Microhoneycomb Monolithen vorbereitet durch die unidirektionale Gefriertrocknung von Zellulose Nanofaser basierte Sols: Methode und Erweiterungen
A subscription to JoVE is required to view this content. Sign in or start your free trial.
1Engineering Laboratory for Functionalized Carbon Materials and Shenzhen Key Laboratory for Graphene-based Materials, Graduate School at Shenzhen,Tsinghua University, 2School of Materials Science and Engineering,Tsinghua University, 3Institute of Multidisciplinary Research for Advanced Materials,Tohoku University, 4Tsinghua-Berkeley Shenzhen Institute (TBSI),Tsinghua University, 5School of Chemical Engineering and Technology,Tianjin University
Chapters
- 00:04Title
- 00:57Preparation of 1 wt% (2,2,6,6-Tetramethylpiperidin-1-yl) oxyl (TEMPO)-mediated Oxidized Cellulose Nanofiber (TOCN) Sol
- 04:01Preparation of TOCN-TiO2 and TOCN-surface-oxidized Carbon Fiber (SOCF) Mixed Sols
- 04:59Microhoneycomb Monolith (MHM) Preparation from 1 Wt% TOCN Sol (MHM-TOCN) or TOCN Mixed Sols (MHM-TOCN/SBR, MHM-TOCN/TiO2, MHM-TOCN/SOCF)
- 06:54Results: Morphologies of the MHM-TOCN, MHM-TOCN/SBR, MHM-TOCN/TiO2, and MHM-TOCN/SOCF
- 08:39Conclusion
Hier präsentieren wir Ihnen ein allgemeines Protokoll um eine Vielzahl von Microhoneycomb Monolithen (MHMs) vorzubereiten, in welche Flüssigkeit mit einem extrem niedrigen Druckverlust passieren kann. MHMs erhalten sollen als Filter verwendet werden, Katalysator unterstützt, Bewegungsart Elektroden, Sensoren und Gerüste für Biomaterialien.