Surface Properties of Synthesized Nanoporous Carbon and Silica Matrices
DOI:

09:31 min

March 27, 2019

, , ,

Chapters

  • 00:04Title
  • 01:42Synthesis of a Silica Matrix as the Ordered Mesoporous Carbon Material Precursor
  • 03:11Impregnation of the Silica Matrix, using a Carbon Precursor
  • 04:15Tempering and Carbonization
  • 04:46Removal of the Silica Matrix by Etching
  • 06:17Capillary Rise Method for Wettability Measurements
  • 07:23Results: Contact Angles vs. the Microscopic Wetting Parameter Measured Inside the Porous Matrices
  • 08:11Conclusion

Summary

Automatic Translation

Aqui nós relatamos a síntese e caracterização de carbono nanoporous ordenada (com um tamanho de poro 4.6 nm) e SBA-15 (com um tamanho de poro 5.3 nm). O trabalho descreve a superfície e propriedades texturais de peneiras moleculares nanoporous, sua molhabilidade e o comportamento de derretimento de D2O confinado nos materiais.