Sputter Growth and Characterization of Metamagnetic B2-ordered FeRh Epilayers

Sputter Vækst og karakterisering af Metamagnetic B2 bestilt FeRh Epilayers

DOI:
10.3791/50603-v

•

12:20 min

•

October 05, 2013

•

, , , , , , ,
1School of Physics and Astronomy,University of Leeds, 2Institute of Materials Research,University of Leeds, 3School of Chemistry,University of Edinburgh, 4Department of Chemical Engineering,Northeastern University, 5Department of Physics,Northeastern University

Chapters

  • 00:05Title
  • 02:02Substrate and Target Preparation
  • 04:13Epilayer Deposition
  • 06:13Post-growth Epilayer Characterization
  • 09:46Analysis of Iron Rhodium Epilayer
  • 11:47Conclusion

Summary

Automatic Translation

Automatic Translation

En fremgangsmåde til fremstilling af epitaksiale lag ordnede legeringer ved sputtering er beskrevet. B2-ordnet FeRh forbindelse anvendes som et eksempel, da den viser en metamagnetic overgang, der afhænger følsomt af graden af ​​kemisk orden og den nøjagtige sammensætning af legeringen.

Tags

Sputter DepositionEpitaxial Thin FilmsB2-ordered FeRhMgO SubstratesX-ray ReflectometryTransmission Electron MicroscopyMetamagnetic Phase TransitionAntiferromagnetic Ground StateEquiatomic StoichiometryB2 Ordering

Article

Embed

ADD TO PLAYLIST

Usage Statistics

Related Videos

Simulation, Fabrication and Characterization of THz Metamaterial Absorbers

Fabrication And Characterization Of Photonic Crystal Slow Light Waveguides And Cavities

Design, fremstilling, and Experimental karakterisering af plasmoniske Photoconductive Terahertz Emitters

Skrivning og lav temperatur Karakterisering af Oxide nanostrukturer

Mønster via optisk mættede Transitions - fremstilling og karakterisering

Protokol for elektrokemisk Test og karakterisering på aprotiske Li-O<sub> 2</sub> Batteri

Fremstilling og karakterisering af superledende Resonatorer

Produktion og karakterisering af vakuum deponerede organisk lysemitterende dioder

Vækst og elektrostatisk/kemiske egenskaber af Metal/LaAlO3/SrTiO3 Heterostructures

Plasma-assisteret molekyl stråle Epitaxy-vækst på mg3n2 og Zn3n2 tynde film

Read Article