservoirs. Removing liquid from the main channels will introduce bubbles. After 2 quick rinses, the devices are filled with autoclaved dH2O and placed back into the incubator for a minimum of 3 hours, or overnight.</li>
<li>The next day, the devices are once again rinsed 2 times quickly with autoclaved dH2O. Then, neural basal media, containing the necessary supplements B27 and glutamax for culturing primary rat neurons, is added to the devices. The devices are placed back in the incubator for future use. The devices are now ready for the seeding of neurons.</li>
</ol>

<ol><li>Park, J. W., Vahidi, B., , A. M., Rhee, S. W., Jeon, N. L. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((Microfluidic+culture+platform+for+neuroscience+research.%5BTitle%5D)+AND+%22Nat+Protoc%22%5BJournal%5D)">Microfluidic culture platform for neuroscience research.</a> Nat Protoc. 1, 2128-2136 (2006).</li>
<li>Taylor, A. M., Blurton-Jones, M., Rhee, S. W., Cribbs, D. H., Cotman, C. W., Jeon, N. L. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/pubmed?term=((A+microfluidic+culture+platform+for+CNS+axonal+injury%2C+regeneration+and+transport%5BTitle%5D)+AND+%22Nat+Methods%22%5BJournal%5D)">A microfluidic culture platform for CNS axonal injury, regeneration and transport.</a> Nat Methods. 2, 599-605 (2005).</li>
</ol>

In this video we have demonstrated how to make and prepare a PDMS microfluidic device that we use to culture neurons in. The device allows us to obtain a pure axonal fraction separated by microgrooves from the compartment containing a mix of cell bodies, dendrites, and axons. These devices allow the researcher to study the effects of various treatments as well as provide a platform to carry out physical injury on the axons and observe what effects these treatments have on the neurons. The device also provides a level of order to culturing neurons that helps facilitate transport studies. In addition, the microgrooves, which separate the cell culture compartment from the axon compartment, allows for fluidic isolation between the two compartments making it possible to treat one side of the device without effecting the other side of the device directly with the treatment. This property allows the researcher to study effects such as signal transduction and transport that result from the treatment.

<table><tbody><tr><td>PDMS</td><td>Reagent</td><td>Dow Corning</td><td></td><td>Sylgard 184 with curing agentPlease consult Dow Corning to find a vendor near you</td></tr><tr><td>Plasam Cleaner</td><td>Tool</td><td>Harrick Scientific Products, Inc.</td><td></td><td>http://www.harrickplasma.com/</td></tr><tr><td>Neural Basal Media</td><td>Reagent</td><td>Invitrogen</td><td>21103-049</td><td>Neural Basal Media is obtained by Invitrogen under their Gibco line of cell culture reagents.</td></tr><tr><td>B27</td><td>Reagent</td><td>Invitrogen</td><td>17504-044</td><td>B27 is a proprietary supplement available through Invitrogen under their Gibco line of cell culture reagents.</td></tr><tr><td>Glutamax</td><td>Reagent</td><td>Invitrogen</td><td>35050-061</td><td>Glutamax is available through Invitrogen under their Gibco line of celll culture reagents.</td></tr><tr><td>Cornig No. 1 Cover Glass</td><td>cover glass</td><td>Corning</td><td>Corning No. X2935 244</td><td>Available through Fisher Scientific, Fish Catalog number 12-531D</td></tr><tr><td>60 mm Petri Dish</td><td>Tool</td><td>Fisher Scientific</td><td>08-757-13A</td><td>60 mm polystyrene sterile petri dishes are used to house the device bound to glass.</td></tr><tr><td>BD Falcon 50 ml Tube</td><td>Tool</td><td>BD Biosciences</td><td>Falcon No. 352098</td><td>Available through Fisher Scientific catalog number 14-959-49A</td></tr><tr><td>BD Falcon 15 ml tube</td><td>Tool</td><td>BD Biosciences</td><td>Falcon No. 352097</td><td>Available through Fisher Scientific catalog number 14-959-70C</td></tr><tr><td>Poly-L-Lysine</td><td>Reagent</td><td>Sigma-Aldrich</td><td>P-1274</td><td></td></tr><tr><td>New Item</td><td></td><td></td><td></td><td></td></tr></tbody></table>

fabrication of a microfluidic device for the compartmentalization of neuron soma and axons

Fabrication of a Microfluidic Device for the Compartmentalization of Neuron Soma and Axons

