Fabrication of Fully Solution Processed Inorganic Nanocrystal Photovoltaic Devices

Troy K. Townsend; Dario Durastanti; William B. Heuer; Edward E. Foos; Woojun Yoon; Joseph G. Tischler

doi:10.3791/54154

Journal

/

Engineering

/

Tillverkning av helt Lösning bearbetade oorganiska nanokristall Solceller Devices

Fabrication of Fully Solution Processed Inorganic Nanocrystal Photovoltaic Devices

JoVE Journal
Engineering

A subscription to JoVE is required to view this content. Sign in or start your free trial.

JoVE Journal Engineering

Fabrication of Fully Solution Processed Inorganic Nanocrystal Photovoltaic Devices

Tillverkning av helt Lösning bearbetade oorganiska nanokristall Solceller Devices

Please note that all translations are automatically generated. Click here for the English version.

10,405 Views

•

11:06 min

•

July 08, 2016

DOI:

10.3791/54154-v

DOI:

10.3791/54154-v

•

11:06 min

July 08, 2016

•

10393 Views

Troy K. Townsend¹, Dario Durastanti¹, William B. Heuer², Edward E. Foos³, Woojun Yoon⁴, Joseph G. Tischler⁴

¹Department of Chemistry and Biochemistry,St. Mary’s College of Maryland ²Department of Chemistry,U.S. Naval Academy ³NSWC Indian Head EOD Technology Division ⁴Electronics and Devices Division,Naval Research Laboratory

Summary

Detta protokoll beskriver syntesen och lösning avsättning av oorganiska nanokristaller lager för lager för att framställa tunna film elektronik på icke-ledande ytor. Lösningsmedels stabiliserade bläck kan producera kompletta solcellsanordningar på glassubstrat via spinn och spraybeläggning efter efteravsättning ligand utbyte och sintring.