Préparation de ZnO nanotige / graphène / ZnO nanotige épitaxiale double hétérostructure pour piézoélectriques Nanogénérateur à l'aide de préchauffage hydrothermale
A subscription to JoVE is required to view this content. Sign in or start your free trial.
1Department of Nanoenergy Engineering, BK21 Plus Nanoconvergence Technology Division,Pusan National University (PNU), Miryang, 2Department of Cogno-Mechatronics Engineering,Pusan National University (PNU), Busan, 3SKKU Advanced Institute of Nanotechnology (SAINT), Center for Human Interface Nanotechnology (HINT), SKKU-Samsung Graphene Center,Sungkyunkwan University (SKKU)
Chapters
- 00:05Title
- 01:08Chemical Vapor Deposition (CVD) Growth of Single Layered Graphene
- 02:20Preparation of Graphene/Polyethylene Terephthalate (PET) Substrate
- 04:03Synthesis of ZnO Nanorod/Graphene/ZnO Nanorod Epitaxial Double Heterostructure
- 05:23Fabrication of Piezoelectric Nanogenerator
- 07:01Electrical Performance Measurement Setup
- 08:18Results: Scanning Electron Microscopy (SEM) Images of Hydrothermally Grown ZnO Nanorod and Representative Results for the Piezoelectric Nanogenerator
- 10:10Conclusion
Une étape procédé de fabrication pour obtenir autoportante double hétérostructure épitaxiale est présenté. Cette approche pourrait atteindre une couverture de ZnO avec une densité en nombre plus élevé que celui de l'hétérostructure épitaxiale unique, conduisant à une nanogénérateur piézoélectrique avec un rendement électrique de sortie accrue.