In this video, we demonstrate the technique of soft lithography with polydimethyl siloxane (PDMS) which we use to fabricate a microfluidic device for culturing neurons. Previously, a silicon wafer was patterned with the design for the neuron microfluidic device using SU-8 and photolithography to create a master mold, or what we simply refer to as a "master". Next, we pour the silicon polymer PDMS on top of the master which is then cured by heating the PDMS to 80&deg;C for 1 hour. The PDMS forms a negative mold of the device. The PDMS is then carefully cut and lifted away from the master. Holes are punched where the reservoirs will be and the excess PDMS trimmed away from the device. Nitrogen is used to blow away any excess debris from the device. At this point the devices are now ready for use and can either bonded to corning No. 1 cover glass with a plasma sterilizer/cleaner or can be reversibly bound to the cover glass by simply placing the device on top of the cover glass. The reversible bonding of the device to glass is covered in a separate video and requires first that the device be sterilized either with 70% ethanol or by autoclaving. Plasma treating sterilizes the devices so no further treatment is necessary. It is, however, important, when plasma-treating the devices, to add liquid to the devices within 10 minutes of the plasma treatment while the surfaces are still hydrophilic. Waiting longer than 10 minutes to add liquid to the device makes it difficult for the liquid to enter the device. The neuron devices are typically plasma-bound to cover glass and 0.5 mg/ml poly-L-lysine (PLL) in pH 8.5 borate buffer is immediately added to the device. After a minimum of 3 hours incubating with PLL, the devices are washed with dH2O water a minimum of 3 times with at least 15 minutes between each wash. Next, the water is removed and fresh media is added to the device. At this point the device is ready for use. It is important to remember at this point to never remove all the media from the device. Always leave media in the main channel.

In this video we demonstrate the technique of soft lithography with polydimethyl siloxane (PDMS) which we use to farbricate a microfluidic device for culturing neurons.

In this video, we demonstrate the technique of soft lithography with polydimethyl siloxane (PDMS) which we use to fabricate a microfluidic device for ...

