In Situ Synthesis of Gold Nanoparticles without Aggregation in the Interlayer Space of Layered Titanate Transparent Films
Please note that all translations are automatically generated. Click here for the English version.

在没有聚集的层状钛酸盐薄膜透明的层间金纳米粒子的原位合成

DOI:
10.3791/55169-v

•

07:08 min

•

January 17, 2017

•

, , , , ,
1Department of Material Science and Technology, Faculty of Engineering,Niigata University

Chapters

  • 00:05Title
  • 00:49Synthesis of TNS Films
  • 04:08Results: In Situ Synthesis of AuNP within Layered Titanate Films
  • 05:42Conclusion

Summary

Automatic Translation

Automatic Translation

在这里，我们提出了一个协议为原位合成层状钛酸盐薄膜的夹层空间内的黄金纳米粒子（纳米金）的无金纳米颗粒的聚集。即使4个月后没有观察到的光谱变化。合成的材料已预期在催化，光催化，并具有成本效益的电浆设备的开发应用程序。

Tags

Gold NanoparticlesLayered TitanateTransparent FilmsNanostructured HybridsMetal NanoparticlesRadial SemiconductorsPigmentsDyesCatalystsPhotocatalystsNanostructuresIn Situ SynthesisMethyl ViologenTetrachloroauric AcidSodium Borohydride

Article

Embed

ADD TO PLAYLIST

Usage Statistics

Related Videos

黄金纳米粒子作为软木塞氮掺杂碳纳米管杯的合成与功能构造

检测和钯的回收，从城市矿山黄金和钴金属使用标有纳米货车车轮形的孔隙新型传感器/吸附剂

制备与表征超导谐振器的

厚度均匀葛电沉积<sub> 23</sub>锑<sub> 7</sub>取值<sub> 70</sub>和As<sub> 40</sub>取值<sub> 60</sub>硫系玻璃薄膜

放电等离子烧结设备中使用的钛酸锶双晶体的形成

用斜角沉积法制备高吸收介质的超薄彩色薄膜

结构转换的原位和原位研究方法: 金属玻璃结晶的实例

等离子金纳米粒子空化的可控核增强高强度聚焦超声应用

Gdba2cu 3 o7 的射频磁控管散射-/la0.67sr 0.67 mno 3 准双层薄膜上的 srtio 3 (sto) 单晶基板上

大面积地下纳米化的可控、可定制金纳米粒子通过包盖湿法

Read Article