Welcome to the laboratory of Dr.Newly John. The John Lab specializes in engineering microfluidic platforms for biological applications. In this video, we will demonstrate the production and utilization of a microfluidic device designed for compartmentalizing and the culturing of primary neurons.The neuron device was first published in Nature Methods in August of 2005. Since its introduction, the neuron device has been used widely by collaborators all over the world. The neuron device consists of a piece of PDMS that has been cast on a silicon wafer containing an SUA pattern of the device, which was previously created by photolithography.The device has three main features, four reservoirs, eight millimeters in diameter, two main channels each 1.5 millimeter wide, seven millimeters long and a hundred microns tall and micro grooves, which are 10 micrometers wide and three micrometers in height that join the two main channels. The micro grooves can vary in length from 150 microns to 900 microns, though the standard length of choice is 450 microns. Observing the device so that the main channels and the micro grooves are vertical, we can see that the reservoirs on the left of the grooves are connected via the main channels, as are the reservoirs on the right.This feature allows liquid to flow through the main channel, which is an important feature, making it possible to load cells and change media. The neuron device has three major advantages over traditional tissue culture platforms. One, it allows for the com compartmentalization of cell bodies or soma and the axons With the neuron device, it is possible to obtain pure axonal fractions.The size and length of the micro grooves allow axons to pass through the other main channel while preventing the saw bodies from crossing over. Number two, due to the design of the device and taking advantage of hydrostatic pressure, it is possible to subject either the cell side and or the axon side of the device to separate treatments simply by maintaining the volume and the reservoirs higher on one side of the device versus the other. And number three, the pure axonal fraction of the device can be cut by vacuum suction, allowing the researcher to study and observe axonal regeneration.Researcher Hina Lee will now demonstrate preparing the microfluidic neuron Device. A three Ang silicon wafer with a pattern made out of SU eight by a photolithography is used to cast the poly dimethyl Sloane PDMS microfluidic mold. We refer to the SUA pattern silicon wafer as master molds or simply masters.PDMS is mixed with curing agent at a weight for weight ratio of 10 to one. That is, for example, 15 grams of PDMS per 1.5 grams of curing agent. The PDMS is then mixed well and poured onto the silicon wafer.The silicon wafer is contained within a 10 centimeter polystyrene Petri dish. It takes approximately 12 grams to 15 grams of PDMS to cover the MAs with a thickness of approximately four millimeter. The master with the PDMS is then placed in a vacuum desiccate with the lid off the Petri dish and vacuum is applied.This is done to help remove air bubbles from the PDMS that were introduced during the stirring of the curing agent. It takes approximately 15 minutes for the air bubbles to be removed. The master with PDMS is removed from the desiccate after 15 minutes in the vacuum desiccate.There are still a few remaining bubbles on the PDMS master. An air gun with a 0.45 micron filter is used to remove any remaining bubbles. The master is then placed on an 80 degree hot plate for one hour to cure.If a vacuum desiccate is not available, the master can be left at room temperature for several hours. The air bubbles will eventually dissipate on their own. If no hot plate is available, the PDMS will cure at room temperature after 24 hours.It's important to make sure that the master is level During the curing process. Once the PDMS is cured on The master, it is taken to a clean hood using a surgical blade. A circle cut around the perimeter of the devices is made.It is important that when one inserts the blade into the PDMS to make contact with the silicon wafer, but not to put too much pressure on the wafer or else the master will crack with a circle cut all the way around the devices. There are four devices per each three inch silicon master. The PDMS is carefully lifted off the master.This can be started by gently twisting the surgical blade as it is inserted into the prior cut. It's really thin with the PDMS devices on the mold. Face up reservoirs are punched into the device using an eight millimeter tissue biopsy punch.The debris left in the puncher is pushed out with a rod. The devices are then quartered and excess PDMS trimmed away so that the device will fit neatly onto a Corning cover. Glass number one size 24 millimeter by 40 millimeter nitrogen air is used to blow away any excess debris.Stubborn debris can also be removed using 3M Scotch Brand 4 7 1 vinyl tape. The clean devices are now ready for plasma bonding. A herrick plasma cleaner is used to Bond the neuron devices to the cover slips briefly.The devices and the cover slips are placed on a tray, and the tray will then be placed into the plasma cleaner and a vacuum pump used to evacuate air from the chamber. It is important to note that the PDMS devices are placed face up. That is with the design face up so that they will be exposed to the plasma gas.After the vacuum pressure has reached 300, millitorr power is turned onto electric coil and set to high. All is cracked on the door to let a little bit of air into the chamber, which will help generate the plasma. The devices and the cover glass are plasma treated for two minutes.Notice the purple color in the chamber. That's the actual plasma. The electric coil creates plasma, which is a partially ionized gas consisting of electrons, ions, and neutral atos or molecules.The plasma creates reactive species on the surface of the glass and the device, which when placed together will form a permanent bond. The plasma also turns the surface's hydrophilic, which helps facilitate the addition of liquids. The plasma cleaner also sterilizes the devices.After plasma treating for two minutes, the power in the vacuum is turned off and air is led into the chamber. The plasma treated services of the glass and the microfluidic device are assembled in contact with each other in a clean bench. The devices are then placed in a sterile 60 millimeter dishes.The plasma treated surfaces of the glass and the device form a tight irreversible bond. Within 10 minutes of plasma bonding, the device is to the glass polyol lysine is added to the device. After 10 minutes, the hydrophilicity of the device will decrease.Making it difficult for the PLL to enter the device. It is important to check for air bubbles in the device after the addition of PLL. An easy method to remove air bubbles present is to use a P 200 pipette filled with 100 microliters of liquid.In this case, PLL place the tip directly at the opening of the main channel, then depress the P 200 forcefully. This may need to be repeated several times, but eventually the force from the pipette will drive the bubbles out. The devices containing PLL are allowed to incubate overnight and a standard tissue culture incubator at 37 degrees with 5%CO2.After 24 hours of incubation with PLL, the devices are rinsed twice quickly with autoclave deionized water. During this process, liquid is never entirely removed from the main channels, only from the reservoirs. Removing liquid from the main channels will introduce bubbles.After two quick rinses, the devices are filled with autoclave deionized water once again and placed back in the incubator for a minimum of three hours or overnight. The next day, after the devices have been incubated with water overnight or for a minimum of three hours, they're once again brought into the biosafety cabinet and rinse twice with deionized water. Then neural basal media containing the necessary supplements, B 27 and glutamate for culturing primary rat neurons is added to the devices.The devices are then placed back in the incubator for future use. The devices are now ready for seating neurons. In this video, We have demonstrated the technique of soft lithography, which we use to manufacture our neuron devices.These devices can be used to culture neurons and other cell types of interest. The primary advantage of these devices is the ability to separate and compartmentalize the culturing of the neuron cell bodies on one side of the device from a pure axonal fraction on the other side of the device. In the next video, we will show you how we prepare E 18 fetal rack cortical neurons and how we load the cells into the device.So that's it from the John Lab. Thanks for watching.

fabrication-microfluidic-device-for-compartmentalization-neuron-soma

Research

JoVE Journal

Biology

In this video we demonstrate the preparation of E18 Cortical Rat Neurons.

Preparing E18 Cortical Rat Neurons for Compartmentalization in a Microfluidic Device

This video describes the fabrication and use of a microfluidic device to culture central nervous system (CNS) neurons.  This device is compatible with ...

BioMEMS: Forging New Collaborations Between Biologists and Engineers

We developed a novel multi-compartment neuron co-culture microsystem platform for in vitro CNS axon-glia interaction research. The platform is capable of conducting up to six independent experiments in parallel and was fabricated using a newly developed macro/micro hybrid fabrication method.

A Multi-compartment CNS Neuron-glia Co-culture Microfluidic Platform

This video demonstrates the utilization of a pre-assembled plastic microfluidic chip for the compartmentalized culture of primary rat hippocampal neurons. The neurons are plated into one of the microfluidic compartments, where they attach and grow, extending their axons through the chip's microgrooves into the adjacent compartment. The narrow microgrooves prevent neuronal cell bodies from entering, thereby enabling physical separation between the somatic and axonal compartments.

Compartmentalized Primary Murine Neuron Culture Using Plastic Microfluidic Chips

The video demonstrates the differentiation of neural stem cells (NSCs) using a microfluidic device comprising a somatic and an axonal compartment separated by a microgroove barrier. NSCs are introduced into the somatic compartment and are allowed to adhere. The NSCs differentiate into neurons inside the somatic compartment and extend axons through the microgroove barrier to the axonal compartment.

Differentiation of Neural Stem Cells to Neurons Using a Compartmentalized Microfluidic Device

Protocols for single neuron microfluidic arraying and water masking for the in-chip plasma patterning of biomaterial coatings are described. Highly interconnected co-cultures can be prepared using minimal cell inputs.

Preparation of Neuronal Co-cultures with Single Cell Precision

This manuscript details the fabrication of micro-tissue engineered neural networks: three-dimensional micron-sized constructs comprised of long aligned axonal tracts spanning aggregated neuronal population(s) encased in a tubular hydrogel. These living scaffolds can serve as functional relays to reconstruct or modulate neural circuitry or as biofidelic test-beds mimicking gray-white matter neuroanatomy.

Anatomically Inspired Three-dimensional Micro-tissue Engineered Neural Networks for Nervous System Reconstruction, Modulation, and Modeling

This protocol describes the use of plastic chips to culture and compartmentalize primary murine neurons. These chips are preassembled, user-friendly, and compatible with high-resolution, live, and fluorescence imaging. This protocol describes how to plate rat hippocampal neurons within these chips and perform fluidic isolation, axotomy and immunostaining.

Use of Pre-Assembled Plastic Microfluidic Chips for Compartmentalizing Primary Murine Neurons

This protocol demonstrates the use of compartmentalized microfluidic chips, injection molded in a cyclic olefin copolymer to cultured neurons differentiated from human stem cells. These chips are preassembled and easier-to-use than traditional compartmentalized poly(dimethylsiloxane) devices. Multiple common experimental paradigms are described here, including viral labeling, fluidic isolation, axotomy, and immunostaining.

Compartmentalization of Human Stem Cell-Derived Neurons within Pre-Assembled Plastic Microfluidic Chips

The present protocol describes the seeding and staining of neuronal mitochondria in microfluidic chambers. The fluidic pressure gradient in these chambers allows for the selective treatment of mitochondria in axons to analyze their properties in response to pharmacological challenges without affecting the cell body compartment.

Microfluidics-Assisted Selective Depolarization of Axonal Mitochondria

This protocol describes a microfluidic system modeling neuronal metabolic dynamics post-axonal injury, enabling imaging, multi-omics analysis, and mechanistic studies of intrinsic metabolic remodeling.

Microfluidic Chip for Axonal Injury Models Construction and Enabling Multi-Omics Analysis

Learn soft lithography using PDMS to fabricate a microfluidic device for compartmentalizing neuron soma and axons. This method enables pure axonal fraction collection and advanced neurobiology studies.

Fabrication of a Microfluidic Device for the Compartmentalization of Neuron Soma and Axons

Explore More Videos